JPH06193280A - Concrete repairing method with unidirectionally arranged fiber-reinforced sheet - Google Patents
Concrete repairing method with unidirectionally arranged fiber-reinforced sheetInfo
- Publication number
- JPH06193280A JPH06193280A JP4359043A JP35904392A JPH06193280A JP H06193280 A JPH06193280 A JP H06193280A JP 4359043 A JP4359043 A JP 4359043A JP 35904392 A JP35904392 A JP 35904392A JP H06193280 A JPH06193280 A JP H06193280A
- Authority
- JP
- Japan
- Prior art keywords
- reinforcing fiber
- fiber sheet
- resin
- repair
- concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、一方向に配列した強化
繊維を有する強化繊維シートをコンクリート補修面に適
合し、この強化繊維にマトリクス樹脂を含浸させて硬化
することによりコンクリート面を補修する方法に関する
ものであり、特に、強化繊維シートのコンクリート面に
対する接着強度を向上させ、補修強度を増大することの
できるコンクリート補修方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention adapts a reinforcing fiber sheet having reinforcing fibers arranged in one direction to a concrete repair surface, and impregnates the reinforcing fiber with a matrix resin to cure the concrete surface to repair the concrete surface. The present invention relates to a method, and more particularly to a concrete repair method capable of improving the adhesive strength of a reinforcing fiber sheet to a concrete surface and increasing the repair strength.
【０００２】[0002]
【従来の技術】近年、橋梁や高架道路などの橋脚を繊維
強化プラスチックにより補修することが行なわれてい
る。本出願人は、特開平３−２２２７３４号公報、特開
平３−２２４９０１号公報などに記載されるように、補
修現場で施工性良く補修を行なうことができ且つ補修後
の強度も向上した構築物の補修のための強化繊維シート
を提案した。図４にこの一方向配列強化繊維シートの概
略を示す。2. Description of the Related Art In recent years, bridge piers such as bridges and elevated roads have been repaired with fiber reinforced plastics. As described in JP-A-3-222734, JP-A-3-224901, etc., the applicant of the present invention can construct a structure which can be repaired at a repair site with good workability and also has improved strength after repair. A reinforced fiber sheet for repair was proposed. FIG. 4 shows an outline of the unidirectionally arranged reinforcing fiber sheet.
【０００３】つまり、強化繊維シート１は、接着剤層３
が設けられた支持体２と、接着剤層３を介して支持体２
上に一方向に配列して接着された強化繊維４とからな
る。又、この強化繊維シート１は、橋梁や高架道路など
の補修現場で強化繊維４にマトリクス樹脂を含浸させ
て、補修面に貼り付けた後硬化される。That is, the reinforcing fiber sheet 1 has the adhesive layer 3
And the support 2 provided with the adhesive 2 and the support 2
The reinforcing fibers 4 are arranged in one direction and bonded to the upper side. Further, the reinforcing fiber sheet 1 is hardened after the reinforcing fiber 4 is impregnated with a matrix resin at a repair site such as a bridge or an elevated road and attached to the repair surface.
【０００４】この強化繊維シ−ト１上の強化繊維４への
マトリクス樹脂の含浸は、シ−ト１を補修面に貼り付け
る前に行なうか、或は、補修面にマトリクス樹脂を塗布
し、その上からシ−ト１を貼り付けて押し付けることに
よりマトリクス樹脂を強化繊維に含浸させることが行な
われている。又、よりマトリクス樹脂の強化繊維への含
浸性を良くするために、強化繊維シ−ト１の支持体２を
ガラス繊維クロスシートなどで作製し、強化繊維シ−ト
１を補修面に貼り付けた後、支持体２側からマトリクス
樹脂を塗布し、マトリクス樹脂を強化繊維へと含浸させ
ることが行なわれている。The impregnation of the reinforcing resin 4 on the reinforcing fiber sheet 1 with the matrix resin is carried out before the sheet 1 is attached to the repair surface, or the matrix resin is applied to the repair surface. A matrix resin is impregnated into the reinforcing fiber by pasting and pressing the sheet 1 from above. In order to improve the impregnation property of the matrix resin into the reinforcing fiber, the support 2 of the reinforcing fiber sheet 1 is made of glass fiber cloth sheet or the like, and the reinforcing fiber sheet 1 is attached to the repair surface. After that, the matrix resin is applied from the support 2 side to impregnate the reinforcing resin with the matrix resin.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、本発明
者らの研究実験の結果によると、補修面が橋梁や高架道
路のコンクリート面であり、しかも物理的に長さが十分
に採れず、強化繊維シートのための貼付け面積を十分に
確保し得ないような補強箇所の場合には、上記いずれの
方法にて強化繊維シート１をコンクリート面に貼り付け
たとしても、図５に示すように、矢印Ｍ方向に曲げ応力
が加わる場合には、梁５のコンクリート補修面５ａと強
化繊維シート１との間の接着面に発生する剪断応力によ
り、先ず、強化繊維シート１のいずれかの端部が剥離
し、その後この剥離が強化繊維シート１全体へと波及
し、強化繊維シート１による補強効果が急激に低下する
ことが分かった。However, according to the results of the research and experiment conducted by the present inventors, the repair surface is a concrete surface of a bridge or an elevated road, and the physical length of the repair surface is not sufficient. In the case of a reinforced portion where the pasting area for the sheet cannot be sufficiently secured, even if the reinforcing fiber sheet 1 is pasted on the concrete surface by any of the above methods, as shown in FIG. When a bending stress is applied in the M direction, first, one of the ends of the reinforcing fiber sheet 1 peels off due to the shearing stress generated on the adhesive surface between the concrete repair surface 5a of the beam 5 and the reinforcing fiber sheet 1. After that, it was found that this peeling spreads to the entire reinforcing fiber sheet 1 and the reinforcing effect of the reinforcing fiber sheet 1 suddenly decreased.
【０００６】従って、本発明の目的は、一方向配列強化
繊維シートにより橋梁や高架道路などを初めとする構築
物の補修をするに際し、十分な貼付け面積を確保し得な
い場合においても、強化繊維シートのコンクリート補修
面に対する接着強度を向上させ、補修強度を増大するこ
とのできるコンクリート補修方法を提供することであ
る。Therefore, an object of the present invention is to provide a reinforced fiber sheet even when it is not possible to secure a sufficient pasting area when repairing a structure such as a bridge or an elevated road by using the unidirectionally arranged reinforced fiber sheet. It is an object of the present invention to provide a concrete repairing method capable of improving the adhesive strength to a concrete repair surface and increasing the repair strength.
【０００７】[0007]
【課題を解決するための手段】上記目的は本発明に係る
一方向配列強化繊維シートによるコンクリート補修方法
にて達成される。要約すれば本発明は、一方向に配列し
た強化繊維を有する強化繊維シートをコンクリート補修
面に適合し、この強化繊維にマトリクス樹脂を含浸させ
て硬化することによりコンクリート面を補修する方法に
おいて、強化繊維シートの両端部に位置してコンクリー
ト面に溝を形成し、この溝に樹脂を充填することを特徴
とする一方向配列強化繊維シートによるコンクリート補
修方法である。好ましくは、前記溝部に位置した強化繊
維シートの端部は、樹脂が充填された溝内へと折り込ま
れる。The above objects can be achieved by the method for repairing concrete with a unidirectionally arranged reinforcing fiber sheet according to the present invention. In summary, the present invention provides a method of repairing a concrete surface by adapting a reinforcing fiber sheet having unidirectionally arranged reinforcing fibers to a concrete repair surface, impregnating the reinforcing fiber with a matrix resin and curing. A concrete repair method using a unidirectionally arranged reinforced fiber sheet, characterized in that grooves are formed on a concrete surface at both ends of a fiber sheet and the grooves are filled with resin. Preferably, the end of the reinforcing fiber sheet located in the groove is folded into the resin-filled groove.
【０００８】[0008]
【実施例】図１は本発明に係る補修方法の一実施例を示
すものであって、本実施例では、一方向配列強化繊維シ
ート１を使用して梁５などを補修する場合を示す断面図
である。EXAMPLE FIG. 1 shows an example of a repairing method according to the present invention. In this example, a cross section showing a case where a unidirectionally arranged reinforcing fiber sheet 1 is used to repair a beam 5 or the like. It is a figure.
【０００９】本発明に使用される一方向配列強化繊維シ
ート１は、任意の構成のものを使用し得るが、例えば、
図４に示されるように、支持体２と、接着剤層３を介し
てこの支持体２上に一方向に配列して接着された強化繊
維４とにて構成される。The unidirectionally arranged reinforcing fiber sheet 1 used in the present invention may have an arbitrary constitution.
As shown in FIG. 4, it is composed of a support body 2 and reinforcing fibers 4 which are arranged in one direction on the support body 2 via an adhesive layer 3 and bonded.
【００１０】支持体２は、補修時における強化繊維４へ
のマトリクス樹脂の含浸性を良くするために、スクリム
クロス、ガラスペーパー、ガラス不織布、ガラス繊維ク
ロス、ポリアミド、ＰＰＳ（ポリフェニレンサルファイ
ド）などの各種ポリマーの不織布などを使用するのが好
ましい。The support 2 is made of scrim cloth, glass paper, glass non-woven fabric, glass fiber cloth, polyamide, PPS (polyphenylene sulfide) or the like in order to improve the impregnation property of the matrix resin into the reinforcing fibers 4 during repair. It is preferable to use a polymer non-woven fabric or the like.
【００１１】又、接着剤層３を形成する接着剤として
は、原則として支持体２上に強化繊維４を一時的に接着
できるものならば何でもよいが、好ましくは接着剤はマ
トリクス樹脂との相溶性のよい樹脂を使用することが良
く、例えばマトリクス樹脂としてエポキシ樹脂を使用す
るときには、エポキシ系の接着剤を用いることがよい。
接着剤層３の厚みとしては、強化繊維４を支持体２上に
一時的に接着できればよいことから、１〜５０μｍ、好
ましくは３〜２０μｍ程度あればよい。In principle, any adhesive can be used as the adhesive for forming the adhesive layer 3 as long as the reinforcing fibers 4 can be temporarily adhered to the support 2, but the adhesive is preferably a matrix resin. It is preferable to use a resin having a good solubility. For example, when an epoxy resin is used as the matrix resin, an epoxy adhesive is preferably used.
The thickness of the adhesive layer 3 may be 1 to 50 μm, preferably 3 to 20 μm, as long as the reinforcing fibers 4 can be temporarily adhered to the support 2.
【００１２】強化繊維４としては、ピッチ系炭素繊維、
ボロン繊維、ＰＡＮ系炭素繊維、アラミド繊維、ガラス
繊維、スチール繊維、ポリエステル繊維、ポリエチレン
繊維など各種の繊維を使用することができる。又、これ
らの繊維は単独で使用する他、２種以上を組合せて繊維
をハイブリッド化して使用することもできる。As the reinforcing fiber 4, pitch-based carbon fiber,
Various fibers such as boron fiber, PAN-based carbon fiber, aramid fiber, glass fiber, steel fiber, polyester fiber and polyethylene fiber can be used. Further, these fibers may be used alone or in combination of two or more kinds to hybridize the fibers.
【００１３】強化繊維４は、これをフィラメントとして
収束剤で多数本収束した繊維束又は軽度に撚りをかけて
収束した繊維束を接着剤層３上に並べて上方から押し潰
すことにより軽度にバラされ、これにより強化繊維４は
収束剤または撚りによる結合により複数層に積層した状
態で、支持体２上に接着剤層３を介して一方向に配列し
て接着される。The reinforcing fibers 4 are lightly separated by arranging a large number of fiber bundles, which are bundled with a sizing agent, as filaments, or lightly twisted and bundled fiber bundles on the adhesive layer 3 and crushing them from above. As a result, the reinforcing fibers 4 are bonded and arranged in one direction on the support 2 via the adhesive layer 3 in a state of being laminated in a plurality of layers by a binding agent or a binding by twisting.
【００１４】このような一方向配列の強化繊維シート１
は、図１に示すように、橋梁や高架道路の梁などの構築
物の補修現場で、ローラ、刷毛、吹付け等の適宜な塗布
手段により強化繊維シート１の強化繊維４にマトリクス
樹脂を塗布して含浸させ、強化繊維４の側を構築物の補
修箇所側として補修されるコンクリート面に貼り付け
る。必要に応じて、強化繊維シート１は所望の数だけ積
層される。好ましくは、積層の度ごとに、支持体２の側
からハンドローラ等でマトリクス樹脂の含浸操作を行な
う。その後、その上にカバーを行い、その後そのまま放
置して、或は加熱して、マトリクス樹脂を硬化する。Such a unidirectionally arranged reinforcing fiber sheet 1
As shown in FIG. 1, a matrix resin is applied to the reinforced fibers 4 of the reinforced fiber sheet 1 by an appropriate application means such as rollers, brushes, spraying, etc. at the repair site of structures such as bridges and beams of elevated roads. Then, the reinforcing fiber 4 side is attached to the concrete surface to be repaired as the side of the structure to be repaired. If necessary, the reinforcing fiber sheets 1 are laminated in a desired number. Preferably, the matrix resin is impregnated with a hand roller or the like from the side of the support 2 every time the layers are laminated. After that, a cover is provided on it, and then it is left as it is or heated to cure the matrix resin.
【００１５】このように、本発明の強化繊維シート１
は、補修に用いる際、補修現場で強化繊維４にマトリク
ス樹脂を含浸させて使用されるが、補修箇所へのシート
１の貼り付け後そのまま放置することにより、マトリク
ス樹脂を硬化することができるようにするために、マト
リクス樹脂は室温硬化型の樹脂を使用するのが好まし
い。Thus, the reinforcing fiber sheet 1 of the present invention
When used for repair, the reinforcing fiber 4 is impregnated with the matrix resin at the repair site, and the matrix resin can be cured by leaving it as it is after the sheet 1 is attached to the repair location. Therefore, it is preferable to use a room temperature curable resin as the matrix resin.
【００１６】室温硬化型樹脂としては、硬化剤及び硬化
促進剤の配合を調節して室温で硬化するようにしたエポ
キシ樹脂、不飽和ポリエステル樹脂等が使用できる。As the room temperature curable resin, an epoxy resin, an unsaturated polyester resin or the like in which the composition of a curing agent and a curing accelerator is adjusted to cure at room temperature can be used.
【００１７】別法として、補修箇所に室温硬化型のマト
リクス樹脂を例えば１００μｍ程度の厚みに塗布し、次
いで強化繊維４の側を補修箇所側として強化繊維シート
１を貼り付ける。必要に応じて、引き続き、同じ手順に
て、強化繊維シート１を所望の数だけ積層し、最後に支
持体２の側から強化繊維４にマトリクス樹脂３０を含浸
させる。又、このとき、各シート１を積層する度に、支
持体２の側から強化繊維４にマトリクス樹脂を含浸させ
ることもできる。その後は、上記と同様に、シート１上
にカバーを行い、その後そのまま放置してマトリクス樹
脂を硬化させる。As an alternative method, a room temperature curing type matrix resin is applied to the repaired portion in a thickness of, for example, about 100 μm, and then the reinforcing fiber sheet 1 is attached with the side of the reinforcing fiber 4 as the repaired portion side. If necessary, subsequently, the desired number of reinforcing fiber sheets 1 are laminated by the same procedure, and finally the reinforcing fibers 4 are impregnated with the matrix resin 30 from the support 2 side. At this time, each time the sheets 1 are laminated, the reinforcing fibers 4 may be impregnated with the matrix resin from the support 2 side. After that, as in the above case, the sheet 1 is covered and then left as it is to cure the matrix resin.
【００１８】本発明によると、強化繊維シート１による
補修工事を行なうに際して、図１及び図２に示すよう
に、先ず、補修されるコンクリート面には、強化繊維シ
ートの両端部に位置して、この強化繊維シートの両端縁
部に沿って、即ち、強化繊維の軸線に対して直交する方
向に、コンクリート面に溝１０が形成される。According to the present invention, when carrying out repair work using the reinforcing fiber sheet 1, first, as shown in FIGS. 1 and 2, the concrete surface to be repaired is positioned at both ends of the reinforcing fiber sheet. Grooves 10 are formed on the concrete surface along both edges of the reinforcing fiber sheet, that is, in a direction orthogonal to the axis of the reinforcing fiber.
【００１９】前記溝１０の幅Ｗ及び深さＤは、任意とす
ることができるが、一般に、幅Ｗは、５〜３０ｍｍ、通
常８ｍｍ程度とされ、その深さＤは、５〜１０ｍｍ、通
常８ｍｍ程度とされる。本発明にて重要なことは、強化
繊維シート１の両端部が、溝１０の上に位置することで
あり、換言すれば、本発明を有効に実施するには強化繊
維シート１の両端部の溝１０への突出量△Ｗは、少なく
とも２ｍｍ以上が必要である。又、溝１０の断面形状
は、図示されるようにＵ字形状とすることもできるが、
矩形断面とすることもできる。更に、溝１０の幅Ｈは、
強化繊維シート１の幅ｈと同じとすることもできるが、
例えば１０〜２０ｍｍ程度大きくすることが望ましい。The width W and the depth D of the groove 10 may be arbitrary, but generally, the width W is 5 to 30 mm, usually about 8 mm, and the depth D is 5 to 10 mm, usually. It is about 8 mm. What is important in the present invention is that both ends of the reinforcing fiber sheet 1 are located above the grooves 10. In other words, in order to effectively carry out the present invention, both ends of the reinforcing fiber sheet 1 are The protrusion amount ΔW into the groove 10 needs to be at least 2 mm or more. The cross-sectional shape of the groove 10 may be U-shaped as shown in the drawing,
It can also have a rectangular cross section. Further, the width H of the groove 10 is
Although it can be the same as the width h of the reinforcing fiber sheet 1,
For example, it is desirable to increase the size by about 10 to 20 mm.
【００２０】更に、本発明では、前記溝１０に樹脂１１
が充填される。この樹脂１１は、強化繊維シート１の両
端部に対する接着力が大とされるものであれば任意のも
のを使用し得るが、好ましくはマトリクス樹脂との相溶
性のよい樹脂を使用することが良く、例えばマトリクス
樹脂としてエポキシ樹脂を使用するときには、エポキシ
系の接着剤などを用いるのが好ましい。更に、不飽和ポ
リエステル樹脂、ビニルエステル樹脂、ウレタン樹脂な
どを使用し得る。Further, in the present invention, resin 11 is provided in the groove 10.
Is filled. Any resin can be used as the resin 11 as long as it has a large adhesive force to both ends of the reinforcing fiber sheet 1, but it is preferable to use a resin having a good compatibility with the matrix resin. For example, when an epoxy resin is used as the matrix resin, it is preferable to use an epoxy adhesive or the like. Further, unsaturated polyester resin, vinyl ester resin, urethane resin and the like can be used.
【００２１】更に、本発明の他の実施例によると、図３
に示すように、溝１０に位置した強化繊維シートの端部
を、樹脂１１が充填された溝内へと折り込むこともでき
る。この場合に、強化繊維シート端部の折り込み量△Ｌ
は５〜３０ｍｍ、通常８ｍｍ程度とされる。Further, according to another embodiment of the present invention, FIG.
As shown in, the end portion of the reinforcing fiber sheet located in the groove 10 can be folded into the groove filled with the resin 11. In this case, the amount of folding of the reinforcing fiber sheet edge ΔL
Is 5 to 30 mm, usually about 8 mm.
【００２２】本発明者らは、強化繊維４として炭素繊維
を使用し、支持体２としてガラス繊維クロスシートを使
用した強化繊維シート１を作製した。炭素繊維糸目付け
は１７５ｇ／ｍ2 であった。又、強化繊維シートはその
長さが１３５ｍｍ、幅が１５０ｍｍであり、強化繊維は
長手方向に配列された。The present inventors produced a reinforcing fiber sheet 1 using carbon fibers as the reinforcing fibers 4 and a glass fiber cloth sheet as the support 2. The carbon fiber yarn weight was 175 g / m 2 . The reinforcing fiber sheet had a length of 135 mm and a width of 150 mm, and the reinforcing fibers were arranged in the longitudinal direction.
【００２３】試験片は、厚さ５０ｍｍ、幅１５０ｍｍ、
長さ４００ｍｍの断面が矩形とされるコンクリート片で
あり、幅Ｗ×深さＤ×長さＨ＝８×８×１５０ｍｍとさ
れる溝１０が、中心間距離１３５ｍｍにて形成された。
従って、強化繊維シート１の両端部の溝１０への突出量
△Ｗは４ｍｍであった。The test piece has a thickness of 50 mm and a width of 150 mm,
Grooves 10 each having a length of 400 mm and a rectangular cross section, and having a width W × depth D × length H = 8 × 8 × 150 mm were formed with a center-to-center distance of 135 mm.
Therefore, the protrusion amount ΔW of the both ends of the reinforcing fiber sheet 1 into the groove 10 was 4 mm.
【００２４】強化繊維シート１が貼り付けられるコンク
リート面５ａはサンダーがけを行ない、その後、プライ
マーを塗布して下地処理を行なった。その後、このコン
クリート面に、マトリクス樹脂を含浸した強化繊維シー
ト１を貼り付けた。マトリクス樹脂としてはエポキシ樹
脂を使用した。又、コンクリート面に形成した溝１０内
には、エポキシ系接着剤１１を充填した。The concrete surface 5a to which the reinforcing fiber sheet 1 was attached was sanded, and then a primer was applied to perform a surface treatment. Then, the reinforcing fiber sheet 1 impregnated with the matrix resin was attached to the concrete surface. An epoxy resin was used as the matrix resin. An epoxy adhesive 11 was filled in the groove 10 formed on the concrete surface.
【００２５】図６に示すように、上記試験片を、互いに
３００ｍｍ離隔した支点に支持して、試験片の中央部に
押圧荷重Ｐを付与した。As shown in FIG. 6, the test piece was supported by fulcrums separated from each other by 300 mm, and a pressing load P was applied to the central portion of the test piece.
【００２６】図５に示す従来の補修方法では、押圧荷重
Ｐが８５０Ｋｇ、変形量０．４５ｍｍにて試験片Ｓの中
央部に亀裂が発生し、同時に、強化繊維シート１は一方
の端部から剥離し、十分な強化繊維シート１による補強
効果が得られなかった。In the conventional repairing method shown in FIG. 5, a crack is generated in the central portion of the test piece S when the pressing load P is 850 kg and the deformation amount is 0.45 mm, and at the same time, the reinforcing fiber sheet 1 starts from one end. It was peeled off, and a sufficient reinforcing effect by the reinforcing fiber sheet 1 was not obtained.
【００２７】一方、図１に示す本発明の補修方法によれ
ば、押圧荷重Ｐが８５０Ｋｇ、変形量０．４５ｍｍにて
試験片Ｓの中央部に亀裂が発生し始めたが、脆性的破壊
に至ることはなかった。更に押圧荷重を増大したとこ
ろ、押圧荷重Ｐが１０２０Ｋｇ、変形量０．８ｍｍにて
試験片Ｓは中央部より破壊した。しかしながら、強化繊
維シート１の両端部がコンクリート面から剥離すること
はなく、従来の補修方法より約２０％程度補修強度が増
大した。On the other hand, according to the repairing method of the present invention shown in FIG. 1, a crack started to occur in the central portion of the test piece S when the pressing load P was 850 kg and the deformation amount was 0.45 mm, but brittle fracture occurred. It never came. When the pressing load was further increased, the pressing load P was 1020 kg and the deformation amount was 0.8 mm, and the test piece S was broken from the central portion. However, both ends of the reinforcing fiber sheet 1 were not separated from the concrete surface, and the repair strength was increased by about 20% as compared with the conventional repair method.
【００２８】又、図２に示す本発明の補修方法によれ
ば、先の場合と同様に、押圧荷重Ｐが８５０Ｋｇ、変形
量０．４５ｍｍにて試験片Ｓの中央部に亀裂が発生し始
めたが、脆性的破壊に至ることはなく、更に押圧荷重を
増大したところ、押圧荷重Ｐが１１００Ｋｇ、変形量
０．９ｍｍにて試験片Ｓは中央部より破壊した。しかし
ながら、強化繊維シート１の両端部がコンクリート面か
ら剥離することはなく、従来の補修方法より約３０％程
度補修強度が増大した。Further, according to the repairing method of the present invention shown in FIG. 2, as in the previous case, a crack starts to occur in the central portion of the test piece S when the pressing load P is 850 kg and the deformation amount is 0.45 mm. However, brittle fracture did not occur, and when the pressing load was further increased, the test piece S broke from the central part when the pressing load P was 1100 kg and the deformation amount was 0.9 mm. However, both ends of the reinforcing fiber sheet 1 were not separated from the concrete surface, and the repair strength was increased by about 30% as compared with the conventional repair method.
【００２９】[0029]
【発明の効果】以上説明したように、本発明に係る一方
向配列強化繊維シートによるコンクリート補修方法によ
れば、強化繊維シートの両端部に位置してコンクリート
面に溝を形成し、この溝に樹脂が充填され、好ましく
は、更に、強化繊維シートの両端部が溝内へと折り込ま
れるので、強化繊維シートのコンクリート補修面に対す
る接着強度が向上し、その結果、補修効果が増大する。As described above, according to the method for repairing concrete with a unidirectionally arranged reinforcing fiber sheet according to the present invention, grooves are formed on the concrete surface at both ends of the reinforcing fiber sheet, and the grooves are formed in the grooves. It is filled with resin, and preferably both ends of the reinforcing fiber sheet are folded into the groove, so that the adhesive strength of the reinforcing fiber sheet to the concrete repair surface is improved, and as a result, the repair effect is increased.
【図１】本発明のコンクリート面補修方法の一実施例を
説明する断面図である。FIG. 1 is a cross-sectional view illustrating an embodiment of a concrete surface repairing method of the present invention.
【図２】本発明のコンクリート面補修方法の一実施例を
説明する、図１の下方より見た図である。FIG. 2 is a view for explaining an embodiment of the concrete surface repairing method of the present invention, which is seen from below in FIG.
【図３】本発明のコンクリート面補修方法の他の実施例
を説明する断面図である。FIG. 3 is a sectional view for explaining another embodiment of the concrete surface repairing method of the present invention.
【図４】本発明に使用し得る強化繊維シートの一実施例
を説明する図である。FIG. 4 is a diagram illustrating an example of a reinforcing fiber sheet that can be used in the present invention.
【図５】従来のコンクリート面補修方法を説明する図で
ある。FIG. 5 is a diagram illustrating a conventional concrete surface repairing method.
【図６】試験片を使用した補強試験方法を説明する斜視
図である。FIG. 6 is a perspective view illustrating a reinforcing test method using a test piece.
１ 強化繊維シート ２ 支持体 ３ 接着剤層 ４ 強化繊維 ５ 被補強体 １０ 溝 １１ 充填樹脂 1 Reinforcing Fiber Sheet 2 Support 3 Adhesive Layer 4 Reinforcing Fiber 5 Reinforced Body 10 Groove 11 Filling Resin
Claims (2)
繊維シートをコンクリート補修面に適合し、この強化繊
維にマトリクス樹脂を含浸させて硬化することによりコ
ンクリート面を補修する方法において、強化繊維シート
の両端部に位置してコンクリート面に溝を形成し、この
溝に樹脂を充填することを特徴とする一方向配列強化繊
維シートによるコンクリート補修方法。1. A method for repairing a concrete surface by adapting a reinforcing fiber sheet having reinforcing fibers arranged in one direction to a concrete repair surface, impregnating the reinforcing fiber with a matrix resin and curing the resin. A method for repairing concrete with a unidirectionally arranged reinforcing fiber sheet, characterized in that a groove is formed on a concrete surface at both ends of and a resin is filled into the groove.
部を、樹脂が充填された溝内へと折り込むことを特徴と
する請求項１の一方向配列強化繊維シートによるコンク
リート補修方法。2. The method for repairing concrete with a unidirectionally arranged reinforced fiber sheet according to claim 1, wherein an end portion of the reinforced fiber sheet located in the groove portion is folded into a groove filled with resin.