JPH0813397A - Wallpaper and its production - Google Patents
Wallpaper and its productionInfo
- Publication number
- JPH0813397A JPH0813397A JP6149945A JP14994594A JPH0813397A JP H0813397 A JPH0813397 A JP H0813397A JP 6149945 A JP6149945 A JP 6149945A JP 14994594 A JP14994594 A JP 14994594A JP H0813397 A JPH0813397 A JP H0813397A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- wallpaper
- vinyl chloride
- foaming agent
- foamed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、一般住宅、店舗、オフ
ィス等に使用される内装用の壁紙に関し、詳しくは、壁
紙表面に合成樹脂フィルムをラミネートして、汚れ防止
機能を付与した壁紙とその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a wallpaper for interiors used in general houses, shops, offices, etc., and more specifically, a wallpaper with a synthetic resin film laminated on the surface of the wallpaper to impart a stain prevention function. The manufacturing method is related.
【０００２】[0002]
【従来の技術】一般的に壁紙は、紙特有の風合がある紙
壁紙、エンボス加工がしやすく、発泡性、耐水性の加工
が容易な塩ビ壁紙、柔らかさ本物の風合を有するクロス
壁紙、その他、自然の素材（コルク、竹等）を生かした
特殊壁紙、の４つに分類される。特に、塩ビ壁紙は豊富
な表現が可能で、かつ、耐久性、施工性、生産性の面で
優れていることから壁紙の主流として多く使用されてい
る。2. Description of the Related Art Generally, wallpaper is a paper wallpaper that has a texture unique to paper, a PVC wallpaper that is easy to emboss, is easy to foam and has water resistance, and is a cross wallpaper that has a soft texture. , And other special wallpapers that make use of natural materials (cork, bamboo, etc.). In particular, PVC wallpaper is widely used as a mainstream wallpaper because it can be used in a variety of expressions and is excellent in durability, workability, and productivity.
【０００３】一例を挙げるならば、図２に示す如く、裏
打紙（３１）に塩化ビニル樹脂をコーティングして層
（３２）を形成するか又は塩化ビニルシート（３２）を
ラミネートして、この上にグラビア印刷による絵柄層
（３３）を設け、この上に発泡量の大きいＡＤＣＡ（ア
ゾ−ジ−カルボン−アミド）系の発泡剤を配合した塩ビ
ペーストをスクリーン印刷等により設け層（３４）を形
成して、加熱、発泡させて凹凸模様を形成したものであ
る。さらに図示はしないが、この上からさらにエンボス
加工による凹凸模様を形成し、一層の立体感や風合の表
現をした壁紙が公知である。As an example, as shown in FIG. 2, a backing paper (31) is coated with a vinyl chloride resin to form a layer (32), or a vinyl chloride sheet (32) is laminated on the backing paper (31). A pattern layer (33) is formed by gravure printing, and a vinyl chloride paste containing an ADCA (azo-di-carbon-amide) -based foaming agent having a large foaming amount is provided thereon by screen printing or the like to form a layer (34). Then, it is heated and foamed to form an uneven pattern. Although not shown in the drawing, a wallpaper is known in which an embossed pattern is further formed on the wallpaper to provide a more three-dimensional effect and texture.
【０００４】しかし、加熱、発泡させてスポンジ状の塩
ビペースト層（３４）を形成した壁紙は、表面が汚れや
すく、しかも擦れ等に対しての表面強度が弱い欠点があ
る。このために通常は、汚れ防止機能、表面強度の向上
を付与する対策がとられている。一つは、この壁紙の表
面に樹脂フィルムをラミネートすることで、耐汚染性と
耐磨耗性を付与するものである。もう一つは、同様に表
面にグラビア印刷による樹脂コーティング処理を行う方
法である。However, the wallpaper formed by heating and foaming to form the sponge-like vinyl chloride paste layer (34) has the drawback that the surface is easily soiled and the surface strength against rubbing is weak. For this reason, measures are usually taken to impart an antifouling function and improve the surface strength. One is to impart stain resistance and abrasion resistance by laminating a resin film on the surface of this wallpaper. The other is a method of similarly performing resin coating treatment by gravure printing on the surface.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、前述し
た表面に樹脂フィルムをラミネートする方法において、
ラミネートする際の加熱、加圧により、スポンジ状の塩
ビペースト層（３４）が潰れてしまい、この層（３４）
によるレリーフ状の凹凸模様効果が半減してしまう。こ
のため、壁紙の表面にはメカニカルエンボス加工の凹凸
模様を形成した場合のみ、ラミネートすることが可能で
あった。一方、樹脂コーティング処理の場合には、発泡
剤を発泡させた層は勿論、ケミカルエンボス（発泡抑制
インキによる凹凸模様）等の発泡工程を必要とする壁紙
にも対応することができるが、耐溶剤性、耐薬品性、耐
磨耗性等の物性的機能は前者よりも著しく劣る問題があ
った。However, in the method of laminating a resin film on the above-mentioned surface,
The sponge-like PVC paste layer (34) is crushed by the heat and pressure applied during lamination, and this layer (34)
The relief-like uneven pattern effect due to is halved. Therefore, it was possible to laminate the wallpaper only when the uneven pattern of mechanical embossing was formed on the surface of the wallpaper. On the other hand, in the case of resin coating treatment, it can be applied not only to the layer in which the foaming agent is foamed, but also to wallpaper that requires a foaming process such as chemical embossing (uneven pattern with foaming suppression ink) There is a problem that physical properties such as resistance, chemical resistance and abrasion resistance are remarkably inferior to the former.
【０００６】そこで本発明は、発泡工程を必要とする壁
紙で、しかも汚れ防止機能、耐磨耗性等の表面強度を向
上させるため、表面に合成樹脂フィルムのラミネート加
工を行っても、発泡した塩ビペーストによる凹凸模様を
維持することができる壁紙とその製造方法を提供するこ
とを目的とする。Therefore, the present invention is a wallpaper that requires a foaming process, and in order to improve the surface strength such as stain prevention function and abrasion resistance, it is foamed even if a synthetic resin film is laminated on the surface. An object of the present invention is to provide a wallpaper that can maintain an uneven pattern due to a PVC paste and a method for manufacturing the wallpaper.
【０００７】[0007]
【課題を解決するための手段】上記の目的を達成するた
め、第１の発明によれば、裏打紙等の基材（１１）上
に、塩化ビニル樹脂層（１２）を設け、この上に、絵柄
層（１３）とカプセル発泡剤を配合した塩ビペースト層
（１４）を設け、該塩ビペースト層（１４）を発泡させ
た後、全面に合成樹脂フィルム（１５）でラミネートし
たことを特徴とする壁紙である。To achieve the above object, according to the first invention, a vinyl chloride resin layer (12) is provided on a base material (11) such as a backing paper, and a vinyl chloride resin layer (12) is provided thereon. A vinyl chloride paste layer (14) containing a pattern layer (13) and a capsule foaming agent is provided, the vinyl chloride paste layer (14) is foamed, and then laminated on the entire surface with a synthetic resin film (15). It is a wallpaper.
【０００８】また、第２の発明によれば、前記塩化ビニ
ル樹脂層（１２）にカプセル発泡剤を配合し、加熱、発
泡してなることを特徴とするものである。According to a second aspect of the invention, the vinyl chloride resin layer (12) is characterized in that a capsule foaming agent is blended and heated and foamed.
【０００９】さらに第３の発明によれば、裏打紙等の基
材（１１）上に、カプセル発泡剤を配合してなる塩化ビ
ニル樹脂層（１２）を形成し、該塩化ビニル樹脂層（１
２）を加熱、発泡させ、この上に絵柄層（１３）とカプ
セル発泡剤を配合してなる塩化ビペースト層（１４）を
絵柄状に形成し、前記塩ビペースト層（１４）を加熱、
発泡させた後、この発泡させた塩ビペースト層（１４）
上に、合成樹脂フィルム（１５）をラミネートしてなる
ことを特徴とする壁紙の製造方法である。Further, according to the third invention, a vinyl chloride resin layer (12) containing a capsule foaming agent is formed on a substrate (11) such as a backing paper, and the vinyl chloride resin layer (1) is formed.
2) is heated and foamed, and a vinyl chloride paste layer (14) obtained by blending a pattern layer (13) and a capsule foaming agent is formed in a pattern thereon, and the vinyl chloride paste layer (14) is heated,
After foaming, this foamed PVC paste layer (14)
A method for producing wallpaper, which comprises laminating a synthetic resin film (15) on the top.
【００１０】[0010]
【作用】本発明の壁紙は、少なくともカプセル発泡剤を
配合した塩化ビニル樹脂層（１２）と、塩ビペースト層
（１４）を加熱、発泡させた後、この上を被覆するよう
に合成樹脂フィルム（１５）をラミネートすることによ
り、壁紙の表面に汚れ防止機能と耐磨耗性等の表面強度
を付与するものである。従来、発泡量の大きいＡＤＣＡ
（アゾ−ジ−カルボン−アミド）系等の発泡剤を使用し
て凹凸模様を形成していたが、汚れ防止機能を付与する
ために、この上に合成樹脂フィルムをラミネートする
と、加熱、加圧によりスポンジ状の塩ビペースト層に
「へたり」が発生し、凹凸模様が縮んでしまうので、表
面のラミネート加工を行うことができなかった。これに
対して、本発明に係わるカプセル発泡剤は、熱によりガ
スを発生して膨らむのではなく、加熱することによりカ
プセル発泡剤本体が膨張し体積を増すことで膨らみを出
すもので、合成樹脂フィルム（１５）をラミネートして
も「へたり」の度合が僅かで、汚れ防止機能や表面強度
を付与することができる。In the wallpaper of the present invention, the vinyl chloride resin layer (12) containing at least the capsule foaming agent and the vinyl chloride paste layer (14) are heated and foamed, and then the synthetic resin film (covering the upper layer) By laminating 15), the surface of the wallpaper is provided with a stain preventing function and a surface strength such as abrasion resistance. Conventionally, a large amount of foaming ADCA
Although a concavo-convex pattern was formed using a foaming agent such as (azo-di-carvone-amide) type, when a synthetic resin film is laminated on this to impart a stain prevention function, heating and pressing are performed. As a result, “sagging” occurs in the sponge-like PVC paste layer and the uneven pattern shrinks, so that the surface cannot be laminated. On the other hand, the capsule foaming agent according to the present invention does not swell by generating gas due to heat, but causes swelling by expanding the volume of the capsule foaming agent body by heating and increasing the volume. Even if the film (15) is laminated, the degree of “fatigue” is slight, and a stain preventing function and surface strength can be imparted.
【００１１】[0011]
【実施例】以下、本発明に係わる実施例を図に基づき詳
細に説明する。図１は、本発明の壁紙の積層構成の一例
を示す断面図である。Embodiments of the present invention will be described in detail below with reference to the drawings. FIG. 1 is a cross-sectional view showing an example of the laminated structure of the wallpaper of the present invention.
【００１２】本発明の壁紙は図１に示す如く、原紙、難
燃紙等の裏打紙による基材（１１）上に、塩化ビニル樹
脂を処理して層（１２）を形成する。この塩化ビニル樹
脂層（１２）は、一例を示すならば下記に示す組成によ
り形成されている。 〔組成〕 塩化ビニル樹脂 １００重量部 可塑剤 ６０〃 安定剤 ３〃 充填剤（炭酸カルシューム） ５０〃 着色剤（白） ３０〃 これは白ベースの組成であり、着色については着色剤を
加えても基材の色を隠蔽する。この組成からなる塩化ビ
ニル樹脂を処理（塗布、乾燥）、又は塩化ビニルシート
をラミネートして層（１２）を形成する。なお、塩化ビ
ニル樹脂層（１２）の形成は、上記の組成に限定するも
のではなく、この組成に加えてカプセル発泡剤を５〜１
０重量部配合した組成とすることが望ましい。この場合
は塗布と同時に、加熱、発泡させることで塩化ビニル樹
脂層（１２）が厚みを増し、壁紙の施工性の一つである
腰の強さが向上する。As shown in FIG. 1, the wallpaper of the present invention comprises a base material (11) made of a backing paper such as base paper or flame-retardant paper, which is treated with vinyl chloride resin to form a layer (12). The vinyl chloride resin layer (12) is formed by the following composition, as an example. [Composition] Vinyl chloride resin 100 parts by weight Plasticizer 60 〃 Stabilizer 3 〃 Filler (calcium carbonate) 50 〃 Colorant (white) 30 〃 This is a white-based composition, even if a colorant is added for coloring Hide the color of the substrate. A layer (12) is formed by treating (coating and drying) a vinyl chloride resin having this composition or laminating a vinyl chloride sheet. The formation of the vinyl chloride resin layer (12) is not limited to the above composition, and 5 to 1 of the capsule foaming agent is added to this composition.
It is desirable that the composition is 0 part by weight. In this case, the thickness of the vinyl chloride resin layer (12) is increased by heating and foaming at the same time as application, and the strength of the waist, which is one of the workability of wallpaper, is improved.
【００１３】次に、この発泡された塩化ビニル樹脂層
（１２）上に、グラビア印刷方式により複数色からなる
絵柄層（１３）を形成する。さらにこの上に、チタンホ
ワイトやカプセル発泡剤等を配合し、グラビア印刷方式
により塩ビペーストを絵柄状に印刷して層（１４）を形
成するとともに、加熱、発泡させるものである。この際
の塩ビペースト組成の一例を下記に示す。 〔組成〕 塩化ビニル樹脂 １００重量部 可塑剤（ジオクチルフタレート） ５０〃 安定剤 ２〃 充填剤（炭酸カルシューム） ５０〃 カプセル発泡剤 １０〃 隠蔽剤（チタンホワイト） １０〃 希釈剤 適宜Next, a pattern layer (13) of a plurality of colors is formed on the foamed vinyl chloride resin layer (12) by a gravure printing method. Further, titanium white, a capsule foaming agent, or the like is further mixed on this, and a vinyl chloride paste is printed in a pattern by a gravure printing method to form a layer (14), and the layer is heated and foamed. An example of the vinyl chloride paste composition at this time is shown below. [Composition] Vinyl chloride resin 100 parts by weight Plasticizer (dioctyl phthalate) 50〃 Stabilizer 2〃 Filler (calcium carbonate) 50〃 Capsule foaming agent 10〃 Concealing agent (titanium white) 10〃 Diluent Appropriately
【００１４】この塩ビペースト層（１４）と、前述した
塩化ビニル樹脂層（１２）に配合するカプセル発泡剤
は、カプセルの外側は熱可塑性樹脂による中空の粒子
で、この中空部分に揮発性物質（例えば、イソブタン等
の揮発性炭化水素）が封入されているもので、また、カ
プセルを形成する熱可塑性樹脂には、塩化ビニリデン−
アクリルニトリル共重合体等を使用することができる。
このカプセルの粒径としては、５〜２０μｍものが好ま
しい。このカプセル発泡剤は、１２０〜１４０℃程度の
加熱をすることで封入されている揮発物質がカプセル内
で揮発して、カプセルを膨潤させることで体積が増加し
て発泡状態を形成する。既に市販されているものとし
て、松本油脂製薬（株）製の「マツモトマイクロスフェ
アーＦ−４０Ｄ」、エクスパンセル社製の「エクスパン
セルＤｕ−４６２」等がある。なお、本実施例において
は「マツモトマイクロスフェアーＦ−４０Ｄ」を使用し
た。The capsule foaming agent blended in the vinyl chloride paste layer (14) and the vinyl chloride resin layer (12) described above is a hollow particle made of a thermoplastic resin on the outside of the capsule, and a volatile substance ( For example, volatile hydrocarbons such as isobutane) are encapsulated, and the thermoplastic resin forming the capsule is vinylidene chloride-
Acrylonitrile copolymer etc. can be used.
The capsule preferably has a particle size of 5 to 20 μm. When the capsule foaming agent is heated at about 120 to 140 ° C., the encapsulated volatile substance volatilizes inside the capsule and swells the capsule to increase the volume and form a foamed state. As commercially available products, there are "Matsumoto Microsphere F-40D" manufactured by Matsumoto Yushi-Seiyaku Co., Ltd. and "Expansel Du-462" manufactured by Expancel. In this example, "Matsumoto Microsphere F-40D" was used.
【００１５】次に、発泡させた塩化ビペースト層（１
４）上に、合成樹脂フィルム（１５）をラミネートす
る。これは汚れ防止機能や耐磨耗性等の表面強度を付与
するためで、合成樹脂フィルム（１５）としては限定す
るものではないが、好ましくは、エチレン酢酸ビニルア
ルコール共重合樹脂フィルムがよい。なお、この合成樹
脂フィルム（１５）のラミネートはドライラミネーショ
ン方式がよく、温度１２０〜１５０℃、圧力３〜７ｋｇ
／ｃｍで行った。Next, the foamed vinyl chloride paste layer (1
4) Laminate a synthetic resin film (15) on it. This is because it imparts a surface strength such as a stain prevention function and abrasion resistance, and the synthetic resin film (15) is not limited, but an ethylene vinyl acetate alcohol copolymer resin film is preferable. The synthetic resin film (15) is preferably laminated by a dry lamination method at a temperature of 120 to 150 ° C. and a pressure of 3 to 7 kg.
/ Cm.
【００１６】以上の条件でラミネートしたが、発泡させ
た塩ビペースト層（１４）と塩化ビニル樹脂層（１２）
は、若干の潰れは見られたが発泡した状態を残し、ラミ
ネートした合成樹脂フィルム（１５）の表面は平滑面に
ならずに、下層の凹凸模様と同調した凹凸が形成され
る。以上により汚れ防止機能、表面強度を付与するため
の合成樹脂フィルム（１５）をラミネートすることが可
能となった。Laminated under the above conditions, the foamed vinyl chloride paste layer (14) and vinyl chloride resin layer (12)
Although some crushing was observed, the foamed state remained, and the surface of the laminated synthetic resin film (15) did not become a smooth surface, and irregularities were formed in synchronization with the irregular pattern of the lower layer. As described above, it becomes possible to laminate the synthetic resin film (15) for imparting the stain prevention function and the surface strength.
【００１７】[0017]
【発明の効果】以上の構成により、本発明の壁紙は、カ
プセル発泡剤を配合した塩化ビニル樹脂層、絵柄状の塩
ビペースト層を加熱、発泡させた後、この上を被覆する
ように合成樹脂フィルムをラミネートすることにより、
壁紙の表面に汚れ防止機能と表面強度が向上するととも
に、耐溶剤性、耐薬品性等の物性面においても耐久性を
有する壁紙が得られる。これにより従来、発泡量の大き
い発泡剤を使用して凹凸模様等の意匠性を得ていたが、
汚れ防止機能等を付与するために、合成樹脂フィルムを
ラミネートする際の、加熱、加圧によりスポンジ状の塩
ビペースト層に「へたり」が発生し、発泡した塩ビペー
スト層による凹凸模様が縮んでしまうので、表面のラミ
ネート加工を行うことが不可能で、凹凸模様はエンボス
仕上げしかできなかった。これに対して、カプセル発泡
剤は、ガスを発生させて膨らむのではなく、熱によりカ
プセル発泡剤本体が膨張し体積を増すことにより脹らみ
を出すもので、合成樹脂フィルムをラミネートしても
「へたり」の度合が僅かので、汚れ防止機能等を付与す
ることができるとともに、柔らかな風合の意匠性が得ら
れる優れた壁紙となる。EFFECTS OF THE INVENTION With the above-mentioned constitution, the wallpaper of the present invention is made of synthetic resin so that the vinyl chloride resin layer containing the capsule foaming agent and the polyvinyl chloride paste layer in the form of a pattern are heated and foamed, and then coated thereon. By laminating the film,
It is possible to obtain a wallpaper having not only a stain prevention function and a surface strength improved on the surface of the wallpaper, but also durability in terms of physical properties such as solvent resistance and chemical resistance. Due to this, conventionally, a foaming agent with a large foaming amount was used to obtain design characteristics such as an uneven pattern,
In order to impart a stain prevention function, etc., when the synthetic resin film is laminated, "fatigue" occurs in the sponge-like PVC paste layer due to heat and pressure, and the uneven pattern due to the foamed PVC paste layer shrinks. Therefore, the surface cannot be laminated, and the uneven pattern can only be embossed. On the other hand, the capsule foaming agent does not swell by generating gas, but expands by increasing the volume of the capsule foaming agent main body by heat and expanding the volume, even if a synthetic resin film is laminated. Since the degree of "fatigue" is slight, it becomes an excellent wallpaper that can be provided with a stain-preventing function and the like, and can also be designed with a soft texture.
【図１】本発明の壁紙の積層構成の一例を示す断面図で
ある。FIG. 1 is a cross-sectional view showing an example of a laminated structure of a wallpaper of the present invention.
【図２】従来の壁紙の積層構成の一例を示す断面図であ
る。FIG. 2 is a cross-sectional view showing an example of a laminated structure of a conventional wallpaper.
１１，３１…基材 １２，３２…塩化ビニル樹脂層 １３，３３…絵柄層 １４，３４…塩ビペースト層 １５ …合成樹脂フィルム 11, 31 ... Base material 12, 32 ... Vinyl chloride resin layer 13, 33 ... Picture layer 14, 34 ... PVC paste layer 15 ... Synthetic resin film
Claims (3)
樹脂層（１２）を設け、この上に、絵柄層（１３）とカ
プセル発泡剤を配合した塩ビペースト層（１４）を設
け、該塩ビペースト層（１４）を発泡させた後、全面に
合成樹脂フィルム（１５）でラミネートしたことを特徴
とする壁紙。1. A vinyl chloride resin layer (12) is provided on a substrate (11) such as a backing paper, and a vinyl chloride paste layer (14) containing a pattern layer (13) and a capsule foaming agent is provided thereon. A wallpaper, which is provided, foams the vinyl chloride paste layer (14), and is then laminated with a synthetic resin film (15) on the entire surface.
ル発泡剤を配合し、加熱、発泡させたことを特徴とする
請求項１に記載の壁紙。2. The wallpaper according to claim 1, wherein the vinyl chloride resin layer (12) is mixed with a capsule foaming agent and heated to foam.
泡剤を配合してなる塩化ビニル樹脂層（１２）を形成
し、該塩化ビニル樹脂層（１２）を加熱、発泡させ、こ
の上に絵柄層（１３）とカプセル発泡剤を配合してなる
塩ビペースト層（１４）を絵柄状に形成し、前記塩ビペ
ースト層（１４）を加熱、発泡させた後、この発泡させ
た塩ビペースト層（１４）上に、合成樹脂フィルム（１
５）をラミネートしてなることを特徴とする壁紙の製造
方法。3. A vinyl chloride resin layer (12) formed by blending a capsule foaming agent on a base material (11) such as backing paper, and the vinyl chloride resin layer (12) is heated to foam. A vinyl chloride paste layer (14) formed by blending a pattern layer (13) and a capsule foaming agent is formed thereon in a pattern, and the vinyl chloride paste layer (14) is heated and foamed. On the paste layer (14), the synthetic resin film (1
A method for producing wallpaper, which comprises laminating 5).