JPH0416972A - Conductive resin material - Google Patents
Conductive resin materialInfo
- Publication number
- JPH0416972A JPH0416972A JP2121715A JP12171590A JPH0416972A JP H0416972 A JPH0416972 A JP H0416972A JP 2121715 A JP2121715 A JP 2121715A JP 12171590 A JP12171590 A JP 12171590A JP H0416972 A JPH0416972 A JP H0416972A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- conductive
- phenol
- rosin
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は、電子写真複写機等に用いられる現像ロール
の構成成分となる導電性樹脂材料に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to a conductive resin material that is a component of a developing roll used in an electrophotographic copying machine or the like.
〔従来の技術］
−ｉに、電子写真複写機は、つぎのようにして複写する
ようになっている。すなわち、軸を中心に回転する感光
ドラムの外周面を、コロトロンによるイオン帯電ないし
は帯電ロールによる摩擦帯電により、−様にプラスもし
くはマイナスに帯電させ、その感光ドラムの表面に、原
稿光像のスリット露光を投射し、原稿光像に対応した静
電潜像を形成する。そして、現像ロールとトナーとを接
触させその摩擦によりトナーを帯電させ、これを上記感
光ドラムの静電潜像に電気的吸引力によって付着させト
ナー像を形成し、このトナー像を複写紙に転写し定着さ
せることにより複写するようになっている。[Prior Art] -i. An electrophotographic copying machine is designed to copy in the following manner. That is, the outer circumferential surface of a photosensitive drum that rotates around its axis is positively or negatively charged by ion charging by a corotron or frictional charging by a charging roll, and the surface of the photosensitive drum is exposed to a slit of an optical image of the original. is projected to form an electrostatic latent image corresponding to the original optical image. Then, the developing roll and the toner are brought into contact, and the toner is charged by the friction, and the toner is attached to the electrostatic latent image on the photosensitive drum by electric attraction to form a toner image, and this toner image is transferred to copy paper. Copies are made by fixing the image.
〔発明が解決しようとする課題］
このような構造の電子写真複写機において、特に最近で
は、複写画像の画質の向上が求められており、微細な画
像であっても鮮明な状態で得られることが望まれている
。しかしながら、現在の段階では、トナー等の現像剤に
対する電荷の付与がいまだ充分とはいえず、しかも−旦
電荷が付与された現像剤についても、現像ロール中の導
電材成分の除電効果によって電荷が失われるため、高画
質の複写画像の形成に関しては問題がある。[Problems to be Solved by the Invention] In electrophotographic copying machines having such a structure, there has been a demand, especially recently, to improve the image quality of copied images, and it is desirable to be able to obtain even minute images in a clear state. is desired. However, at the current stage, it cannot be said that charging toner and other developers is sufficient, and even once charged, the charge is removed by the neutralizing effect of the conductive material component in the developing roll. This poses a problem when it comes to forming high-quality copied images.
この発明は、このような事情に鑑みなされたもので、高
画質の複写画像を形成することができる導電性樹脂材料
の提供をその目的とする。The present invention was made in view of the above circumstances, and an object of the present invention is to provide a conductive resin material that can form high-quality copied images.
上記の目的を達成するため、この発明の導電性樹脂材料
は、下記の（Ａ）〜（Ｅ）成分を含有するという構成を
とる。In order to achieve the above object, the conductive resin material of the present invention is configured to contain the following components (A) to (E).
（Ａ）フェノールノボラック樹脂。(A) Phenol novolac resin.
（Ｂ）ロジンフェノール樹脂。(B) Rosin phenolic resin.
（Ｃ）硬化剤。(C) Hardening agent.
（Ｄ）充填剤。(D) Filler.
（Ｅ）導電材。(E) Conductive material.
〔作用］
本発明者らは、上記従来の欠点を解決する目的で、現像
ロールの構成材料を中心に研究を重ねた。その結果、現
像ロールを構成する導電性樹脂材料として、フェノール
ノボラック樹脂とロジンフェノール樹脂とを併用したも
のを用いると、そのロジンフェノール樹脂の作用により
、正帯電トナーをプラス帯電させる場合に、帯電量が大
幅に向上することを見いだしこの発明に到達した。[Function] In order to solve the above-mentioned conventional drawbacks, the present inventors have conducted extensive research focusing on the constituent materials of the developing roll. As a result, if a combination of phenol novolak resin and rosin phenol resin is used as the conductive resin material constituting the developing roll, the amount of charge will decrease due to the action of the rosin phenol resin when positively charging toner. This invention was achieved by discovering that this can be significantly improved.
この発明の導電性樹脂材料は、フェノールノボラック樹
脂〈（Ａ）成分〉、ロジンフェノール樹脂〈（Ｂ）成分
）、硬化剤〈（Ｃ）成分）、充填剤〈（Ｄ）成分〉およ
び導電材〈（Ｅ）成分〉を用いて得られる６通常、この
導電性樹脂材料は、ペレット状、粉末状になっている。The conductive resin material of the present invention includes a phenol novolak resin (component (A)), a rosin phenolic resin (component (B)), a curing agent (component (C)), a filler (component (D)), and a conductive material. This conductive resin material obtained using component (E)> is usually in the form of pellets or powder.
上記、（Ａ）成分のフェノールノボラック樹脂としては
、特に制限するものではなく、従来から使用されている
フェノールノボラック樹脂をそのまま使用することがで
きる。The phenol novolak resin of component (A) is not particularly limited, and conventionally used phenol novolak resins can be used as they are.
また、上記フェノールノボラック樹脂と併用する（Ｂ）
成分のロジンフェノール樹脂は、下記の式で表されるよ
うに、ロジンとフェノールとを酸の下で反応させて得ら
れたものである。In addition, (B) used in combination with the above phenol novolak resin
The component rosin phenol resin is obtained by reacting rosin and phenol in the presence of an acid, as represented by the following formula.
そして、上記フェノールノボラック樹脂とロジンフェノ
ール樹脂との使用割合は、フェノールノボラック樹脂８
０重量部（以下「部」と略す）に対してロジンフェノー
ル樹脂２０部の割合からフェノールノボラック樹脂５０
部に対しロジンフェノール樹脂５０部の割合の範囲内に
選ばれる。この範囲であれば、正帯電トナーに対する大
幅な帯電量の向上効果が得られるようになる。The ratio of the phenol novolac resin and rosin phenol resin used is 80% of the phenol novolac resin.
From the ratio of 20 parts of rosin phenol resin to 0 parts by weight (hereinafter abbreviated as "parts"), 50 parts of phenol novolak resin
part of rosin phenolic resin to 50 parts of rosin phenolic resin. Within this range, the effect of significantly improving the amount of charge on positively charged toner can be obtained.
このようなフェノールノボラック樹脂とロジンフェノー
ル樹脂との合計含有量は、これらが導電性樹脂材料全体
の２０〜７０重量％の範囲内になるように設定すること
が帯電量の向上効果および現像ロールの機械的強度等の
点から好ましい。The total content of such phenol novolak resin and rosin phenol resin should be set within the range of 20 to 70% by weight of the entire conductive resin material to improve the charge amount and improve the development roll. Preferable from the viewpoint of mechanical strength and the like.
上記（Ｃ）成分の硬化剤は、上記（Ａ）成分のフェノー
ルノボラック樹脂およびｔＢｕ−フェノールノボラック
の硬化剤となるものであり、通常へキサメチレンテトラ
ミンが使用される。The curing agent for component (C) serves as a curing agent for the phenol novolac resin and tBu-phenol novolac for component (A), and hexamethylenetetramine is usually used.
上記（Ａ）成分および（Ｂ）成分とともに用いられる（
Ｄ）成分の充填剤としては、ガラス繊維、ケイ酸カルシ
ウム（ワラストナイト）等があげられる。Used with the above (A) component and (B) component (
Examples of the filler of component D) include glass fiber and calcium silicate (wollastonite).
また、（Ｅ）成分の導電材としては、カーボンブラック
、グラフアイｆ−，Ｃ−３ｎＯ□、 Ｃ−ＴｌＯ２等
があげられる。Further, examples of the conductive material of component (E) include carbon black, grapheye f-, C-3nO□, C-TlO2, and the like.
なお、上記（Ａ）〜（Ｅ）成分以外に、ステアリン酸等
の離型剤、水酸化カルシウム等の難燃剤、フルフラール
、ポリクレジルホスフェイト等の可塑剤ならびに染料、
顔料等の着色剤が必要に応して用いられる。In addition to the above components (A) to (E), mold release agents such as stearic acid, flame retardants such as calcium hydroxide, plasticizers such as furfural and polycresyl phosphate, and dyes,
Coloring agents such as pigments are used as necessary.
上記のような（Ａ）〜（Ｅ）成分を配合するに際しては
、導電材のうち特にＣＴｉ０ｚおよびＣ３ｎＯｚの少な
くとも一方をロジンフェノール樹脂と併用すると、その
相乗効果により正帯電トナーに対するプラス電荷の帯電
量の一層の向上効果が得られるようになる。When blending the above-mentioned components (A) to (E), if at least one of the conductive materials CTi0z and C3nOz is used in combination with the rosin phenol resin, the synergistic effect will increase the amount of positive charge on the positively charged toner. Further improvement effects can be obtained.
この発明の導電性樹脂材料は、上記原料を用い、例えば
つぎのようにして製造することができる。すなわち、上
記例示のフェノールノボラック樹脂〈（Ａ）成分〉、ロ
ジンフェノール樹脂＜（Ｂ）成分を用い、これに上記（
Ｃ）および（Ｄ）成分材料ならびにその他の添加剤を適
宜に配合してベース成分材料とし、これに（Ｅ）成分の
導電材を配合する。この場合、導電材の使用割合は上記
ベース成分材料中の樹脂（フェノールノボラック十ロジ
ンフェノール樹脂）１００部に対して２０〜３５０部の
割合で配合することが効果の点で好ましい。つぎに、こ
のような配合物を、従来公知のニーダーのような混合機
で混合、混練し、ついで粉砕してペレット状等に形成す
ることにより得られる。なお、上記混合混練に際しては
、上記のように原料を配合してから投入し混合する以外
に、各原料をＲ合表に従って順次投入し混合、混練する
ことも行われる。The conductive resin material of the present invention can be manufactured using the above-mentioned raw materials, for example, in the following manner. That is, the above-exemplified phenol novolac resin <(A) component> and the rosin phenol resin <(B) component are used, and the above-mentioned ((A) component) is used.
Component materials C) and (D) and other additives are appropriately blended to form a base component material, and a conductive material as component (E) is blended therein. In this case, from the viewpoint of effectiveness, it is preferable that the conductive material be used in a ratio of 20 to 350 parts per 100 parts of the resin (phenol novolak and rosin phenol resin) in the base component material. Next, such a blend is mixed and kneaded using a conventionally known mixer such as a kneader, and then pulverized to form pellets or the like. In addition, when mixing and kneading, in addition to blending the raw materials as described above and then adding and mixing them, each raw material is also sequentially added, mixed, and kneaded according to the R combination table.
このようにして得られたこの発明の導電性樹脂材料は、
通常、押出成形機等を用いて円筒状に押出成形され、図
面に示すように芯金１の外周に、導電層２として外嵌さ
れる。この場合、外嵌に際しては、金属粉末等の微細導
電材粒子を含んだ接着剤を芯金１の外周面もしくは円筒
成形体の内周面に塗布することが行われ、これが導電性
接着剤層３になる。このようにして得られた現像ロール
では、導電層２がこの発明の導電性樹脂材料で構成され
ており、ロジンフェノール樹脂の作用により、正帯電ト
ナーに対するプラス電荷の帯電量の大幅な向上効果を実
現することができる。The conductive resin material of the present invention thus obtained is
Usually, it is extruded into a cylindrical shape using an extrusion molding machine or the like, and is fitted around the outer periphery of the core bar 1 as a conductive layer 2, as shown in the drawings. In this case, when externally fitting, an adhesive containing fine conductive material particles such as metal powder is applied to the outer peripheral surface of the core bar 1 or the inner peripheral surface of the cylindrical molded body, and this forms a conductive adhesive layer. It becomes 3. In the developing roll thus obtained, the conductive layer 2 is made of the conductive resin material of the present invention, and the effect of the rosin phenol resin significantly improves the amount of positive charge on the positively charged toner. It can be realized.
なお、上記現像ロールは、電子写真複写機のみならず、
ファクシミリ、プリンター等にも広く使用される。Note that the above developing roll can be used not only for electrophotographic copying machines, but also for electrophotographic copying machines.
Widely used for facsimiles, printers, etc.
以上のように、この発明の導電性樹脂材料は、フェノー
ルノボラック樹脂、硬化剤、充填剤、導電材を含み、上
記フェノールノボラック樹脂とロジンフェノール樹脂と
を併用しているため、これで現像ロールを構成した場合
に、ロジンフェノール樹脂の作用により、正帯電トナー
に対する大幅な帯電量の向上効果を実現することができ
る。したがって、これを電子写真複写機等に用いた場合
には、複写画像の高画質化効果を得ることができるよう
になる。As described above, the conductive resin material of the present invention contains a phenol novolak resin, a curing agent, a filler, and a conductive material, and since the above-mentioned phenol novolac resin and rosin phenol resin are used together, it can be used as a developing roll. In this case, the action of the rosin phenol resin can significantly improve the amount of charge on positively charged toner. Therefore, when this is used in an electrophotographic copying machine or the like, it is possible to obtain the effect of increasing the quality of the copied image.
つぎに、実施例について説明する。Next, examples will be described.
後記の表に示す各原料を同表に示す割合で配合した。そ
して、これらをニーダ−を用いて均一に混合混練したの
ち、粉砕して粒径０．１〜２ＩＩＩＩ１１程度のペレッ
トをつくった。The raw materials shown in the table below were blended in the proportions shown in the table. Then, these were uniformly mixed and kneaded using a kneader, and then pulverized to form pellets having a particle size of about 0.1 to 2III11.
つぎに、このようにして得られた導電性樹脂材料を用い
、外径が２５ｍｍで導電層の厚みが２１１Ｉｌｎの現像
ロールをつくった。得られた現像ロールにおける電気抵
抗および負帯電トナーに対する帯電量の向上効果と、正
帯電トナーに対する帯電量の向上効果を同表に併せて示
した。なお、帯電量は比較例１の帯電量を１００とし、
これを基準に数値が大きいものが帯電量が向上しており
、低いものが帯電量が低下していることを示している。Next, a developing roll having an outer diameter of 25 mm and a conductive layer thickness of 211 ln was made using the conductive resin material thus obtained. The electrical resistance of the obtained developing roll and the effect of improving the amount of charge on negatively charged toner and the effect of improving the amount of charge on positively charged toner are also shown in the same table. Note that the amount of charge is based on the amount of charge of Comparative Example 1 as 100,
Based on this, a larger value indicates an improved charge amount, and a lower value indicates a decreased charge amount.
（以下余白）
上記の表から明らかなように、実施測高によれば、正帯
電トナーに対する帯電量の大幅な向上効果が得られ、高
画質で鮮明な複写画像が得られることがわかる。(The following is a blank space) As is clear from the above table, according to the actual height measurement, it is possible to obtain a significant improvement effect in the amount of charge for positively charged toner, and to obtain a high quality and clear copy image.
図面はこの発明の導電性樹脂材料を用いた現像ロールの
構成図である。
■・・・芯金 ２・・・導電層 ３・・・導電性接着剤
層特許出願人 東海ゴム工業株式会社The drawing is a configuration diagram of a developing roll using the conductive resin material of the present invention. ■... Core metal 2... Conductive layer 3... Conductive adhesive layer Patent applicant Tokai Rubber Industries Co., Ltd.
Claims (1)
とする導電性樹脂材料。 （Ａ）フェノールノボラック樹脂。 （Ｂ）ロジンフェノール樹脂。 （Ｃ）硬化剤。 （Ｄ）充填剤。 （Ｅ）導電材。(1) A conductive resin material characterized by containing the following components (A) to (E). (A) Phenol novolac resin. (B) Rosin phenolic resin. (C) Hardening agent. (D) Filler. (E) Conductive material.