JPH0195076A - Ink jet printer - Google Patents
Ink jet printerInfo
- Publication number
- JPH0195076A JPH0195076A JP25152587A JP25152587A JPH0195076A JP H0195076 A JPH0195076 A JP H0195076A JP 25152587 A JP25152587 A JP 25152587A JP 25152587 A JP25152587 A JP 25152587A JP H0195076 A JPH0195076 A JP H0195076A
- Authority
- JP
- Japan
- Prior art keywords
- recording material
- platen
- ink
- recording
- receiving layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明はインクジェットプリンター（以下ＩＪＰという
）に関し、更に詳しくはプラテンに接触している被記録
材を着色又は変色させることのないＩＪＰに関する。DETAILED DESCRIPTION OF THE INVENTION (Field of Industrial Application) The present invention relates to an inkjet printer (hereinafter referred to as an IJP), and more particularly to an IJP that does not color or discolor a recording material that is in contact with a platen.
（従来の技術）
インクジェット記録方法は、記録ヘッドのオリフィスか
ら記録液の小滴を紙等の被記録材上に付着させて記録を
行う記録方法であり、騒音の発生が少なく、特別な定着
処理を要することなく、高速記録及びフルカラー記録が
行える記録方法として注目されてし）る。(Prior art) The inkjet recording method is a recording method in which small droplets of recording liquid are deposited on a recording material such as paper from an orifice of a recording head, and generates little noise and requires special fixing treatment. It is attracting attention as a recording method that can perform high-speed recording and full-color recording without the need for
このインクジェット記録方法に用いられる記録液として
は、主に染料等の記録剤と、溶媒としての水若しくは水
と各種水溶性有機溶剤との混合物とから形成されている
ものが一般的である。The recording liquid used in this inkjet recording method is generally formed from a recording agent such as a dye, and water as a solvent or a mixture of water and various water-soluble organic solvents.
このようにインクジェット記録方法においては、水性系
の記録液が使用されるために、記録に用いる被記録材に
は、記録液の吸収性及び定着性に優れていることが要求
される。As described above, since an aqueous recording liquid is used in the inkjet recording method, the recording material used for recording is required to have excellent recording liquid absorption and fixing properties.
なかでも、２色以上の記録液を用いた多色インクジェッ
ト記録においては、被記録材上に付着する記録液の量も
多くなるので、記録液の吸収性及び定着性に特に優れて
いることが要求される。Among these, in multicolor inkjet recording using recording liquids of two or more colors, the amount of recording liquid that adheres to the recording material is large, so it is important to have particularly excellent recording liquid absorption and fixing properties. required.
このような特性に優れた被記録材としては、紙等の基材
上に、記録液の吸収性及び定着性に優れた多孔質のイン
ク受容層が設けられたものが知られている。As a recording material having excellent characteristics, one in which a porous ink-receiving layer having excellent recording liquid absorption and fixing properties is provided on a base material such as paper is known.
（発明が解決しようとしている間迎点）上記インクジェ
ット記録方法で記録を実施する場合において、被記録材
をロール紙の形態で使用する場合には、プリンターの作
動を停止又は中断すると被記録材とプラテンとが長時間
密着した状態に置かれることになる。(The point at which the invention is trying to solve) When performing recording using the above inkjet recording method, if the recording material is used in the form of roll paper, if the printer operation is stopped or interrupted, the recording material will be damaged. The platen will be in close contact with the platen for a long period of time.
このように被記録材とプラテンとが長時間密着して放置
されると、プラテンと被記録材とが接触している被記録
材の表側、すなわち被記録材の記録面であるインク受容
層及びその周辺に着色や変色が生じ、このような着色や
変色が生じたまま印字を再開すると十分な濃度と鮮明な
画像が得られないという問題が生じ、特に形成する画像
がカラー画像である場合には大きな問題となる。このよ
うな被記録材の着色や変色の開運は、特に使用する被記
録材がシリカ顔料を含むインク受容層を有する場合に顕
著であった。If the recording material and the platen are left in close contact with each other for a long time, the front side of the recording material where the platen and the recording material are in contact, that is, the ink receiving layer which is the recording surface of the recording material, Coloring or discoloration occurs around the area, and if printing is resumed with such coloring or discoloration occurring, a problem arises in that a sufficient density and clear image cannot be obtained, especially when the image to be formed is a color image. becomes a big problem. Such coloration or discoloration of the recording material was particularly noticeable when the recording material used had an ink receiving layer containing a silica pigment.
従って、本発明の目的は、被記録材としてシリカ顔料を
含有するインク受容層を有する被記録材を用いた場合に
も上述の様な被記録材の着色又は変色の問題を生じない
プラテンを用いたＩＪＰを提供することである。Therefore, an object of the present invention is to use a platen that does not cause the above-mentioned problem of coloring or discoloration of the recording material even when a recording material having an ink receiving layer containing silica pigment is used as the recording material. The aim is to provide the IJP that was
（問題点を解決するための手段） 以上の目的は以下の本発明によって達成される。(Means for solving problems) The above objects are achieved by the present invention as described below.
すなわち、本発明は、ゴム部材からなり、該ゴム部材が
、シリカ顔料を含むインク受容層を有するインクジェッ
ト用被記録材と６０℃の条件で密着させた場合に、該密
着部のインク受容層及びその周辺を実質的に着色又は変
色させないゴム材料からなるプラテンを備えたことを特
徴とするＩＪＰである。That is, the present invention comprises a rubber member, and when the rubber member is brought into close contact with an inkjet recording material having an ink receiving layer containing a silica pigment at 60° C., the ink receiving layer and This IJP is characterized in that it includes a platen made of a rubber material that does not substantially color or discolor the surrounding area.
（作 用）
ＩＪＰのプラテンとして、被記録材のインク受容層を着
色又は変色させないゴム材料からなるプラテンを使用す
ることによって、変色や着色のない画像、特に鮮明なカ
ラー画像を提供することができる。(Function) By using a platen made of a rubber material that does not color or discolor the ink receiving layer of the recording material as the IJP platen, it is possible to provide images without discoloration or coloring, especially clear color images. .
（好ましい実施態様）
次に好ましい実施態様を挙げて本発明を更に詳しく説明
する。(Preferred Embodiments) Next, the present invention will be described in more detail by citing preferred embodiments.
本発明のＩＪＰにおけるプラテンとは、ＩＪＰにおいて
、インクを噴射するインクジェットノズルに対向する紙
等の被記録材を所定の角度に保持するとともに、噴射さ
れたインクを受容した被記録材をインクの噴射に連動し
て搬送する作用を有するものであって、通常は片端又は
両端が駆動装置に連結されている直径数Ｃ１１のロール
形状を有している。The platen in IJP of the present invention refers to a platen that holds a recording material such as paper at a predetermined angle facing an inkjet nozzle that jets ink, and also holds the recording material that has received the jetted ink at a predetermined angle. It has a roll shape with a diameter of C11, and usually has one or both ends connected to a drive device.
従来のプラテンは一般に、合成ゴム、天然ゴム、合成プ
ラスチック等を主材料とし、その他必要に応じて可塑剤
、滑剤、軟化剤、加工助剤、熱安定剤、老化防止剤、酸
化防止剤等の添加剤が添加され、所定の形状に成形され
ている。Conventional platens are generally made of synthetic rubber, natural rubber, synthetic plastic, etc. as main materials, and may contain other additives such as plasticizers, lubricants, softeners, processing aids, heat stabilizers, anti-aging agents, antioxidants, etc. Additives are added and molded into a predetermined shape.
以上の如き従来のプラテンを用いてインクジェット記録
を実施すると、使用する被記録材が特にシリカ顔料を含
むインク受容層を有するものである時に、前述の如き問
題が生じるものであった。When inkjet recording is carried out using the conventional platen as described above, the above-mentioned problems occur especially when the recording material used has an ink receiving layer containing silica pigment.
これらの問題は、プラテンを被記録材に長時間接触させ
ておくときに、プラテン中の上記の様な添加剤、特に常
温で液状である添加剤が被記録材に移行するためである
と考えられている。These problems are thought to be due to the above additives in the platen, especially those that are liquid at room temperature, migrating to the recording material when the platen is left in contact with the recording material for a long time. It is being
又、シリカ顔料を含むインク受容層を有する被記録材と
は、従来公知の普通紙、加工紙、合成紙、プラスチック
フィルム等を基材とし、その表面に少なくとも１層のイ
ンク受容層を有するものであり、該インク受容層がシリ
カ顔料を主成分とする填料と例えばポリビニルアルコー
ルのような親水性ポリマーをバインダーとして形成され
ているものであり、従来、カラー画像の形成用として知
られているものである。Furthermore, a recording material having an ink-receiving layer containing a silica pigment refers to a material that is made of conventionally known plain paper, processed paper, synthetic paper, plastic film, etc., and has at least one ink-receiving layer on its surface. The ink-receiving layer is formed using a filler mainly composed of silica pigment and a hydrophilic polymer such as polyvinyl alcohol as a binder, and is conventionally known for forming color images. It is.
以上の如きシリカ顔料を含むインク受容層を有する被記
録材に対して着色や変色を生じないプラテンを選択する
方法は、いずれの方法でもよいが、好ましい方法は、プ
ラテンに上記の被記録材を接触させて一定温度に加熱し
て、被記録材の変色又は着色の度合を反射濃度で定量化
し、着色又は変色が一定値以下のものを採用する方法で
ある。Any method may be used to select a platen that does not cause coloring or discoloration on the recording material having an ink receiving layer containing silica pigment as described above, but the preferred method is to use the above recording material on the platen. In this method, the recording material is brought into contact and heated to a certain temperature, and the degree of discoloration or coloring of the recording material is quantified by reflection density, and those whose coloration or discoloration is below a certain value are adopted.
具体的にはプラテンに上記被記録材を巻きつけ（プラテ
ンと被記録材の裏面とが接触する）、６０℃の条件で２
日間放置し、紙の反射濃度が０．１以下のものを採用す
ることにより、実際のインクジェット記録において、記
録を長時間中断し、被記録材がプラテンに巻き付いた状
態でも被記録材の着色や変色を十分に防止することがで
きる。Specifically, the above recording material was wrapped around a platen (the platen and the back surface of the recording material were in contact), and heated at 60°C for 2 hours.
By using paper with a reflection density of 0.1 or less after being left for several days, in actual inkjet recording, even if recording is interrupted for a long time and the recording material is wrapped around the platen, coloring and coloring of the recording material will not occur. Discoloration can be sufficiently prevented.
以上の如きプラテンは、ゴム材と各種添加剤とからなる
組成物を成形して得られるものであり、本発明の目的に
適したプラテンは、ゴム部材として、例えば、スチレン
ブタジェンゴム、ブタジェンゴム、イソプレンゴム、Ｅ
ＰＤＭ、ウレタンゴム、シリコンゴム、クロロブレンゴ
ム等が使用でき、又、添加剤としては常温で固体のもの
を使用するのが好ましい。The above-mentioned platen is obtained by molding a composition made of a rubber material and various additives, and a platen suitable for the purpose of the present invention includes, for example, styrene-butadiene rubber, butadiene rubber, Isoprene rubber, E
PDM, urethane rubber, silicone rubber, chloroprene rubber, etc. can be used, and it is preferable to use additives that are solid at room temperature.
例えば、老化防止剤としては、常温で十分に固体である
もの、例えば、ポリ（２，２，４−トリメチル−１，２
−シトロキノリン）（軟化点８０〜１１０℃）、ジアリ
ール−ｐ−フェニレンジアミン（融点８０℃以上）、Ｎ
、Ｎ’−ジー２−ナフチル−ｐ−フェニレンジアミン（
融点２２５℃以上）、２．２′−メチレンビス（４−メ
チル−６−ｔｅｒｔ−ブチルフェノール）（融点１２０
℃）、ブチリデンビス（メチル−ブチルフェノール）（
融点２０５℃以上）等が挙げられる。For example, anti-aging agents include those that are sufficiently solid at room temperature, such as poly(2,2,4-trimethyl-1,2
-citroquinoline) (softening point 80-110°C), diaryl-p-phenylenediamine (melting point 80°C or higher), N
, N'-di-2-naphthyl-p-phenylenediamine (
(melting point: 225°C or higher), 2,2'-methylenebis(4-methyl-6-tert-butylphenol) (melting point: 120°C or higher)
°C), butylidene bis(methyl-butylphenol) (
melting point of 205°C or higher).
これに対して従来公知のプラテン社、上記老化防止剤と
して、常温で液状のものが使用されているため、前述の
ように老化防止剤の滲み出しにより被記録材が着色又は
変色するものであった。On the other hand, since Platen's conventionally known anti-aging agent is liquid at room temperature, the recording material may be colored or discolored due to the anti-aging agent oozing out as described above. Ta.
これに対して本発明では、上記の如く常温で固体の老化
防止剤等の添加剤を用いてプラテンを形成することによ
って、被記録材を着色又は変色させないプラテンとする
ことができた。勿論、老化防止剤以外の添加剤について
も常温で液状でないものを使用するのが好ましい。In contrast, in the present invention, by forming the platen using an additive such as an anti-aging agent that is solid at room temperature as described above, it was possible to create a platen that does not cause the recording material to be colored or discolored. Of course, it is preferable to use additives other than anti-aging agents that are not liquid at room temperature.
本発明のＩＪＰは上記のプラテンを備えていることを特
徴とし、その他のＩＪＰの構造はいずれも従来公知の構
造でよく特に限定されてよい。The IJP of the present invention is characterized by being equipped with the above-described platen, and the other structures of the IJP may be conventionally known structures and may be particularly limited.
（効 果）
以上の如き本発明のＩＪＰによれば、インクジェット記
録を長時間中断しても、被記録材が着色したり変色する
ことがなく、鮮明なインクジェット記録物を与えること
ができる。(Effects) According to the IJP of the present invention as described above, even if inkjet recording is interrupted for a long time, the recording material does not become colored or discolored, and a clear inkjet recording can be provided.
（実施例） 次に実施例を挙げて本発明を更に具体的に説明する。(Example) Next, the present invention will be explained in more detail with reference to Examples.
実施例１乃至２及び比較例１乃至３
下記第１表に記載の材料から通常の方法に従って直径３
ｃｍ及び長さ２０ｃｍのプラテンを成形した。これらの
プラテンに、Ｌ質紙を基材とし、その表面にシリカ系多
孔質白色顔料とポリビニルアルコールとからなる塗工液
を塗工してインク受容層を形成したインクジェット用被
記録材を巻き付け、６０℃のオーブン中に４８時間放置
し、インク受容層の変色の度合を反射濃度で評価した。Examples 1 to 2 and Comparative Examples 1 to 3 Diameter 3
A platen with a length of 20 cm and a length of 20 cm was molded. Wrapping around these platens is an inkjet recording material that is made of L-quality paper and whose surface is coated with a coating liquid consisting of a silica-based porous white pigment and polyvinyl alcohol to form an ink-receiving layer. The ink-receiving layer was left in an oven at 60° C. for 48 hours, and the degree of discoloration of the ink-receiving layer was evaluated based on reflection density.
尚、プラテンは被記録材の裏面（インク受容層の無い面
）から接触させた。Note that the platen was brought into contact with the recording material from the back surface (the surface without the ink-receiving layer).
γ １ −
１１１之Ｍ 反射濃度
実施例Ｉ ＣＲゴム（［：Ｒ−Ｆ−３８）
０．０４（常温で固体の老化防止剤を使用）
実施例２ ＣＲゴム（ＣＲ−Ｐ−３９） ０
．０４（常温で固体の老化防止剤を使用）
実施例３ 注型ウレタンゴム ０．０４（常温
で固体の老化防止剤を使用）
比較例Ｉ ＣＲゴム（ＣＲ−Ｆ−２９） ０
、１２（常温で液状の老化防止剤を使用）
比較例２ ＰＳラバー （ノンスレックス）
０．１２（常温で液状の老化防止剤を使用）
上記表において、（：Ｒ−Ｆ−３８，０Ｒ−Ｆ−３９及
びＣＲ−Ｆ−２９はいずれもクロロプレンゴム（成行商
事製）であり、ＰＳラバーはウレタンゴム（成行商事製
）であり、注型ウレタンゴムは武田薬品製である。γ 1-111-M Reflection Density Example I CR Rubber ([:R-F-38)
0.04 (using anti-aging agent that is solid at room temperature) Example 2 CR rubber (CR-P-39) 0
．． 04 (Using an anti-aging agent that is solid at room temperature) Example 3 Cast urethane rubber 0.04 (Using an anti-aging agent that is solid at room temperature) Comparative Example I CR rubber (CR-F-29) 0
, 12 (Using liquid anti-aging agent at room temperature) Comparative example 2 PS rubber (non-sleek)
0.12 (using a liquid anti-aging agent at room temperature) In the above table, (: R-F-38, 0R-F-39 and CR-F-29 are all chloroprene rubber (manufactured by Seiko Shoji), The PS rubber is urethane rubber (manufactured by Seiko Shoji), and the cast urethane rubber is manufactured by Takeda Pharmaceutical.
尚、テスト前のインク受容層の反射濃度は０．０４であ
る。Note that the reflection density of the ink receiving layer before the test was 0.04.
以上第１表から明らかな通り、上記のプラテンは、被記
録材を着色又は変色させることがないのに対し、比較例
のプラテンを備えたＩＪＰは被記録材を著しく着色又は
変色させるものであった。As is clear from Table 1, the platen described above does not color or discolor the recording material, whereas the IJP equipped with the platen of the comparative example does not significantly color or discolor the recording material. Ta.
又、実際に上記の各プラテンを実際のＩＪＰに装着し、
これに上記被記録材を同様に巻き付け、６力月間放置し
た後、カラー画像を記録したところ、実施例の場合には
汚れのない鮮明なカラー画像が得られたのに対し、比較
例の場合には、プラテン接着部が帯状に黄変し、カラー
画像にも黄変した帯が現われた。Also, actually attach each of the above platens to the actual IJP,
When the above-mentioned recording material was wrapped in the same manner and left for 6 months, a color image was recorded. In the case of the example, a clear color image with no stains was obtained, whereas in the case of the comparative example In this case, the adhesive part of the platen became yellowed in a band-like manner, and a yellowed band also appeared on the color image.
Claims (2)
含むインク受容層を有するインクジェット用被記録材と
６０℃の条件で密着させた場合に、該密着部のインク受
容層及びその周辺を実質的に着色又は変色させないゴム
材料からなるプラテンを備えたことを特徴とするインク
ジェットプリンター。(1) Consisting of a rubber member, when the rubber member is brought into close contact with an inkjet recording material having an ink-receiving layer containing silica pigment at a temperature of 60°C, the ink-receiving layer and its surroundings in the contact area are An inkjet printer comprising a platen made of a rubber material that does not substantially color or discolor.
ものである特許請求の範囲第（１）項に記載のインクジ
ェットプリンター。(2) The inkjet printer according to claim (1), wherein the additive added to the rubber member is solid at room temperature.