JP7444503B1 - fatty acid ester - Google Patents
fatty acid ester Download PDFInfo
- Publication number
- JP7444503B1 JP7444503B1 JP2023073667A JP2023073667A JP7444503B1 JP 7444503 B1 JP7444503 B1 JP 7444503B1 JP 2023073667 A JP2023073667 A JP 2023073667A JP 2023073667 A JP2023073667 A JP 2023073667A JP 7444503 B1 JP7444503 B1 JP 7444503B1
- Authority
- JP
- Japan
- Prior art keywords
- fatty acid
- formula
- alcohol
- acid ester
- mol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】新規な脂肪酸エステルを提供する。【解決手段】脂肪酸エステルを形成する混合脂肪酸が、下記式（１）で表される脂肪酸及び下記式（２）で表される脂肪酸を、式（１）：式（２）のモル比が１０～６５：３５～９０で含み、芳香族脂肪酸を０．０１～１モル％含む、脂肪酸エステルとする。TIFF0007444503000022.tif2682（１）TIFF0007444503000023.tif2862（２）【選択図】なし[Object] To provide a novel fatty acid ester. [Solution] A mixed fatty acid forming a fatty acid ester contains a fatty acid represented by the following formula (1) and a fatty acid represented by the following formula (2) at a molar ratio of formula (1):formula (2) of 10. to 65:35 to 90, and contains 0.01 to 1 mol% of aromatic fatty acid, which is a fatty acid ester. TIFF0007444503000022.tif2682 (1) TIFF0007444503000023.tif2862 (2) [Selection diagram] None
Description
本発明は、脂肪酸エステル等に関する。 The present invention relates to fatty acid esters and the like.
イソステアリン酸エステル等の分岐脂肪酸エステルは、潤滑油等の種々の用途に使用されている。
例えば、特許文献１には、多分岐脂肪酸又はそのエステルを含み、環状化合物を特定割合で含む組成物が開示されている。
Branched fatty acid esters such as isostearate esters are used in various applications such as lubricating oils.
For example, Patent Document 1 discloses a composition containing a hyperbranched fatty acid or an ester thereof and a cyclic compound in a specific proportion.
本発明の目的は、新規な脂肪酸エステル等を提供することである。 An object of the present invention is to provide novel fatty acid esters and the like.
本発明の他の目的は、低粘度性を有する脂肪酸エステルを提供することである。 Another object of the present invention is to provide fatty acid esters with low viscosity.
本発明の他の目的は、優れた低温流動性を有する脂肪酸エステルを提供することである。 Another object of the present invention is to provide fatty acid esters with excellent cold flow properties.
本発明の他の目的は、良好な潤滑性を有する潤滑油用組成物を提供することである。 Another object of the present invention is to provide a lubricating oil composition having good lubricity.
本発明の他の目的は、良好な保存安定性を有する脂肪酸エステルを提供することである。 Another object of the present invention is to provide fatty acid esters with good storage stability.
本発明者らは、種々の分岐脂肪酸エステルの中でも、特定の構造の脂肪酸（多分岐脂肪酸）を高割合で含む［さらには、特定の構造の脂肪酸（単分岐脂肪酸及び芳香族脂肪酸）を特定割合で含む］混合脂肪酸を用いて脂肪酸エステルを形成することにより、脂肪酸エステルの動粘度を効率よく低くしうること等を見出し、さらに鋭意研究を重ね、本発明を完成させた。 The present inventors found that among various branched fatty acid esters, fatty acids with a specific structure (hyperbranched fatty acids) are contained in a high proportion [furthermore, fatty acids with a specific structure (monobranched fatty acids and aromatic fatty acids) are contained in a specific proportion]. The present inventors have discovered that the kinematic viscosity of fatty acid esters can be efficiently lowered by forming fatty acid esters using mixed fatty acids, and after further intensive research, they have completed the present invention.
一般的に、脂肪酸エステルを形成する脂肪酸中の分岐率が高い（単分岐脂肪酸の割合が低い）ほど、脂肪酸エステルの動粘度は高くなると考えられている中、本願発明では動粘度を効率よく低くしうることは極めて予想外であった。 Generally, it is believed that the higher the branching rate (lower the proportion of monobranched fatty acids) in the fatty acids that form the fatty acid ester, the higher the kinematic viscosity of the fatty acid ester.However, the present invention efficiently lowers the kinematic viscosity. What could have happened was extremely unexpected.
なお、本発明者らは、特許文献１に記載の組成物では、動粘度が高くなる場合があるのに対し、本願発明では、動粘度を低くしうること等も見出した。 In addition, the present inventors have also discovered that while the composition described in Patent Document 1 may have a high kinematic viscosity, the present invention can lower the kinematic viscosity.
本発明は、以下の脂肪酸エステル等に関する。
［１］
脂肪酸エステルを形成する混合脂肪酸が、下記式（１）で表される脂肪酸及び下記式（２）で表される脂肪酸を、式（１）で表される脂肪酸：式（２）で表される脂肪酸のモル比が１０～６５：３５～９０で含み、下記式（３）で表される脂肪酸を０．０１～１モル％含む、脂肪酸エステル。
The present invention relates to the following fatty acid esters, etc.
[1]
The mixed fatty acids forming the fatty acid ester include a fatty acid represented by the following formula (1) and a fatty acid represented by the following formula (2), a fatty acid represented by the formula (1): a fatty acid represented by the formula (2) A fatty acid ester containing a fatty acid molar ratio of 10 to 65:35 to 90, and containing 0.01 to 1 mol% of a fatty acid represented by the following formula (3).
（式（１）中、ｊ及びｋは、ｊ＋ｋ＝１３を満たす０～１３の整数を示す。）
(In formula (1), j and k represent integers from 0 to 13 that satisfy j+k=13.)
（式（２）中、ｌは、式（２）の炭素数の合計が１８を満たす８～１３の整数を示し、
Ｒ１は、Ｈ又はＣＨ３を示す。
ただし、ｌ個のＲ１は同一又は異なり、ｌ個中少なくとも２個のＲ１がＣＨ３を示す。）
(In formula (2), l represents an integer from 8 to 13 where the total number of carbon atoms in formula (2) satisfies 18,
R1 represents H or CH3 .
However, 1 R 1 's are the same or different, and at least 2 R 1 's out of 1 represent CH 3 . )
（式（３）中、Ｒ２、Ｒ３、Ｒ４、Ｒ５、Ｒ６及びＲ７は、Ｈ、（ａ）又は（ｂ）を示し、（ａ）及び（ｂ）をそれぞれ１つずつ含む。）
(In formula (3), R 2 , R 3 , R 4 , R 5 , R 6 and R 7 represent H, (a) or (b), and one each of (a) and (b) include.)
（式（ａ）及び（ｂ）中、ｍ及びｎは、式（３）の炭素数の合計が１８、及びｍ＋ｎ≦９を満たす０～９の整数を示す。
ただし、Ｒ8及びＲ9は、Ｈ又はＣＨ３を示し、ｍ個のＲ8は、同一又は異なり、ｎ個のＲ9は、同一又は異なる。）
［２］
脂肪酸エステルを形成するアルコールが、脂肪族アルコールを含む、［１］記載の脂肪酸エステル。
［３］
脂肪酸エステルを形成するアルコールが、１価アルコール、２価アルコール又は３価以上のアルコールを含む、［１］又は［２］記載の脂肪酸エステル。
［４］
脂肪酸エステルを形成するアルコールが、（１）グリセリン又はポリグリセリン、（２）ネオペンチルポリオール又は（３）糖アルコールを含む、［１］～［３］のいずれか記載の脂肪酸エステル。
［５］
流動点が２０℃以下である、［１］～［４］のいずれか記載の脂肪酸エステル。
［６］
［１］～［５］のいずれか記載の脂肪酸エステルを含む組成物。
［７］
［１］～［６］のいずれか記載の脂肪酸エステル又は組成物を含む、潤滑油用組成物。
［８］
［１］～［６］のいずれか記載の脂肪酸エステル又は組成物を含む、化粧品用組成物。
［９］
［１］～［６］のいずれか記載の脂肪酸エステル又は組成物を含む、樹脂用組成物。
(In formulas (a) and (b), m and n represent integers from 0 to 9 that satisfy the total number of carbon atoms in formula (3) of 18 and m+n≦9.
However, R 8 and R 9 represent H or CH 3 , m R 8 are the same or different, and n R 9 are the same or different. )
[2]
The fatty acid ester according to [1], wherein the alcohol forming the fatty acid ester includes an aliphatic alcohol.
[3]
The fatty acid ester according to [1] or [2], wherein the alcohol forming the fatty acid ester includes a monohydric alcohol, a dihydric alcohol, or a trivalent or higher alcohol.
[4]
The fatty acid ester according to any one of [1] to [3], wherein the alcohol forming the fatty acid ester includes (1) glycerin or polyglycerin, (2) neopentyl polyol, or (3) sugar alcohol.
[5]
The fatty acid ester according to any one of [1] to [4], which has a pour point of 20°C or less.
[6]
A composition comprising the fatty acid ester according to any one of [1] to [5].
[7]
A lubricating oil composition comprising the fatty acid ester or composition according to any one of [1] to [6].
[8]
A cosmetic composition comprising the fatty acid ester or composition according to any one of [1] to [6].
[9]
A resin composition comprising the fatty acid ester or composition according to any one of [1] to [6].
本発明によれば、新規な脂肪酸エステルを提供できる。
このような脂肪酸エステルは、動粘度を効率よく低くしうる。このような脂肪酸エステルは、潤滑油等に好適に使用しうる。
According to the present invention, a novel fatty acid ester can be provided.
Such fatty acid esters can efficiently lower kinematic viscosity. Such fatty acid esters can be suitably used in lubricating oils and the like.
本発明の一態様の脂肪酸エステルでは、流動点を効率よく低くしうる。このような脂肪酸エステルは、潤滑油等に好適に使用しうる。 The fatty acid ester of one embodiment of the present invention can efficiently lower the pour point. Such fatty acid esters can be suitably used in lubricating oils and the like.
本発明の一態様の脂肪酸エステルは、良好な潤滑性を奏しうる。 The fatty acid ester of one embodiment of the present invention can exhibit good lubricity.
本発明の一態様の脂肪酸エステルは、良好な保存安定性を奏しうる。 The fatty acid ester of one embodiment of the present invention can exhibit good storage stability.
本発明の一態様の脂肪酸エステルは、化粧品に配合した際に優れた使用感を得られる。 The fatty acid ester of one embodiment of the present invention provides an excellent feeling of use when blended into cosmetics.
特許文献１より、潤滑油用途で使用される脂肪酸エステルの流動点は低いほど良いとされる。 According to Patent Document 1, the lower the pour point of the fatty acid ester used in lubricating oil applications, the better.
［脂肪酸エステル］
本発明の脂肪酸エステルは、通常、脂肪酸とアルコールとのエステルである。
[Fatty acid ester]
The fatty acid ester of the present invention is usually an ester of a fatty acid and an alcohol.
脂肪酸
脂肪酸エステルを形成する脂肪酸は、混合脂肪酸であってよい。
混合脂肪酸は、通常、特定の脂肪酸（１）、脂肪酸（２）及び脂肪酸（３）を含む。
The fatty acids forming the fatty acid fatty acid ester may be mixed fatty acids.
Mixed fatty acids usually include specific fatty acids (1), fatty acids (2) and fatty acids (3).
脂肪酸（１）は、例えば、下記式（１）で表される脂肪酸であってよい。 The fatty acid (1) may be, for example, a fatty acid represented by the following formula (1).
（式（１）中、ｊ及びｋは、ｊ＋ｋ＝１３を満たす０～１３の整数を示す。）
(In formula (1), j and k represent integers from 0 to 13 that satisfy j+k=13.)
なお、式（１）で表される脂肪酸は、単分岐イソステアリン酸ということができる。 Note that the fatty acid represented by formula (1) can be called monobranched isostearic acid.
脂肪酸（１）は、後述の実施例に記載の測定条件のガスクロマトグラフィー測定において、保持時間が５．８～６．４分の範囲のピークに対応していてもよい。 Fatty acid (1) may correspond to a peak with a retention time in the range of 5.8 to 6.4 minutes in gas chromatography measurement under the measurement conditions described in Examples below.
なお、ガスクロマトグラフィーの測定方法は、特に限定されず、公知の方法を使用することができる。 Note that the gas chromatography measurement method is not particularly limited, and any known method can be used.
脂肪酸（２）は、例えば、下記式（２）で表される脂肪酸であってよい。 The fatty acid (2) may be, for example, a fatty acid represented by the following formula (2).
（式（２）中、ｌは、式（２）の炭素数の合計が１８を満たす８～１３の整数を示し、
Ｒ１は、Ｈ又はＣＨ３を示す。
ただし、ｌ個のＲ１は同一又は異なり、ｌ個中少なくとも２個のＲ１がＣＨ３を示す。）
(In formula (2), l represents an integer from 8 to 13 where the total number of carbon atoms in formula (2) satisfies 18,
R1 represents H or CH3 .
However, 1 R 1 's are the same or different, and at least 2 R 1 's out of 1 represent CH 3 . )
なお、式（２）で表される脂肪酸は、多分岐イソステアリン酸ということができる。 Note that the fatty acid represented by formula (2) can be called multibranched isostearic acid.
脂肪酸（２）は、後述の実施例に記載の測定条件のガスクロマトグラフィー測定において、保持時間が４．７～５．８分の範囲のピークに対応していてもよい。 Fatty acid (2) may correspond to a peak with a retention time in the range of 4.7 to 5.8 minutes in gas chromatography measurement under the measurement conditions described in Examples below.
脂肪酸（３）は、例えば、下記式（３）で表される脂肪酸であってよい。 The fatty acid (3) may be, for example, a fatty acid represented by the following formula (3).
（式（３）中、Ｒ２、Ｒ３、Ｒ４、Ｒ５、Ｒ６及びＲ７は、Ｈ、（ａ）又は（ｂ）を示し、（ａ）及び（ｂ）をそれぞれ１つずつ含む。）
(In formula (3), R 2 , R 3 , R 4 , R 5 , R 6 and R 7 represent H, (a) or (b), and one each of (a) and (b) include.)
（式（ａ）及び（ｂ）中、ｍ及びｎは、式（３）の炭素数の合計が１８、及びｍ＋ｎ≦９を満たす０～９の整数を示す。
ただし、Ｒ8及びＲ9は、Ｈ又はＣＨ３を示し、ｍ個のＲ8は、同一又は異なり、ｎ個のＲ9は、同一又は異なる。）
(In formulas (a) and (b), m and n represent integers from 0 to 9 that satisfy the total number of carbon atoms in formula (3) of 18 and m+n≦9.
However, R 8 and R 9 represent H or CH 3 , m R 8 are the same or different, and n R 9 are the same or different. )
脂肪酸（３）は、例えば、１Ｈ－ＮＭＲ測定やＭＳ測定によって確認することができる。
１Ｈ－ＮＭＲおよびＭＳの測定方法としては、特に限定されず、公知の方法を使用してよい。
Fatty acid (3) can be confirmed, for example, by 1 H-NMR measurement or MS measurement.
1 H-NMR and MS measurement methods are not particularly limited, and known methods may be used.
混合脂肪酸における脂肪酸（１）の含有量は、脂肪酸エステルの動粘度を効率よく低くしうる、流動点を効率よく低くしうる等の観点から、例えば、６５モル％以下（例えば、６０モル％以下）、好ましくは５５モル％以下（例えば、５０モル％以下）、より好ましくは４５モル％以下（例えば、４０モル％以下）程度であってよく、例えば、１０モル％以上、１５モル％以上、２０モル％以上、２５モル％以上、３０モル％以上、３５モル％以上程度であってよい。 The content of fatty acid (1) in the mixed fatty acid is, for example, 65 mol% or less (for example, 60 mol% or less) from the viewpoint of efficiently lowering the kinematic viscosity of the fatty acid ester and efficiently lowering the pour point. ), preferably about 55 mol% or less (for example, 50 mol% or less), more preferably about 45 mol% or less (for example, 40 mol% or less), for example, 10 mol% or more, 15 mol% or more, It may be approximately 20 mol% or more, 25 mol% or more, 30 mol% or more, or 35 mol% or more.
なお、これらの範囲（上限値と下限値）を適宜組み合わせて範囲を選択してもよい（例えば、１０～６５モル％等）。 Note that the range may be selected by appropriately combining these ranges (upper limit and lower limit) (for example, 10 to 65 mol%, etc.).
混合脂肪酸における脂肪酸（１）の含有量は、脂肪酸エステルの動粘度を効率よく低くしうる、流動点を効率よく低くしうる等の観点から、例えば、６５重量％以下（例えば、６０重量％以下）、好ましくは５５重量％以下（例えば、５０重量％以下）、より好ましくは４５重量％以下（例えば、４０重量％以下）程度であってよく、例えば、１０重量％以上、１５重量％以上、２０重量％以上、２５重量％以上、３０重量％以上、３５重量％以上程度であってよい。 The content of fatty acid (1) in the mixed fatty acid is, for example, 65% by weight or less (for example, 60% by weight or less) from the viewpoint of efficiently lowering the kinematic viscosity of the fatty acid ester and efficiently lowering the pour point. ), preferably 55% by weight or less (for example, 50% by weight or less), more preferably about 45% by weight or less (for example, 40% by weight or less), for example, 10% by weight or more, 15% by weight or more, It may be approximately 20% by weight or more, 25% by weight or more, 30% by weight or more, or 35% by weight or more.
なお、これらの範囲（上限値と下限値）を適宜組み合わせて範囲を選択してもよい（例えば、１０～６５重量％等）。 Note that the range may be selected by appropriately combining these ranges (upper limit and lower limit) (for example, 10 to 65% by weight, etc.).
混合脂肪酸における脂肪酸（２）の含有量は、脂肪酸エステルの動粘度を効率よく低くしうる、流動点を効率よく低くしうる等の観点から、例えば、３５モル％以上（例えば、４０モル％以上）、好ましくは４５モル％以上（例えば、５０モル％以上）、より好ましくは５５モル％以上（例えば、６０モル％以上）程度であってよく、例えば、９０モル％以下、８５モル％以下、８０モル％以下、７５モル％以下、７０モル％以下、６５モル％以下程度であってよい。 The content of fatty acid (2) in the mixed fatty acid is, for example, 35 mol% or more (for example, 40 mol% or more) from the viewpoint of efficiently lowering the kinematic viscosity of the fatty acid ester and efficiently lowering the pour point. ), preferably 45 mol% or more (for example, 50 mol% or more), more preferably 55 mol% or more (for example, 60 mol% or more), for example, 90 mol% or less, 85 mol% or less, It may be about 80 mol% or less, 75 mol% or less, 70 mol% or less, or about 65 mol% or less.
なお、これらの範囲（上限値と下限値）を適宜組み合わせて範囲を選択してもよい（例えば、３５～９０モル％等）。 Note that the range may be selected by appropriately combining these ranges (upper limit and lower limit) (for example, 35 to 90 mol%, etc.).
混合脂肪酸における脂肪酸（２）の含有量は、脂肪酸エステルの動粘度を効率よく低くしうる、流動点を効率よく低くしうる等の観点から、例えば、３５重量％以上（例えば、４０重量％以上）、好ましくは４５重量％以上（例えば、５０重量％以上）、より好ましくは５５重量％以上（例えば、６０重量％以上）程度であってよく、例えば、９０重量％以下、８５重量％以下、８０重量％以下、７５重量％以下、７０重量％以下、６５重量％以下程度であってよい。 The content of fatty acid (2) in the mixed fatty acid is, for example, 35% by weight or more (for example, 40% by weight or more) from the viewpoint of efficiently lowering the kinematic viscosity of the fatty acid ester and efficiently lowering the pour point. ), preferably 45% by weight or more (for example, 50% by weight or more), more preferably about 55% by weight or more (for example, 60% by weight or more), for example, 90% by weight or less, 85% by weight or less, It may be about 80% by weight or less, 75% by weight or less, 70% by weight or less, or about 65% by weight or less.
なお、これらの範囲（上限値と下限値）を適宜組み合わせて範囲を選択してもよい（例えば、３５～９０重量％等）。 Note that a range may be selected by appropriately combining these ranges (upper limit and lower limit) (for example, 35 to 90% by weight, etc.).
混合脂肪酸における脂肪酸（３）の割合は、特に限定されないが、脂肪酸エステルの動粘度を効率よく低くしうる、流動点を効率よく低くしうる等の観点から、０．０１モル％から１モル％が好ましく、例えば、０．９モル％以下、好ましくは０．８モル％以下、更に好ましくは、０．７モル％以下程度であってもよく、例えば、０．０１モル％以上、０．０２モル％以上、０．０３モル％以上程度であってもよい。 The proportion of fatty acid (3) in the mixed fatty acid is not particularly limited, but from the viewpoint of efficiently lowering the kinematic viscosity of the fatty acid ester and efficiently lowering the pour point, it is from 0.01 mol% to 1 mol%. is preferable, for example, 0.9 mol% or less, preferably 0.8 mol% or less, more preferably 0.7 mol% or less, for example, 0.01 mol% or more, 0.02 mol% or less. It may be about mol% or more, and about 0.03 mol% or more.
なお、これらの範囲（上限値と下限値）を適宜組み合わせて範囲を選択してもよい（例えば、０．０１～１モル％、０．５～０．８モル％等）。 Note that the range may be selected by appropriately combining these ranges (upper limit value and lower limit value) (for example, 0.01 to 1 mol%, 0.5 to 0.8 mol%, etc.).
混合脂肪酸における脂肪酸（３）の割合は、特に限定されないが、脂肪酸エステルの動粘度を効率よく低くしうる、流動点を効率よく低くしうる等の観点から、０．０１重量％から１重量％が好ましく、例えば、０．９重量％以下、好ましくは０．８重量％以下、更に好ましくは、０．７重量％以下程度であってもよく、例えば、０．０１重量％以上、０．０２重量％以上、０．０３重量％以上程度であってもよい。 The proportion of fatty acid (3) in the mixed fatty acid is not particularly limited, but from the viewpoint of efficiently lowering the kinematic viscosity of the fatty acid ester and efficiently lowering the pour point, it is 0.01% by weight to 1% by weight. is preferable, for example, 0.9% by weight or less, preferably 0.8% by weight or less, more preferably 0.7% by weight or less, for example, 0.01% by weight or more, 0.02% by weight or less. It may be about 0.03% by weight or more, or about 0.03% by weight or more.
なお、これらの範囲（上限値と下限値）を適宜組み合わせて範囲を選択してもよい（例えば、０．０１～１重量％、０．５～０．８重量％等）。 Note that a range may be selected by appropriately combining these ranges (upper limit value and lower limit value) (for example, 0.01 to 1% by weight, 0.5 to 0.8% by weight, etc.).
混合脂肪酸において、脂肪酸（１）の含有量：脂肪酸（２）の含有量のモル比は、脂肪酸エステルの動粘度を効率よく低くしうる、流動点を効率よく低くしうる等の観点から、例えば、１０～６５：３５～９０、好ましくは２０～６０：４０～８０であってもよい。 In mixed fatty acids, the molar ratio of fatty acid (1) content to fatty acid (2) content is determined from the viewpoint of efficiently lowering the kinematic viscosity of the fatty acid ester, efficiently lowering the pour point, etc. , 10-65:35-90, preferably 20-60:40-80.
混合脂肪酸中の脂肪酸（１）の含有量、脂肪酸（２）の含有量、並びに、これら含有量のモル比の測定方法は、特に限定されないが、例えば、ガスクロマトグラフィーを用いて測定してもよい。ガスクロマトグラフィーの測定方法は、特に限定されず、公知の方法を使用することができる。なお、これらの含有量やモル比の測定においては、混合脂肪酸中に脂肪酸（３）、もしくは後述の他の脂肪酸が含まれていてもよい。 The method for measuring the content of fatty acid (1), the content of fatty acid (2), and the molar ratio of these contents in the mixed fatty acid is not particularly limited, but for example, it may be measured using gas chromatography. good. The measuring method of gas chromatography is not particularly limited, and any known method can be used. In addition, in measuring these contents and molar ratios, the fatty acid (3) or other fatty acids described below may be included in the mixed fatty acid.
なお、ガスクロマトグラフィーを用いて測定した混合脂肪酸中の脂肪酸（１）の含有量（割合）及び脂肪酸（２）の含有量（割合）は、通常、混合脂肪酸中の各脂肪酸のモル％及び重量％と同一（又は、対応）している。 In addition, the content (ratio) of fatty acid (1) and the content (ratio) of fatty acid (2) in the mixed fatty acid measured using gas chromatography are usually the mol% and weight of each fatty acid in the mixed fatty acid. It is the same as (or corresponds to) %.
混合脂肪酸中の脂肪酸（３）の割合は、１Ｈ－ＮＭＲ測定によって算出してもよい。例えば、後述の実施例に記載のように、式（１）～（３）及び後述の他の脂肪酸のα位の水素の積分値と、式（３）のＲ２、Ｒ３、Ｒ４、Ｒ５、Ｒ６及びＲ７中の式（ａ）及び式（ｂ）を除く水素（すなわち、芳香族領域の水素）の積分値から算出してもよい。 The proportion of fatty acid (3) in the mixed fatty acid may be calculated by 1 H-NMR measurement. For example, as described in Examples below, the integral value of hydrogen at the α-position of formulas (1) to (3) and other fatty acids described below, and R 2 , R 3 , R 4 of formula (3), It may be calculated from the integral value of hydrogen excluding formulas (a) and (b) in R 5 , R 6 and R 7 (that is, hydrogen in the aromatic region).
混合脂肪酸は、脂肪酸（１）～（３）以外の他の脂肪酸を含んでいてもよい。
他の脂肪酸は、通常、脂肪酸（１）～（３）の製造に由来する成分である。
The mixed fatty acid may contain other fatty acids than fatty acids (1) to (3).
Other fatty acids are usually components derived from the production of fatty acids (1) to (3).
他の脂肪酸としては、例えば、非芳香族脂肪酸（芳香族基を有しない脂肪酸）（例えば、脂肪酸（１）及び脂肪酸（２）以外のＣ８－２４脂肪酸、Ｃ１６－１８直鎖脂肪酸）等が挙げられる。
他の脂肪酸は、１種又は２種以上含んでいてもよい。
Other fatty acids include, for example, non-aromatic fatty acids (fatty acids that do not have an aromatic group) (for example, C 8-24 fatty acids other than fatty acids (1) and fatty acids (2), C 16-18 straight chain fatty acids), etc. can be mentioned.
One or more types of other fatty acids may be included.
混合脂肪酸が他の脂肪酸を含有する場合も、ほとんど含有していないことが好ましい。混合脂肪酸における他の脂肪酸の割合は、例えば、３モル％以下（例えば、２モル％以下、１モル％以下等）であってもよく、例えば、３重量％以下（例えば、２重量％以下、１重量％以下等）であってもよい。 Even when the mixed fatty acid contains other fatty acids, it is preferable that they contain almost no other fatty acids. The proportion of other fatty acids in the mixed fatty acid may be, for example, 3 mol% or less (for example, 2 mol% or less, 1 mol% or less, etc.), and for example, 3% by weight or less (for example, 2 mol% or less, 1% by weight or less).
混合脂肪酸としては、合成（製造）したものを使用してもよく、市販品を使用してもよく、市販品を混合したものを使用してもよい。また、混合脂肪酸は、蒸留したものを使用してもよい。なお、蒸留方法は、特に限定されず、公知の方法を使用してもよい。蒸留を行う場合、初留をカットしたものを使用してもよい。蒸留を行うことによって、式（３）の脂肪酸の含有割合が低い混合脂肪酸を効率よく得やすい。 As the mixed fatty acid, a synthesized (manufactured) one may be used, a commercially available product may be used, or a mixture of commercially available products may be used. Further, the mixed fatty acid may be distilled. Note that the distillation method is not particularly limited, and any known method may be used. When distilling, the first distillate may be cut. By performing distillation, it is easy to efficiently obtain a mixed fatty acid having a low fatty acid content of formula (3).
混合脂肪酸を合成する場合は、例えば、オレイン酸を含む混合脂肪酸を原料に、触媒としてモルデナイトを使用して異性化反応を行い、その後、水素化触媒存在下での水添反応を行い、水添後、融点差を利用して固体酸と液体酸を分別し、最後に、液体酸を蒸留して、イソステアリン酸を含む混合脂肪酸を得ることができる。 When synthesizing a mixed fatty acid, for example, an isomerization reaction is performed using a mixed fatty acid containing oleic acid as a raw material using mordenite as a catalyst, and then a hydrogenation reaction is performed in the presence of a hydrogenation catalyst. Thereafter, the solid acid and liquid acid are separated using the difference in melting point, and finally, the liquid acid is distilled to obtain a mixed fatty acid containing isostearic acid.
混合脂肪酸中は、シクロペンタノン類（例えば、アルキルシクロペンタノン）、ラクトン等を含有していないことが好ましい。
混合脂肪酸がシクロペンタノン類を含有する場合、混合脂肪酸中のシクロペンタノン類の割合は、０．１モル％以下、０．１重量％以下等が好ましい。
混合脂肪酸がラクトンを含有する場合、混合脂肪酸中のラクトンの割合は、１．０モル％以下、１．０重量％以下等が好ましい。
The mixed fatty acid preferably does not contain cyclopentanones (eg, alkylcyclopentanone), lactones, and the like.
When the mixed fatty acid contains cyclopentanones, the proportion of the cyclopentanones in the mixed fatty acid is preferably 0.1% by mole or less, 0.1% by weight or less, etc.
When the mixed fatty acid contains lactone, the proportion of lactone in the mixed fatty acid is preferably 1.0 mol% or less, 1.0% by weight or less, etc.
アルコール
脂肪酸エステルを形成するアルコール（又は、脂肪酸エステルの原料となるアルコール）としては、例えば、脂肪族アルコール（脂環式アルコールを含む）、非脂肪族アルコール（例えば、芳香族アルコール等）が挙げられるが、特に脂肪族アルコールであってもよい。
Examples of alcohols that form alcohol fatty acid esters (or alcohols that serve as raw materials for fatty acid esters) include aliphatic alcohols (including alicyclic alcohols) and non-aliphatic alcohols (e.g., aromatic alcohols, etc.) However, it may also be an aliphatic alcohol, in particular an aliphatic alcohol.
アルコールは、モノオール（一価アルコール）であってもよく、ポリオール（多価アルコール）であってもよい。なお、アルコールは、第１級、第２級、第３級、鎖状（直鎖状、分岐鎖状）、環状などのいずれであってもよく、飽和、不飽和のいずれであってもよい（特に、飽和であってもよい）。 The alcohol may be a monool (monohydric alcohol) or a polyol (polyhydric alcohol). The alcohol may be primary, secondary, tertiary, chain (linear, branched), cyclic, etc., and may be saturated or unsaturated. (In particular, it may be saturated).
代表的なアルコールとしては、例えば、脂肪族モノオール［例えば、アルカノール（例えば、メタノール、エタノール、ノルマルプロパノール、イソプロパノール、ノルマルブタノール、イソブタノール、アミルアルコール、２－エチルヘキサノール等）等］、芳香族モノオール（例えば、フェノール等）等の１価のアルコール；脂肪族ジオール［例えば、アルカンジオール（例えば、エチレングリコール、プロピレングリコール、ブチレングリコール、ネオペンチルグリコール、ヘキサンジオール等）、ポリアルキレングリコール（例えば、ジエチレングリコール、ポリエチレングリコール、ポリプロピレングリコール等）等］等の２価のアルコール；アルカンポリオール［例えば、アルカントリオール（例えば、グリセリン、トリメチロールエタン、トリメチロールプロパン等）、アルカンテトラオール（例えば、ペンタエリスリトール等）等］、アルカンポリオールの縮合物［ポリアルカントリ乃至ヘキサオール（例えば、ジグリセリン、ジトリメチロールプロパン、ジペンタエリスリトール等）、糖アルコール（例えば、グルコース、マルトース、ソルビトール、マルチトール、トレハロース等）等］の３価以上のアルコール等が挙げられる。 Typical alcohols include, for example, aliphatic monools [e.g., alkanols (e.g., methanol, ethanol, normal propanol, isopropanol, normal butanol, isobutanol, amyl alcohol, 2-ethylhexanol, etc.)], aromatic monools, etc. monohydric alcohols such as alcohols (e.g., phenol, etc.); aliphatic diols [e.g., alkanediols (e.g., ethylene glycol, propylene glycol, butylene glycol, neopentyl glycol, hexanediol, etc.), polyalkylene glycols (e.g., diethylene glycol); dihydric alcohols such as [e.g., polyethylene glycol, polypropylene glycol, etc.]; alkane polyols [e.g., alkanetriols (e.g., glycerin, trimethylolethane, trimethylolpropane, etc.), alkanetetraols (e.g., pentaerythritol, etc.)]; ], condensates of alkane polyols [polyalkane tri-hexaols (e.g., diglycerin, ditrimethylolpropane, dipentaerythritol, etc.), sugar alcohols (e.g., glucose, maltose, sorbitol, maltitol, trehalose, etc.)] Examples include trihydric or higher alcohols.
アルコールの分子量は、モノオールかポリオールか、縮合物であるか否か等にもよるが、例えば、１０００以下、５００以下、４００以下、３００以下（例えば、２６０以下）等であってもよい。 The molecular weight of the alcohol may be, for example, 1000 or less, 500 or less, 400 or less, 300 or less (for example, 260 or less), etc., depending on whether it is a monool or polyol, whether it is a condensate, etc.
アルコールは、１種であってもよく、２種以上組み合わせてもよい。 The alcohol may be used alone or in combination of two or more.
上記アルコールの中でも、脂肪酸エステルの動粘度を効率よく低くしうる、流動点を効率よく低くしうる等の観点から、脂肪族アルコールを好適に使用してもよく、１価アルコール、２価アルコール、３価以上のアルコール等を好適に使用してもよい。
アルコールとしては、例えば、アルカノール（例えば、メタノール、２－エチルヘキサノール等）、ジオール類（例えば、１，３－ブチレングリコール等）、グリセリン類（例えば、グリセリン、ポリグリセリン等）、ネオペンチルポリオール類（例えば、ネオペンチルグリコール、トリメチロールプロパン、ペンタエリスリトール、ジペンタエリスリトール等）、ソルビタン等を好適に使用してもよい。
Among the above-mentioned alcohols, aliphatic alcohols may be preferably used from the viewpoint of efficiently lowering the kinematic viscosity of the fatty acid ester, efficiently lowering the pour point, etc., monohydric alcohols, dihydric alcohols, Trivalent or higher alcohols may also be suitably used.
Examples of the alcohol include alkanols (e.g., methanol, 2-ethylhexanol, etc.), diols (e.g., 1,3-butylene glycol, etc.), glycerins (e.g., glycerin, polyglycerin, etc.), neopentyl polyols (e.g., For example, neopentyl glycol, trimethylolpropane, pentaerythritol, dipentaerythritol, etc.), sorbitan, etc. may be suitably used.
脂肪酸エステル
脂肪酸エステルは、全エステルであってもよく、部分エステルであってもよい。
Fatty acid ester The fatty acid ester may be a whole ester or a partial ester.
脂肪酸エステルのエステル化率は、アルコールの種類等にもより、特に限定されないが、例えば、全エステルの場合は、例えば、９５％以上、好ましくは９８％以上、より好ましくは９９％以上、さらに好ましくは９９．５％以上であってもよい。
脂肪酸エステルのエステル化率は、部分エステルの場合は、特に限定されないが、例えば、５０％以上（例えば、６０％以上、６５％以上、７０％以上、７５％以上、８０％以上、８５％以上）であってもよく、５０％以下（例えば、４０％以下、３５％以下、３０％以下、２５％以下、２０％以下、１５％以下、１０％以下）であってもよい。
The esterification rate of the fatty acid ester is not particularly limited depending on the type of alcohol, but for example, in the case of all esters, it is, for example, 95% or more, preferably 98% or more, more preferably 99% or more, and even more preferably may be 99.5% or more.
The esterification rate of the fatty acid ester is not particularly limited in the case of a partial ester, but for example, 50% or more (for example, 60% or more, 65% or more, 70% or more, 75% or more, 80% or more, 85% or more). ) or 50% or less (for example, 40% or less, 35% or less, 30% or less, 25% or less, 20% or less, 15% or less, 10% or less).
なお、エステル化率の測定方法としては、特に限定されず、公知の方法（例えば、後述の実施例に記載の方法）を用いてよい。 Note that the method for measuring the esterification rate is not particularly limited, and any known method (for example, the method described in Examples below) may be used.
脂肪酸エステルにおいて、上記混合脂肪酸由来のユニット中の式（１）、式（２）及び式（３）の各脂肪酸由来のユニットの割合は、エステル化率によらず、通常、エステル化前の混合脂肪酸中の各脂肪酸の割合を反映している。 In the fatty acid ester, the ratio of units derived from each fatty acid of formula (1), formula (2), and formula (3) in the unit derived from the above mixed fatty acid is determined depending on the esterification rate, and usually, the proportion of units derived from the fatty acids before esterification is It reflects the proportion of each fatty acid in the fatty acid.
脂肪酸エステルの合成方法は、上記脂肪酸（混合脂肪酸）とアルコールを用いてエステル化する方法であれば、特に限定されず、公知のエステル化方法を使用することができる。例えば、混合脂肪酸とアルコールとを酸触媒下で縮合させる方法によってエステル化してもよい。なお、エステル化の際の温度や時間は、特に限定されない。 The method for synthesizing the fatty acid ester is not particularly limited as long as it is a method of esterifying the fatty acid (mixed fatty acid) and alcohol, and any known esterification method can be used. For example, esterification may be performed by condensing a mixed fatty acid and an alcohol under an acid catalyst. Note that the temperature and time during esterification are not particularly limited.
脂肪酸エステルに要求される物性に応じて、混合脂肪酸以外の脂肪酸を混合してエステル化しても良い。混合脂肪酸以外の脂肪酸としては、例えば、Ｃ４－２５飽和脂肪酸（例えば、ヘキサン酸、ヘプタン酸、オクタン酸、デカン酸、ドデカン酸、テトラデカン酸、ヘキサデカン酸、オクタデカン酸、ベヘン酸等）、Ｃ４－２５不飽和脂肪酸（例えば、オレイン酸、リノール酸、リノレン酸、エルカ酸等）、及びこれらの混合物等を使用しても良い。なお、当該混合脂肪酸以外の脂肪酸は、通常、上述した混合脂肪酸中の他の脂肪酸とは異なる。 Depending on the physical properties required of the fatty acid ester, fatty acids other than the mixed fatty acid may be mixed and esterified. Examples of fatty acids other than mixed fatty acids include C 4-25 saturated fatty acids (for example, hexanoic acid, heptanoic acid, octanoic acid, decanoic acid, dodecanoic acid, tetradecanoic acid, hexadecanoic acid, octadecanoic acid, behenic acid, etc.), C 4 -25 unsaturated fatty acids (eg, oleic acid, linoleic acid, linolenic acid, erucic acid, etc.), mixtures thereof, etc. may also be used. Note that the fatty acids other than the mixed fatty acid are usually different from the other fatty acids in the above-mentioned mixed fatty acid.
混合脂肪酸以外の脂肪酸を使用する場合、当該脂肪酸の割合は、本発明の効果を奏する限り、特に限定されない。例えば、混合脂肪酸全体に対して、５０モル％以下（例えば、４０モル％以下等）であってもよく、５０重量％以下（例えば、４０重量％以下等）であってもよい。 When using fatty acids other than mixed fatty acids, the proportion of the fatty acids is not particularly limited as long as the effects of the present invention are achieved. For example, it may be 50 mol % or less (for example, 40 mol % or less), or 50 weight % or less (for example, 40 weight % or less) with respect to the entire mixed fatty acid.
脂肪酸エステルは、脂肪酸エステル以外の他の未反応成分（例えば、アルコール、脂肪酸等の未反応物等）を一部含有していてもよく、このような場合も、脂肪酸エステルの範疇に含まれる。 The fatty acid ester may partially contain unreacted components other than the fatty acid ester (for example, unreacted substances such as alcohol and fatty acids), and such cases are also included in the category of fatty acid ester.
他の未反応成分は、１種又は２種以上でもよい。 One or more types of other unreacted components may be used.
脂肪酸エステルの流動点は、アルコールの種類等にもよるが、常温で使用できる等の観点から、例えば、２０℃以下（例えば、１５℃以下）、好ましくは１０℃以下（例えば、８℃以下）、より好ましくは５℃以下（例えば、３℃以下）程度であってもよく、例えば、―１００℃以上（例えば、―９０℃以上、―８０℃以上、―７０℃以上、―６０℃以上、―５０℃以上）程度であってもよい。 The pour point of the fatty acid ester depends on the type of alcohol, etc., but from the viewpoint of being usable at room temperature, it is, for example, 20°C or lower (e.g., 15°C or lower), preferably 10°C or lower (e.g., 8°C or lower). , more preferably about 5°C or lower (for example, 3°C or lower), for example, -100°C or higher (for example, -90°C or higher, -80°C or higher, -70°C or higher, -60°C or higher, -50°C or higher).
なお、これらの範囲（上限値と下限値）を適宜組み合わせて範囲を選択してもよい（例えば、―５０～１０℃等）。 Note that a range may be selected by appropriately combining these ranges (upper limit value and lower limit value) (for example, -50 to 10°C, etc.).
流動点の測定方法は、特に限定されず、慣用の方法を使用してもよい。具体的には、後述の方法（自動流動点・曇り点試験器 ｍｐｃ－６形（田中科学機器製作株式会社製）を用いた方法）にて流動点を測定してもよい。 The method for measuring pour point is not particularly limited, and a conventional method may be used. Specifically, the pour point may be measured by the method described below (method using an automatic pour point/cloud point tester MPC-6 type (manufactured by Tanaka Scientific Instruments Manufacturing Co., Ltd.)).
脂肪酸エステルの４０℃における動粘度は、アルコールの種類等にもよるが、潤滑油等の用途に好適に使用できる等の観点から、例えば、１５００ｍｍ２／ｓ以下（例えば、１３００ｍｍ２／ｓ以下）、好ましくは１０００ｍｍ２／ｓ以下（例えば、８００ｍｍ２／ｓ以下、５００ｍｍ２／ｓ以下）程度であってもよく、例えば、５ｍｍ２／ｓ以上、１０ｍｍ２／ｓ以上程度であってもよい。 The kinematic viscosity of the fatty acid ester at 40°C depends on the type of alcohol, etc., but from the viewpoint of suitability for use in lubricating oils, etc., the kinematic viscosity at 40°C is, for example, 1500 mm 2 /s or less (for example, 1300 mm 2 /s or less). , preferably about 1000 mm 2 /s or less (eg, 800 mm 2 /s or less, 500 mm 2 /s or less), and may be, for example, about 5 mm 2 /s or more, 10 mm 2 /s or more.
なお、これらの範囲（上限値と下限値）を適宜組み合わせて範囲を選択してもよい（例えば、５～１５００ｍｍ２／ｓ等）。 Note that a range may be selected by appropriately combining these ranges (upper limit value and lower limit value) (for example, 5 to 1500 mm 2 /s, etc.).
動粘度の測定方法は、特に限定されず、慣用の方法を使用してもよく、具体的には、後述の方法（ＪＩＳ Ｋ ２２８３）にて測定してもよい。 The method for measuring kinematic viscosity is not particularly limited, and a conventional method may be used. Specifically, the measurement may be performed using the method described below (JIS K 2283).
［脂肪酸エステルの用途等］
本発明の脂肪酸エステルは、種々の用途［例えば、潤滑油、金属加工油、圧延油、金属切削油、化粧品（用添加剤）、樹脂用組成物等］に使用できる。脂肪酸エステルに、何らかの添加剤を加えて組成物としてもよい。
化粧品用途としては、特に限定されないが、例えば、パーソナルケア用途の剤（例えば、ＵＶ遮蔽剤、抗老化剤、保湿剤等）を含む組成物に添加してもよい。
樹脂用組成物用途において、樹脂としては、特に限定されないが、例えば、耐寒性樹脂（例えば、ポリαオレフィン系樹脂、ポリ塩化ビニル系樹脂、ポリカーボネート系樹脂、フッ素系樹脂、ポリシロキサン系樹脂等をベースとする耐寒性樹脂等）、感光性樹脂（例えば、エポキシ系樹脂、ポリシロキサン系樹脂等をベースとする感光性樹脂等）、可塑剤（例えば、一塩基性有機酸エステル、多塩基性有機酸エステル等の有機系可塑剤；有機リン酸系、有機亜リン酸系等のリン酸系可塑剤等）等であってもよい。
[Applications of fatty acid esters, etc.]
The fatty acid ester of the present invention can be used for various purposes [for example, lubricating oil, metal processing oil, rolling oil, metal cutting oil, cosmetics (additives), resin compositions, etc.]. A composition may be prepared by adding some kind of additive to the fatty acid ester.
Cosmetic applications are not particularly limited, but may be added, for example, to compositions containing agents for personal care (eg, UV shielding agents, anti-aging agents, humectants, etc.).
In the use of resin compositions, resins include, but are not particularly limited to, cold-resistant resins (e.g., polyα-olefin resins, polyvinyl chloride resins, polycarbonate resins, fluorine resins, polysiloxane resins, etc.). (based on cold-resistant resins, etc.), photosensitive resins (e.g., photosensitive resins based on epoxy resins, polysiloxane resins, etc.), plasticizers (e.g., monobasic organic acid esters, polybasic organic acid esters, etc.), Organic plasticizers such as acid esters; phosphoric acid plasticizers such as organic phosphoric acid type and organic phosphorous acid type, etc.) may also be used.
次に、実施例を挙げて本発明をさらに具体的に説明するが、本発明はこれらの実施例により何ら限定されるものではなく、多くの変形が本発明の技術的思想内で当分野において通常の知識を有する者により可能である。 Next, the present invention will be described in more detail with reference to Examples, but the present invention is not limited to these Examples in any way, and many modifications can be made within the technical idea of the present invention in the art. It can be done by a person with ordinary knowledge.
［ガスクロマトグラフィー測定］
ガスクロマトグラフィー分析の前処理として、混合脂肪酸を下記方法によりメチル化を行った。
・メチル化方法：混合脂肪酸０．１ｍＬに、メチル化試薬である三ふっ化ほう素メタノール錯体メタノール溶液（富士フイルム和光純薬株式会社製）５ｍＬを加え、１００℃のサンドバスで３０分加熱した。これに飽和食塩水５０ｍＬとヘキサン３ｍＬを加えて攪拌し、上層のヘキサン溶液を抜き出して、これをメチル化した混合脂肪酸のヘキサン溶液とした。
上記処理を行った混合脂肪酸中のメチル化した式（１）と式（２）のガスクロマトグラフは、以下の条件で測定した。
・分析装置：株式会社島津製作所製 ＧＣ２０１４
・分析カラム：ジーエルサイエンス株式会社製キャピラリーカラム「ＩｎｅｒｔＣａｐ １ＨＴ」
・カラムの長さ：５ｍ
・カラム内径：０．５３ｍｍ
・昇温条件：１００℃で１分保持した後、２０℃／分で３５０℃まで昇温し２０分保持。
・試料導入及び温度：スプリット試料導入法、３８０℃
・スプリットのガス流量及びキャリアガス：１５．１ｍＬ／分、ヘリウム
・カラムのガス流量及びキャリアガス：２．５ｍＬ／分、ヘリウム
・検出器及び温度：水素炎イオン化検出器（ＦＩＤ）、３８０℃
・注入試料：１．０μＬ（メチル化した混合脂肪酸のヘキサン溶液）
[Gas chromatography measurement]
As a pretreatment for gas chromatography analysis, mixed fatty acids were methylated by the following method.
・Methylation method: 5 mL of boron trifluoride methanol complex methanol solution (manufactured by Fujifilm Wako Pure Chemical Industries, Ltd.), which is a methylation reagent, was added to 0.1 mL of mixed fatty acids, and heated in a sand bath at 100°C for 30 minutes. . 50 mL of saturated saline and 3 mL of hexane were added to this and stirred, and the hexane solution in the upper layer was extracted, and this was used as a hexane solution of methylated mixed fatty acids.
Methylated formulas (1) and (2) in the treated mixed fatty acids were measured by gas chromatography under the following conditions.
・Analyzer: GC2014 manufactured by Shimadzu Corporation
・Analytical column: Capillary column “InertCap 1HT” manufactured by GL Sciences, Inc.
・Column length: 5m
・Column inner diameter: 0.53mm
・Temperature raising conditions: After holding at 100°C for 1 minute, the temperature was raised to 350°C at 20°C/min and held for 20 minutes.
・Sample introduction and temperature: split sample introduction method, 380°C
・Split gas flow rate and carrier gas: 15.1 mL/min, helium column gas flow rate and carrier gas: 2.5 mL/min, helium ・Detector and temperature: Flame ionization detector (FID), 380°C
・Injection sample: 1.0 μL (hexane solution of methylated mixed fatty acids)
［１Ｈ－ＮＭＲ測定］
混合脂肪酸中の式（３）の１Ｈ－ＮＭＲスペクトルは、以下の条件で測定した。
・ＮＭＲ装置：ブルカー・バイオスピン製
・分光計：ブルカー・バイオスピン製 ＡＶＡＮＣＥ ＩＩＩ ＨＤ ４００
・データポイント数：６４ｋ
・ダミースキャン回数：２回
・観測核：１Ｈ
・積算回数：１６回
・観測周波数：４００．２６ＭＨｚ
・ＮＭＲ試料管：５ｍｍφ
・サンプル量：５～２０ｍｇ
・測定溶媒：重クロロホルム
・重溶媒量：０．６ｍＬ
・測定温度：室温
式（１）～（３）及び他の脂肪酸のα位の水素の積分値を２としたときの、式（３）のＲ２、Ｒ３、Ｒ４、Ｒ５、Ｒ６及びＲ７中の４つの水素（すなわち、芳香族領域の水素）の積分値を算出し、当該算出値を４で割り、モル％に換算することによって、混合脂肪酸中の式（３）の脂肪酸の割合を算出した。例えば、芳香族領域の水素の前記算出値が４の場合、４／４＝１（すなわち、混合脂肪酸中の式（３）の脂肪酸の割合は１００モル％）である。
[ 1 H-NMR measurement]
The 1 H-NMR spectrum of formula (3) in mixed fatty acids was measured under the following conditions.
・NMR device: Bruker Biospin ・Spectrometer: Bruker Biospin AVANCE III HD 400
・Number of data points: 64k
・Number of dummy scans: 2 times ・Observation core: 1 H
・Number of integration: 16 times ・Observation frequency: 400.26MHz
・NMR sample tube: 5mmφ
・Sample amount: 5-20mg
・Measurement solvent: heavy chloroform ・Heavy solvent amount: 0.6 mL
・Measurement temperature: room temperature R 2 , R 3 , R 4 , R 5 , R of formula (3) when the integral value of hydrogen at the α-position of formulas (1) to ( 3 ) and other fatty acids is 2 By calculating the integral value of the four hydrogens in 6 and R7 (i.e. hydrogen in the aromatic region), dividing the calculated value by 4, and converting it to mol%, the formula (3) in the mixed fatty acid can be calculated. The proportion of fatty acids was calculated. For example, when the calculated value of hydrogen in the aromatic region is 4, 4/4=1 (that is, the proportion of the fatty acid of formula (3) in the mixed fatty acid is 100 mol%).
［エステル化率］
本発明における脂肪酸エステルのエステル化率（％）とは、下記式により算出される値である。下記式中のエステル価は、ＪＩＳ Ｋ ００７０に基づいて算出される。
エステル化率（％）＝｛エステル価／（エステル価＋水酸基価）｝×１００
[Esterification rate]
The esterification rate (%) of fatty acid ester in the present invention is a value calculated by the following formula. The ester value in the formula below is calculated based on JIS K 0070.
Esterification rate (%) = {ester value / (ester value + hydroxyl value)} x 100
［酸価］
ＪＩＳ Ｋ ００７０（中和滴定法）に従って測定した。
[Acid value]
It was measured according to JIS K 0070 (neutralization titration method).
［水酸基価］
ＪＩＳ Ｋ ００７０（中和滴定法）に従って測定した。
[Hydroxyl value]
It was measured according to JIS K 0070 (neutralization titration method).
［けん化価］
ＪＩＳ Ｋ ００７０（中和滴定法）に従って測定した。
[Saponification value]
It was measured according to JIS K 0070 (neutralization titration method).
［動粘度］
ＪＩＳ Ｋ ２２８３に従って、得られた脂肪酸エステル又は混合脂肪酸の動粘度を測定した。
[Kinematic viscosity]
The kinematic viscosity of the obtained fatty acid ester or mixed fatty acid was measured according to JIS K 2283.
［流動点の測定方法］
自動流動点・曇り点試験器 ｍｐｃ－６形（田中科学機器製作株式会社製）を用いて、取扱説明書に記載の方法に従って、各種脂肪酸エステル又は混合脂肪酸の流動点を測定し、評価を行った。尚、この測定方法は米国規格（ＡＳＴＭ Ｄ６７４９－０２（２０１８） 石油製品の流動点（自動エア圧力法）のための標準試験方法）に従っており、また、日本工業規格（ＪＩＳ Ｋ ２２６９：１９８７ 原油及び石油製品の流動点並びに石油製品曇り点試験方法）に対応している測定方法である。具体的には、当該試験器の測定用セルに各種脂肪酸エステル組成物又は混合脂肪酸を標線まで入れ、４５℃まで予備加熱した後、予期点＋４０℃までは４℃／分、それ以降は試験終了まで１℃／分の速度で冷却した。
[Method of measuring pour point]
Using an automatic pour point/cloud point tester MPC-6 type (manufactured by Tanaka Scientific Instruments Manufacturing Co., Ltd.), the pour points of various fatty acid esters or mixed fatty acids were measured and evaluated according to the method described in the instruction manual. Ta. This measurement method is in accordance with the American Standard (ASTM D6749-02 (2018) Standard Test Method for Pour Point (Automated Air Pressure Method) of Petroleum Products), and is in accordance with the Japanese Industrial Standard (JIS K 2269:1987 Crude Oil and This measurement method corresponds to the pour point of petroleum products and the cloud point test method for petroleum products. Specifically, various fatty acid ester compositions or mixed fatty acids are poured into the measurement cell of the tester up to the marked line, and after preheating to 45°C, the test is carried out at 4°C/min until the expected point +40°C, and thereafter. Cooling was performed at a rate of 1° C./min until completion.
［潤滑性試験］
ＡＳＴＭ Ｄ４１７２に従い、摩擦磨耗試験機（神鋼造機株式会社製）を使用し、脂肪酸エステルの耐摩耗性を評価した。ボールとして、径１／２インチ（ＳＵＪ２）を用い、荷重３０ｋｇｆ、回転速度１５００ｒｐｍ、温度５０℃、試験時間３０分の条件下でシェル四球摩耗試験での摩耗痕径（ｍｍ）を測定して評価した。本評価においては、摩耗痕径が小さいほど、耐摩耗性に優れることを意味する。
[Lubricity test]
According to ASTM D4172, the abrasion resistance of the fatty acid ester was evaluated using a friction abrasion tester (manufactured by Shinko Zoki Co., Ltd.). Evaluation was performed by measuring the wear scar diameter (mm) in a shell four-ball wear test using a 1/2 inch diameter ball (SUJ2) under the conditions of a load of 30 kgf, a rotation speed of 1500 rpm, a temperature of 50°C, and a test time of 30 minutes. did. In this evaluation, the smaller the wear scar diameter, the better the wear resistance.
［脂肪酸エステルの原料］
脂肪酸エステルの製造に用いた原料は下記の通りである。
[Raw material for fatty acid ester]
The raw materials used for producing the fatty acid ester are as follows.
（アルコール）
メタノール；東京化成工業株式会社製試薬
２－エチルヘキサノール（２ＥＨＯＨ）；東京化成工業株式会社製試薬
１，３－ブチレングリコール（１，３－ＢＧ）；東京化成工業株式会社製試薬
グリセリン；東京化成工業株式会社製試薬
ネオペンチルグリコール（ＮＰＧ）；東京化成工業株式会社製試薬
トリメチロールプロパン（ＴＭＰ）；東京化成工業株式会社製試薬
ペンタエリスリトール（ＰＥ）；Ｐｅｒｓｔｏｒｐ社製
ジペンタエリスリトール（ＤｉＰＥ）；Ｐｅｒｓｔｏｒｐ社製
ソルビトール；商品名；Ｄ－ソルビトール；東京化成工業株式会社製試薬
(alcohol)
Methanol; reagent manufactured by Tokyo Chemical Industry Co., Ltd. 2-ethylhexanol (2EHOH); reagent manufactured by Tokyo Chemical Industry Co., Ltd. 1,3-butylene glycol (1,3-BG); reagent manufactured by Tokyo Chemical Industry Co., Ltd. Glycerin; reagent manufactured by Tokyo Chemical Industry Co., Ltd. Reagent neopentyl glycol (NPG) manufactured by Tokyo Chemical Industry Co., Ltd.; Reagent trimethylolpropane (TMP) manufactured by Tokyo Chemical Industry Co., Ltd.; Reagent pentaerythritol (PE) manufactured by Tokyo Chemical Industry Co., Ltd.; Dipentaerythritol (DiPE) manufactured by Perstorp; Manufactured by Sorbitol; Trade name: D-Sorbitol; Reagent manufactured by Tokyo Kasei Kogyo Co., Ltd.
（脂肪酸）
脂肪酸は、下記に示すように調製を行った混合脂肪酸１～３を使用した。
(fatty acid)
The fatty acids used were mixed fatty acids 1 to 3 prepared as shown below.
［混合脂肪酸１の調製］
オレイン酸（Ｅｖｙａｐ社製；オレイン酸含有率８０％、リノール酸含有率１１％）に触媒としてモルデナイトを使用して異性化反応を行った。その後、水素化触媒下で水添反応を行い、融点差を利用して固体酸、液体酸の分別を行った。最後に、得られた液体酸を蒸留して混合脂肪酸１を得た。
[Preparation of mixed fatty acid 1]
An isomerization reaction was performed on oleic acid (manufactured by Evyap; oleic acid content: 80%, linoleic acid content: 11%) using mordenite as a catalyst. Thereafter, a hydrogenation reaction was performed under a hydrogenation catalyst, and the solid acid and liquid acid were separated using the difference in melting point. Finally, the obtained liquid acid was distilled to obtain mixed fatty acid 1.
［混合脂肪酸２の調製］
混合脂肪酸１及び単分岐イソステアリン酸を多く含む混合脂肪酸を、混合脂肪酸１：単分岐イソステアリン酸を多く含む混合脂肪酸の重量比が１：１になるように混合して、混合脂肪酸２を得た。なお、単分岐イソステアリン酸を多く含む混合脂肪酸は、オレイン酸を原料に触媒としてフェリエライトを使用して異性化反応を行い、その後、水素化触媒下での水添反応、融点差を利用した固体酸と液体酸の分別、最後に、液体酸を蒸留することで得られる混合脂肪酸を使用した。
[Preparation of mixed fatty acid 2]
Mixed fatty acid 1 and mixed fatty acid containing a large amount of monobranched isostearic acid were mixed so that the weight ratio of mixed fatty acid 1:mixed fatty acid containing a large amount of monobranched isostearic acid was 1:1 to obtain mixed fatty acid 2. In addition, mixed fatty acids containing a large amount of monobranched isostearic acid are produced by performing an isomerization reaction using oleic acid as a raw material and using ferrierite as a catalyst, followed by a hydrogenation reaction under a hydrogenation catalyst, and solidification using the difference in melting point. Fractionation of acids and liquid acids.Finally, mixed fatty acids obtained by distilling liquid acids were used.
［混合脂肪酸３の調製］
炭素数１８の不飽和脂肪酸の重合により副生したモノマー酸を水素化触媒存在下での水添反応、融点差を利用した固体酸と液体酸の分別、最後に、得られた液体酸を蒸留して混合脂肪酸３を得た。
[Preparation of mixed fatty acid 3]
Hydrogenation reaction of monomer acids produced by polymerization of unsaturated fatty acids having 18 carbon atoms in the presence of a hydrogenation catalyst, separation of solid acids and liquid acids using the difference in melting points, and finally, distillation of the obtained liquid acids. Mixed fatty acid 3 was obtained.
なお、混合脂肪酸１～３の組成は下記表１の通りである。 The compositions of mixed fatty acids 1 to 3 are shown in Table 1 below.
（実施例１）
攪拌器、温度計、滴下ロート、導入管を備えた１Ｌの４つ口フラスコに、混合脂肪酸１を３９８ｇ（１．４０モル）及び触媒として、パラトルエンスルホン酸を総量に対し２．０重量％仕込み、１２０℃まで昇温した。そこへ、メタノール２６９ｇ（８．４０モル）を滴下ロートを用いて徐々に液中へ吹き込み、エステル化反応を行った。酸価が１．０ｍｇＫＯＨ／ｇ以下になったところで反応を終了し、エステル化粗物を得た。次いで、得られたエステル化粗物を酸価に対して過剰の苛性ソーダ水溶液で中和、水洗後、脱水した。さらに、得られたエステル化粗物に対してそれぞれ０．５重量％の活性白土とセライトを投入し、８０℃で３０分攪拌した後、１時間減圧下で攪拌した。その後、常圧に戻し、濾過してそれらを除去することで脂肪酸エステルＡを得た。
なお、当該脂肪酸エステルのエステル化率は、９９．９％であった。
(Example 1)
In a 1 L four-necked flask equipped with a stirrer, thermometer, dropping funnel, and inlet tube, 398 g (1.40 mol) of mixed fatty acid 1 and 2.0% by weight of paratoluenesulfonic acid based on the total amount as a catalyst were added. The mixture was prepared and the temperature was raised to 120°C. Then, 269 g (8.40 mol) of methanol was gradually blown into the liquid using a dropping funnel to perform an esterification reaction. The reaction was terminated when the acid value became 1.0 mgKOH/g or less, and an esterified crude product was obtained. Next, the obtained esterified crude product was neutralized with an aqueous solution of caustic soda in excess of the acid value, washed with water, and then dehydrated. Further, activated clay and celite were added in an amount of 0.5% by weight, respectively, based on the obtained esterified crude product, and the mixture was stirred at 80° C. for 30 minutes and then for 1 hour under reduced pressure. Thereafter, fatty acid ester A was obtained by returning the pressure to normal pressure and removing them by filtration.
Note that the esterification rate of the fatty acid ester was 99.9%.
（実施例２）
攪拌器、温度計、冷却管付きディーンスターク管を備えた１Ｌの４つ口フラスコに、混合脂肪酸１を４３５ｇ（１．５３モル）、２－エチルヘキサノール２６０ｇ（２．００モル）、及び触媒として、パラトルエンスルホン酸を総量に対し０．１重量％仕込み、窒素雰囲気下で２００℃まで昇温した。２００℃到達後、減圧し、留出してくる生成水をディーンスターク管で除去しながら２３０℃まで昇温し、エステル化反応を行った。酸価が１．０ｍｇＫＯＨ／ｇ以下になったところで反応を終了した。反応終了後、２３０℃で過剰のアルコール分及び低沸点成分を留去した。得られたエステル化粗物に対してそれぞれ０．２重量％の活性白土とセライトを投入し、８０℃で３０分攪拌した後、１時間減圧下で攪拌した。その後、常圧に戻し、濾過してそれらを除去して本発明の脂肪酸エステルＢを得た。
なお、当該脂肪酸エステルのエステル化率は、９９．９％であった。
(Example 2)
In a 1 L four-necked flask equipped with a stirrer, thermometer, and Dean-Stark tube with condenser, 435 g (1.53 mol) of mixed fatty acid 1, 260 g (2.00 mol) of 2-ethylhexanol, and as a catalyst were added. , para-toluenesulfonic acid was added in an amount of 0.1% by weight based on the total amount, and the temperature was raised to 200°C under a nitrogen atmosphere. After reaching 200°C, the pressure was reduced, and the temperature was raised to 230°C while removing distilled water using a Dean-Stark tube to carry out an esterification reaction. The reaction was terminated when the acid value became 1.0 mgKOH/g or less. After the reaction was completed, excess alcohol and low-boiling components were distilled off at 230°C. 0.2% by weight of each of activated clay and celite were added to the resulting esterified crude product, and the mixture was stirred at 80° C. for 30 minutes and then for 1 hour under reduced pressure. Thereafter, the pressure was returned to normal, and these were removed by filtration to obtain fatty acid ester B of the present invention.
Note that the esterification rate of the fatty acid ester was 99.9%.
（実施例３）
攪拌器、温度計、冷却管付きディーンスターク管を備えた１Ｌの４つ口フラスコに、混合脂肪酸１を６８２ｇ（２．４０モル）、１，３－ブチレングリコール９０ｇ（１．００モル）、及び触媒として、パラトルエンスルホン酸を総量に対し０．１重量％仕込み、窒素雰囲気下で１７０℃まで昇温した。１７０℃到達後、減圧し、留出してくる生成水をディーンスターク管で除去しながら、エステル化反応を行った。水酸基価が５．０ｍｇＫＯＨ／ｇ以下になったところで反応を終了した。反応終了後、エステル化粗物に対してそれぞれ０．２重量％の活性白土とセライトを投入し、８０℃で３０分攪拌した後、１時間減圧下で攪拌した。その後、常圧に戻し、濾過してそれらを除去した。次いで、得られたエステル化濾過物の過剰の酸と低沸点成分を薄膜蒸留器により留去して、脂肪酸エステルＣを得た。
なお、当該脂肪酸エステルのエステル化率は、９９．７％であった。
(Example 3)
In a 1 L four-necked flask equipped with a stirrer, thermometer, and Dean-Stark tube with condenser, 682 g (2.40 mol) of mixed fatty acid 1, 90 g (1.00 mol) of 1,3-butylene glycol, and As a catalyst, para-toluenesulfonic acid was added in an amount of 0.1% by weight based on the total amount, and the temperature was raised to 170°C under a nitrogen atmosphere. After reaching 170° C., the pressure was reduced and the esterification reaction was carried out while removing the distilled water using a Dean-Stark tube. The reaction was terminated when the hydroxyl value became 5.0 mgKOH/g or less. After the reaction was completed, activated clay and celite were added in an amount of 0.2% by weight each based on the esterified crude material, and the mixture was stirred at 80° C. for 30 minutes and then for 1 hour under reduced pressure. Thereafter, the pressure was returned to normal pressure and they were removed by filtration. Next, excess acid and low boiling point components of the obtained esterified filtrate were distilled off using a thin film distiller to obtain fatty acid ester C.
Note that the esterification rate of the fatty acid ester was 99.7%.
（実施例４）
攪拌器、温度計、脱水管－冷却管を備えた１Ｌの４つ口フラスコに、混合脂肪酸１を２８４ｇ（１．００モル）、グリセリン４６１ｇ（５．００モル）を入れ、窒素雰囲気下で２５０℃まで昇温し、エステル化反応を行った。酸価が１．０ｍｇＫＯＨ／ｇ以下になったところで反応を終了した。次いで、薄膜蒸留器により得られたエステル化粗物中の過剰のアルコールと低沸点成分を留去し、次いで薄膜蒸留器でモノグリセライドを留出させ、脂肪酸エステルＤを得た。
なお、当該脂肪酸エステルのエステル化率は、３３．６％であった。
(Example 4)
284 g (1.00 mol) of mixed fatty acid 1 and 461 g (5.00 mol) of glycerin were placed in a 1 L four-necked flask equipped with a stirrer, a thermometer, and a dehydration tube/cooling tube, and the mixture was heated to 250 g (5.00 mol) under a nitrogen atmosphere. The temperature was raised to ℃ and an esterification reaction was carried out. The reaction was terminated when the acid value became 1.0 mgKOH/g or less. Next, excess alcohol and low boiling point components in the obtained esterified crude product were distilled off using a thin film distiller, and then monoglycerides were distilled off using a thin film distiller to obtain fatty acid ester D.
Note that the esterification rate of the fatty acid ester was 33.6%.
（実施例５）
攪拌器、温度計、脱水管－冷却管を備えた１Ｌの４つ口フラスコに、混合脂肪酸１を５６９ｇ（２．００モル）、グリセリン４６ｇ（０．５０モル）を入れ、窒素雰囲気下で２５０℃まで昇温し、エステル化反応を行った。水酸基価が０．５ｍｇＫＯＨ／ｇ以下になったところで反応を終了した。得られたエステル化粗物の過剰の酸と低沸点成分を薄膜蒸留器により留去して、トリグリセライドである脂肪酸エステルＥを得た。
なお、当該脂肪酸エステルのエステル化率は、９９．４％であった。
(Example 5)
569 g (2.00 mol) of mixed fatty acid 1 and 46 g (0.50 mol) of glycerin were placed in a 1 L four-necked flask equipped with a stirrer, a thermometer, and a dehydration tube-cooling tube, and the mixture was heated to 250 g (0.50 mol) under a nitrogen atmosphere. The temperature was raised to ℃ and an esterification reaction was carried out. The reaction was terminated when the hydroxyl value became 0.5 mgKOH/g or less. Excess acid and low boiling point components of the obtained esterified crude product were distilled off using a thin film distiller to obtain fatty acid ester E, which is a triglyceride.
Note that the esterification rate of the fatty acid ester was 99.4%.
（実施例６）
攪拌器、温度計、脱水管－冷却管を備えた１Ｌの４つ口フラスコに、混合脂肪酸１を５６９ｇ（２．００モル）、ネオペンチルグリコール８５ｇ（０．８２モル）、及び触媒として、パラトルエンスルホン酸を総量に対し０．１重量％仕込み、窒素雰囲気下で２３０℃まで昇温した。２３０℃到達後、減圧し、留出してくる生成水を除去しながら、エステル化反応を行った。水酸基価が５．０ｍｇＫＯＨ／ｇ以下になったところで反応を終了した。反応終了後、エステル化粗物に対してそれぞれ０．５重量％の活性白土とセライトを投入し、８０℃で３０分攪拌した後、１時間減圧下で攪拌した。その後、常圧に戻し、濾過してそれらを除去した。次いで、得られたエステル化濾過物の過剰の酸と低沸点成分を薄膜蒸留器により留去して、脂肪酸エステルＦを得た。
なお、当該脂肪酸エステルのエステル化率は、９８．８％であった。
(Example 6)
In a 1L four-necked flask equipped with a stirrer, thermometer, and dehydration tube/cooling tube, 569 g (2.00 mol) of mixed fatty acid 1, 85 g (0.82 mol) of neopentyl glycol, and 100% of parasitide as a catalyst were placed. Toluenesulfonic acid was added in an amount of 0.1% by weight based on the total amount, and the temperature was raised to 230°C under a nitrogen atmosphere. After reaching 230°C, the pressure was reduced and the esterification reaction was carried out while removing the distilled water. The reaction was terminated when the hydroxyl value became 5.0 mgKOH/g or less. After the reaction was completed, activated clay and celite were added in an amount of 0.5% by weight each based on the esterified crude material, and the mixture was stirred at 80° C. for 30 minutes and then for 1 hour under reduced pressure. Thereafter, the pressure was returned to normal, and they were removed by filtration. Next, excess acid and low boiling point components of the obtained esterified filtrate were distilled off using a thin film distiller to obtain fatty acid ester F.
Note that the esterification rate of the fatty acid ester was 98.8%.
（実施例７）
ネオペンチルグリコールの代わりにトリメチロールプロパン７４ｇ（０．５５モル）を使用した以外は、実施例６と同様の方法により、脂肪酸エステルＧを得た。
なお、当該脂肪酸エステルのエステル化率は、９８．６％であった。
(Example 7)
Fatty acid ester G was obtained in the same manner as in Example 6, except that 74 g (0.55 mol) of trimethylolpropane was used instead of neopentyl glycol.
Note that the esterification rate of the fatty acid ester was 98.6%.
（実施例８）
ネオペンチルグリコールの代わりにペンタエリスリトール５７ｇ（０．４２モル）を使用した以外は、実施例６と同様の方法により、脂肪酸エステルＨを得た。
なお、当該脂肪酸エステルのエステル化率は、９８．５％であった。
(Example 8)
Fatty acid ester H was obtained in the same manner as in Example 6, except that 57 g (0.42 mol) of pentaerythritol was used instead of neopentyl glycol.
Note that the esterification rate of the fatty acid ester was 98.5%.
（実施例９）
ネオペンチルグリコールの代わりにジペンタエリスリトール７０ｇ（０．２８モル）を使用した以外は、実施例６と同様の方法により、脂肪酸エステルＩを得た。
なお、当該脂肪酸エステルのエステル化率は、９５．４％であった。
(Example 9)
Fatty acid ester I was obtained in the same manner as in Example 6, except that 70 g (0.28 mol) of dipentaerythritol was used instead of neopentyl glycol.
Note that the esterification rate of the fatty acid ester was 95.4%.
（実施例１０）
攪拌器、温度計、脱水管－冷却管を備えた１Ｌの４つ口フラスコに、混合脂肪酸１を４８３ｇ（１．７０モル）、ソルビトール２１０ｇ（１．１５モル）、及び触媒として、２５．５％苛性ソーダ水溶液を総量に対し０．５重量％、亜リン酸を総量に対し０．１重量％仕込み、窒素雰囲気下で２３０℃まで昇温し、エステル化反応を行った。酸価が７．０ｍｇＫＯＨ／ｇ以下になったところで反応を終了した。反応終了後、エステル化粗物に対して１．０重量％のセライトを投入し、１２０℃で３０分攪拌した後、１時間減圧下で攪拌した。その後、常圧に戻し、濾過してセライトを除去することで、脂肪酸エステルＪを得た。
なお、当該脂肪酸エステルのエステル化率は、４２．８％であった。
(Example 10)
In a 1 L four-necked flask equipped with a stirrer, thermometer, dehydration tube and cooling tube, 483 g (1.70 mol) of mixed fatty acid 1, 210 g (1.15 mol) of sorbitol, and 25.5 g of sorbitol as a catalyst were added. % caustic soda aqueous solution to the total amount and phosphorous acid to the total amount by 0.1% by weight, and the temperature was raised to 230° C. under a nitrogen atmosphere to perform an esterification reaction. The reaction was terminated when the acid value became 7.0 mgKOH/g or less. After the reaction was completed, 1.0% by weight of Celite based on the esterified crude material was added, stirred at 120°C for 30 minutes, and then stirred for 1 hour under reduced pressure. Thereafter, fatty acid ester J was obtained by returning the pressure to normal pressure and removing Celite by filtration.
Note that the esterification rate of the fatty acid ester was 42.8%.
（実施例１１～２０）
混合脂肪酸１の代わりに混合脂肪酸２を使用した以外はそれぞれ実施例１～１０と同様の方法により、脂肪酸エステルＫ～Ｔを得た。
(Examples 11-20)
Fatty acid esters K to T were obtained in the same manner as in Examples 1 to 10, except that mixed fatty acid 2 was used instead of mixed fatty acid 1.
（比較例１～１０）
混合脂肪酸１の代わりに混合脂肪酸３を使用した以外はそれぞれ実施例１～１０と同様の方法により、脂肪酸エステルを得た。
(Comparative Examples 1 to 10)
Fatty acid esters were obtained in the same manner as in Examples 1 to 10, except that mixed fatty acid 3 was used instead of mixed fatty acid 1.
（参考例１～３）
参考例１～３は、それぞれ、混合脂肪酸１～３そのものについて測定した。
(Reference examples 1 to 3)
Reference Examples 1 to 3 were measured using mixed fatty acids 1 to 3 themselves, respectively.
表２が示すように、本発明の混合脂肪酸１を使用した実施例１～１０は、混合脂肪酸１よりも単分岐構造が多く、芳香族脂肪酸の割合も多い混合脂肪酸３を使用した比較例１～１０よりも動粘度が低くなった。
同様に、本発明の混合脂肪酸２を使用した実施例１１～２０は、混合脂肪酸２と単分岐構造が同等で、芳香族脂肪酸の割合が多い混合脂肪酸３を使用した比較例１～１０よりも動粘度が低くなった。
As shown in Table 2, Examples 1 to 10 using Mixed Fatty Acid 1 of the present invention have more monobranched structures than Mixed Fatty Acid 1, and Comparative Example 1 using Mixed Fatty Acid 3 having a higher proportion of aromatic fatty acids. The kinematic viscosity was lower than ~10.
Similarly, Examples 11 to 20 using Mixed Fatty Acid 2 of the present invention have the same monobranched structure as Mixed Fatty Acid 2, but are better than Comparative Examples 1 to 10 using Mixed Fatty Acid 3, which has a higher proportion of aromatic fatty acids. Kinematic viscosity decreased.
表３が示すように、本発明の混合脂肪酸１を使用した実施例１～１０では、流動点は、混合脂肪酸１よりも単分岐構造が多く、芳香族脂肪酸の割合も多い混合脂肪酸３を使用した比較例１～１０と比較して、低い傾向となった。
同様に、本発明の混合脂肪酸２を使用した実施例１１～２０では、流動点は、混合脂肪酸２と単分岐構造が同等で、芳香族脂肪酸の割合が多い混合脂肪酸３を使用した比較例１～１０と比較して、低い傾向となった。
As shown in Table 3, in Examples 1 to 10 using Mixed Fatty Acid 1 of the present invention, the pour point was higher than that of Mixed Fatty Acid 1 when Mixed Fatty Acid 3 was used, which had more monobranched structures and a higher proportion of aromatic fatty acids. Compared to Comparative Examples 1 to 10, the trend was lower.
Similarly, in Examples 11 to 20 using Mixed Fatty Acid 2 of the present invention, the pour point was the same as that of Mixed Fatty Acid 2 in the monobranched structure, and Comparative Example 1 using Mixed Fatty Acid 3 with a high proportion of aromatic fatty acids. This is a lower trend compared to ~10.
表４が示すように、本発明の混合脂肪酸１を使用した実施例１～１０では、潤滑性も、混合脂肪酸１よりも単分岐構造が多く、芳香族脂肪酸の割合も多い混合脂肪酸３を使用した比較例１～１０と同等に良好であった。
同様に、本発明の混合脂肪酸２を使用した実施例１１～２０でも、潤滑性は、混合脂肪酸２と単分岐構造が同等で、芳香族脂肪酸の割合が多い混合脂肪酸３を使用した比較例１～１０と同等に良好であった。
As shown in Table 4, in Examples 1 to 10 using mixed fatty acid 1 of the present invention, the lubricity was also improved by using mixed fatty acid 3, which had more monobranched structures and a higher proportion of aromatic fatty acids than mixed fatty acid 1. The results were as good as those of Comparative Examples 1 to 10.
Similarly, in Examples 11 to 20 using Mixed Fatty Acid 2 of the present invention, the lubricity was the same as that of Comparative Example 1 using Mixed Fatty Acid 3, which had the same monobranched structure as Mixed Fatty Acid 2 and had a high proportion of aromatic fatty acids. It was as good as ~10.
（試験例１）
脂肪酸エステルＨまたはＲを用いて、下記表５に記載の配合により、それぞれ乳液Ａ、Ｂを調製した。なお、得られた乳液は白色であった。
(Test example 1)
Emulsions A and B were prepared using fatty acid ester H or R according to the formulations shown in Table 5 below. Note that the obtained emulsion was white.
上記乳液ＡおよびＢを、４０℃で２カ月間保管し、ｐＨの経時変化を調べた。
なお、対照乳液としては、脂肪酸エステルＨまたはＲの代わりに比較例８の脂肪酸エステルを使用した以外は表５と同じ配合で調製したものを使用した。
脂肪酸エステルＨを使用した乳液ＡのｐＨは、調製直後：４．８７、上記保管１カ月後：４．６７、上記保管２カ月後：４．７０であり、大きく変動しなかった。
脂肪酸エステルＲを使用した乳液ＢのｐＨは、調製直後：４．８９、上記保管１カ月後：４．７０、上記保管２カ月後：４．６９であり、大きく変動しなかった。
なお、対照乳液のｐＨは、調製直後：５．２６、上記保管１カ月後：５．４２、上記保管２カ月後：５．３３であった。
このように、本発明の脂肪酸エステルを用いた乳液ＡおよびＢは、保存安定性が対照乳液と同等に良好であった。
The above-mentioned emulsions A and B were stored at 40° C. for 2 months, and changes in pH over time were examined.
As a control emulsion, one prepared with the same formulation as in Table 5 was used, except that the fatty acid ester of Comparative Example 8 was used instead of fatty acid ester H or R.
The pH of emulsion A using fatty acid ester H was 4.87 immediately after preparation, 4.67 after one month of storage, and 4.70 after two months of storage, and did not vary significantly.
The pH of emulsion B using fatty acid ester R was 4.89 immediately after preparation, 4.70 after one month of storage, and 4.69 after two months of storage, and did not vary significantly.
The pH of the control emulsion was 5.26 immediately after preparation, 5.42 after one month of storage, and 5.33 after two months of storage.
As described above, the emulsions A and B using the fatty acid ester of the present invention had storage stability as good as that of the control emulsion.
（試験例２）
試験例１の乳液Ａ、Ｂと対照乳液を、被験者６名のヒトの両腕の前腕（肘から手首の範囲）に約１ｇずつを塗布し、官能評価を行った。評価方法を下記に示す。
下記評価１～５について各人に１～５点で採点を行ってもらい、６名の平均値を算出した。評価１～４については５点に近いほど良好な結果であったことを表し、評価５については１点に近いほど良好な結果であったことを表す。
評価１：しっとり感
評価２：こく感
評価３：浸透感
評価４：伸び
評価５：べたつき
(Test example 2)
Approximately 1 g each of Emulsions A and B of Test Example 1 and the control emulsion were applied to the forearms (range from the elbow to the wrist) of six human subjects, and a sensory evaluation was performed. The evaluation method is shown below.
Each person was asked to rate the evaluations 1 to 5 below on a scale of 1 to 5, and the average score of the 6 people was calculated. For evaluations 1 to 4, the closer the score is to 5 points, the better the result is, and for the evaluation 5, the closer the score is to 1 point, the better the result is.
Evaluation 1: Moist feeling Evaluation 2: Body feeling Evaluation 3: Penetrating feeling Evaluation 4: Spreadiness Evaluation 5: Stickiness
表６が示すように、本発明の脂肪酸エステルを用いた乳液ＡおよびＢは、官能評価が良好であり、特に、しっとり感が良好であった。 As shown in Table 6, the emulsions A and B using the fatty acid ester of the present invention had good sensory evaluation, and in particular, had good moist feeling.
本発明によれば、新規な脂肪酸エステルを提供できる。このような脂肪酸エステルは、種々の用途、例えば、潤滑油、化粧品、樹脂等に使用できる。 According to the present invention, a novel fatty acid ester can be provided. Such fatty acid esters can be used in various applications, such as lubricating oils, cosmetics, resins, and the like.
Claims (10)
（式（１）中、ｊ及びｋは、ｊ＋ｋ＝１３を満たす０～１３の整数を示す。）
（式（２）中、ｌは、式（２）の炭素数の合計が１８を満たす８～１３の整数を示し、
Ｒ１は、Ｈ又はＣＨ３を示す。
ただし、ｌ個のＲ１は同一又は異なり、ｌ個中少なくとも２個のＲ１がＣＨ３を示す。）
（式（３）中、Ｒ２、Ｒ３、Ｒ４、Ｒ５、Ｒ６及びＲ７は、Ｈ、（ａ）又は（ｂ）を示し、（ａ）及び（ｂ）をそれぞれ１つずつ含む。）
（式（ａ）及び（ｂ）中、ｍ及びｎは、式（３）の炭素数の合計が１８、及びｍ＋ｎ≦９を満たす０～９の整数を示す。
ただし、Ｒ8及びＲ9は、Ｈ又はＣＨ３を示し、ｍ個のＲ8は、同一又は異なり、ｎ個のＲ9は、同一又は異なる。） The mixed fatty acids forming the fatty acid ester include a fatty acid represented by the following formula (1) and a fatty acid represented by the following formula (2), a fatty acid represented by the formula (1): a fatty acid represented by the formula (2) The molar ratio of fatty acids is 10-65:35-90 when the total fatty acids represented by formula (1) and formula (2) is 100, and the fatty acid represented by formula (3) below is A mixture of fatty acid esters containing 0.01 to 1 mol% when the total mixed fatty acid is 100 mol%, and the alcohol forming the fatty acid ester is an aliphatic alcohol (however, a mixture of fatty acid esters represented by the following formula (1) The molar ratio of the fatty acid represented by the formula (1) to the fatty acid represented by the formula (2) is expressed by the formula (1) and the formula (2). It contains 65:35 when the total fatty acid is 100, and contains 0.01 to 1 mol% of the fatty acid represented by the following formula (3) when the total mixed fatty acid is 100 mol%, and the fatty acid (except when the alcohol forming the ester is an aliphatic alcohol, a mixture of fatty acid esters).
(In formula (1), j and k represent integers from 0 to 13 that satisfy j+k=13.)
(In formula (2), l represents an integer from 8 to 13 where the total number of carbon atoms in formula (2) satisfies 18,
R1 represents H or CH3 .
However, 1 R 1 's are the same or different, and at least 2 R 1 's out of 1 represent CH 3 . )
(In formula (3), R 2 , R 3 , R 4 , R 5 , R 6 and R 7 represent H, (a) or (b), and one each of (a) and (b) include.)
(In formulas (a) and (b), m and n represent integers from 0 to 9 that satisfy the total number of carbon atoms in formula (3) of 18 and m+n≦9.
However, R 8 and R 9 represent H or CH 3 , m R 8 are the same or different, and n R 9 are the same or different. )