JPH05262370A - Packaging film and packaging body of foamed body - Google Patents
Packaging film and packaging body of foamed bodyInfo
- Publication number
- JPH05262370A JPH05262370A JP17662492A JP17662492A JPH05262370A JP H05262370 A JPH05262370 A JP H05262370A JP 17662492 A JP17662492 A JP 17662492A JP 17662492 A JP17662492 A JP 17662492A JP H05262370 A JPH05262370 A JP H05262370A
- Authority
- JP
- Japan
- Prior art keywords
- film
- packaging
- metal powder
- packaging film
- white pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【産業上の利用分野】本発明は、包装フィルム及び発泡
体の包装体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a packaging film and a foam packaging body.
【従来の技術】断熱折版屋根板の裏打ち断熱材として使
用される発泡体は、薄板鉄板に貼着するために熱可塑性
樹脂発泡体の表面に低融点樹脂が塗工されたものであっ
て、その包装には、従来より、熱可塑性樹脂よりなる厚
さ２０〜１００μｍの透明な包装フィルムを使用し、長
さ５０〜３００ｍのロール状に巻回した発泡体を上記の
ような包装フィルムで被覆したものを包装体としてい
た。2. Description of the Related Art A foam used as a backing heat insulating material for a heat-insulating folded roof plate is a thermoplastic resin foam coated with a low-melting resin to be attached to a thin iron plate. For its packaging, conventionally, a transparent packaging film made of a thermoplastic resin and having a thickness of 20 to 100 μm has been used, and a foamed body wound in a roll shape having a length of 50 to 300 m is wrapped with the packaging film as described above. The coated product was used as a package.
【０００１】[0001]
【発明が解決しようとする課題】しかし、このような包
装体を夏季屋外に放置すると、太陽光線が吸収され易
く、また吸収された熱が放熱され難いために、被包装物
である発泡体の表面温度が上昇し、低融点樹脂が溶融し
て当接する自背面に接着するブロッキングを起こし、使
用に際し展開する時に破損を生じることがある。However, when such a package is left outdoors in the summer, sunlight is easily absorbed and the absorbed heat is difficult to dissipate. The surface temperature rises, the low melting point resin melts and causes blocking that adheres to the abutting back surface of the low melting point resin, which may cause damage when developed during use.
【０００２】そこで、包装体内の温度上昇を抑えるため
に、包装フィルムと発泡体との間に断熱材やクラフト紙
等を挿入して太陽光線を遮るようにすることが行われて
いる。しかし、このような包装体にすると、包装費用が
嵩むと共に、余分な廃棄物が発生することとなる。Therefore, in order to suppress the temperature rise in the package, a heat insulating material, kraft paper, or the like is inserted between the packaging film and the foam to block the sunlight. However, such a package increases the packaging cost and generates extra waste.
【０００３】また、ユーザーの注文や使用目的によって
発泡体に異なった着色が施されているような場合には、
断熱材やクラフト紙に遮られて発泡体の色の識別が困難
となり、在庫管理上支障をきたすことがある。If the foam is colored differently depending on the user's order or purpose of use,
It may be difficult to identify the color of the foam because it is blocked by the heat insulating material and kraft paper, which may hinder inventory management.
【０００４】本発明は上記のような従来技術の問題点に
鑑みてなされたものであって、その目的の１は、太陽光
線の透過、吸収を困難にして熱の吸収を少なくし、通気
性を良くすることによって、包装体内の温度上昇を抑え
ることのできる包装フィルムを提供することである。The present invention has been made in view of the problems of the prior art as described above, and one of the objects thereof is to make it difficult to transmit and absorb the sun's rays to reduce the heat absorption and to improve the air permeability. It is to provide a packaging film capable of suppressing the temperature rise in the packaging body by improving the temperature.
【０００５】本発明の目的の２は、太陽光線による内部
の温度上昇を抑え、被包装物の発泡体に塗工された低融
点樹脂が溶融してブロッキングを起こすことのない包装
体を提供することである。The second object of the present invention is to provide a package in which the internal temperature rise due to sunlight is suppressed and the low melting point resin coated on the foam of the packaged product does not melt and cause blocking. That is.
【０００６】本発明の目的の３は、太陽光線の透過、吸
収を困難にして熱の吸収を少なくし、通気性を良くする
ことによって、包装体内の温度上昇を抑えるとともに、
内部が透視できる包装フィルムを提供することである。The third object of the present invention is to suppress the temperature rise in the package by making it difficult to transmit and absorb the sun rays to reduce the heat absorption and improve the air permeability.
The purpose of the present invention is to provide a packaging film that allows the inside to be seen through.
【０００７】本発明の目的の４は、太陽光線による内部
の温度上昇を抑え、被包装物の発泡体に塗工された低融
点樹脂が溶融してブロッキングを起こすことがなく、且
つ必要に応じ発泡体の色を容易に識別できる包装体を提
供することである。The fourth object of the present invention is to prevent the internal temperature from rising due to sunlight, to prevent the low melting point resin coated on the foam of the packaged product from melting and causing blocking, and if necessary. An object of the present invention is to provide a package in which the color of foam can be easily identified.
【０００８】[0008]
【課題を解決するための手段】上記の目的を達成するた
めに、本発明の包装フィルムは、白色顔料または金属粉
末を含有するか白色顔料または金属粉末を含有する層が
設けられた熱可塑性樹脂フィルムに、小さい貫通孔が穿
設されていることを要旨とするものである。In order to achieve the above object, the packaging film of the present invention comprises a thermoplastic resin containing a white pigment or a metal powder or a layer containing a white pigment or a metal powder. The gist is that small through holes are formed in the film.
【０００９】また、本発明の包装フィルムは、白色顔料
または金属粉末を含有するか白色顔料または金属粉末を
含有する層が設けられた部分と、透明な部分よりなる熱
可塑性樹脂フィルムに、小さな貫通孔が穿設されている
ことを要旨とするものである。Further, the packaging film of the present invention has a small penetration through a thermoplastic resin film comprising a transparent portion and a portion provided with a layer containing a white pigment or a metal powder or a layer containing a white pigment or a metal powder. The gist is that holes are provided.
【００１０】更に、本発明の発泡体の包装体は、熱可塑
性樹脂発泡体の表面に低融点樹脂が塗工された発泡体
が、請求項１または２の包装フィルムで被覆されている
ことを要旨とするものである。Further, in the foamed package of the present invention, the foamed product in which the low melting point resin is applied to the surface of the thermoplastic resin foam is covered with the packaging film according to claim 1 or 2. It is a summary.
【００１１】本発明に使用する熱可塑性樹脂フィルム
は、厚さが２０〜１５０μｍのポリエチレンもしくはポ
リプロピレン樹脂製のフィルムが好適に使用される。The thermoplastic resin film used in the present invention is preferably a polyethylene or polypropylene resin film having a thickness of 20 to 150 μm.
【００１２】本発明において、白色顔料または金属粉末
を含有する熱可塑性樹脂フィルムを得る方法としては、
白色顔料または金属粉末を原料ペレットとともに押出成
形機に供給する、白色顔料または金属粉末を予め添加し
た原料ペレットを押出成形機に供給する等によってフィ
ルムを成形する等が挙げられる。In the present invention, as a method for obtaining a thermoplastic resin film containing a white pigment or metal powder,
Examples of the method include forming a film by supplying a white pigment or a metal powder together with a raw material pellet to an extruder, or supplying a raw material pellet to which a white pigment or a metal powder is added in advance to an extruder.
【００１３】また、白色顔料または金属粉末を含有する
層が設けられた熱可塑性樹脂フィルムを得る方法として
は、上記のような白色顔料または金属粉末を含有する原
料と透明な原料を用いて二層押出成形する、透明な熱可
塑性樹脂フィルムの少なくとも片面に、白色顔料または
金属粉末を含有する塗料、印刷インク等による塗工ある
いは印刷を施してもよい。Further, as a method for obtaining a thermoplastic resin film provided with a layer containing a white pigment or metal powder, two layers are prepared by using a raw material containing the above white pigment or metal powder and a transparent raw material. At least one surface of the transparent thermoplastic resin film to be extrusion-molded may be coated or printed with a paint containing a white pigment or a metal powder, a printing ink, or the like.
【００１４】本発明に使用する白色顔料としては、例え
ば酸化チタン、亜鉛華、鉛白、硫化亜鉛、リトポン等
が、また金属粉末としては、例えばアルミニウム、アル
ミナ、ブロンズ等の粉末が挙げられる。これらの白色顔
料または金属粉末を含有する熱可塑性樹脂フィルムを成
形する場合、その含有量は１０〜３０重量％とするのが
好ましい。含有量がこれより少ないと太陽光線の透過率
の低下が充分でなく、多過ぎるとフィルムの引張強度が
低下する。Examples of the white pigment used in the present invention include titanium oxide, zinc white, lead white, zinc sulfide, lithopone and the like, and examples of the metal powder include powders of aluminum, alumina, bronze and the like. When molding a thermoplastic resin film containing these white pigments or metal powders, the content is preferably 10 to 30% by weight. If the content is less than this, the solar light transmittance is not sufficiently reduced, and if it is too large, the tensile strength of the film is reduced.
【００１５】本発明に使用する白色顔料または金属粉末
を含有するか白色顔料または金属粉末を含有する層が設
けられた部分と、透明な部分よりなる熱可塑性樹脂フィ
ルムは、厚さが２０〜１５０μｍのポリエチレンもしく
はポリプロピレン樹脂製のフィルムで、大きな面積比率
を占める白色顔料または金属粉末を含有するか白色顔料
または金属粉末を含有する層が設けられた部分に、一本
もしくは複数本の帯状、あるいは一定間隔で複数の窓状
等に透明な部分が設けられているものが好適に使用され
る。透明な部分の面積比率が大きすぎると、太陽光線の
透過量が多くなって包装体内の温度が上昇しやすくなる
ので、被包装物の色の識別が容易にできる程度の巾ある
いは面積のものとする。なお、透明な部分は無色である
ことが好ましいが、被包装物の色が識別できる程度の淡
い色に着色されていてもよい。The thermoplastic resin film used in the present invention, which is composed of a transparent portion and a portion provided with a layer containing the white pigment or the metal powder or containing the white pigment or the metal powder, has a thickness of 20 to 150 μm. Film made of polyethylene or polypropylene resin, containing a large area ratio of white pigment or metal powder, or a layer provided with a white pigment or metal powder, in the portion provided with one or more strips, or a constant Those having a plurality of transparent portions such as windows at intervals are preferably used. If the area ratio of the transparent part is too large, the amount of transmitted sunlight will increase and the temperature inside the package will easily rise.Therefore, the width or area should be such that the color of the packaged item can be easily identified. To do. The transparent portion is preferably colorless, but may be colored in a light color such that the color of the packaged item can be identified.
【００１６】白色顔料または金属粉末を含有するか白色
顔料または金属粉末を含有する層が設けられた部分と、
透明な部分よりなる熱可塑性樹脂フィルムを得る手段と
しては、 白色顔料または金属粉末を含有する熱可塑性樹脂と透
明な熱可塑性樹脂を別々の押出成形機で溶融混練して一
つの金型内に供給し、金型内で白色顔料または金属粉末
を含有する樹脂層と透明な樹脂層とを融着させ１枚の連
続したフィルムとして成形する、 別々に得られた白色顔料または金属粉末を含有するか
白色顔料または金属粉末を含有する層が設けられた熱可
塑性樹脂フィルムと、透明な熱可塑性樹脂フィルムとを
熱融着する、 別々に得られた白色顔料または金属粉末を含有するか
白色顔料または金属粉末を含有する層が設けられた熱可
塑性樹脂フィルムと、透明な熱可塑性樹脂フィルムとを
接着剤、粘着剤、粘着テープ等で連結する、 透明な熱可塑性樹脂フィルムの少なくとも片面に、白
色顔料または金属粉末を含有する塗料、印刷インク等に
よる塗工あるいは印刷を施す、 等が挙げられる。A portion containing a layer containing white pigment or metal powder or containing white pigment or metal powder;
As a means to obtain a thermoplastic resin film consisting of transparent parts, a thermoplastic resin containing white pigment or metal powder and a transparent thermoplastic resin are melt-kneaded by separate extruders and fed into one mold. Then, the resin layer containing the white pigment or metal powder and the transparent resin layer are fused together in a mold to form a continuous film. Does the white pigment or metal powder obtained separately be contained? A thermoplastic resin film provided with a layer containing a white pigment or a metal powder, and a transparent thermoplastic resin film are heat-sealed, containing separately obtained white pigment or a metal powder, or a white pigment or a metal A thermoplastic resin film provided with a layer containing powder and a transparent thermoplastic resin film are connected by an adhesive, a pressure sensitive adhesive, an adhesive tape or the like. At least one surface may be coated or printed with a paint containing a white pigment or a metal powder, a printing ink, or the like.
【００１７】熱可塑性樹脂フィルムに穿設する小さい貫
通孔は、通気性、孔によるフィルム強度の低下、孔あけ
加工の容易さ等の点から、直径０．２〜５ｍｍの丸孔、
長さ０．２〜５ｍｍの切り目を×状に入れたもの等が、
１０〜１００ｍｍの間隔で、包装フィルムのほぼ全面に
穿設したものが好適である。The small through holes formed in the thermoplastic resin film are circular holes having a diameter of 0.2 to 5 mm, from the viewpoints of air permeability, reduction of film strength due to the holes, ease of perforating processing, and the like.
Those with a 0.2- to 5-mm-long cut in the shape of x are
It is preferable that the packaging film is perforated substantially at an interval of 10 to 100 mm.
【００１８】本発明で包装される熱可塑性樹脂発泡体と
しては、例えば独立気泡を有するポリエチレン樹脂発泡
体が、また、熱可塑性樹脂発泡体に塗工される低融点樹
脂としては、例えばスチレン−ブタジエン共重合体ラテ
ックスが挙げられる。The thermoplastic resin foam to be packaged in the present invention is, for example, a polyethylene resin foam having closed cells, and the low melting point resin applied to the thermoplastic resin foam is, for example, styrene-butadiene. A copolymer latex is mentioned.
【００１９】[0019]
【作用】本発明の包装フィルムは、白色顔料または金属
粉末を含有するか白色顔料もしくは金属粉末を含有する
層が設けられているから、太陽光線はその多くが包装フ
ィルムの表面で反射されて透過し難く、吸収され難い。
また、小さい貫通孔が穿設されているので、通気性が良
好である。Since the packaging film of the present invention is provided with a layer containing a white pigment or a metal powder or a layer containing a white pigment or a metal powder, most of the sun rays are reflected by the surface of the packaging film and transmitted. Hard to do and hard to absorb.
Further, since the small through holes are formed, the air permeability is good.
【００２０】また、本発明の発泡体の包装体は、上記の
包装フィルムで被覆されているので、太陽熱が吸収され
難く、また、貫通孔を通って内部に蓄積された熱が放熱
され易いので、包装体内の温度上昇が抑えられる。Further, since the foam package of the present invention is covered with the above-mentioned packaging film, it is difficult to absorb solar heat, and the heat accumulated inside through the through hole is easily radiated. The temperature rise inside the package is suppressed.
【００２１】更に、本発明の包装フィルムは白色顔料ま
たは金属粉末を含有するか白色顔料または金属粉末を含
有する層が設けられた部分と、透明な部分よりなる熱可
塑性樹脂フィルムに、小さい貫通孔が穿設されているの
で、太陽光線はその多くが包装フィルムの表面で反射さ
れて透過し難く、吸収され難い。また、通気性が良好で
ある。更に、透明な部分が設けられているので、その部
分から内部が透視できる。Furthermore, the packaging film of the present invention is a thermoplastic resin film comprising a transparent portion and a portion provided with a layer containing a white pigment or a metal powder or a layer containing a white pigment or a metal powder, and a small through hole. Since most of the sun rays are reflected by the surface of the packaging film, it is difficult for them to pass through, and it is difficult to be absorbed. Also, the air permeability is good. Further, since the transparent portion is provided, the inside can be seen through from that portion.
【００２２】更にまた、本発明の発泡体の包装体は、上
記の包装フィルムで被覆されているので、太陽熱が吸収
され難く、貫通孔を通って内部に蓄積された熱が放熱さ
れ易いので、包装体内の温度上昇が抑えられる。また、
透明な部分から発泡体の色が容易に識別できる。Further, since the foam package of the present invention is covered with the above-mentioned packaging film, it is difficult to absorb solar heat and the heat accumulated inside through the through hole is easily radiated. The temperature rise inside the package is suppressed. Also,
The color of the foam can be easily identified from the transparent part.
【００２３】[0023]
【実施例】以下本発明の実施例を、図面を参照して説明
する。図１は第１発明の包装フィルムの実施例を示す平
面図、図２は第１発明の包装フィルムを用いた包装体の
実施例を示す斜視図、図３は第２発明の包装フィルムの
実施例を示す平面図、図４は第２発明の包装フィルムに
穿設する貫通孔の実施例を示す説明図であって、（Ａ）
は貫通孔の形状を示す平面図、（Ｂ）は貫通孔の配列状
態を示す平面図、図５は第２発明の包装フィルムを用い
た包装体の実施例を示す斜視図である。Embodiments of the present invention will be described below with reference to the drawings. 1 is a plan view showing an embodiment of a packaging film of the first invention, FIG. 2 is a perspective view showing an embodiment of a packaging body using the packaging film of the first invention, and FIG. 3 is an implementation of the packaging film of the second invention. FIG. 4 is a plan view showing an example, and FIG. 4 is an explanatory view showing an example of a through hole formed in the packaging film of the second invention,
Is a plan view showing the shape of the through holes, (B) is a plan view showing the arrangement state of the through holes, and FIG. 5 is a perspective view showing an embodiment of a package using the packaging film of the second invention.
【００２４】（実施例１）白色顔料として酸化チタン粉
末を３０重量％含有する厚さ４０μｍ、巾２，３００ｍ
ｍの乳白色のポリエチレンフィルム１のほぼ全面に、直
径１ｍｍの貫通孔２を中心間距離３６ｍｍの間隔をおい
て斜め格子状に配列して穿設し、図１に示されるような
包装フィルム３を得た。Example 1 A white pigment containing 30% by weight of titanium oxide powder, having a thickness of 40 μm and a width of 2,300 m.
Through holes 2 having a diameter of 1 mm are arranged in a diagonal lattice pattern at an interval of a center distance of 36 mm on substantially the entire surface of the milk-white polyethylene film 1 of m, and a packaging film 3 as shown in FIG. 1 is formed. Obtained.
【００２５】また、発泡倍率４０ｃｍ3 ／ｇ、厚さ４ｍ
ｍ、長さ２００ｍの、クリーム色のポリエチレン樹脂発
泡体の表面に、低融点樹脂として軟化点６２℃のスチレ
ン−ブタジエン共重合体のラテックスを塗布量６ｇ／ｍ
2の割合で塗工乾燥し、塗工面を内方にして紙芯５に巻
回した巻重体４を、前記包装フィルム３で被覆して、図
２に示されるような包装体６を得た。Further, the expansion ratio is 40 cm 3 / g and the thickness is 4 m.
m, 200 m in length, cream-colored polyethylene resin foam surface coated with a latex of styrene-butadiene copolymer having a softening point of 62 ° C. as a low melting point resin 6 g / m
The wound body 4 wound around the paper core 5 with the coated surface facing inward was coated and dried at a ratio of 2 , and the packaging film 3 was coated to obtain a packaging body 6 as shown in FIG. ..
【００２６】得られた包装体６を外気温３２℃の屋外
で、直射日光下に放置して包装体６内の温度の経時変化
を測定するとともに、ブロッキング発生の有無を観察し
た。その結果、包装体６内の温度は６０分経過後には５
３〜５５℃とほぼ一定温度に止まり、低融点樹脂の軟化
点６２℃には達せず、また、ブロッキングは観察されな
かった。The obtained package 6 was left outdoors under an external temperature of 32 ° C. under direct sunlight to measure the change with time of the temperature inside the package 6 and to observe the occurrence of blocking. As a result, the temperature inside the package 6 is 5 after 60 minutes.
The temperature remained at a substantially constant temperature of 3 to 55 ° C., the softening point of the low melting point resin did not reach 62 ° C., and blocking was not observed.
【００２７】（実施例２）白色顔料として酸化チタン粉
末３０重量％を含有するポリエチレン樹脂と、顔料ある
いは金属粉末を含有しないポリエチレン樹脂を、別々の
押出機で加熱溶融・混練して一つの金型に供給し、金型
内で融着させて、乳白色の部分７の中央に１５０ｍｍ巾
の帯状の透明な部分８が押出方向と平行に配置された、
厚さ４０μｍ、巾２，３００ｍｍの二色フィルム９を成
形し、二色フィルム９のほぼ全面に、図４（Ａ）に示さ
れるような×状切り目の貫通孔２ａを図４（Ｂ）のよう
に斜め格子状に配列して穿設し、図３に示されるような
包装フィルム３ａを得た。Example 2 A polyethylene resin containing 30% by weight of titanium oxide powder as a white pigment and a polyethylene resin containing no pigment or metal powder were heated and melted and kneaded by separate extruders to form a single mold. And melted in a mold, and a strip-shaped transparent portion 8 having a width of 150 mm was arranged in the center of the milky white portion 7 in parallel with the extrusion direction.
A dichroic film 9 having a thickness of 40 μm and a width of 2300 mm is formed, and a through hole 2a having a cross cut as shown in FIG. 4 (A) is formed on almost the entire surface of the dichroic film 9 as shown in FIG. 4 (B). As described above, they were arranged in a diagonal grid pattern and perforated to obtain a packaging film 3a as shown in FIG.
【００２８】また、発泡倍率４０ｃｍ3 ／ｇ、厚さ４ｍ
ｍ、長さ２００ｍの、それぞれ白色、クリーム色、ピン
ク色、青色、緑色に着色されたポリエチレン樹脂発泡体
の表面に、低融点樹脂として軟化点６２℃のスチレン−
ブタジエン共重合体のラテックスを塗布量６ｇ／ｍ2の
割合で塗工乾燥し、塗工面を内方にして紙芯に巻回した
巻重体４ａを、前記包装フィルム３ａで被覆して、図５
に示されるような包装体６ａを得た。The expansion ratio is 40 cm 3 / g and the thickness is 4 m.
m, a length of 200 m, and a styrene resin having a softening point of 62 ° C. as a low melting point resin on the surface of a polyethylene resin foam colored in white, cream, pink, blue and green, respectively.
A latex of a butadiene copolymer is applied and dried at a coating amount of 6 g / m 2 , and a roll 4a wound around a paper core with the coated surface inward is coated with the packaging film 3a,
A package 6a as shown in was obtained.
【００２９】得られた包装体６ａにつき、実施例１と同
じ方法で外気温３２℃の屋外で直射日光下に放置し、包
装体６ａ内の温度の経時変化を測定するとともに、ブロ
ッキング発生の有無を観察した。その結果、包装体６ａ
内の温度は実施例１と同様に、低融点樹脂の軟化点６２
℃以下の５６℃に止まった。また、ブロッキングは観察
されなかった。The obtained package 6a was left outdoors under direct sunlight at an outside temperature of 32 ° C. in the same manner as in Example 1 to measure the time-dependent change in temperature inside the package 6a and determine whether blocking occurred. Was observed. As a result, the package 6a
The internal temperature is the same as in Example 1, and the softening point of the low melting point resin is 62.
The temperature stopped at 56 ° C, which was below ℃. Also, no blocking was observed.
【００３０】また、倉庫内で５ｍの距離から目視により
巻重体４ａの色の識別を行ったところ、包装フィルム３
ａに形成されている帯状の透明な部分８から巻重体４ａ
の一部が明瞭に見え、その色を容易に識別することがで
きた。なお、実施例１の包装体６では、巻重体４の色の
識別は困難であった。When the color of the roll 4a was visually identified from the distance of 5 m in the warehouse, the packaging film 3
The band-shaped transparent portion 8 formed on the a
A part of the was clearly visible and its color could be easily identified. In the package 6 of Example 1, it was difficult to identify the color of the roll 4.
【００３１】（比較例１）包装フィルムとして透明で貫
通孔が穿設されていないポリエチレンフィルムを用いた
こと以外、実施例１と同様にして得られた包装体につ
き、実施例１と同じ方法で包装体内の温度の経時変化の
測定及びブロッキング発生有無の観察を行った。その結
果、包装体内の温度は、６０分経過後には低融点樹脂の
軟化点を超え、発泡体はその端縁において自背面と融着
し、ブロッキングを生じた。(Comparative Example 1) A package obtained in the same manner as in Example 1 except that a transparent polyethylene film having no through holes was used as the packaging film was prepared in the same manner as in Example 1. The change with time of the temperature in the package was measured and the presence or absence of blocking was observed. As a result, the temperature inside the package exceeded the softening point of the low melting point resin after 60 minutes had passed, and the foam was fused to its back surface at the edge thereof, resulting in blocking.
【００３２】（比較例２）包装フィルムとして透明で貫
通孔が穿設されていないポリエチレンフィルムを用い、
包装フィルムと発泡体の巻重体との間に発泡倍率３０
倍、厚さ４ｍｍの白色のポリエチレン発泡体よりなる断
熱材と秤量７０ｇ／ｃｍ2 のクラフト紙を挿入したこと
以外は、実施例１と同様にして包装体を得、得られた包
装体につき実施例１と同じ方法で包装体内の温度の経時
変化の測定及びブロッキング発生有無の観察を行った。
その結果、包装体内の温度は６０分経過後５７℃、１２
０分経過後６０℃となり、実施例１の場合より若干高か
ったが、低融点樹脂の軟化点には達せず、またブロッキ
ングは観察されなかった。(Comparative Example 2) A polyethylene film which is transparent and has no through holes is used as a packaging film.
Expansion ratio of 30 between the wrapping film and the roll of foam
Double, a package was obtained in the same manner as in Example 1 except that a heat insulating material made of a white polyethylene foam having a thickness of 4 mm and kraft paper weighing 70 g / cm 2 were inserted. The same method as in Example 1 was used to measure the change in temperature with time in the package and observe the occurrence of blocking.
As a result, the temperature inside the package was 57 ° C, 12 after 60 minutes.
After 0 minutes, the temperature became 60 ° C., which was slightly higher than that of Example 1, but the softening point of the low melting point resin was not reached, and blocking was not observed.
【００３３】なお、実施例２と同じ方法で巻重体の色の
識別を試みたが、巻重体は断熱材とクラフト紙で覆われ
ているので、当然のことながら、全く透視できなかっ
た。Although an attempt was made to identify the color of the wound body in the same manner as in Example 2, the wound body was covered with a heat insulating material and kraft paper, and as a matter of course, could not be seen through.
【００３４】上記実施例１，２及び比較例１，２の包装
体内の温度の経時変化を、表１にまとめて記す。Table 1 shows the changes over time in the temperature inside the packages of Examples 1 and 2 and Comparative Examples 1 and 2.
【００３５】[0035]
【表１】 [Table 1]
【００３６】[0036]
【発明の効果】第１発明の包装フィルムは前記の通り構
成されているので、太陽光線に曝されても包装体内の温
度が上昇し難く、昇温によって品質が劣化しやすい物品
の包装に好適に使用される。Since the packaging film of the first invention is configured as described above, it is suitable for packaging of articles in which the temperature inside the package is unlikely to rise even when exposed to sunlight and the quality of which easily deteriorates due to temperature rise. Used for.
【００３７】第２発明の包装フィルムは前記の通り構成
されているので、太陽光線に曝されても包装体内の温度
が上昇し難く、昇温によって品質が劣化しやすい物品の
包装で、且つ外から内容物の色等の識別が必要な場合の
包装に好適に使用される。Since the wrapping film of the second invention is constructed as described above, it is a wrapping for articles in which the temperature inside the wrapping does not easily rise even when exposed to sunlight, and the quality of which tends to deteriorate due to temperature rise, and It is suitable for packaging when it is necessary to identify the color of the contents.
【００３８】第３発明の発泡体の包装体は、第１発明の
包装フィルムで被覆されているので、包装体内の温度が
上昇し難く、従って熱可塑性樹脂発泡体の表面に塗工さ
れた低融点樹脂が溶融してブロッキングを起こすのが防
止される。Since the foam package of the third invention is covered with the packaging film of the first invention, the temperature inside the package is unlikely to rise, and therefore the low temperature applied on the surface of the thermoplastic resin foam. The melting point resin is prevented from melting and blocking.
【００３９】また、第２発明の包装フィルムで被覆され
ている発泡体の包装体にあっては、包装体内の温度が上
昇し難く、従って熱可塑性樹脂発泡体の表面に塗工され
た低融点樹脂が溶融してブロッキングを起こすのが発生
すのが防止されるとともに、包装フィルムの透明な部分
から内容物の熱可塑性樹脂発泡体の色が容易に識別でき
るので、在庫管理が容易となる。Also, in the case of the foam package covered with the packaging film of the second invention, the temperature inside the package is unlikely to rise, and therefore the low melting point applied to the surface of the thermoplastic resin foam. The resin is prevented from melting and causing blocking, and the color of the thermoplastic resin foam of the content can be easily identified from the transparent portion of the packaging film, which facilitates inventory management.
【００４０】[0040]
【図１】第１発明の包装フィルムの実施例を示す平面図
である。FIG. 1 is a plan view showing an embodiment of a packaging film of the first invention.
【図２】第１発明の包装フィルムを用いた包装体の実施
例を示す斜視図である。FIG. 2 is a perspective view showing an embodiment of a packaging body using the packaging film of the first invention.
【図３】第２発明の包装フィルムの実施例を示す平面図
である。FIG. 3 is a plan view showing an embodiment of the packaging film of the second invention.
【図４】第２発明の包装フィルムに穿設する貫通孔の実
施例を示す説明図であって、（Ａ）は貫通孔の形状を示
す平面図、（Ｂ）は貫通孔の配列状態を示す平面図、で
ある。FIG. 4 is an explanatory view showing an embodiment of through holes formed in the packaging film of the second invention, (A) is a plan view showing the shape of the through holes, and (B) is an arrangement state of the through holes. FIG.
【図５】第２発明の包装フィルムを用いた包装体の実施
例を示す斜視図である。FIG. 5 is a perspective view showing an embodiment of a packaging body using the packaging film of the second invention.
１ 乳白色のポリエチレンフィルム ２，２ａ 貫通孔 ３，３ａ 包装フィルム ４，４ａ 巻重体 ５ 紙芯 ６，６ａ 包装体 ７ 乳白色の部分 ８ 透明な部分 ９ 二色フィルム 1 Milky-white polyethylene film 2,2a Through hole 3,3a Packaging film 4,4a Rolled body 5 Paper core 6,6a Packaging 7 Milky white part 8 Transparent part 9 Two-color film
Claims (3)
色顔料または金属粉末を含有する層が設けられた熱可塑
性樹脂フィルムに、小さい貫通孔が穿設されていること
を特徴とする包装フィルム。1. A packaging film, characterized in that a small through hole is formed in a thermoplastic resin film containing a layer containing a white pigment or a metal powder or a layer containing a white pigment or a metal powder.
色顔料または金属粉末を含有する層が設けられた部分
と、透明な部分よりなる熱可塑性樹脂フィルムに、小さ
い貫通孔が穿設されていることを特徴とする包装フィル
ム。2. A small through hole is formed in a thermoplastic resin film comprising a transparent portion and a portion provided with a layer containing a white pigment or a metal powder or a layer containing a white pigment or a metal powder. A packaging film characterized in that
が塗工された発泡体が、請求項１または２の包装フィル
ムで被覆されていることを特徴とする発泡体の包装体。3. A foam package comprising a thermoplastic resin foam coated with a low melting point resin on the surface thereof and covered with the packaging film according to claim 1 or 2.