JPH08145185A - Gland packing - Google Patents

Abstract

PURPOSE: To secure a required recovering capability of compression and contacting capability with a shaft so as to provide a good sealing property over a long period by filling the filling material into a center core and the surface layer parts of a surface layers to be coated at higher dense than that of inner layer parts. CONSTITUTION: In a multi-braided wire structure, a center core 1 of square- braided wire structure is arranged at the center part of a cross section. Also, an impregnation density of filling material of a center core inner layer part 22 is lower than that of a surface layer part 21, the good elasticity of the center core 1 of square-braided wire structure is not impaired. Then, because an impregnation density of filling material 3 of the inner layer part 22 of a surface coated layer 2 is also lower than that of the surface layer part 21, the entire packing can maintain a good recovering capability of compression. Thus it can be suppress for the volume of the gland packing from being reduced according to the flowing out of the filling material 3. Also a good sealing property and lubrication capability can be maintained by the filling material 3 filled densely into the surface layer part 21 of the gland packing 2.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a string-shaped gland packing used for shaft sealing parts of various equipment such as pumps, agitators and valves.

[0002]

2. Description of the Related Art Conventionally, as the gland packing, various fibers including carbonized fibers are braided in a string shape by square knitting, lattice knitting, circular knitting or the like, or the above-mentioned fibers are circular knitting. Alternatively, there is known a multi-braid structure in which a center core is formed by braiding in a square shape by square braiding, and the periphery thereof is covered with a surface coating layer by circular knitting. These gland packings are impregnated with a plugging material such as polytetrafluoroethylene (PTFE), and the plugging material allows a fluid to penetrate inside the packing and leak, or cause a gap between the packing and the shaft or box. In addition to preventing leakage from the vehicle, desired lubricity can be ensured. This filling material is
The inside of the packing is uniformly impregnated, or the surface layer of the packing is mainly impregnated.

[0003]

In any of the above gland packings, since the filling material gradually flows out during use, there is a problem in that the sealing performance is deteriorated due to the volume reduction. In particular, the gland packing made of a single braid with lattice knitting is robust and has dense stitches, so it has good contact with the shaft, but it has poor compression restorability, so it seals with the outflow of plugging material. There is a problem that the property is greatly reduced. In addition, the gland packing made of a single braid in a square knit or a circular knit has a loose stitch, so it is excellent in compression restorability, but is inferior in contact with the shaft, local contact occurs, and the shaft is easily worn and When the knitting yarn is cut by sliding contact with the shaft, there is a problem that the braided structure is broken and the sealing performance is greatly reduced.

Further, since the conventional gland packing having a multi-braid structure is a composite of a core formed by circular knitting or square knitting and a surface coating layer formed by circular knitting, the gland packing is extremely excellent in compression restoring property, but does not come into contact with the shaft. There is a problem in that it is inferior in performance, the local contact easily occurs, the shaft is easily worn, the amount of leakage increases, and frequent additional tightening is required.

[0005] The present invention has been made in view of the above problems, and a gland capable of securing desired compression restorability and contact with a shaft and exhibiting good sealing performance over a long period of time. The purpose is to provide packing.

[0006]

A gland packing according to the present invention for achieving the above object is a string-shaped gland packing formed by braiding a large number of knitting yarns made of carbonized fiber. The core of the knitting structure is arranged, and the periphery of the core is covered with a surface coating layer of a lattice knitting structure, and the surface of the core and the surface coating layer is higher than the respective inner layer portions. The plugging material is impregnated at a density. It is preferable that the surface layer portion of each of the core and the surface coating layer is impregnated with a plugging material in an amount of 5 to 40% by weight. Further, the impregnation density ratio between the surface layer portion and the inner layer portion is determined as follows. 5: 1 to 3: 1, and 8: 1 in the surface coating layer.
５5: 1 is preferred.

[0007]

According to the gland packing having the above-described structure, the gland packing has a multi-braided structure in which a center core having a square knitting structure is disposed at the center of the cross section, and the impregnation density of the plugging material in the inner core layer is higher than that in the surface layer. Because it is low, without impairing the good elasticity of the core having the square knitting structure, and the impregnation density of the plugging material in the inner layer portion of the surface coating layer, coupled with a point lower than the surface layer portion, as a whole packing, Good compression / restoration can be ensured. For this reason, a decrease in the volume of the gland packing due to the outflow of the plugging material can be effectively suppressed.

[0008] Further, the sealing material with which the surface layer of the surface coating layer is impregnated at a high density can ensure good sealability and lubricity, and at the same time, a seal gap is generated due to wear of the sealing material. On the other hand, it is possible to compensate for this gap by restoring the elasticity of the center core. Furthermore, since the surface coating layer has a lattice knitting structure having a stitch that is about 2 to 4 times denser than the core, good contact with the shaft can be ensured, and the surface is knitted by sliding contact with the shaft. Even when the yarn is cut, the breakage of the braided structure can be prevented. In particular, when the surface layer portion of each of the core and the surface coating layer is impregnated with 5 to 40% by weight of a plugging material, lubricity and flexibility suitable for packing are obtained.
Flexibility and compression restorability can be ensured.

[0009]

【Example】

<Embodiment 1> FIG. 1 is a perspective view showing an embodiment of a gland packing according to the present invention. This gland packing has a multi-braided structure in which a core 1 of a square knitting structure is disposed at the center of the cross section, and the periphery of the core 1 is covered with a surface coating layer 2 having a lattice knitting structure. As shown in FIG. 2, the core 1 is made of eight knitting yarns 1 a made of carbonized fiber obtained by carbonizing an acrylic fiber, and is previously filled with a plugging material 3 made of PTFE fine particles (manufactured by Daikin Industries, Ltd.). : Trade name “Dai Flon”), and then the cord is braided by a square braid with two paths, and the surface layer 11 is impregnated with the plugging material 3 made of PTFE fine particles in the dispersion. When the plugging material 3 is impregnated, the plugging material 3 that has passed through the surface layer portion 11 is slightly impregnated into the inner layer portion 12. Here, the plugging material 3 of the surface layer portion 11 is impregnated with 30% by weight, and has a density approximately three times that of the plugging material 3 of the inner layer portion 12.

The surface coating layer 2 is formed by lattice knitting 20 knitting yarns 2a in which carbon fiber is impregnated with a filler material made of PTFE fine particles in advance with three paths, and then the surface layer portion 21 is formed.
The plugging material 3 made of fine particles of PTFE is impregnated again, and the plugging material 3 of the surface layer portion 21 is 40% denser than that of the inner layer portion 22 by about 8 times. Wt% impregnated. As the plugging material 3, a mixture of lubricating oil, solid lubricating material, and the like is used in addition to PTFE fine particles alone. Further, in the gland packing of the present embodiment, the cross-sectional area of the core 1 is configured to occupy about 25% in the cross section of the gland packing.

<Embodiment 2> FIG. 3 is a perspective view showing a main part of another embodiment of the gland packing of the present invention. The gland packing of this embodiment is the same as the gland packing of the first embodiment except that the number of the knitting yarns 2a of the surface coating layer 2 is 3
The number is six and the number of paths is four.

The gland packing having the above structure has a multi-braided structure in which a center core 1 of a square knitting structure is disposed at the center of the cross section and the periphery thereof is covered with a surface coating layer 2. The impregnation density of the plugging material 3 is set to about 1/3 of that of the surface layer portion 11, and the good elasticity of the core 1 having the square knitting structure is not impaired, and the surface coating layer 2 Since the impregnation density of the plugging material 3 in the inner layer portion 22 is set to be about 1/8 lower than that of the surface layer portion 21, good compression restorability can be exhibited as a whole packing. For this reason, it is possible to effectively suppress a decrease in the volume of the gland packing due to the outflow of the plugging material 3, and it is possible to exhibit good sealing properties over a long period of time.

Further, since the plugging material 3 of the surface layer portion 21 of the surface coating layer 2 has a high density, it is possible to ensure good sealing properties and lubricity. In addition, when the plugging material 3 of the surface coating layer 2 is worn out, the gap generated on the sealing surface can be compensated by restoring the core 1 by elasticity. For this reason, good sealing properties and lubricity can be ensured for a longer period.

Further, since the surface coating layer 2 has a dense knitted lattice structure, good contact with the shaft can be secured. Therefore, it is possible to prevent abrasion of the shaft due to local contact with the shaft, and to prevent the braided structure from being broken even when the knitting yarn 2a is cut by sliding contact with the shaft. Can be prevented. In particular, the surface layer portions 11 and 2 of the core 1 and the surface coating layer 2, respectively.
1, the plugging material 3 is impregnated with 5 to 40% by weight, and the impregnation density ratio between the surface layer portions 11 and 21 and the inner layer portions 12 and 22 of the core 1 and the surface coating layer 2 is 5:
1-3: 1, and 8: 1 in the surface coating layer 2.
When the ratio is set to ５5: 1, lubricity, flexibility, flexibility, and compression restorability more preferable as packing can be secured.

That is, the impregnation amount of the plugging material 3 is 5% by weight.
If it is less than 40% by weight, it is difficult to secure good sealing properties and lubricity, and if it exceeds 40% by weight, the surface layer portion 11,
21 becomes hard, and it becomes difficult to secure appropriate flexibility, flexibility, and compression restoring property. Moreover, when the impregnation density ratio of the surface layer portion 11 and the inner layer portion 12 of the core 1 becomes smaller than 3: 1, the impregnation density of the inner layer portion 12 relatively increases,
If the elasticity of the square knitting is impaired and becomes greater than 5: 1, the impregnation density of the inner layer portion 12 is relatively reduced, so that the core 1 itself becomes too flexible and the shape retention as a packing decreases. , Lowering the working pressure limit. On the other hand, in the surface coating layer 2, when the impregnation density ratio between the surface layer portion 21 and the inner layer portion 22 is smaller than 5: 1, the impregnation density of the inner layer portion 22 becomes relatively high, and the lattice knitting forming the surface coating layer 2 is performed. Combined with the dense structure, the flexibility of the packing is impaired, and if it is larger than 8: 1, the impregnation density of the inner layer portion 12 is relatively reduced, which hinders the maintenance of the lubrication characteristics for a long time. Become.

Table 1 shows the physical characteristics of the gland packing of the second embodiment and a gland packing having a conventional multi-braided structure (Comparative Example 1). In the comparative example 1, as shown in FIG. 11, the periphery of a core 51 in which a knitting yarn of carbonized fiber was square-braided was covered with a surface coating layer 52 made of a square braid. 52 is a method of braiding a knitting yarn of carbonized fiber with a number of paths of 2 and then braiding the surface layer with P
It is impregnated with 40% by weight of a plugging material composed of fine particles of TFE.

[0017]

[Table 1]

The compression ratio in Table 1 is 100 m in inner diameter.
m, an outer diameter of 129 mm, and a thickness of 14.5 mm are stacked in five stages, and the inner and outer peripheries and the bottom are restrained by a mold, with a load of 25 kgf / cm ² and a pressing speed of 2.5.
It is a value obtained by measuring the amount of compressive deformation Δt when compressing under pressure at kg / (cm ² · min) and calculating using the following equation. Compressibility = Δt / t × 100 t: Initial thickness of packing Further, after compressing and compressing the gland packing under the above conditions, the load is reduced to zero, and the compression recovery amount Δt
1 is a value calculated using the following formula. Compression restoring rate = Δt1 / Δt × 100 From Table 1, it is clear that the gland packing of Example 2 exhibits the same compression restoring property and flexibility as the conventional gland packing having a multi-braided structure.

Next, with respect to the gland packing of Example 2 and the gland packing of Comparative Example 1, the sealing characteristics of the packing, the packing reduction characteristics, the shaft sleeve wear characteristics, Dynamic characteristics tests such as packing retightening characteristics and sliding characteristics were performed. (1) Test device Test device main body 90, pressure load device 91, shaft drive device 92
And a control device 93 (see FIG. 4). In the test apparatus main body 90, a packing box 90a on which a gland packing is mounted is arranged on a gantry 90e, and a shaft driving is performed on a rotating shaft thereof through a bearing device 90b, a shaft torque detector 90c, and a bearing device 90d. The rotational force of the device 92 is input. The pressure loading device 91 supplies an arbitrary pressure to the gland packing mounted on the packing box 90a by supplying the fluid in the water tank 91a to the packing box 90a by the water suction pump 91b.

(2) Test method Seal characteristics Water leakage is automatically measured and accumulated in a data logger. Packing weight loss characteristics Measure the weight of the packing before and after the test and calculate the packing weight loss. Shaft sleeve wear characteristics Measure the surface roughness of the shaft sleeve before and after the test and calculate the wear amount of the shaft sleeve. Re-tightening characteristics of packing Each time the leakage exceeds 500 cc / min, the retightening adjustment is performed and the number of times is counted. Sliding characteristics The dynamic torque is measured by the shaft torque detector 90c.

(3) Test conditions Packing dimensions Inner diameter 100 mm, outer diameter 129 mm, thickness 14.5 mm Packing arrangement number 5 rows Test time 2000 hours (continuous operation) Shaft sleeve eccentricity 100 μm (200 μm TIR) Fluid type Shimizu Fluid temperature Room temperature ~ 45 ° C Fluid pressure Start-up 10kgf / cm ^2- axis rotation speed 1910rpm (shaft sleeve peripheral speed 10m / s)

The results of the above dynamic characteristic test were as follows. (1) Seal Characteristics The leakage amount over time of Example 2 and Comparative Example 1 is shown in FIGS. In Comparative Example 1, as is clear from FIG. 6, the leakage amount is large and fluctuates greatly, and therefore it is necessary to frequently perform the tightening adjustment. Also, large local wear has occurred on the sliding surface of the shaft sleeve. Furthermore, it was confirmed from the sliding trace of the packing that sealing was performed only in a narrow range. On the other hand, in Example 2, the leakage amount was small and stable as is apparent from FIG. In addition, the sliding surface of the shaft sleeve was hardly subjected to local wear, and was in a relatively uniform and favorable state. From the change in the above leakage amount,
FIG. 7 shows the seal characteristics of the packing as a change in the seal gap. The above-mentioned seal gap is calculated from the following concentric gap leak equation. Q = πDh ³ ΔP / 12ηa Q: Leakage amount (cm ³ / sec) D: Diameter of shaft sleeve (cm) h: Seal gap (cm) ΔP: Pressure difference (kgf / cm ² ) η: Fluid viscosity (kgf) -Sec / cm < ² >) a: Seal length (cm) From FIG. 7, the seal gap of Example 2 is about 1 / compared with Comparative Example 1.
It is clear that the change was small and the change was stable. Also, the shaft runout (shaft sleeve eccentricity) is 100
Since it is the test data in the case of μm, it can be seen that Example 2 is superior to Comparative Example 1 in the followability to shaft runout.

(2) Packing weight reduction characteristics The weight reduction rates of Example 2 and Comparative Example 1 over time are shown in FIG. As is clear from the figure, in both Example 2 and Comparative Example 1, 6 to 7 were obtained within 200 hours from the start of operation.
Although a weight loss of% by weight occurred, the weight loss thereafter was very small. Further, it is considered that the decrease in weight was due not to abrasion of the base fiber of the packing but to an outflow of oil contained in the packing, and no abrasion of the packing base material affecting the life was observed.

(3) Shaft Sleeve Wear Characteristics FIG. 9 shows the wear characteristics of the shaft sleeve due to sliding contact with the packing in relation to the test time and the maximum wear depth of the shaft sleeve. As is clear from the figure, in both cases, the amount of wear of the sleeve itself is extremely small, but in the case of Comparative Example 1, the sleeve wears at a considerable rate in proportion to the operating time. In No. 2, the wear rate is smaller than the running time.
Therefore, in the evaluation of the life, Example 2 is superior to Comparative Example 1.

(4) Packing Retightening Characteristics The average number of times of packing retightening when the packing was replaced every 2000 hours and the operation test was performed three times was as shown in Example 2.
Was 2 times, while Comparative Example 1 was 10 times. Further, the retightening rate of the packing is obtained by the following equation, and the result is shown in FIG. ε = ΔL / L × 100 ε: Retightening ratio (%) ΔL: Retightening amount (mm) L: Total height of packing when mounted (mm) As seen from FIG. Regarding the evaluation of life, Example 2 is superior to Comparative Example 1, and it is considered that Example 2 has about 3 times as long life as Comparative Example 1.

(5) Sliding Characteristics The average dynamic torque of Example 2 was 14.8 kg in the case where the packing was replaced every 2000 hours and the running test was performed three times.
f · cm, whereas Comparative Example 1 had 19.0 kg
It was f · cm. From this result, it is clear that Example 2 has better sliding characteristics than Comparative Example 1. From this result, it is possible to easily predict that the life of the second embodiment is prolonged.

The results of the evaluation of the above-mentioned dynamic characteristic tests are summarized in Table 2. In Table 2, "◎"
The evaluation was made on a four-point scale of “△”, “「 ”, and“ × ”, with“ ◎ ”being the highest evaluation and“ X ”being the lowest. For reference, the evaluation of Example 1 and the conventional gland packing (Comparative Examples 2 and 3) is also described. In Comparative Example 2, a plurality of knitting yarns 60 in which carbonized fibers are impregnated with a filling material made of PTFE fine particles are lattice-knitted with four paths,
A filling material 6 made of PTFE fine particles on the surface layer 61.
2 has a single braided structure (see FIG. 12). Further, in Comparative Example 3, the surface coating layer 7 made of a circular braid was formed around a core 71 made of a square braided carbon fiber knitting yarn.
2 and the surface coating layer 72
Is obtained by knitting a knitting yarn in which a carbon fiber is impregnated with a filler material made of PTFE fine particles, and then weaving the surface layer thereof again with a filler material 73 made of PTFE fine particles. 13).

[0028]

[Table 2]

The gland packing of the present invention is not limited to the above embodiment, and various design changes can be made, for example, by increasing or decreasing the number of knitting yarns 1a.

[0030]

As described above, according to the gland packing of the present invention, good compression and restoring properties can be exhibited, so that the volume of the gland packing decreases with the outflow of the plugging material. It can be suppressed effectively. In addition, the packing material with which the surface layer of the surface coating layer is impregnated with high density ensures good sealing and lubricity, and even if the packing material wears, the elastic recovery of the core is achieved. By the action, it is possible to suppress the generation of a gap on the sealing surface. Furthermore, since the surface coating layer has a lattice knit structure of a dense stitch, good contact with the shaft can be ensured, and even when the knitting yarn is cut by sliding contact with the shaft, the braided structure can be formed. Destruction can be prevented. Therefore, a good sealing property can be secured for a long period of time. In particular, when the surface layer of each of the core and the surface coating layer is impregnated with 5 to 40% by weight of a plugging material, lubricity, flexibility, flexibility, and compression recovery suitable as packing are obtained. As a result, it is possible to ensure a good sealing property over a longer period of time, thereby producing a unique effect.

[Brief description of drawings]

FIG. 1 is a perspective view of an essential part showing an embodiment of a gland packing of the present invention.

FIG. 2 is a perspective view of a main part of a core.

FIG. 3 is a perspective view of a main part showing another embodiment.

FIG. 4 is a schematic diagram of a test apparatus.

FIG. 5 is a graph showing the amount of leakage in the example.

FIG. 6 is a graph showing a leakage amount of a comparative example.

FIG. 7 is a graph showing a change in a seal gap.

FIG. 8 is a graph showing a weight reduction rate of packing.

FIG. 9 is a graph showing a wear amount of a shaft sleeve.

FIG. 10 is a graph showing a retightening rate of a packing.

FIG. 11 is a perspective view of a main part of Comparative Example 1.

12 is a perspective view of a main part of Comparative Example 2. FIG.

FIG. 13 is a perspective view of a main part of Comparative Example 3.

[Explanation of symbols]

 1 Core 1a Knitting yarn 11 Surface layer 12 Inner layer 2 Surface coating layer 21 Surface layer 22 Inner layer

 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Hiroyuki Shinokura Inventor Hiroyuki Shinokura 1 at 541, Shimuchi Shinji, Uchiba, Mita-shi, Hyogo Japan Pillar Industry Co., Ltd. Mita factory

Claims (2)

[Claims] 1. A string-shaped gland packing formed by braiding a number of knitting yarns made of carbonized fiber, wherein a center core of a square knitting structure is arranged at a center portion of a cross section, and a periphery of the center core is a lattice knitting structure. A gland packing, characterized in that the surface layer of the core and the surface layer is impregnated with a filler at a higher density than the inner layer. . 2. The gland packing according to claim 1, wherein the surface layer of each of the core and the surface coating layer is impregnated with a plugging material in an amount of 5 to 40% by weight.