JPH02155998A - Detergent composition for scouring pad - Google Patents
Detergent composition for scouring padInfo
- Publication number
- JPH02155998A JPH02155998A JP30959788A JP30959788A JPH02155998A JP H02155998 A JPH02155998 A JP H02155998A JP 30959788 A JP30959788 A JP 30959788A JP 30959788 A JP30959788 A JP 30959788A JP H02155998 A JPH02155998 A JP H02155998A
- Authority
- JP
- Japan
- Prior art keywords
- water
- composition
- scoring
- weight
- polyethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、優れたfIC#力、研磨力’に41、被洗浄
面t−傷付けることがなく、長く繰シ返し使用すること
ができ、便用後の防錆効果に優れ、かつ製造時に乾脈工
程を必要としないスコアリング、Qラドを得るための洗
浄剤組成物に関する。[Detailed Description of the Invention] [Industrial Application Field] The present invention has excellent fIC# power, polishing power'41, and can be used repeatedly for a long time without damaging the surface to be cleaned. The present invention relates to a detergent composition for obtaining scoring and Qrad, which has an excellent antirust effect after toilet use and does not require a dry pulse process during production.
家庭内の台所の汚れ、例えば鍋、アライノ9ン等に付着
した煮ごぼれ、焦げつき汚れ、焼き付汚れ、ガス277
周辺の現き付き汚A。Dirt in the kitchen at home, such as boiled dirt, burnt dirt, baked-on dirt, gas 277 on pots, etc.
Surrounding stains A.
換気扇のベタ付き油汚れ、タイル目地の汚れなどは、ど
この家庭にも存在し目立つものであるが、なかなか落と
しにくい汚れでるる。Sticky oil stains on ventilation fans and stains on tile joints are noticeable in every home, but they are difficult to remove.
これらの汚れの洗浄手段として、スコアリングツ9ツド
の使用が一般に行なわれている。As a means of cleaning these stains, scoring tools are generally used.
このスコアリングツ9ツドは、一般に金属タワシなどに
洗浄剤成分として石wMを付層させてなるものでるる。This scoring tool is generally made by adding a layer of stone as a cleaning agent component to a metal scrubber or the like.
スコアリングツリッドの洗Pp剤成分として五感が使用
されてきた背景には、安価でめ9、便用時の泡立ちも良
く、金属タワシなどに付層させる前に石鹸水溶液(高温
溶解)にてハンドリングし、水分を蒸散させること(乾
燥工程)により同化し、型部れせず、貯蔵安定性が良い
という利点がめったからでるる。The reason behind the use of Gosense as a detergent component in ScoringTrid is that it is inexpensive, has good lathering properties during toilet use, and can be used in a soap solution (dissolved at high temperature) before being applied to a metal scrubbing brush. It rarely has the advantage of being assimilated by handling and evaporating moisture (drying process), not causing mold deformation, and having good storage stability.
しかし従来のスコアリング、eラドにおいては、洗浄力
が充分でない、製造時の乾燥工程に多大な労力1時間を
安し1作業環境が悪い等の問題点かめり、さらに洗浄剤
として石鑵を付着させただけでは、すぐに洗浄剤が溶は
出してしまい、艮〈繰シ返しf5ことが困難でるるとい
う問題点かろシ、これを解決するための洗浄剤組成物が
望まれていた。However, conventional scoring and e-rad systems have many problems, such as insufficient cleaning power, a large amount of labor required for the drying process during manufacturing, and a poor work environment. If the cleaning agent is simply attached, the cleaning agent immediately dissolves, making it difficult to repeat the process.There has been a need for a cleaning agent composition that can solve this problem.
そこで1本発明者らは上記課題を解決すべく種々検討し
た結果、洗浄剤成分に一定の分子tt有する?リエチレ
ングリコール及び増粘剤を配合した洗浄剤組成物を用い
れば、洗浄力、研磨力が同上し、被vc浄面を傷付ける
ことがなく、長く繰り返し使用することがでキルスコア
リング/eツド會得ることができること、並びにその製
造過程において乾燥工程を必貴としないことを見出し本
発明を完成した。Therefore, the present inventors conducted various studies to solve the above problem, and found that the detergent components have a certain molecule tt? If a cleaning composition containing lyethylene glycol and a thickener is used, the cleaning power and polishing power will be the same as above, and it will not damage the surface to be cleaned and can be used repeatedly for a long time, resulting in kill scoring/e-tsudo meetings. The present invention was completed based on the discovery that a drying step is not necessary in the manufacturing process.
すなわち、本発明は次の成分(8)〜(ロ)、(5)平
均分子量が4000〜13,000の?リエチレングリ
コール 10〜90重量%(均 増粘剤
0.1−15[jlチG) 界面活性剤
1〜50を量チ0 水
0〜5重量−を含有することを特徴とするスコアリング
、eラド用洗浄剤組成切を提供するものでるる。That is, the present invention uses the following components (8) to (b) and (5) having an average molecular weight of 4,000 to 13,000. Liethylene glycol 10-90% by weight (uniform thickener)
0.1-15 [jlchiG) Surfactant
Measure 1-50 water
The present invention provides a cleaning agent composition for scoring and e-rad, characterized by containing 0 to 5% by weight.
本発明において用いられる(5)成分の?リエチレング
リコールの平均分子量は2.ooo〜1a、ooo、好
ましくはa、ooo〜へ000でろる。Component (5) used in the present invention? The average molecular weight of lyethylene glycol is 2. ooo to 1a, ooo, preferably a, ooo to 000.
配合量は10〜90重量%(以下、単にチで示す)、好
ましくは20〜80チである。The blending amount is 10 to 90% by weight (hereinafter simply referred to as ``H''), preferably 20 to 80% by weight.
(B) g分の増粘剤としては、合成高分子、天然尚分
子、粘土鉱物%鍍化エチレン付711Im非イオン性界
面活性剤等が使用される。(B) As the thickener for g, synthetic polymers, natural natural molecules, clay minerals, 711Im nonionic surfactants with % blackened ethylene, etc. are used.
合成高分子としては1例えばylr 17アクリルrI
R1,&リマレイン戚項、アクリル戚−マレイン戚共重
合体の臘、インブチレン−マレイン酸共重合体の塩、ス
チレン−マレイン酸共重合体の塩、アリルアルコール−
マレイン酸共重合体の塩、ゾインプチレンーマレイン酸
共重合体の塩、部分架m型f’l)アクリル酸又はその
項、ポリビニルアルコール、破りビニルピロリドン等が
挙けられる。Synthetic polymers include 1, for example, ylr, 17 acrylic rI
R1, & limalein, acrylic-maleic copolymer salt, imbutylene-maleic acid copolymer salt, styrene-maleic acid copolymer salt, allyl alcohol.
Examples include salts of maleic acid copolymers, salts of zoinbutylene-maleic acid copolymers, partially cross-linked m-type f'l) acrylic acid, polyvinyl alcohol, broken vinyl pyrrolidone, and the like.
天然高分子としては1例えばキサンタンガム、クルコマ
ンナン、クインスシードガム、ローカストピーンガム、
アラビアガム、アルギン酸ソーダ、カッノ9−カラギー
ナン、2ムダ−カラギーナン、アイオターカラギーナン
。Examples of natural polymers include xanthan gum, curcomannan, quince seed gum, locust pea gum,
Gum arabic, sodium alginate, 9-carrageenan, 2-carrageenan, iotar carrageenan.
ペクチン、ヒアルロン酸、コンドロイチン4硫酸、コン
ドロイチン8釦凱デルマタン謔酸、コンドロイチン4.
8ゾ硫酸、ゲルマタン4.8ゾ硫酸、ケラタン懺酸及び
へ/eシラン酸などの天然多srs;メチルセルロース
。Pectin, hyaluronic acid, chondroitin 4 sulfate, chondroitin 8 kankai dermatan choic acid, chondroitin 4.
Natural polysrs such as 8zosulfuric acid, germatane 4.8zosulfuric acid, keratan phosphoric acid and he/e silane acid; methylcellulose.
エチルセルロース、カルボキシメチルセルロースナトリ
ウム、ヒドロキシエチルセルロース、ヒドロキシグロビ
ルセルロースなどのセルロース酵導体等が挙げられる。Examples include cellulose fermentation conductors such as ethyl cellulose, sodium carboxymethyl cellulose, hydroxyethyl cellulose, and hydroxyglobil cellulose.
粘土鉱物としては、スメクタイト又tI′i複鎖W遺倉
粘土鉱物等を主成分とする粘土鉱91J類が好ましく、
具体的には、例えばモンモリロナイト、ノントロナイト
、ノq−ミギュライト、アタノ9ルゾヤイト、セピオラ
イト4を挙げることができる。As the clay mineral, clay minerals 91J containing smectite or tI'i double-chain W Ikura clay mineral as a main component are preferred;
Specifically, examples thereof include montmorillonite, nontronite, noq-migulite, atano9 ruzoite, and sepiolite 4.
酸化エチレン付加盤の非イオン性界面活性剤としては、
r1i化エチレン付加モル畝が50〜200のモノアル
キル(Csz〜go)frしくはシアルキル(Csx〜
10 )エーテル又ハエステル型のものが挙げられる。As a nonionic surfactant for ethylene oxide addition board,
Monoalkyl (Csz~go) fr or sialkyl (Csx~
10) Examples include ether or haester types.
(B)成分の増粘剤は(5)成分の/リエチレングリコ
ールの共存下で、吸水時にグル化能を高め、金属タワシ
等への洗浄成分の付層性を高めることができ、この結果
洗浄成分の流出が防止でき、Iaシ返しの使用が可能と
なる。この効果を発揮するため、φ)成分は0.1〜1
5チ、特に0.5〜10%配合することが好ましい。In the coexistence of component (5) /liethylene glycol, the thickener component (B) can enhance the gluing ability when absorbing water and increase the layering of the cleaning component on metal scrubbing brushes, etc., resulting in cleaning. It is possible to prevent the components from flowing out, and it is possible to use the Ia filter. In order to exhibit this effect, the φ) component is 0.1 to 1
It is preferable to add 5%, especially 0.5 to 10%.
本発明において用いられるC)成分の界面活性剤として
は鴎イオン性界面活性剤、非イオン性界面活性剤、mイ
オン性界面活性剤、両性界面活性剤が使用されるが、t
#に陰イオン性界面活性剤または非イオン性界面活性剤
が好ましい。As the surfactant for component C) used in the present invention, there are used ionic surfactants, nonionic surfactants, ionic surfactants, and amphoteric surfactants.
# is preferably an anionic surfactant or a nonionic surfactant.
本発明において使用される陰イオン性界面活性剤として
は1例えば炭素数8〜22の脂肪酸塩、炭素数8〜22
のアルキル健酸塩、アルキル基の炭素数が8〜16のア
ルキルベンゼンスルホン11!@、アルキル基の炭素数
がlθ〜20でろシ酸化エチレン付加モル数が1−10
でめる?リオキシエチレンアルキルエーテル硫酸@1ア
ルキル基の炭素数が8〜12で酸化エチレン付加モル数
が1−10の?リオキシエチレンアルキルフェノールW
*エステル塩、炭素数8〜18のα−オレフィンをスル
ホ/化して得られるα−オレフィンスルホン酸塩、炭素
数8〜200792フインから得られるアルカンスルホ
ン#R塩などが挙げられる。これらのうち、酸化エチレ
ンを付加したもの及びは酸塩系の活性剤は、錆に対する
影響が認められる場合がろるので、その場合は防錆剤を
併用するのが好ましい。Examples of the anionic surfactants used in the present invention include 1, for example, fatty acid salts having 8 to 22 carbon atoms;
Alkyl benzene sulfone with an alkyl group of 8 to 16 carbon atoms 11! @, the number of carbon atoms in the alkyl group is lθ~20 and the number of moles of ethylene oxide added is 1-10
Demeru? Lyoxyethylene alkyl ether sulfate @1 The number of carbon atoms in the alkyl group is 8 to 12 and the number of moles of ethylene oxide added is 1 to 10? Lyoxyethylene alkylphenol W
*Ester salts, α-olefin sulfonates obtained by sulfonating α-olefins having 8 to 18 carbon atoms, alkanesulfone #R salts obtained from fins having 8 to 200,792 carbon atoms, and the like. Among these, those to which ethylene oxide is added and acid salt type activators may have an effect on rust, so in that case it is preferable to use a rust preventive agent together.
非イオン性界面活性剤としては、例えば炭素数8〜20
の高級アルコールに酸化エチレン1〜20モルを付加し
た?リオ中ジエチレンアル中ルエーテル、アルキル基の
炭素数が8〜12のアルキルフェノールに酸化エチレン
1〜20モルを付加した?リオキシエチレンアルキルフ
ェノールエーテル、R素数8〜20の脂肪酸とゾエタノ
ールアミン、ゾイソfロノ9ノール7オンなどのアルカ
ノールアミンから導かれる脂BH#Ilアルカノールア
ミドなどが挙げられる。これらのうち、?リオキシエチ
レンアルキルエーテル、?リオギシエチレンアルキルフ
ェノールエーテル等の酸化エチレンを付〃uし九非イオ
ン性界面活性剤は、錆に対する影響が認められる場合が
ろるので、その場合は防錆剤を併用するのが好ましい。As a nonionic surfactant, for example, a carbon number of 8 to 20
Added 1 to 20 moles of ethylene oxide to higher alcohol? Diethylene ether in alcohol, 1 to 20 moles of ethylene oxide added to an alkylphenol whose alkyl group has 8 to 12 carbon atoms? Examples include lyoxyethylene alkylphenol ether, a fatty BH#Il alkanolamide derived from a fatty acid having an R prime number of 8 to 20, and an alkanolamine such as zoethanolamine and zoisoflono9ol7one. Of these? Lioxyethylene alkyl ether,? Nonionic surfactants containing ethylene oxide, such as ethylene alkylphenol ether, may have an effect on rust, so in that case it is preferable to use a rust preventive.
界面活性剤の配合量は1〜50%、好ましくは5〜30
%でるる。The amount of surfactant blended is 1 to 50%, preferably 5 to 30%.
It's %.
本発明はスコアリングツ9ツド襄造時の乾燥工程を省く
ことをその目的の一つとするものでめ夛、したがって組
成物中の水含量は5s以下であることが必要でるる。One of the objects of the present invention is to omit the drying step during the scoring process, and therefore it is necessary that the water content in the composition be 5 seconds or less.
本発明組成物には上記必須成分の他に、必要に応じて種
々の任意成分を配合することができる。臀に水不溶性研
磨剤に)を配合すれば、洗浄力をさらに同上嘔せること
ができる。かかる水不溶性研磨剤としては1例えば二酸
化ケイ素、酸化アルミニウム、水d化アルミニウム、f
f化マグネシウム、酸化チタン、炭化ケイ素、炭酸カル
シウム、リン酸カルシウム。In addition to the above-mentioned essential components, the composition of the present invention may contain various optional components as required. If a water-insoluble abrasive () is added to the buttocks, the cleaning power can be further increased. Examples of such water-insoluble abrasives include silicon dioxide, aluminum oxide, aluminum hydride, f
Magnesium fluoride, titanium oxide, silicon carbide, calcium carbonate, calcium phosphate.
酸化クロム、合成ゼオライト、天然ゼオライト、コラン
ダム、エメリー けい石、石英砂。Chromium oxide, synthetic zeolite, natural zeolite, corundum, emery silica, quartz sand.
カルサイト、ドロマイト、娶るいは塩化ビニル、?リス
チレン、−リエチレy、 ABSなどの?リマーピーズ
などが挙げられる。このうち、平均粒径l〜40μの二
酸化ケイ素、炭酸カルシウム、けい石がとくに好ましい
。水不溶性研磨剤の配合量は5〜50%%時に10〜4
0%が好ましい。Calcite, dolomite, or vinyl chloride? Listyrene, -riethyre, ABS, etc.? Examples include Rimapees. Among these, silicon dioxide, calcium carbonate, and silica stone having an average particle size of 1 to 40 μm are particularly preferred. The amount of water-insoluble abrasive is 5-50% and 10-4%.
0% is preferred.
また本発明組成物には上記成分以外に、無機塩、着色剤
、香料、殺薗剤、防黴剤、防錆剤などを必要に応じて刀
口えることができる。In addition to the above-mentioned components, the composition of the present invention may optionally contain inorganic salts, colorants, fragrances, insecticides, fungicides, rust preventives, and the like.
無機塩としては、炭酸ノー、ダ、炭酸カリなどの炭r!
1項;メタケイ戚ソーダ、2号ケイ酸ソーダなどのケイ
酸塩、ホウ砂、メタホウ酸ソーダなどのホウ酸塩:オル
トリン酸ソーダ。Inorganic salts include charcoal such as carbonate no, da, and potassium carbonate.
Item 1: Silicates such as metasilicic soda and No. 2 sodium silicate, borates such as borax and sodium metaborate: sodium orthophosphate.
トリ?リリン酸ソーダ、ビロリン酸ソーダなどのリン酸
塩が使用できる。蝋戚ソーダ、硫酸カリタムなどの梶e
R塩も使用できるが、錆に対する影響がみとめられる場
合がろるので、その場合は防錆剤を併用するの゛が好ま
しい。bird? Phosphates such as sodium lyphosphate and sodium birophosphate can be used. Kajie such as wax-related soda and potassium sulfate
R salts can also be used, but in some cases they may have an effect on rust, so in that case it is preferable to use a rust preventive.
本発明組成物を用いてスコアリングパッドを製造するに
は、例えばまず研磨剤#I巌を過当な形に成形し、これ
に破りエチレングリコールの融点以上の温度で混合した
本発明組成物を注入、重布、浸漬などの方法で付層させ
、放冷すればよい。In order to manufacture a scoring pad using the composition of the present invention, for example, first, abrasive #I is molded into an appropriate shape, and then the composition of the present invention mixed at a temperature equal to or higher than the melting point of ethylene glycol is poured into the mold. It may be applied by layering, layering, dipping, etc., and then allowed to cool.
スコアリングツ9ツドを傳成する研磨剤細線には、普通
、鋼、ステンレス、真鍮などの金sm線や、ナイロン、
ウレタンなどが用いられる。就中、研磨力、手の感触が
良い点からとくに鋼が好ましい。スコアリング)Qラド
を構成する細Ii!は太すざるとキズがつきやすく、手
の感触が悪いが、細すざると研磨力がおちるので平均径
1〜500μ、籍にlθ〜70μが好ましく、断面の形
状はいかなるものでも良く、例えば三角、四角、円、偏
平などを用いることができる。細線の全体の形状は円形
、正方形、長方形、小判形、楕円形(いずれも厚みを持
つ)、球形などの形で使用することができる。The abrasive thin wire that makes up the scoring tool is usually gold SM wire made of steel, stainless steel, brass, etc., nylon,
Urethane or the like is used. Among these, steel is particularly preferred because of its good polishing power and good feel in the hand. Scoring) The details that make up Qrad! Thick colanders tend to scratch easily and feel uncomfortable in the hands, but thin colanders reduce the abrasive power, so the average diameter is preferably 1 to 500μ, and the diameter is preferably lθ to 70μ.The cross-sectional shape may be any shape, for example Triangles, squares, circles, flat shapes, etc. can be used. The overall shape of the thin wire can be circular, square, rectangular, oval, oval (all have thickness), spherical, etc.
次に実施例を挙げて本発明の詳細な説明するが、本発明
はこれに制約されるものではない。EXAMPLES Next, the present invention will be described in detail with reference to Examples, but the present invention is not limited thereto.
実施例1
(1) 平均直径20〜50μのスチール細線52を
、直径7.5 cm X 6.0備(厚さ1.5国)の
小判形ノ♀ツドにH,型し、ノQツド内部に80℃で配
合した表−1に示す本発明組成′4!IJを52注入成
型し、放冷してスコアリングツ9ツドf:製造した。Example 1 (1) A thin steel wire 52 with an average diameter of 20 to 50 μm was shaped into an oval shaped hole with a diameter of 7.5 cm x 6.0 cm (thickness of 1.5 cm), and a hole was formed into a hole. Composition '4 of the present invention shown in Table 1, which was blended inside at 80°C! 52 IJs were injection molded and allowed to cool to produce a scoring tube.
(2)得られたスコアリングツ讐ツドについて、下記の
試験方法に従い、洗浄力、傷付は性、繰シ返し使用性を
試験した。その結果t−表−1に示す。(2) The obtained scoring needles were tested for detergency, scratch resistance, and repeated usability according to the following test methods. The results are shown in Table 1.
く洗浄力〉
3X8mの鉄のテストピースに、ナタネ油/カーゴンブ
ラック(重量比: 5/1 ) t−1、O?塗布した
ものを180℃で100分変性させたものを使用した。Cleaning power> On a 3 x 8 m iron test piece, rapeseed oil/cargon black (weight ratio: 5/1) t-1, O? The coated material was denatured at 180° C. for 100 minutes and then used.
評価法は、スコアリングツ9ツドに水を含ませて、l峙
/dの荷Xによシ30回況浄した後の重量減少率よシ相
対洗浄′4を求め、下記の2111り5段階評価を行な
った。The evaluation method is to soak the scoring tube 9 in water and wash it 30 times with a load of l/d, then calculate the relative cleaning'4 by the weight loss rate, and calculate A graded evaluation was performed.
相対洗浄力(%)
5:81−100
2:21 40
1: 0〜20
〔相対洗浄力(%) :比較品AI
(表−1参照)の洗浄力t50とした〕く傷付は性〉
スコアリングツ9ツドに水を含ませて、浴槽中流し台の
材質であるステンレス表面を50回洗浄後、傷の有無を
肉眼観察し、評価を行なった。Relative cleaning power (%) 5:81-100 2:21 40 1: 0-20 [Relative cleaning power (%): Detergent power t50 of comparison product AI (see Table 1)] Damage is more likely. The stainless steel surface, which is the material of the sink in the bathtub, was washed 50 times with water soaked in a scoring tube, and then the presence or absence of scratches was visually observed and evaluated.
Q:傷付けない。Q: It won't hurt.
Δ:やや傷付ける。Δ: Slightly hurt.
X:傷付ける。X: Hurt.
く繰り返し使用〉
スコアリングツリッドに水を宮ませて、浴槽や流し台の
材質でろるステンレス表面’i50回洗浄後、紋った。Repeated use > Pour water into the scoring grid and wash the stainless steel surface of the bathtub or sink 50 times before stains appear.
これ拘り返し行ない、何回で泡立ちの減少及び型くずれ
が起こるかを観察し、評1曲した。I repeated this process repeatedly, observed how many times it took for the foaming to decrease and the shape to lose its shape, and then made a review.
実施例2
表−2に示す不発BA組成物を用いる以外は実施例1と
同様にしてスコアリングツqツドを製造し、その評価金
した。その結果t−表−2に示す。Example 2 A scoring kit was produced and evaluated in the same manner as in Example 1, except that the unexploded BA composition shown in Table 2 was used. The results are shown in Table 2.
以下栄白
〔発明の効果〕
本発明のスコアリングツ9ツド用洗浄剤組成物を使用し
て製造したスコアリングツqツドは、優れた洗浄力、研
磨力′t−有し、被洗#面を傷つけることなく、長く繰
シ返し使用することができると共に、使用後の防錆効果
において優れている。しかも本発明のスコアリング/e
ツド用洗浄剤組成物を使用すれば、転球工程を賛チるこ
となく簡単な操作でスコアリングツ9ツド1c製造する
ことができるという利点を有する。[Effects of the Invention] Scoring tools manufactured using the cleaning composition for scoring tools of the present invention have excellent cleaning power and polishing power, and have excellent cleaning power and polishing power. It can be used repeatedly for a long time without damaging the surface, and has an excellent rust prevention effect after use. Moreover, the scoring/e of the present invention
The use of the cleaning agent composition for scoring has the advantage that the scoring tube 9 can be manufactured by a simple operation without compromising the ball rolling process.
以上that's all
Claims (1)
チレングリコール10〜90重量% (B)増粘剤0.1〜15重量% (C)界面活性剤1〜50重量% (D)水0〜5重量% を含有することを特徴とするスコアリングパッド用洗浄
剤組成物。 2、次の成分(A)〜(E) (A)平均分子量が2,000〜13,000のポリエ
チレングリコール10〜90重量% (B)増粘剤0.1〜15重量% (C)界面活性剤1〜50重量% (D)水0〜5重量% (E)水不溶性研磨剤5〜50重量% を含有することを特徴とするスコアリングパッド用洗浄
剤組成物。[Claims] 1. The following components (A) to (D) (A) 10 to 90% by weight of polyethylene glycol having an average molecular weight of 2,000 to 13,000 (B) Thickener 0.1 to 15% A cleaning composition for a scoring pad, comprising: (C) 1 to 50% by weight of a surfactant (D) 0 to 5% by weight of water. 2. The following components (A) to (E) (A) 10 to 90% by weight of polyethylene glycol with an average molecular weight of 2,000 to 13,000 (B) 0.1 to 15% by weight of thickener (C) Interface A cleaning composition for a scoring pad, comprising: 1 to 50% by weight of an activator; (D) 0 to 5% by weight of water; and (E) 5 to 50% by weight of a water-insoluble abrasive.