JPH0624808B2 - Laminate - Google Patents
LaminateInfo
- Publication number
- JPH0624808B2 JPH0624808B2 JP60294906A JP29490685A JPH0624808B2 JP H0624808 B2 JPH0624808 B2 JP H0624808B2 JP 60294906 A JP60294906 A JP 60294906A JP 29490685 A JP29490685 A JP 29490685A JP H0624808 B2 JPH0624808 B2 JP H0624808B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- diallyl phthalate
- weight
- parts
- unsaturated polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 （発明の技術分野） 本発明は、表面特性が優れた熱硬化性樹脂積層板に関す
る。TECHNICAL FIELD OF THE INVENTION The present invention relates to a thermosetting resin laminate having excellent surface characteristics.
（従来技術） 熱硬化性樹脂積層板、特にジアリルフタレート樹脂積層
板は、優れた成形性，ポストフォーム加工性を有してお
り、また物理的，化学的特性にも優れた積層板として知
られ、中でも化粧板は落着いた風合いをもつ材料として
好評を博している。しかし、ジアリルフタレート樹脂積
層板は、硬度及び耐シガレット性等の耐熱性の点でメラ
ミン樹脂積層板より劣っており、特にデスク，カウンタ
ー等に代表される天板への使用に際して難点があった。(Prior Art) Thermosetting resin laminates, especially diallyl phthalate resin laminates, are known to have excellent moldability and post-form processability as well as physical and chemical properties. Above all, veneer is popular as a material with a calm texture. However, the diallyl phthalate resin laminated board is inferior to the melamine resin laminated board in terms of hardness and heat resistance such as cigarette resistance, and there is a difficulty in using it particularly for a top board typified by desks, counters and the like.
（発明の目的） 本発明は、上記の如き欠点がなく表面特性の改善された
ジアリルフタレート樹脂もしくは該樹脂と不飽和ポリエ
ステル樹脂との混合樹脂を用いる熱硬化性樹脂積層板を
提供することを目的とする。(Object of the Invention) An object of the present invention is to provide a thermosetting resin laminate using a diallyl phthalate resin or a mixed resin of the resin and an unsaturated polyester resin, which does not have the above-mentioned drawbacks and has improved surface characteristics. And
（発明の構成） 本発明は、印刷紙、織布及び不織布から選ばれた含浸用
基材に下記熱硬化性樹脂組成物が含浸され硬化された表
面層と、合板、パーチクルボード、樹脂が含浸され硬化
されたクラフト紙及び金属板から選ばれた基板とが積層
一体化された積層板である。(Structure of the Invention) The present invention comprises a surface layer obtained by impregnating a substrate for impregnation selected from a printing paper, a woven fabric and a non-woven fabric with the following thermosetting resin composition and cured, and plywood, particle board and resin. It is a laminated plate in which a cured kraft paper and a substrate selected from metal plates are laminated and integrated.
上記熱硬化性樹脂組成物は、ジアリルフタレート樹脂又
は、少なくとも20重量％のジアリルフタレート樹脂と不
飽和ポリエステル樹脂との混合樹脂100重量部に対し
て、分子内にアクリロイル基又はメタアクリロイル基を
４個以上有するジペンタエリスリトールのポリアクリレ
ート又はポリメタアクリレートあるいはこれらの混合物
５〜70重量部と上記樹脂の硬化剤を含む、熱硬化性樹脂
組成物からなる。The thermosetting resin composition is a diallyl phthalate resin or, with respect to 100 parts by weight of a mixed resin of at least 20 wt% diallyl phthalate resin and an unsaturated polyester resin, four acryloyl groups or methacryloyl groups in the molecule. It comprises a thermosetting resin composition containing 5 to 70 parts by weight of a polyacrylate or polymethacrylate of dipentaerythritol or a mixture thereof and the curing agent for the above resin.
本発明におけるジアリルフタレート樹脂とは、既に知ら
れているオルソ，イソ又はテレ−ジアリルフタレートプ
レポリマーの単独またはこれらの混合物もしくはこれら
の変性プレポリマー等のジアリルフタレート系プレポリ
マーをいう。また不飽和ポリエステル樹脂は通常知られ
ている常温で液体状のものもしくは固体状のものが用い
られる。不飽和ポリエステル樹脂を混合樹脂として用い
る場合、ジアリルフタレート樹脂の特徴を生かした積層
板とするためには、ジアリルフタレート樹脂が樹脂中少
なくとも20重量％必要である。The diallyl phthalate resin in the present invention refers to a diallyl phthalate prepolymer such as an already known ortho, iso or tere-diallyl phthalate prepolymer alone or a mixture thereof or a modified prepolymer thereof. As the unsaturated polyester resin, a generally known liquid one or solid one at room temperature is used. When the unsaturated polyester resin is used as the mixed resin, at least 20% by weight of the diallyl phthalate resin in the resin is required in order to obtain a laminated board that takes advantage of the characteristics of the diallyl phthalate resin.
本発明に用いられるジペンタエリスリトールのポリアク
リレート又はポリメタアクリレート（以下両者を総称し
てポリ（メタ）アクリレートという）としては、分子内
にアクリロイル基又はメタアクリロイル基（以下両者を
総称して（メタ）アクリロイル基という）を４個以上有
するポリ（メタ）アクリレートの単独もしくは混合物が
用いられる。（メタ）アクリロイル基が３個以下のポリ
又はモノ（メタ）アクリレートではジアリルフタレート
樹脂もしくは不飽和ポリエステル樹脂との相溶性が充分
でなく、目的とする効果が得られない。As the polyacrylate or polymethacrylate of dipentaerythritol used in the present invention (hereinafter, both are collectively referred to as poly (meth) acrylate), an acryloyl group or a methacryloyl group (hereinafter both are collectively referred to as (meth)). ) A poly (meth) acrylate having four or more acryloyl groups) is used alone or as a mixture. Poly or mono (meth) acrylates having 3 or less (meth) acryloyl groups do not have sufficient compatibility with the diallyl phthalate resin or the unsaturated polyester resin, and the desired effects cannot be obtained.
本発明に用いられるポリ（メタ）アクリレートは、ジペ
ンタエリスリトールジハイドロオキシテトラアクリレー
ト，ジペンタエリスリトールジハイドロオキシテトラメ
タアクリレート，ジペンタエリスリトールモノハイドロ
オキシペンタアクリレート，ジオペンタエリスリトール
モノハイドロオキシペンタメタアクリレート，ジペンタ
エリスリトールヘキサアクリレート，ジペンタエリスリ
トールヘキサメタアクリレートの六種類であり、これら
は単独で又は混合物として用いられる。配合量はジアリ
ルフタレート樹脂又は不飽和ポリエステル樹脂とジアリ
ルフタレート樹脂の混合樹脂100重量部に対して５〜70
重量部、好ましくは10〜50重量部の範囲が適当である。
５重量部未満では本発明の目的とする表面特性の改善効
果が充分に得られず、また70重量部を越えると硬化物が
固くなりすぎて脆くなったり、加工時樹脂がベトついて
作業性に問題を生ずることになる。The poly (meth) acrylate used in the present invention includes dipentaerythritol dihydroxytetraacrylate, dipentaerythritol dihydroxytetramethacrylate, dipentaerythritol monohydroxypentaacrylate, diopentaerythritol monohydroxypentamethacrylate, There are six kinds of dipentaerythritol hexaacrylate and dipentaerythritol hexamethacrylate, which are used alone or as a mixture. The compounding amount is 5 to 70 relative to 100 parts by weight of diallyl phthalate resin or a mixed resin of unsaturated polyester resin and diallyl phthalate resin.
A range of parts by weight, preferably 10 to 50 parts by weight is suitable.
If the amount is less than 5 parts by weight, the effect of improving the surface properties, which is the object of the present invention, cannot be sufficiently obtained. If the amount is more than 70 parts by weight, the cured product becomes too hard and becomes brittle, and the resin becomes sticky during processing to improve workability. This will cause problems.
本発明の組成物には、通常知られるジアリルフタレート
樹脂又は不飽和ポリエステル樹脂の硬化剤が添加され
る。また必要に応じて他種の反応性モノマーや該技術分
野に通常用いられる添加剤、例えば内部離型剤，充填
剤，難燃剤，重合禁止剤，顔料等を添加することができ
る。A commonly known curing agent for diallyl phthalate resin or unsaturated polyester resin is added to the composition of the present invention. Further, if necessary, other kinds of reactive monomers and additives usually used in the technical field such as an internal mold release agent, a filler, a flame retardant, a polymerization inhibitor, a pigment and the like can be added.
本発明組成物を用いて積層板を製造するには、適当な溶
剤、例えばアセトン，トルエン，メチルエチルケトン等
の有機溶剤に組成物を溶解させて樹脂液を調製し、これ
を基材に用途に応じて適量含浸せしめて乾燥後、合板や
パーチクルボード、あるいは通常の樹脂を含浸せしめた
クラフト紙をコアとして積層加熱成形することによって
達成される。また本発明組成物を含浸せしめた基材を加
熱硬化させた後、アルミニウム板等の金属板に接着剤を
用いて積層することもできる。To produce a laminate using the composition of the present invention, a resin solution is prepared by dissolving the composition in an appropriate solvent, for example, an organic solvent such as acetone, toluene, methyl ethyl ketone, etc. It is achieved by impregnating a suitable amount of the resin and drying it, and then laminating and heat-molding it with plywood, particle board, or ordinary resin-impregnated kraft paper as the core. Further, the base material impregnated with the composition of the present invention may be heat-cured and then laminated on a metal plate such as an aluminum plate using an adhesive.
上記含浸用基材としては、印刷紙，織布，不織布が選ば
れる。加熱成形条件は、従来知られるジアリルフタレー
ト樹脂又は不飽和ポリエステル樹脂の成形条件でよく、
通常100〜160℃、１〜60kg／cm2、１〜60分間で充分で
ある。As the base material for impregnation, printing paper, woven cloth, or non-woven cloth is selected. The heat molding conditions may be those of conventionally known diallyl phthalate resin or unsaturated polyester resin,
Usually, 100 to 160 ° C., 1 to 60 kg / cm 2 , and 1 to 60 minutes are sufficient.
（発明の効果） 本発明のジペンタエリスリトールのポリ（メタ）アクリ
レートを含む組成物を用いた積層板は、該ポリ（メタ）
アクリレートを含まない従来のジアリルフタレート樹脂
もしくは不飽和ポリエステル樹脂を用いた積層板と較べ
て引き掻き硬度及び耐シガレット性等の表面特性が飛躍
的に向上しており、従来使用困難とされていた天板用に
も使用可能となったものである。(Effects of the Invention) A laminate using the composition containing the poly (meth) acrylate of dipentaerythritol of the present invention is
Surface properties such as scratch hardness and cigarette resistance are dramatically improved compared to conventional laminates using acrylate-free diallyl phthalate resin or unsaturated polyester resin, making it difficult to use. It can also be used for boards.
（実施例） 実施例１〜３ 比較例１〜３ 表１に示される樹脂組成物をベタ印刷された坪量100ｇ
／m2の印刷紙に含浸させ、乾燥後樹脂付着量130ｇ／m2
の含浸紙を得た。(Examples) Examples 1 to 3 Comparative Examples 1 to 3 Solid weight 100 g of the resin composition shown in Table 1
/ M 2 impregnated in printing paper and dried, resin adhesion amount 130g / m 2
To obtain an impregnated paper.
別に通常のジアリルフタレート樹脂を含浸させたクラフ
ト紙（総坪量240ｇ／m2、内樹脂付着量100ｇ／m2）２枚
を用意し、その２枚重ねの上に上記含浸紙を重ね、ツヤ
有り鏡面板を用いて130℃、30kg／cm2でプレスし、挿入
20分後に水冷して積層板を得た。Separately, prepare two sheets of kraft paper impregnated with a normal diallyl phthalate resin (total basis weight 240 g / m 2 , inner resin adhesion amount 100 g / m 2 ), and stack the above-mentioned impregnated paper on top of the two sheets, and then gloss Insert by pressing at 130 ° C, 30kg / cm 2 using a mirror plate
After 20 minutes, it was cooled with water to obtain a laminated plate.
上記積層板の表面引き掻き硬度及び耐シガレット性を測
定しその結果を表１に示した。The surface scratch hardness and cigarette resistance of the above laminated plate were measured, and the results are shown in Table 1.
表面引き掻き硬度：ＪＡＳ規格Ａ試験による10点平均
値、深さ（μ）。Surface scratch hardness: 10-point average value by JAS standard A test, depth (μ).
耐シガレット性：火付きタバコを２分間放置後メタノー
ルで清拭した後の表面状態の観察。Cigarette resistance: Observation of the surface condition after leaving a lit cigarette for 2 minutes and wiping it with methanol.
評価 （２点による平均） ○ 変色殆んどなし × 焼けによる着色あり なお、比較例２は樹脂組成物が混ざり合わず成形ができ
なかった。また比較例３は本発明に使用されるポリ（メ
タ）アクリレートとは異なる他種のポリアクリレートを
使用した例である。Evaluation (Average of 2 points) O Almost no discoloration x Coloring due to burning In Comparative Example 2, the resin compositions were not mixed and molding was not possible. Comparative Example 3 is an example in which another type of polyacrylate different from the poly (meth) acrylate used in the present invention was used.
Claims (1)
用基材に下記熱硬化性樹脂組成物（Ｉ）が含浸され硬化
された表面層と、合板、パーチクルボード、樹脂が含浸
され硬化されたクラフト紙及び金属板から選ばれた基板
とが積層一体化された積層板。 （Ｉ）ジアリルフタレート樹脂又は、少なくとも20重量
％のジアリルフタレート樹脂と不飽和ポリエステル樹脂
との混合樹脂100重量部に対して、分子内にアクリロイ
ル基又はメタアクリロイル基を４個以上有するジペンタ
エリスリトールのポリアクリレート又はポリメタアクリ
レートあるいはこれらの混合物５〜70重量部と上記樹脂
の硬化剤を含む、熱硬化性樹脂組成物。1. A surface layer obtained by impregnating a thermosetting resin composition (I) below onto a substrate for impregnation selected from a printing paper, a woven fabric and a non-woven fabric, and a plywood, a particle board, and a resin. A laminated plate in which the kraft paper and the substrate selected from the metal plates are laminated and integrated. (I) A diallyl phthalate resin or a dipentaerythritol having 4 or more acryloyl groups or methacryloyl groups in a molecule with respect to 100 parts by weight of a mixed resin of at least 20% by weight of a diallyl phthalate resin and an unsaturated polyester resin. A thermosetting resin composition comprising 5 to 70 parts by weight of a polyacrylate or polymethacrylate or a mixture thereof and a curing agent for the above resin.