JPH06264328A - Smooth-surface cloth, recording cloth for heat-transfer printer, cloth for air-bag, clothes, spinnaker and production of smooth-surface cloth - Google Patents
Smooth-surface cloth, recording cloth for heat-transfer printer, cloth for air-bag, clothes, spinnaker and production of smooth-surface clothInfo
- Publication number
- JPH06264328A JPH06264328A JP5049079A JP4907993A JPH06264328A JP H06264328 A JPH06264328 A JP H06264328A JP 5049079 A JP5049079 A JP 5049079A JP 4907993 A JP4907993 A JP 4907993A JP H06264328 A JPH06264328 A JP H06264328A
- Authority
- JP
- Japan
- Prior art keywords
- cloth
- fabric
- smooth
- less
- surface smooth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、表面の平滑性に富んだ
布帛に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fabric having a smooth surface.
【0002】より詳細には、第1に、文字あるいは画像
あるいは識別マーク等を記録するに適した表面を有する
布帛に関する。More specifically, firstly, it relates to a cloth having a surface suitable for recording characters, images, identification marks, or the like.
【0003】第2に、衣料や雑貨等の製品に関する。よ
り詳しくは、高艶性、防汚性、防塵性、防ダニ性、防寒
性、解れ防止性等に優れた衣料や雑貨等の製品に関す
る。Secondly, it relates to products such as clothing and sundries. More specifically, it relates to products such as clothing and miscellaneous goods which are excellent in high glossiness, antifouling property, dustproof property, mitesproof property, coldproof property, and loosening prevention property.
【0004】なお、本発明で言う布帛とは、絹や木綿等
の天然繊維、ポリエステル系やポリアミド系やポリアク
リロニトリル系等の合成繊維、セルロース系やタンパク
質系の再生繊維及び半合成繊維等から成る織物、編み
物、不織布、ボンデッドファブリック、コーティングフ
ァブリック等を指す。The cloth referred to in the present invention is composed of natural fibers such as silk and cotton, synthetic fibers such as polyester type, polyamide type and polyacrylonitrile type, regenerated fibers of cellulose type and protein type and semi-synthetic fibers. Textiles, knits, non-woven fabrics, bonded fabrics, coated fabrics, etc.
【0005】なお、また、本発明で言う製品とは、衣料
や帽子や襷や旗や鞄や傘やテントや自動車用エアーバッ
グや落下傘、パラグライダー、軽量簡易飛行装置等に使
用される滑空用クロスやスピンネーカー、セールクロス
や布団等、布帛を材料として用い得るもの全てを指す。The product referred to in the present invention is a glide cloth used for clothing, hats, limbs, flags, bags, umbrellas, tents, automobile air bags, parachutes, paragliders, lightweight simple flight devices, etc. , Spinnaker, sail cloth, futon, and the like, all of which can use cloth as a material.
【0006】[0006]
【従来の技術】先ず、本発明の第1の技術分野に関して
説明する。2. Description of the Related Art First, a first technical field of the present invention will be described.
【0007】感熱転写プリンターや昇華型感熱転写プリ
ンター等で文字や画像や識別マーク等の布帛への記録を
試みた場合、布帛の表面平滑性が従来の記録体である感
熱転写専用紙やポリエステルコーティング紙等に比べて
格段に劣るため、殆ど全くと言って良い程画像を記録す
ることはできなかった。When an attempt is made to record characters, images, identification marks, etc. on a cloth with a heat-sensitive transfer printer, a sublimation-type heat-transfer printer, etc., the surface smoothness of the cloth is a conventional recording medium such as heat-sensitive transfer exclusive paper or polyester coating. Since it is much inferior to paper and the like, it was almost impossible to record an image.
【0008】次に、本発明の第2の技術分野に関して説
明する。Next, the second technical field of the present invention will be described.
【0009】衣料や雑貨等の布帛を用いた製品におい
て、多種多様なニーズあるいは感性に応えるため、艶の
ある布帛を用いようとする試みが既になされており、一
部は製品となっている。ところが、これまでそのような
布帛は本質的に柔軟なポリアミド系繊維でしか達成され
ておらず、他の繊維を用いた衣料では柔軟性が失われ、
パリパリになるという問題があった。In order to meet a wide variety of needs and sensibilities in products using cloth such as clothing and miscellaneous goods, attempts have been made to use glossy cloth, and some of them are products. However, until now, such a fabric has been achieved only with essentially flexible polyamide fibers, and clothing using other fibers loses flexibility,
There was a problem of becoming crisp.
【0010】また、防寒性や防ダニ性等を付与する為に
は、布帛の繊維密度、織物の場合には織密度を増大する
必要があるが、それだけでは限界があった。Further, in order to impart the cold-proof property and the mite-proof property, it is necessary to increase the fiber density of the cloth and the woven density in the case of the woven cloth, but this alone has a limit.
【0011】[0011]
【発明が解決しようとする課題】本発明の第一の目的
は、上記問題点を解決し、感熱転写プリンターや昇華型
感熱転写プリンター等を用いて文字や画像や識別マーク
等を布帛に高濃色で鮮明に記録することにある。SUMMARY OF THE INVENTION The first object of the present invention is to solve the above-mentioned problems and to use a thermal transfer printer, a sublimation type thermal transfer printer, or the like to print characters, images, identification marks, etc. on a fabric with high density. To record clearly in color.
【0012】また、本発明の第二の目的は、衣料や雑貨
等において、ポリアミド系繊維以外の繊維からなるもの
でも、パリパリしない艶のある衣料や雑貨等の製品を提
供せんとすることにある。また、それに加えて、防汚
性、防ダニ性、防寒性、解れ防止性等に優れた衣料や雑
貨等の製品を提供することも目的とする。A second object of the present invention is to provide a product such as clothing and miscellaneous goods which is not crispy but glossy even if it is made of a fiber other than polyamide fiber. . In addition to the above, it is also an object to provide products such as clothing and miscellaneous goods which are excellent in antifouling property, anti-mite property, anti-cold property, and anti-loosening property.
【0013】[0013]
【課題を解決するための手段】本発明の表面平滑布帛
は、少なくとも布帛の片面の表面粗さが中心線平均粗さ
3μm未満であること特徴とするものであり、また、少
なくとも布帛の片面の表面粗さが最大高さ10μm未満
であることを特徴とするものであり、また、少なくとも
布帛の片面が実質的にベック平滑度が30秒以上である
ことを特徴とするものであり、また、少なくとも布帛の
片面の上方からの2次元撮影像において、幅5μm以上
かつ長さ50μm以上かつ深さ3μm以上を満たす谷部
の面積が、全面積の5%未満であることを特徴とするも
のである。また、本発明の熱転写プリンタ用記録布帛、
エアーバッグ用布帛、衣料およびスピンネーカーは、上
述の表面平滑布帛を用いることを特徴とするものであ
る。The surface smooth cloth of the present invention is characterized in that the surface roughness of at least one side of the cloth is less than the center line average roughness of 3 μm, and at least one surface of the cloth is at least one side. The maximum height is less than 10 μm, and at least one side of the fabric has a Bekk smoothness of 30 seconds or more. At least in a two-dimensional image taken from above one side of the cloth, the area of the valley portion that satisfies the width of 5 μm or more, the length of 50 μm or more and the depth of 3 μm or more is less than 5% of the total area. is there. Further, a recording cloth for a thermal transfer printer of the present invention,
The fabric for air bags, clothing, and spinnaker are characterized by using the above-mentioned smooth surface fabric.
【0014】本発明の表面平滑布帛の製造方法は、布帛
に、140以上230℃以下の温度で10以上3000
kg/cm2 以下の圧力をかけることを特徴とするものであ
る。また、さらに、本発明の表面平滑布帛の製造方法
は、高圧水流処理を少なくとも布帛の片面の全面積に施
した後、140以上230℃以下の温度で1以上300
0kg/cm2 以下の圧力を掛けることを特徴とするもので
ある。The method for producing a smooth surface fabric according to the present invention is applied to a fabric at a temperature of 140 to 230 ° C. and a temperature of 10 to 3000.
It is characterized by applying a pressure of kg / cm 2 or less. Further, in the method for producing a surface smooth fabric of the present invention, after the high-pressure water stream treatment is applied to at least the entire area of one side of the fabric, the temperature is 140 to 230 ° C. and the temperature is 1 to 300.
It is characterized by applying a pressure of 0 kg / cm 2 or less.
【0015】[0015]
【作用】上記の第一の目的に対しては、鋭意検討の末、
例えば超極細繊維布帛を用いて、高圧プレスを施し、場
合によっては繊維断面が変形するまでプレスすることを
特徴とする著しく表面が平滑な布帛を用いることによっ
て達成され得ることを見い出した。[Function] For the above-mentioned first purpose, after intensive study,
It has been found that this can be achieved, for example, by using a microfiber fabric, which is subjected to a high-pressure press and optionally pressing until the fiber cross section is deformed, using a significantly smooth surfaced fabric.
【0016】また、第二の目的に対しては、例えば上記
方法により作製された、格段に表面が平滑性に富んだ布
帛から構成されてなることを特徴とする製品によって達
成される。The second object is achieved by a product characterized by comprising a cloth having a remarkably smooth surface, which is produced by the above method.
【0017】なお、本発明で言う中心線平均粗さ及び最
大高さとは、JIS B0601に定められる表面粗さ
の定義と表示に基づくものであり、カットオフ値80μ
m、測定長さ800μmにおいて、JIS B0651
に定められる触針式表面粗さ測定器を用い、先端曲率半
径2μmの触針を使用して測定されるものを指す。The center line average roughness and the maximum height referred to in the present invention are based on the definition and display of the surface roughness defined in JIS B0601, and the cutoff value is 80 μm.
m, measurement length 800 μm, JIS B0651
It is measured by using a stylus with a stylus type surface roughness measuring device defined in 1. and a stylus having a tip curvature radius of 2 μm.
【0018】なお、また、本発明で言うベック平滑度と
は、JIS P8119に定められている紙及び板紙の
ベック試験器による平滑度試験方法に基づき得られる表
面の平滑度を指す。本発明では、該方法に準じて布帛の
表面平滑度を規定するものである。ただし、布帛のベッ
ク平滑度の測定に際し、布帛試料の端やゴム製押さえ板
からはみ出た部分は熱融着や適当な樹脂による封止を施
し、また、布帛内部も表面に影響を与えぬように樹脂含
浸を施す等し、実質的に表面平滑度のみを測定できるよ
う注意深く測定試料を作製するものとする。The Beck's smoothness referred to in the present invention refers to the smoothness of the surface obtained based on the Beck's smoothness test method for papers and boards defined in JIS P8119. In the present invention, the surface smoothness of the cloth is defined according to the method. However, when measuring the Bekk smoothness of the fabric, the edges of the fabric sample and the part protruding from the rubber pressing plate are heat-sealed or sealed with an appropriate resin, and the inside of the fabric does not affect the surface. A sample to be measured shall be carefully prepared so that only the surface smoothness can be measured by, for example, impregnating the surface with resin.
【0019】なお、また、本発明で言う撥水度とは、J
IS L1092に定められている繊維製品の防水性試
験方法に基づく撥水度試験の結果を指す。The water repellency referred to in the present invention is J
It refers to the result of a water repellency test based on the waterproofness test method for textiles defined in IS L1092.
【0020】なおまた、本発明で言う識別マークとは、
バーコード、二次元コード、OCR (Optical Character
Recognition )等に記号化されたものであって、それら
に応じた任意の読み取り装置によって光学的に読み取り
処理可能なものであれば、規格は特に限定されるもので
はない。The identification mark referred to in the present invention is
Bar code, 2D code, OCR (Optical Character
The standard is not particularly limited as long as it is a symbolized image such as Recognition) and can be optically read by an arbitrary reading device according to them.
【0021】以下、本発明をさらに詳細に説明する。The present invention will be described in more detail below.
【0022】本発明の表面平滑布帛は、少なくとも布帛
の片面の表面粗さが中心線平均粗さ3μm未満である、
及び/または、少なくとも布帛の片面の表面粗さが最大
高さ10μm未満である、及び/または、少なくとも布
帛の片面が実質的にベック平滑度が30秒以上である、
及び/または、少なくとも布帛の片面の上方からの2次
元撮影像において、幅5μm以上かつ長さ50μm以上
かつ深さ3μm以上を満たす谷部の面積が、全面積の5
%未満であることを特徴とする。これらの規定によっ
て、本発明の第1の目的に対して、感熱転写プリンター
や昇華型感熱転写プリンター等の記録体として用いられ
る専用紙に匹敵する表面平滑度を有する布帛となり得る
のである。また、染色によって画像等を形成した場合に
は、非常に高濃色で鮮明な画像となる。The surface smooth cloth of the present invention has a surface roughness of at least one side of the cloth of less than 3 μm of center line average roughness.
And / or at least one surface of the fabric has a maximum surface roughness of less than 10 μm, and / or at least one surface of the fabric has a Beck smoothness of 30 seconds or more.
And / or at least in a two-dimensional photographed image from above one side of the cloth, the area of the valley portion satisfying a width of 5 μm or more, a length of 50 μm or more and a depth of 3 μm or more is 5% of the total area.
It is less than%. According to these rules, for the first object of the present invention, a cloth having a surface smoothness comparable to that of a dedicated paper used as a recording body of a thermal transfer printer, a sublimation thermal transfer printer, or the like can be obtained. Further, when an image or the like is formed by dyeing, the image becomes a very dark and clear image.
【0023】これらの条件は、中心線平均粗さが1μm
未満であることがより好ましく、また、最大高さが3μ
m未満であることがより好ましく、また、実質的にベッ
ク平滑度が50秒以上であることがより好ましく、ま
た、上記の布帛の上方からの2次元撮影像において、幅
5μm以上かつ長さ50μm以上かつ深さ3μm以上を
満たす谷部の面積が、全面積の3%未満であることがよ
り好ましい。Under these conditions, the center line average roughness is 1 μm.
Is more preferable, and the maximum height is 3μ.
It is more preferable that it is less than m, and it is more preferable that the Beck smoothness is substantially 50 seconds or more. Further, in a two-dimensional photographed image of the above fabric from above, the width is 5 μm or more and the length is 50 μm. It is more preferable that the area of the valley portion satisfying the above and the depth of 3 μm or more is less than 3% of the total area.
【0024】更に、これらの条件は、中心線平均粗さが
0.5μm未満であることが非常に好ましく、また、最
大高さが5μm未満であることが非常に好ましく、ま
た、実質的にベック平滑度が100秒以上であることが
非常に好ましく、また、上記の布帛の上方からの2次元
撮影像において、幅5μm以上かつ長さ50μm以上か
つ深さ3μm以上を満たす谷部の面積が、全面積の1%
未満であることが非常に好ましい。Furthermore, it is highly preferred that these conditions have a center line average roughness of less than 0.5 μm, and a maximum height of less than 5 μm, and substantially no Beck. It is very preferable that the smoothness is 100 seconds or more, and in the two-dimensional photographed image from above the fabric, the area of the valley portion that satisfies the width of 5 μm or more, the length of 50 μm or more, and the depth of 3 μm or more, 1% of total area
It is highly preferred that it is less than.
【0025】これらの布帛は、本発明の第2の目的に対
して、非常に表面が平滑であるので、高艶性が発現す
る。また、布帛表面の繊維が極めて緻密でなければ実質
的に上記条件は満足し得ることができないので、逆に上
記条件を満足し得れば、防ダニ性や羽毛類の抜け防止性
あるいは保持性が発現し、通気性も抑制されるので防寒
性も発現するのである。更にまた、繊維が緻密である
故、解れに対しても強く、汚れも付着しにくくなり、防
水性も良い。For the second object of the present invention, these cloths have a very smooth surface, so that high glossiness is exhibited. If the fibers on the surface of the fabric are not extremely dense, the above conditions cannot be substantially satisfied. On the contrary, if the above conditions can be satisfied, the mites-preventing property, the fall-off preventing property or the retaining property of feathers can be achieved. Is exhibited, and air permeability is also suppressed, so that cold protection is also exhibited. Furthermore, since the fibers are dense, they are resistant to loosening, dirt is less likely to adhere, and they have good waterproofness.
【0026】本発明の表面平滑布帛に用いられる繊維と
しては、特に限定されるものではなく、いかなる繊維を
も用い得るが、単繊維繊度が0.001デニール以上1
デニール未満の超極細繊維から主としてなる布帛であれ
ば、パリパリ調にならないので、極めて好ましく用いら
れるものである。また、後述するが、本発明の表面平滑
布帛を製造する方法において、通常繊維の場合は、繊維
断面を元の形状から変形せしめないと上記の条件を満足
するものになりにくいが、該調極細繊維使いの布帛の場
合には、その変形量は少なくても済むか、あるいは変形
させずとも上記条件を満足する表面平滑布帛になりうる
のである。The fiber used in the surface smooth fabric of the present invention is not particularly limited, and any fiber can be used, but the single fiber fineness is 0.001 denier or more 1
A fabric mainly composed of ultrafine fibers of less than denier does not give a crisp tone, and is therefore extremely preferably used. Further, as will be described later, in the method for producing a surface smooth fabric of the present invention, in the case of ordinary fibers, it is difficult to satisfy the above conditions unless the fiber cross section is deformed from the original shape, In the case of a fabric using fibers, the amount of deformation may be small, or a surface smooth fabric satisfying the above conditions may be obtained without being deformed.
【0027】本発明の布帛は、織物でも編み物でも不織
布でも、その組織は問わないが、織物であり、特に、そ
の組織が平織である場合、解れ防止や寸法/形状安定性
に優れているので、好ましく用いられる。The fabric of the present invention may be woven, knitted or non-woven, regardless of its structure, but is a woven fabric, and particularly when the structure is a plain weave, it is excellent in preventing loosening and dimensional / shape stability. , Preferably used.
【0028】また、布帛の厚さは、特に限定されない
が、200μm以下であれば、パリパリしたりゴワゴワ
したりしないので、好ましい。かかる厚さを実現する意
味でも、調極細繊維使いの布帛は好ましいものである。The thickness of the cloth is not particularly limited, but is preferably 200 μm or less because it does not become crispy or stiff. In terms of realizing such a thickness, a fabric using ultrafine fibers is preferable.
【0029】本発明の布帛に用いられる繊維の組成につ
いては、なんら限定しないが、少なくとも40%がポリ
エステル系繊維からなる、もしくは、主としてポリエス
テル系繊維及び/またはポリアミド系繊維からなるの
が、染色した場合等に高堅牢性を期待できるので、好ま
しく用いられるものである。ポリエステル系繊維やポリ
アミド系繊維については、事細かに列挙するまでもな
く、公知の全てのポリエステルやポリアミドを用いるこ
とができる。また、これらとは別にポリフェニレンサル
ファイドやポリフェニレンスルフォンから主としてなる
布帛も好ましく用いられるものである。The composition of the fibers used in the fabric of the present invention is not particularly limited, but at least 40% is composed of polyester fibers, or is composed mainly of polyester fibers and / or polyamide fibers, which are dyed. It is preferably used because high fastness can be expected in some cases. Regarding the polyester fiber and the polyamide fiber, it is possible to use all known polyesters and polyamides, without mentioning them in detail. In addition to these, a cloth mainly composed of polyphenylene sulfide or polyphenylene sulfone is also preferably used.
【0030】本発明の第1の目的に対しては勿論、第2
の目的に対しても、文字あるいは画像あるいは識別マー
ク等の布帛への記録のタイミングは、必ずしも上述の布
帛が表面平滑度の高い状態で行われるのが必須ではな
く、例えば、予め従来からの捺染によってバックグラウ
ンド的に画像等が染められた状態で、表面平滑性を付与
して本発明の表面平滑布帛とし、感熱転写プリンターや
昇華型感熱転写プリンター等を用いて、更に文字や画像
や識別マーク等を記録することも好ましいものである。For the first object of the present invention, of course, the second
Also for the purpose of, the timing of recording characters, images, identification marks, etc. on the cloth does not necessarily have to be performed in a state where the above-mentioned cloth has a high surface smoothness. The surface smoothness is imparted to the surface smooth cloth of the present invention in the state where the image and the like are dyed in the background by using a thermal transfer printer or a sublimation type thermal transfer printer, and further characters, images or identification marks It is also preferable to record etc.
【0031】本発明の第2の目的の衣料等に用いる場合
には、元々防水性が良好であるが、更に撥水加工が施さ
れていると好ましい結果を得ることがあるので、適宜用
いるべきである。その際、撥水度が90点以上であるこ
とが好ましく、本発明者らの知見によれば、超極細繊維
使いの布帛では、撥水度が100点になるので、超極細
繊維使いの布帛の薄さと相まって、ウィンドブレーカー
やグランドジャケット等には極めて好ましく用いられる
ものである。When it is used for clothing or the like for the second object of the present invention, it is originally excellent in waterproofness, but if water-repellent treatment is further applied, desirable results may be obtained, so it should be used appropriately. Is. At that time, it is preferable that the water repellency is 90 points or more. According to the knowledge of the present inventors, since the water repellency of the cloth using the ultrafine fibers is 100, the cloth using the ultrafine fibers is obtained. Combined with the thinness, it is extremely preferably used for windbreakers, ground jackets and the like.
【0032】また、たとえば、スピンネーカーのような
帆に使うとき、加工後に撥水処理をしてよいが、防汚加
工をするのも好ましい。しかし、一般にプレス後に、こ
れらの加工をすることは困難性を伴なうので、先にこれ
らの加工を施した後、プレス加工をするのが好ましい。
その場合、微細な組織の隅々まで処理剤が染みわたると
いう、極めて優れた特徴が発揮される。この加工法は、
スピンネーカーの場合に限るものではない。For example, when used for a sail such as a spinnaker, water repellent treatment may be carried out after processing, but it is also preferable to carry out antifouling processing. However, since it is generally difficult to perform these processes after pressing, it is preferable to perform these processes first and then press process.
In that case, an extremely excellent feature that the treating agent permeates every corner of the fine structure is exhibited. This processing method is
It is not limited to the case of spinnaker.
【0033】本発明の表面平滑布帛は、自動車の衝突時
のドライバーを保護するエアーバッグのための布帛とし
ても、通気性が抑制された布帛であるので、好ましく用
いられる。The smooth surface fabric of the present invention is preferably used as a fabric for an air bag which protects a driver at the time of a collision of an automobile, because it is a fabric whose breathability is suppressed.
【0034】上述してきた本発明の表面平滑布帛の製造
方法は、特に限定されるものではないが、布帛に、14
0以上230℃以下の温度で、10以上3000kg/cm
2 以下、好ましくは30以上1000kg/cm2 以下、さ
らに好ましくは50以上500kg/cm2 以下のカレンダ
ー処理またはプレス処理を施すことによって、本発明の
表面平滑布帛が得られる。その場合、圧力や温度等を適
宜調節し、繊維断面の形状を元のままにするか、変形さ
せるかは、目的に応じて適宜選択すれば良いが、変形さ
せると、より平滑な表面になるので、特に本発明の第1
の目的に対しては好ましい。The method for producing the surface smooth cloth of the present invention described above is not particularly limited, but the cloth is
10 to 3000 kg / cm at a temperature of 0 to 230 ° C
The surface smooth fabric of the present invention can be obtained by calendering or pressing at 2 or less, preferably 30 or more and 1000 kg / cm 2 or less, and more preferably 50 or more and 500 kg / cm 2 or less. In that case, the pressure and temperature may be adjusted as appropriate to select whether the shape of the fiber cross section should remain unchanged or be deformed, depending on the purpose, but when deformed, a smoother surface is obtained. Therefore, especially the first of the present invention
It is preferable for the purpose of.
【0035】また、布帛に高圧の水流処理を施し、繊維
束を充分開繊させてから、カレンダー処理またはプレス
処理を施せば、上記方法よりも低い圧力で、本発明の表
面平滑布帛が得られるので、好ましい。その条件は、適
宜選択すれば良いが、140以上230℃以下の温度で
1以上3000kg/cm2 以下、好ましくは3以上100
0kg/cm2 以下、さらに好ましくは5以上500kg/cm
2 以下のの圧力で得られる。If the fabric is subjected to a high-pressure water stream treatment to sufficiently open the fiber bundle and then calendered or pressed, the surface smooth fabric of the present invention can be obtained at a pressure lower than that of the above method. Therefore, it is preferable. The conditions may be appropriately selected, but at a temperature of 140 to 230 ° C., 1 to 3000 kg / cm 2 or less, preferably 3 to 100.
0 kg / cm 2 or less, more preferably 5 or more and 500 kg / cm
Obtained at a pressure of 2 or less.
【0036】本発明は、上記のように高艶性、防汚性、
防塵性、防ダニ性、防寒性、解れ防止性、防水性等に優
れた特性を有するので、ウィンドブレーカーやグランド
ジャケットや防塵服等の衣料、帽子、水着、襷、旗、
鞄、傘、テント、自動車用エアーバッグ、落下傘、パラ
グライダー、軽量簡易飛行装置等に使用される滑空用ク
ロスやスピンネーカー、セールクロス、帆、布団、幌、
カーテン類等のインテリア類、各種ディスプレイ品、イ
ンクリボン等に好ましく用いられるのは勿論のこと、予
想外の効果として種々のコーティングを施す場合に、そ
のコーティング剤の塗布量を少なくすることができ、コ
ーティング用基布としても好ましく用いられるものであ
る。これらは、場合にもよるが、布帛が超極細繊維であ
る場合に、特に好ましい効果が現れることが多い。The present invention, as described above, has high glossiness, antifouling property, and
Since it has excellent properties such as dustproof, tickproof, coldproof, unraveling, and waterproof, clothing such as windbreakers, ground jackets and dustproof clothing, hats, swimwear, leggings, flags,
Bags, umbrellas, tents, automobile air bags, parachutes, paragliders, gliding cloths, spinnakers, sailcloths, sails, futons, hoods, etc.
Not only is it preferably used for interiors such as curtains, various display products, ink ribbons, etc., but when applying various coatings as an unexpected effect, the coating amount of the coating agent can be reduced, It is also preferably used as a base fabric for coating. Although depending on the case, these often have particularly preferable effects when the cloth is ultrafine fibers.
【0037】[0037]
【実施例】以下、実施例によって本発明を更に詳細に説
明する。なお、本発明の有効性や権利の範囲はこれによ
って限定されたり、制限を受けるものではない。The present invention will be described in more detail with reference to the following examples. It should be noted that the scope of the validity and rights of the present invention is not limited to or limited by this.
【0038】実施例1 先ず、単繊維繊度0.06デニールの超極細ポリエステ
ルフィラメント700本からなる織糸を、それぞれ経糸
と緯糸に用いて成る高密度布帛にウォータージェットパ
ンチ処理を施した後、通称24トンプレスマシンを用い
て20kg/cm2、190℃にてカレンダー処理を施し
て、表面が平滑かつ緻密な表面平滑布帛を得た。Example 1 First, a high-density fabric composed of 700 ultrafine polyester filaments having a single fiber fineness of 0.06 denier was used as a warp and a weft, respectively. A 24 ton press machine was used to carry out calendering treatment at 20 kg / cm 2 and 190 ° C. to obtain a surface smooth fabric having a smooth and dense surface.
【0039】得られた表面平滑布帛のベック平滑度は、
約70秒であった。The Beck smoothness of the obtained surface smooth fabric is
It was about 70 seconds.
【0040】次に、この布帛に染料型感熱転写プリンタ
ーを用いてバーコードを記録した。そのバーコードをバ
ーコード検証機(RJS ENTERPRISES INC., MODEL AUTOSC
AN6000 )によって検証した結果、IN SPEC の優れたバ
ーコード記録が達成されていることを確認した。Next, a bar code was recorded on the cloth by using a dye type thermal transfer printer. The bar code is a bar code verifier (RJS ENTERPRISES INC., MODEL AUTOSC
As a result of verification by AN6000), it was confirmed that excellent bar code recording of IN SPEC was achieved.
【0041】比較として、上記カレンダー処理を行わず
に得た布帛では、ベック平滑度は10秒以下しかなく、
感熱転写プリンターによって記録されたバーコードの検
証結果は、OUT OF SPEC であり、バーコードとして要求
されるスペックを満たさないものであり、本発明の重要
性が示された。For comparison, the fabric obtained without the above calender treatment had a Beck smoothness of 10 seconds or less,
The verification result of the bar code recorded by the thermal transfer printer is OUT OF SPEC, which does not meet the specifications required as the bar code, and the importance of the present invention was shown.
【0042】実施例2 実施例1で作製した超極細ポリエステル表面平滑布帛を
用いて、衣料としてウィンドブレーカーを製作した。Example 2 Using the ultrafine polyester surface smooth fabric produced in Example 1, a windbreaker was produced as clothing.
【0043】その結果、感性に溢れた艶があり、しかも
それでいてパリパリ感の少ない衣料ができあがった。ま
た、通風の遮断性も極めて優れていた。As a result, a garment having a gloss full of sensibilities and yet a crispness was produced. In addition, the ventilation blocking property was also extremely excellent.
【0044】[0044]
【発明の効果】以上の如く、本発明によれば、従来殆ど
不可能であった布帛への感熱転写プリンターや昇華型感
熱転写プリンター等からの文字や画像や識別マーク等の
記録を、高濃色で鮮明な記録で達成し得るものである。
また、衣料等の布帛製品として、薄さ、柔らかさ、艶、
防塵性、防汚性、防ダニ性、防寒性、解れ防止性等に、
更に染色品の時には高濃色性等の効果を有する。As described above, according to the present invention, recording of characters, images, identification marks and the like from a heat-sensitive transfer printer, a sublimation-type heat-transfer printer or the like onto a cloth, which has been almost impossible in the past, can be performed with high density. This can be achieved by vivid recording in color.
Also, as fabric products such as clothing, thinness, softness, luster,
Dustproof, antifouling, miteproof, coldproof, loosening preventive, etc.
Further, when it is a dyed product, it has effects such as high darkness.
Claims (24)
平均粗さ3μm未満であること特徴とする表面平滑布
帛。1. A surface-smoothed cloth, wherein at least one surface of the cloth has a center line average roughness of less than 3 μm.
平均粗さ0.5μm未満であること特徴とする表面平滑
布帛。2. A surface-smoothed cloth, wherein at least one surface of the cloth has a center line average roughness of less than 0.5 μm.
さ10μm未満であることを特徴とする表面平滑布帛。3. A surface-smoothed cloth having a maximum surface roughness of less than 10 μm on at least one side of the cloth.
さ5μm未満であることを特徴とする表面平滑布帛。4. A surface-smoothed cloth having a maximum surface roughness of less than 5 μm on at least one side of the cloth.
滑度が30秒以上であることを特徴とする表面平滑布
帛。5. A surface smooth cloth, wherein at least one side of the cloth has a Bekk smoothness of substantially 30 seconds or more.
滑度が50秒以上であることを特徴とする表面平滑布
帛。6. A surface smooth cloth, wherein at least one side of the cloth has a Bekk smoothness of substantially 50 seconds or more.
滑度が100秒以上であることを特徴とする表面平滑布
帛。7. A surface-smoothed cloth, wherein at least one side of the cloth has a Bekk smoothness of substantially 100 seconds or more.
撮影像において、幅5μm以上かつ長さ50μm以上か
つ深さ3μm以上を満たす谷部の面積が、全面積の5%
未満であることを特徴とする表面平滑布帛。8. The area of a valley that fills a width of 5 μm or more, a length of 50 μm or more, and a depth of 3 μm or more in at least a two-dimensional photographed image from above one side of the cloth is 5% of the total area.
Surface smooth fabric characterized by being less than.
撮影像において、幅5μm以上かつ長さ50μm以上か
つ深さ3μm以上を満たす谷部の面積が、全面積の1%
未満であることを特徴とする表面平滑布帛。9. A two-dimensional image taken from the upper side of at least one side of the cloth has an area of a valley portion satisfying a width of 5 μm or more, a length of 50 μm or more and a depth of 3 μm or more of 1% of the total area.
Surface smooth fabric characterized by being less than.
001デニール以上1デニール未満の超極細繊維から主
としてなることを特徴とする請求項1、2、3、4、
5、6、7、8または9記載の表面平滑布帛。10. The fibers constituting the cloth have a single fiber fineness of 0.
A superfine fiber having a denier of 001 or more and less than 1 denier is mainly used.
A surface smooth fabric according to 5, 6, 7, 8 or 9.
求項1、2、3、4、5、6、7、8、9または10記
載の表面平滑布帛。11. The surface-smoothed fabric according to claim 1, 2, 3, 4, 5, 6, 7, 8, 9 or 10, wherein the fabric is a woven fabric.
平織であることを特徴とする請求項1、2、3、4、
5、6、7、8、9または10記載の表面平滑布帛。12. The cloth is a woven cloth, and the structure of the woven cloth is a plain weave.
The surface smooth fabric according to 5, 6, 7, 8, 9 or 10.
ものであることを特徴とする請求項1、2、3、4、
5、6、7、8、9、10、11または12記載の表面
平滑布帛。13. The cloth according to claim 1, wherein the cloth has a thickness of 200 μm or less.
The surface smooth cloth according to 5, 6, 7, 8, 9, 10, 11 or 12.
%がポリエステル系繊維からなることを特徴とする請求
項1、2、3、4、5、6、7、8、9、10、11、
12または13記載の表面平滑布帛。14. The fabric comprises at least 40 fibers.
% Consists of polyester fibers, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11,
The surface smooth cloth according to 12 or 13.
ステル系繊維及び/またはポリアミド系繊維からなるこ
とを特徴とする請求項1、2、3、4、5、6、7、
8、9、10、11、12または13記載の表面平滑布
帛。15. The fibers constituting the cloth are mainly composed of polyester fibers and / or polyamide fibers, 1, 2, 3, 4, 5, 6, 7,
The surface smooth fabric according to 8, 9, 10, 11, 12 or 13.
るいは識別マーク等が記録されてなることを特徴とする
請求項1、2、3、4、5、6、7、8、9、10、1
1、12、13、14または15記載の表面平滑布帛。16. The cloth has a smooth surface on which characters, images, identification marks or the like are recorded, and the smooth surface of the cloth is characterized by: 1
The surface smooth fabric according to 1, 12, 13, 14 or 15.
水加工されたものであることを特徴とする請求項1、
2、3、4、5、6、7、8、9、10、11、12、
13、14、15または16記載の表面平滑布帛。17. The fabric according to claim 1, wherein the surface of the fabric has a water repellency of 90 or more.
2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12,
The surface smooth cloth according to 13, 14, 15 or 16.
6、7、8、9、10、11、12、13、14、1
5、16または17記載の表面平滑布帛からなることを
特徴とする熱転写プリンタ用記録布帛。18. Mainly claim 1, 2, 3, 4, 5,
6, 7, 8, 9, 10, 11, 12, 13, 14, 1
A recording cloth for a thermal transfer printer, which is made of the surface smooth cloth described in 5, 16, or 17.
6、7、8、9、10、11、12、13、14、1
5、16または17記載の表面平滑布帛からなることを
特徴とするエアーバッグ用布帛。19. Mainly claim 1, 2, 3, 4, 5,
6, 7, 8, 9, 10, 11, 12, 13, 14, 1
A fabric for an air bag, which is made of the surface smooth fabric according to 5, 16, or 17.
4、5、6、7、8、9、10、11、12、13、1
4、15、16または17記載の表面平滑布帛が用いら
れてなることを特徴とする衣料。20. At least a part of claims 1, 2, 3,
4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 1
A garment characterized in that the surface smooth fabric according to 4, 15, 16 or 17 is used.
4、5、6、7、8、9、10、11、12、13、1
4、15、16または17記載の表面平滑布帛が用いら
れてなることを特徴とするスピンネーカー。21. At least a part of claims 1, 2, 3,
4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 1
A spinnaker comprising the surface smooth cloth according to 4, 15, 16 or 17.
で10以上3000kg/cm2 以下の圧力をかけることを
特徴とする表面平滑布帛の製造方法。22. A method for producing a surface smooth fabric, which comprises applying a pressure of 10 or more and 3000 kg / cm 2 or less at a temperature of 140 or more and 230 ° C. or less to the fabric.
で10以上3000kg/cm2 以下の圧力をかけ、少なく
とも布帛の表面層に位置する繊維の一部または全部を元
の断面形状から変形せしめることを特徴とする表面平滑
布帛の製造方法。23. A pressure of 10 or more and 3000 kg / cm 2 or less is applied to the fabric at a temperature of 140 or more and 230 ° C. or less to deform at least a part or all of the fibers located in the surface layer of the fabric from the original cross-sectional shape. A method for producing a surface-smoothed fabric, comprising:
全面積に施した後、140以上230℃以下の温度で1
以上3000kg/cm2 以下の圧力を掛けることを特徴と
する表面平滑布帛の製造方法。24. After the high-pressure water stream treatment is applied to at least the entire area of one side of the fabric, the treatment is conducted at a temperature of 140 to 230 ° C.
A method for producing a surface-smooth fabric, which comprises applying a pressure of 3000 kg / cm 2 or less.