Floor material for golf training range

Info

Publication number
JPH03170177A
JPH03170177A JP31218289A JP31218289A JPH03170177A JP H03170177 A JPH03170177 A JP H03170177A JP 31218289 A JP31218289 A JP 31218289A JP 31218289 A JP31218289 A JP 31218289A JP H03170177 A JPH03170177 A JP H03170177A
Authority
JP
Japan
Prior art keywords
base layer
density
surface material
hardness
elasticity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP31218289A
Other languages
Japanese (ja)
Inventor
Nobuyuki Kataoka
信幸 片岡
Tadatoshi Yamada
山田 忠利
Seisuke Tomita
誠介 冨田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bridgestone Corp
Original Assignee
Bridgestone Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bridgestone Corp filed Critical Bridgestone Corp
Priority to JP31218289A priority Critical patent/JPH03170177A/en
Publication of JPH03170177A publication Critical patent/JPH03170177A/en
Pending legal-status Critical Current

Abstract

PURPOSE:To obtain the elasticity approximate to the elasticity of natural lawn simply by laying the floor material on concrete by laminating a surface material on a base layer consisting of a foamed material having specific repulsive elasticity, density and hardness. CONSTITUTION:The foamed body to constitute the base layer to be laminated with the surface material thereon is made of the foamed material having <=25% repulsive elasticity at 20 deg.C, 0.1 to 0.5g/cm<3> density and <=50 deg. hardness by SRIS. This material is exemplified by foamed rubber or urethane sponge, etc. Sufficient impact absorbing performance is not obtainable if the repulsive elasticity at 20 deg.C exceeds 25%. The weight increases if the density exceeds 0.5g/cm<3>. The impact absorbing performance and strength are insufficient if the density is below 0.1g/cm<3>. The impact absorbing performance is insufficient if the hardness by the SRIS exceeds 50 deg.. The thickness of the base layer is preferably >=2mm and above all, 10 to 20mm. A non-woven fabric, etc., are used in addition to the surface material of the artificial lawn, etc., as the surface material. The surface material may be simply superposed on the base layer or may be adhered by an adhesive agent or pinned thereto.

Description

【発明の詳細な説明】 [産業上の利用分野] 本発明はゴルフ練習場用床材料に係り、特にゴルフ練習
場のフエアーウェイや打席に敷いて用いるに好通な、ゴ
ルフボールのリバウンドが改良されたゴルフ練習場用床
材料に関するものである。
[Detailed Description of the Invention] [Industrial Application Field] The present invention relates to a flooring material for a golf driving range, which is particularly suitable for use as a flooring material for the fairway or batting area of a golf driving range, and has improved rebound of golf balls. The present invention relates to flooring materials for golf driving ranges.

[従来の技術] 従来、殆どのゴルフ練習場では天然の芝は用いられてお
らず、手入れが簡単で・耐久性に優れた人工芝、ニード
ルバンチ等の人工床材が表面材として用いられている。
[Conventional technology] Traditionally, most golf driving ranges do not use natural grass, but artificial flooring materials such as artificial grass and needle bunch, which are easy to maintain and have excellent durability, are used as surface materials. There is.

これらの表面材は、打席まわり或いはフェア一ウエイや
バッティンググリーンのコンクリート面上に、直接敷設
されている。
These surface materials are laid directly around the batting area or on the concrete surface of the fairway or batting green.

[発明が解決しようとする課題] コンクリート上に人工芝やニードルパンチ等の表面材を
直接敷設したものでは、打撃されたゴルフボールが衝突
した際、弾みが強すぎるため、次のような欠点があった
[Problems to be solved by the invention] When a surface material such as artificial turf or needle punch is laid directly on concrete, when a golf ball is hit, the momentum is too strong, resulting in the following drawbacks: there were.

■ 狭い練習場内では跳ね返ったボールがフレーヤーに
当たるなどの危険がある。
■ There is a risk of a ball bouncing off and hitting a player in the small practice area.

■ ボールの弾み方が天然芝とは大きく異なるため、プ
レーヤーにとっては実際のゴルフ場における感覚と異和
感がある。
■ The way the ball bounces is very different from natural grass, so it feels different for players than on an actual golf course.

■ ボールが強く衝突するため、ボールの損傷が激しい
。即ち、表面材の色がボールに移る、或いは物理的に損
傷を受けるなどして、ボールが早期に劣化する。
■ The ball collides strongly, causing severe damage to the ball. That is, the color of the surface material transfers to the ball, or the ball is physically damaged, resulting in premature deterioration of the ball.

本発明は上記従来の問題点を解決し、天然芝に近い弾性
を有するゴルフ練習場用床材料を提供することを目的と
する。
An object of the present invention is to solve the above-mentioned conventional problems and to provide a floor material for a golf driving range that has elasticity close to that of natural grass.

[課題を解決するための手段] 本発明のゴルフ練習場用床材料は、20℃における反発
弾性が25%以下、密度が0.1〜0.5g/cm’で
、SRI Sによる硬度が506以下の発泡体の上に表
面材が積層されてなることを特徴とする。
[Means for Solving the Problems] The golf driving range flooring material of the present invention has a rebound resilience of 25% or less at 20°C, a density of 0.1 to 0.5 g/cm', and a hardness of 506 by SRI S. It is characterized in that a surface material is laminated on the following foam.

以下に本発明を詳細に説明する。The present invention will be explained in detail below.

本発明において、その上に表面材をfJt層する基層と
なる発泡体は、20℃における反発弾性が25%以下、
好ましくは15%以下、密度がO、1 〜0.5g/c
IT1″で、SRI Sによる硬度が50゜以下、好ま
しくは30”以下のものである。このような発泡体とし
ては、発泡ゴム又はウレタンスポンジ等が挙げられ、例
えば、■ スチレン含有量が40〜75重量%であるス
チレンープタジエン共重合体もしくはスチレンーブタジ
エン共重合体と、全体のO〜40重量%の他のゴム戒分
とからなるボリマー100重量部、 ■ 30〜300重量部の充填剤、 ■ 5〜100重量部の可塑剤、 ■ 0.5〜30重量部の発泡剤、 からなる混合物に加硫剤、加硫促進剤を加え、加硫発泡
して得られる低レジリエンスゴム発泡体が好ましい。
In the present invention, the foam serving as the base layer on which the surface material is layered has a rebound resilience of 25% or less at 20°C;
Preferably 15% or less, density O, 1 to 0.5 g/c
IT1'' and SRIS hardness of 50° or less, preferably 30'' or less. Examples of such foams include foamed rubber and urethane sponges. 100 parts by weight of a polymer consisting of O to 40% by weight of other rubber components; ■ 30 to 300 parts by weight of filler; ■ 5 to 100 parts by weight of plasticizer; ■ 0.5 to 30 parts by weight of blowing agent. A low resilience rubber foam obtained by adding a vulcanizing agent and a vulcanization accelerator to a mixture consisting of , and vulcanizing and foaming the mixture is preferred.

このような発泡体の20℃での反発弾性が25%を超え
ると得られる床材料に十分な衝撃吸収性能が得られず、
また、密度が0.5g/cm3を超えると得られる床材
料の重量が重くなり、密度0.1g/crn’未満では
衝撃吸収性能及び強度が不十分となる。SRI Sによ
る硬度が50゛を超えると衝撃吸収性能が不足する。な
お、SRI Sによる硬度とは、アスカーC型硬度計(
日本ゴム協会規格0101)による硬度測定により求め
られた硬度である。
If the impact resilience of such a foam at 20°C exceeds 25%, the resulting floor material will not have sufficient impact absorption performance.
Further, if the density exceeds 0.5 g/cm3, the weight of the resulting floor material becomes heavy, and if the density is less than 0.1 g/crn', the impact absorption performance and strength will be insufficient. If the SRIS hardness exceeds 50°, the shock absorption performance will be insufficient. In addition, the hardness by SRI S refers to the Asker C type hardness tester (
This is the hardness determined by hardness measurement according to Japan Rubber Association Standard 0101).

本発明において、このような発泡体で構成される基層の
厚さは、2mm以上、とりわけ10〜20mmであるこ
とが好ましい。
In the present invention, the thickness of the base layer made of such a foam is preferably 2 mm or more, particularly 10 to 20 mm.

このような発泡体よりなる基層上に積層する表面材とし
ては、通常、ゴルフ練習場等で使用されている人工芝、
ニードルパンチ等の表面材の他、不織布、布、ビニール
シ一ト等を用いることができる。これらの表面材は、上
記発泡体よりなる基層上に単に重ねただけでも良く、ま
た、適当な接着剤により接着したり、ピン、釘などのよ
うな固定具で接合して一体化しても良い。
The surface material to be laminated on the base layer made of foam is usually artificial turf, which is used in golf driving ranges, etc.
In addition to surface materials such as needle punches, nonwoven fabrics, cloth, vinyl sheets, etc. can be used. These surface materials may be simply layered on the base layer made of the above-mentioned foam, or may be bonded with a suitable adhesive or joined with fixing devices such as pins, nails, etc. to be integrated. .

本発明のゴルフ練習場用床材料は、常法に従って、コン
クリート又は土等の上に敷設するのみで良く、施工性に
も極めて優れる。
The flooring material for a golf driving range of the present invention can be simply laid on concrete, soil, etc. according to a conventional method, and has excellent workability.

[作用コ 本発明のゴルフ練習場用床材料は、特定の反発弾性、密
度及び硬度を有する発泡体よりなる基層の上に、表面材
が積層されたものであるため、本発明のゴルフ練習場用
床材料をコンクリート上に敷設するのみで、この発泡体
の基層により天然芝に近い適度な弾性、即ちボールのリ
バウンドが得られる。
[Function] The golf driving range flooring material of the present invention has a surface material laminated on a base layer made of a foam having a specific impact resilience, density, and hardness. By simply laying the flooring material on concrete, the foam base layer provides an appropriate level of elasticity similar to that of natural grass, ie, ball rebound.

[実施例] 以下に実施例及び比較例を挙げて、本発明をより具体的
に説明する。
[Example] The present invention will be described in more detail by giving Examples and Comparative Examples below.

実施例1.2 第1表に示す物性のスチレンーブタジエン共重合体の発
泡体よりなる基層(厚さ15mm)の上に、表面材とし
て人工芝(厚さ4mm)を接着剤で接着して本発明のゴ
ルフ練習場用床材料を製造した。
Example 1.2 Artificial turf (4 mm thick) was bonded as a surface material onto a base layer (15 mm thick) made of styrene-butadiene copolymer foam having the physical properties shown in Table 1. A golf driving range flooring material of the present invention was manufactured.

このゴルフ練習場用床材料をコンクリート上に敷設して
、ゴルフボールを21mの高さから自然落下させて跳ね
返り高さを測定した。結果を第1表に示す。
This floor material for a golf driving range was laid on concrete, and a golf ball was allowed to fall naturally from a height of 21 m, and the height of rebound was measured. The results are shown in Table 1.

比較例1 発泡体の基層を用いずに、コンクリート上は直接人工芝
を敷設して実施例1と同様にしてゴルフボールの跳ね返
り高さを測定した。結果を第1表に示す。
Comparative Example 1 The bounce height of a golf ball was measured in the same manner as in Example 1 by laying artificial turf directly on the concrete without using a foam base layer. The results are shown in Table 1.

第1表より本発明のゴルフ練習場用床材料によれば、適
度なリバウンドが得られることが明らかである。
From Table 1, it is clear that the golf driving range flooring material of the present invention can provide an appropriate rebound.

第 1 表 *2:日本ゴム協会規格0101 [発明の効果] 以上詳述した通り、本発明のゴルフ練習場用床材料は、
適度な弾性を有し、天然芝に近いボールのリバウンド特
性を有するため、 ■ 打撃されたゴルフボールが過度に弾み、プレーヤー
や床、壁等に当たるなどの危険が防止され、安全に練習
をすることができる。
Table 1 *2: Japan Rubber Association Standard 0101 [Effects of the invention] As detailed above, the golf driving range flooring material of the present invention:
It has moderate elasticity and ball rebound characteristics similar to natural grass, so you can practice safely by preventing the risk of a golf ball hitting players, floors, walls, etc. due to excessive bounce. Can be done.

■ 天然芝と同程度の感触が得られ、練習効果が向上す
る。
■ Provides a feel similar to that of natural grass, improving practice effectiveness.

■ ボールの損傷が防止される。また、床材側の損傷も
防止される。
■ Damage to the ball is prevented. Moreover, damage to the flooring material side is also prevented.

等の優れた効果.が得られる。しかも、本発明のゴルフ
練習場用床材料は、単にコンクリートや土の上に敷設す
るのみで良く、その施工性にも優れる。
Excellent effects such as is obtained. Moreover, the golf driving range flooring material of the present invention can be simply laid on concrete or soil, and has excellent workability.

Claims (1)

【特許請求の範囲】[Claims] (1)20℃における反発弾性が25%以下、密度が0
.1〜0.5g/cm^3で、SRISによる硬度が5
0゜以下の発泡体の上に表面材が積層されてなることを
特徴とするゴルフ練習場用床材料。
(1) Impact resilience at 20°C is 25% or less, density is 0
.. 1~0.5g/cm^3, hardness by SRIS is 5
A flooring material for a golf driving range, characterized in that a surface material is laminated on a foam having an angle of 0° or less.
JP31218289A 1989-11-30 1989-11-30 Floor material for golf training range Pending JPH03170177A (en)