JPH0740027Y2 - Veneer for construction - Google Patents
Veneer for constructionInfo
- Publication number
- JPH0740027Y2 JPH0740027Y2 JP1989087315U JP8731589U JPH0740027Y2 JP H0740027 Y2 JPH0740027 Y2 JP H0740027Y2 JP 1989087315 U JP1989087315 U JP 1989087315U JP 8731589 U JP8731589 U JP 8731589U JP H0740027 Y2 JPH0740027 Y2 JP H0740027Y2
- Authority
- JP
- Japan
- Prior art keywords
- decorative board
- construction
- impregnated
- paper
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】 （産業上の利用分野） 本考案は、床面または壁面に直貼りすることにより、床
面等の表面を美麗に仕上げるための建築用化粧板に関す
るものである。DETAILED DESCRIPTION OF THE INVENTION (Industrial field of application) The present invention relates to a decorative board for construction for directly finishing the surface such as a floor surface by directly attaching it to a floor surface or a wall surface.
（従来の技術） 建物における床面や壁面に対しては、例えば第１図に示
すように、タイルのように所定形状に切断した多数の化
粧板を配列して直貼りすることにより、これらの床面等
の表面を美麗に仕上げることが行なわれる。(Prior Art) For a floor surface or a wall surface in a building, for example, as shown in FIG. 1, by arranging a large number of decorative plates cut in a predetermined shape like tiles and directly pasting them, The surface such as the floor is beautifully finished.
従来のこの種の化粧板としては、例えば木質合板の表面
に所定の着色や模様を付した表面材を貼付したものがあ
る。このような木質合板を基材とする化粧板は、建築用
化粧板としての所定の耐熱性を有すること、及び特に床
材として使用したときの所定の表面硬度を有するという
長所はあるものの、次のような短所をも有している。As a conventional decorative board of this type, there is, for example, one in which a surface material having a predetermined color or pattern is attached to the surface of a wooden plywood. Such a decorative board using a wooden plywood as a base material has the advantage that it has a predetermined heat resistance as a decorative board for construction and has a predetermined surface hardness when used as a flooring material, It also has the following disadvantages.
すなわち、 ・木質合板を基材とする化粧板は、木質合板によるある
一定の剛性を有しているものであるから、完全な平面で
はないコンクリートからなる床面等に対して、全面がぴ
ったりと密着した状態で直貼りすることができず、剥れ
等の問題を発生し易いものとなり得る。That is, since the veneer made of wood plywood has a certain rigidity due to the wood plywood, the entire surface fits perfectly against the floor surface made of concrete that is not a perfect plane. It cannot be directly attached in a close contact state, which may easily cause problems such as peeling.
・直張りすべき面が、壁面等のコーナーにおけるような
曲面であると、木質合板を基材とする化粧板はその直貼
りが殆んど不可能である。-If the surface to be directly attached is a curved surface such as a corner of a wall surface, it is almost impossible to directly attach a decorative board using wood plywood as a base material.
・このような化粧板を所定形状のものとするためには、
工場等において切断しなければならないが、この化粧板
の端部にササクレが生じないように切断することは困難
である。特に、施工現場においてこの化粧板を所定形状
に小さくしなければならない場合に、端部にササクレが
生じないように切断することは非常に困難であって、そ
の施工性は極めて悪いものである。・ In order to make such a decorative plate into a predetermined shape,
Although it must be cut in a factory or the like, it is difficult to cut so that the edges of this decorative plate are not crispy. In particular, when it is necessary to reduce the size of this decorative plate to a predetermined shape at the construction site, it is very difficult to cut it so that the end portion is not crispy, and the workability is extremely poor.
これに対して、塩ビタイルやリノタイル、あるいはホモ
ジニアスタイル等の軟質材料を基材とするものが提案さ
れているが、これらは上記の欠点はないものの、逆に床
材として使用する場合の表面硬度が不足するものであ
り、耐熱性にも劣るものである。On the other hand, although vinyl tiles, lino tiles, or those using a soft material such as a homogeneous style as a base material have been proposed, although these do not have the above-mentioned drawbacks, on the contrary, the surface hardness when used as a floor material. Is insufficient and the heat resistance is also poor.
そこで、本考案者等は、上述した各短所を全て解決する
ことのできる化粧板をどのように構成したらよいかにつ
いて鋭意研究を重ねてきた結果、本考案を完成したので
ある。Therefore, the inventors of the present invention have completed the present invention as a result of earnestly researching how to construct a decorative plate that can solve all of the above-mentioned disadvantages.
（考案が解決しようとする課題） 本考案は、以上の経験に基づいてなされたもので、その
解決しようとする課題は、従来の化粧板における建築用
としての条件の不満足である。(Problems to be Solved by the Invention) The present invention has been made based on the above experience, and the problem to be solved is that the conventional decorative board is not satisfied with the conditions for construction.
そして、本考案の目的とするところは、十分な耐熱性・
硬度を有し、施工性にも優れた建築用化粧板（10）を安
価に提供することにある。And the purpose of this invention is to have sufficient heat resistance
An object is to provide a decorative decorative board (10) having hardness and excellent workability at low cost.
（課題を解決するための手段） 以上の課題を解決するために、本考案の採った手段は、
実施例において使用する符号を付して説明すると、 厚みが1mm以上の塩化ビニル系基材と表装材とを接着層
を介して接着してなる建築用化粧板において、 前記表装材を、耐摩耗性微粉末を混入した樹脂含浸オー
バーレイ紙からなる保護層、印刷が施された樹脂含浸パ
ターン紙からなるパターン層および樹脂含浸コアー紙か
らなるコアー層を積層して一体成型した、厚み0.6mm以
下の積層材にて構成したことを特徴とする建築用化粧
板。(Means for Solving the Problems) In order to solve the above problems, the means adopted by the present invention are
Explaining with the reference numerals used in the examples, in the decorative decorative board for construction having a thickness of 1 mm or more and a vinyl chloride base material and a covering material bonded via an adhesive layer, the covering material, wear resistance Of a protective layer consisting of resin-impregnated overlay paper mixed with a resin fine powder, a pattern layer consisting of printed resin-impregnated pattern paper and a core layer consisting of resin-impregnated core paper are integrally molded and have a thickness of 0.6 mm or less. A decorative board for construction characterized by being composed of laminated materials.
である。Is.
即ち、本考案の特徴は、塩化ビニル系基材（以下は、単
に「塩ビ系基材」という）の表面に積層接着する表装材
の構成にあり、特にこの表装材を、最外層を構成してい
る保護層を、耐摩耗性を付与するために、アルミナやSi
Cの如き高硬度耐摩耗性微粉末を混入抄造して得られる
混抄紙に樹脂を含浸したオーバーレイ紙にて形成すると
共に、この樹脂含浸オーバーレイ紙に対しては更に、模
様印刷が施された樹脂含浸パターン紙と樹脂含浸コアー
紙を裏打ち接着して一体成型した積層材とした点の構成
にある。この表装材の詳しい構造については、実施例の
記載にあわせて説明する。That is, the feature of the present invention lies in the constitution of the covering material which is laminated and adhered to the surface of the vinyl chloride base material (hereinafter, simply referred to as “vinyl chloride base material”). In particular, this covering material constitutes the outermost layer. The protective layer is coated with alumina or Si to provide wear resistance.
Formed with overlay paper impregnated with resin on a mixed paper obtained by mixing paper with high hardness and abrasion resistant fine powder such as C, and further, resin on which pattern printing was applied to this resin-impregnated overlay paper The point is that the impregnated pattern paper and the resin-impregnated core paper are lined and bonded to form a laminated material. The detailed structure of this cover material will be described along with the description of the embodiment.
ここで、表装材（11）の全体としての厚みが0.6mm以下
であることが必要な第一理由は、もしこの表装材（11）
の厚みが0.6mmより大きい場合には、塩ビ系基材（12）
の折角の弾力性及び柔軟性を十分生かすことができなく
なって、当該建築用化粧板（10）をコンクリート等から
形成された床面や壁面の凹凸に完全に沿わせることがで
きなくなるからである。また、表装材（11）の全体とし
ての厚みが0.6mm以下であることが必要な第二の理由
は、表装材（11）の厚みが0.6mmより大きくなると、打
ち抜き等の装置にて第１図のような形状に剪断する場
合、表装材（11）の小口面にバリ等が発生し易くなり、
剪断が困難になるからである。これと同様な理由によっ
て、塩ビ系基材（12）の厚みは1mm以上である必要があ
る。Here, the first reason why the total thickness of the covering material (11) needs to be 0.6 mm or less is if the covering material (11) is
If the thickness is larger than 0.6 mm, PVC base material (12)
This is because it is not possible to make full use of the elasticity and flexibility of the corner, and it becomes impossible to completely fit the architectural decorative board (10) to the unevenness of the floor surface or wall surface formed of concrete or the like. . The second reason why the total thickness of the covering material (11) is required to be 0.6 mm or less is that when the thickness of the covering material (11) is larger than 0.6 mm, it is not possible When shearing into the shape as shown in the figure, burrs etc. are likely to occur on the edge of the surface covering material (11),
This is because shearing becomes difficult. For the same reason as above, the thickness of the vinyl chloride base material (12) needs to be 1 mm or more.
また、この建築用化粧板（10）は、特に床面を構成する
場合に、リノリウムや塩ビタイルのように耐摩耗性に劣
るものであってはならないから、その表装材（11）を構
成する保護層（11a）としては耐摩耗性を有する必要が
あるのであり、そのために耐摩耗性物質を含有する保護
層（11a）を有している必要がある。In addition, since this architectural decorative board (10) must not be inferior in wear resistance like linoleum or vinyl chloride, especially when it constitutes a floor surface, it constitutes its covering material (11). The protective layer (11a) needs to have abrasion resistance, and therefore needs to have the protective layer (11a) containing an abrasion resistant substance.
（考案の作用） 次に、本考案に係る建築用化粧板（10）の作用につい
て、その施工の態様とも併せて説明する。(Operation of Device) Next, the operation of the architectural decorative board (10) according to the present invention will be described together with its construction mode.
まず、この建築用化粧板（10）は、これを多数配列して
一定の模様を形成すべく、第１図の施工例におけるよう
な形状に予じめ切断されるものであるが、その切断は一
般の裁断装置あるいは打ち抜き装置で十分可能である。
すなわち、木質合板を基材とするものであれば、端部に
ササクレが生じないように、時間をかけて回転鋸歯等で
行なわなければならないが、本考案に係る建築用化粧板
（10）を所謂タイルとして構成する場合には剪断作業で
短時間内で容易に行なえるものである。この場合、建築
用化粧板（10）を構成している表装材（11）にも塩ビ系
基材（12）にもササクレは全く生じないものであり、そ
の端部は美麗に仕上げられる。First, this architectural decorative board (10) is preliminarily cut into a shape as in the construction example of FIG. 1 so as to form a certain pattern by arranging a large number of the decorative boards. A general cutting device or punching device is sufficient.
That is, if the wood-based plywood is used as the base material, it must be done with a rotating sawtooth or the like over time so that the edges do not become rough. When it is constructed as a so-called tile, it can be easily done within a short time by shearing work. In this case, neither the surface covering material (11) that constitutes the decorative board for construction (10) nor the vinyl chloride base material (12) has a sharp edge, and its end is beautifully finished.
このことは、当該建築用化粧板（10）を現場に合わせて
さらに小さく切断する場合にも同様である。すなわち、
この建築用化粧板（10）の切断は、鋸を使用した時間の
かかる作業を行なわなくとも、工事用鋏あるいはカッタ
ーナイフ等を使用することによって、短時間内にササク
レが生じないように行なえるものである。This also applies to the case where the architectural decorative board (10) is cut into smaller pieces according to the site. That is,
This construction decorative plate (10) can be cut without using saws in a short time by using construction scissors or a cutter knife, without the need for time-consuming work using a saw. It is a thing.
このような建築用化粧板（10）、及びこれを所定形状に
さらに切断したものは、床面等を構成するために、小さ
な凹凸のあるコンクリート等からなるものの表面に接着
材を使用して直貼りするのであるが、このとき、各建築
用化粧板（10）等は床面等の凹凸を吸収するのである。
すなわち、建築用化粧板（10）の裏面には所定の柔軟性
を有する塩ビ系基材（12）が裏打ちされており、この塩
ビ系基材（12）の表面が床面側となるのであるから、こ
の塩ビ系基材（12）によって床面上の小さな凹凸は吸収
され、当該建築用化粧板（10）の床面に対する直貼りは
空間を形成せず、完全に密着した状態でなされるのであ
る。従って、長時間経過した場合でも、当該建築用化粧
板（10）は剥れ等の問題は生じないのである。Such a decorative board for construction (10), and one that is further cut into a predetermined shape, use an adhesive on the surface of what is made of concrete with small irregularities to form the floor surface, etc. At this time, the decorative boards for construction (10) and the like absorb the irregularities on the floor surface and the like.
That is, the back surface of the architectural decorative board (10) is lined with a vinyl chloride base material (12) having a predetermined flexibility, and the surface of this vinyl chloride base material (12) is the floor side. From this, the PVC base material (12) absorbs small irregularities on the floor surface, and the direct application of the architectural decorative board (10) to the floor surface does not form a space but is in a completely adhered state. Of. Therefore, even if a long time has passed, the problem such as peeling of the architectural decorative board (10) does not occur.
また、この建築用化粧板（10）を使用して構成した床面
においては、この建築用化粧板（10）を構成している表
装材（11）の保護層（11a）が表面に出ており、しかも
この保護層（11a）内には耐摩耗性物質が含有されてい
るから、当該建築用化粧板（10）の上を靴をはいた人が
何回も歩いたとしても、当該建築用化粧板（10）は殆ん
ど摩耗しない。従って、この建築用化粧板（10）は耐久
性に優れたものとなっている。しかも、この建築用化粧
板（10）は、特にその表面が耐摩耗性物質を含有する保
護層（11a）によって構成されているため、耐熱性にも
優れたものとなっているものである。In addition, on the floor surface formed by using this architectural decorative board (10), the protective layer (11a) of the covering material (11) constituting this architectural decorative board (10) is exposed on the surface. Moreover, since the protective layer (11a) contains an abrasion resistant substance, even if a person wearing shoes walks on the architectural decorative board (10) many times, The decorative veneer (10) is hardly worn. Therefore, this architectural decorative board (10) has excellent durability. Moreover, the decorative board for construction (10) has excellent heat resistance because the surface thereof is composed of the protective layer (11a) containing a wear-resistant substance.
そして、この建築用化粧板（10）は、塩ビ系基材（12）
によって裏打ちされているから、この上を歩く人や家具
の移動等によって生ずる振動を十分吸収するものであ
り、騒音を階下へ伝えることはないものである。The architectural decorative board (10) is made of vinyl chloride base material (12).
Since it is lined with, it sufficiently absorbs vibrations caused by people walking on it, movement of furniture, etc., and does not transmit noise to the downstairs.
勿論、この建築用化粧板（10）は、壁面を美麗に仕上げ
る場合にも十分使用可能である。壁面は曲面によって構
成されることもあるが、前述したように、当該建築用化
粧板（10）はそれ自体は、塩ビ系基材（12）によって十
分な柔軟性を有したものとなっているから、壁の曲面に
完全に沿わせた状態で直貼りが可能だからである。Of course, this decorative veneer for construction (10) can be sufficiently used for finishing a wall surface beautifully. The wall surface may be formed of a curved surface, but as described above, the architectural decorative board (10) itself has sufficient flexibility due to the vinyl chloride base material (12). Therefore, it is possible to directly attach the tape along the curved surface of the wall.
（実施例） 次に、本考案を、図面に示した実施例に基づいて詳細に
説明する。(Example) Next, this invention is demonstrated in detail based on the Example shown in drawing.
この建築用化粧板（10）は、第２図に示したように、表
装材（11）に対して塩ビ系基材（12）を接着層（13）等
を使用して一体化したものであり、これら表装材（11）
及び塩ビ系基材（12）として大きな面積を有するものを
採用して形成されるものである。そして、互いに一体化
された大きな面積の表装材（11）及び塩ビ系基材（12）
は、例えば第１図に示したような正方形のタイルとし
て、工場において、たとえば第４図に示すような所謂ト
ムソン刃を備えた打ち抜き装置によって、予じめ定寸に
剪断されて建築用化粧板（10）とされるのである。As shown in FIG. 2, this decorative board for construction (10) is made by integrating a vinyl chloride base material (12) with an adhesive layer (13) and the like to a surface material (11). Yes, these cover materials (11)
And a vinyl chloride base material (12) having a large area. Then, a large-area surface covering material (11) and a vinyl chloride base material (12) integrated with each other.
Is a square tile as shown in FIG. 1, for example, in a factory, for example, by a punching device provided with a so-called Thomson blade as shown in FIG. (10).
建築用化粧板（10）を構成する表装材（11）は、保護層
（11a）、パターン層（11b）及びコア層（11c）を使用
して、第３図に示すようなものとして構成される。すな
わち、本実施例においては、保護層（11a）として、21g
/m2のオーバーレイ紙であって、α−セルロースパルプ
繊維に対して８％の耐摩耗性物質を混入抄造した混抄紙
を採用し、またパターン層（11b）としては、例えば80g
/m2のチタン紙に所定の模様を印刷したものを採用し
た。この場合に使用した耐摩耗性物質は、例えば、18μ
ｍの酸化アルミニウム55％、炭化珪素15％、酸化珪素30
％からなるものであり、その他に炭化バナジウムや炭化
タングステン等の高硬度物質の微粉末が採用される。The covering material (11) constituting the architectural decorative board (10) is constructed as shown in FIG. 3 by using the protective layer (11a), the pattern layer (11b) and the core layer (11c). It That is, in this example, as the protective layer (11a), 21 g
/ m 2 overlay paper, which is a mixed paper in which 8% of abrasion resistant substance is mixed with α-cellulose pulp fiber, and the pattern layer (11b) is, for example, 80 g.
A titanium paper of / m 2 with a predetermined pattern printed was used. The abrasion resistant material used in this case is, for example, 18μ
m aluminum oxide 55%, silicon carbide 15%, silicon oxide 30
%, And fine powders of high hardness substances such as vanadium carbide and tungsten carbide are also used.
そして、保護層（11a）に対して45g/m2、パターン層（1
1b）に対しては80g/m2の量でメラミン樹脂を含浸し、こ
れらを、例えば160g/m2のクラフト紙にフェノール樹脂
溶液を45％含浸させて構成したコア層（11c）に第３図
に示したように積層して、連続プレス等により、50kg/c
m2の圧力で160℃で40秒間一体成型した。And 45g / m 2 to the protective layer (11a), the pattern layer (1
For 1b), a melamine resin was impregnated in an amount of 80 g / m 2 , and the core layer (11c) was formed by impregnating these with, for example, 160 g / m 2 of kraft paper impregnated with 45% of a phenol resin solution. Laminate as shown in the figure, and press 50kg / c by continuous pressing.
It was integrally molded for 40 seconds at 160 ° C. under a pressure of m 2 .
このように形成した表装材（11）は厚さが0.4mmであ
り、これについて、JIS−Ｋ−6902によるテーパー型ア
ブレーザー試験機で摩耗回数を測定したところ、1400回
の値となり、保護層（11a）の光沢及び透明性は全面均
一であった。The surface covering material (11) thus formed had a thickness of 0.4 mm, and the number of times of wear of this was measured with a taper type ablaser tester according to JIS-K-6902. The gloss and transparency of (11a) were uniform over the entire surface.
一方、塩ビ系基材（12）としては、塩化ビニル樹脂に対
して90％以下の充填材を加えて板状のものとして構成し
た。この場合に使用した充填材は、炭酸カルシウム、タ
ルクあるいはクレー等であった。On the other hand, the vinyl chloride base material (12) was made into a plate-like one by adding 90% or less of a filler to a vinyl chloride resin. The filler used in this case was calcium carbonate, talc, clay or the like.
以上のような表装材（11）及び塩ビ系基材（12）を、第
４図に示すような装置にって一体化した。すなわち、ロ
ールに巻き取っておいた表装材（11）に対して順次接着
層（13）となるべき接着剤を塗布して乾燥させ、これに
対して他のロールに巻き取っておいた塩ビ系基剤（12）
をプレスロールにより接着したのである。その後は、所
定形状の建築用化粧板（10）となるべくトムソン刃等に
よる打ち抜き装置によって剪断したのである。The above facing material (11) and the vinyl chloride base material (12) were integrated by an apparatus as shown in FIG. That is, an adhesive that should form the adhesive layer (13) is sequentially applied to the covering material (11) wound on a roll and dried, and the vinyl chloride-based material wound on another roll is used. Base (12)
Was bonded by a press roll. After that, the architectural decorative board (10) having a predetermined shape was sheared by a punching device such as a Thomson blade as much as possible.
なお、接着層（13）となるべき接着剤としては、表装剤
（11）の裏面にロールコーター等で切一塗布が行なえる
ようにするため、耐熱性と耐水性に優れたウレタン系接
着剤等のような二液性タイプの接着剤を使用した。The adhesive that should form the adhesive layer (13) is a urethane adhesive that has excellent heat resistance and water resistance so that the back surface of the surface covering agent (11) can be coated with a roll coater. A two-part type adhesive such as
（考案の効果） 以上説明した通り、本考案においては、表装材を、耐摩
耗性物質を混入した樹脂含浸オーバーレイ紙からなる保
護層、印刷が施された樹脂含浸パターン紙からなるパタ
ーン層および樹脂含浸コアー紙からなるコアー層を、積
層して一体成型した厚み0.6mm以下の積層材にて構成し
た ことにその構成上の特徴があり、これにより、十分な耐
熱性・硬度を有し、施工性にも優れた建築用化粧板（1
0）を安価に提供することができるのである。(Effects of the Invention) As described above, in the present invention, as the covering material, the protective layer made of the resin-impregnated overlay paper mixed with the abrasion resistant substance, the pattern layer made of the printed resin-impregnated pattern paper and the resin are used. A characteristic of the construction is that the core layer made of impregnated core paper is laminated and integrally molded to form a laminated material with a thickness of 0.6 mm or less. Decorative veneer with excellent properties (1
0) can be provided at low cost.
第１図は本考案に係る建築用化粧板を使用した状態を示
す部分斜視図、第２図は建築用化粧板の部分拡大断面
図、第３図は表装材の部分拡大断面図、第４図は表装材
と塩ビ系基材とを一体化する装置の概略側面図である。 符号の説明 10……建築用化粧板、11……表装材、11a……保護層、1
1b……パターン層、11c……コア層、12……塩ビ系基
材、13……接着層。FIG. 1 is a partial perspective view showing a state in which a building decorative board according to the present invention is used, FIG. 2 is a partially enlarged sectional view of a building decorative board, and FIG. 3 is a partially enlarged sectional view of a cover material. The figure is a schematic side view of an apparatus for integrating a cover material and a vinyl chloride base material. Explanation of symbols 10 …… Decorative veneer for construction, 11 …… Surface material, 11a …… Protective layer, 1
1b ... Pattern layer, 11c ... Core layer, 12 ... PVC base material, 13 ... Adhesive layer.
Claims (1)
材とを接着層を介して接着してなる建築用化粧板におい
て、 前記表装材を、耐摩耗性微粉末を混入した樹脂含浸オー
バーレイ紙からなる保護層、印刷が施された樹脂含浸パ
ターン紙からなるパターン層および樹脂含浸コアー紙か
らなるコアー層を積層して一体成型した、厚み0.6mm以
下の積層材にて構成したことを特徴とする建築用化粧
板。1. A decorative board for construction, comprising a vinyl chloride base material having a thickness of 1 mm or more and a covering material bonded together via an adhesive layer, wherein the covering material is impregnated with a resin containing abrasion-resistant fine powder. A protective layer made of overlay paper, a pattern layer made of printed resin-impregnated pattern paper, and a core layer made of resin-impregnated core paper were laminated and integrally molded, and composed of a laminated material having a thickness of 0.6 mm or less. Characteristic architectural veneer.