JPH075814A - Tacky adhesive sheet for decoration - Google Patents
Tacky adhesive sheet for decorationInfo
- Publication number
- JPH075814A JPH075814A JP14620593A JP14620593A JPH075814A JP H075814 A JPH075814 A JP H075814A JP 14620593 A JP14620593 A JP 14620593A JP 14620593 A JP14620593 A JP 14620593A JP H075814 A JPH075814 A JP H075814A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- layer
- adhesive sheet
- release
- sensitive adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、巻き癖が少なく、マー
キング層の打ち抜き加工が容易で作業性の良い装飾用粘
着シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative pressure-sensitive adhesive sheet having less curl, easy stamping of a marking layer and good workability.
【0002】[0002]
【従来の技術】装飾用粘着シートは、剥離性台紙層−粘
着剤層−所望の着色等を施したマーキング用の基材層の
三層構造から成っており、被着体に貼り付け施工する時
は、マーキング層(所望の着色等を施したマーキング用
の基材層及び粘着剤層)を所望の形状に機械(カッティ
ングマシン)又は手切りで打ち抜き加工し、不要な部分
のカス取りを行った後、マーキング層の上に、弱粘着性
の粘着剤層を有したアプリケーションシートを貼り付
け、剥離性台紙からマーキング層をアプリケーションシ
ートに転写し、被着体に貼り付け施工した後、アプリケ
ーションシートのみを剥離、除去する作業方法が採られ
ている。2. Description of the Related Art A decorative pressure-sensitive adhesive sheet has a three-layer structure including a releasable mount layer, a pressure-sensitive adhesive layer, and a base layer for marking which is colored as desired. At this time, the marking layer (the marking base layer and the adhesive layer with the desired coloring, etc.) is punched into a desired shape by a machine (cutting machine) or by hand cutting, and unnecessary parts are removed. After applying the application sheet with a weak adhesive layer on the marking layer, transfer the marking layer from the releasable backing sheet to the application sheet and attach it to the adherend, and then apply the application sheet. The work method of peeling and removing only is adopted.
【0003】装飾用粘着シートのうち、屋内用もしくは
屋外短期用の装飾用粘着シートは、一般的に、剥離紙層
(130〜180μm)−粘着剤層(15〜30μm)
−軟質塩化ビニル系樹脂シートから成る基材層(50〜
150μm)の三層構造から成り、例えば巾460mm
×長さ10mの巻物状で製品化されている。Among the decorative pressure-sensitive adhesive sheets, a decorative pressure-sensitive adhesive sheet for indoor or outdoor use is generally a release paper layer (130 to 180 μm) -adhesive layer (15 to 30 μm).
-A base material layer (50-
150 μm) three-layer structure, for example, width 460 mm
× It is commercialized as a roll with a length of 10 m.
【0004】しかし、上記屋内用もしくは屋外短期用の
装飾用粘着シートは、巻き物状態にある時に巻き癖が発
生し、使用時水平に展開した時もその巻き癖が解消され
ず、マーキング層の打ち抜き加工に支障が起こりがちで
ある。特にフラットタイプのカッティングマシンで打ち
抜き加工する時は、一旦平置きにする必要があるが、巻
き癖が強いと平置きにするのが困難となり、打ち抜き加
工適性が悪くなるという問題点がある。However, the above-mentioned indoor or outdoor short-term decorative pressure-sensitive adhesive sheet has a curling tendency when it is in a rolled state, and the curling tendency is not eliminated even when it is spread horizontally during use, and the marking layer is punched out. Processing tends to be hindered. In particular, when punching with a flat type cutting machine, it is necessary to put the plate flat once, but if the winding tendency is strong, it becomes difficult to put it flat and the suitability for punching becomes poor.
【0005】[0005]
【発明が解決しようとする課題】本発明は、上記従来の
問題点を解消するため、巻き物状態から水平に展開した
時の巻き癖が少なく、フラットタイプのカッティングマ
シンでマーキング層を打ち抜き加工する時でも、平置き
が容易であり、打ち抜き加工適性に優れた装飾用粘着シ
ートを提供することを目的とする。SUMMARY OF THE INVENTION In order to solve the above-mentioned conventional problems, the present invention has less curling habit when horizontally rolled from a rolled state, and when punching a marking layer with a flat type cutting machine. However, it is an object of the present invention to provide a decorative pressure-sensitive adhesive sheet that can be easily placed flat and has excellent suitability for punching.
【0006】[0006]
【課題を解決するための手段】本発明の巻き癖の少ない
装飾用粘着シートは、坪量100g/m2 以下の紙にア
ンカーコートとしてポリエチレン樹脂を押出しラミネー
トし、その片面又は両面に離型剤を塗工して得られる剥
離紙を剥離性台紙として用い、又、ポリ塩化ビニル系樹
脂100重量部に対し、可塑剤24重量部以上を配合
し、成形して得られる軟質塩化ビニル系樹脂シートをマ
ーキング層の基材として用いることにより得られる。The decorative pressure-sensitive adhesive sheet with less curl of the present invention is obtained by extruding and laminating a polyethylene resin as an anchor coat on a paper having a basis weight of 100 g / m 2 or less, and releasing agent on one or both sides thereof. A soft vinyl chloride-based resin sheet obtained by applying the above-mentioned release paper as a release liner, and by mixing 24 parts by weight or more of a plasticizer with 100 parts by weight of a polyvinyl chloride-based resin and molding the mixture. Is used as the base material of the marking layer.
【0007】本発明の装飾用粘着シートに剥離性台紙と
して使用される剥離紙は、坪量100g/m2 以下の紙
(クラフト紙、グラシン紙、上質紙等)にアンカーコー
トとしてポリエチレン樹脂を押出しラミネートし、その
片面又は両面に離型剤を塗工して得られる。The release paper used as the release liner for the decorative pressure-sensitive adhesive sheet of the present invention is a polyethylene resin extruded as an anchor coat on paper having a basis weight of 100 g / m 2 or less (kraft paper, glassine paper, high-quality paper, etc.). It is obtained by laminating and coating a release agent on one or both sides.
【0008】上記剥離紙に使用される紙の坪量は、10
0g/m2 以下であることが必要であり、紙の坪量が1
00g/m2 を超えたものであると、得られる剥離紙の
腰が強くなりすぎて、巻き癖改善効果が得られない。The basis weight of the paper used for the release paper is 10
It must be 0 g / m 2 or less, and the basis weight of the paper is 1
When it is more than 00 g / m 2 , the obtained release paper becomes too stiff and the curling habit improving effect cannot be obtained.
【0009】紙にアンカーコートとして押出しラミネー
トされるポリエチレン樹脂の厚みは、特に限定されるも
のではないが、片面15〜30μm程度が好ましい。The thickness of the polyethylene resin extruded and laminated as an anchor coat on paper is not particularly limited, but is preferably about 15 to 30 μm on one side.
【0010】上記剥離紙の片面又は両面に塗工される離
型剤としては、特に限定されるものではないが、シリコ
ン系もしくは長鎖アルキル基含有化合物等が挙げられ、
一般的には、シリコン系が好適に使用される。シリコン
系離型剤の塗工量は、固形分で片面0.3〜1.0g/
m2 程度が好ましい。The release agent coated on one side or both sides of the release paper is not particularly limited, and examples thereof include silicon-based or long-chain alkyl group-containing compounds.
Generally, a silicon-based material is preferably used. The coating amount of the silicone-based release agent is 0.3 to 1.0 g / solid side on one side.
About m 2 is preferable.
【0011】本発明の装飾用粘着シートに粘着剤層とし
て使用される粘着剤は、特に限定はされず、通常のゴム
系溶剤型又はエマルジョン型粘着剤、アクリル系溶剤型
又はエマルジョン型粘着剤等が使用されるが、耐候性の
良いアクリル系粘着剤が好ましい。The pressure-sensitive adhesive used as the pressure-sensitive adhesive layer in the decorative pressure-sensitive adhesive sheet of the present invention is not particularly limited, and ordinary rubber-based solvent-based or emulsion-based pressure-sensitive adhesives, acrylic solvent-based or emulsion-based pressure-sensitive adhesives, etc. However, an acrylic adhesive having good weather resistance is preferable.
【0012】本発明の装飾用粘着シートのマーキング層
に基材として用いられる軟質塩化ビニル系樹脂シート
は、ポリ塩化ビニル系樹脂100重量部に対して、24
重量部以上の可塑剤と、顔料、安定剤及び必要なら有機
溶剤等を混合したポリ塩化ビニル系樹脂のプラスチゾル
又はオルガノゾル分散液もしくは溶液をカレンダ成形、
押出し成形、流延成形等により、厚み50〜150μm
のシート状に成形して得られる。The soft vinyl chloride resin sheet used as a substrate for the marking layer of the decorative pressure-sensitive adhesive sheet of the present invention is 24 parts with respect to 100 parts by weight of polyvinyl chloride resin.
Calender molding a plastisol or organosol dispersion or solution of polyvinyl chloride resin in which a plasticizer of more than parts by weight, a pigment, a stabilizer, and an organic solvent, if necessary, is mixed,
By extrusion molding, casting, etc., thickness 50-150 μm
It is obtained by molding into a sheet shape.
【0013】上記基材に使用する可塑剤としては、特に
限定されるものではないが、ジブチルフタレート、ジオ
クチルフタレート等のフタル酸エステル系可塑剤やポリ
エステル系可塑剤等が好適に使用される。The plasticizer used for the base material is not particularly limited, but phthalate ester plasticizers such as dibutyl phthalate and dioctyl phthalate and polyester plasticizers are preferably used.
【0014】上記基材では、ポリ塩化ビニル系樹脂10
0重量部に対し、可塑剤を24重量部以上配合すること
が必要であり、可塑剤の配合量が、24重量部未満であ
ると、基材が硬くなりすぎて、巻き癖改善効果が乏しく
なる。In the above base material, the polyvinyl chloride resin 10 is used.
It is necessary to add 24 parts by weight or more of the plasticizer to 0 part by weight. If the amount of the plasticizer is less than 24 parts by weight, the base material becomes too hard and the curling habit improving effect is poor. Become.
【0015】[0015]
【作用】本発明により得られる装飾用粘着シートは、剥
離性台紙として、坪量100g/m2 以下の紙にアンカ
ーコートとしてポリエチレン樹脂を押出しラミネート
し、その片面又は両面に離型剤を塗工して得られる剥離
紙を用い、且つ、マーキング層の基材として、ポリ塩化
ビニル系樹脂100重量部に対し、可塑剤24重量部以
上を配合し成形して得られる軟質塩化ビニル系樹脂シー
トを用いて成るものであり、巻き癖が少なく、フラット
タイプのカッティングマシンでマーキング層を打ち抜き
加工する時でも、平置きが容易であり、打ち抜き加工適
性に優れたものである。The decorative pressure-sensitive adhesive sheet obtained by the present invention is used as a release liner, and a polyethylene resin is extruded and laminated as an anchor coat on a paper having a basis weight of 100 g / m 2 or less, and a release agent is coated on one side or both sides. A soft vinyl chloride resin sheet obtained by using the release paper obtained as described above and molding 24 parts by weight or more of a plasticizer with 100 parts by weight of polyvinyl chloride resin as a base material of the marking layer and molding the mixture. Since it is used, the curling tendency is small, and even when the marking layer is punched by a flat type cutting machine, it can be easily placed flat and has excellent suitability for punching.
【0016】[0016]
【実施例】本発明をさらに詳しく説明するため、以下に
実施例をあげる。なお、実施例中の「部」は「重量部」
を意味する。EXAMPLES In order to explain the present invention in more detail, examples will be given below. In the examples, "part" is "part by weight".
Means
【0017】(実施例1〜3、比較例1〜2)(Examples 1 to 3, Comparative Examples 1 and 2)
【0018】(1)剥離紙の作成 表1に示すとおり、坪量65〜135g/m2 の範囲の
クラフト紙の両面に、ポリエチレン樹脂を片面20μm
の厚みで押出しラミネートしたものの片面に、シリコン
系離型剤を固形分で0.7g/m2 塗工して離型処理を
施し、剥離紙を得た。( 1) Preparation of release paper As shown in Table 1, polyethylene resin is applied to both sides of a kraft paper having a basis weight of 65 to 135 g / m 2 with 20 μm on one side.
The release paper was obtained by applying a silicone-based release agent in a solid content of 0.7 g / m 2 on one side of the extrusion-laminated sheet having a thickness of 3 to perform release treatment.
【0019】(2)評価 図1に示すように、得られた剥離紙6を、外径2インチ
の紙管1に巻き付け、40℃で3日間保管後、10℃、
20℃、30℃の各温度に1時間放置した後、各温度下
で紙管1から長さ1mで水平に展開し、平置きにして5
分後の各温度における巻き癖高さ(mm)7を測定し
た。結果は表1に示すとおりであった。( 2) Evaluation As shown in FIG. 1, the obtained release paper 6 was wrapped around a paper tube 1 having an outer diameter of 2 inches, stored at 40 ° C. for 3 days, and then at 10 ° C.
After left at each temperature of 20 ° C and 30 ° C for 1 hour, at each temperature, the paper tube 1 is horizontally spread with a length of 1 m and placed flatly for 5 hours.
The curl height (mm) 7 at each temperature after the measurement was measured. The results are as shown in Table 1.
【0020】[0020]
【表1】 [Table 1]
【0021】表1に示されたとおり、実施例1〜3の剥
離紙6は、紙の坪量の減少に伴い巻き癖高さ7も減少す
る。これに対し、比較例1〜2の剥離紙6は、水平に展
開した後、自然に巻き戻りが起こり、巻き癖高さ7を測
定出来なかった。As shown in Table 1, in the release papers 6 of Examples 1 to 3, the curl height 7 also decreases as the basis weight of the paper decreases. On the other hand, the release papers 6 of Comparative Examples 1 and 2 were naturally unwound after being spread horizontally, and the curl height 7 could not be measured.
【0022】(実施例4〜7、比較例3〜5)(Examples 4 to 7, Comparative Examples 3 to 5)
【0023】(1)基材の作成 表2に示すとおり、ポリ塩化ビニル系樹脂100部に対
し、可塑剤(ジオクチルフタレート)の配合量を12〜
36部の範囲で種々変え、赤色顔料8部、安定剤2部等
を加えた配合組成のプラスチゾル分散液をカレンダー法
で成形し、厚み90μmの軟質塩化ビニル樹脂系シート
の基材3を得た。( 1) Preparation of Base Material As shown in Table 2, the compounding amount of the plasticizer (dioctyl phthalate) is 12 to 100 parts of the polyvinyl chloride resin.
A plastisol dispersion having a composition of 8 parts of red pigment, 2 parts of stabilizer, etc. was variously molded in a range of 36 parts by a calender method to obtain a base material 3 of a soft vinyl chloride resin sheet having a thickness of 90 μm. .
【0024】(2)評価 得られた基材3の巻き癖高さ7を、実施例1と同様の方
法で測定した結果は表2に示すとおりであった。( 2) Evaluation The curl height 7 of the obtained substrate 3 was measured by the same method as in Example 1 and the results are shown in Table 2.
【0025】[0025]
【表2】 [Table 2]
【0026】表2に示されたとおり、実施例4〜7の基
材3の巻き癖高さ7は1.3mm以下と良好である。こ
れに対し、比較例3〜5の基材3の巻き癖高さ7は3.
3mm以上であった。As shown in Table 2, the curl height 7 of the base material 3 of Examples 4 to 7 is as good as 1.3 mm or less. On the other hand, the curl height 7 of the base material 3 of Comparative Examples 3 to 5 is 3.
It was 3 mm or more.
【0027】(実施例8)(Embodiment 8)
【0028】(1)剥離紙の作成 坪量100g/m2 のクラフト紙を用い、実施例1と同
様にして剥離紙6を得た。( 1) Preparation of Release Paper Release paper 6 was obtained in the same manner as in Example 1 using kraft paper having a basis weight of 100 g / m 2 .
【0029】(2)基材の作成 ポリ塩化ビニル系樹脂100部に対する可塑剤(ジオク
チルフタレート)の配合量を24部とし、実施例4と同
様にして厚み70μmの軟質塩化ビニル系樹脂シートを
作成し、基材3を得た。( 2) Preparation of base material A flexible vinyl chloride resin sheet having a thickness of 70 μm was prepared in the same manner as in Example 4, except that the compounding amount of the plasticizer (dioctyl phthalate) was 24 parts with respect to 100 parts of the polyvinyl chloride resin. Then, the base material 3 was obtained.
【0030】(3)装飾用粘着シートの作成 得られた剥離紙6の片面に、アクリル系溶剤型粘着剤
(固形分30%)を固形分の塗工厚が23μmになるよ
うに塗工し、得られた基材3を貼り合わせて装飾用粘着
シート2を作成し、外径2インチ及び3インチの紙管1
に巻き取り、巾460mm×長さ10mの巻き物を得
た。( 3) Preparation of decorative pressure-sensitive adhesive sheet An acrylic solvent-based pressure-sensitive adhesive (30% solid content) was coated on one surface of the obtained release paper 6 so that the coating thickness of the solid content was 23 μm. Then, the obtained base material 3 is attached to form a decorative pressure-sensitive adhesive sheet 2, and a paper tube 1 having an outer diameter of 2 inches and 3 inches is produced.
It was wound on a roll to obtain a roll having a width of 460 mm and a length of 10 m.
【0031】(4)評価 得られた巻き物を、50℃で1週間保管後取り出し、2
0℃で1時間放置した後、その温度下で、図2に示すよ
うに剥離紙6を上にした状態で紙管1から長さ1mで水
平に展開し、平置きにして5分後の巻き癖高さ(巻き癖
高さA)7を測定した。又、図3に示すように基材3を
上にした状態で紙管1から長さ1mで水平に展開し、平
置きにして5分後の巻き癖高さ(巻き癖高さB)7も同
様の方法で測定した。結果は表3に示すとおりであっ
た。( 4) Evaluation The obtained roll was stored at 50 ° C. for 1 week and then taken out, 2
After leaving at 0 ° C. for 1 hour, at that temperature, as shown in FIG. 2, with the release paper 6 on top, the paper tube 1 was horizontally spread with a length of 1 m and placed flat for 5 minutes. The curl height (curl height A) 7 was measured. In addition, as shown in FIG. 3, with the base material 3 facing upward, the paper core 1 is horizontally developed with a length of 1 m and placed flat for 5 minutes and the curl height (curl height B) 7 Was also measured by the same method. The results are shown in Table 3.
【0032】(比較例6)(Comparative Example 6)
【0033】剥離紙6の作成において、クラフト紙の坪
量を120g/m2 としたこと以外は、実施例8と同様
にして装飾用粘着シート2の巻き物を得た。In the production of the release paper 6, a scroll of the decorative pressure-sensitive adhesive sheet 2 was obtained in the same manner as in Example 8 except that the basis weight of the kraft paper was 120 g / m 2 .
【0034】得られた装飾用粘着シート2の巻き癖高さ
(巻き癖高さA及びB)7を実施例8と同様にして測定
した結果は表3に示すとおりであった。The curl heights (curl heights A and B) 7 of the obtained decorative pressure-sensitive adhesive sheet 2 were measured in the same manner as in Example 8 and the results are shown in Table 3.
【0035】(比較例7)(Comparative Example 7)
【0036】基材3の作成において、ポリ塩化ビニル系
樹脂100部に対する可塑剤(ジオクチルフタレート)
の配合量を20部としたこと以外は、実施例8と同様に
して装飾用粘着シート2の巻き物を得た。In the preparation of the base material 3, a plasticizer (dioctyl phthalate) is added to 100 parts of polyvinyl chloride resin.
A scroll of the decorative pressure-sensitive adhesive sheet 2 was obtained in the same manner as in Example 8 except that the compounding amount was 20 parts.
【0037】得られた装飾用粘着シート2の巻き癖高さ
(巻き癖高さA及びB)7を実施例8と同様にして測定
した結果は表3に示すとおりであった。The curl heights (curl heights A and B) 7 of the obtained decorative pressure-sensitive adhesive sheet 2 were measured in the same manner as in Example 8 and the results are shown in Table 3.
【0038】[0038]
【表3】 [Table 3]
【0039】表3に示されたとおり、本発明外の比較例
6及び7に比べて、本発明により得られた実施例8の装
飾用粘着シート2の巻き癖高さ7は低い値であり、巻き
癖改善効果が認められる。また、紙管1の外径が大きい
方が、巻き癖高さ7が低いことも認められる。As shown in Table 3, the curl height 7 of the decorative pressure-sensitive adhesive sheet 2 of Example 8 obtained by the present invention is lower than that of Comparative Examples 6 and 7 outside the present invention. , A curling habit improving effect is recognized. It is also recognized that the larger the outer diameter of the paper tube 1 is, the lower the curl height 7 is.
【0040】装飾用粘着シート2を実際に使用する場合
の展開方法は、図3に示されるように基材3を上にした
状態で行われるが、表3に示される実施例8で外径3イ
ンチの紙管1を使用した場合の巻き癖高さ(巻き癖高さ
B)7の結果5mmは、フラットタイプのカッティング
マシンでマーキング層5の打ち抜き加工をする場合で
も、何ら支障の無いレベルである。When the decorative pressure-sensitive adhesive sheet 2 is actually used, the developing method is carried out with the base material 3 facing up as shown in FIG. 3, but the outer diameter in Example 8 shown in Table 3 is used. As a result of the curl height 7 (curl height B) 7 when the 3-inch paper tube 1 is used, the level of 5 mm is no problem even when the marking layer 5 is punched by a flat type cutting machine. Is.
【0041】[0041]
【発明の効果】以上のように、本発明による装飾用粘着
シートは、巻き癖が大幅に改善されているので、フラッ
トタイプのカッティングマシンでマーキング層の打ち抜
き加工をする場合でも、支障無く平置きでき、打ち抜き
加工適性に優れたものである。As described above, since the decorative pressure-sensitive adhesive sheet according to the present invention has a significantly improved curling habit, even when the marking layer is punched with a flat type cutting machine, it can be placed flat without any trouble. It is capable of punching and has excellent suitability for punching.
【0042】[0042]
【図1】剥離紙又は基材を、紙管から1mの長さで水平
に展開した時の正面図である。FIG. 1 is a front view when a release paper or a base material is horizontally developed with a length of 1 m from a paper tube.
【図2】装飾用粘着シートを剥離紙を上にして、紙管か
ら1mの長さで水平に展開した時の正面図である。FIG. 2 is a front view of the decorative pressure-sensitive adhesive sheet with the release paper on the top and when it is horizontally developed at a length of 1 m from the paper tube.
【図3】装飾用粘着シートを基材を上にして、紙管から
1mの長さで水平に展開した時の正面図である。FIG. 3 is a front view of the decorative pressure-sensitive adhesive sheet, with the base material facing upward, when the pressure-sensitive adhesive sheet is horizontally developed at a length of 1 m from the paper tube.
1 紙管 2 装飾用粘着シート 3 基材 4 粘着剤 5 マーキング層 6 剥離紙 7 巻き癖高さ(mm) 8 支持台 1 Paper Tube 2 Adhesive Sheet for Decoration 3 Base Material 4 Adhesive 5 Marking Layer 6 Release Paper 7 Curling Height (mm) 8 Support
Claims (1)
粘着剤層とマーキング用の基材層から成るマーキング層
をこの順に設けた装飾用粘着シートであって、剥離性台
紙が、坪量100g/m2 以下の紙にポリエチレン樹脂
を押出しラミネートし、その片面又は両面に離型剤を塗
工して得られる剥離紙であり、マーキング層の基材が、
ポリ塩化ビニル系樹脂100重量部に対し、可塑剤24
重量部以上を配合し成形して得られる軟質塩化ビニル系
樹脂シートであることを特徴とする装飾用粘着シート。1. A decorative pressure-sensitive adhesive sheet comprising a release liner and a marking layer comprising a pressure-sensitive adhesive layer and a base material layer for marking provided on the release liner in this order. Is a release paper obtained by extruding and laminating a polyethylene resin on a paper having a basis weight of 100 g / m 2 or less, and applying a release agent on one or both surfaces thereof, wherein the base material of the marking layer is
Plasticizer 24 per 100 parts by weight of polyvinyl chloride resin
A decorative pressure-sensitive adhesive sheet, characterized in that it is a soft vinyl chloride resin sheet obtained by blending parts by weight or more and molding.