JPH0798922B2 - White α-cyanoacrylate adhesive composition - Google Patents
White α-cyanoacrylate adhesive compositionInfo
- Publication number
- JPH0798922B2 JPH0798922B2 JP15741188A JP15741188A JPH0798922B2 JP H0798922 B2 JPH0798922 B2 JP H0798922B2 JP 15741188 A JP15741188 A JP 15741188A JP 15741188 A JP15741188 A JP 15741188A JP H0798922 B2 JPH0798922 B2 JP H0798922B2
- Authority
- JP
- Japan
- Prior art keywords
- cyanoacrylate
- white
- weight
- parts
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 （イ）産業上の利用分野 本発明は瞬間接着剤として有用なα−シアノアクリレー
ト接着剤組成物に関し、さらに詳しくは白色のα−シア
ノアクリレート接着剤組成物に関する。DETAILED DESCRIPTION OF THE INVENTION (a) Field of Industrial Application The present invention relates to an α-cyanoacrylate adhesive composition useful as an instant adhesive, and more particularly to a white α-cyanoacrylate adhesive composition.
（ロ）従来の技術 一般式 （式中Ｒは炭素数16以下のアルキル、アルケニル、アラ
ルキル、アルコキシアルキル、ハロアルキル、シクロヘ
キシル、フェニル等）で示されるα−シアノアクリレー
トは極めてアニオン重合を起し易く固体表面や空気中の
水分、アルカリ物質等のアニオン活性種により触媒の添
加や加熱を行なう事なく短時間で重合硬化する性質を有
するので、ゴム、プラスチックス、金属、ガラス等の接
着に瞬間接着剤として広く利用されている。(B) Conventional technology General formula (Wherein R is an alkyl, alkenyl, aralkyl, alkoxyalkyl, haloalkyl, cyclohexyl, phenyl etc. having 16 or less carbon atoms) α-cyanoacrylate is extremely prone to anionic polymerization, and solid surface or water in the air, alkali It has a property of being polymerized and cured by an anion active species such as a substance in a short time without adding a catalyst or heating, so that it is widely used as an instant adhesive for adhesion of rubber, plastics, metal, glass and the like.
α−シアノアクリレートは一般に透明な、高い剪断強度
の接着剤であり、その透明の故にほとんどの適用に極め
て好都合である。しかしながら、ある場合には白色の接
着ラインを生じる材料が要求される。例えば、黒色又は
暗色の表面上に透明な又は透明に着色されたα−シアノ
アクリレート接着剤を塗布した場合、塗布されているか
否かの確認が困難である。又、装飾用の白色板の接着に
透明のα−シアノアクリレート接着剤を用いるとその接
着境界部が目立ち不都合な場合がある。これらの場合、
白色α−シアノアクリレート接着剤があれば、塗布の確
認が容易になり、又、接着境界部も白色となり接着の痕
跡が残らず好都合である。α−シアノアクリレートを白
色にする方法としては白色顔料、例えばアルミナ（US 3
663501）や酸化チタン、炭酸カルシウム（US 3607542）
を添加する方法、可塑剤や溶剤を添加して乳白色にする
方法（特開昭62−232474）、ポリフッ化ビニリデン粉末
を添加してチクソ性をもつ白色ペーストにする方法（特
開昭53−30642）等が知られている。Alpha-cyanoacrylates are generally transparent, high shear strength adhesives, and their transparency makes them very convenient for most applications. However, in some cases a material that produces a white bond line is required. For example, when a transparent or transparently colored α-cyanoacrylate adhesive is applied on a black or dark surface, it is difficult to confirm whether or not it is applied. Further, if a transparent α-cyanoacrylate adhesive is used for adhering a white plate for decoration, the adhering boundary portion may be noticeably inconvenient. In these cases,
If there is a white α-cyanoacrylate adhesive, the application can be easily confirmed, and the adhesive boundary portion becomes white, which is convenient because no adhesive trace remains. A white pigment such as alumina (US 3
663501), titanium oxide, calcium carbonate (US 3607542)
, A method of adding a plasticizer or a solvent to give a milky white color (JP-A-62-232474), and a method of adding polyvinylidene fluoride powder to give a white paste having thixotropy (JP-A-53-30642). ) Etc. are known.
（ハ）発明が解決しようとする課題 白色顔料、例えばアルミナを使用する方法や酸化チタ
ン、炭酸カルシウムを使用する方法は、これらの材料が
α−シアノアクリレートにとって強力な活性剤であり、
保存安定性が悪くなる。可塑剤を添加して硬化後乳白に
する方法はいんぺい性のない半透明の硬化物ゆえに効果
が低く使用範囲が限定される。α−シアノアクリレート
100部にポリフッ化ビニリデン粉末を60部程度混合した
時、チクソ性をもつ白色ペーストができることが教示さ
れているが、この場合、α−シアノアクリレートの接着
性が極度に低下するため接着剤として不都合である。(C) Problems to be Solved by the Invention White pigments, for example, a method using alumina, a method using titanium oxide, calcium carbonate, these materials are strong activators for α-cyanoacrylate,
Storage stability becomes poor. The method of adding a plasticizer to give an opalescence after curing has a low effect due to a semitransparent cured product having no opacity and its use range is limited. α-cyanoacrylate
It is taught that a white paste having thixotropy can be formed when about 60 parts of polyvinylidene fluoride powder is mixed with 100 parts, but in this case, the adhesiveness of α-cyanoacrylate is extremely reduced, which is not suitable as an adhesive. Is.
（ニ）課題を解決するための手段 本発明者らは前述の欠点を解決し、保存安定性がよく、
いんぺい性があり、且つ接着力も十分に保持した白色の
α−シアノアクリレート接着剤について鋭意検討し、本
発明を完成した。本発明は （１）α−シアノアクリレートに、該α−シアノアクリ
レート100重量部に対し、重合度200−20000のポリ塩化
ビニル粉末を５−40重量部及び増粘剤を添加し、粘度を
1000〜100000CPとしたことを特徴とする白色α−シアノ
アクリレート接着剤組成物。(D) Means for Solving the Problems The present inventors have solved the above-mentioned drawbacks and have good storage stability,
The present invention has been completed by earnestly investigating a white α-cyanoacrylate adhesive having a high resistance and a sufficient adhesive force. The present invention includes (1) 5-40 parts by weight of polyvinyl chloride powder having a degree of polymerization of 200-20000 and a thickening agent are added to 100 parts by weight of the α-cyanoacrylate, and a viscosity improver is added.
A white α-cyanoacrylate adhesive composition characterized by having a viscosity of 1,000 to 100,000 CP.
（２）α−シアノアクリレートに、該α−シアノアクリ
レート100重量部に対し、重合度200−20000のポリ塩化
ビニル粉末を５−40重量部及びチクソトロピック剤を添
加し、粘度を1000〜100000CPとしたことを特徴とする白
色α−シアノアクリレート接着剤組成物。(2) To α-cyanoacrylate, 5-40 parts by weight of polyvinyl chloride powder having a degree of polymerization of 200-20000 and a thixotropic agent are added to 100 parts by weight of the α-cyanoacrylate, and the viscosity is adjusted to 1000 to 100000 CP. A white α-cyanoacrylate adhesive composition characterized in that.
（３）α−シアノアクリレートに、該α−シアノアクリ
レート100重量部に対し、重合度200−20000のポリ塩化
ビニル粉末を５−40重量部及び増粘剤及びチクソトロピ
ック剤を添加し、粘度を1000〜100000CPとしたことを特
徴とする白色α−シアノアクリレート接着剤組成物。で
ある。(3) To the α-cyanoacrylate, 5-40 parts by weight of polyvinyl chloride powder having a degree of polymerization of 200-20000, a thickener and a thixotropic agent are added to 100 parts by weight of the α-cyanoacrylate, and the viscosity is adjusted. A white α-cyanoacrylate adhesive composition characterized by having a viscosity of 1,000 to 100,000 CP. Is.
本発明に用いられるポリ塩化ビニル粉末としては重合度
200〜20000のものを用いる。粉末の粒子径は通常0.5〜2
00ミクロンであり、１〜100ミクロンのものが好まし
い。ポリ塩化ビニル粉末の添加量はα−シアノアクリレ
ート100重量部に対し５〜40重量部がよく、好ましくは1
0〜40重量部である。又、増粘剤、チクソトロピック剤
は夫々単独で又は混合して用いることができる。増粘剤
やチクソトロピック剤の添加は、長期保存した時、ポリ
塩化ビニル粉末の浮遊や沈降が起こりにくく、均一な組
成物を維持するのに効果がある。接着剤組成物の粘度は
1000〜10万cpである。この場合の粘度はJIS・K6838に準
じて測定を行い、チクソトロピックな組成物の場合ロー
タを高速回転で駆動させたときの粘度を組成物の粘度と
する。増粘剤としては例えばポリメチルメタアクリレー
ト、ポリα−シアノアクリレート及びセルロースエステ
ル等であり、チクソトロピック剤としてはフュームドシ
リカが使用される。本発明で用いられるα−シアノアク
リレートとしては例えばメチル−α−シアノアクリレー
ト、エチル−α−シアノアクリレート、プロピル−α−
シアノアクリレート、ブチル−α−シアノアクリレー
ト、アリル−α−シアノアクリレート、２−メトキシエ
チル−α−シアノアクリレート、２−エトキシエチル−
α−シアノアクリレート、２−クロロエチル−α−シア
ノアクリレート、シクロヘキシル−α−シアノアクリレ
ート等である。The degree of polymerization of the polyvinyl chloride powder used in the present invention is
Use the one of 200 to 20000. Particle size of powder is usually 0.5-2
It is 00 microns, preferably 1 to 100 microns. The amount of polyvinyl chloride powder added is preferably 5 to 40 parts by weight, preferably 1 to 100 parts by weight of α-cyanoacrylate.
It is 0 to 40 parts by weight. Further, the thickener and the thixotropic agent can be used alone or in combination. Addition of a thickener or a thixotropic agent is effective in maintaining a uniform composition because the polyvinyl chloride powder is unlikely to float or settle when stored for a long period of time. The viscosity of the adhesive composition is
It is 100 to 100,000 cp. The viscosity in this case is measured according to JIS K6838, and in the case of a thixotropic composition, the viscosity when the rotor is driven at high speed is the viscosity of the composition. The thickener is, for example, polymethylmethacrylate, poly α-cyanoacrylate, cellulose ester or the like, and the thixotropic agent is fumed silica. Examples of the α-cyanoacrylate used in the present invention include methyl-α-cyanoacrylate, ethyl-α-cyanoacrylate and propyl-α-.
Cyanoacrylate, butyl-α-cyanoacrylate, allyl-α-cyanoacrylate, 2-methoxyethyl-α-cyanoacrylate, 2-ethoxyethyl-
Examples include α-cyanoacrylate, 2-chloroethyl-α-cyanoacrylate, cyclohexyl-α-cyanoacrylate and the like.
α−シアノアクリレート接着剤組成物の他の添加物は、
それが接着力や白色度に不利に影響しない範囲において
添加できる。この様な添加物としては、例えば安定剤及
び着色剤であり、適する安定剤は酸化防止剤又はラジカ
ル重合防止剤、例えば二酸化イオウ、スルホン酸、ホウ
素フッ化物、ヒドロキノン、ヒドロキノンモノメチルエ
ーテル、カテコール及びピロガロール等である。これら
の添加量はα−シアノアクリレートに対して約0.0001〜
５％である。さらにDBP、DOP、TCP、トリブトキシエチ
ルホスフェート、その他各種エステル類等の軟化剤ある
いはα−シアノアクリレートと相溶性のある他のポリマ
ー等を添加併用することが出来る。本発明のα−シアノ
アクリレート接着剤組成物は重合時の体積収縮率も低下
するので、被接着体の変形あるいは剥離等の現象を防止
することが可能である。また耐水性が向上するため、耐
水性を必要とする人工大理石に適用した場合、白色化さ
れた接着剤としての効果に加え、接着性能上も有意性が
ある。Other additives of the α-cyanoacrylate adhesive composition are
It can be added as long as it does not adversely affect the adhesive strength or whiteness. Such additives are, for example, stabilizers and colorants, suitable stabilizers being antioxidants or radical polymerization inhibitors such as sulfur dioxide, sulphonic acid, boron fluorides, hydroquinone, hydroquinone monomethyl ether, catechol and pyrogallol. Etc. The addition amount of these is about 0.0001 to α-cyanoacrylate.
5%. Further, a softening agent such as DBP, DOP, TCP, tributoxyethyl phosphate and various esters, or another polymer compatible with α-cyanoacrylate can be added and used in combination. Since the volume contraction rate of the α-cyanoacrylate adhesive composition of the present invention during polymerization is also reduced, it is possible to prevent a phenomenon such as deformation or peeling of the adherend. Further, since the water resistance is improved, when it is applied to an artificial marble requiring water resistance, it has a significant effect on the adhesive performance in addition to the effect as a whitened adhesive.
（ホ）実施例 次に本発明を実施例で説明する。(E) Example Next, the present invention will be described with reference to an example.
（１）接着剤組成物の調製 実施例1,5,6 エチル−α−シアノアクリレート（田岡化学工業社製）
100重量部にSO220ppm、ハイドロキノン1000ppmを添加
し、増粘剤としてダイアナールBR−85（ポリメチルメタ
クリレート、重量平均分子量10万〜30万、三菱レーヨン
社製）10重量部を溶解した後、スミリットSX−4G（ポリ
塩化ビニル粉末、平均粒度100ミクロン、重合度約400、
住友化学工業社製）又はスミリットPX−QHH（ポリ塩化
ビニル粉末、平均粒度２ミクロン、重合度約4000、住友
化学工業社製）を表１に記載した量添加し、ディスパー
により分散させて白色均一接着剤組成物を得た。(1) Preparation of adhesive composition Example 1,5,6 Ethyl-α-cyanoacrylate (manufactured by Taoka Chemical Industry Co., Ltd.)
20 ppm SO 2 and 1000 ppm hydroquinone were added to 100 parts by weight, and 10 parts by weight of DIANAL BR-85 (polymethylmethacrylate, weight average molecular weight 100,000 to 300,000, manufactured by Mitsubishi Rayon Co., Ltd.) as a thickener was dissolved, and then Sumit SX-4G (Polyvinyl chloride powder, average particle size 100 microns, degree of polymerization about 400,
Sumitomo Chemical Co., Ltd.) or Smilit PX-QHH (polyvinyl chloride powder, average particle size 2 microns, degree of polymerization about 4000, Sumitomo Chemical Co., Ltd.) was added in an amount shown in Table 1 and dispersed by a disper to give a white uniform color. An adhesive composition was obtained.
実施例2,3,7,9,12,15 エチル−α−シアノアクリレート（前記と同じ）100重
量部にSO220ppm、ハイドロキノン1000ppmを添加し、増
粘剤としてダイアナールBR−85（前記と同じ）を表１に
記載した量溶解した後、スミリットSX−4G（前記と同
じ）、スミリットPX−QHH（前記と同じ）、スミリットE
X13（ポリ塩化ビニル粉末、平均粒度５ミクロン重合度
約1300住友化学工業社製）、スミリットPXUH（ポリ塩化
ビニル粉末平均粒度１ミクロン重合度約6000住友化学工
業社製）、又は高分子量PVC（平均粒度10ミクロン重合
度約15000のPVC粉末）を表１に記載した量添加し、ディ
スパーにより分散させ、さらに、チクソトロピック剤と
してアエロジル200（ヒュームドシリカ粉末、日本アエ
ロジル社製）を表−１に記載した量、添加しディスパー
により分散させ、白色均一な接着剤組成物を得た。Example 2,3,7,9,12,15 20 ppm of SO 2 and 1000 ppm of hydroquinone were added to 100 parts by weight of ethyl-α-cyanoacrylate (the same as above), and Dyanal BR-85 (same as above) as a thickener. ) Was dissolved in the amount shown in Table 1 and then Smilit SX-4G (same as above), Smilit PX-QHH (same as above), Smilit E
X13 (Polyvinyl chloride powder, average particle size 5 microns Polymerization degree about 1300 Sumitomo Chemical Co., Ltd.), Sumitto PXUH (Polyvinyl chloride powder average particle size 1 micron degree about 6000 Sumitomo Chemical Co., Ltd.), or high molecular weight PVC (average) A PVC powder having a particle size of 10 microns and a degree of polymerization of about 15,000) is added in an amount shown in Table 1, dispersed by a disperser, and further Aerosil 200 (fumed silica powder, manufactured by Nippon Aerosil Co., Ltd.) as a thixotropic agent is shown in Table 1. The stated amount was added and dispersed by a disper to obtain a white uniform adhesive composition.
実施例4,8,10,13,16 エチル−α−シアノアクリレート（前記と同じ）100重
量部にSO220ppm、ハイドロキノン1000ppmを添加し、ス
ミリットSX−4G（前記と同じ）、スミリットPX−QHH
（前記と同じ）、スミリットEX13（前記と同じ）、スミ
リットPXUH（前記と同じ）又は高分子量PVC（前記と同
じ）を表１に記載した量添加し、ディスパーにより分散
させてさらにチクソトロピック剤としてアエロジル200
（前記と同じ）を表１に記載した量添加しディスパーに
より分散させ、白色均一な接着剤組成物を得た。Example 4,8,10,13,16 Ethyl-α-cyanoacrylate (same as above) 100 parts by weight of SO 2 20 ppm, hydroquinone 1000 ppm was added, Sumitto SX-4G (same as above), Sumitto PX-QHH
(Same as above), Sumit EX13 (same as above), Sumit PXUH (same as above) or high molecular weight PVC (same as above) are added in the amounts shown in Table 1 and dispersed by a disper to further serve as a thixotropic agent. Aerosil 200
(Same as above) was added in an amount shown in Table 1 and dispersed by a disper to obtain a white uniform adhesive composition.
実施例11,14,17 エチル−α−シアノアクリレート（前記と同じ）100重
量部にSO220ppmハイドロキノン1000ppmを添加し、増粘
剤としてダイアナールBR−85（前記と同じ）を表１に記
載した量溶解した後、スミリットEX−13（前記と同
じ）、スミリットPXUH（前記と同じ）又は高分子量PVC
（前記と同じ）を表１に記載した量添加し、ディスパー
により分散させ、白色均一な接着剤組成物を得た。Was added SO 2 20 ppm hydroquinone 1000ppm Example 11,14,17 ethyl -α- cyanoacrylate (the same as) 100 parts by weight, trade name: DIANAL BR-85 as a thickener and (the same) as described in Table 1 After dissolving in a certain amount, Smilit EX-13 (same as above), Smilit PXUH (same as above) or high molecular weight PVC
(Same as above) was added in an amount shown in Table 1 and dispersed by a disper to obtain a white uniform adhesive composition.
比較例１ エチル−α−シアノアクリレート（前記と同じ）にSO22
0ppm、ハイドロキノン1000ppmを添加し、そのまま用い
た。Comparative Example 1 Ethyl-α-cyanoacrylate (same as above) with SO 2 2
0 ppm and hydroquinone 1000 ppm were added and used as they were.
比較例２ エチル−α−シアノアクリレート（前記と同じ）にSO22
0ppm、ハイドロキノン1000ppmを添加し、この100重量部
にダイアナールBR−85（前記と同じ）10重量部溶解し
た。Comparative Example 2 Ethyl-α-cyanoacrylate (same as above) with SO 2 2
0 ppm and hydroquinone 1000 ppm were added, and 10 parts by weight of Dyanal BR-85 (same as above) was dissolved in 100 parts by weight of this.
比較例３ エチル−α−シアノアクリレート（前記と同じ）にSO22
0ppm、ハイドロキノン1000ppmを添加し、この100重量部
に、スミリットSX−4G（前記と同じ）20重量部をディス
パーで分散した。Comparative Example 3 Ethyl-α-cyanoacrylate (same as above) with SO 2 2
0 ppm and hydroquinone 1000 ppm were added, and to 100 parts by weight of this, 20 parts by weight of Summit SX-4G (same as above) was dispersed with a disper.
比較例４ エチル−α−シアノアクリレート（前記と同じ）にSO22
0ppm、ハイドロキノン1000ppmを添加し、この100重量部
にスミリットPX−QHH（前記と同じ）20重量部をディス
パーで分散した。Comparative Example 4 Ethyl-α-cyanoacrylate (same as above) with SO 2 2
0 ppm and 1000 ppm of hydroquinone were added, and 20 parts by weight of Summit PX-QHH (same as above) was dispersed in 100 parts by weight of this with a disper.
比較例５ エチル−α−シアノアクリレート（前記と同じ）にSO22
0ppm、ハイドロキノン1000ppmを添加し、この100重量部
にポリフッ化ビニリデン粉末60重量部をディスパーで分
散した。Comparative Example 5 Ethyl-α-cyanoacrylate (same as above) with SO 2 2
0 ppm and 1000 ppm of hydroquinone were added, and 60 parts by weight of polyvinylidene fluoride powder was dispersed by a disper in 100 parts by weight thereof.
比較例６ エチル−α−シアノアクリレート（前記と同じ）にSO22
0ppm、ハイドロキノン1000ppmを添加し、この100重量部
にシクロヘキサン30重量部溶解した。Comparative Example 6 Ethyl-α-cyanoacrylate (same as above) with SO 2 2
0 ppm and 1000 ppm of hydroquinone were added, and 30 parts by weight of cyclohexane was dissolved in 100 parts by weight of this.
（２）試験方法 粘度:JIS K6838に準じ測定した。(2) Test method Viscosity: Measured according to JIS K6838.
セットタイム:JIS K6861−８に準じ測定した。被着材
は鋼−鋼で試験した。Set time: Measured according to JIS K6861-8. The adherend was tested steel-steel.
引張剪断強度：被着材は鋼−鋼の場合はJIS K6861−
に準じ、ポリメチルメタクリレート系人工大理石同志の
場合はJIS K6849に準じて測定した。Tensile shear strength: Steel for adherend-JIS K6861 for steel-
In the case of polymethylmethacrylate artificial marbles, the measurement was performed according to JIS K6849.
白色度：黒色ゴム板上に巾2mm×長さ10cm塗布した時
の外観をみて、◎、○、△、×、の判定をした。Whiteness: Appearance when coated on a black rubber plate with a width of 2 mm and a length of 10 cm was judged to be ◎, ○, △, ×.
◎：白色、○：白色〜乳白色、△：乳白色、×：無色 耐水性：接着した鋼板を40℃温水に５日間浸せき後、
引張剪断強度を測定し、強度保持率を示した。⊚: White, ∘: White to milky white, Δ: Milky white, ×: Colorless Water resistance: After soaking the adhered steel plate in warm water at 40 ° C. for 5 days,
The tensile shear strength was measured and the strength retention was shown.
保存安定性:60℃95％R.H7日間保存後の粘度、白色度
を前記の方法でみた。Storage stability: Viscosity and whiteness after storage for 7 days at 60 ° C and 95% RH were examined by the methods described above.
（３）結果 表１の結果から、本発明の接着剤組成物が接着強度を低
下させることなく、いんぺい力の強い白色の接着剤であ
ることがわかった。増粘剤またはチクソトロピック剤を
添加しない場合は直後の使用では十分な白色を示した
が、長期保存の時、層分離を起こした。ポリフッ化ビニ
リデン粉末の場合は十分な白色を得るためにはその接着
強度を著しく犠牲にしなければならない。又エチル−α
−シアノアクリレートに溶け、その重合物には溶けない
シクロヘキサンの添加は半透明の乳白色しか得られず白
色度において不十分であった。(3) Results From the results in Table 1, it was found that the adhesive composition of the present invention is a white adhesive having a strong anti-paining force without lowering the adhesive strength. When no thickening agent or thixotropic agent was added, a white color was obtained immediately after use, but layer separation occurred during long-term storage. In the case of polyvinylidene fluoride powder, its adhesive strength must be significantly sacrificed in order to obtain a sufficient white color. Also ethyl-α
-Addition of cyclohexane, which is soluble in cyanoacrylate but not in its polymer, gave only a translucent milky white color and was insufficient in whiteness.
実施例18,19 比較例７−９ 厚さ5mm×巾5cm×長さ10cmにわたり白色人工大理石をつ
き合わせ接着する時、接着剤層を50〜200μとした場
合、完全硬化後その接着境界部が目視により容易に判別
できるか否かを試験した。はみ出した接着剤硬化物はサ
ンディングによりとり除いた。Examples 18 and 19 Comparative Examples 7-9 When a white artificial marble having a thickness of 5 mm, a width of 5 cm and a length of 10 cm is butt-bonded to each other, when the adhesive layer is 50 to 200 μ, the bonding boundary portion is completely cured. It was tested whether or not it could be easily visually identified. The adhesive cured product that had run off was removed by sanding.
以上より本発明の白色接着剤組成物はいんぺい性が十分
強く、白色人工大理石の接着をした時、その接着境界部
が判別できないほどきれいに仕上がることが判る。 From the above, it can be seen that the white adhesive composition of the present invention has sufficiently strong opacity, and when the white artificial marble is adhered, the adhesion boundary part is finished so clearly that it cannot be distinguished.
Claims (3)
アクリレート100重量部に対し、重合度200−20000のポ
リ塩化ビニル粉末を５−40重量部及び増粘剤を添加し、
粘度を1000〜100000CPとしたことを特徴とする白色α−
シアノアクリレート接着剤組成物。1. To α-cyanoacrylate, 5-40 parts by weight of polyvinyl chloride powder having a degree of polymerization of 200-20000 and a thickener are added to 100 parts by weight of the α-cyanoacrylate,
White α- characterized by viscosity of 1000-100,000 CP
Cyanoacrylate adhesive composition.
アクリレート100重量部に対し、重合度200−20000のポ
リ塩化ビニル粉末を５−40重量部及びチクソトロピック
剤を添加し、粘度を1000〜100000CPとしたことを特徴と
する白色α−シアノアクリレート接着剤組成物。2. To α-cyanoacrylate, 5-40 parts by weight of a polyvinyl chloride powder having a degree of polymerization of 200-20000 and a thixotropic agent are added to 100 parts by weight of the α-cyanoacrylate, and a viscosity of 1000-is obtained. A white α-cyanoacrylate adhesive composition characterized by having 100000 CP.
アクリレート100重量部に対し、重合度200−20000のポ
リ塩化ビニル粉末を５−40重量部及び増粘剤及びチクソ
トロピック剤を添加し、粘度を1000〜100000CPとしたこ
とを特徴とする白色α−シアノアクリレート接着剤組成
物。3. To α-cyanoacrylate, 5-40 parts by weight of polyvinyl chloride powder having a degree of polymerization of 200-20000, a thickener and a thixotropic agent are added to 100 parts by weight of the α-cyanoacrylate, A white α-cyanoacrylate adhesive composition having a viscosity of 1,000 to 100,000 CP.