JPH07134228A - Two-groove spiral slot and its production - Google Patents

Abstract

PURPOSE:To provide a process for production of two-groove spiral slots having a groove size and spiral pitch stable over a long period of time. CONSTITUTION:A tensile wire is set at a rotary supplying machine 10 and is supplied to a extruder 14 while applying tension on the wire by a powder clutch 12 and rotating and twisting (in the same direction as the direction of the twists applied in a second stage) the wire. Next, a PC/PBT resin is extruded in a molten state on the outer periphery of the tension wire to coat the wire with this resin. The resin is cooled to solidify in a cooling tank 16 and while straight housing grooves are being sized by a sizing key 18, the tensile wire is taken off by a take-off machine 20. Next, the resulted molding is introduced into a heat treating furnace 22 and is passed through a furnace 22 to heat and soften the PC/PBT resin. Thereafter, the tensile wire is supplied to a sizing device 26 via a rotation preventive guide 24 having a projection engaging with the grooves. The device 26 is used to size the groove while rotating by engaging with the spiral housing grooves formed according to the twists applied by a rotary take-off machine 28. The straight square housing grooves of the slots are made to be spiral, fixed and sized under cooling in the device 26.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing an optical fiber carrying slot having a highly accurate housing groove suitable for housing and carrying an optical fiber tape or the like. A method of making a twisted two-groove spiral slot that rotates about a long axis.

[0002]

2. Description of the Related Art Optical fiber cables are currently used as subscriber cables for public communications, and are expected to be further used as cables to be connected to homes in the future. It is said that an ultrahigh-density optical fiber cable, which is much higher in density than the current one, is required for use in such applications.

In such an ultra high density optical fiber cable, it is desirable to use a multifilament tape core wire arranged in a high density. For example, in Japanese Patent Laid-Open No. 143710/1992, a multifilamentary tape core wire is used. There is disclosed a slot provided with a concave groove for accommodating and carrying the stepwise. By the way, when a tape core wire of this kind is used to form a cable, the cross-sectional area A of the groove for accommodating this and the cross-sectional area B of the slot body are
It is desirable to use slots such that A / (A + B)> 30%. At this time, the optimum slot shape is a rectangle (hereinafter referred to as a square groove).

Further, when a spiral twist is applied to the groove for accommodating the optical fiber, the tension applied to the optical fiber becomes uniform when the slot is bent, which is advantageous in that the transmission loss is small. Occurs. Such slots are used by gathering them in a state in which they are twisted together with high density around separately made tension members, or because the groove has a spiral shape, it can be used alone as an optical cable.

As a method of manufacturing such a slot,
Extrusion molding of thermoplastic resin is generally adopted,
There were two problems described below. That is, the first problem is that the size of the square groove in which the optical fiber is housed is required to be highly accurate, and moreover, it is necessary to secure this over the entire length of the slot. The second problem is that the groove is formed in a spiral shape.

In particular, in the second problem, in the conventional manufacturing method, when melt-extruding, the die corresponding to the target sectional shape of the slot is extruded while rotating,
A method of forming a spiral groove and then cooling and solidifying is adopted. However, in such a conventional manufacturing method, since the die is rotated, the apparatus becomes complicated,
Further, since the molten resin is extruded while rotating, it is necessary to design the die in consideration of its melt viscoelasticity,
Furthermore, there is a limit to the resin that can be used in terms of the heat resistance of the packing of the rotating and sliding parts, and furthermore, even if a die with such a design is used for molding, the groove shape can still be completely deformed. It had a built-in problem such as being unable to suppress it.

In this case, in particular, the concave groove is formed by dividing the upper and lower sides of the slot body, and the ratio of the cross-sectional area occupied by the groove portion is very large, and the total of the two groove depths is the outer height of the slot. It was very difficult to obtain a stable spiral groove in a slot having a deep groove such as / 3 or more. Therefore, the applicant of the present invention proposes a method for manufacturing a two-groove spiral slot having a new structure in order to solve such a problem.
It has already been proposed in No. 12072. In the manufacturing method according to this proposal, first, a molded product having a linear groove is formed in the first step, and in the subsequent second step, the linear groove is twisted into a spiral shape. I am trying. However, according to subsequent studies, the manufacturing method according to this proposal also has the technical problems described below.

[0008]

That is, in the method of manufacturing a two-groove spiral slot according to the above application, the two-groove spiral slot is manufactured without twisting the tension member in advance. However, in such a manufacturing method, when the first and second steps are continuously performed,
In any of these cases, the final product tension members are twisted.

When the twist applied to the tension member is within the elastic limit of the tension member,
A force that elastically twists back acts, and so-called springback occurs even if the plastic deformation region is reached beyond the elastic limit. These forces act in the opposite direction to untwist the helix applied to the slot body. Therefore, when the tension wound around the bobbin is released, tensile tension is applied to the slot, partial heat is applied to the slot, and the resin is softened, the spiral pitch varies.

Furthermore, if the tension member is twisted and wound on a bobbin and stored for a long period of time, the spiral pitch may change. When such a spiral pitch fluctuates, when rewinding and inserting the optical fiber tape core wire into the groove, it becomes difficult to insert the core wire and local transmission loss may increase. found.

The present invention has been made in view of the above-mentioned conventional problems, and an object of the present invention is to provide a two-groove spiral slot in which the spiral pitch does not change even when it is stored for a long period of time. It is to provide a manufacturing method.

[0012]

In order to achieve the above object, the present invention comprises a tension member and a main body made of thermoplastic resin, and two spiral grooves for accommodating and carrying an optical fiber tape core wire and the like. In the method for manufacturing the two-groove spiral slot provided in the main body portion, after the thermoplastic resin is extruded around the tension member, the storage groove is cooled at a temperature lower than the melting point and extends linearly in the longitudinal direction. And a first step of forming a molded product having, the molded product above the softening point of the thermoplastic resin, is twisted around a major axis in a temperature range of less than the melting point to impart twist, and then cooled and solidified to A second step of forming a storage groove in a spiral shape, and when the first and second steps are continuously performed, when the tension member is supplied in the first step, in the second step With Characterized in that the addition of twist of twisting the same direction.

As another invention, a two-groove having a tension member and a main body made of thermoplastic resin, and two spiral grooves for accommodating and carrying an optical fiber tape core wire and the like are provided in the main body. In the method of manufacturing a spiral slot, the first step of forming a molded product having a storage groove extending linearly in the longitudinal direction by extruding the thermoplastic resin around the tension member and then cooling at a temperature lower than the melting point. And, after this molded article is twisted around a long axis in a temperature range of the softening point of the thermoplastic resin or higher and lower than the melting point, it is cooled and solidified to form the storage groove in a spiral shape. When the tension member is supplied in the first step when the first and second steps are performed separately, a twist in a direction opposite to the twist applied in the second step is applied. And wherein the Rukoto.

The tension member in the present invention means
High-strength, high-modulus organic fiber (aromatic polyamide, aromatic polyester, polyamide, polyester, vinylon), inorganic fiber (glass fiber, carbon fiber, ceramic fiber, metal fiber), and their aggregates (fiber bundle, A twisted structure, a braid, etc.), and a FRP / FRTP filament, a thin metal wire, a metal wire assembly, etc., which uses the above-mentioned fibers and fiber assemblies as reinforcing fibers A member that receives a tension applied to the slot body during manufacturing, when the slots are assembled into a cable, when the cable is laid, or when the cable is used.

The arrangement and configuration of the tension members in the slot main body should be taken into consideration the tension applied to the slot main body when the slots are manufactured, when the slots are assembled into a cable, when the cables are laid, or when the cables are used. And set it. Further, the thermoplastic resin that can be used in the present invention is selected from various crystalline thermoplastic resins according to the performance required as an optical fiber carrying slot, for example, various polyethylene and various nylon, various polypropylene, etc. Among them, the low temperature embrittlement temperature is −40 ° C. or lower, and the flexural modulus at room temperature is 100.
A resin of kg / mm ² or more is preferable, and in addition to high density polyethylene, nylon 12, PBT (polyethylene butylene terephthalate), etc., these crystalline thermoplastic resins and A
Polymer alloys with non-crystalline thermoplastic resins such as BS and PC are recommended.

The softening point of the resin in the present invention means
It refers to the value measured by the JIS K7207 B method.
When a polymer alloy is selected as the thermoplastic resin of the present invention, it is generally very difficult to define the melting point and softening point of the amorphous thermoplastic resin, but in the present invention,
Since the amorphous and crystalline thermoplastic resins are mixed and used, the melting point or softening point is substantially that of the crystalline thermoplastic resin.

In the first step of the present invention, when the first and second steps are continuously performed, the tension member is supplied while being twisted in the same direction as the twist imparted in the second step, and When the first step and the second step are performed separately, the tension member is supplied while being twisted in the direction opposite to the twist applied in the second step, and a thermoplastic resin is desired around the tension member. After extruding into a cross-sectional shape, it is cooled at a temperature below the melting point to obtain a molded product having a linear storage groove.

At this time, if necessary, a method of sizing while cooling, a method of cooling and solidifying below the softening point, and a method of sizing while cooling and solidifying below the softening point can be selected. In the second step, the molded product having the linear storage groove obtained in the first step is twisted by rotating around the major axis while maintaining the temperature condition of the softening point of the thermoplastic resin or higher and lower than the melting point. And then solidified by cooling to form the storage groove in a spiral shape.

In this second step, the thermoplastic resin is heated before the twist is added, while the twist is added, or after the twist is added, and the twist is fixed by heat shaping to a temperature at least near the softening point. To obtain a slot with a predetermined spiral pitch. It should be noted that, if necessary, if the groove is sized at an appropriate position in the second step of forming the twist, the dimension and shape of the groove become uniform.
In order to add twist by rotating the molded product having the linear storage groove obtained in the first step around the major axis, it is common to add twist by a rotary take-off machine. If the process and the second process are not performed consecutively, they are wound on a drum in the first process and fed while being rewound in the second process, or the drum is rotated so that it is twisted. However, it is also possible to rewind and supply to a normal take-up machine.

In each of the above steps, sizing means contacting solids corresponding to the shape and outer shape of the groove to make the shape uniform, and in sizing a linear groove, the sizing key is After the twist forming, a plurality of sizing pins that can follow the spiral groove in rotation are used.

[0021]

According to the method of manufacturing the two-groove spiral slot having the above structure, when the first and second steps are continuously performed, the tension member is applied in the second step when the tension member is supplied in the first step. Since the twist in the same direction as the twist is applied, the tension member is substantially not twisted in the first and second steps, and as a result, no twist remains in the tension member in the final product.

Further, when the first and second steps are performed separately, when the tension member is supplied in the first step, a twist in a direction opposite to the twist applied in the second step is added, so In the member, the twist added in the first step is untwisted in the second step, so that no twist remains in the tension member in the final product.

[0023]

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT A preferred embodiment of the present invention will be described in detail below with reference to the accompanying drawings. Example 1 As shown in the cross-sectional shape of FIG. 1, a main body 1 having a substantially H-shaped overall shape, a pair of spiral rectangular storage grooves 2 and 2 provided above and below the main body 1, and the rectangular shape. A slot 4 having one tension member 3 arranged on the center of the housing grooves 2 and 2 so as to be located at the center of the main body 1 was manufactured by the method shown in FIG. In this manufacturing method, the target rectangular storage groove 2 has a width of 3.6 mm and a depth of 2.0 mm, and the slot 4 has an outer diameter of 6.4 mm.

In the manufacturing method shown in FIG. 2, a 0.22 × 5 steel cord (manufactured by Tokyo Steel Co., Ltd.) is set as the tension member 3 on the rotary feeder 10, and the powder clutch 12 is 2 kg / piece. Applying the tension of 10
While rotating at rpm, twisting (in the same direction as twisting to be added to the rectangular storage groove 2 in the second step described later) is added, the guide 13
Through the nozzle at a speed of 5 m / min to a predetermined position of the nipple mounted on the head portion of the extruder 14.

On the outer periphery of the tension member 3, a die corresponding to the sectional shape of FIG.
A resin (Teijin Co., Ltd., trade name; H-7500N) was extruded in a molten state to coat the resin, and then cooled and solidified in the cooling tank 16. At this time, a sizing key 18 was provided in the cooling tank 16, and the sizing key 18 was used to sizing the linear storage groove while the sizing key 18 was used to take it out. The above is the first step, and a molded product having a linear rectangular storage groove is obtained by this step.

Subsequently, the obtained molded product is treated with a heat treatment furnace 2
Introduced in 2. The heat treatment furnace 22 was of a hot air generator type, and the set temperature thereof was 300 ° C., the inlet temperature of the furnace 22 was 250 ° C., and the outlet temperature thereof was 200 ° C. After passing through the heat treatment furnace 22 at a speed of 5 m / min to heat and soften the PC / PBT resin, the PC / PBT resin was supplied to a sizing device 26 via a rotation preventing guide 24 having a projection engaging with the groove. .

The sizing device 26 is set with five sets of sizing pins that fit into the spiral storage groove formed by the twist applied by the rotary take-up machine 28 installed in the subsequent stage and rotate to size the groove. It was
In the sizing device 26, the slots 4 are spirally formed, fixed, and sized while the slots 4 are being cooled (second process).

The two-groove spiral slot 4 manufactured by the above process was then wound around the drum 32 by the rotary winder 30. The two-groove spiral slot 4 manufactured in such a process adds a twist in the same direction as the twist imparted by the rotary take-up machine 28 in the second process when the tension member 3 is supplied in the first process. In the first and second steps, the tension member 3 is not substantially twisted,
As a result, no twist remains in the tension member 3 in the final product.

In order to examine the state of the storage groove 2 of the slot 4 obtained, it was rewound from the drum 32 by about 10 m and cut, and the groove width and the spiral pitch of the spiral rectangular storage groove 2 were measured. As a result, the groove width was 3.55 to 3.65 mm and the spiral pitch was 495 to 505 mm. The slots 4 formed in this way may be a large number or may be used alone as an optical fiber cable. However, if the groove size or the spiral pitch changes during long-term use, transmission loss increases. Cause

Therefore, the slot 4 was subjected to a heat test at 100 ° C. for 1 hour. The results are shown in Table 1. As is clear from the results shown in the table, in the case of this example,
It can be seen that there is almost no change in the groove size and the spiral pitch, and there is little concern about changes over time.

[0031] As no twist applied to Comparative Example 1 the tension member 3, without rotating, except that inserted into a predetermined position of the nipple attached to the head portion of the extruder 14, second channel under the same conditions as in Example 1 Spiral slots were created and the groove width and spiral pitch were measured in the same manner as in Example 1. Table 1 shows the obtained measurement results.
Is shown in.

Example 2 The two-groove spiral slot 4 having the sectional shape shown in FIG. 1 was manufactured by the method shown in FIG. In the manufacturing method shown in the figure, as the tension member 3, a unidirectionally reinforced FRP having an FRP diameter of 0.85 mmφ using aramid fiber as a reinforcing material (manufactured by Ube Nitto Kasei Co., Ltd., trade name; Compose K-1.2- 08
5) is set in the rotary feeder 40, and is rotated at 10 rpm to add a twist (a direction opposite to the twist to be added to the rectangular storage groove 2 in the second step described later) and guide 4 at a speed of 5 m / min.
It was supplied to a predetermined position of a nipple attached to the head portion of the extruder 44 via the No.

On the outer periphery of the tension member 3, HDPE resin (Showa Denko KK, trade name; Shorex 2008E) corresponding to the cross-sectional shape of FIG.
-3) was extruded in a molten state for coating, and then cooled and solidified in the cooling tank 46. At this time, a sizing key 48 was provided in the cooling tank 46, and the sizing key 48 was used to sizing the linear storage groove while the sizing key 50 was used to pull the sizing key. The above is the first step, and by this step, a molded product having a linear rectangular storage groove is obtained.
The obtained molded product was once wound around the bobbin 52.

Then, the bobbin 52 around which the molded product obtained in the first step is wound is set in the rotary feeder 54, and 1
It was introduced into the heat treatment furnace 56 through the guide 55 while rotating at 0 rpm and adding twist. This heat treatment furnace 56
Is a hot air generator type, and its set temperature is 20
The temperature was 0 ° C., the inlet temperature of the furnace 56 was 160 ° C., and the outlet temperature was 140 ° C. After passing through the heat treatment furnace 56 at a speed of 5 m / min to heat and soften the HDPE resin, a rotation prevention guide 58 having a projection engaging with the groove is provided on the rear side and supplied to the sizing device 60. did.

The sizing device 60 is set with five sets of sizing pins that fit into the spiral storage groove formed by the twisting applied by the rotary take-up machine 62 installed at the subsequent stage and rotate to size the groove. It was
In the sizing device 60, the slots 4 are spirally cooled, fixed, and sized, while the linear rectangular storage grooves are being cooled (second step).

The two-groove spiral slot 4 manufactured by the above process was then wound on the drum 64. Since the two-groove spiral slot 4 manufactured in such a process applies a twist in the direction opposite to the twist applied in the second process when the tension member 3 is supplied in the first process, the tension member 3 is The twist added in the first step is untwisted in the second step, so that no twist remains in the tension member 3 in the final product. Table 1 shows the measurement results of the groove dimensions and the spiral pitch of the obtained slots 4.

Comparative Example 2 A two-groove spiral slot was prepared under the same conditions as in Example 2 except that the molded product was supplied in the second step of Example 2 without rotating, and the groove width was obtained in the same manner as in Example 2. And the spiral pitch was measured. The obtained measurement results are shown in Table 1.

Example 3 The two-groove spiral slot 4 having the sectional shape shown in FIG. 1 was manufactured by the method shown in FIG. In the manufacturing method shown in the figure, as the tension member 3, a 0.8 mmφ single steel wire (manufactured by Tokyo Steel Co., Ltd., trade name; PGW0.72) is set on the rotary feeder 70 and rotated at 10 rpm. While adding a twist (a direction opposite to the twist to be added to the rectangular storage groove 2 in the second step described later), at a speed of 5 m / min, through the guide 72, to a predetermined position of the nipple attached to the head portion of the extruder 74. Supplied.

On the outer periphery of the tension member 3, a die corresponding to the sectional shape of FIG.
A resin (Teijin Co., Ltd., trade name; H-7500N) was extruded in a molten state to coat the resin, and then cooled and solidified in a cooling tank 76. At this time, a sizing key 78 was provided in the cooling tank 76, and the linear storage groove was sized by the sizing key 78 and was taken by the take-up machine 80. The above is the first step, and a molded product having a linear rectangular storage groove is obtained by this process, and the obtained molded product is temporarily wound around the bobbin 82.

Then, the bobbin 82 around which the molded product obtained in the first step is wound is set in the feeder 84, and the bobbin 82 is rewound from the bobbin 82 via the rotation preventing guide 84 having a projection engaging with the groove. And introduced into the heat treatment furnace 86. The heat treatment furnace 86 is of a hot air generator type, and its set temperature is 300 ° C. and the inlet temperature of the furnace 86 is 250 ° C.
Then, the outlet temperature was set to 200 ° C. By passing through the heat treatment furnace 86 at a speed of 5 m / min, PC / PBT
After the resin was softened by heating, it was supplied to the sizing device 90.

The sizing device 90 is set with five sets of sizing pins that fit into the spiral storage groove formed by the twisting applied by the rotary take-up machine 92 installed in the subsequent stage and rotate to size the groove. It was
In the sizing device 90, the slots 4 are spirally formed, fixed, and sized in a straight rectangular storage groove while being cooled (second step).

The two-groove spiral slot 4 manufactured by the above process was then wound around the drum 96 by the rotary winder 94. Since the two-groove spiral slot 4 manufactured in such a process applies a twist in the direction opposite to the twist applied in the second process when the tension member 3 is supplied in the first process, the tension member 3 is The twist added in the first step is untwisted in the second step, so that no twist remains in the tension member 3 in the final product. Table 1 shows the measurement results of the groove dimensions and the spiral pitch of the obtained slots 4.

Comparative Example 3 The double groove was formed under the same conditions as in Example 1 except that the tension member 3 was inserted into a predetermined position of a nipple mounted on the head portion of the extruder 14 without being rotated so that twisting was not applied. Spiral slots were created, and the groove width and spiral pitch were measured in the same manner as in Example 3. Table 1 shows the obtained measurement results.
Is shown in.

In the above embodiment, the groove shape sizing step is provided in each of the first and second steps, but this sizing step is not always necessary.

[Table 1] In Table 1, TM is an abbreviation for tension member, and rigidity is a value of torsional rigidity.

The torsional rigidity was measured by the following method.
FIG. 5 is an explanatory diagram of a method for measuring the torsional rigidity. In this measuring method, a test table B fixed on a base A, a plate electronic balance C, and a pair of arms D and E are prepared. A glass tube F having an inner diameter similar to the outer diameter of the tension member or the slot body was fixed on the test stand B. In the measurement, first
A 500 mm long sample piece (tension member or slot body) for measuring the torsional rigidity is inserted into the glass tube F, and the arms D and E are fixed to both ends thereof. Arm D
A pointed screw G is screwed onto the tip of the fulcrum, and this point is used as a fulcrum, and the tip of this fulcrum is brought into contact with the plate of the upper electronic balance C. At this time, the length between the center of the fulcrum and the fixed center of the arm D on the test piece side was set to 80 mm.

When the arm E is rotated, the arm D
Since the load is applied to the upper electronic balance C via the fulcrum of, the load generated when the arm E is rotated once is defined as the torsional rigidity.

[0047]

As described above in detail, according to the manufacturing method of the present invention, since no twist remains in the tension member of the manufactured two-groove spiral slot, the groove size and the spiral pitch change with time. High accuracy is maintained.

[Brief description of drawings]

FIG. 1 is a sectional view of a slot to which a manufacturing method according to the present invention is applied.

FIG. 2 is an explanatory view showing the first embodiment of the manufacturing method according to the present invention in the order of steps.

FIG. 3 is an explanatory view showing a second embodiment of the manufacturing method according to the present invention in the order of steps.

FIG. 4 is an explanatory view showing a third embodiment of the manufacturing method according to the present invention in the order of steps.

FIG. 5 is an explanatory diagram of a method for measuring the torsional rigidity of the slot and the tension member.

[Explanation of symbols]

 1 Main Body 2 Rectangular Storage Groove 3 Tensile Strength Wire 4 Slot 10 Rotating Feeder 14 Extruder 16 Cooling Tank 20 Pulling Machine 22 Heat Treatment Furnace 26 Sizing Device 28 Rotating Pulling Machine 30 Rotating Winding Machine

Claims (2)

[Claims] 1. A method of manufacturing a two-groove spiral slot, which comprises a tension member and a main body made of a thermoplastic resin, and two spiral grooves for accommodating and carrying an optical fiber tape core wire and the like are provided in the main body. In the first step, the thermoplastic resin is extruded around the tension member and then cooled at a temperature lower than the melting point to form a molded product having a storage groove extending linearly in the longitudinal direction. After the softening point of the thermoplastic resin, after twisting by rotating around the major axis in a temperature range of less than the melting point,
A second step of forming the accommodation groove in a spiral shape by cooling and solidifying, when the first and second steps are continuously performed, when supplying the tension member in the first step,
A method for manufacturing a two-groove spiral slot, characterized in that a twist in the same direction as the twist applied in the second step is added. 2. A method of manufacturing a two-groove spiral slot, which comprises a tension member and a main body made of a thermoplastic resin, and two spiral grooves for accommodating and carrying an optical fiber tape core wire and the like are provided in the main body. In the first step, the thermoplastic resin is extruded around the tension member and then cooled at a temperature lower than the melting point to form a molded product having a storage groove extending linearly in the longitudinal direction. After the softening point of the thermoplastic resin, after twisting by rotating around the major axis in a temperature range of less than the melting point,
Including a second step of cooling and solidifying to form the storage groove in a spiral shape, when the first and second steps are performed separately, when supplying the tension member in the first step,
A method for manufacturing a two-groove spiral slot, characterized in that a twist in a direction opposite to the twist applied in the second step is applied.