JPH07113032A - Antistatic agent for acrylic resin and acrylic resin composition containing the same - Google Patents

Abstract

PURPOSE:To obtain the antistatic agent, comprising at least one of specific two kinds of sulfonates, a polyalkylene glycol, a specified nonionic surfactant and a specific anionic surfactant and having stabilized antistatic performances. CONSTITUTION:This antistatic agent comprises (A) at least one of (A-1) a sulfonate expressed by formula I [R<1> is a 6-20C alkyl or alkenyl; (m) is 2-4; (n) is l-100; M<1> is an alkaline (earth) metal or phosphonium having four hydrocarbon groups] and (A-2) a sulfonate expressed by formula II [R<2> and R<3> are each the same as R<1>; (p) is the same as (m); (q) is the same as (n); M<2> and M<3> are each the same as M<1>], (B) a polyalkylene glycol expressed by formula III [(r) is 2-4; (s) is 2-100], (C) a nonionic surfactant consisting essentially of a 6-14C fatty acid diethanolamide, etc., and (D) an anionic surfactant expressed by formula IV [R<4> is a 6-22C long-chain alkyl, alkenyl, etc.; M<4> is an alkaline (earth) metal] and satisfies formulas V to VII expressed in terms of blending weight ratios.

Description

Detailed Description of the Invention

[0001]

FIELD OF THE INVENTION The present invention relates to a novel antistatic agent for acrylic resins and an acrylic resin composition containing the same. More specifically, the present invention is not limited to extrusion molding of an acrylic resin, but also in injection molding, the antistatic performance can be exhibited immediately after molding, and the transparency and moldability of the acrylic resin are not impaired. TECHNICAL FIELD The present invention relates to an antistatic agent for base resins and an acrylic resin composition containing the same, which is excellent in antistatic properties, transparency, and moldability.

[0002]

2. Description of the Related Art Acrylic resins are widely used as materials for films, fibers, molded articles, etc. due to their excellent transparency, optical properties, good mechanical properties, processing properties and appearance.
Among them, it is widely used for lighting equipment, signboards, and decorations.
However, since this acrylic resin is generally hydrophobic and has a high electric insulation property, it is easily charged due to the accumulation of static electricity, and as a result, its appearance is impaired, and work in processes such as processing, packaging, printing and painting is performed. It is inevitable that the efficiency will decrease and it will also cause an accident due to spark discharge. Therefore, various antistatic methods for acrylic resins have been studied.

By the way, as an internal addition type antistatic agent for general synthetic resins, cationic, anionic and nonionic surfactants are known, and these antistatic agents have an antistatic effect. Is expressed by bleeding out on the surface of synthetic resin.

However, it is difficult to use a cationic surfactant having a poor thermal stability for an acrylic resin because the processing temperature of the resin is relatively high, and the glass of the resin is used. Since the transition temperature is also higher than that of polyethylene and polypropylene, it is necessary to add a large amount when using a nonionic surfactant, but in that case the heat distortion temperature and transparency decrease, and the resin's original basic characteristics However, it is unavoidable that the surfactant excessively bleeds out on the resin surface and causes the molded article to become sticky, making it unusable for practical use.

On the other hand, as the antistatic surfactant,
When thermal stability is required, anionic surfactants such as alkyl sulfonic acid metal salts and alkyl benzene sulfonic acid metal salts have been proposed (JP-A-49-7344).
3, JP-A-52-47072, JP-A-54.
-37154 gazette).

However, these internal-kneading type antistatic surfactants have insufficient compatibility with the acrylic resin which is originally hydrophobic, so that the transparency is deteriorated and the appearance is deteriorated. Have

Also proposed is a method of improving the decrease in transparency by using an alkane sulfonate, an alkylbenzene sulfonate and a fatty acid monoglyceride in combination with an acrylic resin and using a sulfonate type anionic surfactant as an antistatic agent. (Japanese Patent Laid-Open No. 1-1975
No. 52), the improvement effect is not always satisfactory.

On the other hand, as an antistatic agent for polyolefin or polystyrene, a sulfonic acid metal salt having a free carboxyl group neutralized with an amine compound (Japanese Patent Publication No. 58-1).
9692) or a sulfonic acid metal salt having a carboxyl group esterified with an aliphatic alcohol or polyethylene glycol (Japanese Patent Publication No. 58-53658).
Is proposed.

However, when these antistatic agents are applied to acrylic resins, they are unavoidably deteriorated in appearance due to deterioration of transparency and dispersibility.

[0010]

Under the above circumstances, the present inventors have previously proposed an acrylic resin composition capable of imparting stable antistatic properties without impairing the transparency of the acrylic resin. A proposal has been made (Japanese Patent Application No. 4-119948). However, in order to obtain a surface resistance value of 1 × 10 ¹² Ω or less, which is a standard of antistatic performance in an injection-molded product, this product is conditioned for about 24 hours. It takes time and there is a problem in terms of immediate effect. Further, the present inventors have proposed to use a nonionic surfactant having a specific carbon chain length as an essential component in order to solve the above problems (Japanese Patent Application No. 5-1).
83028). The surface resistance value of the injection-molded product immediately after molding of this product could be set to the order of 10 ¹¹ Ω, but depending on the application, a higher antistatic performance (10 ¹⁰ Ω) can be obtained.
Ω order) was required, and it was still insufficient to adapt to all applications.

On the other hand, up to now, regarding the antistatic method of an acrylic resin, particularly an injection-molded article, as a method of using a nonionic surfactant having a carbon chain length of 12 or less, lauric acid monoglyceride is used as another nonionic agent. Method in combination with a hydrophilic surfactant (Japanese Patent Publication No. 2-14377), and a method in which diethanollaurylamine is compounded (JP-A-62-29).
Japanese Patent No. 5944) has been proposed. However, in these methods, unless the amount of the nonionic surfactant added to the acrylic resin is 4 parts by weight or more, sufficient antistatic effect cannot be obtained immediately after injection molding.
The heat distortion temperature of the acrylic resin is lowered, and the volatility of the surfactant is high, which causes silver marks on the surface of the molded product, which damages the appearance of the surface of the molded product and causes severe smoke during molding. There are many disadvantages such as inconvenience.

Under such circumstances, the present invention exhibits highly stable antistatic performance immediately after molding with a low addition amount, regardless of the molding method, as compared with conventionally known antistatic agents for acrylic resins. In addition, the object of the present invention is to provide an antistatic agent for acrylic resins, which is excellent in transparency and moldability of a molded product.

[0013]

Means for Solving the Problems As a result of intensive studies to develop an antistatic agent for acrylic resins having the above-mentioned preferable characteristics, the present inventors have found that a sulfonate and a polyalkylene having a specific structure can be obtained. It was found that the object can be achieved by combining glycol with a specific nonionic surfactant and / or a specific sulfonic acid type anionic surfactant, and the present invention has been completed based on this finding. .

That is, the present invention provides (A) (A-1) general formula (I)

[Chemical 3] And (A-2) general formula (II)

[Chemical 4] (In the formula, R ¹ , R ² and R ³ are a linear or branched alkyl group or alkenyl group having 6 to 20 carbon atoms,
They may be the same or different from each other, m and p are integers of 2 to 4, and n and q are 1 to
100, m and n or p and q may be the same or different, and M ¹ , M ² and M
³ is an alkali metal, an alkaline earth metal or a phosphonium group having four hydrocarbon groups, which may be the same or different from each other. And (B) general formula (III) HO {(CH2) rO} sH (III) (r in the formula is an integer of 2 to 4, s is 2 to 100). A polyalkylene glycol represented by (C) a fatty acid glyceride derived from a fatty acid having 6 to 14 carbon atoms and having a fatty acid monoglyceride content of 70% by weight or more, and a fatty acid diethanolamine derived from a fatty acid having 6 to 14 carbon atoms and diethanolamine de and the number of carbon atoms is N- substituted by 6-14 alkyl or alkenyl group, further (D) formula _{^{(IV) R 4 SO 3 M}} 4 (IV) ( However, R ⁴ is formula (A-1) and does not contain a sulfonic acid residue (A-2), linear or branched long chain alkyl or alkenyl group having 6 to 22 carbon atoms or carbon atoms, At least 1 selected from the group consisting of an alkylaryl group of 8 to 30 and M ⁴ is an alkali metal or an alkaline earth metal).
Consisting of a seed and each component (A-1), (A-2),
(B), (C), and (D) are the following relational expressions in terms of blending weight ratio: {(A-1) + (A-2)} / (B) = 90 / 10-3
0/70 and the relational expression {(A-1) + (A-2) + (B)} / (C) = 20 /
80 to 100/0 and the relational expression {(A-1) + (A-2) + (B) + (C)} / (D)
= 99/1 to 50/50 are provided, and an antistatic agent for acrylic resins is provided.

R ¹ , R ² and R ³ in the above-mentioned component (A) which is the composition component of the antistatic agent of the present invention are each an alkyl group or an alkenyl group having 6 to 20 carbon atoms, and these are linear. And R ¹ and R ² and R ³ may be the same as or different from each other. Examples of such a group include a hexyl group, an octyl group, a decyl group, a dodecyl group, a tridecyl group, a tetradecyl group, a pentadecyl group, a hexadecyl group, a hexadecenyl group, an octadecyl group, and an octadecenyl group. R
^When the carbon number of ¹ , R ² and R ³ is less than 6, the compatibility with the acrylic resin is poor and the transparency may be impaired, and when it exceeds 20, the antistatic performance is deteriorated.

Further, (CH2) m and (CH2) p are alkylene groups having 2 to 4 carbon atoms, such as ethylene group and propylene group, which may be used alone or in combination of two or more kinds. May be the same as or different from each other, and it is particularly preferable to contain an ethylene group in a number of 70% or more based on the total number of the alkylene groups. N and q are 1 to 100, preferably 3 to 80
However, when these are more than 100, the antistatic effect is not further improved, and when they are blended with an acrylic resin, the physical properties of the resin are impaired, which is economically disadvantageous, and less than 1, particularly 0. When it becomes a carboxylic acid, the heat resistance is deteriorated, which causes a problem in handleability.

The sulfonates of the components (A-1) and (A-2) are alkali metal salts, alkaline earth metal salts or phosphonium salts having four hydrocarbon groups of the corresponding sulfonic acids. And the general formula (I) and (I
M ¹ , M ² and M ^{3 in} I) may be the same or different from each other. The alkali metal salt is preferably sodium salt, potassium salt, lithium salt or the like, and the alkaline earth metal salt is preferably magnesium salt, calcium salt or the like.

Examples of the phosphonium salt include those represented by the general formula (V)

[Chemical 5] (In the formula, R ⁵ , R ⁶ , R ⁷ and R ⁸ are an optionally substituted linear or branched alkyl group having 1 to 18 carbon atoms or a phenyl group). Examples thereof include a hydroxyl group, a halogen atom and an amino group. As such, for example, tetramethylphosphonium salt, tetraethylphosphonium salt, tetrabutylphosphonium salt, trimethylstearylphosphonium salt, trimethyldodecylphosphonium salt, trimethylphenylphosphonium salt, triphenylmethylphosphonium salt, tetraphenylphosphonium salt, di ( Examples thereof include 2-hydroxyethyl) dibutylphosphonium salt and p-hydroxyphenyltriethylphosphonium salt. These phosphonium salts are particularly effective as a resin composition having high heat resistance.

These (A-1) component and (A-2) component, that is, each sulfonate represented by the above general formula (I) or general formula (II) may be used alone,
You may use it in combination of 2 or more type.

In the present invention, at least two components (A-1) and (A-2) are blended and used so that only the component (A-1) or the component (A-2) is used alone. Compared with the case, the antistatic property, particularly the stability of the performance over time and the transparency are improved, which is advantageous.

The blending weight ratio of the component (A-1) and the component (A-2) is 9: 1 to 1: 9, preferably 8: 2 to 2: 8.
It is selected in the range of. If this ratio is higher than 9: 1, the antistatic property is lowered, and if it is lower than 1: 9, the transparency is lowered.

The components (A-1) and (A-2) are, for example, those represented by the general formula (VI).

[Chemical 6] (In the formula, R ⁹ is a linear or branched alkyl group or alkenyl group having 6 to 20 carbon atoms, R ¹⁰ is a hydrogen atom or an alkyl group, and M ⁵ is a hydrogen atom or the above salt residue.) The compound represented by the formula (VII) HO-{(CH2) tO} uH (VII) (wherein t is an integer of 2 to 4 and the alkylene group of (CH2) t is alone. Or may be a combination of two or more thereof, u is 1 to 100, and {(CH
2) The alkyleneoxy group or polyalkyleneoxy group of tO} u may be used alone or in combination of two or more thereof) or reacted with the alkylene glycol or polyalkylene glycol of the general formula (V
The lower alkyl ester of the compound of formula (I) is represented by the general formula (VI
The one in which I) is transesterified with glycol and M is a hydrogen atom can be produced by subjecting the sulfonic acid of these reaction products to a predetermined salt forming reaction.

The compound of the general formula (VI) and the general formula (V
The molar ratio of the glycol of II) used is 0.5: 1.
A range of up to 2.0: 1 is preferred. In this case, the reaction product contains the component (A-1), the component (A-2), and optionally the polyalkylene glycol of the component (B) described below, and constitutes the compounding component of the present invention as it is. It is advantageous.

Regarding the reaction conditions for obtaining the above-mentioned reaction product suitable as a blending component of the present invention, in the case of a dehydration esterification reaction, the reaction temperature is 50 to 15 at atmospheric pressure or reduced pressure.
0 ° C., preferably 80 to 120 ° C., reaction time 30 minutes to
It is suitable for 20 hours, preferably 2 to 12 hours. In the case of transesterification reaction, the reaction temperature is 50 to 150 ° C., preferably 80 to 120 ° C., and the reaction time is 10 minutes to 20 hours, preferably 30 minutes to 6 hours under normal pressure or reduced pressure.

These reactions are carried out without solvent or in a solvent such as carbon tetrachloride or xylene. The reaction temperature and the reaction time are appropriately selected depending on the molar ratio, the degree of reduced pressure and the like.

In the transesterification reaction, a conventional catalyst such as an acid catalyst such as p-toluenesulfonic acid or sulfuric acid, or a base catalyst such as sodium hydroxide, potassium hydroxide or sodium hydrogen carbonate is used. When the starting material is an unneutralized material, it is not necessary to add an acid catalyst.

The salt formation reaction method is not particularly limited, and a conventionally known method can be used. For example, by reacting the sulfonic acid of the reaction product with an alkali metal hydroxide, carbonate, hydrogencarbonate or the like, the sulfonic acid alkali metal salt can be obtained.

The phosphonium salt can be obtained by allowing a halogen salt of a phosphonium compound to act on the alkali metal salt of sulfonic acid to cause metathesis, or by directly acting on a phosphonium hydroxide compound.

In the compound of the above general formula (III) which is the component (B) which is the composition component of the antistatic agent of the present invention,
r is an integer of 2 to 4, preferably 2 or 3, and (C
The alkylene group of H2) r may be a single type or a combination of two or more types. Further, s is selected in the range of 2 to 100, preferably 3 to 80, and the polyoxyalkylene group of {(CH2) rO} s may be a single type or a combination of two or more types. As such a compound,
Polyethylene glycol, polypropylene glycol,
Examples thereof include ethylene glycol-propylene glycol copolymers.

The nonionic surfactant as the component (C) which is the composition component of the antistatic agent of the present invention has a carbon number of 6 to 1.
A fatty acid glyceride having a fatty acid monoglyceride content of 70% by weight or more and a carbon number of 6
The main component is at least one selected from fatty acid diethanolamides derived from fatty acids of 14 to 14 and diethanolamines N-substituted with alkyl or alkenyl groups having 6 to 14 carbon atoms. If the carbon number is too small, the volatility becomes high and problems such as smoking occur, and if it is too large, the immediate effect of the antistatic performance cannot be obtained.

Regarding the fatty acid glyceride as the component (C), the content of the fatty acid monoglyceride needs to be 70% by weight or more, and the fatty acid diglyceride and the fatty acid triglyceride can be contained within the range. When the content of fatty acid monoglyceride is less than 70% by weight, the immediate effect of antistatic performance cannot be obtained.

These nonionic surfactants include:
For example, caproic acid monoglyceride, caproic acid diglyceride, caproic acid triglyceride, octylic acid monoglyceride, octylic acid diglyceride, octylic acid triglyceride, decanoic acid monoglyceride, decanoic acid diglyceride, decanoic acid triglyceride, lauric acid monoglyceride, lauric acid diglyceride, lauric acid triglyceride, myristin Acid monoglyceride, myristic acid diglyceride, myristic acid triglyceride, caproic acid diethanolamide, octyl acid diethanolamide, decanoic acid diethanolamide, lauric acid diethanolamide, myristic acid diethanolamide, diethanolhexylamine, diethanoloctylamine, diethanollaurylamine, diethanolmyristyl Examples include amines.

In the compound of the above general formula (IV) which is the component (D) which is the composition component of the antistatic agent of the present invention, R
⁴ does not include a sulfonic acid residue of the general formulas (A-1) and (A-2), and has a linear or branched long-chain alkyl group or alkenyl group having 6 to 22 carbon atoms, or 8 to 3 carbon atoms.
Is an alkylaryl group of 0, and M4 is composed of one or more compounds selected from alkali metals or alkaline earth metals. Examples of such compounds include sodium octyl sulfonate, lithium octyl sulfonate, potassium octyl sulfonate, sodium isooctyl sulfonate, sodium octadecyl sulfonate, sodium nonyl sulfonate,
Sodium decyl sulfonate, lithium dodecyl sulfonate, sodium isooctylbenzene sulfonate, sodium octadecyl benzene sulfonate, sodium isooctadecyl sulfonate, potassium octyl benzene sulfonate,
Examples thereof include sodium nonylbenzene sulfonate and sodium dodecylbenzene sulfonate. In the present invention, when the chain length of the long-chain alkyl group of the sulfonic acid metal salt is shorter than C6, the surface of the acrylic resin molded article becomes sticky, which is unsuitable.

In the antistatic agent of the present invention, as a secondary component, for example, ethylene glycol stearate,
Polyethylene glycol stearic acid ester, polyethylene glycol lauric acid ester, palmitic acid monoglyceride, palmitic acid diglyceride, palmitic acid triglyceride, stearic acid monoglyceride, stearic acid diglyceride, stearic acid triglyceride,
Pentaerythritol monostearate, pentaerythritol dilaurate, stearyl alcohol, lauryl alcohol, octyl alcohol,
Glycerin monostearate succinate, diethanol stearyl amine, diethanol palmityl amine, palmitic acid diethanolamide, stearic acid diethanolamide, etc. can be contained. These may be used alone or in combination of two or more.

In the antistatic agent of the present invention, the preferable compounding ratio of each component is {(A-1) + (A-2)} on a weight basis.
/ (B) is 90/10 to 30/70, preferably 85/1
5-40 / 60, {(A-1) + (A-2)} + (B)
/ (C) is 20/80 to 100/0, preferably 25/7
5-100 / 0, {(A-1) + (A-2) + (B) +
(C)} / (D) is 99/1 to 50/50, preferably 9
The range is 5/5 to 60/40. If it deviates from this range, it becomes difficult to obtain a sufficient effect. That is, although the component (C) is an optional component, by adding the component,
Antistatic performance during injection molding appears immediately after molding.

As the acrylic resin to which the antistatic agent of the present invention can be applied, for example, methyl methacrylate homopolymer or methyl methacrylate and 50% by weight or less of acrylic acid ester or methacrylic acid ester, acrylic acid, methacrylic acid can be used. Examples thereof include copolymers with acids, styrene, acrylonitrile, butadiene and the like. Examples of the acrylate ester include methyl acrylate, ethyl acrylate and butyl acrylate, and examples of the methacrylate ester include ethyl methacrylate, butyl methacrylate and cyclohexyl methacrylate. Further, a rubber component such as polybutadiene, styrene-butadiene rubber, acrylonitrile-butadiene rubber or the like can be added to the acrylic resin by a conventional method for the purpose of improving the strength of the molded product.

The antistatic agent of the present invention can be used by preparing a masterbatch kneaded in a resin in a high concentration in advance and diluting it at the time of molding. This masterbatch is used with respect to 100 parts by weight of an acrylic resin. 6 to 50 parts by weight, preferably 10 to 40 parts by weight can be compounded and produced. If the amount is more than 50 parts by weight, it is difficult to uniformly disperse the master batch during preparation, and the concentration of the antistatic agent is too high, resulting in poor dispersibility upon dilution.

By blending the antistatic agent of the present invention with the acrylic resin, an acrylic resin composition having excellent antistatic properties, transparency and moldability is prepared. Regarding the compounding amount of the antistatic agent at this time, in the case of ordinary use, the above (A-1) is added to 100 parts by weight of the acrylic resin.
The compounding ingredients of (A-2), (B), (C) and (D) are added so that the total amount is 0.5 to 6.0% by weight, preferably 1.0 to 4.0 parts by weight. Is preferred. This amount is 0.
If it is less than 5 parts by weight, the effect of imparting the antistatic property is not sufficiently exhibited, and if it exceeds 6 parts by weight, the antistatic effect is not further improved and the physical properties of the acrylic resin are adversely affected, which is not preferable.

As a method for preparing this, it is preferable to knead a predetermined compounding component into an acrylic resin. The kneading method is not particularly limited, and a conventionally known method, for example, a method of blending an acrylic resin and a blending component and then melt-kneading with an extruder, or kneading the blending component into an acrylic resin at a high concentration in advance Prepare a mixed masterbatch,
A method of diluting this at the time of molding can be used.

When the acrylic resin composition is prepared, various commonly used additive components may be used in combination, if necessary. Examples of such additive components include phosphorus-based antioxidants such as trisnonylphenyl phosphite and triphenyl phosphite, dioctadecyl 3,3′-thiodipropionate, didodecyl 3,3′-thiodipropionate, and the like. Sulfur antioxidants, butylated hydroxytoluene, tetrakis [methylene-3-
(3 ', 5'-di-t-butyl-4'-hydroxyphenyl) propionate] Methane and other phenolic antioxidants, UV absorbers, nucleating agents, ethylenebisamides, monoalkylamides, montanic acid waxes, polyolefin waxes Examples thereof include lubricants such as fatty acid metal salts, optical brighteners such as oxazole-based and coumarin-based agents, resin strength-reinforcing or light-scattering inorganic fillers such as barium sulfate, titanium oxide and calcium carbonate, and other coloring agents.

The acrylic resin composition thus prepared can be molded by various molding methods such as injection molding, extrusion molding and blow molding. For example, it covers lighting equipment, electric meters, electronic equipment and the like. It is preferably used as a material for molded articles such as parts, parts, meter covers, films, sheets, panels and fibers.

[0042]

INDUSTRIAL APPLICABILITY The antistatic agent for acrylic resin of the present invention can impart stable antistatic performance without impairing the transparency of the acrylic resin, and can be added at a low addition amount regardless of the molding method. The highly stable antistatic performance can be exhibited immediately after molding, and the remarkable effect that the moldability is also excellent.

[0043]

The present invention will be described in more detail by way of examples, which should not be construed as limiting the invention thereto.

The performance of the molded product was evaluated as follows. (1) Surface resistance value Toa Denpa Co., Ltd. hyper-insulator SM-10E was used for the measurement. (2) Antistatic performance The surface resistance was measured, and when the measured value was x (Ω), it was evaluated according to the following criteria. ⊚: x <1 × 10 ¹¹ ◯: 1 × 10 ¹¹ ≦ x <1 × 10 ^{12 Δ: 1 × 10 12} ≦ x <1 × 10 ¹³ ×: x ≧ 1 × 10 ¹³

Examples 1 to 8 and Comparative Examples 1 to 5 Types and compounding weight ratios [(A-1) / (A-2) = 80 shown in Table 1 of acrylic resins [EH] manufactured by Kuraray Co., Ltd. /
20]] are shown in Tables 2 and 3 respectively.
The mixture was added in the addition amount shown in 1 and premixed with a Henschel mixer, and melt-kneaded at 230 ° C. using a vented twin-screw extruder. At that time, the degree of smoke emitted from the vent was visually confirmed.

Next, the obtained strand pellets were cut with a pelletizer and pelletized. After drying the pellets, extrusion molding at 230 ° C. with a T-bed extruder,
After producing a test piece of 120 × 1000 × 1 mm, its surface resistance value was measured immediately under the condition of 23 ° C. and 65% RH and after 1 week of molding. Further, the transparency and moldability of the molded product were visually evaluated. The results are shown in Tables 2 and 3.

Examples 9 to 11 and Comparative Examples 6 to 8 Acrylic resin [G1-P manufactured by Kuraray Co., Ltd.]
And the compounding weight ratio [(A-1) / (A-2) =
Each of the antistatic agents consisting of the compounding components of 80/20] was added in an addition amount shown in Tables 2 and 3, and the mixture obtained by premixing with a Henschel mixer was used to obtain a mixture at 230 ° C. using a vented twin-screw extruder. It was melt-kneaded. At that time, the degree of smoke emitted from the vent was visually confirmed.

Next, the obtained strand was cut with a pelletizer and pelletized. After drying the pellets, injection molding is performed at 240 ° C using an injection molding machine and 100 x
A 100 × 2 mm test piece was prepared. After creating test pieces, 2
The surface resistance value was measured immediately under the condition of 3 ° C. and 65% RH and one week after the molding. Further, regarding the moldability of the test piece, the surface condition of the molded product was visually determined. The results are shown in Tables 3 and 4.

[0048]

[Table 1]

Each symbol in Table 1 has the following meaning. ABS: branched alkylbenzene sulfonic acid Na salt (average carbon chain length 12), LAS: linear alkylbenzene sulfonic acid Na salt (average carbon chain length 12), PS: paraffin sulfonic acid Na salt (average carbon number 14) LMG: lauric acid Monoglyceride, LDAd: lauric acid diethanolamide, LDAn: lauryl diethanolamine, SMG: stearic acid monoglyceride. Further, R ¹ , R ² and R ³ in the table are represented as Ck (k is the number of carbon atoms) depending on the number of carbon atoms of the alkyl group.

[0050]

[Table 2]

[0051]

[Table 3]

─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. ⁶ Identification code Internal reference number FI technical display area C08L 71:00)

Claims (2)

[Claims] 1. (A) (A-1) general formula: And (A-2) general formula: (In the formula, R ¹ , R ² and R ³ are a linear or branched alkyl group or alkenyl group having 6 to 20 carbon atoms,
They may be the same or different from each other, m and p are integers of 2 to 4, and n and q are 1 to
100, m and n or p and q may be the same or different, and M ¹ , M ² and M
³ is an alkali metal, an alkaline earth metal or a phosphonium group having four hydrocarbon groups, which may be the same or different from each other. At least one selected from the above, and (B) a polyalkylene glycol represented by the general formula HO {(CH2) rO} sH (where r is an integer of 2 to 4 and s is 2 to 100). , (C) a fatty acid glyceride derived from a fatty acid having 6 to 14 carbon atoms and having a fatty acid monoglyceride content of 70% by weight or more, a fatty acid diethanolamide derived from a fatty acid having 6 to 14 carbon atoms and 6 carbon atoms A nonionic surfactant containing as a main component at least one selected from diethanolamines N-substituted with an alkyl group or an alkenyl group of 1 to 14; R ⁴ SO ₃ M ⁴ (wherein R does not include a sulfonic acid residue of the general formulas (A-1) and (A-2), and is a straight-chain or branched long-chain alkyl group having 6 to 22 carbon atoms or An alkenyl group or an alkylaryl group having 8 to 30 carbon atoms, and M4 is an alkali metal or an alkaline earth metal), and at least one selected from the anionic surfactants, and Each component (A-1), (A-2),
(B), (C), and (D) are the following relational expressions in terms of blending weight ratio: {(A-1) + (A-2)} / (B) = 90 / 10-3
0/70 and the relational expression {(A-1) + (A-2) + (B)} / (C) = 20 /
80 to 100/0 and the relational expression {(A-1) + (A-2) + (B) + (C)} / (D)
= 99/1 to 50/50, The antistatic agent for acrylic resins characterized by the above-mentioned. 2. An acrylic resin composition obtained by blending the antistatic agent for acrylic resin according to claim 1 with an acrylic resin.