JPH06257067A - Mat and its production - Google Patents
Mat and its productionInfo
- Publication number
- JPH06257067A JPH06257067A JP3700093A JP3700093A JPH06257067A JP H06257067 A JPH06257067 A JP H06257067A JP 3700093 A JP3700093 A JP 3700093A JP 3700093 A JP3700093 A JP 3700093A JP H06257067 A JPH06257067 A JP H06257067A
- Authority
- JP
- Japan
- Prior art keywords
- tatami mat
- rug
- mat
- coating
- ions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は畳表に抗菌性，脱臭性等
を付与した敷物およびその製造方法に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a rug in which a tatami mat has antibacterial properties and deodorant properties, and a method for producing the rug.
【０００２】[0002]
【従来の技術】従来よく知られているように、い草を織
上げて構成される畳表については、カビ菌その他の細菌
類の付着、悪臭の発生、あるいは日焼け等による変色
等、種々の不具合が生じる。2. Description of the Related Art As is well known in the art, tatami mats made by weaving rush have various problems such as adhesion of mold and other bacteria, generation of bad odor, discoloration due to sunburn, etc. Occurs.
【０００３】近年、このような不具合に対処するため
に、化学薬品等からなる防カビ剤、脱臭剤、抗菌剤ある
いは日焼け防止剤等を畳等に塗布または注入することが
行われている。[0003] In recent years, in order to deal with such a problem, antifungal agents, deodorants, antibacterial agents, sunscreen agents and the like made of chemicals have been applied or injected onto tatami mats and the like.
【０００４】[0004]
【発明が解決しようとする課題】ところが、これまでの
技術では必ずしも所期の効果が得られない場合があり、
また専門的知識を必要としたり、取扱や利用方法が面倒
で、利用者に十分な満足が与えられていない。However, there are cases where the desired effects cannot always be obtained with the conventional techniques,
In addition, the users are not fully satisfied because they require specialized knowledge and are troublesome to handle and use.
【０００５】本発明はこのような事情に鑑みてなされた
もので、畳表自体が高い抗菌効果および脱臭効果を有
し、しかも優れた耐光機能を有し、使用者は何等の手間
も必要としないで快適性が得られる敷物およびその製造
方法を提供することを目的とする。The present invention has been made in view of such circumstances, and the tatami mat itself has a high antibacterial effect and a deodorizing effect, and also has an excellent light resistance function, and the user does not need any trouble. It is an object of the present invention to provide a rug and a method of manufacturing the rug that provides comfort.
【０００６】[0006]
【課題を解決するための手段および作用】本発明の敷物
は、畳表の少なくとも表面に、セラミックスと、銀イオ
ンまたは銅イオンとを含むコーティング層を形成したも
のである（請求項１）。Means and Actions for Solving the Problems The rug of the present invention is one in which a coating layer containing ceramics and silver ions or copper ions is formed on at least the surface of a tatami mat (claim 1).
【０００７】本発明によれば、セラミックスに担持され
た銀イオン（Ａｇ+ ）または銅イオン（Ｃｕ+ ）が高い
抗菌イオンとしての触媒機能を発揮し、あらゆる細菌、
カビ等の培養防止に効果を奏する。また、セラミックス
の膜は、その活性度によりあらゆる臭気（例えば動物の
腐敗臭等）を吸着し、大きい消臭力を発揮する。According to the present invention, silver ions (Ag + ) or copper ions (Cu + ) supported on ceramics exert a catalytic function as a high antibacterial ion, and all bacteria,
It is effective in preventing the culture of mold and the like. Further, the ceramic film adsorbs all kinds of odors (for example, rotting odor of animals) due to its activity, and exerts a great deodorizing power.
【０００８】本発明において望ましくは、セラミックス
が金属酸化物、または金属酸化物と合成樹脂との複合材
を主体として構成されるものである（請求項２）。In the present invention, preferably, the ceramic is mainly composed of a metal oxide or a composite material of a metal oxide and a synthetic resin (claim 2).
【０００９】ここで、望ましい金属酸化物は、Ｓｉ
Ｏ2 ，Ａｌ2 Ｏ 3，ＴｉＯ2 またはＺｒＯ2 から選択さ
れる１種または２種以上の材料であり（請求項３）、ま
た望ましい合成樹脂は、ポリアミドまたはアクリルであ
る（請求項４）。Here, the desirable metal oxide is Si.
The material is one or more materials selected from O 2 , Al 2 O 3 , TiO 2 or ZrO 2 (claim 3), and the desirable synthetic resin is polyamide or acrylic (claim 4).
【００１０】これらの金属酸化物の金属イオンは、接触
する空気中の酸素の一部を活性酸素化して、酸化分解
し、優れた脱臭性能を発揮する。これらは活性炭やゼオ
ライト等と異なり、飽和状態となることがなく、長期間
に亘って脱臭機能を維持することができる。The metal ions of these metal oxides convert some of the oxygen in the air with which they come into contact with active oxygen to undergo oxidative decomposition and exhibit excellent deodorizing performance. Unlike activated carbon and zeolite, these do not become saturated and can maintain the deodorizing function for a long period of time.
【００１１】また、前記合成樹脂を含むものは、動植物
繊維との馴染性がよく、被覆性を向上させることができ
るとともに、乾燥硬化が常温でなされ敷物製造の容易性
確保に好適である。The resin containing the above-mentioned synthetic resin has good compatibility with animal and plant fibers, can improve the covering property, and is suitable for ensuring the ease of rug production because it is dried and cured at room temperature.
【００１２】さらに、セラミックスによるコーティング
層は耐光性を増強し、日焼け防止により畳表の青色保持
期間を通常の畳表の２倍以上に長期化できるとともに、
遠赤外線を発することにより、健康維持にも効果的なも
のとなる。Further, the coating layer made of ceramics enhances the light resistance, and by preventing sunburn, the blue holding period of the tatami mat can be extended to more than twice that of the normal tatami mat.
By emitting far infrared rays, it is also effective for maintaining health.
【００１３】また、本発明の敷物製造方法は、織上げ前
の畳表材料を、超微粒子状のセラミックスと、銀イオン
または銅イオンとを含むコーティング材の溶液に浸漬
し、乾燥後に織上げる方法である（請求項５）。Further, the method for producing a rug of the present invention is a method in which the tatami mat material before weaving is dipped in a solution of a coating material containing ultrafine particle ceramics and silver ions or copper ions, dried and then woven. There is (claim 5).
【００１４】本発明において、畳表材料は、い草，糸等
であり、織上げ前のコーティング材溶液への浸漬によ
り、これら材料の１本１本のそれぞれ全体表面にコーテ
ィング層が形成される。In the present invention, the tatami mat material is rush, thread or the like, and a coating layer is formed on the entire surface of each of these materials by dipping in the coating material solution before weaving.
【００１５】したがって、本発明によれば、乾燥後に織
上げられる畳表がその材料１本毎に抗菌・脱臭コーティ
ングが施されたものとして、極めて高い抗菌効果および
脱臭効果を有し、かつ優れた耐光機能を有するものとな
る。また、セラミックスおよび銀または銅は超微粒子状
であるから、それら粒子の表面積が極めて大きく、各材
料ひいては畳表全体に亘る広大な範囲で前記機能が発揮
される。Therefore, according to the present invention, as the tatami mat to be woven after drying is provided with antibacterial / deodorant coating for each material thereof, it has an extremely high antibacterial effect and deodorant effect, and has excellent light resistance. It has a function. Further, since ceramics and silver or copper are in the form of ultrafine particles, the surface area of these particles is extremely large, and the above-mentioned function is exerted in a vast range over each material, and thus over the entire tatami mat.
【００１６】本発明の別の方法は、織上げた畳表に、超
微粒子状のセラミックスと、銀イオンまたは銅イオンと
を含むコーティング層を浸漬または塗装により形成する
方法である（請求項６）。Another method of the present invention is a method of forming a coating layer containing ultrafine particle ceramics and silver ions or copper ions on a woven tatami mat by dipping or coating (claim 6).
【００１７】本発明において、浸漬の場合には畳表の全
表面および液の浸入し得る隙間部に抗菌・脱臭コーティ
ングが施される。塗装の場合には、主として塗装面、例
えば表面，裏面等に抗菌・脱臭コーティングが施され
る。In the present invention, in the case of immersion, an antibacterial / deodorant coating is applied to the entire surface of the tatami mat and the gaps into which liquid can enter. In the case of painting, an antibacterial / deodorant coating is mainly applied to the painted surface, for example, the front surface or the back surface.
【００１８】塗装方法としては、例えばコーティング材
の溶液を静電塗装，スプレイ，印刷あるいはロールコー
ティング等によって塗布する方法等が採用できる。As a coating method, for example, a method of applying a solution of a coating material by electrostatic coating, spraying, printing or roll coating can be adopted.
【００１９】本発明によれば、所要面に前記各機能を有
する畳表が製造できる。According to the present invention, a tatami mat having the above-mentioned functions on the required surface can be manufactured.
【００２０】[0020]
【実施例】以下、本発明の実施例を説明する。表１に、
本発明で使用するコーティング材の主成分、溶剤、処理
法（塗布等の適性）、乾燥硬化条件等を示している。EXAMPLES Examples of the present invention will be described below. In Table 1,
The main components of the coating material used in the present invention, the solvent, the treatment method (suitability for coating, etc.), the dry curing conditions, etc. are shown.
【００２１】実施例１ 本実施例で使用したコーティング材の主成分は、表１に
示すように、ＳｉＯ2，Ａｌ2 Ｏ3 ，Ａｇ+ である。こ
れらの超微粒子をアルコールに溶かし、畳表にスプレイ
方式で塗布し、８０〜１２０℃で乾燥硬化させた。乾燥
に要した時間は１０〜３０分である。Example 1 As shown in Table 1, the main components of the coating material used in this example are SiO 2 , Al 2 O 3 and Ag + . These ultrafine particles were dissolved in alcohol, applied on a tatami mat by a spray method, and dried and cured at 80 to 120 ° C. The time required for drying is 10 to 30 minutes.
【００２２】実施例２ 本実施例で使用したコーティング材の主成分は、同表に
示すように、ＳｉＯ2，Ａｇ+ である。これらの超微粒
子を水に溶かし、畳表にスプレイ方式で塗布し、常温で
乾燥硬化させた。乾燥に要した時間は１５〜９０分であ
る。Example 2 The main components of the coating material used in this example are SiO2 and Ag + , as shown in the table. These ultrafine particles were dissolved in water, applied on a tatami mat by a spray method, and dried and cured at room temperature. The time required for drying is 15 to 90 minutes.
【００２３】実施例３ 本実施例で使用したコーティング材の主成分は、同表に
示すように、ＳｉＯ2，ＴｉＯ2 ，Ａｇ+ である。これ
らの超微粒子をキシレンに溶かし、畳表にスプレイ方式
で塗布し、１５０℃で乾燥硬化させた。乾燥に要した時
間は略３０分である。Example 3 The main components of the coating material used in this example are SiO 2 , TiO 2 and Ag + , as shown in the table. These ultrafine particles were dissolved in xylene, applied on a tatami mat by a spray method, and dried and cured at 150 ° C. The time required for drying is about 30 minutes.
【００２４】実施例４ 本実施例で使用したコーティング材の主成分は、実施例
２と同様に、ＳｉＯ2，Ａｇ+ である。ただし、これら
の超微粒子を溶かす溶剤はアルコールとした。これを畳
表に印刷方式で塗布し、８０〜１２０℃で乾燥硬化させ
た。乾燥に要した時間は１０〜３０分である。Example 4 The main components of the coating material used in this example are SiO 2 and Ag + , as in Example 2. However, the solvent for dissolving these ultrafine particles was alcohol. This was applied to a tatami mat by a printing method and dried and cured at 80 to 120 ° C. The time required for drying is 10 to 30 minutes.
【００２５】実施例５ 本実施例で使用したコーティング材の主成分は、表１に
示すように、ＳｉＯ2，ＺｒＯ2 ，Ａｇ+ である。これ
らの超微粒子を溶かす溶剤はアルコールとした。これを
畳表に印刷方式で塗布し、８０〜１２０℃で乾燥硬化さ
せた。乾燥に要した時間は１０〜３０分である。Example 5 As shown in Table 1, the main components of the coating material used in this example are SiO 2 , ZrO 2 and Ag + . The solvent for dissolving these ultrafine particles was alcohol. This was applied to a tatami mat by a printing method and dried and cured at 80 to 120 ° C. The time required for drying is 10 to 30 minutes.
【００２６】実施例６ 本実施例で使用したコーティング材の主成分は、実施例
３と同様に、ＳｉＯ2，ＴｉＯ2 ，Ａｇ+ である。これ
らの超微粒子を溶かす溶剤はアルコールとした。これを
畳表に印刷方式で塗布し、８０〜１２０℃で乾燥硬化さ
せた。乾燥に要した時間は１０〜３０分である。Example 6 The main components of the coating material used in this example are SiO 2 , TiO 2 and Ag + , as in Example 3. The solvent for dissolving these ultrafine particles was alcohol. This was applied to a tatami mat by a printing method and dried and cured at 80 to 120 ° C. The time required for drying is 10 to 30 minutes.
【００２７】実施例７ 本実施例で使用したコーティング材の主成分は、表１に
示すように、ＳｉＯ2，Ａｌ2 Ｏ3 ，Ａｇ+ の超微粒子
およびポリアミドである。これらをアルコールに溶か
し、畳表に静電塗装方式で塗布し、常温で乾燥硬化させ
た。乾燥に要した時間は１５〜９０分である。Example 7 As shown in Table 1, the main components of the coating material used in this example are ultrafine particles of SiO 2 , Al 2 O 3 and Ag + and polyamide. These were dissolved in alcohol, applied on the tatami mat by an electrostatic coating method, and dried and cured at room temperature. The time required for drying is 15 to 90 minutes.
【００２８】実施例８ 本実施例で使用したコーティング材の主成分は、同表に
示すように、ＳｉＯ2，Ａｇ+ の超微粒子およびポリア
ミドである。これらを水に溶かし、その水溶液に畳表を
浸漬し、常温で乾燥硬化させた。乾燥に要した時間は１
５〜９０分である。Example 8 The main components of the coating material used in this example are SiO2, Ag + ultrafine particles and polyamide, as shown in the table. These were dissolved in water, the tatami mat was dipped in the aqueous solution, and dried and cured at room temperature. It took 1 time to dry
5 to 90 minutes.
【００２９】他の実施例 前記各実施例以外に、織上げ前の畳表材料を、超微粒子
状のセラミックスと、銀イオンまたは銅イオンとを含む
コーティング材の溶液に浸漬し、乾燥後に織上げ、また
は織上げた畳表に、超微粒子状のセラミックスと、銀イ
オンまたは銅イオンとを含むコーティング層を浸漬また
は塗装により形成する方法を、下記（１）〜（７）のよ
うに種々実施した。Other Examples In addition to the above-mentioned respective examples, the tatami mat material before weaving is dipped in a solution of a coating material containing ultrafine particulate ceramics and silver ions or copper ions, dried and then woven, Alternatively, various methods of forming a coating layer containing ultrafine particle ceramics and silver ions or copper ions by dipping or coating on the woven tatami mat were carried out as in the following (1) to (7).
【００３０】（１）畳表を、コーティング材をアルコー
ル系または水で希釈した溶液に、浸漬後６０〜１５０℃
にて乾燥させた。乾燥時間はアルコール系の場合、５〜
２０秒間、水の場合１０〜２５秒間とした。(1) The tatami mat is soaked in a solution prepared by diluting the coating material with alcohol or water at 60 to 150 ° C.
It was dried at. If alcohol is used, the drying time is 5
It was set to 20 seconds and 10 to 25 seconds for water.
【００３１】（２）畳表を、コーティング材に直接浸漬
後、６０〜１５０℃にて乾燥させた。乾燥時間は５〜２
０秒間とした。(2) The tatami mat was directly immersed in the coating material and then dried at 60 to 150 ° C. Drying time is 5 to 2
It was set to 0 seconds.
【００３２】（３）畳表に、コーティング材をアルコー
ル系または水で希釈した溶液を、静電塗装方式、スプレ
イ方式、あるいはロールコーティング方式で付着させ、
６０〜１５０℃にて乾燥させた。乾燥時間はアルコール
系の場合、２〜１０秒間、水の場合５〜２０秒間とし
た。(3) A solution prepared by diluting the coating material with alcohol or water is applied to the tatami mat by an electrostatic coating method, a spray method, or a roll coating method,
It was dried at 60 to 150 ° C. The drying time was 2 to 10 seconds for alcohol and 5 to 20 seconds for water.
【００３３】（４）畳表に、コーティング材を直接、静
電塗装方式、スプレイ方式あるいはロールコーティング
方式で付着させ、６０〜１５０℃にて乾燥させた。乾燥
時間は５〜２０秒間とした。(4) The coating material was directly applied to the tatami mat by an electrostatic coating method, a spray method or a roll coating method, and dried at 60 to 150 ° C. The drying time was 5 to 20 seconds.
【００３４】（５）前記（１）〜（４）の各方法におい
て、自然乾燥方式にて、製造した。乾燥時間は１５〜９
０分間とした。(5) In each of the above methods (1) to (4), a natural drying method was used. Drying time is 15-9
It was set to 0 minutes.
【００３５】（６）前記（１）〜（５）の各製造方法と
同様の条件において、畳表に織上げる前の段階で、畳表
となる素材（い草，糸等）に個々にコーティングを施し
て、敷物を製造した。(6) Under the same conditions as in each of the production methods (1) to (5), the material (grass, thread, etc.) to be the tatami mat is individually coated at the stage before weaving to the tatami mat. , Manufactured rugs.
【００３６】（７）前記（１）〜（５）の各製造段階
で、コーティング材に顔料、界面活性剤、または硬化触
媒等を添加した。(7) A pigment, a surfactant, a curing catalyst or the like was added to the coating material in each of the production steps (1) to (5).
【００３７】以上の実施例１〜８および他の実施例の結
果、畳表自体が高い抗菌効果および脱臭効果を有し、し
かも優れた耐光機能を有し、使用者は何等の手間も必要
としないで快適性が得られる敷物が製造できた。As a result of the above Examples 1 to 8 and other Examples, the tatami mat itself has a high antibacterial effect and deodorizing effect, and also has an excellent light resistance function, and the user does not need any trouble. We were able to manufacture a rug that gives comfort.
【００３８】なお、本発明は、カーペットその他の敷物
についても応用できることは勿論である。Of course, the present invention can be applied to carpets and other rugs.
【００３９】[0039]
【表１】 [Table 1]
【００４０】[0040]
【発明の効果】以上で詳述したように、請求項１の発明
に係る敷物によれば、セラミックスに担持された銀イオ
ンまたは銅イオンが高い抗菌イオンとしての触媒機能を
発揮し、あらゆる細菌、カビ等の培養防止に効果が奏さ
れ、またセラミックスの膜は、その活性度によりあらゆ
る臭気（例えば動物の腐敗臭等）を吸着し、大きい消臭
力が発揮できる。As described above in detail, according to the rug according to the invention of claim 1, silver ions or copper ions supported on the ceramics exert a catalytic function as high antibacterial ions, and all bacteria, It is effective in preventing the culturing of mold and the like, and the ceramic film adsorbs all kinds of odors (for example, rotting odor of animals) due to its activity, and can exert a great deodorizing power.
【００４１】請求項２〜４の発明によれば、金属酸化物
の金属イオンが、接触する空気中の酸素の一部を活性酸
素化して、酸化分解し、優れた脱臭性能を発揮できる。
これらは活性炭やゼオライト等と異なり、飽和状態とな
ることがなく、長期間に亘って脱臭機能を維持すること
ができる。また、合成樹脂を含むものは、動植物繊維と
の馴染性がよく、被覆性を向上させることができるとと
もに、乾燥硬化が常温でなされるので敷物製造の容易性
が確保できる。さらに、セラミックスによるコーティン
グ層は耐光性を増強し、日焼け防止により畳表の青色保
持期間を通常の畳表の２倍以上に長期化できるととも
に、遠赤外線を発することにより、健康維持にも効果的
なものとなる。According to the second to fourth aspects of the invention, the metal ions of the metal oxide can activate a part of oxygen in the air which comes into contact with it to oxidize and decompose, thereby exhibiting excellent deodorizing performance.
Unlike activated carbon and zeolite, these do not become saturated and can maintain the deodorizing function for a long period of time. In addition, a resin containing a synthetic resin has good compatibility with animal and plant fibers, can improve the covering property, and can be dried and cured at room temperature, so that the rug can be easily manufactured. Furthermore, the ceramic coating layer enhances the light resistance, the blue retention period of the tatami mat can be extended to more than twice as long as that of a normal tatami mat by preventing sunburn, and it is effective for maintaining health by emitting far infrared rays. Becomes
【００４２】また、請求項５の発明に係る敷物の製造方
法によれば、乾燥後に織上げられる畳表がその材料１本
毎に抗菌・脱臭コーティングが施されたものとして、極
めて高い抗菌効果および脱臭効果を有し、かつ優れた耐
光機能を有するものとなる。また、セラミックスおよび
銀または銅は超微粒子状であるから、それら粒子の表面
積が極めて大きく、各材料ひいては畳表全体に亘る広大
な範囲で前記機能が発揮される。Further, according to the method of manufacturing a rug according to the invention of claim 5, the tatami mat to be woven after drying is provided with an antibacterial / deodorant coating for each material thereof, and thus has an extremely high antibacterial effect and deodorant. It has an effect and an excellent light resistance function. Further, since ceramics and silver or copper are in the form of ultrafine particles, the surface area of these particles is extremely large, and the above-mentioned function is exerted in a vast range over each material, and thus over the entire tatami mat.
【００４３】さらに、請求項６の発明によれば、所要面
に前記各機能を有する畳表が製造できる。Further, according to the invention of claim 6, it is possible to manufacture a tatami mat having the above functions on a required surface.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ａ４７Ｇ 27/02 Ｂ 7137−3Ｋ Ｄ０６Ｍ 23/00 Ｅ０４Ｆ 15/02 １０２ Ｎ 7805−2Ｅ １０４ Ａ 7805−2Ｅ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification number Reference number within the agency FI Technical display location A47G 27/02 B 7137-3K D06M 23/00 E04F 15/02 102 N 7805-2E 104 A 7805- 2E
Claims (6)
と、銀イオンまたは銅イオンとを含むコーティング層を
形成してなることを特徴とする敷物。1. A rug characterized in that a coating layer containing ceramics and silver ions or copper ions is formed on at least the surface of a tatami mat.
属酸化物と合成樹脂との複合材を主体とする請求項１に
記載の敷物。2. The rug according to claim 1, wherein the ceramic is mainly composed of a metal oxide or a composite material of a metal oxide and a synthetic resin.
ＴｉＯ2 またはＺｒＯ2 から選択される１種または２種
以上の材料からなる請求項２に記載の敷物。3. The metal oxide is SiO 2 , Al 2 O 3 ,
The rug according to claim 2, which is composed of one or more materials selected from TiO 2 and ZrO 2 .
からなる請求項２に記載の敷物。4. The rug according to claim 2, wherein the synthetic resin is made of polyamide or acrylic.
ラミックスと、銀イオンまたは銅イオンとを含むコーテ
ィング材の溶液に浸漬し、乾燥後に織上げることを特徴
とする敷物の製造方法。5. A method for producing a rug, wherein the tatami mat material before weaving is dipped in a solution of a coating material containing ultrafine particulate ceramics and silver ions or copper ions, and dried and then weaved.
クスと、銀イオンまたは銅イオンとを含むコーティング
層を浸漬または塗装により形成することを特徴とする敷
物の製造方法。6. A method for producing a rug, which comprises forming a coating layer containing ultrafine particulate ceramics and silver ions or copper ions on a woven tatami mat by dipping or coating.