JPH07278426A - Composition for vulcanizing blend rubber - Google Patents
Composition for vulcanizing blend rubberInfo
- Publication number
- JPH07278426A JPH07278426A JP7555094A JP7555094A JPH07278426A JP H07278426 A JPH07278426 A JP H07278426A JP 7555094 A JP7555094 A JP 7555094A JP 7555094 A JP7555094 A JP 7555094A JP H07278426 A JPH07278426 A JP H07278426A
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- dithiocarbonate
- weight
- epichlorohydrin
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は改善された物性を有する
エピクロルヒドリン系重合体ゴムとハロゲン含有アクリ
ルゴムとのブレンドゴム加硫用組成物に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a blend rubber vulcanizing composition of an epichlorohydrin type polymer rubber having improved physical properties and a halogen-containing acrylic rubber.
【0002】[0002]
【従来の技術】エピクロルヒドリン系ゴムとハロゲン含
有アクリルゴムとのブレンドゴムは従来公知の加硫剤、
例えば2−メルカプトイミダゾリンにより加硫されるこ
とが知られている。この加硫ゴムはハロゲン含有アクリ
ルゴムによる耐熱老化性とエピクロルヒドリン系重合体
ゴムによる耐燃料油性との改善効果を併せ持つことも知
られている。しかしながら、この両者のそれぞれに有効
な加硫剤は通常異なるものであり、両者に共通の加硫剤
であっても互に加硫速度が異なるために、加工上あるい
は加硫後の物性において必ずしも十分な結果が得られて
いない。即ち上記の加硫剤、2−メルカプトイミダゾリ
ンにおいては、ハロゲン含有アクリルゴムの加硫速度が
遅く、このためエピクロルヒドリン系重合体ゴムとのブ
レンドゴムの加硫物は、例えば圧縮永久歪性について満
足な結果が得られていない。2. Description of the Related Art A blend rubber of epichlorohydrin rubber and halogen-containing acrylic rubber is a conventionally known vulcanizing agent,
For example, it is known to be vulcanized by 2-mercaptoimidazoline. It is also known that this vulcanized rubber has both the heat aging resistance due to the halogen-containing acrylic rubber and the fuel oil resistance improvement effect due to the epichlorohydrin-based polymer rubber. However, effective vulcanizing agents for both of them are usually different, and even vulcanizing agents common to both are different in vulcanizing speed from each other. Not enough results have been obtained. That is, in the above-mentioned vulcanizing agent, 2-mercaptoimidazoline, the vulcanization rate of the halogen-containing acrylic rubber is slow, and therefore the vulcanized product of the blended rubber with the epichlorohydrin-based polymer rubber is satisfactory in compression set, for example. No results have been obtained.
【0003】本出願人は先にこのような技術的課題を解
決する目的で、上記ブレンドゴムに対して2,3−ジメ
ルカプトピラジン誘導体もしくは2,3−ジメルカプト
キノキサリン誘導体と受酸剤となる金属化合物、例えば
マグネシア、消石灰、ケイ酸カルシウムのような周期律
表第II族金属の化合物、あるいは周期律表第IVA族金属
の化合物とを含む加硫物性に優れたブレンドゴム加硫用
組成物を提案している(特開昭59−1565号)。し
かしここに例示されている受酸剤を用いた加硫用組成物
は保存中に加硫が進行して粘度が上昇し、賦形が困難に
なる等、保存安定性に難点があり、その改善が望まれて
いた。For the purpose of solving such technical problems, the present applicant has previously used a 2,3-dimercaptopyrazine derivative or 2,3-dimercaptoquinoxaline derivative and an acid acceptor for the above blended rubber. Blend rubber vulcanization composition having excellent vulcanization physical properties, containing a metal compound, for example, a compound of Group II metal of the periodic table such as magnesia, slaked lime, calcium silicate, or a compound of Group IVA metal of the periodic table (Japanese Patent Laid-Open No. 59-1565). However, the vulcanizing composition using the acid acceptor exemplified here has a problem in storage stability such as vulcanization progresses during storage to increase viscosity and makes shaping difficult. Improvement was desired.
【0004】[0004]
【発明が解決しようとする課題】本発明は、上記のよう
に速やかな加硫速度と改善された加硫物性を有するとと
もに、長期の保存安定性に優れたエピクロルヒドリン系
重合体ゴムとハロゲン含有アクリルゴムとのブレンドゴ
ム加硫用組成物を提供することを目的とするものであ
る。DISCLOSURE OF THE INVENTION The present invention has a rapid vulcanization rate and improved vulcanization physical properties as described above, and is superior in long-term storage stability with epichlorohydrin-based polymer rubbers and halogen-containing acrylics. An object of the present invention is to provide a composition for vulcanizing a blended rubber with a rubber.
【0005】[0005]
【課題を解決するための手段】本発明者らは上記ブレン
ドゴムの組成物について鋭意研究の結果、特定の2,3
−ジメルカプトピラジン誘導体もしくは2,3−ジメル
カプトキノキサリン誘導体と金属化合物としてハイドロ
タルサイト類を配合することにより、上述の目的を達成
し得ることを見出し本発明を完成したものである。DISCLOSURE OF THE INVENTION The inventors of the present invention have earnestly studied the composition of the above blended rubber, and as a result, a specific few
The present invention has been completed by finding that the above object can be achieved by blending a dimercaptopyrazine derivative or a 2,3-dimercaptoquinoxaline derivative with hydrotalcites as a metal compound.
【0006】本発明はすなわち、(a)エピクロルヒド
リン系重合体ゴム40〜99重量%、(b)ハロゲン含
有アクリルゴム1〜60重量%とよりなるブレンドゴム
100重量部に対して、(c)下記一般式(I)で表さ
れる2,3−ジメルカプトピラジン誘導体又は下記一般
式(II) で表される2,3−ジメルカプトキノキサリン
誘導体0.1〜10重量部及び(d)ハイドロタルサイ
ト類0.1〜20重量部を含むことを特徴とするブレン
ドゴム加硫用組成物である。The present invention is based on 100 parts by weight of a blend rubber comprising (a) 40 to 99% by weight of epichlorohydrin type polymer rubber and (b) 1 to 60% by weight of a halogen-containing acrylic rubber, and (c) the following: 0.1 to 10 parts by weight of a 2,3-dimercaptopyrazine derivative represented by the general formula (I) or a 2,3-dimercaptoquinoxaline derivative represented by the following general formula (II), and (d) hydrotalcite It is a composition for vulcanizing a blended rubber, characterized in that the composition contains 0.1 to 20 parts by weight.
【0007】[0007]
【化2】 (但し、R1 R2 R3 R4 R5 及びR6は同一でも異な
っていてもよく、水素原子又は炭素数1〜4のアルキル
基を表す)[Chemical 2] (However, R 1 R 2 R 3 R 4 R 5 and R 6 may be the same or different and represent a hydrogen atom or an alkyl group having 1 to 4 carbon atoms.)
【0008】本発明のエピクロルヒドリン系重合体ゴム
とは、エピクロルヒドリン単独重合体ゴムあるいはエピ
クロルヒドリンと他のエポキシドとの共重合体ゴムを総
称し、例えばポリエピクロルヒドリンゴム、エピクロル
ヒドリン−アリルグリシジルエーテル共重合体ゴム、エ
ピクロルヒドリン−エチレンオキシド共重合体ゴム、エ
ピクロルヒドリン−エチレンオキシド−アリルグリシジ
ルエーテル共重合体ゴム等の単独重合体ゴム、二元共重
合体ゴム、三元共重合体ゴムが代表例として挙げられ
る。The epichlorohydrin-based polymer rubber of the present invention is a generic term for epichlorohydrin homopolymer rubber or copolymer rubber of epichlorohydrin and other epoxides, for example, polyepichlorohydrin rubber, epichlorohydrin-allylglycidyl ether copolymer rubber, Typical examples thereof include homopolymer rubbers such as epichlorohydrin-ethylene oxide copolymer rubber and epichlorohydrin-ethylene oxide-allyl glycidyl ether copolymer rubber, binary copolymer rubbers, and ternary copolymer rubbers.
【0009】本発明においてはこれ等の単一ゴムあるい
は2種以上の混合ゴムとして使用される。共重合体ゴム
の場合、その構成成分であるエピクロルヒドリンが20
〜99モル%で他のエポキシドが1〜80モル%のもの
が加硫物の物性上好ましい。例えば上記のエピクロルヒ
ドリン−アリルグリシジルエーテル共重合体ゴムにおい
てはエピクロルヒドリン80〜99モル%、アリルグリ
シジルエーテル1〜20モル%のゴム、エピクロルヒド
リン−エチレンオキシド共重合体ゴムおいては、エピク
ロルヒドリン25〜90モル%、エチレンオキシド10
〜75モル%のゴム、エピクロルヒドリン−エチレンオ
キシド−アリルグリシジルエーテル共重合体ゴムにおい
ては、エピクロルヒドリン24〜80モル%、エチレン
オキシド19〜75モル%、アリルグリシジルエーテル
1〜20モル%のゴムがそれぞれ好ましく用いられる。
またその分子量は、ムーニー粘度表示によって通常用い
られるM1+4 100℃ 30〜150程度のものがその
まま用いられる。In the present invention, these single rubbers or mixed rubbers of two or more kinds are used. In the case of a copolymer rubber, its constituent component, epichlorohydrin, is 20
It is preferable that the vulcanizate has a physical property of ˜99 mol% and other epoxide of 1 to 80 mol%. For example, in the above epichlorohydrin-allyl glycidyl ether copolymer rubber, epichlorohydrin 80 to 99 mol%, allyl glycidyl ether 1 to 20 mol% rubber, and epichlorohydrin-ethylene oxide copolymer rubber, epichlorohydrin 25 to 90 mol%, Ethylene oxide 10
In the rubber of 75 mol% to epichlorohydrin-ethylene oxide-allyl glycidyl ether copolymer, the rubber of 24 to 80 mol% of epichlorohydrin, 19 to 75 mol% of ethylene oxide, and 1 to 20 mol% of allyl glycidyl ether are preferably used. .
The molecular weight of M 1 + 4 100 ° C. of about 30 to 150, which is usually used according to the Mooney viscosity display, is used as it is.
【0010】本発明において用いられるハロゲン含有ア
クリルゴムは、アクリル酸エステル系単量体40〜9
9.9重量%、加硫成分としてのハロゲン含有単量体1
0〜0.1重量%及びこれ等の単量体と共重合可能な少
なくとも1種の他の単量体30〜0重量%よりなる共重
合体である。アクリル酸エステル系単量体としては、ア
ルキルアクリレート、アルコキシアクリレート、アルキ
ルチオアルキルアクリレート、シアノアルキルアクリレ
ート等がある。これ等を具体的に例示すれば、エチルア
クリレート、ブチルアクリレート、メトキシエチルアク
リレート、エトキシエチルアクリレート、エチルチオエ
チルアクリレート等を挙げることができる。ハロゲン含
有単量体としてはビニルクロロアセテート、アリルクロ
ロアセテート、2−クロロエチルアクリレート、2−ク
ロロエチルビニルエーテル、5−クロロメチル−2−ノ
ルボルネン、5−クロロアセトキシメチル−2−ノルボ
ルネン等がある。共重合可能な他の単量体としては、ア
クリロニトリル、メタクリロニトリル、スチレン、α−
メチルスチレン、イソブチレン、アクリルアミド、酢酸
ビニル、塩化ビニリデン等のビニル化合物あるいはビニ
リデン化合物、ジビニルベンゼン、ジアリルフタレー
ト、アルキレングリコールジアクリレート、アルキレン
グリコールジメタクリレート、トリメチロールプロパン
トリアクリレート等のポリエン化合物がある。またその
分子量はムーニー粘度表示によって通常用いられるML
1+4 100℃ 20〜100程度のものがそのまま用い
られる。The halogen-containing acrylic rubber used in the present invention is an acrylic ester monomer 40 to 9
9.9% by weight, a halogen-containing monomer 1 as a vulcanizing component
It is a copolymer comprising 0 to 0.1% by weight and 30 to 0% by weight of at least one other monomer copolymerizable with these monomers. Examples of the acrylic acid ester-based monomer include alkyl acrylate, alkoxy acrylate, alkylthioalkyl acrylate, and cyanoalkyl acrylate. Specific examples of these include ethyl acrylate, butyl acrylate, methoxyethyl acrylate, ethoxyethyl acrylate, and ethylthioethyl acrylate. Examples of the halogen-containing monomer include vinyl chloroacetate, allyl chloroacetate, 2-chloroethyl acrylate, 2-chloroethyl vinyl ether, 5-chloromethyl-2-norbornene and 5-chloroacetoxymethyl-2-norbornene. Other copolymerizable monomers include acrylonitrile, methacrylonitrile, styrene, α-
There are vinyl compounds such as methylstyrene, isobutylene, acrylamide, vinyl acetate, and vinylidene chloride or vinylidene compounds, and polyene compounds such as divinylbenzene, diallyl phthalate, alkylene glycol diacrylate, alkylene glycol dimethacrylate, and trimethylolpropane triacrylate. Moreover, the molecular weight is ML which is usually used by the Mooney viscosity display.
1 + 4 100 ° C. A temperature of about 20 to 100 is used as it is.
【0011】本発明組成物におけるブレンドゴムのブレ
ンド割合は、エピクロルヒドリン系重合体ゴム40〜9
9重量%、ハロゲン含有アクリルゴム1〜60重量%で
あり、好ましくは前者が45〜95重量%、後者が55
〜5重量%の範囲である。エピクロルヒドリン系重合体
ゴムが上記範囲未満であれば組成物の加硫速度が低下
し、一方ハロゲン含有アクリルゴムが上記範囲未満であ
れば加硫物の耐熱性の改良を実質的に望みえない。The blend ratio of the blended rubber in the composition of the present invention is such that epichlorohydrin type polymer rubbers 40 to 9 are used.
9% by weight, 1-60% by weight of halogen-containing acrylic rubber, preferably 45-95% by weight of the former and 55% by weight of the latter.
Is in the range of up to 5% by weight. When the epichlorohydrin-based polymer rubber is less than the above range, the vulcanization rate of the composition is lowered, while when the halogen-containing acrylic rubber is less than the above range, improvement in heat resistance of the vulcanized product cannot be substantially expected.
【0012】本発明組成物の一般式(I)で表される
2,3−ジメルカプトピラジン誘導体を例示すると、ピ
ラジン−2,3−ジチオカーボネート、5−エチルピラ
ジン−2,3−ジチオカーボネート、5,6−ジメチル
ピラジン−2,3−ジチオカーボネート、5−n−ブチ
ルピラジン−2,3−ジチオカーボネート等が挙げられ
る。また一般式(II)で表される2,3−ジメルカプト
キノキサリン誘導体を例示するとキノキサリン−2,3
−ジチオカーボネート、6−メチルキノキサリン−2,
3−ジチオカーボネート、6−イソプロピルキノキサリ
ン−2,3−ジチオカーボネート、5,8−ジメチルキ
ノキサリン−2,3−ジチオカーボネート等が挙げられ
る。この中特に6−メチルキノキサリン−2,3−ジチ
オカーボネートが好ましい。一般式(I)又は一般式
(II)で表される加硫剤の配合量はブレンドゴムの合計
量100重量部に対して0.1〜10重量部、好ましく
は0.5〜5重量部用いられる。配合量がこの範囲未満
では加硫速度が低下し、一方この範囲を越えると得られ
た加硫物が剛直になり過ぎてゴム加硫物に通常期待され
る物性が得られなくなる。Examples of the 2,3-dimercaptopyrazine derivative represented by the general formula (I) of the composition of the present invention include pyrazine-2,3-dithiocarbonate, 5-ethylpyrazine-2,3-dithiocarbonate, Examples thereof include 5,6-dimethylpyrazine-2,3-dithiocarbonate and 5-n-butylpyrazine-2,3-dithiocarbonate. Further, exemplifying a 2,3-dimercaptoquinoxaline derivative represented by the general formula (II) is quinoxaline-2,3.
-Dithiocarbonate, 6-methylquinoxaline-2,
Examples thereof include 3-dithiocarbonate, 6-isopropylquinoxaline-2,3-dithiocarbonate and 5,8-dimethylquinoxaline-2,3-dithiocarbonate. Of these, 6-methylquinoxaline-2,3-dithiocarbonate is particularly preferable. The compounding amount of the vulcanizing agent represented by the general formula (I) or the general formula (II) is 0.1 to 10 parts by weight, preferably 0.5 to 5 parts by weight, based on 100 parts by weight of the total amount of the blended rubber. Used. If the compounding amount is less than this range, the vulcanization rate will decrease, while if it exceeds this range, the vulcanizate obtained will be too rigid and the properties normally expected of rubber vulcanizates will not be obtained.
【0013】本発明に用いられる(c)成分のハイドロ
タルサイト類は、下記一般式(III) Mgx Aly (OH)2x+3y-2 CO3 ・wH2 O (III) (但しxは1〜10、yは1〜5、wは実数を表す)で
示される。これ等の化合物を例示すれば、Mg4.5 Al
2 (OH)13CO3 ・3.5H2 O、Mg4.5 Al
2 (OH)13CO3 、Mg4 Al2 (OH)12CO 3 ・
3.5H2 O、Mg6 Al2 (OH)16CO3 ・4H2
O、Mg5 Al2 (OH)14CO3 ・4H2 O、Mg3
Al2 (OH)10CO3 ・1.7H2 O等を挙げること
ができる。Hydro of the component (c) used in the present invention
The talcites are represented by the following general formula (III) MgxAly(OH)2x + 3y-2CO3・ WH2O (III) (where x is 1 to 10, y is 1 to 5, and w is a real number)
Shown. Examples of these compounds include Mg4.5Al
2(OH)13CO3・ 3.5H2O, Mg4.5Al
2(OH)13CO3, MgFourAl2(OH)12CO 3・
3.5H2O, Mg6Al2(OH)16CO3・ 4H2
O, MgFiveAl2(OH)14CO3・ 4H2O, Mg3
Al2(OH)TenCO3・ 1.7H2To list O etc.
You can
【0014】これ等のハイドロタルサイト類は、本発明
組成物のブレンドゴムの合計量100重量部に対して
0.1〜20重量部、好ましくは1〜10重量部の範囲
で用いられる。この範囲の量未満では本発明の目的とす
る速やかな加硫速度と良好な保存安定性を共に達成する
ことが困難であり、またこの範囲を超えても特に効果が
増大することはない。These hydrotalcites are used in an amount of 0.1 to 20 parts by weight, preferably 1 to 10 parts by weight, based on 100 parts by weight of the total blend rubber of the composition of the present invention. If the amount is less than this range, it is difficult to achieve both the rapid vulcanization rate and good storage stability aimed at by the present invention, and if the amount exceeds this range, the effect is not particularly increased.
【0015】このようなハイドロタルサイト類は耐水性
の良好なハロゲン含有エラストマーを与える受酸剤とし
て公知である(特開昭57−151652号公報)。ま
た塩素化ポリエチレンを有機過酸化物等により加硫を行
なう際、ハイドロタルサイト類を配合して耐熱性を向上
させる事も知られている(特開昭62−7754号公
報、特開昭62−7755号公報等)。しかしながらハ
イドロタルサイト類と特定の加硫剤である2,3−ジメ
ルカプトピラジン誘導体又は2,3−ジメルカプトキノ
キサリン誘導体とを組合せることによってエピクロルヒ
ドリン系重合体ゴムとハロゲン含有アクリルゴムとのブ
レンドゴム加硫用組成物の保存安定性が改善されること
については全く開示されていない。Such hydrotalcites are known as an acid acceptor which gives a halogen-containing elastomer having good water resistance (JP-A-57-151652). It is also known that when chlorinated polyethylene is vulcanized with an organic peroxide or the like, it is blended with hydrotalcites to improve heat resistance (Japanese Patent Laid-Open No. 62-7754, Japanese Patent Laid-Open No. 62-7544). -7755). However, by blending hydrotalcites with a specific vulcanizing agent, a 2,3-dimercaptopyrazine derivative or a 2,3-dimercaptoquinoxaline derivative, a blend rubber of an epichlorohydrin-based polymer rubber and a halogen-containing acrylic rubber No mention is made of an improvement in the storage stability of the vulcanizing composition.
【0016】本発明加硫用組成物において、加硫速度の
調整、加硫物の熱安定性の見地から受酸剤となる金属化
合物を更に用いることもできる。それ等の化合物には周
期律表第II族金属の酸化物、水酸化物、炭酸塩、カルボ
ン酸塩、ケイ酸塩、ホウ酸塩、亜燐酸塩、周期律表第IV
A族金属の酸化物、塩基性炭酸塩、塩基性カルボン酸
塩、塩基性亜燐酸塩、塩基性亜硫酸塩、三塩基性硫酸塩
等がある。具体的な例としては、マグネシア、水酸化マ
グネシウム、水酸化バリウム、炭酸マグネシウム、炭酸
バリウム、生石灰、消石灰、炭酸カルシウム、ケイ酸カ
ルシウム、ステアリン酸カルシウム、ステアリン酸亜
鉛、フタル酸カルシウム、亜燐酸カルシウム、亜鉛華、
酸化錫、リサージ、鉛丹、鉛白、二塩基性フタル酸鉛、
二塩基性炭酸鉛、ステアリン酸錫、塩基性亜燐酸鉛、塩
基性亜燐酸錫、塩基性亜硫酸鉛、三塩基性硫酸鉛等を挙
げることができる。また本発明の組成物には、上記の他
に当該技術分野で行われる各種の老化防止剤、充填剤、
補強剤、可塑剤、加工助剤、顔料、難燃剤等を任意に配
合できる。In the composition for vulcanization of the present invention, a metal compound serving as an acid acceptor can be further used from the viewpoint of adjusting the vulcanization rate and the thermal stability of the vulcanized product. Such compounds include oxides, hydroxides, carbonates, carboxylates, silicates, borates, phosphites of Group II metals of the periodic table, Group IV of the periodic table.
Examples include Group A metal oxides, basic carbonates, basic carboxylates, basic phosphites, basic sulfites, and tribasic sulfates. Specific examples include magnesia, magnesium hydroxide, barium hydroxide, magnesium carbonate, barium carbonate, quicklime, slaked lime, calcium carbonate, calcium silicate, calcium stearate, zinc stearate, calcium phthalate, calcium phosphite, zinc. flower,
Tin oxide, litharge, red lead, white lead, dibasic lead phthalate,
Examples thereof include dibasic lead carbonate, tin stearate, basic lead phosphite, basic tin phosphite, basic lead sulfite, and tribasic lead sulfate. Further, the composition of the present invention, in addition to the above, various anti-aging agents, fillers, which are performed in the art
Reinforcing agents, plasticizers, processing aids, pigments, flame retardants and the like can be optionally mixed.
【0017】また加硫速度を調整する目的で公知の加硫
促進剤、加硫遅延剤を配合することは有効である。これ
等加硫促進剤の例としては、硫黄、チウラムスルフィド
類、モルホリンポリスルフィド類、アミン類、アミンの
弱酸塩類、塩基性シリカ、四級アンモニウム塩類、四級
ホスホニウム塩類等を挙げることができる。一方、加硫
遅延剤としては、N−シクロヘキシルチオフタルイミド
等を挙げることができる。Further, it is effective to add known vulcanization accelerators and vulcanization retarders for the purpose of adjusting the vulcanization rate. Examples of these vulcanization accelerators include sulfur, thiuram sulfides, morpholine polysulfides, amines, weak acid salts of amines, basic silica, quaternary ammonium salts, and quaternary phosphonium salts. On the other hand, examples of the vulcanization retarder include N-cyclohexylthiophthalimide and the like.
【0018】本発明組成物の配合方法としては、従来ポ
リマー加工の分野において利用されている任意の手段、
例えばミキシングロール、バンバリーミキサー、各種ニ
ーダー類等を利用することができる。本発明の組成物
は、通常100〜200℃に加熱することで加硫物とす
ることができる。加硫時間は温度によって異なるが0.
5〜300分の間で行われるのが普通である。加硫成型
の方法としては、金型による圧縮成型、射出成型、スチ
ーム缶、エアーバス、赤外線あるいはマイクロウエーブ
による加熱等任意の方法を用いることができる。As a method for compounding the composition of the present invention, any means conventionally used in the field of polymer processing,
For example, a mixing roll, a Banbury mixer, various kneaders, etc. can be used. The composition of the present invention can be usually made into a vulcanized product by heating at 100 to 200 ° C. The vulcanization time varies depending on the temperature, but is 0.
It is usually performed for 5 to 300 minutes. As the vulcanization molding method, any method such as compression molding with a mold, injection molding, steam can, air bath, heating with infrared rays or microwave can be used.
【0019】[0019]
【実施例】以下、本発明を実施例、比較例により具体的
に説明する。 実施例1〜7、比較例1〜5 第1表に示す各配合物を60〜70℃のオープンロール
で混練し、その保存安定性を第2表に示す。また各配合
物のシート化したものを混練直後に金型に入れ、170
℃、80kg/cm2 で15分間加圧成型を行った。得
られた各加硫物の物性試験を行い、その結果を第3表に
示す。また実施例1、3、6及び比較例1、2、3の配
合物の加硫曲線を、混練直後にJSRキュラストメータ
ーIII 型を用いて、振幅角3°、170℃で測定し、そ
の結果を図1〜3に示す。EXAMPLES The present invention will be specifically described below with reference to examples and comparative examples. Examples 1 to 7 and Comparative Examples 1 to 5 Each compound shown in Table 1 was kneaded with an open roll at 60 to 70 ° C, and its storage stability is shown in Table 2. Also, the sheeted product of each compound is put into a mold immediately after kneading, and 170
Pressure molding was carried out at 80 ° C. and 80 kg / cm 2 for 15 minutes. The physical properties of the obtained vulcanizates were tested, and the results are shown in Table 3. The vulcanization curves of the blends of Examples 1, 3, 6 and Comparative Examples 1, 2, 3 were measured immediately after kneading using a JSR curlastometer type III at an amplitude angle of 3 ° and 170 ° C. The results are shown in FIGS.
【0020】[0020]
【表1】 [Table 1]
【0021】[0021]
【表2】 [Table 2]
【0022】第1表において *1 「エピクロマーH」(商品名 ダイソー社製、M
L1+4 100℃ 50) *2 「エピクロマーC」(商品名 ダイソー社製、エ
ピクロルヒドリン/エチレンオキシド(50/50モル
比)共重合体、ML1+4 100℃ 65) *3 「エピクロマーCG−104」(商品名 ダイソ
ー社製、エピクロルヒドリン/エチレンオキシド/アク
リルグリシジルエーテル(63/34/3モル比)共重
合体、ML1+4 100℃ 65) *4 エチルアクリレート/ビニルクロロアセテート、
97/3重量比、ML1+4 100℃ 55 *5 エチルアクリレート/ブチルアクリレート/メト
キシエチルアクリレート/2−クロロエチルビニルエー
テル、60/20/15/5重量比 ML1+4 100℃ 35 *6 「カープレックス#1120」(商品名 塩野義
製薬社製) *7 Mg4.5 Al2 (OH)13CO3 ・3.5H2 O *8 Mg4.5 Al2 (OH)13CO3 *9 Mg6 Al2 (OH)16CO3 ・4H2 O *10 1,8−ジアザビシクロ(5,4,0)ウンデ
セン−7In Table 1, * 1 "Epichromer H" (trade name, manufactured by Daiso Co., Ltd., M
L 1 + 4 100 ° C. 50) * 2 “Epichromer C” (trade name, manufactured by Daiso Co., epichlorohydrin / ethylene oxide (50/50 molar ratio) copolymer, ML 1 + 4 100 ° C. 65) * 3 “Epichromer CG-104 (Trade name, manufactured by Daiso, epichlorohydrin / ethylene oxide / acrylic glycidyl ether (63/34/3 molar ratio) copolymer, ML 1 + 4 100 ° C. 65) * 4 Ethyl acrylate / vinyl chloroacetate,
97/3 weight ratio, ML 1 + 4 100 ℃ 55 * 5 ethyl acrylate / butyl acrylate / methoxyethyl acrylate / 2-chloroethyl vinyl ether, 60/20/15/5 by weight ratio ML 1 + 4 100 ℃ 35 * 6 " Carplex # 1120 "(trade name, manufactured by Shionogi & Co., Ltd.) * 7 Mg 4.5 Al 2 ( OH) 13 CO 3 · 3.5H 2 O * 8 Mg 4.5 Al 2 (OH) 13 CO 3 * 9 Mg 6 Al 2 (OH) 16 CO 3 · 4H 2 O * 10 1,8- diazabicyclo (5,4,0) undecene-7
【0023】[0023]
【表3】 [Table 3]
【0024】[0024]
【表4】 [Table 4]
【0025】[0025]
【表5】 [Table 5]
【0026】以上の表において各実施例はハイドロタル
サイト類を配合しない例(比較例1)、及びハイドロタ
ルサイト類を配合せず本発明と異なる加硫剤を使用した
例(比較例2)と比べて、第2表に示すように保存安定
性が大幅に改善されていることが判る。ハイドロタルサ
イト類と本発明と異なる加硫剤とを組合せた配合例(比
較例3)は、図1、2に示すように各実施例と比べ加硫
速度が著しく遅れている。ハロゲン含有アクリルゴムを
含まないエピクロルヒドリン系ゴムを使用した例(比較
例4)は耐熱老化性が悪く、またブレンドゴム比が本発
明範囲外である例(比較例5)は、加硫速度が遅いため
引張強さ、圧縮永久歪が低下しまた耐油性も劣る。In the above table, each Example is an example in which no hydrotalcites are blended (Comparative Example 1), and an example in which no hydrotalcites are blended and a vulcanizing agent different from the present invention is used (Comparative Example 2). It can be seen that the storage stability is significantly improved as shown in Table 2 in comparison with. As shown in FIGS. 1 and 2, the compounding example (comparative example 3) in which hydrotalcites and a vulcanizing agent different from the present invention were combined had a significantly slower vulcanization rate than the respective examples. An example using an epichlorohydrin-based rubber not containing a halogen-containing acrylic rubber (Comparative Example 4) has poor heat aging resistance, and an example in which the blend rubber ratio is outside the range of the present invention (Comparative Example 5) has a slow vulcanization rate. Therefore, the tensile strength and compression set are lowered, and the oil resistance is also poor.
【0027】[0027]
【発明の効果】本発明によれば、速やかな加硫速度と改
善された加硫物性とともに長期の保存安定性に優れたエ
ピクロルヒドリン系重合体ゴムとハロゲン含有アクリル
ゴムとのブレンドゴム加硫用組成物が得られる。INDUSTRIAL APPLICABILITY According to the present invention, a blend rubber vulcanizing composition of a blend rubber of an epichlorohydrin-based polymer rubber and a halogen-containing acrylic rubber, which is excellent in rapid vulcanization rate, improved vulcanization physical properties and long-term storage stability. The thing is obtained.
【図1】実施例1、3、6における組成物の混練直後の
加硫曲線である。FIG. 1 is a vulcanization curve immediately after kneading of the compositions in Examples 1, 3, and 6.
【図2】比較例1〜3における組成物の混練直後の加硫
曲線である。FIG. 2 is a vulcanization curve immediately after kneading the compositions in Comparative Examples 1 to 3.
Claims (5)
40〜99重量%、(b)ハロゲン含有アクリルゴム1
〜60重量%よりなるブレンドゴム100重量部に対し
て、(c)下記一般式(I)で表される2,3−ジメル
カプトピラジン誘導体又は下記一般式(II)で表される
2,3−ジメルカプトキノキサリン誘導体0.1〜10
重量部及び(d)ハイドロタルサイト類0.1〜20重
量部を含むことを特徴とするブレンドゴム加硫用組成
物。 【化1】 (但し、R1 R2 R3 R4 R5 及びR6 は同一でも異な
っていてもよく、水素原子又は炭素数1〜4のアルキル
基を表す)1. An (a) epichlorohydrin-based polymer rubber 40 to 99% by weight, and (b) a halogen-containing acrylic rubber 1
To 100 parts by weight of the blended rubber consisting of 60 to 60% by weight, (c) 2,3-dimercaptopyrazine derivative represented by the following general formula (I) or 2,3 represented by the following general formula (II). -Dimercaptoquinoxaline derivative 0.1-10
A blend rubber vulcanizing composition, characterized in that it comprises 0.1 part by weight and (d) 0.1 to 20 parts by weight of hydrotalcites. [Chemical 1] (However, R 1 R 2 R 3 R 4 R 5 and R 6 may be the same or different and represent a hydrogen atom or an alkyl group having 1 to 4 carbon atoms.)
ピラジン−2,3−ジチオカーボネート、5−エチルピ
ラジン−2,3−ジチオカーボネート、5,6−ジメチ
ルピラジン−2,3−ジチオカーボネート、5−n−ブ
チルピラジン−2,3−ジチオカーボネートの少なくと
も1種である請求項1に記載の加硫用組成物。2. The 2,3-dimercaptopyrazine derivative is pyrazine-2,3-dithiocarbonate, 5-ethylpyrazine-2,3-dithiocarbonate, 5,6-dimethylpyrazine-2,3-dithiocarbonate, 5 The vulcanizing composition according to claim 1, which is at least one of -n-butylpyrazine-2,3-dithiocarbonate.
体がキノキサリン−2,3−ジチオカーボネート、6−
メチルキノキサリン−2,3−ジチオカーボネート、6
−イソプロピルキノキサリン−2,3−ジチオカーボネ
ート、5,8−ジメチルキノキサリン−2,3−ジチオ
カーボネートの少なくとも1種である請求項1に記載の
加硫用組成物。3. The 2,3-dimercaptoquinoxaline derivative is quinoxaline-2,3-dithiocarbonate, 6-.
Methylquinoxaline-2,3-dithiocarbonate, 6
-The vulcanizing composition according to claim 1, which is at least one of isopropylquinoxaline-2,3-dithiocarbonate and 5,8-dimethylquinoxaline-2,3-dithiocarbonate.
体が6−メチルキノキサリン−2,3−ジチオカーボネ
ートである請求項1に記載の加硫用組成物。4. The vulcanizing composition according to claim 1, wherein the 2,3-dimercaptoquinoxaline derivative is 6-methylquinoxaline-2,3-dithiocarbonate.
I) Mgx Aly (OH)2x+3y-2 CO3 ・wH2 O (III) (但し、xは1〜10、yは1〜5、wは実数を表す)
で表される請求項1〜4のいずれかに記載の加硫用組成
物。5. A hydrotalcite compound represented by the following general formula (II
I) Mg x Al y (OH ) 2x + 3y-2 CO 3 · wH 2 O (III) ( where, x is 1 to 10, y is 1 to 5, w represents a real number)
The vulcanizing composition according to any one of claims 1 to 4, represented by: