JPH0351267B2 - - Google Patents

Info

Publication number
JPH0351267B2
JPH0351267B2 JP24624183A JP24624183A JPH0351267B2 JP H0351267 B2 JPH0351267 B2 JP H0351267B2 JP 24624183 A JP24624183 A JP 24624183A JP 24624183 A JP24624183 A JP 24624183A JP H0351267 B2 JPH0351267 B2 JP H0351267B2
Authority
JP
Japan
Prior art keywords
weight
brush
alloy material
sliding
sliding contact
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP24624183A
Other languages
Japanese (ja)
Other versions
JPS60138886A (en
Inventor
Susumu Fujishima
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tanaka Kikinzoku Kogyo KK
Original Assignee
Tanaka Kikinzoku Kogyo KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tanaka Kikinzoku Kogyo KK filed Critical Tanaka Kikinzoku Kogyo KK
Priority to JP24624183A priority Critical patent/JPS60138886A/en
Publication of JPS60138886A publication Critical patent/JPS60138886A/en
Publication of JPH0351267B2 publication Critical patent/JPH0351267B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】[Detailed description of the invention]

本発明は、摺動接点装置に係り、特にそれを構
成するブラシとコンミテータ又はスリツプリング
の材料の改良に関する。 従来の摺動接点装置は、Au69〜74重量%、
Pt6.5〜10.5重量%、Ag2.5〜6.5重量%、Cu12.5〜
16.5重量%、Zn0.1〜2重量%の合金材料にて構
成したブラシと、Ag−Cd0.5〜15重量%の合金材
料にて構成したコンミテータ又はスリツプリング
とを組合わせて成るものである。 ところで、この摺動接点装置のブラシは、コン
ミテータ又はスリツプリングとの摺動時に凝着し
て耐摩耗性が劣つていた。 一方、コンミテータ又はスリツプリングは、
Ag−Cd0.5〜15重量%の合金材料により構成さ
れ、ブラシとの摺動時、粘着性が高く耐摩耗性に
劣るものであつた。 本発明は、斯かる欠点を解消すべくなされたも
のであり、ブラシの耐摩耗性を向上させ、コンミ
テータ又はスリツプリングの耐摩耗性を向上させ
た摺動接点装置を提供せんとするものである。 本発明の摺動接点装置は、組成比でAu69〜74
重量%、Pt6.5〜10.5重量%、Ag2.5〜6.5重量%、
Cu12.5〜16.5重量%、Zn0.1〜2重量%のAu−Pt
−Ag−Cu−Znが95〜99.5重量%及び残部がCo、
Sn及びTiの少なくとも1種を合計で0.5〜5重量
%から成る合金材料にて構成したブラシと、Ag
−Cu3〜12重量%又はAg−Cu3〜12重量%−Cd5
重量%以下の合金材料にて構成したコンミテータ
又はスリツプリングとを組合わせて成るものであ
る。 本発明の摺動接点装置に於いて、ブラシを組成
比でAu69〜74重量%、Pt6.5〜10.5重量%、
Ag2.5〜6.5重量%、Cu12.5〜16.5重量%、Zn0.1
〜2重量%のAu−Pt−Ag−Cu−Znが95〜99.5重
量%及び残部がCo、Sn及びTiの少なくとも1種
を合計で0.5〜5重量%から成る合金材料にて構
成した理由は、前記Au−Pt−Ag−Cu−Znの合
金材料の耐摩耗性を向上すべく硬くして摺動時の
凝着を防止する為で、0.5重量%未満ではその効
果を発揮できず、5重量%を超えると酸化物の発
生量が多くなり、接触抵抗が高くなり、その上不
安定となるものである。また、Au、Pt、Ag、
Cu、Znの含有量は、前記従来の合金材料の組成
比に変更を加えない範囲とすることにより、従来
の合金材料の特性は損なわれることなく発揮され
ることとなるものである。 コンミテータ又はスリツプリングを、Ag−
Cu3〜12重量%又はAg−Cu3〜12重量%−Cd5重
量%以下の合金材料にて構成した理由は、ブラシ
との摺動時の粘着性を抑えて耐摩耗性を向上させ
る為で、Cuの含有量が3重量%未満ではその効
果が得られず、12重量%を超えると摺動時に発生
する酸化物の量が多くなりすぎて接触抵抗が高く
不安定になり、Cdの含有量が5重量%を超える
とこれが酸化Cdとなつた際、接触抵抗が高くな
り、耐摩耗性が劣下するものである。従つて、
Cuの含有量は3〜12重量%、Cdの含有量は5重
量%を超えないようにしたものである。 次に本発明による摺動接点装置の具体的な実施
例と従来例について説明する。 下記の表−1の左欄に示す成分組成の実施例及
び従来例の合金材料より成る線径0.7mmのブラシ
線材を各々長さ8mmに切断し、2本並列させて一
端を幅10mm、長さ13mm、厚さ0.2mmの台材に溶接
し、他端に2Rの円弧状の接触部を曲成してブラ
シを作つた。一方下記の表−1の右欄に示す成分
組成の実施例及び従来例の合金材料により成る厚
さ0.5mmの板材を打抜いて直径50mmのスリツプリ
ングを作つた。然してこれらブラシ及びスリツプ
リングを夫々組合わせて摺動接点装置を作り、
夫々ブラシをスリツプリングに接触させ、スリツ
プリングを正逆回転させて下記の試験条件にて摺
動試験を行ない、ブラシ及びスリツプリングの摩
耗量と接触抵抗を測定した処、下記の表−2に示
すような結果を得た。 試験条件 電流:0.6A 電圧:12V 負荷:抵抗負荷 回転数:1000回転/分 周速度:120〜130m/min 接触力:100g 摺動時間:7時間
The present invention relates to a sliding contact device, and particularly to improvements in the materials of the brush, commutator, or slip ring constituting the sliding contact device. Conventional sliding contact devices are made of Au69~74% by weight,
Pt6.5~10.5wt%, Ag2.5~6.5wt%, Cu12.5~
It is a combination of a brush made of an alloy material containing 16.5% by weight of Zn and 0.1 to 2% by weight of Zn, and a commutator or slip ring made of an alloy material of 0.5 to 15% by weight of Ag-Cd. . By the way, the brush of this sliding contact device adheres to the commutator or the slip ring when sliding, and has poor wear resistance. On the other hand, a commutator or slip ring is
It was composed of an alloy material containing 0.5 to 15% by weight of Ag-Cd, and had high stickiness and poor abrasion resistance when sliding with a brush. The present invention has been made to eliminate such drawbacks, and aims to provide a sliding contact device in which the wear resistance of the brush is improved and the wear resistance of the commutator or slip ring is improved. . The sliding contact device of the present invention has a composition ratio of Au69 to Au74.
Weight%, Pt6.5~10.5wt%, Ag2.5~6.5wt%,
Au-Pt with Cu12.5~16.5wt%, Zn0.1~2wt%
-Ag-Cu-Zn is 95 to 99.5% by weight and the balance is Co,
A brush made of an alloy material containing a total of 0.5 to 5% by weight of at least one of Sn and Ti;
−Cu3~12wt% or Ag−Cu3~12wt%−Cd5
It is combined with a commutator or a slip ring made of an alloy material of less than % by weight. In the sliding contact device of the present invention, the composition ratio of the brush is 69 to 74% by weight of Au, 6.5 to 10.5% by weight of Pt,
Ag2.5~6.5wt%, Cu12.5~16.5wt%, Zn0.1
The reason why the alloy material is composed of ~2% by weight of Au-Pt-Ag-Cu-Zn is 95-99.5% by weight and the balance is at least 0.5-5% by weight of at least one of Co, Sn and Ti in total. , in order to improve the wear resistance of the Au-Pt-Ag-Cu-Zn alloy material, it is hardened to prevent adhesion during sliding, and if it is less than 0.5% by weight, the effect cannot be achieved. If it exceeds % by weight, the amount of oxides generated will increase, contact resistance will increase, and furthermore, it will become unstable. Also, Au, Pt, Ag,
By setting the contents of Cu and Zn within a range that does not change the composition ratio of the conventional alloy material, the characteristics of the conventional alloy material can be exhibited without being impaired. Commutator or slip spring, Ag-
The reason why it is made of an alloy material containing less than 3 to 12 weight % Cu or 3 to 12 weight % Ag-Cu and 5 weight % Cd is to suppress the stickiness when sliding with the brush and improve wear resistance. If the content of Cd is less than 3% by weight, the effect cannot be obtained, and if it exceeds 12% by weight, the amount of oxide generated during sliding becomes too large, resulting in high contact resistance and instability. If it exceeds 5% by weight, when it becomes oxidized Cd, the contact resistance increases and wear resistance deteriorates. Therefore,
The content of Cu is 3 to 12% by weight, and the content of Cd is not more than 5% by weight. Next, specific embodiments and conventional examples of the sliding contact device according to the present invention will be described. Brush wire rods with a wire diameter of 0.7 mm made of alloy materials of the example and conventional example shown in the left column of Table 1 below were each cut into lengths of 8 mm, and two wire rods were placed in parallel with one end having a width of 10 mm and a length of 8 mm. A brush was made by welding it to a base material with a length of 13 mm and a thickness of 0.2 mm, and a 2R arc-shaped contact part was curved at the other end. On the other hand, slip rings with a diameter of 50 mm were made by punching out 0.5 mm thick plates made of alloy materials having the compositions shown in the right column of Table 1 below. Therefore, a sliding contact device was made by combining these brushes and slip rings, respectively.
A sliding test was conducted under the following test conditions by bringing each brush into contact with the slip ring and rotating the slip ring in forward and reverse directions.The wear amount and contact resistance of the brush and slip ring were measured, and the results are shown in Table 2 below. We obtained the results shown below. Test conditions Current: 0.6A Voltage: 12V Load: Resistance load Rotation speed: 1000 rotations/Division speed: 120-130m/min Contact force: 100g Sliding time: 7 hours

【表】【table】

【表】【table】

【表】 上記の表−2で明らかなように実施例1〜13の
摺動接点装置のブラシとスリツプリングは、夫々
従来例1、2の摺動接点のブラシとスリツプリン
グに比し摩耗量が著しく少なく、接触抵抗は同等
に安定していることが判る。これはひとえに実施
例1〜13の摺動接点装置のブラシを構成している
合金材料が、Co、Sn、Tiの少なくとも1種の添
加により硬くなり摺動時の耐凝着性が向上し、ま
た摺動時に発生する酸化物の量が摩耗量とバラン
スしているからに他ならない。また実施例1〜13
の摺動接点装置のスリツプリングを構成している
合金材料のCuによつて摺動時の粘着性が高くな
るのが抑えられて耐摩耗性が向上しているからに
他ならない。 以上詳記した通り本発明の摺動接点装置は、従
来の摺動接点装置に比べブラシとコンミテータ又
はスリツプリングの耐摩耗性が著しく優れてい
て、摩耗粉の発生量が極めて少なく、従来の摺動
接点装置にとつて代わることのできる画期的なも
のと云える。
[Table] As is clear from Table 2 above, the brushes and slip rings of the sliding contact devices of Examples 1 to 13 have a higher amount of wear than the brushes and slip rings of the sliding contact devices of Conventional Examples 1 and 2, respectively. It can be seen that the contact resistance is significantly lower and the contact resistance is equally stable. This is because the alloy material constituting the brush of the sliding contact devices of Examples 1 to 13 becomes hard due to the addition of at least one of Co, Sn, and Ti, and the adhesion resistance during sliding is improved. This is also because the amount of oxide generated during sliding is in balance with the amount of wear. Also, Examples 1 to 13
This is because the Cu alloy material that makes up the slip ring of the sliding contact device suppresses the increase in stickiness during sliding and improves wear resistance. As described in detail above, the sliding contact device of the present invention has significantly superior wear resistance of the brush and commutator or slip ring compared to conventional sliding contact devices, generates extremely little wear powder, and is superior to conventional sliding contact devices. It can be said to be an epoch-making device that can replace dynamic contact devices.

Claims (1)

【特許請求の範囲】[Claims] 1 組成比でAu69〜74重量%、Pt6.5〜10.5重量
%、Ag2.5〜6.5重量%、Cu12.5〜16.5重量%、
Zn0.1〜2重量%のAu−Pt−Ag−Cu−Znが95〜
99.5重量%及び残部がCo、Sn及びTiの少なくと
も1種を合計で0.5〜5重量%から成る合金材料
にて構成したブラシと、Ag−Cu3〜12重量%又
はAg−Cu3〜12重量%−Cd5重量%以下の合金材
料にて構成したコンミテータ又はスリツプリング
とを組合わせて成る摺動接点装置。
1 Composition ratio: Au69-74% by weight, Pt6.5-10.5% by weight, Ag2.5-6.5% by weight, Cu12.5-16.5% by weight,
Zn0.1~2wt% Au-Pt-Ag-Cu-Zn 95~
A brush made of an alloy material consisting of 99.5% by weight and the balance of at least one of Co, Sn and Ti in total of 0.5 to 5% by weight, and Ag-Cu3 to 12% by weight or Ag-Cu3 to 12% by weight. A sliding contact device consisting of a commutator or slip ring made of an alloy material containing 5% by weight of Cd or less.
JP24624183A 1983-12-27 1983-12-27 Slide contact unit Granted JPS60138886A (en)