JPH03173698A - Solid correction means - Google Patents
Solid correction meansInfo
- Publication number
- JPH03173698A JPH03173698A JP31322689A JP31322689A JPH03173698A JP H03173698 A JPH03173698 A JP H03173698A JP 31322689 A JP31322689 A JP 31322689A JP 31322689 A JP31322689 A JP 31322689A JP H03173698 A JPH03173698 A JP H03173698A
- Authority
- JP
- Japan
- Prior art keywords
- white pigment
- base material
- coating film
- copolymer
- hydrogenated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は、万年筆、水性サインペン、水性ボールペン等
の水性インキの筆跡や、油性ボールペン、油性サインペ
ン等の油性インキの筆跡、そしてタイプライタ−やプリ
ンターの印字、その他の印刷物の隠蔽修正を行なうため
の固形修正具に関するものである。Detailed Description of the Invention (Field of Industrial Application) The present invention is applicable to water-based ink handwriting such as fountain pens, water-based felt-tip pens, water-based ballpoint pens, oil-based ink handwriting such as oil-based ballpoint pens, oil-based felt-tip pens, etc., and typewriters, etc. This invention relates to a solid correction tool for concealing and correcting printer printing and other printed matter.
(従来の技術と発明が解決しようとする課題)従来、水
性インキや油性インキの筆跡、そして各種印刷による像
等を隠蔽修正するに際しては、白色顔料、バインダー樹
脂及びこの白色顔料を分散する分散媒としての揮発性溶
剤を主成分とする修正液を用いて、その修正箇所に塗布
し、この塗布膜が完全に乾燥してから塗膜上に再筆記等
を行なうという方法を採っていた。しかし乍ら、この様
な修正液を使用した場合には、修正液を塗布してから塗
膜が完全に乾燥するまでに十数秒から数十秒の待ち時間
を必要とするため再筆記に際しての迅速性に欠けるもの
であった。この待ち時間は、溶剤が蒸発するのに必要な
時間であるからこの待ち時間を短縮するためには揮発性
の高い溶剤を使えばよいと考えられるが、それでもこの
待ち時間を実質的に無くするためには、基本的に溶剤を
使用する以上不可能なことである。そこで、待ち時間を
皆無とするためには、溶剤を使用しなければよいことに
なるが、そうなると塗膜自体が固形である必要が生じ、
よってそのものは固体であり、且つ、その塗布可能なも
のには白色顔料が分散されているものが最低必要条件と
なる。かように固体であって、しかも塗布可能なものの
基材としては、一般に描画材としてのクレヨン等に使用
され1−
−
ているワックス類が挙げられるが、ワックス類に白色顔
料を単に分散させたものでは塗布後の塗膜が手指等の擦
過により容易に流れてしまい、従ってその本来の目的を
果たせないことになるばかりか、塗布部分近傍を汚損し
てしまうという別の問題を誘発した。(Prior Art and Problems to be Solved by the Invention) Conventionally, when concealing and correcting handwriting of water-based ink or oil-based ink, or images produced by various types of printing, white pigment, binder resin, and dispersion medium for dispersing this white pigment have been used. The method used was to apply a correction fluid containing a volatile solvent as a main component to the area to be corrected, and then write on the coating again after the coating film had completely dried. However, when using such a correction fluid, it is necessary to wait for several tens of seconds after applying the correction fluid until the paint film is completely dry, making it difficult to rewrite. It lacked promptness. This waiting time is the time required for the solvent to evaporate, so it may be possible to shorten this waiting time by using a highly volatile solvent, but it is still possible to virtually eliminate this waiting time. Basically, this is impossible as long as a solvent is used. Therefore, in order to eliminate waiting time, it would be better not to use a solvent, but then the coating film itself would need to be solid.
Therefore, the minimum requirement is that it is solid and that white pigment is dispersed in the material that can be applied. As a base material for such a solid yet coatable material, there are waxes that are generally used in crayons and the like as drawing materials. After application, the coating film is easily washed away by rubbing with fingers, etc., which not only fails to fulfill its original purpose, but also causes another problem of staining the area near the coating area.
(課題を解決するための手段)
本発明はこれらの状況に基づきなされたものであり、基
本的には固形の修正具が持つ長所を完全に生かし、且つ
、手指等の擦過により流れ難い塗膜を形成し得る基材を
得るべく鋭意研究を重ねたところ、常温で固体の、ポリ
ブチレン又はブチレン系共重合体、若しくは、水素添加
ポリイソプレン又は水素添加イソプレン系共重合体が基
材として最適であることを見い出し、遂に本発明を完成
したものである。(Means for Solving the Problems) The present invention has been made based on these circumstances, and basically takes full advantage of the advantages of solid correction tools, and creates a coating film that is difficult to wash off due to rubbing by fingers, etc. As a result of intensive research to obtain a base material capable of forming the This discovery led to the completion of the present invention.
即ち、本発明は、白色顔料と、基材である常温で固体の
、ポリブチレン又はブチレン系共重合体、若しくは、水
素添加ポリイソプレン又は水素添加イソプレン系共重合
体とから少なくともなる固形修正具を要旨とするもので
ある。That is, the gist of the present invention is a solid correction tool consisting of at least a white pigment and a base material of polybutylene or butylene-based copolymer, or hydrogenated polyisoprene or hydrogenated isoprene-based copolymer. That is.
以下、本発明を詳述する。The present invention will be explained in detail below.
本発明に使用する白色顔料は、筆跡や像を隠蔽するため
に用いるものであって、酸化亜鉛、硫酸バリウム、炭酸
カルシウム、酸化チタン等が挙げられるが、隠蔽力の点
から酸化チタンが最も好ましく用いられる。酸化チタン
は、ルチル型、アナターゼ型など各種利用でき、具体的
には、タイトーン5R−1、同R−’650、同R−3
L、同R−310、同A−110、同A−150、同R
−5N(以上、堺化学工業■製)、タイベークR−58
0、同R−550、同R−930、同A−100、同A
−220(以上、石原産業曲製)、クロノスKR−31
0、同KR−380、同KR−480、同KA−10、
同KA−20、同KA−30(以上、チタン工業■製)
等が挙げられる。The white pigment used in the present invention is used to hide handwriting and images, and examples thereof include zinc oxide, barium sulfate, calcium carbonate, titanium oxide, etc., but titanium oxide is most preferred from the viewpoint of hiding power. used. Titanium oxide can be used in various types such as rutile type and anatase type.
L, R-310, A-110, A-150, R
-5N (manufactured by Sakai Chemical Industry ■), Tybake R-58
0, R-550, R-930, A-100, A
-220 (all manufactured by Ishihara Sangyo Kyoku), Kronos KR-31
0, KR-380, KR-480, KA-10,
KA-20, KA-30 (manufactured by Titanium Kogyo ■)
etc.
これらの白色顔料は、単独でも2種以上適宜混合しても
使用でき、その使用量は、白色顔料の種類によっても事
なるが、筆跡等に対する隠蔽力を考慮すると、固形修正
具全量に対し40重量%以3−
上90重量%以下が望ましい。これは白色顔料の使用割
合が40重装置に満たないと筆跡や像に対する隠蔽力が
不十分となり文字等が透けて見えることがあり、また、
90重量%を越えると塗膜形成能が低下する場合が有る
ためである。These white pigments can be used alone or in a mixture of two or more, and the amount used varies depending on the type of white pigment, but considering the hiding power for handwriting etc., 40% of the total amount of the solid correction tool is used. It is desirable that the content is between 3% and 90% by weight. This is because if the proportion of white pigment used is less than 40 parts, the concealing power for handwriting and images will be insufficient, and letters etc. may be visible through them.
This is because if the amount exceeds 90% by weight, the ability to form a coating may decrease.
本発明において使用する常温で固体の、ポリブチレン又
はブチレン系共重合体、若しくは、水素添加ポリイソプ
レン又は水素添加イソプレン系共重合体は、前述した白
色顔料の分散媒であり、且つ、塗布可能な基材として使
用するものであり、ポリブチレンとしては、テトラック
ス3T、同4T、同5T、同6T(以上、日本石油化学
■製)。The polybutylene or butylene copolymer, hydrogenated polyisoprene or hydrogenated isoprene copolymer, which is solid at room temperature, used in the present invention is a dispersion medium for the above-mentioned white pigment, and has a coatable group. Tetrax 3T, Tetrax 4T, Tetrax 5T, Tetrax 6T (manufactured by Nippon Petrochemical Company) are used as polybutylene.
ビスタネックスLM−MS、同LM−MH(以上、エク
ソン化学■製)が挙げられ、ブチレン系共重合体として
は、スチレンとの共重合物としてループリシール(日本
ループリゾール工業■製)や、イソプレンとの共重合物
としてエッソブチルゴム(エクソン化学■製)があり、
水素添加ポリイソプレンとしてはシェルビス200、同
250(以上、シェル化学■製)が挙げられ、水素添加
イソ−
プレン系共重合体としては、スチレンとの共重合物とし
てシェルビス50(シェル化学■製)がある。Examples of butylene-based copolymers include Vistanex LM-MS and LM-MH (manufactured by Exxon Chemical Co., Ltd.), and examples of butylene-based copolymers include Lupuriseal (manufactured by Japan Lupurizol Industries Co., Ltd.) as a copolymer with styrene, and isoprene There is essobutyl rubber (manufactured by Exxon Chemical Co., Ltd.) as a copolymer with
Examples of hydrogenated polyisoprene include Shell Bis 200 and Shell Bis 250 (manufactured by Shell Chemical ■), and hydrogenated isoprene copolymers include Shell Bis 50 (manufactured by Shell Chemical ■) as a copolymer with styrene. There is.
上記高分子化合物は単独でも2種以上適宜混合しても使
用でき、その使用量は固形修正具全量に対して10〜6
0重量%が好ましい。The above-mentioned polymer compounds can be used alone or in combination of two or more, and the amount used is 10 to 6
0% by weight is preferred.
尚、本発明においては、上記各成分以外に充填材、有色
顔料などの着色材、液状ゴム、鉱物油、油脂や、蜜ろう
、鯨ろう、虫白ろう等の動物系ワックス、キャンデリラ
ワックス、カルナバワックス、木ろう等の植物系ワック
ス、モンタンワックス、オシケライト等の鉱物系ワック
ス、パラフィンワックス、マイクロクリスタリンワック
ス等の石油系ワックスといった天然ワックスや、フィッ
シャートロプシュワックス、低分子量ポリエチレン及び
これらの誘導体、モンタンワックス、パラフィンワック
ス、マイクロクリスタリンワックスのおのおのの誘導体
、セチルアルコール、ステアリン酸、ポリエチレングリ
コールステアレート、カスターワックス等の合成ワック
スや、水性インキでの再筆記迄の時間短縮剤として、ス
ターチ、ポリアクリレート、アクリル酸・ビニルアルコ
ール共重合体、ポリアクリル酸ナトリウム等の高吸水性
高分子物質や、ガーガム、ローカストビーンガム、フィ
ンシードガム、カラギーナン、アルギン酸、アラビアガ
ム、ゼラチン、ポリビニルピロリドンなどの増粘ゲル化
高分子物質と併用し得ること勿論である。In addition, in the present invention, in addition to the above-mentioned components, fillers, colorants such as colored pigments, liquid rubber, mineral oil, fats and oils, animal waxes such as beeswax, spermaceti wax, and insect white wax, candelilla wax, Natural waxes such as vegetable waxes such as carnauba wax and wood wax, mineral waxes such as montan wax and osikelite, petroleum waxes such as paraffin wax and microcrystalline wax, Fischer-Tropsch wax, low molecular weight polyethylene and their derivatives, and montan wax. Derivatives of wax, paraffin wax, microcrystalline wax, synthetic waxes such as cetyl alcohol, stearic acid, polyethylene glycol stearate, castor wax, starch, polyacrylate, Thickening and gelling of super absorbent polymer substances such as acrylic acid/vinyl alcohol copolymer, sodium polyacrylate, gar gum, locust bean gum, fin seed gum, carrageenan, alginic acid, gum arabic, gelatin, polyvinylpyrrolidone, etc. Of course, it can be used in combination with polymeric substances.
本固形修正具を得るには、上記各成分を混合し。To obtain the present solid correction tool, the above components are mixed.
従来公知の二本ロールミル等の分散機にて混合分散を行
ない、型に流し込んで冷却し、成形する等の方法によっ
て得ることができる。It can be obtained by a method such as mixing and dispersing using a conventionally known dispersing machine such as a two-roll mill, pouring into a mold, cooling, and molding.
(作 用)
本発明における基材である、ポリブチレン又はブチレン
系共重合体、若しくは、水素添加ポリイソプレン又は水
素添加イソプレン系共重合体は、それ自体は自己凝集力
が強く、塗布できにくいが。(Function) The base material in the present invention, polybutylene or butylene copolymer, or hydrogenated polyisoprene or hydrogenated isoprene copolymer, itself has a strong self-cohesive force and is difficult to coat.
多量の白色顔料と混練することによって、崩壊性を有す
るようになり、塗布が可能になる6従って。By kneading it with a large amount of white pigment, it becomes disintegrating and can be coated6.
固形修正具の基材としてこれを用いた場合、筆跡や像等
の隠蔽修正具として塗布でき、またその塗膜を擦過して
も塗膜の流れは極力防止される。When this is used as a base material for a solid correction tool, it can be applied as a correction tool for concealing handwriting, images, etc., and even if the coating film is rubbed, it is prevented from running as much as possible.
(実施例) 以下、本発明の詳細な説明する。(Example) The present invention will be explained in detail below.
尖差主上
テトラックス 3T 32部(ポリブ
チレン、日本石油化学曲製)
酸化チタン 60部(クロノ
スKR−380、チタン工業■製)液状ポリブテン
2部(日本石油化学■製)
酸化珪素 6部(ミズカ
シルp、−810、水沢化学工業■製)上記成分を加熱
二本ロールで混合分散を行ない、型に流し込んで冷却し
固形修正具を得た。Point difference main Tetrax 3T 32 parts (polybutylene, manufactured by Nippon Petrochemical Co., Ltd.) Titanium oxide 60 parts (Kronos KR-380, manufactured by Titan Kogyo ■) Liquid polybutene
2 parts (made by Nippon Petrochemical Co., Ltd.) Silicon oxide 6 parts (Mizukashiru P, -810, made by Mizusawa Chemical Co., Ltd.) The above ingredients were mixed and dispersed using two heated rolls, poured into a mold, and cooled to obtain a solid correction tool. Ta.
災凰枇え
シェルビス 50 25部(スチレン
−水素添加イソプレン共重合物、シェル化学曲製)
酸化チタン 50部7
(タイトーンR−650、堺化学工業■製)130°F
パラフインワツクス 10部重質炭酸カルシウム
15部上記成分を実施例1と同様に
なして固形修正具を得た。Shell Bis 50 25 parts (styrene-hydrogenated isoprene copolymer, manufactured by Shell Kagaku Kyoku) Titanium oxide 50 parts 7 (Titone R-650, manufactured by Sakai Chemical Industry ■) 130°F
Parafine wax 10 parts Heavy calcium carbonate 15 parts A solid correction tool was obtained using the above ingredients in the same manner as in Example 1.
笑嵐勇A
シェルビス 200 15部(水素添
加ポリイソプレン、シェル化学■5製)酸化チタン
82部(タイベークR−580
、石原産業■製)白色ワセリン
3部上記成分を実施例1と同様になして固形修正具を
得た。Sho Arashi Isamu A Shell Bis 200 15 parts (hydrogenated polyisoprene, manufactured by Shell Chemical ■5) Titanium oxide
82 parts (Tie Bake R-580
, manufactured by Ishihara Sangyo ■) White petrolatum
3 parts A solid correction tool was obtained using the above ingredients in the same manner as in Example 1.
失胤虹久
シェルビス 50 25部酸化チタン
50部(タイトーンR−6
50、堺化学工業■製)130’Fパラフインワツクス
10部重質炭酸カルシウム
14部サンウェットIM−1000MPS 1部
(高吸水性高分子物質、三洋化成工業■製)上記成分を
実施例1と同様になして固形修正具を得た。Shitane Nijiku Shellbis 50 25 parts Titanium oxide 50 parts (Titone R-6
50, manufactured by Sakai Chemical Industry ■) 130'F paraffin wax 10 parts heavy calcium carbonate
14 parts Sunwet IM-1000MPS 1 part (super absorbent polymer material, manufactured by Sanyo Chemical Industries, Ltd.) A solid correction tool was obtained using the above ingredients in the same manner as in Example 1.
比較例1
130°Fパラフインワツクス 28部酸化チタ
ン 60部(タイト−ンR−
650、堺化学工業■製)白色ワセリン
6部酸化珪素
6部上記成分を実施例1と同様になして固形修正具
を得た。Comparative Example 1 130°F paraffin wax 28 parts titanium oxide 60 parts (Titon R-
650, manufactured by Sakai Chemical Industry ■) White petrolatum
6-part silicon oxide
6 parts A solid correction tool was obtained using the above ingredients in the same manner as in Example 1.
[発明の効果]
上記実施例1〜4及び比較例1で得られた固形修正具を
用いて、紙面に塗布し、これにより形成された塗膜を指
で強く擦ったところ、比較例のものは塗膜が流れてしま
いその塗膜も塗布部以外の近傍部まで拡がってしまった
が、実施例のものはこれに反して塗膜の流れが発生せず
、塗布部近傍を汚損することもみられなかった。[Effects of the Invention] When the solid correction tools obtained in Examples 1 to 4 and Comparative Example 1 were applied to a paper surface and the resulting coating film was strongly rubbed with a finger, it was found that the solid correction tools obtained in Examples 1 to 4 and Comparative Example 1 were In the case of the example, the paint film ran and spread to areas other than the applied area, but in the case of the example, the paint film did not flow, and there was no possibility of staining the area near the applied area. I couldn't.
この様に本発明による固形修正具は、固体としての修正
具の持つ長所を生かし、
且つ、
塗布後の
諸性能も格段価れたものである。As described above, the solid correction tool according to the present invention takes advantage of the advantages of a solid correction tool, and also has significantly improved performance after application.
Claims (1)
又はブチレン系共重合体、若しくは、水素添加ポリイソ
プレン又は水素添加イソプレン系共重合体とから少なく
ともなる固形修正具。A solid correction tool comprising at least a white pigment and a base material of polybutylene or a butylene-based copolymer, or a hydrogenated polyisoprene or a hydrogenated isoprene-based copolymer.