JPH075343B2 - Manufacturing method of colored slip-stop aggregate for paved road - Google Patents
Manufacturing method of colored slip-stop aggregate for paved roadInfo
- Publication number
- JPH075343B2 JPH075343B2 JP32436789A JP32436789A JPH075343B2 JP H075343 B2 JPH075343 B2 JP H075343B2 JP 32436789 A JP32436789 A JP 32436789A JP 32436789 A JP32436789 A JP 32436789A JP H075343 B2 JPH075343 B2 JP H075343B2
- Authority
- JP
- Japan
- Prior art keywords
- manufacturing
- paved road
- aggregate
- slip
- colored slip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 産業上の利用分 本発明は舗装道路の表面に接着剤により固着させて粗面
とすることにより車のスリツプを防止するための着色骨
材の製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing a colored aggregate for preventing slipping of a vehicle by fixing it to a surface of a paved road with an adhesive to form a rough surface.
従来の技術及び発明が解決しようとする問題点 舗装道路用スリツプ止め骨材は、その施工場所を明確に
するために各種の色が付されているが、タイヤとの摩擦
により摩耗しても色が変わらないように表面だけでな
く、骨材の内部まで着色する必要がある。このため、従
来は、陶磁器用坏土に無機顔料を混合して微粉砕したも
のに水を加えて所望の塊に成形し、これを焼成して冷却
した後に粉砕し、分粒していたが、このような方法では
粉砕の際に半分以上が粒径1mm以下の使用不能な微粉末
となつて高価な無機顔料が無駄になる欠点があつた。な
お、陶磁器粒の製造方法としては、上記以外に、陶磁器
用坏土に無機顔料を混合して微粉砕したものに水を加え
て造粒機により所望の粒子に造粒した後に焼成する方法
があり、この方法では原料の無駄はないが外面形状が丸
みを帯びているためスリツプ止め骨材としては不適当で
ある。問題点を解決するための手段 本発明はこのような問題点を解決するための手段とし
て、素焼素地を粉砕し、分粒後に金属錯塩水溶液を含浸
させ、焼成する構成とした。Problems to be Solved by Conventional Techniques and Inventions Slip-stop aggregates for paved roads are given various colors to clarify the construction site, but even when worn due to friction with tires It is necessary to color not only the surface but also the inside of the aggregate so that the color does not change. Therefore, conventionally, a clay was mixed with an inorganic pigment and finely pulverized, water was added to the pulverized mixture to form a desired lump, which was fired, cooled, pulverized, and then sized. However, such a method has a drawback that more than half of the particles become unusable fine powders having a particle size of 1 mm or less during pulverization, and expensive inorganic pigments are wasted. Incidentally, as a method for producing ceramic granules, in addition to the above, there is a method in which water is added to a finely pulverized mixture of an inorganic pigment in a clay for clay and granulated into desired particles by a granulator and then fired. There is no waste of raw materials in this method, but the outer surface shape is rounded, which is unsuitable as a slip stopping aggregate. Means for Solving Problems As a means for solving such problems, the present invention has a structure in which a bismuth substrate is crushed, and after sizing, an aqueous metal complex salt solution is impregnated and fired.
発明の作用及び効果 本発明は上記構成になり、粉砕し、分粒した後に金属錯
塩水溶液を含浸させたから、焼成した骨材は全て使用可
能であつて顔料(金属錯塩水溶液)の無駄がなく、ま
た、母材の原料となる素焼素地は、従来、産業廃棄物と
して処分されていた陶磁器の素焼時に生ずる不良品を活
用することができて低コストで製造することができ、さ
らに、顔料として金属錯塩水溶液を含浸させたから釉薬
のように表面に付着するだけでなく毛細管現象により内
部までしみ込んで焼成により素地と固相反応を生じて発
色するのであつて、摩耗しても色が変わることがないと
ともに、素焼素地を粉砕したものであるから表面が角張
つていてスリツプ止めの効果が大きい。また、金属塩錯
水溶液は焼成時に腐食性ガスを発生せず炉を傷めない効
果がある。Action and Effect of the Invention The present invention has the above-described structure, and is crushed and sized, and then impregnated with the aqueous solution of the metal complex salt. In addition, the unglazed green body that is the raw material of the base material can be manufactured at low cost by utilizing the defective product that is generated when unglazed ceramics, which were conventionally disposed as industrial waste, and can be manufactured at low cost. Since it is impregnated with an aqueous solution of complex salt, it not only adheres to the surface like a glaze, but also penetrates into the interior due to the capillary phenomenon and causes a solid-phase reaction with the substrate by firing to develop color, but the color does not change even when worn At the same time, since the unglazed body is crushed, the surface is angular and the effect of stopping slipping is great. The metal salt complex aqueous solution does not generate corrosive gas during firing and has an effect of not damaging the furnace.
実施例 本発明に顔料として使用する金属錯塩水溶液としてはBE
NCKISER-KNAPSACK社がメラポンという商品名で販売して
いるものが好適である。Example BE was used as an aqueous solution of a metal complex salt used as a pigment in the present invention.
The one sold by NCKISER-KNAPSACK under the product name Melapon is suitable.
ここで、本発明の一実施例を説明すると、陶磁器の素焼
不良品を粉砕し、粒径1〜7mmの範囲のものを用途に応
じて数段階に分粒し、十分に乾燥させた後、鉄を発色元
素とするメラポン2009水溶液中に浸漬して含浸させた
後、乾燥して1100℃〜1300℃で焼成したところ、表面か
ら約2mmの深さまで赤褐色に着色された骨材が得られ
た。Here, explaining one embodiment of the present invention, crushed unglazed porcelain porcelain, sized in a range of particle size 1 ~ 7mm in several stages depending on the application, after sufficiently dried, After immersing it in an aqueous solution of Melapon 2009 containing iron as a coloring element and impregnating it, it was dried and calcined at 1100 ° C to 1300 ° C, and an aggregate colored reddish brown to a depth of about 2 mm from the surface was obtained. .
Claims (1)
液を含浸させ、焼成することを特徴とする舗装道路用ス
リツプ止め着色骨材の製造方法1. A method for producing a colored aggregate for slip-proofing on a pavement, which comprises crushing a bismuth base, sizing, impregnating an aqueous metal complex salt solution, and firing.