JPH0533333Y2 - - Google Patents
Info
- Publication number
- JPH0533333Y2 JPH0533333Y2 JP10692688U JP10692688U JPH0533333Y2 JP H0533333 Y2 JPH0533333 Y2 JP H0533333Y2 JP 10692688 U JP10692688 U JP 10692688U JP 10692688 U JP10692688 U JP 10692688U JP H0533333 Y2 JPH0533333 Y2 JP H0533333Y2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- vinyl chloride
- polymerized
- decorative band
- ethylene copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】
（産業上の利用分野）
この考案は、車輌、家具等の表面に接着するこ
とによつて意匠的な装飾価値を高める美観の優れ
た合成樹脂製装飾帯に関するものである。[Detailed description of the invention] (Field of industrial application) This invention relates to an aesthetically pleasing synthetic resin decorative band that enhances the decorative value by adhering to the surfaces of vehicles, furniture, etc. be.
（従来の技術）
従来、この種の装飾帯は、安価に提供できる塩
化ビニールを主体とした構成材料が使用されてい
る。この塩化ビニールを主体としたものでは長期
間の使用中に光輝が悪化したり、又は変色したり
する欠点がある。そこで、表面のアイオノマー樹
脂の被着シートと内部に埋設する光輝テープの最
上面に同効のアイオノマー樹脂膜を設けた装飾帯
が知られている。（例えば、実開昭61−62099号公
報）
（考案が解決しようとする課題）
上記従来で述べたものにおいては、装飾帯の表
面が大変に美麗となり、且つ温度変化に対する収
縮膨張等を防止する効果がある。然し、アイオノ
マー樹脂は、その材料の性質上大変に流動性が悪
く、従つて、薄肉の樹脂膜を成形するのが大変に
困難である問題点と、装飾帯の光輝テープは表面
が出来る限り薄肉の樹脂膜を以て仕上げる事が必
要であるという問題点を有していた。この考案
は、上記従来の問題点に鑑みてなされたものであ
り、この目的とする所は、装飾帯の被着シートと
光輝テープの上面との接着と金属蒸着膜との接着
性とを著しく優れたものとすると共に、金属蒸着
膜の表面に薄い樹脂膜を作成することによつて光
沢の優れた美しい表面を現出する点にある。(Prior Art) Conventionally, this type of decorative band uses a constituent material mainly made of vinyl chloride, which can be provided at low cost. This vinyl chloride-based material has the disadvantage that its brightness deteriorates or the color changes during long-term use. Therefore, a decorative band is known in which an ionomer resin film having the same effect is provided on the uppermost surface of an ionomer resin adhesion sheet on the surface and a glitter tape embedded inside. (For example, Japanese Utility Model Application Publication No. 61-62099) (Problem to be solved by the invention) In the above-mentioned conventional device, the surface of the decorative band becomes very beautiful and also prevents contraction and expansion due to temperature changes. effective. However, due to the nature of the material, ionomer resin has very poor fluidity, so it is very difficult to form a thin resin film. The problem was that it required finishing with a resin film. This invention was made in view of the above-mentioned conventional problems, and its purpose is to significantly improve the adhesion between the decorative band cover sheet and the top surface of the glitter tape, and the adhesion between the metal vapor deposited film. In addition to making it an excellent product, it also provides a beautiful surface with excellent gloss by forming a thin resin film on the surface of the metal vapor deposited film.
（課題を解決するための手段）
上記目的を達成するために、この考案における
合成樹脂製装飾帯によればアイオノマー樹脂より
なる被着シート２と内部の光輝テープ５と塩化ビ
ニールの基板シート３とから構成し、その光輝テ
ープ５の最下部をエチレン・コ・ポリマーシート
９とすると共に、最下部に塩化ビニールシート１
１を位置してなるものである。また、エチレン・
コ・ポリマーシート９の下面の表面に金属蒸着膜
８を被着したポリエステルシート７を重合体して
ある。このポリエステルシート７の下面には接着
剤１０を介在して該塩化ビニールシート１１を重
合体接着したものである。従つて、この考案の装
飾帯によれば、内部の光輝テープ５と媒体とし、
その最上部のアイオノマー樹脂からエチレン・
コ・ポリマー樹脂に置き変えることによつて、金
属蒸着膜との接着を良好とし、且つ流動性に優れ
ているため、薄肉の樹脂膜を形成すると共に、折
り曲げを容易とする装飾帯を得るものである。(Means for Solving the Problems) In order to achieve the above object, the synthetic resin decorative band in this invention includes an adhesion sheet 2 made of ionomer resin, an internal bright tape 5, and a base sheet 3 made of vinyl chloride. The bottom part of the bright tape 5 is an ethylene copolymer sheet 9, and the bottom part is a vinyl chloride sheet 1.
1. In addition, ethylene
A polyester sheet 7 having a metal vapor-deposited film 8 coated on the lower surface of the co-polymer sheet 9 is made of a polymer. The vinyl chloride sheet 11 is bonded to the lower surface of the polyester sheet 7 with an adhesive 10 interposed therebetween. Therefore, according to the decorative band of this invention, the inner glitter tape 5 and the medium,
From the ionomer resin at the top, ethylene and
By replacing it with a co-polymer resin, it has good adhesion with the metal vapor deposited film and has excellent fluidity, so a thin resin film can be formed and a decorative band that can be easily bent can be obtained. It is.
（作用）
この考案は上記のような構成であり、今これを
車輌、家具及び建築等の装飾帯として使用するに
は、基板シート３の裏面に各種の接着剤を塗着し
て被装着物に接着すれば、被着シート２の表面に
内部の光輝テープ５のアルミニウム等の金属蒸着
膜８が浮上して金属光沢を現出させるものであ
る。(Function) This invention has the above-mentioned configuration, and in order to use it as a decorative band for vehicles, furniture, architecture, etc., various adhesives are applied to the back side of the substrate sheet 3 and the object to be attached is attached. When adhered to the adherend sheet 2, the metal vapor deposited film 8 of aluminum or the like of the inner bright tape 5 floats on the surface of the adherend sheet 2, producing a metallic luster.
（実施例）
次に、この考案の実施例を図面について説明す
ると、合成樹脂を以て長手方向に帯状に成型され
る装飾帯本体１は、表面に露出する被着シート２
をアイオノマー樹脂より構成し、内部に埋設する
光輝テープ５と、この光輝テープ５の下部に塩化
ビニールよりなる基板シート３とのよつて一体的
に成型されている。前記被着シート２は、透明の
アイオノマー樹脂を使用し、長手方向に両側に下
向きの折曲片６，６を形成して該光輝テープ５の
両側面を覆うようになつている。次に、前記光輝
テープ５には、最上部にアイオノマー樹脂よりな
る被着シート２と相溶するエチレン・コ・ポリマ
ー樹脂よりなるエチレン・コ・ポリマーシート７
を設けると共に、最下部に塩化ビニールシート１
１を位置してある。(Example) Next, an example of this invention will be described with reference to the drawings.A decorative band main body 1 made of synthetic resin and molded into a band shape in the longitudinal direction has an adhesive sheet 2 exposed on the surface.
is made of ionomer resin, and is integrally molded with a bright tape 5 embedded therein and a substrate sheet 3 made of vinyl chloride under the bright tape 5. The adhesive sheet 2 is made of a transparent ionomer resin, and has downwardly bent pieces 6, 6 formed on both sides in the longitudinal direction so as to cover both sides of the bright tape 5. Next, on the bright tape 5, an ethylene copolymer sheet 7 made of an ethylene copolymer resin that is compatible with the adherent sheet 2 made of an ionomer resin is placed on the uppermost part.
and a vinyl chloride sheet 1 at the bottom.
1 is located.
また、光輝テープ５の内部に介在される該エチ
レン・コ・ポリマーシート９に下面には、上部に
アルミニウム等の金属蒸着膜８を被着したポリエ
ステルシート７を重合してある。このポリエステ
ルシート７の下面には、各種の接着剤１０を介在
して該塩化ビニールシート１１を重合接着してあ
る。そして、前記光輝テープ５の最上部のエチレ
ン・コ・ポリマーシート９と、アイオノマー樹脂
よりなる被着シート２とを相溶して一体化してあ
る。また、光輝テープ５の最下部の塩化ビニール
シート１１と該塩化ビニールの基板シート３を一
体的に重合接合してある。 Further, on the lower surface of the ethylene co-polymer sheet 9 interposed inside the bright tape 5, there is polymerized a polyester sheet 7 on which a metal vapor-deposited film 8 such as aluminum is coated. The vinyl chloride sheet 11 is polymerized and bonded to the lower surface of the polyester sheet 7 with various adhesives 10 interposed therebetween. The ethylene copolymer sheet 9 on the top of the bright tape 5 and the adherent sheet 2 made of ionomer resin are integrated by being compatible with each other. Furthermore, the vinyl chloride sheet 11 at the bottom of the bright tape 5 and the vinyl chloride substrate sheet 3 are integrally polymerized and bonded.
（考案の効果）
この考案は、上述のとおり構成されているの
で、この装飾帯によれば、内部に埋設する光輝テ
ープを媒体として相溶性のない種類の合成樹脂の
各々の長所及び利点を活用し、且つ接着剤を使用
しないで両者を確実強固に成型できると共に、従
来の欠点である相溶性のない２種類の合成樹脂を
加熱押し出し成型しても金型より抽出時点におい
て、引裂、剥離するのを防止する優れた効果があ
る。また、この装飾帯は内部の光輝テープとの接
合部より雨水の浸入を確実に防止して光輝テープ
を汚染及び変色等から確実に保護するという実利
的な効果がある。そして、光輝テープの最上部に
設けたエチレン・コ・ポリマーシートは、被着シ
ートのアイオノマー樹脂とは相溶性が著しく大き
いため強固に溶融接着させる効果がある。また、
従来の光輝テープに使用するアイオノマー樹脂と
比較してエチレン・コ・ポリマー樹脂は流動性が
大変に良好であるために薄肉のシート膜を形成で
きる効果と、非常に柔軟なために折曲が大変にし
やすいという便利な効果がある。(Effects of the invention) Since this invention is constructed as described above, this decorative band utilizes the merits and advantages of incompatible types of synthetic resins using the glitter tape embedded inside as a medium. Moreover, both can be reliably and firmly molded without using adhesives, and even if two types of incompatible synthetic resins are heated and extruded, which is a drawback of conventional methods, they will not tear or peel off at the time of extraction from the mold. It has an excellent effect of preventing In addition, this decorative strip has the practical effect of reliably preventing rainwater from entering through the joint with the inner glitter tape, thereby reliably protecting the glitter tape from contamination, discoloration, and the like. The ethylene copolymer sheet provided on the top of the bright tape has extremely high compatibility with the ionomer resin of the adherend sheet, so it has the effect of strongly melting and bonding. Also,
Compared to the ionomer resins used in conventional glitter tapes, ethylene copolymer resins have very good fluidity, making it possible to form thin sheet films, and being extremely flexible, making it difficult to bend. It has the advantage of being easy to use.
第１図はこの考案の一部欠除した斜視図、第２
図は同じく断面図、第３図は光輝テープの断面図
である。符号１は装飾帯本体、２は被着シート、
３は基板シート、５は光輝テープ、７はポリエス
テルシート、８は金属蒸着膜、９はエチレン・
コ・ポリマーシート、１０は接着剤、１１は塩化
ビニールシートである。
Figure 1 is a partially cutaway perspective view of this device, Figure 2
The figure is also a cross-sectional view, and FIG. 3 is a cross-sectional view of the bright tape. Code 1 is the decorative band body, 2 is the attached sheet,
3 is a substrate sheet, 5 is a bright tape, 7 is a polyester sheet, 8 is a metal vapor deposited film, 9 is an ethylene film.
A copolymer sheet, 10 is an adhesive, and 11 is a vinyl chloride sheet.
Claims (1)
飾帯本体は、表面に露出するアイオノマー樹脂よ
りなる被着シートと内部に埋設される光輝テープ
と塩化ビニールよりなる基板シートとから構成さ
れる合成樹脂製装飾帯において、前記光輝テープ
には、最上部に被着シート２の裏面との相溶する
エチレン・コ・ポリマーシートを設けると共に、
最下部に塩化ビニールシートを位置し、該エチレ
ン・コ・ポリマーシートの下面には、表面に金属
蒸着膜を被着したポリエステルシートを重合し、
該ポリエステルシートの下面に接着剤を介在して
塩化ビニールシートを重合接着し、前記エチレ
ン・コ・ポリマーシートの上面と該被着シートの
下面とを重合し、且つ最下部の塩化ビニールシー
トと該基板シートとを重合接合した事を特徴とす
る合成樹脂製装飾帯。 The decorative band body is made of synthetic resin and is molded into a longitudinal band shape. It is made of synthetic resin and consists of an adhesive sheet made of ionomer resin exposed on the surface, a glitter tape buried inside, and a base sheet made of vinyl chloride. In the decorative band, the glitter tape is provided with an ethylene copolymer sheet on the top that is compatible with the back surface of the adherend sheet 2,
A vinyl chloride sheet is placed at the bottom, and a polyester sheet whose surface is coated with a metal vapor deposition film is polymerized on the bottom surface of the ethylene copolymer sheet.
A vinyl chloride sheet is polymerized and adhered to the lower surface of the polyester sheet with an adhesive interposed, the upper surface of the ethylene copolymer sheet and the lower surface of the adhered sheet are polymerized, and the lowermost vinyl chloride sheet and the polyester sheet are polymerized. A synthetic resin decorative band characterized by being polymerized and bonded to a substrate sheet.