The present invention relates to a composition containing fine fibrous cellulose and a method for producing the same.

Fine fibrous cellulose with a fiber width of 1,000 nm or less is called cellulose nanofiber, and is used in various fields such as reinforcing materials for composite materials, high-performance filters, displays, solar cells, electronics, transportation equipment, building materials, and medical care. is expected to expand to
In general, fine fibrous cellulose is obtained as a dispersion, but the dispersion has a high viscosity. Have difficulty. On the other hand, if the dispersion is diluted and used for uniform coating, coating and drying must be repeated many times until the desired film thickness is achieved, resulting in poor efficiency. rice field.
In Patent Document 1, as a method for producing a low-viscosity cellulose nanofiber dispersion, wood is selected from which pulp having a specific fiber length distribution can be obtained, and the pulp derived from the wood is defibrated to obtain a cellulose nanofiber dispersion. It describes how to obtain

JP 2018-090949 A

In the method described in Patent Document 1, it was necessary to use specific raw materials, and it was difficult to precisely adjust the viscosity of the resulting dispersion.
An object of the present invention is to provide a fine fibrous cellulose-containing composition that enables the viscosity of a fine fibrous cellulose dispersion to be reduced without changing the concentration of fine fibrous cellulose, and a method for producing the same. .

The present inventors have found that the above problems are solved by a composition containing fine fibrous cellulose and an oxoacid or its salt containing a specific amount of chlorine relative to the fine fibrous cellulose.
That is, the present invention relates to the following <1> to <8>.
<1> Contains fine fibrous cellulose having a fiber width of 1,000 nm or less and an oxoacid containing chlorine or a salt thereof, wherein the content of the oxoacid containing chlorine or a salt thereof relative to 100 parts by mass of the fine fibrous cellulose is A composition containing fine fibrous cellulose, which is 0.0001 parts by mass or more and 10 parts by mass or less.
<2> The oxoacid containing chlorine or a salt thereof includes at least one selected from the group consisting of sodium hypochlorite, potassium hypochlorite and calcium hypochlorite, according to <1>. A composition containing fine fibrous cellulose.
<3> The viscosity of the composition measured by rotating at 23° C. for 3 minutes at a rotation speed of 3 rpm using a Brookfield viscometer when the solid content concentration of fine fibrous cellulose is 0.4% by mass is The fine fibrous cellulose-containing composition according to <1> or <2>, which has a viscosity of 1.0×10 ⁴ mPa·s or less.
<4> The fine fibrous cellulose has an ionic substituent, and the content of the ionic substituent is 0.60 mmol/g or more relative to the dry mass of the fine fibrous cellulose. The fine fibrous cellulose-containing composition according to any one of <3>.
<5> The fine fiber according to any one of <1> to <4>, wherein the composition has a haze of 1.5% or less at 23° C. when the fine fibrous cellulose has a solid content concentration of 0.2% by mass. cellulose-containing composition.
<6> The fine fiber according to any one of <1> to <5>, wherein the content of the chlorine-containing oxoacid or its salt relative to 100 parts by mass of the fine fibrous cellulose is 0.005 parts by mass or more and 2 parts by mass or less. A fibrous cellulose-containing composition.
<7> A step of defibrating the fibrous cellulose in the solvent to obtain a dispersion containing fine fibrous cellulose, and adding an oxoacid containing chlorine or a salt thereof to the dispersion containing fine fibrous cellulose. and wherein the amount of oxo acid containing chlorine or a salt thereof added to 100 parts by mass of fine fibrous cellulose is 0.0001 parts by mass or more and 10 parts by mass or less.
<8> The method for producing a fine fibrous cellulose-containing composition according to <7>, wherein the fibrous cellulose has an ionic substituent.

INDUSTRIAL APPLICABILITY According to the present invention, a fine fibrous cellulose-containing composition and a method for producing the same are provided, which can reduce the viscosity of a fine fibrous cellulose dispersion without changing the concentration of fine fibrous cellulose.

FIG. 1 is a graph showing the relationship between the amount of NaOH added to fine fibrous cellulose having a phosphate group and the electrical conductivity. FIG. 2 is a graph showing the relationship between the amount of NaOH added to fine fibrous cellulose having carboxyl groups and the electrical conductivity.

[Fine fibrous cellulose-containing composition]
The fine fibrous cellulose-containing composition of the present invention contains fine fibrous cellulose having a fiber width of 1,000 nm or less and an oxoacid containing chlorine or a salt thereof, and contains chlorine with respect to 100 parts by mass of fine fibrous cellulose. The content of oxoacid or salt thereof is 0.0001 parts by mass or more and 10 parts by mass or less.
Conventionally, as a method for reducing the viscosity of a dispersion of fine fibrous cellulose, there is a method of increasing the number of defibration treatment steps, but it is difficult to precisely control the viscosity when the viscosity is lowered by fibrillation treatment. In addition, the defibration process is time-consuming and costly.
The fine fibrous cellulose-containing composition of the present invention makes it possible to reduce the viscosity of the fine fibrous cellulose dispersion without changing the concentration of the fine fibrous cellulose. In addition, compared to the method of adjusting the number of fibrillation treatment steps described above, the time required for the viscosity reduction is shorter, and the viscosity can be reduced at a lower cost.
Although the detailed reasons why the above effects are obtained are unknown, some of them are presumed as follows. That is, it is thought that the inclusion of the oxoacid containing chlorine or its salt cuts the molecular chains of some of the fine fibrous cellulose, lowering the molecular weight of the fine fibrous cellulose, thereby reducing the viscosity of the dispersion. be done. However, the viscosity reduction by the chlorine-containing oxoacid or its salt is not only due to the lowering of the molecular weight, but the chlorine-containing oxoacid or its salt causes aggregation of the fine fibrous cellulose to the extent that the haze is not deteriorated. It is also considered that the viscosity of the dispersion is reduced thereby.
The present invention will be described in more detail below.

<Fine fibrous cellulose>
The fine fibrous cellulose-containing composition of the present invention contains fine fibrous cellulose, and the fine fibrous cellulose is fibrous cellulose having a fiber width of 1,000 nm or less. The fiber width of fibrous cellulose can be measured, for example, by electron microscope observation.

The fiber width of the fine fibrous cellulose is preferably 100 nm or less, more preferably 30 nm or less, even more preferably 8 nm or less. Also, the fiber width is preferably 2 nm or more.
The average fiber width of fine fibrous cellulose is, for example, 1000 nm or less. The average fiber width of the fine fibrous cellulose is, for example, preferably 2 nm or more and 1000 nm or less, more preferably 2 nm or more and 100 nm or less, further preferably 2 nm or more and 50 nm or less, and 2 nm or more and 10 nm or less. is particularly preferred. By setting the average fiber width of the fine fibrous cellulose to 2 nm or more, dissolution of the cellulose molecules in water is suppressed, and the effect of improving the strength, rigidity, and dimensional stability of the fine fibrous cellulose is more likely to be exhibited. be able to. The fine fibrous cellulose is, for example, monofibrous cellulose.

The average fiber width of fibrous cellulose is measured, for example, using an electron microscope as follows. First, an aqueous suspension of fibrous cellulose with a concentration of 0.05% by mass or more and 0.1% by mass or less is prepared, and this suspension is cast on a hydrophilized carbon film-coated grid to form a sample for TEM observation. and SEM images of surfaces cast on glass may be observed if they contain wide fibers. Then, an electron microscope image is observed at a magnification of 1,000, 5,000, 10,000, or 50,000 times depending on the width of the fiber to be observed. However, the sample, observation conditions and magnification are adjusted so as to satisfy the following conditions.
(1) A single straight line X is drawn at an arbitrary point in the observed image, and 20 or more fibers intersect the straight line X.
(2) Draw a straight line Y that intersects the straight line perpendicularly in the same image, and 20 or more fibers intersect the straight line Y.
Widths of fibers intersecting the straight lines X and Y are visually read from the observation image satisfying the above conditions. In this way, at least three sets of observed images of surface portions that do not overlap each other are obtained. Then, for each image, the width of the fiber that crosses straight line X and straight line Y is read. This gives at least 20 x 2 x 3 = 120 fiber width readings. Then, the average value of the read fiber widths is taken as the average fiber width of the fibrous cellulose.

The fiber length of the fine fibrous cellulose is not particularly limited. More preferred. By setting the fiber length within the above range, destruction of the crystalline regions of the fine fibrous cellulose can be suppressed. Also, it becomes possible to set the slurry viscosity of the fine fibrous cellulose to an appropriate range. The fiber length of fine fibrous cellulose can be determined by image analysis using TEM, SEM, or AFM, for example.

Preferably, the fine fibrous cellulose has a Type I crystal structure. Here, the fact that the fine fibrous cellulose has a type I crystal structure can be identified in a diffraction profile obtained from a wide-angle X-ray diffraction photograph using CuKα (λ=1.5418 Å) monochromated with graphite. Specifically, it can be identified by having typical peaks at two positions near 2θ=14° or more and 17° or less and 2θ=22° or more and 23° or less.
The proportion of the I-type crystal structure in the fine fibrous cellulose is, for example, preferably 30% or more, more preferably 40% or more, even more preferably 50% or more. As a result, even better performance can be expected in terms of heat resistance and low coefficient of linear thermal expansion. The degree of crystallinity is determined by a conventional method from the pattern of X-ray diffraction profiles (Seagal et al., Textile Research Journal, vol. 29, p. 786, 1959).

Although the axial ratio (fiber length/fiber width) of the fine fibrous cellulose is not particularly limited, it is preferably 20 or more and 10,000 or less, and more preferably 50 or more and 1,000 or less. A sheet containing fine fibrous cellulose can be easily formed by making the axial ratio equal to or higher than the above lower limit. Moreover, when a solvent dispersion is produced, it is easy to obtain an appropriate thickening property. By setting the axial ratio to the above upper limit or less, handling such as dilution becomes easier, for example, when fibrous cellulose is treated as an aqueous dispersion, which is preferable.

The fine fibrous cellulose in this embodiment has, for example, both a crystalline region and an amorphous region. In particular, fine fibrous cellulose having both a crystalline region and an amorphous region and having a high axial ratio is realized by the method for producing fine fibrous cellulose described later.

The fine fibrous cellulose in this embodiment has, for example, at least one of ionic substituents and nonionic substituents. From the viewpoint of improving the dispersibility of the fibers in the dispersion medium and enhancing the defibration efficiency in the fibrillation treatment, it is more preferable that the fine fibrous cellulose has an ionic substituent. The ionic substituents can include, for example, either one or both of an anionic group and a cationic group. Nonionic substituents can also include, for example, alkyl groups and acyl groups. In this embodiment, it is particularly preferable to have an anionic group as an ionic substituent.
The fine fibrous cellulose may not be subjected to a treatment for introducing an ionic substituent.

Examples of the anionic group as the ionic substituent include, for example, a phosphate group or a substituent derived from a phosphate group (sometimes simply referred to as a phosphate group), a carboxy group or a substituent derived from a carboxy group (simply called a carboxy group and a substituent derived from a sulfone group or a sulfone group (sometimes referred to simply as a sulfone group), and at least one selected from a phosphate group and a carboxy group. One type is more preferable, and a phosphate group is particularly preferable.

A phosphoric acid group or a substituent derived from a phosphoric acid group is, for example, a substituent represented by the following formula (1), and is generalized as a phosphoric acid group or a substituent derived from a phosphoric acid group.

In formula (1), a, b and n are natural numbers (where a=b×m). a ^of α ¹ , α ² , ^. All of α ⁿ and α′ may be O ⁻ . Each R is a hydrogen atom, a saturated-linear hydrocarbon group, a saturated-branched hydrocarbon group, a saturated-cyclic hydrocarbon group, an unsaturated linear hydrocarbon group, an unsaturated-branched hydrocarbon group A hydrogen group, an unsaturated-cyclic hydrocarbon group, an aromatic group, or a derivative group thereof.

Examples of the saturated straight-chain hydrocarbon group include, but are not limited to, methyl group, ethyl group, n-propyl group, n-butyl group, and the like. The saturated-branched hydrocarbon group includes, but is not particularly limited to, i-propyl group, t-butyl group, and the like. The saturated cyclic hydrocarbon group includes, but is not particularly limited to, a cyclopentyl group, a cyclohexyl group, and the like. The unsaturated straight-chain hydrocarbon group includes, but is not particularly limited to, a vinyl group, an allyl group, and the like. The unsaturated-branched hydrocarbon group includes i-propenyl group, 3-butenyl group and the like, but is not particularly limited. Examples of the unsaturated-cyclic hydrocarbon group include, but are not particularly limited to, a cyclopentenyl group, a cyclohexenyl group, and the like. Aromatic groups include, but are not particularly limited to, phenyl groups, naphthyl groups, and the like.

In addition, as the derivative group for R, at least one functional group such as a carboxy group, a hydroxy group, or an amino group is added or substituted to the main chain or side chain of the various hydrocarbon groups described above. Examples include, but are not limited to, groups.
Although the number of carbon atoms constituting the main chain of R is not particularly limited, it is preferably 20 or less, more preferably 10 or less. By setting the number of carbon atoms constituting the main chain of R within the above range, the molecular weight of the phosphate group can be set within an appropriate range, facilitating penetration into the fiber raw material and increasing the yield of fine cellulose fibers. can also

β ^b+ is a cation having a valence of 1 or more, which is composed of an organic substance or an inorganic substance. Examples of monovalent or higher valent cations composed of organic substances include aliphatic ammonium and aromatic ammonium. Examples include, but are not particularly limited to, cations of divalent metals such as calcium or magnesium, or hydrogen ions. These can be applied singly or in combination of two or more. As the cation having a valence of 1 or more composed of an organic substance or an inorganic substance, sodium or potassium ions are preferable, but are not particularly limited, since fiber raw materials containing β are not easily yellowed when heated and are easily industrially available.

The phosphoric acid group is a divalent functional group, which corresponds to, for example, phosphoric acid from which a hydroxyl group has been removed. Specifically, it is a group represented by —PO ₃ H ₂ . Substituents derived from a phosphate group include substituents such as salts of phosphate groups and phosphate ester groups. A substituent derived from a phosphate group may be contained in the fine fibrous cellulose as a condensed phosphate group (for example, a pyrophosphate group).
Further, the phosphate group may be, for example, a phosphite group (phosphonic acid group), and the substituent derived from the phosphate group may be a phosphite group salt, a phosphite ester group, or the like. good too.

The amount of the ionic substituent introduced into the fine fibrous cellulose is, for example, preferably 0.10 mmol/g or more, more preferably 0.20 mmol/g or more per 1 g (mass) of fine fibrous cellulose. It is more preferably 0.60 mmol/g or more, and particularly preferably 1.00 mmol/g or more. In addition, the amount of the ionic substituent introduced into the fine fibrous cellulose is, for example, preferably 3.65 mmol/g or less, more preferably 3.50 mmol/g or less per 1 g (mass) of the fine fibrous cellulose. , 3.00 mmol/g or less. By setting the amount of the ionic substituent to be introduced within the above range, the fiber raw material can be easily made finer, and the stability of the fine fibrous cellulose can be enhanced. By setting the amount of the ionic substituent to be introduced within the above range, good properties can be exhibited in various applications such as a thickening agent for fine fibrous cellulose.
Here, the denominator in units of mmol/g indicates the mass of fibrous cellulose when the counter ion of the ionic substituent is hydrogen ion (H ⁺ ).
The amount of ionic substituents introduced into the fine fibrous cellulose can be measured, for example, by conductivity titration. In the measurement by the conductivity titration method, the introduced amount is measured by determining the change in conductivity while adding an alkali such as an aqueous sodium hydroxide solution to the obtained slurry containing fine fibrous cellulose.

FIG. 1 is a graph showing the relationship between the amount of NaOH added to fine fibrous cellulose having a phosphate group and the electrical conductivity.
The amount of phosphate groups introduced into fine fibrous cellulose is measured, for example, as follows.
First, a slurry containing fine fibrous cellulose is treated with a strongly acidic ion exchange resin. In addition, before the treatment with the strongly acidic ion exchange resin, a defibration treatment similar to the fibrillation treatment step described below may be performed on the object to be measured, if necessary. Next, change in electrical conductivity is observed while adding an aqueous sodium hydroxide solution to obtain a titration curve as shown in FIG. As shown in FIG. 1, the electrical conductivity drops sharply at first (hereinafter referred to as "first region"). After that, the conductivity starts to rise slightly (hereinafter referred to as "second region"). After that, the increment of conductivity increases (hereinafter referred to as "third region"). The boundary point between the second region and the third region is defined as the point where the second derivative of the conductivity, that is, the amount of change in the increment (slope) of the conductivity is maximized. Thus, three regions appear in the titration curve. Of these, the amount of alkali required in the first region is equal to the amount of strong acid groups in the slurry used for titration, and the amount of alkali required in the second region is the amount of weak acid groups in the slurry used for titration. be equal. When the phosphate groups condense, the weakly acidic groups are apparently lost, and the amount of alkali required for the second region becomes smaller than the amount of alkali required for the first region. On the other hand, the amount of strongly acidic groups coincides with the amount of phosphorus atoms regardless of the presence or absence of condensation. Therefore, the amount of phosphate groups introduced (or the amount of phosphate groups) or the amount of substituents introduced (or the amount of substituents) means the amount of strongly acidic groups. Therefore, the value obtained by dividing the alkali amount (mmol) required in the first region of the titration curve obtained above by the solid content (g) in the slurry to be titrated is the amount of phosphate group introduced (mmol/ g).

In the above-mentioned phosphate group introduction amount (mmol/g), since the denominator indicates the mass of acid-type fine fibrous cellulose, the amount of phosphate groups possessed by acid-type fine fibrous cellulose (hereinafter referred to as phosphoric acid base amount (called acid form)). On the other hand, when the counterion of the phosphate group is substituted with an arbitrary cation C so as to have a charge equivalent, the denominator is converted to the mass of fine fibrous cellulose when the cation C is the counterion. By doing so, the amount of phosphate groups (hereinafter referred to as the amount of phosphate groups (C-type)) possessed by the fine fibrous cellulose in which the cation C is the counter ion can be obtained.
That is, it is calculated by the following formula.
Phosphate group amount (C type) = phosphate group amount (acid form) / {1 + (W-1) × A / 1000}
A [mmol/g]: Total amount of anions derived from phosphate groups possessed by fibrous cellulose (a value obtained by adding the amount of strongly acidic groups and the amount of weakly acidic groups of phosphate groups)
W: Formula weight per valence of cation C (for example, 23 for Na and 9 for Al)

FIG. 2 is a graph showing the relationship between the amount of NaOH added to fine fibrous cellulose having a carboxyl group and the electrical conductivity.
The amount of carboxyl groups introduced into fine fibrous cellulose is measured, for example, as follows.
First, a slurry containing fine fibrous cellulose is treated with a strongly acidic ion exchange resin. In addition, before the treatment with the strongly acidic ion exchange resin, a defibration treatment similar to the fibrillation treatment step described below may be performed on the object to be measured, if necessary. Next, change in electrical conductivity is observed while adding an aqueous sodium hydroxide solution to obtain a titration curve as shown in FIG. In addition, if necessary, a defibration treatment similar to the fibrillation treatment step to be described later may be performed on the object to be measured. As shown in FIG. 2, the titration curve has a first region where the increment (slope) of the conductivity becomes almost constant after the electrical conductivity decreases, and then the increment (slope) of the conductivity increases. It is divided into a second area. The boundary point between the first region and the second region is defined as the point where the second differential value of the conductivity, that is, the amount of change in the increment (slope) of the conductivity becomes maximum. Then, the value obtained by dividing the alkali amount (mmol) required in the first region of the titration curve by the solid content (g) in the fine fibrous cellulose-containing slurry to be titrated is the introduction amount of the carboxy group ( mmol/g).

In addition, since the denominator of the above-mentioned carboxy group introduction amount (mmol/g) is the mass of the acid-type fine fibrous cellulose, the amount of carboxy groups possessed by the acid-type fine fibrous cellulose (hereinafter referred to as the amount of carboxy groups ( acid form)). On the other hand, when the counterion of the carboxyl group is substituted with any cation C so as to have a charge equivalent, the denominator is converted to the mass of fine fibrous cellulose when the cation C is the counterion. Thus, the amount of carboxy groups (hereinafter referred to as the amount of carboxy groups (C type)) possessed by fibrous cellulose whose counter ion is cation C can be determined.
That is, it is calculated by the following formula.
Carboxy group amount (C type) = carboxy group amount (acid form) / {1 + (W-1) × (carboxy group amount (acid form)) / 1000}
W: Formula weight per valence of cation C (for example, 23 for Na and 9 for Al)

<Method for producing fine fibrous cellulose>
(Fiber raw material containing cellulose)
Fine fibrous cellulose is produced from a fibrous raw material containing cellulose (hereinafter also simply referred to as "fiber raw material").
The fibrous raw material containing cellulose is not particularly limited, but pulp is preferably used because it is readily available and inexpensive. Pulp includes, for example, wood pulp, non-wood pulp, and deinked pulp. Examples of wood pulp include, but are not limited to, hardwood kraft pulp (LBKP), softwood kraft pulp (NBKP), sulfite pulp (SP), dissolving pulp (DP), soda pulp (AP), unbleached kraft pulp (UKP). ) and chemical pulp such as oxygen bleached kraft pulp (OKP), semi-chemical pulp such as semi-chemical pulp (SCP) and chemigroundwood pulp (CGP), groundwood pulp (GP) and thermomechanical pulp (TMP, BCTMP) A mechanical pulp etc. are mentioned. Non-wood pulps include, but are not limited to, cotton-based pulps such as cotton linters and cotton lints, and non-wood-based pulps such as hemp, straw, and bagasse. Examples of deinked pulp include, but are not limited to, deinked pulp made from waste paper. The pulp of this embodiment may be used alone or in combination of two or more.
Among the above pulps, wood pulp and deinked pulp are preferred, for example, from the viewpoint of availability. In addition, among wood pulps, the cellulose ratio is high and the yield of fine fibrous cellulose at the time of defibration is high, and the decomposition of cellulose in the pulp is small, and fine fibrous cellulose of long fibers with a large axial ratio can be obtained. From the point of view, for example, chemical pulp is more preferable, and kraft pulp and sulfite pulp are more preferable. The use of fine fibrous cellulose of long fibers with a large axial ratio tends to increase the viscosity.

As the fiber raw material containing cellulose, for example, cellulose contained in sea squirts and bacterial cellulose produced by acetic acid bacteria can be used.
In place of the fiber raw material containing cellulose, a fiber formed by a linear nitrogen-containing polysaccharide polymer such as chitin or chitosan can be used as a part thereof.

In order to obtain fine fibrous cellulose into which ionic substituents have been introduced as described above, the ionic substituent introduction step of introducing ionic substituents into the fiber raw material containing cellulose described above, a washing step, an alkali treatment step ( Neutralization step) and fibrillation treatment step are preferably included in this order, and an acid treatment step may be included instead of or in addition to the washing step. Examples of the ionic substituent introduction step include a phosphate group introduction step and a carboxy group introduction step. Each of these will be described below.

(Ionic substituent introduction step)
[Phosphate group introduction step]
The step of introducing a phosphate group into the cellulose fiber (phosphate group introduction step) will be described below.
In the step of introducing a phosphate group, at least one compound selected from compounds capable of introducing a phosphate group (hereinafter also referred to as "compound A") is added to cellulose by reacting with a hydroxyl group possessed by a fiber raw material containing cellulose. It is a step of acting on the fiber raw material containing. Through this step, a phosphate group-introduced fiber is obtained.

In the phosphate group-introducing step according to the present embodiment, the reaction between the fiber raw material containing cellulose and compound A is performed in the presence of at least one selected from urea and derivatives thereof (hereinafter also referred to as "compound B"). may On the other hand, the reaction between the cellulose-containing fiber raw material and the compound A may be carried out in the absence of the compound B.

An example of the method of allowing the compound A to act on the fiber raw material in the presence of the compound B includes a method of mixing the compound A and the compound B with the fiber raw material in a dry state, a wet state, or a slurry state. Among these, it is preferable to use a fiber raw material in a dry state or a wet state, and it is particularly preferable to use a fiber raw material in a dry state, because the uniformity of the reaction is high. Although the form of the fiber material is not particularly limited, it is preferably in the form of cotton or a thin sheet, for example.
The compound A and the compound B can be added to the fiber raw material in the form of a powder, a solution dissolved in a solvent, or a melted state by heating to a melting point or higher. Among these, it is preferable to add in the form of a solution dissolved in a solvent, particularly in the form of an aqueous solution, since the uniformity of the reaction is high. Moreover, the compound A and the compound B may be added simultaneously to the fiber raw material, may be added separately, or may be added as a mixture. The method of adding the compound A and the compound B is not particularly limited, but when the compound A and the compound B are in solution, the fiber raw material may be immersed in the solution to absorb the liquid and then taken out, or the fiber raw material may be taken out. The solution may be added dropwise to the Further, the necessary amount of compound A and compound B may be added to the fiber raw material, or after adding excessive amounts of compound A and compound B to the fiber raw material, the excess compound A and compound B are removed by pressing or filtering. may be removed.

Compound A used in this embodiment includes phosphoric acid or its salt, dehydrated condensed phosphoric acid or its salt, and phosphoric anhydride (phosphorus pentoxide), but is not particularly limited. Phosphoric acid of various purities can be used, for example, 100% phosphoric acid (orthophosphoric acid) or 85% phosphoric acid can be used. Dehydration-condensed phosphoric acid is obtained by condensing two or more molecules of phosphoric acid by dehydration reaction, and examples thereof include pyrophosphoric acid and polyphosphoric acid. Phosphates and dehydrated condensed phosphates include lithium salts, sodium salts, potassium salts and ammonium salts of phosphoric acid or dehydrated condensed phosphates, and these can have various degrees of neutralization.
Among these, the efficiency of introducing a phosphate group is high, the fibrillation efficiency is easily improved in the fibrillation step described later, the cost is low, and it is easy to apply industrially. Sodium salt, potassium salt of phosphate, or ammonium salt of phosphate are preferred, and phosphoric acid, sodium dihydrogen phosphate, disodium hydrogen phosphate, or ammonium dihydrogen phosphate are more preferred.

The amount of compound A added to the fiber material is not particularly limited, but for example, when the amount of compound A added is converted to the phosphorus atomic weight, The amount of atoms added is preferably 0.5% by mass or more and 100% by mass or less, more preferably 1% by mass or more and 50% by mass or less, and even more preferably 2% by mass or more and 30% by mass or less. . By setting the amount of phosphorus atoms added to the fiber raw material within the above range, the yield of fine fibrous cellulose can be further improved. On the other hand, by setting the amount of phosphorus atoms added to the fiber raw material to be equal to or less than the above upper limit, it is possible to balance the effect of improving the yield and the cost. Here, the "absolute dry mass (absolute dry mass)" is the absolute dry mass that has reached a constant mass, measured by the method described in ISO 638:2008.

Compound B used in this embodiment is at least one selected from urea and its derivatives as described above. Compound B includes, for example, urea, biuret, 1-phenylurea, 1-benzylurea, 1-methylurea, and 1-ethylurea.
From the viewpoint of improving the uniformity of the reaction, compound B is preferably used as an aqueous solution. From the viewpoint of further improving the uniformity of the reaction, it is preferable to use an aqueous solution in which both compound A and compound B are dissolved.
The amount of compound B added to the fiber raw material (absolute dry mass) is not particularly limited, but is preferably 1% by mass or more and 500% by mass or less, more preferably 10% by mass or more and 400% by mass or less, More preferably, it is 100% by mass or more and 350% by mass or less.

In the reaction between the fiber raw material containing cellulose and compound A, in addition to compound B, for example, amides or amines may be included in the reaction system. Examples of amides include formamide, dimethylformamide, acetamide, dimethylacetamide and the like. Examples of amines include methylamine, ethylamine, trimethylamine, triethylamine, monoethanolamine, diethanolamine, triethanolamine, pyridine, ethylenediamine and hexamethylenediamine. Among these, triethylamine in particular is known to work as a good reaction catalyst.

In the phosphate group-introducing step, it is preferable to heat-treat the fiber raw material after the compound A or the like is added to or mixed with the fiber raw material. As the heat treatment temperature, it is preferable to select a temperature at which the phosphate group can be efficiently introduced while suppressing the thermal decomposition and hydrolysis reaction of the fiber. The heat treatment temperature is, for example, preferably 50° C. or higher and 300° C. or lower, more preferably 100° C. or higher and 250° C. or lower, and even more preferably 130° C. or higher and 200° C. or lower. In addition, for the heat treatment, equipment having various heat media can be used. A drying device, a vacuum drying device, an infrared heating device, a far infrared heating device, or a microwave heating device can be used.

In the heat treatment according to the present embodiment, for example, the compound A is added to a thin sheet-like fiber raw material by a method such as impregnation, and then heated, or the fiber raw material and the compound A are heated while kneading or stirring with a kneader or the like. method can be adopted. This makes it possible to suppress concentration unevenness of the compound A in the fiber raw material and to more uniformly introduce phosphate groups to the surface of the cellulose fibers contained in the fiber raw material. This is because when water molecules move to the surface of the fiber material during drying, the dissolved compound A is attracted to the water molecules by surface tension and similarly moves to the surface of the fiber material (that is, the concentration unevenness of the compound A is It is thought that this is due to the fact that it is possible to suppress the occurrence of
In addition, the heating apparatus used for the heat treatment constantly removes the moisture retained by the slurry and the moisture generated due to the dehydration condensation (phosphorylation) reaction between the compound A and the hydroxyl groups contained in the cellulose etc. in the fiber raw material. A device that can be discharged to the outside is preferable. Such a heating device includes, for example, an air-blowing oven. By constantly draining the water in the device system, it is possible to suppress the hydrolysis reaction of the phosphate ester bond, which is the reverse reaction of phosphorylation, and to suppress the acid hydrolysis of the sugar chains in the fiber. can. Therefore, it is possible to obtain fine fibrous cellulose having a high axial ratio.

The heat treatment time is, for example, preferably 1 second or more and 300 minutes or less, more preferably 1 second or more and 1000 seconds or less, and 10 seconds or more and 800 seconds or less, after water is substantially removed from the fiber raw material. is more preferable. In the present embodiment, the introduction amount of the phosphate group can be set within a preferable range by setting the heating temperature and the heating time within appropriate ranges.

The step of introducing a phosphate group may be performed at least once, but may be performed repeatedly two or more times. By performing the phosphate group-introducing step two or more times, many phosphate groups can be introduced into the fiber raw material. In the present embodiment, one example of a preferred aspect is the case where the phosphate group introduction step is performed twice.

The amount of phosphate groups introduced into the fiber raw material is, for example, preferably 0.10 mmol/g or more, more preferably 0.20 mmol/g or more, more preferably 0.60 mmol/g per 1 g (mass) of fine fibrous cellulose. g or more is more preferable, and 1.00 mmol/g or more is particularly preferable. In addition, the amount of phosphate groups introduced into the fiber raw material is, for example, preferably 5.20 mmol/g or less, more preferably 3.65 mmol/g or less per 1 g (mass) of fine fibrous cellulose. It is more preferably 00 mmol/g or less. By setting the amount of the phosphate group to be introduced within the above range, the fiber raw material can be easily made finer, and the stability of the fine fibrous cellulose can be enhanced.

[Carboxy group introduction step]
In the step of introducing a carboxy group, the fiber raw material containing cellulose is subjected to oxidation treatment such as ozone oxidation, oxidation by the Fenton method, TEMPO oxidation treatment, a compound having a carboxylic acid-derived group or a derivative thereof, or a carboxylic acid-derived group. This is done by treating the compound with an acid anhydride or a derivative thereof.

The compound having a carboxylic acid-derived group is not particularly limited. Examples include tricarboxylic acid compounds. Derivatives of compounds having a carboxylic acid-derived group are not particularly limited, but include, for example, imidized acid anhydrides of compounds having a carboxy group and derivatives of acid anhydrides of compounds having a carboxy group. Examples of imidized acid anhydrides of compounds having a carboxyl group include, but are not particularly limited to, imidized dicarboxylic acid compounds such as maleimide, succinimide and phthalimide.
The acid anhydride of the compound having a group derived from carboxylic acid is not particularly limited. acid anhydrides; In addition, the acid anhydride derivative of the compound having a carboxylic acid-derived group is not particularly limited. Acid anhydrides in which at least some of the hydrogen atoms are substituted with substituents such as alkyl groups and phenyl groups can be mentioned.

In the carboxyl group introduction step, when the TEMPO oxidation treatment is performed, it is preferable to perform the treatment under the condition of pH 6 or more and 8 or less. Such treatment is also referred to as neutral TEMPO oxidation treatment. Neutral TEMPO oxidation treatment includes, for example, sodium phosphate buffer (pH=6.8), pulp as a fiber raw material, and TEMPO (2,2,6,6-tetramethylpiperidine-1-oxyl) as a catalyst. This can be done by adding sodium hypochlorite as a nitroxy radical, sacrificial reagent. Furthermore, coexistence of sodium chlorite enables efficient oxidation of aldehydes generated in the process of oxidation to carboxyl groups.
Moreover, the TEMPO oxidation treatment may be performed under the condition that the pH is 10 or more and 11 or less. Such treatment is also called alkali TEMPO oxidation treatment. Alkaline TEMPO oxidation treatment can be performed, for example, by adding a nitroxy radical such as TEMPO as a catalyst, sodium bromide as a cocatalyst, and sodium hypochlorite as an oxidizing agent to pulp as a fiber raw material. .

The amount of carboxyl groups to be introduced into the fiber raw material varies depending on the type of substituent. For example, when carboxyl groups are introduced by TEMPO oxidation, the amount is preferably 0.10 mmol/g or more per 1 g (mass) of fine fibrous cellulose. , is more preferably 0.20 mmol/g or more, more preferably 0.60 mmol/g or more, and particularly preferably 0.90 mmol/g or more. Also, it is preferably 2.5 mmol/g or less, more preferably 2.20 mmol/g or less, and even more preferably 2.00 mmol/g or less. In addition, when the substituent is a carboxymethyl group, it may be 5.8 mmol/g or less per 1 g (mass) of fine fibrous cellulose.

(Washing process)
In the method for producing fine fibrous cellulose according to the present embodiment, a washing step can be performed on the fibers into which substituents such as ionic substituents have been introduced, if necessary. The washing step is performed by washing the substituent-introduced fiber with water or an organic solvent, for example. Moreover, the washing process may be performed after each process described later, and the number of times of washing performed in each washing process is not particularly limited.

(alkali treatment step)
When producing fine fibrous cellulose, the fiber raw material may be subjected to an alkali treatment between the step of introducing a substituent such as an ionic substituent and the later-described fibrillation treatment step. The method of alkali treatment is not particularly limited, but includes, for example, a method of immersing the substituent-introduced fiber in an alkali solution.
The alkali compound contained in the alkali solution is not particularly limited, and may be an inorganic alkali compound or an organic alkali compound. In the present embodiment, it is preferable to use, for example, sodium hydroxide or potassium hydroxide as the alkaline compound because of its high versatility. Moreover, the solvent contained in the alkaline solution may be either water or an organic solvent. Among them, the solvent contained in the alkaline solution is preferably water or a polar solvent including a polar organic solvent exemplified by alcohol, and more preferably an aqueous solvent including at least water. As the alkaline solution, for example, an aqueous sodium hydroxide solution or an aqueous potassium hydroxide solution is preferable because of its high versatility.

The temperature of the alkaline solution in the alkaline treatment step is not particularly limited, but is preferably, for example, 5°C or higher and 80°C or lower, more preferably 10°C or higher and 60°C or lower. The immersion time of the substituent-introduced fiber in the alkali solution in the alkali treatment step is not particularly limited, but is preferably 5 minutes or more and 30 minutes or less, more preferably 10 minutes or more and 20 minutes or less. The amount of the alkaline solution used in the alkaline treatment is not particularly limited, but for example, it is preferably 100% by mass or more and 100000% by mass or less, and 1000% by mass or more and 10000% by mass or less based on the absolute dry mass of the substituent-introduced fiber. It is more preferable to have

In order to reduce the amount of alkaline solution used in the alkali treatment step, the substituent-introduced fiber may be washed with water or an organic solvent after the step of introducing substituents such as ionic substituents and before the alkali treatment step. good. After the alkali treatment step and before the fibrillation treatment step, it is preferable to wash the alkali-treated substituent-introduced fibers with water or an organic solvent from the viewpoint of improving handleability.

(Acid treatment step)
When producing fine fibrous cellulose, the fiber raw material may be subjected to an acid treatment between the step of introducing a substituent such as an ionic substituent and the later-described fibrillation treatment step. For example, the substituent introduction step, acid treatment, alkali treatment and fibrillation treatment may be performed in this order.
The acid treatment method is not particularly limited, but includes, for example, a method of immersing the fiber raw material in an acidic liquid containing an acid. Although the concentration of the acid liquid used is not particularly limited, it is preferably 10% by mass or less, more preferably 5% by mass or less. Moreover, the pH of the acidic liquid to be used is not particularly limited. Examples of acids contained in the acid solution include inorganic acids, sulfonic acids, and carboxylic acids. Examples of inorganic acids include sulfuric acid, nitric acid, hydrochloric acid, hydrobromic acid, hydroiodic acid, hypochlorous acid, chlorous acid, chloric acid, perchloric acid, phosphoric acid and boric acid. Examples of sulfonic acid include methanesulfonic acid, ethanesulfonic acid, benzenesulfonic acid, p-toluenesulfonic acid, trifluoromethanesulfonic acid and the like. Carboxylic acids include, for example, formic acid, acetic acid, citric acid, gluconic acid, lactic acid, oxalic acid, and tartaric acid. Among these, it is particularly preferable to use hydrochloric acid or sulfuric acid.

The temperature of the acid solution in the acid treatment is not particularly limited. The immersion time in the acid solution in the acid treatment is not particularly limited, but is preferably 5 minutes or more and 120 minutes or less, more preferably 10 minutes or more and 60 minutes or less. The amount of the acid solution used in the acid treatment is not particularly limited. is more preferred.

(defibration treatment)
Fine fibrous cellulose can be obtained by defibrating the fibers into which a substituent such as an ionic substituent is introduced in the fibrillation treatment step.
In the defibration treatment process, for example, a fibrillation treatment device can be used. The fibrillation treatment device is not particularly limited, but includes, for example, a high-speed fibrillator, a grinder (stone mill mill), a high-pressure homogenizer, an ultra-high-pressure homogenizer, a high-pressure collision-type pulverizer, a ball mill, a bead mill, a disk-type refiner, a conical refiner, and a biaxial refiner. A kneader, a vibration mill, a homomixer under high-speed rotation, an ultrasonic disperser, a beater, or the like can be used. Among the above defibration equipment, it is more preferable to use a high-speed fibrillation machine, a high-pressure homogenizer, and an ultrahigh-pressure homogenizer, which are less affected by the grinding media and less likely to cause contamination.

In the fibrillation treatment step, for example, it is preferable to dilute the substituent-introduced fibers with a dispersion medium to form a slurry. As the dispersion medium, one or more selected from organic solvents such as water and polar organic solvents can be used. The polar organic solvent is not particularly limited, but alcohols, polyhydric alcohols, ketones, ethers, esters, aprotic polar solvents and the like are preferable. Examples of alcohols include methanol, ethanol, isopropanol, n-butanol, isobutyl alcohol and the like. Examples of polyhydric alcohols include ethylene glycol, propylene glycol and glycerin. Ketones include acetone, methyl ethyl ketone (MEK), and the like. Examples of ethers include diethyl ether, tetrahydrofuran, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol mono-n-butyl ether, propylene glycol monomethyl ether and the like. Examples of esters include ethyl acetate and butyl acetate. Aprotic polar solvents include dimethylsulfoxide (DMSO), dimethylformamide (DMF), dimethylacetamide (DMAc), N-methyl-2-pyrrolidinone (NMP) and the like.

The solid content concentration of the fine fibrous cellulose at the defibration treatment can be appropriately set. Further, the slurry obtained by dispersing the substituent-introduced fibers in the dispersion medium may contain solids other than the substituent-introduced fibers, such as urea having hydrogen bonding properties.

<Oxoacid containing chlorine or its salt>
The fine fibrous cellulose-containing composition of the present invention contains a chlorine-containing oxoacid or a salt thereof.
The chlorine-containing oxoacid includes hypochlorous acid, chlorous acid, chloric acid, and perchloric acid, with hypochlorous acid being preferred from the viewpoint of availability, stability, and the like.
In addition, as the oxoacid salt containing chlorine, sodium hypochlorite, potassium hypochlorite, hypochlorous acid salts such as calcium hypochlorite; sodium chlorite, potassium chlorite, chlorine Salts of chlorous acid such as copper acid and barium chlorite; chlorates such as sodium chlorate, potassium chlorate, ammonium chlorate, calcium chlorate, barium chlorate, zinc chlorate and silver chlorate; perchlorate Perchlorates such as ammonium perchlorate, potassium perchlorate, sodium perchlorate, calcium perchlorate, silver chlorite and magnesium perchlorate are obtained.
Among these, as the oxoacid containing chlorine or a salt thereof, it is preferable to contain a salt of an oxoacid containing chlorine, more preferably a salt of hypochlorous acid, sodium hypochlorite, hypochlorite It is more preferable to contain at least one selected from the group consisting of potassium chlorate and calcium hypochlorite, and at least one selected from the group consisting of sodium hypochlorite and potassium hypochlorite. Containing sodium hypochlorite is particularly preferred, and sodium hypochlorite is most preferred.

In the fine fibrous cellulose-containing composition of the present invention, the content of the chlorine-containing oxoacid or its salt is 0.0001 parts by mass or more and 10 parts by mass or less relative to 100 parts by mass of the fine fibrous cellulose. If the content of the chlorine-containing oxoacid or its salt is less than 0.0001 parts by mass, a sufficient viscosity-lowering effect cannot be obtained. If exceeded, the fine fibrous cellulose-containing composition tends to yellow.
The content of the chlorine-containing oxoacid or its salt relative to 100 parts by mass of fine fibrous cellulose is preferably 0.0003 parts by mass or more, more preferably 0.001 parts by mass or more, still more preferably 0.003 parts by mass or more, and still more It is preferably 0.005 parts by mass or more, more preferably 0.01 parts by mass or more, preferably 3 parts by mass or less, more preferably 2 parts by mass or less, and even more preferably 1 part by mass or less.
In the oxidation treatment of the cellulose raw material, if an oxoacid containing chlorine or a salt thereof is used as an oxidizing agent, and then the water washing step is performed, then the fibrillation treatment is performed. , the content of the chlorine-containing oxoacid or its salt is less than 0.0001 part by mass with respect to 100 parts by mass of fine fibrous cellulose.

<Fine fibrous cellulose-containing composition>
In the present invention, the fine fibrous cellulose-containing composition may contain components other than fine fibrous cellulose and chlorine-containing oxoacids or salts thereof. Other ingredients may include, for example, water-soluble polymers and surfactants.
Examples of water-soluble polymers include carboxyvinyl polymer, polyvinyl alcohol, alkyl methacrylate/acrylic acid copolymer, polyvinylpyrrolidone, sodium polyacrylate, polyethylene glycol, diethylene glycol, triethylene glycol, polyethylene oxide, propylene glycol, dipropylene glycol, Synthetic water-soluble polymers exemplified by polypropylene glycol, isoprene glycol, hexylene glycol, 1,3-butylene glycol, and polyacrylamide; xanthan gum, guar gum, tamarind gum, carrageenan, locust bean gum, quince seed, alginic acid, pullulan , carrageenan, and pectin; cellulose derivatives, such as carboxymethylcellulose, methylcellulose, and hydroxyethylcellulose; cationized starch, raw starch, oxidized starch, etherified starch, esterified starch , and starches exemplified by amylose; glycerins exemplified by glycerin, diglycerin, and polyglycerin; hyaluronic acid, metal salts of hyaluronic acid, and the like.
The content of the water-soluble polymer in the composition containing fine fibrous cellulose is, for example, preferably 0.05 parts by mass or more, and 0.1 parts by mass or more, relative to 100 parts by mass of fine fibrous cellulose. is more preferable, and 0.5 parts by mass or more is even more preferable. On the other hand, the content of the water-soluble polymer in the composition containing fine fibrous cellulose is preferably 500 parts by mass or less, and preferably 200 parts by mass or less with respect to 100 parts by mass of fine fibrous cellulose. is more preferable, and 100 parts by mass or less is even more preferable. By setting the content of the water-soluble polymer within the above range, both the properties of the fine fibrous cellulose and the properties of the water-soluble polymer can be expressed.

As surfactants, nonionic surfactants, anionic surfactants, cationic surfactants, and amphoteric surfactants can be used. Examples of nonionic surfactants include polyoxyalkylene alkyl ethers, polyglycerin fatty acid esters, glycerin mono-fatty acid esters, glycerin di-fatty acid esters, pluronics, sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, sucrose fatty acid esters, poly Oxyethylene acyl esters, alkyl polyglycosides, fatty acid methyl glycoside esters, alkyl methyl glucamides, fatty acid alkanolamides, and the like. Examples of anionic surfactants include sodium oleate, potassium oleate, sodium laurate, sodium todecylbenzenesulfonate, sodium alkylnaphthalenesulfonate, sodium dialkylsulfosuccinate, sodium polyoxyethylene alkyl ether sulfate, polyoxy Examples include sodium ethylene alkyl allyl ether sulfate, sodium polyoxyethylene dialkyl sulfate, polyoxyethylene alkyl ether phosphate, polyoxyethylene alkyl allyl ether phosphate, and the like. Examples of cationic surfactants include alkyltrimethylammonium salts, dialkyldimethylammonium salts, alkyldimethylbenzylammonium salts, acylaminoethyldiethylammonium salts, acylaminoethyldiethylamine salts, alkylamidopropyldimethylbenzylammonium salts, and alkylpyridinium salts. , quaternary ammonium salts such as alkylpyridinium sulfates, stearamidomethylpyridinium salts, alkylquinolinium salts, alkylisoquinolinium salts, fatty acid polyethylene polyamides, acylaminoethylpyridinium salts, acylcolaminoformylmethylpyridinium salts, Ester-linked amines such as stearoxymethylpyridinium salts, fatty acid triethanolamine, fatty acid triethanolamine formate, trioxyethylene fatty acid triethanolamine, cetyloxymethylpyridinium salts, p-isooctylphenoxyethoxyethyldimethylbenzylammonium salts, and Ether-linked quaternary ammonium salts, heterocyclic amines such as alkylimidazoline, 1-hydroxyethyl-2-alkylimidazoline, 1-acetylaminoethyl-2-alkylimidazoline, 2-alkyl-4-methyl-4-hydroxymethyloxazoline , polyoxyethylene alkylamines, N-alkylpropylene diamines, N-alkyl polyethylene polyamines, N-alkyl polyethylene polyamine dimethyl sulfates, alkyl biguanides, long-chain amine oxides and other amine derivatives. Amphoteric surfactants include, for example, lauryldimethylaminoacetic acid betaine, cocamidopropyl betaine, lauramidopropyl betaine, sodium cocoamphoacetate and the like.
The content of the surfactant in the composition containing fine fibrous cellulose is preferably 0.01 parts by mass or more, and preferably 0.05 parts by mass or more with respect to 100 parts by mass of fine fibrous cellulose. is more preferable, and 0.1 parts by mass or more is even more preferable. On the other hand, the content of the surfactant in the composition containing fine fibrous cellulose is preferably 5 parts by mass or less, and preferably 3 parts by mass or less with respect to 100 parts by mass of fine fibrous cellulose. More preferably, it is 2 parts by mass or less. By setting the content of the surfactant within the above range, both the properties of the fine fibrous cellulose and the properties of the surfactant can be exhibited.
The fine fibrous cellulose-containing composition contains fine fibrous cellulose, a water-soluble polymer, and a surfactant, as well as organic ions, coupling agents, inorganic stratiform compounds, inorganic compounds, leveling agents, preservatives, and antifoaming agents. , organic particles, lubricants, antistatic agents, UV protection agents, dyes, pigments, stabilizers, magnetic powders, orientation promoters, plasticizers, dispersants, and cross-linking agents. may contain.

The fibrous cellulose containing material may contain a solvent. Solvents can include, for example, one or both of water and organic solvents. Examples of organic solvents include alcohols, polyhydric alcohols, ketones, ethers, esters, hydrocarbons, halogens, and aprotic polar solvents. Examples of alcohols include methanol, ethanol, isopropanol, n-butanol, isobutyl alcohol and the like. Examples of polyhydric alcohols include ethylene glycol, propylene glycol and glycerin. Ketones include acetone, methyl ethyl ketone (MEK), and the like. Examples of ethers include diethyl ether, tetrahydrofuran, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol mono-n-butyl ether, propylene glycol monomethyl ether and the like. Examples of esters include ethyl acetate and butyl acetate. Examples of hydrocarbons include n-hexane, toluene, and xylene. Halogens include methylene chloride, trichlorethylene, chloroform, and the like. Aprotic polar solvents include dimethylsulfoxide (DMSO), dimethylformamide (DMF), dimethylacetamide (DMAc), N-methyl-2-pyrrolidinone (NMP) and the like.

Haze of slurry obtained by adjusting the composition containing fine fibrous cellulose to a fine fibrous cellulose solid content concentration of 0.2% by mass, measured at 23° C. using a glass cell with an optical path length of 1 cm in accordance with JIS K 7136. is preferably 2.0% or less. Further, the haze is more preferably 1.5% or less, still more preferably 1.0% or less. On the other hand, the lower limit of haze is not particularly limited, and may be 0%, for example. By setting the haze of the slurry of the fine fibrous cellulose-containing composition within this range, it is possible to form a sheet or the like with higher transparency.
In this embodiment, the haze meter (HM-150, manufactured by Murakami Color Research Laboratory Co., Ltd.) can be used for measurement. As the glass cell with an optical path length of 1 cm, for example, a liquid glass cell with an optical path length of 1 cm (MG-40, reverse optical path, manufactured by Fujiwara Seisakusho Co., Ltd.) can be used. The zero point measurement is performed with deionized water placed in the same glass cell.
The solvent for the haze measurement preferably contains at least water, and the content of water in the entire solvent is preferably 50% by mass or more, more preferably 70% by mass or more, and still more preferably 90% by mass. % or more, particularly preferably 95 mass % or more, and may be 100 mass %.

In the present invention, the fine fibrous cellulose-containing composition was prepared by adjusting the solid content concentration of fine fibrous cellulose to 0.2% by mass, and the slurry was measured in accordance with JIS K 7361 using a glass cell with an optical path length of 1 cm. The total light transmittance is preferably 90% or more. Further, the total light transmittance is more preferably 93% or more, and even more preferably 95% or more. On the other hand, the upper limit of the total light transmittance is not particularly limited, and may be 100%, for example. By setting the total light transmittance of the slurry of the fine fibrous cellulose-containing composition within such a range, it is possible to form a sheet or the like with higher transparency.
In the present embodiment, the total light transmittance can be measured using, for example, a haze meter (HM-150, manufactured by Murakami Color Research Laboratory Co., Ltd.). As the glass cell with an optical path length of 1 cm, for example, a liquid glass cell with an optical path length of 1 cm (MG-40, reverse optical path, manufactured by Fujiwara Seisakusho Co., Ltd.) can be used. The zero point measurement is performed with deionized water placed in the same glass cell.
The solvent used for measuring the total light transmittance described above preferably contains at least water, and the content of water in the entire solvent is preferably 50% by mass or more, more preferably 70% by mass or more, and even more preferably. is 90% by mass or more, particularly preferably 95% by mass or more, and may be 100% by mass.

The viscosity of the slurry obtained by adjusting the fine fibrous cellulose-containing composition to a fine fibrous cellulose solid content concentration of 0.4% by mass, measured using a Brookfield viscometer at 23° C. and a rotation speed of 3 rpm, is preferably It is 1.0×10 ⁴ mPa·s or less, more preferably 8.5×10 ³ mPa·s or less, and still more preferably 7.0×10 ³ mPa·s or less. Although the lower limit of the viscosity is not particularly limited, it is preferably 1.0×10 ³ mPa·s or more, more preferably 1.5×10 ³ mPa·s or more.
Here, for the measurement of the viscosity, for example, a Brookfield viscometer (manufactured by BLOOKFIELD, analog viscometer T-LVT) can be used. The measurement conditions are as follows: dilute the fine fibrous cellulose-containing composition so that the solid content concentration of fine fibrous cellulose is 0.4% by mass; Allow to stand for 24 hours in an environment with a relative humidity of 50%. Thereafter, measurement is performed at a liquid temperature of 23° C. and a viscometer rotation speed of 3 rpm, for example, and the viscosity value at 3 minutes from the start of measurement is defined as the viscosity of the dispersion.
In addition, the solvent at the viscosity measurement described above preferably contains at least water. % or more, particularly preferably 95 mass % or more, and may be 100 mass %.

The form of the fine fibrous cellulose-containing composition is not particularly limited, but examples thereof include liquids such as slurries, solids such as granules, and gels.
(Slurry)
When the fine fibrous cellulose-containing composition is a slurry, the content of fine fibrous cellulose contained in the fine fibrous cellulose-containing composition is 0.1% by mass with respect to the total mass of the fine fibrous cellulose-containing composition. It is preferably 5.0% by mass or less, more preferably 0.3% by mass or more and 3.0% by mass or less, and even more preferably 0.5% by mass or more and 3.0% by mass or less. . By setting the content of the fine fibrous cellulose within the above range, the properties of the fine fibrous cellulose are easily exhibited.
When the fine fibrous cellulose-containing composition is a slurry and the solvent contained in the fine fibrous cellulose-containing composition is water, the content of the solvent is preferably 60% by mass or more, more preferably 90% by mass or more, more preferably 97% by mass or more, and preferably 99.9% by mass or less, more preferably 99.7% by mass or less, still more preferably 99.5% by mass % or less. By setting the content of the solvent within the above range, a suitable viscosity can be obtained.

(solid or gel)
When the fine fibrous cellulose-containing composition is a solid or gel, the content of fine fibrous cellulose contained in the fine fibrous cellulose-containing composition is, for example, the total mass of the fine fibrous cellulose-containing composition. On the other hand, it is preferably 5% by mass or more, more preferably 10% by mass or more, still more preferably 15% by mass or more, and particularly preferably 20% by mass or more. Further, when the composition containing fine fibrous cellulose is a solid or gel, the upper limit of the content of fine fibrous cellulose contained in the composition containing fine fibrous cellulose is not particularly limited. 0.5 mass %. By setting the content of fine fibrous cellulose within the above range, it is possible to obtain a composition containing fine fibrous cellulose which is more excellent in handleability.

When the composition containing fine fibrous cellulose is a solid or gel, the content of the solvent contained in the composition containing fine fibrous cellulose is, for example, 90% of the total mass of the composition containing fine fibrous cellulose. It is preferably not more than 85% by mass, more preferably not more than 80% by mass, and particularly preferably not more than 70% by mass. By setting the upper limit of the content of the solvent within the above range, a fine fibrous cellulose-containing composition with excellent handleability can be obtained. On the other hand, the lower limit of the solvent content in the fine fibrous cellulose-containing composition is not particularly limited, and may be, for example, 0% by mass. In this embodiment, the content of the solvent contained in the composition containing fine fibrous cellulose can be, for example, 0.5% by mass or more relative to the total mass of the composition containing fine fibrous cellulose.
Moreover, when the fine fibrous cellulose-containing composition is in the form of a solid or a gel, the fine fibrous cellulose-containing composition may contain a thickening agent used, for example, in the concentration step described below. For example, when the thickening agent is a metal component, the content of the metal component in the fine fibrous cellulose-containing composition is preferably 1.0% by mass or less, more preferably 0.3% by mass or less. , is more preferably 0.15% by mass or less, and particularly preferably 0.1% by mass or less. Moreover, when the thickening agent is a metal component, the lower limit of the content of the metal component in the fine fibrous cellulose-containing composition is not particularly limited, but can be, for example, 0.0001% by mass. By setting the content of the metal component within the above range, a fine fibrous cellulose-containing composition having excellent redispersibility in a predetermined dispersion medium such as water can be obtained.

When the fine fibrous cellulose-containing composition is particulate, the fine fibrous cellulose-containing includes one or both of powder and particulate. Here, the powdery substance refers to a substance smaller than the granular substance. In general, powder refers to fine particles having a particle size of 1 nm or more and less than 0.1 mm. In addition, the particulate matter refers to particles having a particle diameter of 0.1 mm or more and 10 mm or less. The particle size of the powder can be measured and calculated using, for example, a laser diffraction method. The measurement by the laser diffraction method can be performed using, for example, a laser diffraction/scattering particle size distribution analyzer (Microtrac 3300EXII, Nikkiso Co., Ltd.).

A fine fibrous cellulose-containing composition, which is a solid or gel, can be used as a redispersed slurry, for example, redispersed in a solvent such as water. The type of solvent used to obtain such a redispersion slurry is not particularly limited, but examples include water, organic solvents, and mixtures of water and organic solvents. Examples of organic solvents include alcohols, polyhydric alcohols, ketones, ethers, esters, hydrocarbons, halogens, and aprotic polar solvents. Examples of alcohols include methanol, ethanol, isopropanol, n-butanol, isobutyl alcohol and the like. Examples of polyhydric alcohols include ethylene glycol, propylene glycol and glycerin. Ketones include acetone, methyl ethyl ketone (MEK), and the like. Examples of ethers include diethyl ether, tetrahydrofuran, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol mono-n-butyl ether, propylene glycol monomethyl ether and the like. Examples of esters include ethyl acetate and butyl acetate. Examples of hydrocarbons include n-hexane, toluene, and xylene. Halogens include methylene chloride, trichlorethylene, chloroform, and the like. Aprotic polar solvents include dimethylsulfoxide (DMSO), dimethylformamide (DMF), dimethylacetamide (DMAc), N-methyl-2-pyrrolidinone (NMP) and the like.

(sheet form)
In the present invention, the fine fibrous cellulose-containing composition may be in the form of a sheet.
In the present embodiment, a sheet can be obtained by carrying out the sheet-forming step described below, for example, using the fine fibrous cellulose-containing composition, which is a liquid material as described above.
The content of fine fibrous cellulose in the sheet is, for example, preferably 0.5% by mass or more, more preferably 1% by mass or more, and 5% by mass or more, relative to the total mass of the sheet. is more preferable, and 10% by mass or more is particularly preferable. On the other hand, the upper limit of the content of fine fibrous cellulose in the sheet is not particularly limited, and may be 100% by mass or 95% by mass with respect to the total mass of the sheet.
In particular, from the viewpoint of obtaining a sheet having excellent mechanical strength, the content of fine fibrous cellulose in the sheet is, for example, preferably 60% by mass or more, more preferably 70% by mass or more, and more preferably 80% by mass. % or more, and particularly preferably 90 mass % or more.
Moreover, from the viewpoint of including a large amount of other materials such as water-soluble polymers in the sheet, the content of fine fibrous cellulose in the sheet is preferably 50% by mass or less, for example.

The sheet may contain, for example, a water-soluble polymer. This can further improve the transparency and mechanical strength of the sheet. As the water-soluble polymer, for example, those mentioned above can be used.
The content of the water-soluble polymer in the sheet is, for example, preferably 1% by mass or more, more preferably 5% by mass or more, and preferably 10% by mass or more, relative to the total mass of the sheet. More preferred. Thereby, a sheet having excellent transparency and mechanical properties can be obtained. On the other hand, the content of the water-soluble polymer in the sheet is preferably 99.5% by mass or less, more preferably 95% by mass or less, relative to the total mass of the sheet.

The sheet contains, in addition to fine fibrous cellulose, chlorine-containing oxoacid or its salt, and water-soluble polymer, for example, surfactants, organic ions, coupling agents, inorganic layered compounds, inorganic compounds, leveling agents, preservatives. , antifoaming agents, organic particles, lubricants, antistatic agents, UV protection agents, dyes, pigments, stabilizers, magnetic powders, orientation accelerators, plasticizers, dispersants, and cross-linking agents, or Two or more types may be included.
The sheet may contain a solvent. As the solvent, for example, those mentioned above can be used.
The solvent content in the sheet is, for example, preferably 0.5% by mass or more, more preferably 1% by mass or more, and further preferably 5% by mass or more, relative to the total mass of the sheet. preferable. Thereby, flexibility can be imparted to the sheet. On the other hand, the solvent content in the sheet is, for example, preferably 25% by mass or less, more preferably 15% by mass or less, relative to the total mass of the sheet. Thereby, a sheet having good flexibility can be obtained.
The water content in the sheet can be calculated, for example, by the following procedure. First, a 100 mm square sheet is conditioned at a temperature of 23° C. and a relative humidity of 50% for 24 hours, and then the mass W ₀ of the sheet is measured. Next, the sheet is dried in a constant temperature dryer at 105° C. for 16 hours, and then the mass _W1 of the sheet is measured. From the measured mass, the solvent content in the sheet is calculated according to the following formula (1).
Water content in sheet = 100 x (1-W ₁ /W ₀ ) Formula (1)

The tensile modulus of the sheet is, for example, preferably 2.5 GPa or more, more preferably 3.0 GPa or more, and even more preferably 3.5 GPa or more. Also, the upper limit of the tensile modulus of elasticity of the sheet is not particularly limited, but can be, for example, 50 GPa or less.
Here, the tensile modulus of elasticity of the sheet is a value measured using a tensile tester Tensilon (manufactured by A&D Co., Ltd.), for example, according to JIS P 8113. When measuring the tensile modulus, the test piece for measurement is conditioned at 23° C. and 50% relative humidity for 24 hours, and the measurement is performed under the conditions of 23° C. and 50% relative humidity.
The haze of the sheet is, for example, preferably 2% or less, more preferably 1.5% or less, even more preferably 1% or less. On the other hand, the lower limit of haze of the sheet is not particularly limited, and may be 0%, for example. Here, the haze of the sheet is a value measured using a haze meter (HM-150, manufactured by Murakami Color Research Laboratory Co., Ltd.) in accordance with JIS K 7136, for example.
The total light transmittance of the sheet is, for example, preferably 85% or more, more preferably 90% or more, even more preferably 91% or more. On the other hand, the upper limit of the total light transmittance of the sheet is not particularly limited, and may be 100%, for example. Here, the total light transmittance of the sheet is a value measured using a haze meter (HM-150, manufactured by Murakami Color Research Laboratory Co., Ltd.) in accordance with JIS K 7361, for example.

Although the thickness of the sheet is not particularly limited, it is preferably 5 μm or more, more preferably 10 μm or more, and even more preferably 20 μm or more. The upper limit of the thickness of the sheet is not particularly limited, but can be set to 1000 μm, for example. The thickness of the sheet can be measured, for example, with a stylus thickness gauge (Millitron 1202D, manufactured by Marr Co.).
Although the basis weight of the sheet is not particularly limited, it is preferably 10 g/m ² or more, more preferably 20 g/m ² or more, and even more preferably 30 g/m ² or more. The basis weight of the sheet is not particularly limited, but is preferably 100 g/m ² or less, more preferably 80 g/m ² or less. Here, the basis weight of the sheet can be calculated according to JIS P 8124, for example.
The density of the sheet is not particularly limited, but is preferably 0.1 g/cm ³ or more, more preferably 0.5 g/cm ³ or more, and further preferably 1.0 g/cm ³ or more. preferable. The density of the sheet is not particularly limited, but is preferably 5.0 g/cm ³ or less, more preferably 3.0 g/cm ³ or less. Here, the density of a sheet can be calculated by measuring the thickness and mass of a 50 mm square sheet after conditioning the humidity for 24 hours under conditions of 23° C. and 50% RH.

[Method for producing fine fibrous cellulose-containing composition]
In the present invention, the fine fibrous cellulose described above is preferably produced by a method comprising the following steps 1 and 2 in this order.
Step 1: A step of defibrating fibrous cellulose in a solvent to obtain a dispersion containing fine fibrous cellulose Step 2: Adding an oxoacid containing chlorine or a salt thereof to the dispersion containing fine fibrous cellulose Step of adding In the present invention, the amount of the chlorine-containing oxoacid or its salt added in step 2 is 0.0001 parts by mass or more and 10 parts by mass or less with respect to 100 parts by mass of fine fibrous cellulose. .
Here, the step of obtaining a dispersion liquid containing fine fibrous cellulose in step 1 includes an ionic substituent for introducing an ionic substituent into a fiber raw material containing cellulose, as described in the method for producing fine fibrous cellulose. It is preferable to have an introduction step, a washing step, an alkali treatment step (neutralization step), and a fibrillation treatment step in this order, and an acid treatment step may be provided instead of or in addition to the washing step good. Examples of the ionic substituent introduction step include a phosphate group introduction step and a carboxy group introduction step. Therefore, in the present invention, the fine fibrous cellulose in the dispersion liquid containing fine fibrous cellulose obtained in step 1 preferably has an ionic substituent.

In step 2, a chlorine-containing oxoacid or a salt thereof is added to the dispersion containing fine fibrous cellulose. The method of addition is not particularly limited, but the amount of oxoacid containing chlorine or its salt to be added is 0.0001 parts by mass or more and 10 parts by mass or less with respect to 100 parts by mass of fine fibrous cellulose.
The addition of the chlorine-containing oxoacid or its salt is preferably carried out with stirring so that the chlorine-containing oxoacid or its salt does not exist in the dispersion at a high concentration.

The fibrous cellulose-containing composition of the present invention can be used for various purposes, for example, as a thickening agent. Moreover, it can be mixed with a resin or emulsion and used as a reinforcing material, or a slurry of a fine fibrous cellulose-containing composition can be used to form a film to produce various sheets. The sheet is suitable for use as a light-transmitting substrate for various display devices, various solar cells, and the like. It is also suitable for applications such as substrates for electronic equipment, members for household appliances, window materials for various vehicles and buildings, interior materials, exterior materials, packaging materials, and the like. Furthermore, it is also suitable for applications in which the sheet itself is used as a reinforcing material, in addition to threads, filters, fabrics, cushioning materials, sponges, abrasives, and the like.

EXAMPLES The characteristics of the present invention will be described more specifically below with reference to examples and comparative examples. The materials, amounts used, proportions, treatment details, treatment procedures, etc. shown in the following examples can be changed as appropriate without departing from the gist of the present invention. Therefore, the scope of the present invention should not be construed to be limited by the specific examples shown below.

<Production Example 1>
As raw material pulp, softwood kraft pulp manufactured by Oji Paper Co., Ltd. (solid content 93% by mass, basis weight 208 g / m ² sheet, defibered and Canadian standard freeness (CSF) measured according to JIS P 8121 700 mL) It was used. The raw material pulp was subjected to a phosphorylation treatment as follows. First, a mixed aqueous solution of ammonium dihydrogen phosphate and urea is added to 100 parts by mass (absolute dry mass) of the raw material pulp to obtain 45 parts by mass of ammonium dihydrogen phosphate, 120 parts by mass of urea, and 150 parts by mass of water. A chemical-impregnated pulp was obtained by preparing as follows. Next, the resulting chemical solution-impregnated pulp was heated in a hot air dryer at 165° C. for 200 seconds to introduce phosphoric acid groups into cellulose in the pulp to obtain phosphorylated pulp.

Then, the obtained phosphorylated pulp was washed. In the washing treatment, a pulp dispersion liquid obtained by pouring 10 L of ion-exchanged water into 100 g (absolute dry mass) of phosphorylated pulp is stirred so that the pulp is uniformly dispersed, and then filtration and dehydration are repeated. gone. The washing was finished when the electric conductivity of the filtrate became 100 μS/cm or less.

Next, the washed phosphorylated pulp was subjected to alkali treatment (neutralization treatment) as follows. First, the washed phosphorylated pulp was diluted with 10 L of ion-exchanged water, and then a 1N sodium hydroxide aqueous solution was added little by little while stirring to obtain a phosphorylated pulp slurry having a pH of 12 or more and 13 or less. . Next, the phosphorylated pulp slurry was dehydrated to obtain alkali-treated (neutralized) phosphorylated pulp.

Next, the washing treatment was performed on the phosphorylated pulp after the neutralization treatment. The phosphorylated pulp thus obtained was subjected to infrared absorption spectrum measurement using FT-IR. As a result, absorption due to phosphate groups was observed near 1230 cm ⁻¹ , confirming that phosphate groups were added to the pulp. In addition, when the obtained phosphorylated pulp was tested and analyzed with an X-ray diffraction device, it was found that the A typical peak was confirmed, confirming that it had cellulose type I crystals.

(defibration treatment)
Ion-exchanged water was added to the obtained phosphorylated pulp to prepare a slurry having a solid content concentration of 2% by mass. This slurry was treated four times at a pressure of 200 MPa with a wet atomization device (Starburst, manufactured by Sugino Machine Co., Ltd.) to obtain a fine fibrous cellulose dispersion (A) containing fine fibrous cellulose.

X-ray diffraction confirmed that this fine fibrous cellulose maintained cellulose type I crystals.
Further, when the fiber width of the fine fibrous cellulose was measured using a transmission electron microscope, it was 3 to 5 nm. The amount of phosphate groups (strongly acidic group amount) measured by the measurement method described later was 1.45 mmol/g.

(Measurement of phosphate group content)
The phosphate group content of the fine fibrous cellulose is obtained by diluting a fine fibrous cellulose dispersion containing the target fine fibrous cellulose with ion-exchanged water so that the content becomes 0.2% by mass. It was measured by titration with an alkali after treating the cellulose-containing slurry with an ion-exchange resin.
The ion-exchange resin treatment was carried out by adding 1/10 by volume of a strongly acidic ion-exchange resin (Amberjet 1024; manufactured by Organo Co., Ltd., conditioned) to the fine fibrous cellulose-containing slurry and shaking for 1 hour. After that, the slurry was separated from the resin by pouring it onto a mesh with an opening of 90 μm.
In addition, titration with an alkali was carried out by adding a 0.1 N sodium hydroxide aqueous solution to the fine fibrous cellulose-containing slurry after treatment with an ion exchange resin, and adding 50 μL of the slurry once every 30 seconds. It was carried out by measuring the change in the degree value. The amount of phosphate groups (mmol/g) is obtained by dividing the alkali amount (mmol) required in the region corresponding to the first region shown in FIG. 1 among the measurement results by the solid content (g) in the slurry to be titrated. calculated by

<Production Example 2>
Softwood kraft pulp (undried) manufactured by Oji Paper Co., Ltd. was used as raw material pulp. The raw material pulp was subjected to alkali TEMPO oxidation treatment as follows.
First, the raw pulp equivalent to 100 parts by mass of dry mass, 1.6 parts by mass of TEMPO (2,2,6,6-tetramethylpiperidine-1-oxyl), 10 parts by mass of sodium bromide, and 10000 parts by mass of water distributed in parts. Then, a 13% by mass sodium hypochlorite aqueous solution was added to 3.8 mmol with respect to 1.0 g of pulp to initiate the reaction. During the reaction, a 0.5 M sodium hydroxide aqueous solution was added dropwise to maintain the pH at 10 or more and 10.5 or less, and the reaction was considered completed when no change in pH was observed.

Then, the obtained TEMPO oxidized pulp was washed. The washing treatment is performed by dehydrating the pulp slurry after TEMPO oxidation to obtain a dehydrated sheet, pouring 5000 parts by mass of ion-exchanged water, stirring to uniformly disperse, and then filtering and dehydrating repeatedly. rice field. The washing was finished when the electric conductivity of the filtrate became 100 μS/cm or less.

This dehydrated sheet was subjected to a post-oxidation treatment for residual aldehyde groups as follows. The dehydrated sheet equivalent to 100 parts by mass of dry mass was dispersed in 10000 parts by mass of 0.1 mol/L acetate buffer (pH 4.8). Next, 113 parts by mass of 80% sodium chlorite was added, and the mixture was immediately sealed, followed by reaction at room temperature for 48 hours while stirring at 500 rpm using a magnetic stirrer to obtain a pulp slurry.

Then, the obtained after-oxidized TEMPO oxidized pulp was washed. The washing treatment is carried out by dehydrating the post-oxidized pulp slurry to obtain a dehydrated sheet, pouring 5000 parts by mass of ion-exchanged water, stirring to uniformly disperse, and then filtering and dehydrating repeatedly. rice field. The washing was finished when the electric conductivity of the filtrate became 100 μS/cm or less.

The TEMPO-oxidized pulp thus obtained had a carboxy group content of 1.30 mmol/g as measured by the method described later.

In addition, when the obtained TEMPO oxidized pulp was tested and analyzed with an X-ray diffraction device, it was found that the A typical peak was confirmed, confirming that it had cellulose type I crystals.

(defibration treatment)
Ion-exchanged water was added to the obtained TEMPO oxidized pulp to prepare a slurry having a solid content concentration of 2% by mass. This slurry was treated four times at a pressure of 200 MPa with a wet atomization device (Starburst, manufactured by Sugino Machine Co., Ltd.) to obtain a fine fibrous cellulose dispersion (B) containing fine fibrous cellulose.

X-ray diffraction confirmed that this fine fibrous cellulose maintained cellulose type I crystals.
Further, when the fiber width of the fine fibrous cellulose was measured using a transmission electron microscope, it was 3 to 5 nm. In addition, the amount of carboxyl groups measured by the measuring method described later was 1.30 mmol/g.

(Measurement of carboxy group content)
The carboxy group content of the fine fibrous cellulose is obtained by diluting a fine fibrous cellulose dispersion containing the target fine fibrous cellulose with ion-exchanged water so that the content is 0.2% by mass. The cellulose-containing slurry was treated with an ion-exchange resin and then titrated with an alkali for measurement.
The ion-exchange resin treatment was carried out by adding 1/10 by volume of a strongly acidic ion-exchange resin (Amberjet 1024; manufactured by Organo Co., Ltd., conditioned) to the fine fibrous cellulose-containing slurry and shaking for 1 hour. After that, the slurry was separated from the resin by pouring it onto a mesh with an opening of 90 μm.
In addition, titration with an alkali is carried out by adding 50 μL of a 0.1N sodium hydroxide aqueous solution once every 30 seconds to the fine fibrous cellulose-containing slurry after treatment with an ion-exchange resin. This was done by measuring the change in the value of The amount of carboxyl groups (mmol/g) is obtained by dividing the alkali amount (mmol) required in the region corresponding to the first region shown in FIG. 2 among the measurement results by the solid content (g) in the slurry to be titrated. Calculated.

<Example 1>
Take 100 g of the fine fibrous cellulose dispersion (A) (2% by mass), dilute a sodium hypochlorite solution with an effective chlorine concentration of 12% with ion-exchanged water 100 times, and take 0.17 g. After addition to the fine fibrous cellulose, it was stirred. Thus, a composition containing fine fibrous cellulose and 0.01 parts by mass of sodium hypochlorite per 100 parts by mass of fine fibrous cellulose was obtained.

<Example 2>
In Example 1, the sodium hypochlorite solution having an effective chlorine concentration of 12% was diluted 100 times with deionized water, and the amount added was changed to 2.5 g. Everything else was tested in the same manner as in Example 1.

<Example 3>
In Example 1, the sodium hypochlorite solution having an effective chlorine concentration of 12% was not diluted, and the amount added was changed to 0.17 g. Everything else was tested in the same manner as in Example 1.

<Example 4>
In Example 2, instead of sodium hypochlorite with an effective chlorine concentration of 12%, potassium hypochlorite with an effective chlorine concentration of 12% was used. Everything else was tested in the same manner as in Example 2.

<Example 5>
In Example 2, instead of the fine fibrous cellulose dispersion (A) made from phosphorylated pulp, a fine fibrous cellulose dispersion (B) made from TEMPO oxidized pulp was used. Everything else was tested in the same manner as in Example 2.

<Comparative Example 1>
In Example 1, the sodium hypochlorite solution having an effective chlorine concentration of 12% was diluted 100,000 times with deionized water, and the amount added was changed to 0.17 g. Everything else was tested in the same manner as in Example 1.

<Comparative Example 2>
In Example 1, the sodium hypochlorite solution having an effective chlorine concentration of 12% was not diluted, and the amount added was changed to 8.3 g. Everything else was tested in the same manner as in Example 1.

<Comparative Example 3>
In Comparative Example 2, instead of sodium hypochlorite with an effective chlorine concentration of 12%, potassium hypochlorite with an effective chlorine concentration of 12% was used. Everything else was tested in the same manner as in Comparative Example 2.

<Comparative Example 4>
In Example 1, no sodium hypochlorite solution was added. Everything else was tested in the same manner as in Example 1.

<Comparative Example 5>
In Example 5, no sodium hypochlorite solution was added. Everything else was tested in the same manner as in Example 5.

(Measurement of fiber width of fine fibrous cellulose)
The fiber width of fine fibrous cellulose was measured by the following method.
The supernatant liquid of the above-mentioned fine fibrous cellulose dispersion obtained by treatment with a wet atomization device is diluted with water so that the concentration of fine fibrous cellulose is 0.01% by mass or more and 0.1% by mass or less. It was diluted and added dropwise to a hydrophilized carbon grid film. After drying, it was stained with uranyl acetate and observed with a transmission electron microscope (JEOL-2000EX, manufactured by JEOL Ltd.).

(Measurement of viscosity of fine fibrous cellulose dispersion)
The viscosity of the fine fibrous cellulose dispersion was measured as follows. First, the fine fibrous cellulose dispersion was diluted with ion-exchanged water so that the solid content concentration was 0.4% by mass, and then stirred at 1500 rpm for 5 minutes with a disperser. Then, the viscosity of the resulting dispersion was measured using a Brookfield viscometer (manufactured by BLOOKFIELD, analog viscometer T-LVT). The measurement conditions were a rotation speed of 3 rpm, and the viscosity value after 3 minutes from the start of measurement was taken as the viscosity of the dispersion. In addition, the dispersion liquid to be measured was allowed to stand in an environment of 23° C. and 50% relative humidity for 24 hours before the measurement. The liquid temperature of the dispersion liquid at the time of measurement was 23°C.

(Measurement of Specific Viscosity and Degree of Polymerization of Cellulose Fiber)
The specific viscosity and degree of polymerization of cellulose fibers were measured according to Tappi T230. That is, the viscosity (η ₁ (unit: cP)) measured by dispersing the cellulose fiber to be measured in the dispersion medium and the blank viscosity (η ₀ (unit: cP)) measured only with the dispersion medium are After the measurement, specific viscosity (η _sp ) and intrinsic viscosity ([η] (unit; mL/g)) were measured according to the following formulas.
η _sp = (η ₁ /η ₀ )-1
[η]=η _sp /(c(1+0.28×η _sp ))
Here, c in the formula indicates the concentration (g/mL) of cellulose fibers at the time of viscosity measurement.
Furthermore, the degree of polymerization (DP) of the cellulose fiber was calculated from the following formula.
DP = 1.75 x [η]
Since this degree of polymerization is an average degree of polymerization measured by a viscosity method, it is sometimes referred to as a "viscosity average degree of polymerization".

(Measurement of haze of fine fibrous cellulose dispersion)
The haze of the fine fibrous cellulose dispersion is measured by diluting the fine fibrous cellulose dispersion after the fibrillation treatment step with ion-exchanged water to a concentration of 0.2% by mass, stirring the mixture sufficiently, and measuring the haze with a haze meter. (Murakami Color Research Laboratory, HM-150), using a glass cell for liquids with an optical path length of 1 cm (Fujiwara Seisakusho Co., Ltd., MG-40, reverse light path), measured in accordance with JIS K 7136 did.
The zero point measurement was performed with ion-exchanged water in the same glass cell. In addition, the dispersion liquid to be measured was allowed to stand in an environment of 23° C. and 50% relative humidity for 24 hours before the measurement. The liquid temperature of the dispersion liquid at the time of measurement was 23°C.

(Confirmation of discoloration of fine fibrous cellulose dispersion)
The 0.4% by mass fine fibrous cellulose dispersion was visually observed to confirm the presence or absence of discoloration.

As shown in the examples, focusing on the viscosity, the viscosity of Comparative Example 4, which does not contain chlorine-containing oxoacids or salts thereof, is 11253 mPa s, while Examples 1 to 4 are about 15 to 80% of that. It is thought that a moderate viscosity reduction could be achieved by a simple operation. On the other hand, the viscosity of Comparative Example 1 is too high, so it is unsuitable for the present invention in which the viscosity should be moderately lowered. In Comparative Examples 2 and 3, clear yellowing of the samples was observed, impairing the colorless and transparent characteristics of the fine fibrous cellulose composition.
In addition, the viscosity of Comparative Example 5, which does not contain an oxoacid containing chlorine or a salt thereof, was 19,700 mPa s, whereas the viscosity of Example 5 was about 30% of that. Even when fibrous cellulose was used, it is considered that a moderate viscosity reduction could be achieved by a simple operation. Since Comparative Example 5 has too high a viscosity, it is unsuitable for the present invention in which the viscosity is desired to be moderately lowered.
As for haze, Examples 1 to 4 and Comparative Examples 1 to 3 are not much different from Comparative Example 4. However, yellowing of the dispersion was observed in Comparative Examples 2 and 3 in which the amount of the chlorine-containing oxoacid or salt thereof exceeded the range of the present invention.

INDUSTRIAL APPLICABILITY According to the present invention, it is possible to provide a fine fibrous cellulose composition easily and precisely adjusted to an arbitrary viscosity. In order to adjust the viscosity of fine fibrous cellulose, conventional methods require defibration treatment using a fibrillation machine, and in this method, precise viscosity adjustment is difficult and the procedure is complicated.
The present invention solves these problems, and is expected to be used in various applications such as thickening agents for cosmetics and foods, and composites with resins.

Claims (6)

Containing fine fibrous cellulose having an anionic group with a fiber width of 1,000 nm or less and an oxoacid containing chlorine or a salt thereof,
The content of oxoacid containing chlorine or a salt thereof is less than 0.0001 part by weight with respect to 100 parts by weight of fine fibrous cellulose . , 0.0001 parts by mass or more and 10 parts by mass or less ,
Chlorine-containing oxoacid or salt thereof contains at least one selected from the group consisting of sodium hypochlorite, potassium hypochlorite and calcium hypochlorite,
A composition containing fine fibrous cellulose. When the solid content concentration of fine fibrous cellulose is 0.4% by mass, the viscosity of the composition measured by rotating at 23 ° C. for 3 minutes at a rotation speed of 3 rpm using a Brookfield viscometer is 1.0. 2. The fine fibrous cellulose-containing composition according to claim 1, which has a viscosity of ×10 ⁴ mPa·s or less. 3. The composition containing fine fibrous cellulose according to claim 1, wherein the content of the anionic group is 0.60 mmol/g or more relative to the fine fibrous cellulose. 4. The composition containing fine fibrous cellulose according to any one of claims 1 to 3 , wherein the composition has a haze of 1.5% or less at 23°C when the solid content concentration of the fine fibrous cellulose is 0.2% by mass. . The fine fibrous cellulose-containing composition according to any one of claims 1 to 4 , wherein the amount of the chlorine-containing oxoacid or its salt added to 100 parts by mass of the fine fibrous cellulose is 0.005 parts by mass or more and 2 parts by mass or less. thing. A step of defibrating fibrous cellulose in a solvent to obtain a dispersion containing fine fibrous cellulose, and a step of adding an oxoacid containing chlorine or a salt thereof to the dispersion containing fine fibrous cellulose. have
The amount of oxoacid containing chlorine or a salt thereof added to 100 parts by mass of fine fibrous cellulose is 0.0001 part by mass or more and 10 parts by mass or less,
fibrous cellulose has an anionic group,
Chlorine-containing oxoacid or salt thereof contains at least one selected from the group consisting of sodium hypochlorite, potassium hypochlorite and calcium hypochlorite,
A method for producing a composition containing fine fibrous cellulose.