JPH06191140A - Recording medium and recording method therefor - Google Patents
Recording medium and recording method thereforInfo
- Publication number
- JPH06191140A JPH06191140A JP34503192A JP34503192A JPH06191140A JP H06191140 A JPH06191140 A JP H06191140A JP 34503192 A JP34503192 A JP 34503192A JP 34503192 A JP34503192 A JP 34503192A JP H06191140 A JPH06191140 A JP H06191140A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- light
- recording
- heat
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、高耐蝕性を持つテレフ
ォンカ−ドやオレンジカ−ドとして用いられる記録媒体
およびこの記録媒体に対する記録方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a recording medium used as a telephone card or an orange card having high corrosion resistance and a recording method for the recording medium.
【0002】[0002]
【従来の技術】近年、電話、交通機関、流通分野等にテ
レフォンカードやオレンジカードのような金額減算式の
プリペイドカードが一般的に使用されるようになってき
た。プリペイドカードに対する記録方式は磁気記録や熱
記録、機械的な穴あけが用いられている。ユーザーの使
い易すさの面から磁気記録と熱記録の併用が増えてきて
いる。2. Description of the Related Art In recent years, an amount subtraction type prepaid card such as a telephone card and an orange card has been generally used in the fields of telephone, transportation, distribution and the like. Magnetic recording, thermal recording, and mechanical perforation are used as recording methods for prepaid cards. The combination of magnetic recording and thermal recording is increasing in terms of user friendliness.
【0003】サーマルヘッドなどを用いた感熱記録で
は、記録層にスズ(融点236℃)膜等を採用した保安
性が高いカードが記録媒体として用いられるようになっ
てきた。In heat-sensitive recording using a thermal head or the like, a card having a high security, which uses a tin (melting point 236 ° C.) film as a recording layer, has come to be used as a recording medium.
【0004】このように記録層にスズなどの金属膜を採
用した場合、保安性は非常に高くなるが、金属薄膜を溶
融破壊することにより画像を形成するために、高いエネ
ルギを必要とする。最近では、サーマルヘッドのように
記録媒体と接触して記録するのではなく、レーザ等を用
いて非接触で記録する光記録の需要も高まっている。When a metal film of tin or the like is used for the recording layer as described above, the security is very high, but high energy is required to form an image by melting and breaking the metal thin film. Recently, there is an increasing demand for optical recording in which contactless recording is performed by using a laser or the like instead of contacting with a recording medium for recording as in a thermal head.
【0005】このようなカード媒体の材料として、レー
ザ光等が照射されるとその記録層がレーザ光の熱によっ
て融解、蒸発、凝集などの熱的な変形を生じ、その変形
した領域の光学的な特性が変化することによって画像を
形成する熱的記録材料が知られている(特開昭56−8
293号公報)。As a material for such a card medium, when a laser beam or the like is irradiated, the recording layer undergoes thermal deformation such as melting, evaporation, or aggregation due to the heat of the laser beam, and the optical deformation of the deformed region is caused. A thermal recording material that forms an image by changing its characteristics is known (Japanese Patent Laid-Open No. 56-8).
293).
【0006】また、近赤外付近に主波長を有するレーザ
光によって記録する基材の上に塩基性染料と有機顕色材
とを含有する感熱発色層、近赤外付近を含有する光吸収
層を設けた光記録媒体が開示されている。(特開平2−
209290号公報)。Further, a thermosensitive coloring layer containing a basic dye and an organic developer on a base material for recording with a laser beam having a dominant wavelength in the near infrared region, and a light absorbing layer containing in the near infrared region. An optical recording medium provided with is disclosed. (JP-A-2-
209290).
【0007】これら記録媒体にレーザ光を使用して直接
肉眼で判読可能なレーザ光を画像を記録する記録方式、
および記録装置として特開平2−204087号公報に
開示されている。A recording system in which an image is recorded on the recording medium by using laser light which is directly readable by the naked eye.
Also, a recording device is disclosed in Japanese Patent Application Laid-Open No. 2-204087.
【0008】[0008]
【発明が解決しようとする課題】従来の接触型記録方式
のカード、たとえばサーマルヘッドを用いた感熱記録で
は、記録層にスズ(融点236℃)膜等を用いて、記録
時にはその金属薄膜を溶融破壊することにより画像を形
成する。そのため、記録層上層の保護層等も破壊してし
まい、記録層そのものが外部環境と直接接するので腐食
等が起こり易くなる。In thermal recording using a conventional contact type recording card, for example, a thermal head, a tin (melting point 236 ° C.) film or the like is used for the recording layer, and the metal thin film is melted during recording. An image is formed by destroying. Therefore, the protective layer or the like above the recording layer is also destroyed, and the recording layer itself is in direct contact with the external environment, so that corrosion or the like is likely to occur.
【0009】また、耐蝕性を高めるために金属薄膜を用
いているのに、その金属薄膜を溶融するためには高いエ
ネルギを記録層に与えなければならず、そのため保護層
も同時に破壊してしまい、悪循環を起こしている。Further, although the metal thin film is used to enhance the corrosion resistance, high energy must be applied to the recording layer in order to melt the metal thin film, so that the protective layer is destroyed at the same time. , Is creating a vicious circle.
【0010】一方、レーザ光を利用した非接触型記録の
場合、光吸収層を設けている場合もあるが、基本的には
レーザ光の熱エネルギにより感熱記録層を発色させるも
のである。そのため、数W程度のエネルギが必要とな
り、装置の大型化、高価格化といった問題点が生じる。On the other hand, in the case of non-contact type recording using a laser beam, a light absorbing layer may be provided, but basically, the thermal recording layer is colored by the thermal energy of the laser beam. Therefore, energy of about several watts is required, which causes problems such as an increase in size and cost of the device.
【0011】本発明では、高耐蝕性を有するとともに、
低エネルギでの記録が可能な非接触型感熱破壊の記録媒
体およびこの記録媒体に対する記録方法を提供すること
を目的とする。The present invention has high corrosion resistance and
It is an object of the present invention to provide a non-contact type heat-sensitive destruction recording medium capable of recording with low energy and a recording method for the recording medium.
【0012】[0012]
【課題を解決するための手段】本発明では前記課題を解
決するために、基材と、この基材上に積層された着色層
と、この着色層に積層され該着色層を遮蔽、あるいは着
色層と異なる色に着色された記録層と、この記録層に積
層され光が照射されたとき発熱し、その熱で前記記録層
を溶融破壊する無色または淡色の光−熱変換層と、この
光−熱変換層に積層され該光−熱変換層の吸収主波長と
異なる吸収主波長を有する保護層とを具備してなる。In order to solve the above problems, the present invention provides a substrate, a coloring layer laminated on the substrate, and a coloring layer laminated on the coloring layer to shield or color the coloring layer. A recording layer colored in a color different from that of the layer; a colorless or light-colored light-heat conversion layer laminated on the recording layer to generate heat when irradiated with light and melt and destroy the recording layer with the heat; A protective layer laminated on the heat conversion layer and having an absorption dominant wavelength different from the absorption dominant wavelength of the light-heat conversion layer.
【0013】また、基材と、この基材上に積層された着
色層と、この着色層に積層され光が照射されたとき発熱
する無色または淡色の光−熱変換層と、この光−熱変換
層に積層され該光−熱変換層の吸収主波長と異なる吸収
主波長を有するとともに、前記着色層を遮蔽、あるいは
着色層と異なる色に着色され前記光−熱変換層の発熱に
より溶融破壊される記録層と、この記録層に積層され前
記光−熱変換層の吸収主波長と異なる吸収主波長を有す
る保護層とを具備してなる。Further, a base material, a colored layer laminated on the base material, a colorless or light-colored light-heat conversion layer which is laminated on the colored layer and generates heat when irradiated with light, and the light-heat It is laminated on the conversion layer and has an absorption main wavelength different from the absorption main wavelength of the light-heat conversion layer, and shields the coloring layer or is colored in a color different from the coloring layer and melts and breaks due to heat generation of the light-heat conversion layer. And a protective layer laminated on the recording layer and having an absorption dominant wavelength different from the absorption dominant wavelength of the light-heat conversion layer.
【0014】また、基材と、この基材上に積層された着
色層と、この着色層に積層され光−熱変換材料を含有す
るとともに、前記着色層を遮蔽、あるいは着色層と異な
る色に着色され光が照射されたとき発熱し、その熱で溶
融破壊する記録層と、この記録層に積層され記録層の吸
収主波長と異なる吸収主波長を有する保護層とを具備し
てなる。In addition, the base material, the colored layer laminated on the base material, and the light-heat converting material laminated on the colored layer are contained, and the colored layer is shielded or has a color different from that of the colored layer. It is provided with a recording layer which is colored and generates heat when irradiated with light and melts and breaks down by the heat, and a protective layer which is laminated on the recording layer and has an absorption main wavelength different from the absorption main wavelength of the recording layer.
【0015】さらに、基材上に順次、着色層、記録層、
光−熱変換層および保護層を積層してなる記録媒体に対
して特定波長の光を照射し、この光照射により前記光−
熱変換層を発熱させてその熱で前記記録層を溶融破壊
し、この溶融破壊により前記着色層が露出することによ
り画像を形成する。Further, a colored layer, a recording layer, and a
A recording medium formed by laminating a light-heat conversion layer and a protective layer is irradiated with light of a specific wavelength, and the light irradiation causes the light-
An image is formed by causing the heat converting layer to generate heat and melting and destroying the recording layer by the heat and exposing the colored layer by this melting and destroying.
【0016】[0016]
【作用】上記手段により、熱源が保護層と記録層の間の
光−熱変換層、あるいは、光−熱変換部材を含有する記
録層となり、熱効率が高く、小さなエネルギ−での記録
が可能となり、保護層の傷つきを防止できるとともに、
耐蝕性も非常に高くなる。By the above means, the heat source becomes the light-heat conversion layer between the protective layer and the recording layer, or the recording layer containing the light-heat conversion member, so that the heat efficiency is high and the recording with a small energy becomes possible. , While preventing damage to the protective layer,
Corrosion resistance is also very high.
【0017】[0017]
【実施例】以下、本発明を図1乃至図3に示す一実施例
を参照して説明する。図1は感熱破壊の記録媒体の層構
成を示すもので、図中5は基材である。この基材5上に
は順次、着色層4、記録層3、光−熱変換層2および保
護層1が積層されている。上記光−熱変換層2は無色ま
たは淡色である。上記光−熱変換層2の材料としては光
記録手段の主波長を主吸収波長部に持つことが望まし
い。ここでは、図2の半導体レーザ7の発光主波長であ
る830nmに合わせて、光−熱変換層2の材料として
は近赤外吸収材が用いられている。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below with reference to an embodiment shown in FIGS. FIG. 1 shows the layer structure of a recording medium which suffers from heat-sensitive destruction. In the figure, 5 is a substrate. A colored layer 4, a recording layer 3, a light-heat conversion layer 2 and a protective layer 1 are sequentially laminated on the base material 5. The light-heat conversion layer 2 is colorless or light-colored. As a material for the light-heat conversion layer 2, it is desirable to have the main wavelength of the optical recording means in the main absorption wavelength part. Here, a near-infrared absorbing material is used as the material of the light-heat conversion layer 2 in accordance with the main emission wavelength of 830 nm of the semiconductor laser 7 of FIG.
【0018】近赤外吸収材としてシアニン色素、チオー
ルニッケル錯体などがある。無色または淡色の近赤外吸
収材下地色を白色化するので好ましく、ビス(1,6−
ジクロロ−3,4−ジチオフェノレート)白金−テトラ
プチルアンモニュムなどが挙げられる。レーザ記録に適
した光−熱変換材料については特開昭57−14096
号、特開平2−209290号などに示されている。Examples of near infrared absorbing materials include cyanine dyes and thiol nickel complexes. A colorless or light-colored near-infrared absorbing material is preferable because it makes the underlying color white.
Dichloro-3,4-dithiophenolate) platinum-tetraptylammonium and the like. A light-heat conversion material suitable for laser recording is disclosed in JP-A-57-14096.
And Japanese Patent Laid-Open No. 2-209290.
【0019】また、上記保護層1は基本的に樹脂系の材
料でできていて、光−熱変換層2の吸収主波長である近
赤外波長域(750〜900nm)と異なる吸収主波長
(2000〜3000nm)を有している。上記記録層
3は着色層4を遮蔽、あるいは着色層4と異なる色に着
色されていて、ワックス、熱可塑性樹脂、低融点金属等
が用いられる。The protective layer 1 is basically made of a resin material and has a dominant absorption wavelength (750 to 900 nm) different from the near infrared wavelength range (750 to 900 nm) which is the dominant absorption wavelength of the light-heat conversion layer 2. 2000-3000 nm). The recording layer 3 shields the colored layer 4 or is colored in a color different from that of the colored layer 4, and wax, a thermoplastic resin, a low melting point metal or the like is used.
【0020】ワックスとしては、融点60〜200℃程
度の合成ワックス、カルナバ・ワックス等を、熱可塑性
樹脂としては、ポリエステル樹脂、塩ビ樹脂、酢ビ樹
脂、ポリスチレン樹脂等を、低融点金属としては、ス
ズ、鉛、ビスマス、インジウム等を用いることができ
る。図2は図1の感熱破壊記録媒体6に対し画像を記録
するための記録装置の例を示す。As the wax, synthetic wax having a melting point of about 60 to 200 ° C., carnauba wax, etc., as the thermoplastic resin, polyester resin, vinyl chloride resin, vinyl acetate resin, polystyrene resin, etc., and as the low melting point metal, Tin, lead, bismuth, indium, etc. can be used. FIG. 2 shows an example of a recording device for recording an image on the thermosensitive destruction recording medium 6 of FIG.
【0021】すなわち、図中7は半導体レーザで、この
半導体レーザ7から出射されるレ−ザ光の光路中にはコ
リメータレンズ8、シリンドリカルレンズ9および回転
自在なポリゴンミラー10が配設されている。また、上
記ポリゴンミラー10によって反射されるレ−ザ光の光
路中にはfθレンズ11が設けられている。図中6は矢
印方向に搬送される記録媒体である。That is, reference numeral 7 in the drawing denotes a semiconductor laser, and a collimator lens 8, a cylindrical lens 9 and a rotatable polygon mirror 10 are arranged in the optical path of the laser light emitted from the semiconductor laser 7. . An fθ lens 11 is provided in the optical path of the laser light reflected by the polygon mirror 10. Reference numeral 6 in the figure denotes a recording medium conveyed in the direction of the arrow.
【0022】記録媒体6に画像を形成する場合には、画
像データに従って偏重されたレーザ光が半導体レーザ7
から発光される。このレーザ光はコリメ−タレンズ8お
よびシリンドリカルレンズ9を介してポリゴンミラ−1
0に送られる。このポリゴンミラ−10に送られたレー
ザ光はポリゴンミラーの回転によって偏向され、記録媒
体6の表面を点順次に走査する。When an image is formed on the recording medium 6, the laser beam deviated according to the image data is used as the semiconductor laser 7.
Is emitted from. This laser light is passed through a collimator lens 8 and a cylindrical lens 9 to produce a polygon mirror-1.
Sent to 0. The laser light sent to the polygon mirror 10 is deflected by the rotation of the polygon mirror and scans the surface of the recording medium 6 in a dot-sequential manner.
【0023】この装置では矢印A方向に記録媒体6が搬
送され、あらかじめ求めた記録層3を溶融するのに十分
な半導体レーザ駆動条件で画像データに応じて半導体レ
ーザ7を駆動することにより記録を行なう。In this apparatus, the recording medium 6 is conveyed in the direction of the arrow A, and recording is performed by driving the semiconductor laser 7 in accordance with the image data under the semiconductor laser driving condition sufficient to melt the recording layer 3 which is obtained in advance. To do.
【0024】レーザ光が図1に示す感熱破壊の記録媒体
6に照射されると、図3(a)に示すように、光−熱変
換層2に照射された光は光−熱変換され、照射された光
量に応じた熱を発生する。When the laser beam is applied to the heat-sensitive recording medium 6 shown in FIG. 1, as shown in FIG. 3A, the light applied to the light-heat conversion layer 2 undergoes light-heat conversion. Generates heat according to the amount of light applied.
【0025】この熱により、記録層3の対応する部分が
溶融破壊され、図3(b)に示すように凝集する。光の
照射されない部分は記録層3が着色層4を遮蔽している
ために着色層4が見えないが、光の照射された部分は上
述のように記録層3が破壊され、下層の着色層4が見え
るようになり、記録層3と着色層4のコントラストで画
像が形成される。By this heat, the corresponding portion of the recording layer 3 is melted and destroyed and aggregates as shown in FIG. 3 (b). The colored layer 4 is not visible in the portion not irradiated with light because the recording layer 3 shields the colored layer 4, but in the portion irradiated with light, the recording layer 3 is destroyed as described above, and the colored layer underneath. 4 is visible, and an image is formed with the contrast between the recording layer 3 and the coloring layer 4.
【0026】なお、従来の接触型記録、たとえばサーマ
ルヘッドを用いた感熱破壊記録では、熱源が保護層の外
にあったために、記録層を溶融するためには保護層もそ
れに相当する高い温度にしなければならず、保護層が破
壊され耐蝕性が不十分であった。In conventional contact type recording, for example, thermal destructive recording using a thermal head, since the heat source is outside the protective layer, in order to melt the recording layer, the protective layer is set to a correspondingly high temperature. The protective layer was destroyed and the corrosion resistance was insufficient.
【0027】本発明による感熱破壊の記録媒体6を記録
装置を用いて記録した場合、熱源は保護層1と記録層3
の間の光−熱変換層2であるために、熱効率が高く、保
護層1を多少傷つけてしまうが破壊しないので、耐蝕性
も非常に高くなる。本発明は上記一実施例に限られるも
のではなく、図4に示すように構成されるものであって
も良い。なお、上記一実施例と同一部分については、同
一番号を付してその説明を省略する。図4に示す実施例
においては、光−熱変換層2と記録層3の配置構成が上
記実施例のものと逆になっている。記録層3は光−熱変
換層2の吸収主波長と異なる吸収主波長を有している。When the recording medium 6 for heat-sensitive destruction according to the present invention is recorded by using a recording device, the heat sources are the protective layer 1 and the recording layer 3.
Since it is the light-heat conversion layer 2 between the two, the thermal efficiency is high, and the protective layer 1 is slightly damaged but not destroyed, so that the corrosion resistance is also very high. The present invention is not limited to the above-mentioned embodiment, but may be configured as shown in FIG. The same parts as those in the above-described embodiment are designated by the same reference numerals and the description thereof will be omitted. In the embodiment shown in FIG. 4, the arrangement of the light-heat conversion layer 2 and the recording layer 3 is the reverse of that of the above embodiment. The recording layer 3 has a dominant absorption wavelength different from the dominant absorption wavelength of the light-heat conversion layer 2.
【0028】しかして、この記録媒体に対して、図2の
記録装置の半導体レ−ザ7からのレーザ光が照射される
と、光−熱変換層2に照射された光は光−熱変換され、
照射された光量に応じた熱を発生する。この熱により、
記録層3の対応する部分が溶融破壊され凝集する。光の
照射されない部分は記録層3が着色層4を遮蔽している
ために着色層4が見えないが、光の照射された部分は上
述のように記録層3が破壊され、下層の着色層4が見え
るようになり、記録層3と着色層4のコントラストで画
像が形成される。また、本発明は図5に示すように構成
されるものであっても良い。なお、上記一実施例と同一
部分については、同一番号を付してその説明を省略す
る。図5に示す実施例においては、記録層13には光−
熱変換材料が含有されている。また、保護層1は、記録
層13の吸収主波長と異なる吸収主波長を有している。When the recording medium is irradiated with the laser light from the semiconductor laser 7 of the recording apparatus shown in FIG. 2, the light irradiated on the light-heat conversion layer 2 is converted into light-heat. Is
Generates heat according to the amount of light applied. Due to this heat,
Corresponding portions of the recording layer 3 are melted and destroyed and aggregated. The colored layer 4 is not visible in the portion not irradiated with light because the recording layer 3 shields the colored layer 4, but in the portion irradiated with light, the recording layer 3 is destroyed as described above, and the colored layer underneath. 4 is visible, and an image is formed with the contrast between the recording layer 3 and the coloring layer 4. Further, the present invention may be configured as shown in FIG. The same parts as those in the above-described embodiment are designated by the same reference numerals and the description thereof will be omitted. In the embodiment shown in FIG. 5, the recording layer 13 has a light-
It contains a heat conversion material. Further, the protective layer 1 has a dominant absorption wavelength different from the dominant absorption wavelength of the recording layer 13.
【0029】しかして、この記録媒体に対して、図2の
記録装置の半導体レ−ザ7からのレーザ光が照射される
と、記録層13に照射された光は記録層13内部の光−
熱変換材料により光−熱変換され、照射された光量に応
じた熱を発生する。この熱により、記録層13の対応す
る部分が溶融破壊され凝集する。光の照射されない部分
は記録層13が着色層4を遮蔽しているために着色層4
が見えないが、光の照射された部分は上述のように記録
層13が破壊され、下層の着色層4が見えるようにな
り、記録層13と着色層4のコントラストで画像が形成
される。When the recording medium is irradiated with the laser light from the semiconductor laser 7 of the recording apparatus of FIG. 2, the light irradiated on the recording layer 13 is the light inside the recording layer 13.
Light-heat conversion is performed by the heat conversion material, and heat is generated according to the amount of light applied. Due to this heat, the corresponding portion of the recording layer 13 is melted and destroyed and aggregated. Since the recording layer 13 shields the colored layer 4 from the light-irradiated portion,
Although the recording layer 13 is not visible, the recording layer 13 is destroyed in the light-irradiated portion as described above, and the lower colored layer 4 becomes visible, and an image is formed with the contrast between the recording layer 13 and the colored layer 4.
【0030】[0030]
【発明の効果】本発明は以上説明したように、記録層と
光−熱交換層を積層し、あるいは、記録層中に光−熱変
換層を含有させたから、熱交換効率が高く、小さなエネ
ルギ−で記録することができる。したがって、経済的で
あるとともに、保護層の破壊を防止でき、薬品、水分等
による腐食のない耐蝕性に優れた記録媒体およびこの記
録媒体に対する記録方法を提供することができるという
効果を奏する。As described above, according to the present invention, since the recording layer and the light-heat exchange layer are laminated or the light-heat conversion layer is contained in the recording layer, the heat exchange efficiency is high and the energy consumption is small. It can be recorded with-. Therefore, it is possible to provide a recording medium which is economical, can prevent the protective layer from being destroyed, and has excellent corrosion resistance without being corroded by chemicals, moisture and the like, and a recording method for the recording medium.
【図1】本発明の一実施例である記録媒体の層構成を示
す図。FIG. 1 is a diagram showing a layer structure of a recording medium that is an embodiment of the present invention.
【図2】図1の記録媒体に情報を記録する記録装置を示
す概略構成図。FIG. 2 is a schematic configuration diagram showing a recording device for recording information on the recording medium of FIG.
【図3】図2の記録装置による記録原理を模式的に示す
もので、図3(a)記録媒体にレ−ザ光が照射された状
態を示す図、図3(b)はレ−ザ光の照射により記録層
に情報が記録された状態を示す図。3A and 3B schematically show the recording principle of the recording apparatus shown in FIG. 2. FIG. 3A is a diagram showing a state where the recording medium is irradiated with laser light, and FIG. 3B is a laser. FIG. 6 is a diagram showing a state in which information is recorded on a recording layer by irradiation with light.
【図4】本発明の第1の他の実施例である記録媒体の層
構成を示す図。FIG. 4 is a diagram showing a layer structure of a recording medium that is a first another embodiment of the present invention.
【図5】本発明の第2の他の実施例である記録媒体の層
構成を示す図。FIG. 5 is a diagram showing the layer structure of a recording medium that is a second embodiment of the present invention.
1…保護層、2…光−熱変換層、3…記録層、4…着色
層、5…基材。1 ... Protective layer, 2 ... Light-heat conversion layer, 3 ... Recording layer, 4 ... Colored layer, 5 ... Substrate.
Claims (4)
と異なる色に着色された記録層と、 この記録層に積層され光が照射されたとき発熱し、その
熱で前記記録層を溶融破壊する無色または淡色の光−熱
変換層と、 この光−熱変換層に積層され該光−熱変換層の吸収主波
長と異なる吸収主波長を有する保護層と、を具備してな
ることを特徴とする記録媒体。1. A substrate, a colored layer laminated on the substrate, a recording layer laminated on the colored layer to shield the colored layer or colored in a different color from the colored layer, and the recording layer. And a colorless or light-colored light-heat conversion layer that melts and destroys the recording layer due to the heat when it is irradiated with light, and the absorption of the light-heat conversion layer that is laminated on the light-heat conversion layer. A recording medium comprising: a protective layer having an absorption dominant wavelength different from the dominant wavelength.
または淡色の光−熱変換層と、 この光−熱変換層に積層され該光−熱変換層の吸収主波
長と異なる吸収主波長を有するとともに、前記着色層を
遮蔽、あるいは着色層と異なる色に着色され前記光−熱
変換層の発熱により溶融破壊される記録層と、 この記録層に積層され前記光−熱変換層の吸収主波長と
異なる吸収主波長を有する保護層と、を具備してなるこ
とを特徴とする記録媒体。2. A base material, a colored layer laminated on the base material, a colorless or light-colored light-heat conversion layer which is laminated on the colored layer and generates heat when irradiated with light, and the light-heat It is laminated on the conversion layer and has an absorption main wavelength different from the absorption main wavelength of the light-heat conversion layer, and shields the coloring layer or is colored in a color different from the coloring layer and melts and breaks due to heat generation of the light-heat conversion layer. And a protective layer laminated on the recording layer and having a main absorption wavelength different from the main absorption wavelength of the light-heat conversion layer.
に、前記着色層を遮蔽、あるいは着色層と異なる色に着
色され光が照射されたとき発熱し、その熱で溶融破壊す
る記録層と、 この記録層に積層され記録層の吸収主波長と異なる吸収
主波長を有する保護層と、を具備してなることを記録媒
体。3. A base material, a colored layer laminated on the base material, and a light-heat converting material laminated on the colored layer, and the colored layer is shielded or has a color different from that of the colored layer. A recording layer that is colored and generates heat when irradiated with light, and melts and breaks down by the heat; and a protective layer that is laminated on this recording layer and has a dominant absorption wavelength different from the main absorption wavelength of the recording layer. The recording medium.
変換層および保護層を積層してなる記録媒体に対して特
定波長の光を照射し、この光照射により前記光−熱変換
層を発熱させてその熱で前記記録層を溶融破壊し、この
溶融破壊により前記着色層が露出することにより画像を
形成することを特徴とする記録方法。4. A light source having a specific wavelength is irradiated onto a recording medium in which a coloring layer, a recording layer, a light-heat conversion layer and a protective layer are sequentially laminated on a substrate, and the light irradiation causes the light- A recording method, wherein an image is formed by causing the heat converting layer to generate heat and melting and destroying the recording layer by the heat and exposing the colored layer by the melting and destroying.