JPH01282355A - Both side tinseled yarn - Google Patents

Abstract

PURPOSE:To obtain both side tinseled yarn for silk fabric such as belting, keeping feeling and smoothness of silk, beautiful and having excellent strength, comprising sheet-like slit yarn having transferred layers of metallic sheen on both sides of silk fabric. CONSTITUTION:For instance, metallic sheen transferred foils deposited with silver are adhered on both sides of obverse and reverse of silk fabric 1 through adhesive layers 3 consisted of polyester resin and isocyanate resin, next, base films of said metallic sheen transferred foils are separated, then metallic sheen transferred layers 4 are formed on the silk fabric 1 to afford the aimed both side tinseled yarn, which shows no feeling of physical disorder and is compatable with other silk fabric as silk fabric itself is used as a raw material.

Description

[Detailed description of the invention] [Technical field] The present invention relates to double-sided gold and silver thread.

[Prior Art] Conventionally, double-sided gold and silver threads have been known by using Japanese paper or plastic film as the material and vapor-depositing metal with metal foil attached to both the front and back sides.

[Problems to be Solved by the Invention] However, the conventional double-sided gold and silver thread described above has the following drawbacks.

In the case of washi paper, there is a problem of relatively insufficient strength, and in the case of plastic, the surface is too smooth, spoiling the unique texture of silk fabrics, and making it difficult to express the texture and smoothness of the kumi. was there.

The present invention has been developed in view of the above-mentioned conventional problems, such as the lack of strength when using Japanese paper, and the fact that when using plastic, the surface is too smooth, which impairs the unique texture of silk fabrics, and the texture and smoothness of silk. It is an object of the present invention to provide a double-sided gold and silver thread that can be used satisfactorily for M1 textiles by solving problems such as difficulty in expression.

[Means for solving the problems] The double-sided gold and silver thread of the present invention has a metallic luster transfer layer on both sides of the silk #a material via an undercoat layer and/or an adhesive layer, if necessary. It is characterized by slitting a sheet-like material provided with a top coat resin layer.

[Work] The silk fabric used as the material for the double-sided gold and silver thread of the present invention is:

Since the silk fabric itself is used, it has the effect of producing double-sided gold and silver threads that have the texture of silk. Therefore, even when used for silk fabrics, silk fabrics that are woven easily blend well with each other without giving any discomfort to the materials, have the effect of maintaining the texture of silk and the smoothness of silk, and are beautiful. In addition, it is extremely strong due to the strength of the silk fabric used as the material, and there is no need to worry about it breaking during weaving.

[Example] Next, the double-sided gold and silver thread of the present invention will be explained based on the drawings.

FIGS. 1, 2, and 3 are schematic partial sectional views showing embodiments of the double-sided gold and silver thread of the present invention. In the figure, (1)
is the silk material for the double-sided gold and silver thread of the present invention! If necessary, a primer layer (2) or /
A metallic luster transfer layer (2) and, if necessary, a topcoat resin layer (5) are laminated via an adhesive layer (3).

The silk fabric (1) used in the present invention is a normal silk fabric.The silk fabric (1) may be one piece or may be a laminate of several pieces.

The undercoat layer (2) is used only when the eyes of the silk fabric (1) are not to be exposed, and there are no particular restrictions as long as it has sufficient adhesion to the silk fabric (1), for example, acrylic or melamine resin. It is formed by applying and drying a resin paint such as , epoxy/isocyanate resin, or polyester/isocyanate resin.

There is no particular restriction on the material used to completely adhere the adhesive layer (3 to the metallic luster transfer layer), the silk fabric (1), or the primer layer (2) as long as it has sufficient adhesive properties.

For example, it is formed by applying and drying an adhesive such as acrylic/melamine resin, epoxy/isocyanate resin, or polyester/incyanate resin.

For the metallic luster transfer layer (2), a known metallic luster transfer foil can be used. The metallic luster transfer foil is adhered to both sides of the silk fabric (1) via a primer layer (2) or/and an adhesive layer (5) if necessary, and then the base film of the metallic luster transfer foil is peeled off to form the silk fabric ( A metallic luster transfer layer (2) is formed on 1).

The topcoat resin layer (5) may be provided for the purpose of coloring the metallic color of the metallic luster transfer foil 4 to a desired color or for the purpose of protecting it, and there are no particular restrictions on the resin or coloring agent, and ordinary gold and silver threads may be used. You can use whatever is already in use.

Therefore, since the double-sided gold and silver thread of the present invention uses silk fabric itself as a material instead of Japanese paper or plastic film, it is possible to obtain a double-sided gold and silver thread that has the texture of silk. Therefore, even when used for silk fabrics, silk fabrics that are woven so that they blend well with each other without causing any discomfort between the materials are beautiful as they maintain the texture of silk and the smoothness of the braid, and are also as strong as the silk fabric used as the material. #1: It is very strong and there is no need to worry about it breaking during weaving.
We have made it possible to provide double-sided gold and silver thread that can be used in textiles.

Next, the present invention will be explained with reference to Examples.

Example 1 After adhering silver-plated metallic luster transfer foil to both the front and back sides of a silk fabric using an adhesive made of polyester resin and isocyanate resin, the base film of the metallic luster transfer foil was peeled off to create a silk fabric. A beautiful silver silk fabric was obtained by forming a metallic luster transfer layer on the fabric.

The resulting silver-colored silk fabric was passed through a rough heat-pressing roll, and the elegant masonry pattern of the silk fabric itself was revealed, making it even more elegant.

Cut 100 pieces of silver silk fabric (0,:to:11w)
Micro slits were made in the width of the fabric to create gold and silver threads on both sides.

This thickened double-sided gold and silver thread was woven into an obi along with real silk thread, but there was no thread breakage, and there was no difference in gloss between the front and back sides, resulting in a belt with excellent texture and flexibility.

Example 2 An undercoat layer containing polyurethane resin as the main component was formed on both the front and back sides of a silk fabric, and then a metallic luster transfer foil coated with silver leather was adhered using an adhesive consisting of polyester resin and isocyanate resin. The base film of the metallic luster transfer foil was peeled off to form a metallic luster transfer layer on the wl fabric, yielding a beautiful silver silk fabric.

An orange-blue resin was applied to the surface of the resulting silver silk fabric and dried to form a topcoat layer, resulting in a beautiful golden silk fabric.

100 pieces of the golden group Il & things that were obtained (0103 ■ 4g
) I made a micro slit to get gold and silver threads on both sides.

When this double-sided gold and silver thread was woven into a belt along with real silk thread, there was no thread breakage and no difference in gloss between the front and back sides, resulting in a belt with excellent texture and flexibility.

Example 3 After adhering aluminum-deposited metallic gloss transfer foil to the front side of a silk fabric using an adhesive made of polyester resin and isocyanate resin, the base film of the metallic gloss transfer foil was peeled off to form a silk fabric. A beautiful silver silk fabric was obtained by forming a metallic luster transfer layer on the front side.

An emulsion-based acrylic-vinyl acetate resin adhesive was applied to the back side of the obtained silver silk fabric, and two pieces were adhered together with the adhesive side together to obtain a silver silk fabric with beautiful both sides.

The resulting silver silk fabric was microslit into 80 pieces (0,379ss@) to obtain gold and silver threads on both sides.

When this double-sided gold and silver thread was woven into a belt along with real silk thread, there was no thread breakage and no difference in gloss between the front and back sides, resulting in a belt with excellent texture and flexibility.

[Effects of the invention] Example 1. As is clear from Example 2 and Example 3,
The double-sided gold and silver thread of the present invention uses silk fabric itself as a material, and can obtain a double-sided gold and silver thread that has the texture of silk. Therefore, even when used for silk fabric, the materials do not feel strange and can be easily woven with each other. The silk fabric is beautiful as it maintains the texture and smoothness of silk, and is also extremely strong, demonstrating the strength of the silk fabric used as the material.
The effect is that there is no need to worry about it breaking during weaving.

[Brief explanation of the drawing]

FIGS. 1, 2, and 3 are schematic partial sectional views showing the structure of the double-sided gold and silver thread of the present invention. (Drawing codes) (1) Silk fabric (2): Undercoat layer (3): Adhesive layer (4), metallic luster transfer layer (5), second coat resin layer

Claims (1)

[Scope of Claims] 1. A double-sided gold and silver thread, characterized in that it is a slit thread of a sheet-like material having a metallic luster transfer layer on both sides of a silk fabric. 2. The double-sided gold and silver thread according to claim 1, further comprising a primer layer provided between the silk fabric and the metallic luster transfer layer. 3. The double-sided gold and silver thread according to claim 1, wherein an adhesive layer is provided between the silk fabric and the metallic luster transfer layer. 4. The double-sided gold and silver thread according to claim 1, wherein a primer layer and an adhesive layer are provided between the silk fabric and the metallic luster transfer layer. 5. The double-sided gold and silver thread according to claim 1, further comprising an overcoat resin layer on the metallic luster transfer layer.