JPH043758B2 - - Google Patents

Description

[Detailed description of the invention]

"Industrial Application Field" The present invention relates to a heat-sensitive recording medium, and particularly to a heat-sensitive recording medium that can be fixed with light. ``Prior Art'' Conventionally, a recorded image has been obtained by making use of the coloring reaction between a basic colorless dye and a coloring agent that can develop a color when it comes into contact with the dye, and bringing both coloring substances into contact with each other using heat. Thermosensitive recording media made of this type are well known. Since such a thermal recording medium is structured to obtain a recorded image using heat, if the heat source is mistakenly brought close to the recording medium even after applying heat and recording, the entire heated area will develop color.
It has the defect that necessary records become illegible. Therefore, it has been difficult to apply it to important records that require preservation. Therefore, in recent years, development of a diazo-based heat-sensitive recording material that utilizes a color-forming reaction between a diazo compound and a coupler has been progressing as a heat-sensitive recording material that can be fixed. Generally, in such a diazo-based heat-sensitive recording material, a diazo compound and a coupler are dispersed in the recording layer in the form of discontinuous particles, and a recorded image is formed using a coloring aid that generates alkali when heated. It is configured to obtain. However, inorganic or organic ammonium salts, alkali salts of trichloroacetic acid, urea, etc., which are generally used as color development aids, decompose little by little even at room temperature, so pre-coupling occurs during storage and the recording layer becomes colored. Defects may occur. "Problems to be Solved by the Invention" The purpose of the present invention is to provide a diazo-based thermosensitive recording material that does not cause pre-coupling and has excellent storage stability over a long period of time. This is achieved by using a specific heat-melting basic compound as a coloring aid. "Means for solving the problems" The present invention provides at least a diazonium compound,
This heat-sensitive recording material is characterized in that a heat-sensitive recording layer containing a type of heat-melting basic compound represented by the following general formula [] as a coupler is provided on a support. [In the formula, R ₁ , R ₂ , R ₃ , R ₄ , R ₅ , and R ₆ are each an alkyl group, an alkoxyl group, a nitro group, or an aryl group optionally substituted with a halogen atom;
Aralkyl group; alkyl group; cyclic alkyl group or hydrogen atom. R is an alkylene group; a phenylene group; a naphthylene group or

[Formula] (wherein X represents an alkylene group; SO ₂ ; S; O; NH; or a single bond). [Function] Specific examples of the specific heat-melting basic compound used in the present invention include the following compounds, but of course the compounds are not limited thereto. N,N′,N″,N-tetraphenyl-P-xylene diamidine (mp 233°C). N,N″-dicyclohexyl-decanediamidine (mp 143°C). N,N′,N″,N-tetraphenyl-hexanediamidine (mp 131°C). N,N′,N″,N-tetraphenyl-heptanediamidine (mp 141°C). N,N',N'',N-tetraphenyl-decanediamidine (mp143℃).The heat-melting basic compound represented by the above general formula [] used in the present invention can be used in combination of two or more types. Also, since the blending ratio varies depending on the type of compound used, it cannot be determined unconditionally, but it is generally about 1 to 30 parts by weight, more preferably about 5 to 15 parts by weight, per 1 part by weight of the diazo compound. Various materials are known as diazo compounds that are used in combination with coloring aids made of such specific heat-melting basic compounds, such as p-N,N-dimethylaminobenzenediazonium. , 4-morpholino-2,5-dibutoxybenzenediazonium, 4-(4-methoxy)-benzylamino-2,
5-diethoxybenzenediazonium, 4-morpholinobenzenediazonium, 4-pyrrolidino-
3-methylbenzenediazonium, p-N-ethyl-N-hydroxyethylanilinediazonium, 4-benzamido-2,5-diethoxybenzenediazonium, 2-N,N-diethyl-m-
Toluidine diazonium, 6-morpholino-m-
Examples include double salts of chlorides such as toluidine diazonium and zinc chloride, tetraphenyl boron salts, boron tetrafluoride salts, phosphorous hexafluoride salts, and the like. The coupler is not particularly limited, and various known materials can be used as long as it forms an azo dye by coupling with a diazonium salt in a pressurizing atmosphere. in particular,
For example, resorcinol, catechol, phloroglucin, α-naphthol, 1,5-di-hydroxynaphthalene, 2,5-dimethyl-4-morpholinomethylphenol, sodium 1-hydroxynaphthalene-4-sulfonate, N-(3-morpholinomethylphenol), propyl)-3-hydroxy-2-naphthamide, 2-hydroxy-3-(β-hydroxyethylamide carbonyl)naphthalene, 2-hydroxynaphthalene-3-carbonyldiethanolamine, sodium 2-hydroxynaphthalene-3,6-disulfonate, Acetoacetanilide, 3
-Methyl-5-pyrazolone, 1-phenyl-3-
Methyl-5-pyrazolone, 2-hydroxy-3-
naphthoic acid-β-naphthylamide, 2-hydroxy-3-naphthoic acid-hydroxyethylamide,
1-hydroxy-2-naphthoic acid benzamide,
2-hydroxy-3-naphthoic acid benzamide,
2-Hydroxy-3-naphthoic acid m-nitrobenzamide, 2-hydroxy-3-naphthoic acid-
p-Chlorbenzamide, 2-hydroxy-3-
Naphthoic acid-o-ethoxybenzamide, 2-hydroxy-3-naphthoic acid-2,5-dimethoxybenzamide, etc. are suitable, and by mixing one or more of these, an image of any tone can be obtained. I can do it. The ratio of the diazonium salt and such coupler can be selected as appropriate depending on the materials used, but it is generally appropriate to use about 0.1 to 10 parts by weight of the coupler per 1 part by weight of the diazonium salt. be. Thus, in the present invention, a heat-sensitive recording layer containing at least one of a diazonium compound, a coupler, and a specific heat-melting basic compound as described above is formed on a support.
Generally, such a heat-sensitive recording layer is formed by preparing a coating solution containing the above-mentioned substances and coating it on a support. In addition, sodium naphthalene sulfonate, sodium naphthalene disulfonate, sulfosalicylic acid, magnesium sulfate,
Preservability improvers such as zinc chloride, antioxidants such as thiourea, diphenylthiourea, urea, acid stabilizers such as citric acid, malic acid, tartaric acid, phosphoric acid, saponin, starch, casein, gum arabic, polyvinyl alcohol, polyvinyl acetate emulsion,
Various water-soluble or water-insoluble adhesives such as SBR latex, pigments such as silica, clay, barium sulfate, titanium oxide, calcium carbonate, and dynamic,
Melting point depressants such as vegetable waxes, petroleum waxes, polyhydric alcohol esters of higher fatty acids, higher fatty acid amides, condensates of higher fatty acids and amines, synthetic paraffins, chlorinated paraffins, alkyl or aryl esters of naphthoic acid, etc. etc. are appropriately blended. The coating solution prepared in this way is coated on a suitable support such as paper, plastic film, synthetic paper, metal film, etc., but the coating method is not particularly limited and can be applied using any conventional method. Therefore, by using a suitable coating device such as an air knife coater, roll coater, blade coater, short dwell coater, etc., a dry weight of 3 to 10 g/
It is coated and dried for about ² m2. The heat-sensitive recording material of the present invention thus obtained has excellent storage stability over a long period of time without causing pre-coupling and coloring of the recording layer during storage, unlike conventional recording materials. In addition, in the recording medium of the present invention, a recorded image is formed using a thermal pen, a thermal head, etc. in the same way as a normal heat-sensitive recording medium, and then the entire surface is irradiated with ultraviolet light using a fluorescent light, mercury lamp, etc., to remove the non-recorded areas. A recorded image can be fixed by decomposing unreacted diazonium salt. "Examples" The present invention will be described in more detail with reference to Examples below, but the present invention is not limited thereto. In addition, unless otherwise specified, parts and percentages in examples are as follows:
Weight parts and weight % are shown, respectively. Example 1 Preparation of Solution A p-N,N-diethylaminobenzenediazonium tetraphenylboron 2 parts Calcium carbonate 50 parts 10% aqueous solution of polyvinyl alcohol 50 parts Water 100 parts The above composition was dispersed in a ball mill for 48 hours, and A
A liquid was prepared. Preparation of Solution B 2-hydroxy-3-naphthoic acid-o-ethoxybenzamide 25 parts N,N',N'',N,-tetraphenyl-decanediamidine 25 parts 20% aqueous dispersion of stearic acid amide 40 parts polyvinyl alcohol 10% aqueous solution 50 parts Disperse the above composition in a ball mill for 48 hours,
A liquid was prepared. Using a wire bar, add 49g of the above dispersion B/
Coat and dry to a dry weight of 4 g/m ² on a m ² high-quality paper, and then coat and dry dispersion A to a dry weight of 4 g/m ² on top of the coated layer. A thermosensitive recording material was obtained. Example 2 Preparation of Solution A 4-morpholino-2,5-dibutoxybenzenediazonium phosphorus heptafusinide 2 parts Titanium oxide 50 parts 10% aqueous solution of polyvinyl alcohol 50 parts Water 100 parts The above composition was dispersed in a ball mill for 48 hours. ,A
A liquid was prepared. Preparation of liquid B 2-hydroxy-3-naphthoic acid benzamide
25 parts N, N', N'', N-tetraphenyl-p-xylene diamidine 25 parts 20% aqueous dispersion of stearic acid amide 40 parts 10% aqueous solution of polyvinyl alcohol 50 parts The above composition was dispersed in a ball mill for 48 hours. B
A liquid was prepared. A thermosensitive recording material was obtained in the same manner as in Example 1 except that the above dispersions A and B were used. Example 3 Solution A Preparation 4-(4-methoxy)-benzoylamino-2,
5-Diethoxybenzenediazonium boron tetrafluoride 2 parts Finely powdered silica 25 parts Barium sulfate 25 parts Citric acid 2 parts 10% aqueous solution of polyvinyl alcohol 50 parts Water 100 parts The above composition was dispersed in a ball mill for 48 hours, and A
A liquid was prepared. Preparation of Solution B 2-Hydroxynaphthalene-3-carbonyldiethanolamine 25 parts N,N''-dicyclohexyl-decane diamidine 25 parts Tribenzylamine 10 parts Diphenylthiourea 2 parts 10% aqueous solution of polyvinyl alcohol 50 parts Water 50 parts The above composition Dispersed in a ball mill for 48 hours, B
A liquid was prepared. A thermosensitive recording material was obtained in the same manner as in Example 1 except that the above dispersions A and B were used. Example 4 Preparation of Solution A p-N,N-diethylaminobenzenediazonium tetrafluoroboron 2 parts Thiourea 2 parts Tartaric acid 2 parts 10% toluene solution of vinyl chloride/vinyl acetate copolymer 50 parts Finely powdered silica 25 parts Toluene 50 Part The above composition was dispersed in a ball mill for 48 hours, and A
A liquid was prepared. Preparation of Solution B It was prepared in the same manner as Solution B in Example 1. Using a wire bar, add 49g of the above dispersion A/
Coat and dry to a dry weight of 3 g/m ² on a m ² high-quality paper, and then coat and dry dispersion B on top of the coated layer in a similar manner to a dry weight of 4 g/m ² . A thermosensitive recording material was obtained. Comparative Example 1 A thermosensitive recording material was obtained in the same manner as in Example 1 except that N, N', N'', N-tetraphenyl-decanediamidine in Solution B of Example 1 was changed to stearylamine. Comparative Example 2 A thermosensitive recording material was obtained in the same manner as in Example 2 except that N,N',N'',N-tetraphenyl-p-xylene diamidine in Solution B of Example 2 was replaced with ammonium stearate. Comparative tests were conducted on the color density and storage stability of the six types of heat-sensitive recording materials thus obtained. That is, the recording medium was brought into contact with a hot plate at 110° C. for 2 seconds to develop color, and the image was fixed by exposure to ultraviolet light, and then the color density was measured using a Macbeth densitometer (yellow filter). In addition, regarding storage stability, the heat-sensitive recording material immediately after coating and 30℃, 70%RH
The fog densities of the heat-sensitive recording media after being left for 7 days under the following conditions were measured using a Macbeth densitometer (yellow filter) and compared. The results of each test are shown in Table 1.

【table】

[Table] "Effects" As is clear from the results in Table 1, all the thermosensitive recording materials obtained in the Examples of the present invention had excellent storage stability and exhibited good color density.

Claims (1)

[Scope of Claims] 1. A heat-sensitive recording material, characterized in that a heat-sensitive recording layer containing at least a diazonium compound and a coupler of one kind of heat-melting basic compound represented by the following general formula [] is provided on a support. . [In the formula, R ₁ , R ₂ , R ₃ , R ₄ , R ₅ , and R ₆ are each an alkyl group, an alkoxyl group, a nitro group, or an aryl group optionally substituted with a halogen atom; an aralkyl group; an alkyl group; Group; indicates a cyclic alkyl group or a hydrogen atom. R represents an alkylene group; a phenylene group; a naphthylene group; or [Formula] (wherein X represents an alkylene group; SO ₂ ; S; O; NH; or a single bond). ]