JPH0214017A - Magnetic fiber, production of magnetic fiber and production of magnetic woven cloth - Google Patents
Magnetic fiber, production of magnetic fiber and production of magnetic woven clothInfo
- Publication number
- JPH0214017A JPH0214017A JP63160230A JP16023088A JPH0214017A JP H0214017 A JPH0214017 A JP H0214017A JP 63160230 A JP63160230 A JP 63160230A JP 16023088 A JP16023088 A JP 16023088A JP H0214017 A JPH0214017 A JP H0214017A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- center portion
- fibers
- fiber
- covering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は磁性繊維、磁性繊維の製造方法および磁性織
物の製造方法に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application] The present invention relates to magnetic fibers, methods for producing magnetic fibers, and methods for producing magnetic textiles.
従来における磁性織物は、ナイロンに永久磁石材を混合
してペースト状にし、この混合したものを紡糸し、これ
を織り上げ、その後、電圧を加えて着磁していた。Conventional magnetic fabrics have been made by mixing nylon with a permanent magnetic material to form a paste, spinning the mixture, weaving it, and then magnetizing it by applying voltage.
しかしながら、かかる従来の磁性織物にあっては、磁力
が約70ガウスであるため、医療的に使用した場合磁力
が低すぎるため、医療効果を得にくいものであるという
不都合を有した。However, such conventional magnetic fabrics have a magnetic force of about 70 gauss, which is too low for medical use, making it difficult to obtain medical effects.
この発明の課題は、かかる不都合を解消することである
。An object of the present invention is to eliminate such inconveniences.
前記課題を達成するために、この発明の磁性繊維におい
ては、軸心部とこの軸心部の周囲を被覆する被覆部とを
備え、前記軸心部を永久磁石材で構成するとともに前記
被覆部を合成樹脂材で構成し、前記軸心部を着磁させた
ものである。In order to achieve the above object, the magnetic fiber of the present invention includes an axial center portion and a covering portion that covers the periphery of the axial center portion, the axial center portion is made of a permanent magnetic material, and the covering portion is made of a synthetic resin material, and the shaft center portion is magnetized.
また、前記軸心部を合成樹脂材で構成するとともに前記
被覆部を永久磁石材で構成し、前記被覆部を着磁させて
もよい。Furthermore, the shaft center portion may be made of a synthetic resin material, and the covering portion may be made of a permanent magnet material, and the covering portion may be magnetized.
次ぎに、これらの磁性繊維を製造するには前記軸心部を
着磁させた後、脱磁化し、その後、再度着磁させるか、
また、前記被覆部を着磁させた後、脱磁化し、その後、
再度着磁させればよい。Next, in order to manufacture these magnetic fibers, the shaft center part is magnetized, then demagnetized, and then magnetized again, or the coated part is magnetized and then demagnetized. ,after that,
All you have to do is magnetize it again.
なお、合成樹脂に永久磁石材を混合してペースト状にし
、この混合したものを紡糸した繊維にあって、この繊維
が硬化する以前に着磁させ、その後、脱磁化し、その後
、再度着磁させることによっても磁性繊維を製造するこ
とはできる。In addition, synthetic resin is mixed with a permanent magnetic material to form a paste, and this mixture is spun into fibers, which are magnetized before they harden, then demagnetized, and then magnetized again. Magnetic fibers can also be produced by
また、磁性織物を製造する場合には、軸心部とこの軸心
部の周囲を被覆する被覆部とを備え、前記軸心部を永久
磁石材で構成するとともに前記被覆部を合成樹脂材で構
成した繊維において、前記軸心部を着磁させた後、脱磁
化し、その後、この繊維によって織物を製造し、その後
、この織物を着磁させればよい。In addition, when manufacturing a magnetic fabric, it is provided with a shaft center portion and a covering portion that covers the periphery of the shaft center portion, the shaft center portion is made of a permanent magnetic material, and the covering portion is made of a synthetic resin material. In the constructed fiber, the axial center portion may be magnetized and then demagnetized, then a woven fabric may be manufactured using this fiber, and then this woven fabric may be magnetized.
また、前記軸心部を合成樹脂材で構成するとともに前記
被覆部を永久磁石材で構成した繊維において、前記被覆
部を着磁させた後、脱磁化し、その後、この繊維によっ
て織物を製造し、その後、この織物を着磁させることも
できる。Further, in the fiber in which the shaft center portion is made of a synthetic resin material and the sheathing portion is made of a permanent magnet material, the sheathing portion is magnetized and then demagnetized, and then a woven fabric is manufactured from this fiber. , the fabric can then be magnetized.
なお、合成樹脂に永久磁石材を混合してペースト状にし
、この混合したものを紡糸した繊維にあって、この繊維
が硬化する以前に着磁させ、その後、脱磁化し、その後
、この繊維によって織物を製造し、その後、この織物の
繊維を着磁させることもできる。In addition, synthetic resin is mixed with a permanent magnetic material to form a paste, and this mixture is spun into fibers, which are magnetized before they harden, and then demagnetized. It is also possible to produce a fabric and then magnetize the fibers of this fabric.
この発明の磁性繊維は、軸心部とこの軸心部の周囲を被
覆する被覆部とを備え、前記軸心部を永久磁石材で構成
するとともに前記被覆部を合成樹脂材で構成し、前記軸
心部を着磁させるか、又は、前記軸心部を合成樹脂材で
構成するとともに前記被覆部を永久磁石材で構成し、前
記被覆部を着磁したため、磁力が500〜1500ガウ
スの磁性繊維を得ることができる。The magnetic fiber of the present invention includes an axial center portion and a covering portion that covers the periphery of the axial center portion, the axial center portion is made of a permanent magnetic material, and the covering portion is made of a synthetic resin material; The axial center part is magnetized, or the axial center part is made of a synthetic resin material and the covering part is made of a permanent magnetic material, and the covering part is magnetized, so that the magnetic force is 500 to 1500 Gauss. Fiber can be obtained.
又、この発明の磁性繊維の製造方法または磁性織物の製
造方法は、−旦繊維を着磁させて、繊維中に磁力線の方
向を定め、その後、脱磁化させて、再度、着磁している
ため、磁力が高くなり、約500〜1500ガウスの磁
性繊維または磁性織物を得ることができる。In addition, the method for producing magnetic fibers or the method for producing magnetic textiles of the present invention includes: - first magnetizing the fibers to determine the direction of the lines of magnetic force in the fibers, then demagnetizing them and magnetizing them again. Therefore, the magnetic force becomes high, and it is possible to obtain magnetic fibers or magnetic fabrics with a magnetic force of about 500 to 1500 Gauss.
以下、この発明の実施例を図面に基づいて説明する。 Embodiments of the present invention will be described below based on the drawings.
第1図において、11は磁性繊維1の軸心部であり、フ
ェライト材(この発明の「永久磁石材」に相当する。)
で形成されている。また、12は被覆部であり、前記軸
心部11の周囲を被覆している。この被覆部12はナイ
ロン材で形成されている。このように構成される磁性繊
維lは前記軸心部11を着磁させた後、脱磁化し、その
後、再度着磁することにより製造される。In FIG. 1, 11 is the axial center of the magnetic fiber 1, which is a ferrite material (corresponding to the "permanent magnet material" of this invention).
It is formed of. Further, reference numeral 12 denotes a covering portion, which covers the periphery of the shaft center portion 11. This covering portion 12 is made of nylon material. The magnetic fiber 1 constructed in this manner is manufactured by magnetizing the shaft center portion 11, demagnetizing it, and then magnetizing it again.
第2図は他の磁性繊維2であり、軸心部21をナイロン
材で形成するとともに被覆部22をフェライト材で形成
したものである。このように構成される磁性繊維2は前
記被覆部22を着磁させた後、脱磁化し、その後、再度
着磁することにより製造される。FIG. 2 shows another magnetic fiber 2 in which the axial center portion 21 is formed of a nylon material and the covering portion 22 is formed of a ferrite material. The magnetic fiber 2 configured in this manner is manufactured by magnetizing the covering portion 22, demagnetizing it, and then magnetizing it again.
第3図は更に他の磁性繊維3を示したものであり、ナイ
ロン材、にフェライト材を混合してペースト状にし紡糸
した繊維である。この繊維を硬化する以前に着磁させ、
その後、脱磁化し、その後、再度着磁させることによっ
て磁性繊維3が製造される。FIG. 3 shows still another magnetic fiber 3, which is a fiber made by mixing a nylon material with a ferrite material, forming a paste, and spinning it. Before this fiber is hardened, it is magnetized,
Thereafter, the magnetic fiber 3 is manufactured by demagnetizing and then magnetizing again.
第4図および第5図は磁性織物6の実施例であり、繊維
61を織る上げることにより形成されたものである。こ
の繊維61の軸心部611はフェライト材で形成され、
また、被覆部612はナイロン材で形成されている。か
かる磁性織物6を製造するには、この繊維61の軸心部
611を着磁させた後、脱磁化し、この繊維によって織
物を製造し7、その後、この織物6における繊維61の
軸心部611を着磁させればよい。4 and 5 show examples of the magnetic fabric 6, which is formed by weaving fibers 61. The axial center portion 611 of this fiber 61 is formed of a ferrite material,
Further, the covering portion 612 is made of nylon material. In order to manufacture such a magnetic fabric 6, the axial center part 611 of the fiber 61 is magnetized and then demagnetized, a woven fabric is manufactured using this fiber 7, and then the axial center part 611 of the fiber 61 in this fabric 6 is magnetized. 611 may be magnetized.
また、他の磁性織物の例として、軸心部611をナイロ
ン材で形成するとともに被覆部612をフェライト材で
形成することもできる。この場合、この繊維の被覆部6
12を着磁させた後、脱磁化し、この繊維によって織物
を製造し、その後、この織物における繊維61の被覆部
612を着磁させればよい。Further, as another example of magnetic fabric, the shaft center portion 611 may be formed of a nylon material and the covering portion 612 may be formed of a ferrite material. In this case, the covering portion 6 of this fiber
After magnetizing the fibers 12, the fibers 12 are demagnetized, a woven fabric is manufactured using these fibers, and then the covering portion 612 of the fiber 61 in this woven fabric is magnetized.
更に、他の磁性織物の例として、合成樹脂に永久磁石材
を混合してペースト状にし、紡糸した繊維61を硬化す
る以前に着磁させ、その後、脱磁化し、その後、この繊
維61によって織物を製造し、その後、この織物におけ
る繊維を着磁させればよい。Furthermore, as an example of another magnetic fabric, a synthetic resin is mixed with a permanent magnet material to form a paste, the spun fibers 61 are magnetized before hardening, and then demagnetized, and then the fabric is formed by the fibers 61. After that, the fibers in this fabric may be magnetized.
前記実施例では、永久磁石材としてフェライト材を使用
したが、これに限定されるものではなく、永久磁石材と
して公知のものならば如何なるものでも良く、例えばバ
リウム・フェライト、鉄等であってもよい。In the above embodiment, a ferrite material was used as the permanent magnet material, but the material is not limited to this, and any material known as a permanent magnet material may be used, such as barium ferrite, iron, etc. good.
また、前記実施例では、合成樹脂としてナイロン材を使
用したが、これに限定されるものではなく、合成樹脂材
として公知のものならば如何なるものでも良く、例えば
ゴム等であってもよい。Further, in the above embodiments, nylon material was used as the synthetic resin, but the material is not limited to this, and any known synthetic resin material may be used, such as rubber.
この発明に係る磁性繊維は、軸心部とこの軸心部の周囲
を被覆する被覆部とを備え、前記軸心部を永久磁石材で
構成するとともに前記被覆部を合成樹脂材で構成し、前
記軸心部を着磁させるか、又は、前記軸心部を合成樹脂
材で構成するとともに前記被覆部を永久磁石材で構成し
、前記被覆部を着磁したため、磁力が500−1500
ガウスの磁性繊維を得ることができる。The magnetic fiber according to the present invention includes an axial center portion and a covering portion that covers the periphery of the axial center portion, the axial center portion is made of a permanent magnetic material, and the covering portion is made of a synthetic resin material, The axial center portion is magnetized, or the axial center portion is made of a synthetic resin material and the covering portion is made of a permanent magnetic material, and the covering portion is magnetized, so that the magnetic force is 500-1500.
Gaussian magnetic fibers can be obtained.
又、この発明の磁性繊維の製造方法または磁性織物の製
造方法は、−旦繊維を着磁させて、繊維中に磁力線の方
向を定め、その後、脱磁化させて、再度、着磁している
ため、磁力が高くなり、約500〜1500ガウスの磁
性繊維または磁性織物を得ることができる。In addition, the method for producing magnetic fibers or the method for producing magnetic textiles of the present invention includes: - first magnetizing the fibers to determine the direction of the lines of magnetic force in the fibers, then demagnetizing them and magnetizing them again. Therefore, the magnetic force becomes high, and it is possible to obtain magnetic fibers or magnetic fabrics with a magnetic force of about 500 to 1500 Gauss.
即ち、この発明の磁性繊維または磁性織物は医療効果が
得られる程度の磁力を発揮することができるため、医療
的に使用できるものである。That is, the magnetic fiber or magnetic fabric of the present invention can exhibit a magnetic force sufficient to provide a medical effect, and thus can be used medically.
図面はこの発明の実施例を示すもので、第1図は磁性繊
維の断面図、
第2図は他の磁性繊維の断面図、
第3図は更に他の磁性繊維の断面図、
第4図は磁性織物の断面図、
第5図は第4図のv部拡大図である。
1.2.3 ・・・ 磁性繊維
6 ・・・ 磁性織物
IL 21.611・・・ 軸心部
12、22.612・・・ 被覆部
図面のイ’j”G (’t”r容;こ変更2し)第1
図
第4図
6!
手続補正書
牛
1、事件の表示 昭和63年特許願第160230号
2、発明の名称 磁性繊維、磁性繊維の製造方法およ
び磁性織物の製造方法
3、補正をする者
事件との関係 特許出願人
住所 静岡県浜松市上新屋町200番地の5氏名 佐俸
直樹
4、代理人 〒430
5、補正命令の日付 昭和63年9月27日 (全送
日)3、補正の対象
fl)代理権を証明する書面、(2)図面7、補正の内
容
(1)別紙のように委任状を添付する。The drawings show embodiments of the present invention; FIG. 1 is a cross-sectional view of a magnetic fiber, FIG. 2 is a cross-sectional view of another magnetic fiber, FIG. 3 is a cross-sectional view of another magnetic fiber, and FIG. 4 is a cross-sectional view of another magnetic fiber. is a cross-sectional view of the magnetic fabric, and FIG. 5 is an enlarged view of section v in FIG. 4. 1.2.3 ... Magnetic fiber 6 ... Magnetic textile IL 21.611 ... Axial center portion 12, 22.612 ... Covering part drawing Change 2) 1st
Figure 4 Figure 6! Procedural amendment cow 1, Indication of the case Patent Application No. 160230 of 1988 2, Title of the invention Magnetic fiber, method for manufacturing magnetic fiber and method for manufacturing magnetic fabric 3, Relationship with the case by the person making the amendment Address of the patent applicant Name 5, 200 Kaminayacho, Hamamatsu City, Shizuoka Prefecture Naoki Satou 4, Agent 〒430 5, Date of amendment order September 27, 1986 (all date of delivery) 3, Subject of amendment fl) Proof of authority of agency (2) Drawing 7, Contents of amendment (1) Attach a power of attorney as shown in the attached sheet.
Claims (8)
を備え、前記軸心部を永久磁石材で構成するとともに前
記被覆部を合成樹脂材で構成し、前記軸心部を着磁させ
たことを特徴とする磁性繊維。(1). It comprises a shaft center portion and a covering portion covering the periphery of the shaft center portion, the shaft center portion is made of a permanent magnetic material, the covering portion is made of a synthetic resin material, and the shaft center portion is magnetized. A magnetic fiber characterized by:
を備え、前記軸心部を合成樹脂材で構成するとともに前
記被覆部を永久磁石材で構成し、前記被覆部を着磁させ
たことを特徴とする磁性繊維。(2). It comprises a shaft center portion and a covering portion that covers the periphery of the shaft center portion, the shaft center portion is made of a synthetic resin material, the covering portion is made of a permanent magnet material, and the covering portion is magnetized. A magnetic fiber characterized by:
し、この混合したものを紡糸した繊維にあって、この繊
維が硬化する以前に着磁させ、その後、脱磁化し、その
後、再度着磁させることを特徴とする磁性繊維の製造方
法。(3). A process in which synthetic resin is mixed with a permanent magnetic material to form a paste, and this mixture is spun into fibers, which are magnetized before they harden, then demagnetized, and then magnetized again. A method for producing magnetic fibers characterized by:
を備え、前記軸心部を永久磁石材で構成するとともに前
記被覆部を合成樹脂材で構成した繊維において、前記軸
心部を着磁させた後、脱磁化し、その後、再度着磁させ
ることを特徴とする磁性繊維の製造方法。(4). A fiber comprising a shaft center portion and a covering portion covering the periphery of the shaft center portion, the shaft center portion being made of a permanent magnetic material and the covering portion being made of a synthetic resin material. A method for producing magnetic fibers, which comprises magnetizing, demagnetizing, and then magnetizing again.
を備え、前記軸心部を合成樹脂材で構成するとともに前
記被覆部を永久磁石材で構成した繊維において、前記被
覆部を着磁させた後、脱磁化し、その後、再度着磁させ
ることを特徴とする磁性繊維の製造方法。(5). A fiber comprising an axial center portion and a covering portion covering the periphery of the axial center portion, wherein the axial center portion is made of a synthetic resin material and the covering portion is made of a permanent magnet material, wherein the covering portion is magnetized. 1. A method for producing magnetic fibers, which comprises demagnetizing the fibers and then magnetizing them again.
し、この混合したものを紡糸した繊維にあって、この繊
維が硬化する以前に着磁させ、その後、脱磁化し、その
後、この繊維によって織物を製造し、その後、この織物
の繊維を着磁させることを特徴とする磁性織物の製造方
法。(6). A synthetic resin is mixed with a permanent magnetic material to make a paste, and this mixture is spun into fibers, which are magnetized before they harden, then demagnetized, and then used to make textiles. 1. A method for producing a magnetic fabric, which comprises producing a magnetic fabric, and then magnetizing the fibers of the fabric.
を備え、前記軸心部を永久磁石材で構成するとともに前
記被覆部を合成樹脂材で構成した繊維において、前記軸
心部を着磁させた後、脱磁化し、その後、この繊維によ
って織物を製造し、その後、この織物における前記繊維
の軸心部を着磁させることを特徴とする磁性織物の製造
方法。(7). A fiber comprising a shaft center portion and a covering portion covering the periphery of the shaft center portion, the shaft center portion being made of a permanent magnetic material and the covering portion being made of a synthetic resin material. 1. A method for producing a magnetic fabric, which comprises magnetizing and demagnetizing the fibers, producing a fabric using the fibers, and then magnetizing the axial center of the fibers in the fabric.
を備え、前記軸心部を合成樹脂材で構成するとともに前
記被覆部を永久磁石材で構成した繊維において、前記被
覆部を着磁させた後、脱磁化し、その後、この繊維によ
って織物を製造し、その後、この織物における前記繊維
の被覆部を着磁させることを特徴とする磁性織物の製造
方法。(8). A fiber comprising an axial center portion and a covering portion covering the periphery of the axial center portion, wherein the axial center portion is made of a synthetic resin material and the covering portion is made of a permanent magnet material, wherein the covering portion is magnetized. 1. A method for producing a magnetic fabric, comprising: demagnetizing the fibers, producing a fabric using the fibers, and then magnetizing a covered portion of the fibers in the fabric.