JPH01286835A - Laminated coating film superior in designing properties - Google Patents
Laminated coating film superior in designing propertiesInfo
- Publication number
- JPH01286835A JPH01286835A JP63117656A JP11765688A JPH01286835A JP H01286835 A JPH01286835 A JP H01286835A JP 63117656 A JP63117656 A JP 63117656A JP 11765688 A JP11765688 A JP 11765688A JP H01286835 A JPH01286835 A JP H01286835A
- Authority
- JP
- Japan
- Prior art keywords
- base layer
- mica
- coating
- powder
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明はマイカ粉末のもつ特異な意匠を塗装ムラなく表
出させることができる４ａ層塗膜に関する。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application] The present invention relates to a 4a layer coating film that can express the unique design of mica powder without coating unevenness.
本発明の８！１層塗膜は自動車の上塗り塗装などに利用
される。The 8!1 layer coating film of the present invention is used for top coating of automobiles, etc.
［従来の技術〕
近年、マイカ粉末を含有する塗膜の特異な意匠性が注目
され、自動車の上塗り塗装などに利用されている。すな
わちマイカ粉末を含有させることにより、従来のアルミ
ニウム粉末を含有するメタリック塗膜にはない真珠のよ
うな輝きを付与することができる。[Prior Art] In recent years, the unique design properties of coating films containing mica powder have attracted attention, and they have been used as top coats for automobiles. That is, by including mica powder, it is possible to impart a pearl-like shine that is not present in conventional metallic coatings containing aluminum powder.
しかしながら、マイカ粉末は隠蔽力に劣るため、下地の
色が表出しやすく均一に塗装するのが難しいという不具
合がある。そのため塗色は比較的隠蔽性の高い塗色に限
られ、選択の自由度が小さい。However, since mica powder has poor hiding power, it has the disadvantage that the underlying color tends to show through and is difficult to apply uniformly. Therefore, the paint color is limited to paint colors with relatively high hiding power, and the degree of freedom in selection is small.
そこで例えば特開昭５９−２１５８５７号公報にみられ
るように、マイカ含有塗料の色に近似し隠蔽力の大きな
ソリッドカラーのカラーベース塗料をまず塗装し、次い
でマイカ含有塗料を塗装しで形成された８！ｉ層塗膜が
知られている。このような積層塗膜によれば、マイカ含
有塗膜の隠蔽性が低くとも、表出するカラーベース層の
色はマイカ含有塗膜とほとんど同一であるため、意匠性
が損われるのが防止される。Therefore, as shown in JP-A No. 59-215857, for example, a solid color base paint that approximates the color of the mica-containing paint and has a high hiding power is first applied, and then a mica-containing paint is applied. ! I-layer coatings are known. According to such a laminated coating film, even if the hiding power of the mica-containing coating film is low, the color of the exposed color base layer is almost the same as that of the mica-containing coating film, so the design is prevented from being impaired. .
［発明が解決しようとする課題］
上記したような従来のｆｉ！１層塗膜では、邑ムラはあ
る程度防止できるが、マイカ含有塗料の塗装時の塗装ム
ラによるマイカ粉末のムラは依然として残っている。そ
のため、見る角度によって色が変化して見えるというマ
イカ含有塗膜の意匠性が最大限に発揮されているとはい
い龍い。[Problem to be solved by the invention] The conventional fi! In a single layer coating film, unevenness can be prevented to some extent, but unevenness of mica powder due to unevenness during application of mica-containing paint still remains. Therefore, it is said that the design of the mica-containing coating film, which appears to change color depending on the viewing angle, is maximized.
本発明はこのような事情に鑑みてなされたものであり、
カラーベース塗膜の構成を改良することにより、マイカ
含有塗料の塗装ムラを目立たなくすることを技術的課題
とするものである。The present invention was made in view of these circumstances, and
The technical objective is to make coating unevenness of mica-containing paint less noticeable by improving the composition of the color base coating film.
［課題を解決するための手段］
本発明の槓筈塗膜は、隠蔽力の大きなカラーベース層と
、カラーベース層表面に形成されたマイカベース層とを
有する積層塗膜において、カラーベース層にはマイカ粉
末およびアルミニウム粉末の少なくとも一方が含有され
ていることを特徴とする。[Means for Solving the Problems] The coating film of the present invention is a laminated coating film having a color base layer with a large hiding power and a mica base layer formed on the surface of the color base layer, in which the color base layer contains mica powder. and aluminum powder.
カラーベース層は基体樹脂と着色顔料とを主体とし、マ
イカ粉末およびアルミニウム粉末の少なくとも一方が含
有されている。基体樹脂は塗膜の基体となるものであり
、アクリル樹脂、アルキド樹脂などがメラミン樹脂と架
橋したもの、あるいはアクリル樹脂単独、アクリル樹脂
とｊＪＡＨ素系樹脂との混合物など、従来と同様の基体
樹脂を利用することができる。The color base layer is mainly composed of a base resin and a colored pigment, and contains at least one of mica powder and aluminum powder. The base resin is the base of the coating film, and can be the same as conventional base resins, such as acrylic resin, alkyd resin, etc. crosslinked with melamine resin, acrylic resin alone, or a mixture of acrylic resin and jJAH base resin. can be used.
着色顔料も従来と同様に有機顔料および無機顔料のいず
れも用いることができる。含有されるマイカ粉末または
アルミニウム粉末の光輝性を損わないように、透明性を
有する有機顔料を用いることが好ましい。As the coloring pigment, both organic pigments and inorganic pigments can be used as in the conventional art. It is preferable to use a transparent organic pigment so as not to impair the glitter of the mica powder or aluminum powder contained.
本発明の最大の特徴は、カラーベース層内にマイカ粉末
およびアルミニウム粉末の少なくとら一方を含有すると
ころにある。このように構成することにより、カラーベ
ース層表面に形成されるマイカベース層に塗装ムラが生
じても、カラーベース層に存在するマイカ粉末およびア
ルミニウム粉末の少なくとも一方がマイカベース層を透
過して表出することにより、塗装ムラが目立たず、意匠
性に優れるようになる。The greatest feature of the present invention is that the color base layer contains at least one of mica powder and aluminum powder. With this configuration, even if coating unevenness occurs in the mica base layer formed on the surface of the color base layer, at least one of the mica powder and the aluminum powder present in the color base layer will pass through the mica base layer and be exposed. As a result, uneven coating becomes less noticeable and the design becomes superior.
カラーベース層に用いられるマイカ粉末としては、未処
理マイカ、酸化チタンが被覆されたバールマイカ、金属
メツキされた金属メツキマイカなどを用いることができ
る。またアルミニウム粉末としでは、従来のメタリック
塗料に用いられているアルミニウム粉末が利用できる。As the mica powder used for the color base layer, untreated mica, burr mica coated with titanium oxide, metal-plated mica, etc. can be used. Further, as the aluminum powder, aluminum powder used in conventional metallic paints can be used.
このカラーベース層は隠蔽性に優れている。このように
構成するには、隠蔽力の大きな顔料を使用することで容
易に行なうことができるが、隠蔽力の大きな顔料は透明
性が悪いため、マイカ粉末などの光輝性が損われる場合
がある。従ってアルミニウム粉末などにより隠蔽性を付
与することが望ましい。なお、カラーベース層の隠蔽力
はマイカベース層の隠蔽力に応じて決めることができ、
マイカベース層とカラーベース層とが積層された状態で
ほぼ完全に隠蔽すれば足りる。This color base layer has excellent hiding properties. This structure can be easily achieved by using pigments with high hiding power, but since pigments with high hiding power have poor transparency, the brightness of mica powder etc. may be impaired. . Therefore, it is desirable to provide hiding properties using aluminum powder or the like. The hiding power of the color base layer can be determined according to the hiding power of the mica base layer.
It is sufficient that the mica base layer and the color base layer are almost completely hidden in a laminated state.
マイカベース層は基体樹脂とマイカ粉末とを主体とし、
通常透明性の高い着色顔料で着色されている。ここで基
体樹脂としてはカラーベース層と同様に各種樹脂を利用
できる。またマイカ粉末としては、未処理マイカ粉末、
バールマイカ粉末、金属メツキマイカ粉末のいずれも利
用できるが、バールマイカ粉末を用いれば極めて美麗な
意匠を有する積層塗膜が得られる。なお、マイカ粉末の
含有量は特に制限な（、塗膜物性を損わない範囲上種々
選択される。The mica base layer mainly consists of a base resin and mica powder,
It is usually colored with highly transparent colored pigments. Here, as the base resin, various resins can be used as in the case of the color base layer. In addition, as mica powder, untreated mica powder,
Both burr mica powder and metal-plated mica powder can be used, but if burr mica powder is used, a laminated coating film with an extremely beautiful design can be obtained. Note that the content of mica powder is not particularly limited (it is selected from a variety of values within a range that does not impair the physical properties of the coating film).
マイカベース層はそのままで意匠塗膜とすることができ
るが、マイカベース層表面にクリア塗膜層を形成するこ
とも好ましい。このようにすれば美観が一層向上し、マ
イカベース層を保護することができる。Although the mica base layer can be used as a decorative coating film as it is, it is also preferable to form a clear coating layer on the surface of the mica base layer. In this way, the aesthetic appearance is further improved and the mica base layer can be protected.
本発明の積層塗膜を形成するには、カラーベース層を形
成後マイカベース層が形成される。ウェット−オン−ウ
ェットで形成した後、一体的に乾燥させることもできる
し、カラーベース層が乾燥後マイカベース層を形成して
もよい。To form the laminated coating film of the present invention, a mica base layer is formed after forming a color base layer. The color base layer may be formed wet-on-wet and then dried integrally, or the mica base layer may be formed after the color base layer is dried.
［発明の作用および効果］
本発明のＷＡ７１塗膜は、カラーベース層とマイカベー
ス層とから構成され、カラーベース層にはマイカ粉末お
よびアルミニウム粉末の少なくとも一方が含有されてい
る。従って、たとえば正面から見ると、マイカベース層
のマイカ粉末による真珠光沢が表出した意匠となる。こ
のとき塗装ムラなどによりマイカベース層にムラが生じ
ている場合は、マイカ粉末の少ない部分ではカラーベー
ス層のマイカ粉末またはアルミニウム粉末が表出して、
マイカベース層のマイカ粉末の不足を補う。これにより
ムラが解消されるためほぼ均一な意匠となり従来に比べ
て意匠性に帰れている。また、正面に対して斜め方向か
ら見た場合は、マイカベース層を通してカラーベース層
が見える。カラーベース層は隠蔽性に帰れているため均
一に塗装することが容易であり、均一な意匠となる。[Operations and Effects of the Invention] The WA71 coating film of the present invention is composed of a color base layer and a mica base layer, and the color base layer contains at least one of mica powder and aluminum powder. Therefore, when viewed from the front, for example, the design has a pearlescent luster due to the mica powder of the mica base layer. At this time, if there is unevenness in the mica base layer due to uneven coating, etc., the mica powder or aluminum powder of the color base layer will be exposed in areas with less mica powder.
Make up for the lack of mica powder in the mica base layer. This eliminates unevenness, resulting in a nearly uniform design, which is more aesthetically pleasing than before. Furthermore, when viewed from an oblique direction with respect to the front, the color base layer is visible through the mica base layer. Since the color base layer has a concealing property, it is easy to apply it uniformly, resulting in a uniform design.
すなわち本発明の積層塗膜によれば、従来に比べてムラ
が少なく意匠性に極めて優れている。そして生産ライン
では均一に塗装するのが困難なために従来採用されなか
った塗色でも、本発明の積層ユ膜を適用することにより
可能となり、塗色の自由度が」曽大する。That is, the laminated coating film of the present invention has less unevenness and is extremely superior in design compared to conventional coatings. Furthermore, by applying the laminated film of the present invention, it is possible to apply a coating color that was not previously adopted because it is difficult to apply uniformly on a production line, and the degree of freedom in coating color is greatly increased.
［実施例］ 以下、実施例により具体的に説明する。[Example] Hereinafter, this will be explained in detail using examples.
（実施例１） 第１図に本発明の一実施例の積層塗膜を示す。(Example 1) FIG. 1 shows a laminated coating film according to an embodiment of the present invention.
このｆａ層塗膜は、鋼板１００表面に形成された電看塗
１１！Ｉ層１と、電着塗膜層１表面に形成されたカラー
ベース層２と、カラーベース層２表面に形成されたマイ
カベース層３と、マイカベース層３表面に形成されたク
リア塗膜層４と、より構成される。This fa layer coating film is the electric coating 11! formed on the surface of the steel plate 100! I layer 1, color base layer 2 formed on the surface of electrodeposition coating layer 1, mica base layer 3 formed on the surface of color base layer 2, and clear coating layer 4 formed on the surface of mica base layer 3. , consists of.
各層の構成を製造方法を説明しながら以下に説明する。The structure of each layer will be explained below while explaining the manufacturing method.
（１）電着塗膜？１１
脱脂されリン酸亜鉛化成処理された６００Ｘ１２００ｍ
ｍの鋼板１００に、電着塗料（［ニレクロン９４００Ｊ
関西ペイント（株）製）を電−着塗装し、１８０℃で３
０分焼付けて電着塗膜Ｍ１を形成する。(1) Electrodeposition coating? 11 600X1200m degreased and zinc phosphate chemical conversion treatment
Electrodeposition paint ([Nileclone 9400J
Kansai Paint Co., Ltd.) was electrodeposited and heated at 180°C for 30 minutes.
Baking is performed for 0 minutes to form an electrodeposited coating M1.
（２）カラーベース層２
樹脂固形分４０重量部のアクリル／メラミン混合樹脂中
に、アルミニウム粉末（「アルペースト７１３ＯＮ Ｊ
東洋アルミ社製）が固形分で１０重量部、カーボンブラ
ック（ｒ ＦＷ −２００Ｊ Ｄｅｏｕｓｓａ社製）が
２重量部含有された黒色カラーベース塗料を、専用シン
ナーで塗装粘度（１５秒、フォードカップ＃４）に希釈
し、静電塗装機（ｒＲＥＡオートガンｊランズバーグ社
製）を用いて電着塗膜層１表面に乾燥膜厚で２５〜３０
μｍの厚さに塗装する。そして１４０℃で３０分焼付け
てカラーベース層２を形成する。(2) Color base layer 2 Aluminum powder ("Alpaste 713ON J
A black color base paint containing 10 parts by weight of solids (manufactured by Toyo Aluminum Co., Ltd.) and 2 parts by weight of carbon black (manufactured by Deoussa Co., Ltd. r FW-200J) was applied with a special thinner to reduce the viscosity (15 seconds, Ford Cup #4). diluted to
Paint to a thickness of μm. Then, the color base layer 2 is formed by baking at 140° C. for 30 minutes.
（３）マイカベース層３
上記カラーベース塗料と同一の樹脂固形分４０重化部の
アクリル／メラミン混合樹脂中に、パールマイカ粉末（
［ｌ ｒｉｏｄｉｎ １０１８ Ｊヌル９社製）が固形
分で１０重層部、カーボンブラック（ｒＦＷ −２００
Ｊ Ｄｅｇｕｓｓａ社製）が０．５重Ｍ部含有された黒
色マイカベース塗料を、専用シンナーで塗装粘度（１５
秒、フォードカップ＃４）に希釈し、静電塗装置ｆｆ
（ｒＲＥＡオートガン」ランズバーグ社製）を用いて乾
燥膜厚で１５〜２０μｍの厚さに塗装する。(3) Mica base layer 3 Pearl mica powder (
[l riodin 1018 manufactured by J Null 9 Co., Ltd.] has a solid content of 10 layers, and carbon black (rFW-200
A black mica-based paint containing 0.5 parts by weight (manufactured by J Degussa) was coated with a special thinner to reduce the coating viscosity (15
sec, diluted in Ford Cup #4), electrostatic coating machineff
(rREA Autogun, manufactured by Landsburg) to a dry film thickness of 15 to 20 μm.
（４）クリア塗膜層４
そしてフラッシュタイムを５分とり、アクリル／メラミ
ン樹脂からなるクリア塗料を専用シンナーで塗装粘度（
２０秒、フォードカップ＃４）に希釈し、静電塗装ｆｉ
（ｒミニベル」ランズバーグ社製）を用いて、ウェット
状態のマイカベース層３表面に乾燥膜厚で２５〜３０μ
ｍの厚さに塗装する。そして１４０℃で３０分焼付けて
マイカベース層３およびクリア塗Ｖ；４層４を一体的に
形成する。(4) Clear paint film layer 4 Then, after 5 minutes of flash time, apply a clear paint made of acrylic/melamine resin with a special thinner to a coating viscosity (
20 seconds, diluted in Ford Cup #4) and electrostatically painted fi
(r minibell) manufactured by Landsberg Co., Ltd., was applied to the surface of the wet mica base layer 3 with a dry film thickness of 25 to 30 μm.
Paint to a thickness of m. Then, it is baked at 140° C. for 30 minutes to integrally form the mica base layer 3 and the clear coat V;4 layer 4.
得られた積層塗膜について、塗装ムラの目立ちやすさを
評価し、結果を表に示す。なお、塗装ムラは室内の蛍光
灯下において目視にて評価した。The obtained laminated coating film was evaluated for the conspicuousness of coating unevenness, and the results are shown in the table. The coating unevenness was visually evaluated indoors under fluorescent lighting.
本実施例のａＳ塗躾では、マイカベース層３に塗装ムラ
が生じていても、カラーベース層２に含有されるアルミ
ニウム粉末によりムラが目立たず、意匠性に優れている
。In the aS coating of this embodiment, even if coating unevenness occurs in the mica base layer 3, the unevenness is not noticeable due to the aluminum powder contained in the color base layer 2, and the design is excellent.
（実施例２）
本実施例では、樹脂固形分４０重開部の７クリル／メラ
ミン混合樹脂中に、アルミニウム粉末（「アルペースト
７１３ＯＮ Ｊ東洋アルミ社製）が固形分で１０重ａ部
、パールマイカ粉末（ｒ Ｉ ｒｉｏｄｉｎ ＋０１８
Ｊメルク社製）が５重分部、カーボンブラック（ｒ
ＦＷ −２００Ｊ Ｄｅｇｕｓｓａ社製）が２．３ｆｌ
ａｔ部含有されたカラーベース塗料を用いてカラーベー
ス層２を形成したこと以外は実施例１と同様である。そ
の塗装ムラの目立ちやすさを表に示す。(Example 2) In this example, aluminum powder (Alpaste 713ON J manufactured by Toyo Aluminum Co., Ltd.) was added to a mixed resin of 7 acrylic/melamine with a resin solid content of 40 parts by weight and a pearl powder with a solid content of 10 parts by weight. Mica powder (r I riodin +018
(manufactured by J Merck) is a quintuple part, carbon black (r
FW-200J Degussa) is 2.3fl
The procedure is the same as in Example 1 except that the color base layer 2 was formed using a color base paint containing the at part. The table shows how conspicuous the coating unevenness is.
本実施例でも塗装ムラは目立たず、意匠性に優れている
。また実施例１と比較すると、カラーベース層２にパー
ルマイカ粉末が含有されている分、塗装ムラが目立ちに
くく、意匠性に優れている。Even in this example, the coating unevenness is not noticeable and the design is excellent. Also, compared to Example 1, since the color base layer 2 contains pearl mica powder, coating unevenness is less noticeable and the design is excellent.
（比較例）
本比較例では、樹脂固形分４０！’Ｉｕｆｆｉ部のアク
リル／メラミン混合樹脂中に、酸化チタン（［タイベー
クＣＲ９０Ｊ石原産業（株）製）が３８重置部、カーボ
ンブラック（ｒ ＦＷ −２００Ｊ Ｄｅｇｕｓｓａ社
製）が２重量部含有されたカラーベース塗料を用いてカ
ラーベース層を形成したこと以外は実施例１と同様であ
る。その塗装ムラの目立ちやすさを表に示す。(Comparative example) In this comparative example, the resin solid content is 40! A color base containing 38 parts by weight of titanium oxide (Tybake CR90J manufactured by Ishihara Sangyo Co., Ltd.) and 2 parts by weight of carbon black (r FW-200J manufactured by Degussa) in the acrylic/melamine mixed resin of the Iuffi part. This example is the same as Example 1 except that the color base layer was formed using a paint. The table shows how conspicuous the coating unevenness is.
この比較例の積層塗膜では、カラーベース層２は酸化チ
タンとカーボンブラックで明度が調整されているが、マ
イカベース層３の塗装ムラが著しく目立って意匠性に劣
っている。In the laminated coating film of this comparative example, the brightness of the color base layer 2 is adjusted with titanium oxide and carbon black, but the coating unevenness of the mica base layer 3 is extremely noticeable and the design is poor.
第１図は本発明の一実施例の８１層塗膜の概略断面図で
ある。
１・・・電着塗ｌｌＡ２・・・カラーベース層３・・・
マイカベース１１４・・・クリアｔｉ １０１Ｍ特許出
願人 アイシン化工株式会社
代理人 弁理士 大川 宏FIG. 1 is a schematic cross-sectional view of an 81-layer coating film according to an embodiment of the present invention. 1...Electrodeposition coating llA2...Color base layer 3...
Mica base 114...Clear ti 101M patent applicant Hiroshi Okawa, agent of Aisin Kako Co., Ltd., patent attorney
Claims (1)
ス層表面に形成されたマイカベース層とを有する積層塗
膜において、 該カラーベース層にはマイカ粉末およびアルミニウム粉
末の少なくとも一方が含有されていることを特徴とする
意匠性に優れた積層塗膜。(1) In a laminated coating film having a color base layer with high hiding power and a mica base layer formed on the surface of the color base layer, the color base layer contains at least one of mica powder and aluminum powder. Laminated coating film with excellent design characteristics.