JPH0632382Y2 - Color heat transfer postcard paper - Google Patents
Color heat transfer postcard paperInfo
- Publication number
- JPH0632382Y2 JPH0632382Y2 JP1989097491U JP9749189U JPH0632382Y2 JP H0632382 Y2 JPH0632382 Y2 JP H0632382Y2 JP 1989097491 U JP1989097491 U JP 1989097491U JP 9749189 U JP9749189 U JP 9749189U JP H0632382 Y2 JPH0632382 Y2 JP H0632382Y2
- Authority
- JP
- Japan
- Prior art keywords
- postcard
- color
- heat transfer
- paper
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【考案の詳細な説明】 〔産業上の利用分野〕 本考案は葉書やカードなどとして用いるカラープリンタ
ー用紙に関し、更に詳しくは熱転写プリンター、特に染
料昇華熱転写プリンターに於て、染料をシャープに受容
するカラープリンター用葉書用紙で、カラープリント面
に予め、印刷を施し、その上にカラー画像の印写可能な
受容層を設けたシートを葉書などに用いるものである。[Detailed Description of the Invention] [Industrial field of application] The present invention relates to a color printer paper used as a postcard, a card, and the like. More specifically, in a thermal transfer printer, particularly a dye sublimation thermal transfer printer, a color that sharply receives a dye. A postcard for a printer, which is used for a postcard or the like, in which a color print surface is preliminarily printed and a receiving layer on which a color image can be printed is provided.
最近カラープリンターの開発が進み、特に熱転写方式の
プリンターで鮮明なカラー画像が比較的コンパクトな装
置で実現可能になってきた。熱転写プリントには、染料
昇華、ワックス系溶融インクなどの方式がとられてい
る。Recently, the development of color printers has progressed, and in particular, thermal transfer printers have become possible to realize clear color images with a relatively compact device. For thermal transfer printing, methods such as dye sublimation and wax-based molten ink are used.
このうち染料昇華熱転写方式は、小型ノンインパクトプ
リンターの主流として、小型のカラープリンター、ビデ
オプリンター用としても使われることが多く、昇華染料
熱転写方式で鮮明な画像が得られるシートが検討開発さ
れている。Of these, the dye sublimation thermal transfer method is often used for small color printers and video printers as the mainstream of small non-impact printers, and a sheet that can obtain clear images with the sublimation dye thermal transfer method is being studied and developed. .
昇華染料熱転写方式のプリンターは、フィルム、薄紙等
の基材上にY、M、Cそれぞれの昇華染料インクを塗布
したインクシートを使用する。このインクシートに染着
性の高い樹脂などを塗工した受容シートを重ね合わせ、
サーマルヘッドからの熱により受容シートに各色の昇華
染料が必要濃度で必要な部分だけに転写され画像を形成
する。A sublimation dye thermal transfer printer uses an ink sheet in which a Y, M, and C sublimation dye ink is applied on a substrate such as a film or thin paper. Overlay this ink sheet with a receiving sheet coated with highly dyeable resin,
By the heat from the thermal head, the sublimation dye of each color is transferred to the receiving sheet at the required concentration only on the required portion to form an image.
近年、ビデオ画像などをハードコピーした絵葉書等を、
昇華染料熱転写方式のプリンターを用いて作成すること
が広く行なわれているが、この葉書用紙で、カラープリ
ント面に予め印刷が施し、そのうえに昇華染料熱転写方
式でカラー画像を印写可能な葉書用紙は知られていな
い。In recent years, postcards that are hard copies of video images,
It is widely used to create with a sublimation dye thermal transfer printer, but this postcard paper is preprinted on the color print surface, and a postcard paper that can print a color image with the sublimation dye thermal transfer method is unknown.
本考案は、昇華染料熱転写方式を始めとする各種の熱転
写カラープリンターのカラープリント面に、予め印刷を
施し、そのうえに良好な印字、画像記録適性をもったカ
ラー熱転写葉書用紙を提案することを目的とする。The present invention aims to propose a color heat transfer postcard paper which is preliminarily printed on the color print surface of various heat transfer color printers including the sublimation dye heat transfer system and has good printing and image recording suitability. To do.
かかる現状に鑑み本考案者は、鮮明な記録像を得ること
が出来、走行性、耐久性に優れた、熱転写受容シートに
ついて鋭意研究した。In view of such a current situation, the present inventor has earnestly studied a thermal transfer receiving sheet which can obtain a clear recorded image and is excellent in running property and durability.
その結果、第1図に示されるように、支持体2の片面
に、UV硬化型又は熱硬化型インクを用いて所定の印刷
3を施し、その上に熱転写色材の受容性が良く透明な受
容層1を設け、反対面に葉書として所要の印刷3′をす
ることによりカラー熱転写葉書用紙が得られることを見
い出した。第1図は本考案の葉書用紙の一部縦面図を、
第2図は表からみた本考案の葉書用紙の平面図を示す。As a result, as shown in FIG. 1, a predetermined print 3 is applied to one surface of the support 2 by using a UV curable ink or a thermosetting ink, and the heat transfer coloring material is well received and transparent. It has been found that a color heat transfer postcard paper can be obtained by providing the receiving layer 1 and performing the required printing 3'as a postcard on the opposite side. FIG. 1 is a partial vertical view of the postcard paper of the present invention.
FIG. 2 shows a plan view of the postcard paper of the present invention as seen from the table.
本考案で用いる支持体は、紙や各種の合成紙及び合成樹
脂フィルム(ポリエチレンテレフタレート、ポリエステ
ル、ナイロン等)、あるいは、紙とこれらのフィルムあ
るいは、各種フィルムどうしを貼合せたものが利用でき
る。受容層は、ポリエステル樹脂、ポリカーボネート樹
脂等の染料染着性樹脂に、必要に応じ、離型剤、硬化
剤、増白剤、導電剤等を添加したものが利用できる。As the support used in the present invention, paper, various synthetic papers and synthetic resin films (polyethylene terephthalate, polyester, nylon, etc.), or paper and these films or various films bonded together can be used. For the receiving layer, a dye-dyeing resin such as a polyester resin or a polycarbonate resin to which a release agent, a curing agent, a whitening agent, a conductive agent, or the like is added, if necessary, can be used.
受容層は通常有機溶剤溶液として塗工するので、印刷イ
ンクは、耐溶剤性の良好なUV硬化型インク又は熱硬化
型インクが用いられる。Since the receiving layer is usually applied as an organic solvent solution, a UV curable ink or a thermosetting ink having good solvent resistance is used as the printing ink.
次に実施例をあげて本発明の熱転写カラー葉書用紙を説
明する。実施例において、部は固形分重量部を示す。Next, the thermal transfer color postcard paper of the present invention will be described with reference to examples. In the examples, "part" means "part by weight of solid content".
実施例1 64g/m2上質紙を支持体として、その両面にUV硬
化型インクを用いオフセット印刷を施した(片面は所要
の葉書印刷)。葉書印刷面の反対面に、下記塗料1を用
い受容層を固形分5g/m2形成し熱転写カラー葉書用
紙とした。Example 1 A 64 g / m 2 fine paper was used as a support, and offset printing was performed using UV curable ink on both sides thereof (one side required postcard printing). On the surface opposite to the postcard printing surface, a receiving layer was formed with a solid content of 5 g / m 2 using the following paint 1 to prepare a heat transfer color postcard paper.
塗料1 ポリエステル樹脂(バイロン 200、東洋紡(株)) 100部 シリコーン樹脂(SH−3746 トーレシリコーン(株)) 5部 トルエン 500部 MEK 100部 実施例2 印刷インクとして熱硬化性インク(ラミトップ91黒東
洋インク)を用いグラビア印刷を行った以外は実施例1
と同様にして熱転写カラー葉書用紙を製造した。Paint 1 Polyester resin (Byron 200, Toyobo Co., Ltd.) 100 parts Silicone resin (SH-3746 Torre Silicone Co., Ltd.) 5 parts Toluene 500 parts MEK 100 parts Example 2 Thermosetting ink as a printing ink (Lamitop 91 Kurotoyo) Example 1 except that gravure printing was performed using (ink)
A heat transfer color postcard paper was manufactured in the same manner as in.
実施例3 支持体として上質紙の代りにユポコート(VIF210
王子油化合成紙(株)製)を用いた以外は実施例1と同
様にして熱転写カラー葉書用紙を製造した。Example 3 Instead of high-quality paper as a support, YUPO Coat (VIF210
A thermal transfer color postcard paper was manufactured in the same manner as in Example 1 except that Oji Yuka Synthetic Paper Co., Ltd. was used.
実施例4 支持体としてユポ(FPG60王子油化合成紙(株)
製)/上質紙64g/m2/ユポコート(VIF90王
子油化合成紙(株)製)を接着剤で貼合せたものを用い
た以外は実施例1と同様にして熱転写カラー葉書用紙を
製造した。Example 4 As a support, YUPO (FPG60 Oji Oka Synthetic Paper Co., Ltd.)
Heat-transfer color postcard paper was manufactured in the same manner as in Example 1 except that a high-quality paper 64 g / m 2 / Yupo Coat (manufactured by VIF90 Oji Okaka Synthetic Paper Co., Ltd.) was bonded with an adhesive. .
比較例1 通常のインクを用いて印刷を行った以外実施例1と同様
にして熱転写カラー葉書用紙を作成した。Comparative Example 1 A thermal transfer color postcard paper was prepared in the same manner as in Example 1 except that printing was performed using normal ink.
比較例2 実施例1の上質紙の片面のみUVインクで葉書印刷を
し、反対面に、塗料1で実施例1と同様に受容層を形成
した。ついで受容層のうえに、UVインクで印刷を施し
たが、受容層のぬれ性が悪く、印刷できなかった。Comparative Example 2 Postcard printing was performed with UV ink only on one surface of the high-quality paper of Example 1, and a receiving layer was formed on the opposite surface with paint 1 in the same manner as in Example 1. Then, a UV ink was printed on the receiving layer, but the wettability of the receiving layer was poor and printing could not be performed.
比較例3 受容層の上にUVインク硬化型インクにフッ素系界面活
性剤(フロラード、住友3M社製)を添加し、インクの
表面張力を下げたインクを用いた以外は比較例2と同様
に印刷した。Comparative Example 3 Similar to Comparative Example 2 except that a fluorine-based surfactant (Florard, manufactured by Sumitomo 3M Co., Ltd.) was added to the UV ink curable ink on the receiving layer to use an ink whose surface tension was lowered. Printed.
しかし密着性が悪く、インクの裏移りが生じ、鮮明な印
刷ができなかった。However, the adhesion was poor, and ink set-off occurred, making clear printing impossible.
以上の染料熱転写プリンター用シート上に市販の染料熱
転写カラープリンター(VY−20、日立製)でプリン
トして、評価した。プリント面の印刷について、官能検
査で評価した。結果を表1に示す。The above dye thermal transfer printer sheet was printed with a commercially available dye thermal transfer color printer (VY-20, manufactured by Hitachi) and evaluated. The printing on the printed surface was evaluated by a sensory test. The results are shown in Table 1.
第1図は本考案の葉書用紙の一部断面概略図を示し、第
2図は表からみた本考案の葉書の平面図を示す。 1…受容層、2…支持体、3…印刷インクFIG. 1 shows a partial cross-sectional schematic view of a postcard of the present invention, and FIG. 2 shows a plan view of the postcard of the present invention as seen from the table. 1 ... Receptive layer, 2 ... Support, 3 ... Printing ink
Claims (1)
化型インクを用いて所定の印刷をした印刷面上に、熱転
写色材の受容性が良く透明な受容層を設け、反対面に葉
書としての所要の印刷をした、カラー熱転写葉書用紙。1. A transparent receptive layer having good receptivity for a heat transfer colorant is provided on a printed surface on one side of a base material, on which a predetermined printing is performed by using a UV curable ink or a thermosetting ink, and an opposite surface. Color heat transfer postcard paper with the required printing as a postcard on.