JPH01257048A - Vessel with metallic lid - Google Patents
Vessel with metallic lidInfo
- Publication number
- JPH01257048A JPH01257048A JP63084823A JP8482388A JPH01257048A JP H01257048 A JPH01257048 A JP H01257048A JP 63084823 A JP63084823 A JP 63084823A JP 8482388 A JP8482388 A JP 8482388A JP H01257048 A JPH01257048 A JP H01257048A
- Authority
- JP
- Japan
- Prior art keywords
- ethylene
- vinyl alcohol
- alcohol copolymer
- vessel
- container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔発明の目的〕
（産業上の利用分野）
本発明はプラスチック製容器本体と金属蓋とからなる金
属蓋付容器に関する。DETAILED DESCRIPTION OF THE INVENTION [Object of the Invention] (Field of Industrial Application) The present invention relates to a container with a metal lid, which is composed of a plastic container body and a metal lid.
（従来の技術）
金属性の容器、例えば金属缶は種々の形態を有するもの
があるが、缶体の構造から３ピ一ス缶と２ピ一ス缶とに
区分することができる。３ピ一ス缶はブリキハンダ缶と
も言われ、円筒状胴部とふた及び底部を二重巻締めで密
封した構造である。(Prior Art) Metal containers, such as metal cans, have various shapes, but can be classified into three-piece cans and two-piece cans based on the structure of the can body. A three-piece can, also known as a tin solder can, has a cylindrical body, lid, and bottom sealed with double seams.
一方、２ピ一ス缶はブリキ打抜き缶とも言われ、胴部及
び底部（容器本体）を一体成形したものにふたを二重巻
締めする構造である。On the other hand, a two-piece can is also called a stamped tin can, and has a structure in which the body and bottom (container body) are integrally molded, and the lid is double-sealed.
これら金属缶は食品包装容器として各種食品缶詰、ジュ
ース、清涼飲料、ジャム類、乾燥食品等の容器に使用さ
れ、密封、保存機能が特に優れた剛性容器である。しか
しながら、金属缶には、下記のような改善すべき点があ
る。即ち、■ 金属缶であるために、軽量化に限界があ
る。These metal cans are used as food packaging containers for various canned foods, juices, soft drinks, jams, dried foods, etc., and are rigid containers with particularly excellent sealing and preservation functions. However, metal cans have the following points to be improved. That is, (1) Since it is a metal can, there is a limit to its weight reduction.
■ 衝撃を受けた時、−度つぶれると復元性がなく変形
してしまう。■ When subjected to impact, if it is crushed by a certain degree, it will not recover and will be deformed.
■ プラスチック製容器に比べて、その製造上のエネル
ギーコストが高い。■ Compared to plastic containers, the energy cost of manufacturing them is higher.
■ 容器外装のデイスプレィ効果が、金属の場合、自由
に変えることができず、外装手段は印刷によるしかない
。■ If the container exterior is made of metal, the display effect cannot be changed freely, and the only means of exterior packaging is printing.
■ 内容物を開缶せずに確認できるような透明容器をつ
くることは不可能である。■ It is impossible to create transparent containers that allow the contents to be checked without opening the can.
このような従来の金属缶における欠点を解決するため、
プラスチック製の容器本体に金属蓋を取付けてなる金属
蓋付容器が考えられている。In order to solve these drawbacks of conventional metal cans,
Containers with metal lids are being considered, which are made by attaching a metal lid to a plastic container body.
また、プラスチック製の容器本体に金属蓋を取付ける場
合、容器本体のフランジ部に金属蓋の周縁部を巻締めて
取付けている。Furthermore, when a metal lid is attached to a plastic container body, the peripheral edge of the metal lid is wrapped around the flange portion of the container body.
この容器本体は、一般に次のようにして形成される。す
なわち、プラスチック製の積層シートを加熱し、金型を
用いて熱成形法により複数の容器本体からなる成形品を
形成する。その後、この成形品は切断され、個々の容器
本体毎に分離される。This container body is generally formed as follows. That is, a plastic laminated sheet is heated and a molded article consisting of a plurality of container bodies is formed by thermoforming using a mold. Thereafter, this molded product is cut and separated into individual container bodies.
また積層シートの層構成としては、例えばポリプロピレ
ン／接着層／エチレン・ビニルアルコール共重合体／接
着層／ポリプロピレン；等が用いられている。The layer structure of the laminated sheet includes, for example, polypropylene/adhesive layer/ethylene-vinyl alcohol copolymer/adhesive layer/polypropylene.
この層構成のうち、ポリプロピレンは水蒸気バリヤ性を
高める機能を有し、さらにガスバリヤ性を高めるものと
してエチレン・ビニルアルコール共重合体（以下ＥＶＯ
Ｈ）層が用いられている。Of this layer structure, polypropylene has the function of increasing water vapor barrier properties, and ethylene vinyl alcohol copolymer (hereinafter referred to as EVO) has the function of increasing water vapor barrier properties.
H) layer is used.
このように、ガスバリヤ性の高いＥＶＯＨ層を含む積層
シートで容器本体を形成することにより、容器本体内の
内容物の保存性を高めることができる。In this way, by forming the container body from a laminated sheet containing an EVOH layer with high gas barrier properties, the storage life of the contents within the container body can be improved.
（発明が解決しようとする課題）
上述のように、容器本体内の内容物の保存性を高めるた
めに、ガスバリヤ性の高いＥＶＯＨを含む積層シートに
よって容器本体が形成されている。(Problems to be Solved by the Invention) As described above, the container body is formed of a laminated sheet containing EVOH with high gas barrier properties in order to improve the storage life of the contents within the container body.
しかしながら、このＥＶＯＨ層は水分を含むとそのガス
バリヤ性が急速に低下する性質がある。However, when this EVOH layer contains moisture, its gas barrier properties tend to deteriorate rapidly.
このため、ＥＶＯＨ層に外気または内容物から水分が混
入するとガスバリヤ性が低下し、これによって金属蓋付
容器の保存性も低下してしまう。For this reason, if moisture from the outside air or the contents gets mixed into the EVOH layer, the gas barrier properties will be reduced, and the storage stability of the container with a metal lid will also be reduced.
本発明はこのような点を考慮してなされたものであり、
ＥＶＯＨ層の水分を確実に除去して金属蓋付容器の保存
性を高めることができる金属蓋付容器を提供することを
目的とする。The present invention has been made in consideration of these points,
An object of the present invention is to provide a container with a metal lid that can improve the storage life of the container with a metal lid by reliably removing moisture from an EVOH layer.
（課題を解決するための手段）
本発明は容器本体のフランジ部に金属蓋の周縁部を巻締
めてなる金属蓋付容器であって、前記容器本体はエチレ
ン−ビニルアルコール共重合体層を含むプラスチックで
形成されるとともに、このエチレンビニルアルコール共
重合体層に乾燥剤が混在されていることを特徴としてい
る。(Means for Solving the Problems) The present invention provides a container with a metal lid in which a peripheral portion of a metal lid is wrapped around a flange portion of a container body, the container body including an ethylene-vinyl alcohol copolymer layer. It is characterized by being made of plastic and having a desiccant mixed in this ethylene vinyl alcohol copolymer layer.
（作 用）
プラスチック製容器本体のエチレン・ビニルアルコール
共重合体層に乾燥剤が混在されているので、エチレン・
ビニルアルコール共重合体層が水分によってガスバリヤ
性が低下することはない。(Function) Since a desiccant is mixed in the ethylene/vinyl alcohol copolymer layer of the plastic container body, ethylene/vinyl alcohol
The gas barrier properties of the vinyl alcohol copolymer layer do not deteriorate due to moisture.
（実施例）
以下、図面を参照して本発明の実施例について説明する
。(Example) Hereinafter, an example of the present invention will be described with reference to the drawings.
第１図乃至第４図は本発明による金属蓋付容器の一実施
例を示す図である。1 to 4 are diagrams showing an embodiment of a container with a metal lid according to the present invention.
第１図に示すように、金属蓋付容器１０は、プラスチッ
ク製容器本体１４のフランジ部１５に、アルミニウム製
またはブリキ製の金属蓋の周縁部１２を巻締めて構成さ
れる。As shown in FIG. 1, the metal lidded container 10 is constructed by wrapping a peripheral edge 12 of a metal lid made of aluminum or tin plate around a flange 15 of a plastic container body 14.
次にプラスチック製容器本体１４の製造工程の概略を、
第２図乃至第４図で説明する。Next, the outline of the manufacturing process of the plastic container body 14 is as follows.
This will be explained with reference to FIGS. 2 to 4.
まず、−船釣な熱成形法により容器形成に必要な厚みを
有するプラスチック製の積層シート２１を加熱機２２で
加熱し、金型２３を用いて一般的な成形法により成形品
２４を成形する。成形方法は、圧空成形、真空成形又は
その併用の何れであってもよい（工程（Ａ））。First, a plastic laminated sheet 21 having a thickness necessary for forming a container is heated by a heating machine 22 using a typical thermoforming method, and a molded product 24 is formed using a mold 23 using a general molding method. . The molding method may be air pressure molding, vacuum molding, or a combination thereof (step (A)).
容器本体１４を形成するプラスチック製の積層シート２
１は、食品保存用容器を製造する場合は、酸素ガス、水
蒸気の透過率が少なくなるように構成されたプラスチッ
ク製の積層シートとなっている。Plastic laminated sheet 2 forming the container body 14
1 is a plastic laminated sheet configured to have low oxygen gas and water vapor permeability when manufacturing food storage containers.
例えば積層シート２１の層構成として、次のようなもの
が挙げられる。For example, the layer structure of the laminated sheet 21 may be as follows.
ポリプロピレン／接着層／エチレン・ビニルアルコール
共重合体（ＥＶＯＨ）／接若層／ポリプロピレン；
ポリスチレン／接着層／エチレン・ビニルアルコール共
重合体（ＥＶＯＨ）／接着層／ポリスチレン；
等である。Polypropylene/adhesive layer/ethylene/vinyl alcohol copolymer (EVOH)/adhesive layer/polypropylene; polystyrene/adhesive layer/ethylene/vinyl alcohol copolymer (EVOH)/adhesive layer/polystyrene; and the like.
そして、これらの層構成のうち、ＥＶＯＨ層内にはあら
かじめ乾燥剤、例えばＣａ Ｃ，１！ ２、Ｃａｂ、Ｎ
ａ（Ｊ） 、Ｎａ４ＰＯ４等が混在されている。Of these layer configurations, a desiccant such as Ca C, 1! is added in advance to the EVOH layer. 2, Cab, N
a(J), Na4PO4, etc. are mixed.
すなわち、これらの乾燥剤は共押出しによって積層シー
ト２１を形成する際にＥＶＯＨ層に混在させておく。That is, these desiccants are mixed in the EVOH layer when forming the laminated sheet 21 by coextrusion.
工程（Ａ）において成形された成形品２４は、そのフラ
ンジ部１５が厚すぎて二重巻締めに適さない。このため
、フランジ部１５を熱プレスして、フランジ部１５の厚
みを薄くすると同時に精度を向上させる必要がある。The molded product 24 molded in step (A) has a flange portion 15 that is too thick and is not suitable for double seaming. For this reason, it is necessary to heat press the flange portion 15 to reduce the thickness of the flange portion 15 and at the same time improve accuracy.
即ち、成形された容器本体１４を第３図に示すようにキ
ャビティ２つ内に入れる。キャビティ２９内は加熱され
ており、さらに離型性を良くするために、表面はテフロ
ン加工等の処理がなされている。次いで上部より加熱さ
れたプラグ３０が下降し、フランジ部１５を押潰ず（第
３図）。That is, the molded container body 14 is placed into two cavities as shown in FIG. The inside of the cavity 29 is heated, and the surface is treated with Teflon or the like to further improve mold release properties. Then, the heated plug 30 descends from above without crushing the flange portion 15 (FIG. 3).
この場合プラグ３０の駆動は油圧でもエアー圧でも良い
。フランジ部１５が所定の厚さになった時点で、プラグ
３０は上昇し、プレスによるフランジ潰しは終了する（
工程（Ｂ））。In this case, the plug 30 may be driven by hydraulic pressure or air pressure. When the flange portion 15 reaches a predetermined thickness, the plug 30 rises and the flange crushing by the press ends (
Step (B)).
工程（Ｂ）において、フランジ部１５を所定の厚みに調
整した成型品２４は、刃３３を有するプラグ３４によっ
てフランジ幅が所定の幅となるように打抜かれる（工程
（Ｃ））。In step (B), the molded product 24 with the flange portion 15 adjusted to a predetermined thickness is punched out using a plug 34 having a blade 33 so that the flange width becomes a predetermined width (step (C)).
このようにして、プラスチック製容器本体１４が作成さ
れる。そして、この容器本体１４内に内容物１６が充填
され、容器本体１４のフランジ部１５に金属蓋１１の周
縁部１２が巻締められて金属蓋付容器１０が製造される
。In this way, the plastic container body 14 is created. Then, the container body 14 is filled with the contents 16, and the peripheral edge 12 of the metal lid 11 is wrapped around the flange portion 15 of the container body 14, thereby manufacturing the container 10 with a metal lid.
本実施例によれば、容器１４を形成する積層シート２１
のうち、ＥＶＯＨ層内にあらかじめ乾燥剤が混在されて
いるので、ＥＶＯＨ層に混入する水分を確実に除去する
ことができる。このため、水分によってＥＶＯＨ層のガ
スバリヤ性が低下することはなく、金属蓋付容器１０の
内容物１６の保存性の向上を図ることができる。According to this embodiment, the laminated sheet 21 forming the container 14
Since the desiccant is mixed in the EVOH layer in advance, moisture mixed in the EVOH layer can be reliably removed. Therefore, the gas barrier properties of the EVOH layer are not deteriorated by moisture, and the storage stability of the contents 16 of the container 10 with a metal lid can be improved.
以上説明したように、本発明によれば、プラスチック製
容器本体のエチレン・ビニルアルコール共重合体層に乾
燥剤が混在されているので、水分によるエチレンφビニ
ルアルコール共重合体層のガスバリヤ性の低下を確実に
防止することができる。このため、金属蓋付容器の保存
性の維持向上を図ることができる。As explained above, according to the present invention, since a desiccant is mixed in the ethylene/vinyl alcohol copolymer layer of the plastic container body, the gas barrier properties of the ethylene/vinyl alcohol copolymer layer are reduced due to moisture. can be reliably prevented. Therefore, it is possible to maintain and improve the shelf life of the container with a metal lid.
第１図は本発明による金属蓋付容器の一実施例を示す側
断面図であり、第２図は容器本体の製造工程を示す概略
図であり、第３図は容器本体のフランジ部を薄くする工
程を示す側断面図であり、第４図は容器本体のフランジ
部を所定の幅とするよう打抜く工程を示す側断面図であ
る。
１０・・・金属蓋付容器、１１・・・金属蓋、１２・・
・周縁部、１４・・・容器本体、１５・・・フランジ部
、１６・・・内容物、２１・・・積層シート、２２・・
・加熱機、２３・・・金型、２４・・・成型品、２９・
・・キャビティ、３０・・・プラグ、３３・・・刃、３
４・・・プラグ。
出願人代理人 佐 藤 −雄Fig. 1 is a side sectional view showing an embodiment of a container with a metal lid according to the present invention, Fig. 2 is a schematic diagram showing the manufacturing process of the container main body, and Fig. 3 is a thinner flange portion of the container main body. FIG. 4 is a side sectional view showing the step of punching out the flange portion of the container body to a predetermined width. 10...Container with metal lid, 11...Metal lid, 12...
- Peripheral part, 14... Container body, 15... Flange part, 16... Contents, 21... Laminated sheet, 22...
・Heating machine, 23... Mold, 24... Molded product, 29.
...Cavity, 30...Plug, 33...Blade, 3
4...Plug. Applicant's agent Mr. Sato
Claims (1)
金属蓋付容器において、前記容器本体はエチレン−ビニ
ルアルコール共重合体層を含むプラスチックで形成され
るとともに、このエチレンビニルアルコール共重合体層
に乾燥剤が混在されていることを特徴とする金属蓋付容
器。In a container with a metal lid, in which the peripheral edge of a metal lid is wrapped around the flange of the container body, the container body is made of plastic containing an ethylene-vinyl alcohol copolymer layer, and the container body is made of plastic containing an ethylene-vinyl alcohol copolymer layer. A container with a metal lid characterized in that a desiccant is mixed in the layer.