JPH03193223A - Manufacture of aluminum or aluminum alloy can - Google Patents
Manufacture of aluminum or aluminum alloy canInfo
- Publication number
- JPH03193223A JPH03193223A JP1335849A JP33584989A JPH03193223A JP H03193223 A JPH03193223 A JP H03193223A JP 1335849 A JP1335849 A JP 1335849A JP 33584989 A JP33584989 A JP 33584989A JP H03193223 A JPH03193223 A JP H03193223A
- Authority
- JP
- Japan
- Prior art keywords
- wax
- aluminum
- alloy
- cans
- adhesion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
[産業上の利用分野コ
本発明は、アルミニウムまたはアルミニウム合金製缶の
製造方法に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application] The present invention relates to a method for manufacturing aluminum or aluminum alloy cans.
[従来の技術]
従来から、アルミニウムまたはアルミニウム合金(以下
両者を総称して「アルミ」という)製の素板にワックス
を塗布して深しぼり加工を行い、アルミ缶を製造すると
いう技術が行なわれている。この従来の技術によれば、
ワックスを塗布することによって、アルミ缶にしわや亀
裂が生じるおそれを減少させることができるという利点
がある。[Prior Art] Conventionally, a technology has been used to manufacture aluminum cans by applying wax to a blank plate made of aluminum or aluminum alloy (hereinafter collectively referred to as "aluminum") and deep drawing. ing. According to this conventional technique,
Application of wax has the advantage of reducing the risk of wrinkles and cracks forming in the aluminum can.
[発明が解決しようとする課題]
しかしながら、上記従来の技術においては、単位面積当
たりのアルミ素板へのワックス付着量を一定とすること
ができないため、ワックス付着量が適正値に対して過多
または過少となることがあった。深しぼり加工において
、ワックス付着量が過多である場合には、アルミ缶表面
にワックスとアルミナ粉との混合物が付着し、アルミ缶
表面が汚れる危険性が高くなり、また、ワックス付着量
が過少である場合には、アルミ缶にしわや亀裂が生じる
危険性が高くなる。このように、従来の技術においては
、ワックスの付着量が過多ますこは過少となって、アル
ミ缶における不良品発生率が高くなるおそれがあるとい
う不都合がある。[Problems to be Solved by the Invention] However, in the above-mentioned conventional technology, it is not possible to keep the amount of wax deposited on the aluminum base plate constant per unit area, so the amount of wax deposited may be excessive or excessive compared to the appropriate value. Sometimes it was too low. In the deep drawing process, if too much wax is applied, a mixture of wax and alumina powder will adhere to the surface of the aluminum can, increasing the risk of staining the surface of the aluminum can. In some cases, there is an increased risk that aluminum cans will wrinkle or crack. As described above, in the conventional technology, there is a problem that the amount of wax attached is too large and the amount of wax is too small, which may increase the incidence of defective products in aluminum cans.
本発明は、上記した事情に鑑みてなされたもので、アル
ミ素板へのワックス付着量を適正値に保つことのできる
アルミ缶の製造方法を提供することを目的とする。The present invention has been made in view of the above-mentioned circumstances, and an object of the present invention is to provide a method for manufacturing aluminum cans that can maintain the amount of wax adhering to an aluminum base plate at an appropriate value.
[課題を解決するための手段]
本発明者は、アルミ素板へのワックス付着量を適正な範
囲内に維持するために、鋭意研究を重ねた結果、ワック
スの付着量が、ワックスの温度条件によって決定される
という事実を見出し、本発明をなすに至った。[Means for Solving the Problems] In order to maintain the amount of wax adhering to an aluminum base plate within an appropriate range, the inventor of the present invention has conducted intensive research and found that the amount of wax adhering depends on the temperature conditions of the wax. The present invention was made based on the discovery of the fact that
すなわち、本発明は、アルミ素板の表面に、温度条件を
制御してワックスを塗布した後、深しぼり加工を行い、
アルミ缶を製造する方法に構成している。That is, the present invention applies wax to the surface of an aluminum base plate under controlled temperature conditions, and then performs a deep drawing process.
A method for manufacturing aluminum cans is provided.
本発明において使用することができるワックスとしては
、例えば、「ルブリカントに39J(商品名、デクスタ
ーミドランド株式会社製)を挙げることができる。As the wax that can be used in the present invention, for example, Lubricant 39J (trade name, manufactured by Dexter Midland Co., Ltd.) can be mentioned.
[発明の効果]
本発明は、アルミ素板の表面に、温度条件を制御してワ
ックスを塗布した後、深しぼり加工を行うアルミ缶の製
造方法に構成されているので、アルミ素板へのワックス
付着量を適正値に保つことができ、このため、製造され
たアルミ缶における不良品の発生率を低く押さえること
ができるという効果がある。[Effects of the Invention] The present invention is configured as an aluminum can manufacturing method in which wax is applied to the surface of an aluminum base plate under controlled temperature conditions, and then deep drawing processing is performed. The amount of wax deposited can be maintained at an appropriate value, which has the effect of keeping the incidence of defective products in manufactured aluminum cans low.
[実施例コ
(実施例)
使用するワックスを[ルブリカントに39J(商品名、
デクスターミドランド株式会社製)とし、ワックス温度
T(’C)と単位面積当たりのアルミ表面へのワックス
付着量との関係を調べてその結果を得た。[Example (Example)] The wax used was [lubricant 39J (trade name,
(manufactured by Dexter Midland Co., Ltd.), and the relationship between the wax temperature T ('C) and the amount of wax deposited on the aluminum surface per unit area was investigated to obtain the results.
ついで、ワックスの付着量と、アルミ缶における不良品
発生率との関係を調べ、ワックス付着量が一定の範囲に
ある場合に、不良品発生率が低くなるという結果を得た
。Next, we investigated the relationship between the amount of wax adhesion and the incidence of defective products in aluminum cans, and found that when the amount of wax adhesion was within a certain range, the incidence of defective products decreased.
そこで、適正なワックス付着量を得ることのできるワッ
クスの温度T(”C)を算出し、この温度範囲内にワッ
クスの温度を制御して、アルミ素板に塗布することによ
り、アルミ素板に対するワックス付着量を、適正値の範
囲内とすることができた。Therefore, by calculating the wax temperature T ("C) that can obtain the appropriate amount of wax adhesion, and controlling the wax temperature within this temperature range and applying it to the aluminum base plate, it is possible to The amount of wax attached was able to be within the appropriate range.
ついで、アルミ素板に対して深しぼり加工を行い、アル
ミ缶を製造したところ、不良品の発生率を低く押さえる
ことができた。Next, when aluminum cans were manufactured by deep drawing the aluminum blanks, it was possible to keep the incidence of defective products low.
(比較例)
温度条件を制御せずにアルミ素板にワックスを塗布した
ところ、上記実施例に比較して不良品の発生率が高くな
った。(Comparative Example) When wax was applied to an aluminum blank plate without controlling the temperature conditions, the incidence of defective products was higher than in the above example.
Claims (1)
温度条件を制御してワックスを塗布した後、深しぼり加
工を行うことを特徴とするアルミニウムまたはアルミニ
ウム合金製缶の製造方法。On the surface of aluminum or aluminum alloy base plate,
A method for producing an aluminum or aluminum alloy can, which comprises applying wax under controlled temperature conditions and then deep drawing.