JP7134116B2 - Inkjet ink composition for building materials, image recording method and image recorded matter - Google Patents

Description

TECHNICAL FIELD The present disclosure relates to an inkjet ink composition for building materials, an image recording method, and an image recorded matter.

2. Description of the Related Art Conventionally, various studies have been made on inks used for recording images.
For example, Patent Document 1 describes (A) N-vinyl as an ink composition that ensures long-term storage stability, has excellent continuous ejection property, hue of an image obtained by curing, and adhesion to a substrate. It contains lactams, (B) other polymerizable compounds, (C) a polymerization initiator, and (D) a basic compound, and (A) N-vinyl lactams are less than 15% by weight of the total weight of the ink composition. Disclosed is an ink composition comprising:
Moreover, in Patent Document 2, C.I. I. Pigment Yellow 42 (PY42), a basic polymer dispersant, a polymerization initiator, and a polymerizable compound, the pH of PY42 is 3 to 6, and the basic polymer dispersant has an amine value of 10 Disclosed is an ink composition for inkjet recording characterized by ∼45 mg KOH/g.
Further, in Patent Document 3, as a yellow ink for inkjet that is dark in color, has excellent ink stability, and has excellent weather resistance that can be used for outdoor materials such as siding materials, a yellow pigment (a) Disclosed is a yellow inkjet ink containing Sea Eye Pigment Yellow 42 and (b) Sea Eye Pigment Red 101. US Pat.
Further, in Patent Document 4, the ink has excellent wettability after landing on the recording surface of a recording medium made of a polyolefin material such as polyethylene or polypropylene having a low wetting tension, and the solid portion is uniformly coated without repelling or unevenness. As a photocurable inkjet ink composition that can obtain a high-quality image in a short time without dot shapes in fine line portions and pattern edge portions and without bleeding, pigments and polymerizable compounds are used. Disclosed is a photocurable ink for inkjet printers, which comprises a mixture and a photopolymerization initiator, and contains 3 to 12% by weight of a fluorine-containing (meth)acrylate as one component of the mixture of polymerizable compounds. It is

Japanese Unexamined Patent Application Publication No. 2008-201876 JP 2014-47236 A JP 2009-149719 A JP 2006-056958 A

However, in Patent Documents 1 to 4, no consideration is given to the adhesion and abrasion resistance of images over time in an outdoor environment when images are recorded on building materials.
An object of one aspect of the present disclosure is to provide an inkjet ink composition for building materials and an image recording method capable of recording an image on building materials with excellent adhesion over time and abrasion resistance over time in an outdoor environment, and building materials and the outdoor environment. An object of the present invention is to provide an image recorded matter having an image excellent in adhesion under a background and abrasion resistance over time.

Specific means for solving the problems include the following aspects.
<1> a monomer A that is a polymerizable monomer having a fluorine atom;
an inorganic pigment containing at least one element selected from the group consisting of cobalt, aluminum, iron, bismuth, vanadium, titanium and carbon;
An inkjet ink composition for building materials containing
<2> The inorganic pigment is C.I. I. Pigment Blue 28, C.I. I. Pigment Red 101, C.I. I. Pigment Yellow 42, C.I. I. Pigment Yellow 184, C.I. I. Pigment White 6 and C.I. I. The inkjet ink composition for building materials according to <1>, which is at least one selected from the group consisting of Pigment Black 7.
<3> The inkjet ink composition for building materials according to <1> or <2>, further comprising a monomer B that is a (meth)acrylate compound that has an aromatic ring and does not have a fluorine atom.
<4> The inkjet ink composition for building materials according to any one of <1> to <3>, further comprising a monomer C that is N-vinylcaprolactam.
<5> Furthermore, it contains a monomer B which is a (meth)acrylate compound having an aromatic ring and which does not have a fluorine atom, and a monomer C which is an N-vinylcaprolactam,
The inkjet ink composition for building materials according to <1> or <2>, wherein the ratio of the content of monomer A to the total content of monomer B and monomer C is 0.004 to 1.
<6> The inkjet ink for building materials according to any one of <1> to <5>, further comprising a monomer D which is a radically polymerizable monomer having an aliphatic cyclic structure and having no fluorine atom. Composition.
<7> Furthermore, at least one compound selected from the group consisting of an organic solvent, an alkyl (meth)acrylate having an alkyl group having 1 to 4 carbon atoms, and styrene which may have a substituent other than a fluorine atom. The inkjet ink composition for building materials according to any one of <1> to <6>, which contains H.
<8> The content of the compound H is 0.05% by mass to 35% by mass with respect to the total content of all the polymerizable monomers contained in the inkjet ink composition for building materials. An inkjet ink composition for building materials.
<9> The inkjet ink composition for building materials according to any one of <1> to <8>, further comprising a photopolymerization initiator.
<10> The inkjet ink composition for building materials according to any one of <1> to <9>, which is an inkjet ink composition for polyvinyl chloride building materials.
<11> A step of applying the inkjet ink composition for building materials according to any one of <1> to <10> onto a building material by an inkjet method;
A step of irradiating the inkjet ink composition for building materials applied on the building material with an active energy ray;
An image recording method comprising:
<12> The image recording method according to <11>, wherein the building material is a polyvinyl chloride building material.
<13> building materials;
an image, which is a cured product of the inkjet ink composition for building materials according to any one of <1> to <10>, placed on the building material;
image recording.
<14> The image recorded matter according to <13>, wherein the building material is a polyvinyl chloride building material.

According to one aspect of the present disclosure, an inkjet ink composition for building materials and an image recording method capable of recording an image with excellent adhesion and abrasion resistance over time on building materials in outdoor environments, and building materials and outdoor environments Provided is an image recorded matter having an image excellent in adhesion over time and resistance to rubbing over time.

In the present disclosure, a numerical range represented using "to" means a range including the numerical values described before and after "to" as lower and upper limits.
In the present disclosure, the amount of each component in the composition means the total amount of the above substances present in the composition unless otherwise specified when there are multiple substances corresponding to each component in the composition. do.
In the numerical ranges described step by step in the present disclosure, the upper or lower limit value described in a certain numerical range may be replaced with the upper or lower limit value of another numerical range described step by step, Alternatively, the values shown in the examples may be substituted.
In the present disclosure, the term "process" includes not only independent processes, but also processes that cannot be clearly distinguished from other processes, as long as the intended purpose of the process is achieved.
In the present disclosure, combinations of preferred aspects are more preferred aspects.
In the present disclosure, "light" is a concept that includes active energy rays such as γ-rays, β-rays, electron beams, ultraviolet rays, and visible rays.
In the present disclosure, ultraviolet rays may be referred to as "UV (Ultra Violet) light".
In the present disclosure, "(meth) acrylic acid" is a concept that includes both acrylic acid and methacrylic acid, "(meth) acrylate" is a concept that includes both acrylate and methacrylate, and "(meth) ) acrylamide” is a concept that includes both acrylamide and methacrylamide, and “(meth)acryloyl group” is a concept that includes both acryloyl group and methacryloyl group.
In this disclosure, "C.I." means Color Index.

In the present disclosure, "ink-jet ink composition for building materials" means an inkjet ink composition used for recording images on building materials.
Further, in the present disclosure, the term "image" means a film in general formed using the inkjet ink composition for building materials, and the terms "image recording" and "image recording" refer to film formation and film formation, respectively. means formation.
Also, the concept of "image" in the present disclosure includes a solid image.

[Inkjet ink composition for building materials]
The inkjet ink composition for building materials of the present disclosure (hereinafter also simply referred to as "ink") is a group consisting of monomer A, which is a polymerizable monomer having a fluorine atom, cobalt, aluminum, iron, bismuth, vanadium, titanium, and carbon. and an inorganic pigment containing at least one element selected from

According to the ink of the present disclosure, it is possible to record an image on a building material with excellent adhesion over time and abrasion resistance over time in an outdoor environment.
Here, the term "adhesion over time" means the adhesion between a building material and an image over time in an outdoor environment.
In addition, the abrasion resistance over time means the abrasion resistance of an image after aging in an outdoor environment.
Although adhesion over time and abrasion resistance over time are fundamentally different performances, they may be correlated with each other. For example, as a result of improved adhesion over time, abrasion resistance over time may be improved.

The reason why the ink of the present disclosure exhibits the effect of the image adhesion over time and abrasion resistance over time is presumed as follows. However, the inks of the present disclosure are not limited for the following reasons.

In images recorded on building materials, the adhesiveness and aging of images change over time due to components such as moisture, acid rain, oil, sulfur oxides (SOx), and nitrogen oxides (NOx) in the air in an outdoor environment. Abrasion resistance may decrease.
In this regard, in the image recorded with the ink of the present disclosure, fluorine atoms derived from the monomer A are unevenly distributed on the surface of the image. As a result, it is thought that the deterioration of the image adhesion and abrasion resistance over time in an outdoor environment can be suppressed.

In addition, the ink of the present disclosure contains an inorganic pigment (hereinafter also referred to as "specific inorganic pigment") containing at least one element selected from the group consisting of cobalt, aluminum, iron, bismuth, vanadium, titanium and carbon. do.
The specific inorganic pigment is a pigment that is excellent in weather resistance, that is, durability in an outdoor environment. For this reason, the fact that the ink of the present disclosure contains the specific inorganic pigment is also considered to contribute to the effect of the adhesion over time and the abrasion resistance over time in an outdoor environment.

<Specific inorganic pigment>
The ink of the present disclosure contains at least one specific inorganic pigment (that is, an inorganic pigment containing at least one element selected from the group consisting of cobalt, aluminum, iron, bismuth, vanadium, titanium and carbon).
As the specific inorganic pigment, known pigments (for example, pigments described in Color Index (C.I.), etc.) can be used.

From the viewpoint of adhesion over time and abrasion resistance over time, C.I. I. Pigment Blue 28, C.I. I. Pigment Red 101, C.I. I. Pigment Yellow 42, C.I. I. Pigment Yellow 184, C.I. I. Pigment 6 and C.I. I. At least one selected from the group consisting of Pigment Black 7 is preferred.

-Pigment Blue 28-
C. I. Pigment Blue 28 (hereinafter also simply referred to as PB28) is a cyan inorganic pigment composed of cobalt aluminate. PB28 that can be used in the ink of the present disclosure is not particularly limited, but the following commercially available PB28 can be preferably used.
Examples of commercially available PB28 include Luconyl EH0843, Sicopal L6210, Sicopal K6310, and Xfast6310 (manufactured by BASF).

-Pigment Red 101-
C. I. Pigment Blue 101 (hereinafter also simply referred to as PR101) is a magenta inorganic pigment composed of iron (III) oxide. PR101 that can be used in the ink of the present disclosure is not particularly limited, but the following commercially available PR101 can be preferably used.
市販のＰＲ１０１としては、例えば、ＳｉｃｏｔｒａｎｓＬ２７１５、ＳｉｃｏｔｒａｎｓＬ２８１６、ＳｉｃｏｔｒａｎｓＬ２８１７、ＳｉｃｏｔｒａｎｓＬ２８１８、ＳｉｃｏｔｒａｎｓＬ２９１５（以上、ＢＡＳＦ社製）、Ｃａｐｐｏｘｙｔ Ｒｅｄ ４４３４Ｂ、Ｃａｐｐｏｘｙｔ Ｒｅｄ ４４３５Ｂ、Ｃａｐｐｏｘｙｔ Ｒｅｄ ４４３７Ｂ、Ｃａｐｐｏｘｙｔ Ｒｅｄ ４４３８Ｂ（以上、Ｃａｐｐｅｌｌｅ社製）等が挙げbe done.

-Pigment Yellow 42-
C. I. Pigment Yellow 42 (hereinafter also simply referred to as PY42) is a yellow inorganic pigment made of iron oxide. PY42 that can be used in the ink of the present disclosure is not particularly limited, but the following commercially available PY42 can be preferably used.
Examples of commercially available PY42 include Sicotrans L1915, Sicotrans L1916 (manufactured by BASF), Cappoxyt Yellow 4212X, and Cappoxyt Yellow 4214X (manufactured by Cappelle).

-Pigment Yellow 184-
C. I. Pigment Yellow 184 (hereinafter also simply referred to as PY184) is a yellow inorganic pigment composed of bismuth vanadate. PY184 that can be used in the ink of the present disclosure is not particularly limited, but the following commercially available PY184 can be preferably used.
市販のＰＹ１８４としては、例えば、ＳｉｃｏｐａｌＬ１１００、ＳｉｃｏｐａｌＬ１１１０、ＳｉｃｏｐａｌＬ１１２０、ＳｉｃｏｐａｌＬ１６００（以上、ＢＡＳＦ社製）、Ｌｙｓｏｐａｃ Ｙｅｌｌｏｗ ６６０１Ｂ、Ｌｙｓｏｐａｃ Ｙｅｌｌｏｗ ６６１１Ｂ、Ｌｙｓｏｐａｃ Ｙｅｌｌｏｗ ６６１５Ｂ、Ｌｙｓｏｐａｃ Ｙｅｌｌｏｗ ６６１６Ｂ（以上、Ｃａｐｐｅｌｌｅ社製）が挙げられる。

-Pigment White 6-
C. I. Pigment White 6 (hereinafter also simply referred to as PW6) is a white inorganic pigment made of titanium oxide. PW6 that can be used in the ink of the present disclosure is not particularly limited, but the following commercially available PW6 can be preferably used.
Examples of commercially available PW6 include KRONOS 2300 (manufactured by KRONOS) and Typaque CR60-2 (manufactured by Ishihara Sangyo Co., Ltd.).

-Pigment Black 7-
C. I. Pigment Black 7 (hereinafter also simply referred to as PBK7) is a black inorganic pigment containing carbon (specifically, carbon black). PBK7 that can be used in the ink of the present disclosure is not particularly limited, but the following commercially available PBK7 can be preferably used.
Examples of commercially available PBK7 include SPECIAL BLACK 250 (manufactured by BASF) and Mogul E (manufactured by Cabot).

The smaller the average particle size of the specific inorganic pigment, the more excellent the color developability. The volume average particle size of the specific inorganic pigment is preferably 0.01 μm to 0.4 μm, more preferably 0.02 μm to 0.3 μm.

In the present disclosure, the volume average particle diameter means a value measured with a laser diffraction/scattering particle size distribution analyzer.
Examples of the measuring device include a particle size distribution measuring device “Microtrac MT-3300II” (manufactured by Nikkiso Co., Ltd.).

The content of the specific inorganic pigment in the ink of the present disclosure is preferably 0.01% by mass to 30% by mass, more preferably 0.1% by mass to 25% by mass, relative to the total amount of the ink. , more preferably 0.1% by mass to 15% by mass. Within the above numerical range, the storage stability and color development of the ink are further improved.

The ink of the present disclosure may further contain colorants other than the specific inorganic pigment.
As other colorants, known pigments such as pigments described in the Color Index can be used. For other colorants, reference may be made to known documents such as paragraph 0097 of International Publication No. 2015/115600 as appropriate.

The inks of the present disclosure may contain at least one pigment dispersant.
Regarding the pigment dispersant, it is possible to appropriately refer to known documents such as paragraphs 0152 to 0158 of JP-A-2011-225848 and paragraphs 0132-0149 of JP-A-2009-209352.

<Polymerizable Monomer Having Fluorine Atom (Monomer A)>
The ink of the present disclosure contains at least one monomer A, which is a polymerizable monomer having a fluorine atom.

Monomer A is preferably a radically polymerizable monomer.
Monomer A when it is a radically polymerizable monomer has a fluorine atom and a radically polymerizable group.

The radically polymerizable group in the radically polymerizable monomer in the present disclosure is preferably an ethylenically unsaturated group (that is, a group containing an ethylenic double bond), more preferably a vinyl group, an allyl group, or a (meth)acryloyl group. , (meth)acryloyl groups are more preferred.

The molecular weight of the monomer A is preferably 1000 or less, more preferably 750 or less, even more preferably 500 or less.

When the monomer A is a radically polymerizable monomer, the monomer A may be a monofunctional radically polymerizable monomer (hereinafter also simply referred to as "monomer A-1"), or a difunctional or higher radically polymerizable monomer. (hereinafter simply referred to as "monomer A-2"), but from the viewpoint of image adhesion and availability, monomer A-1 is more preferred.

As the monomer A-1,
2,2,2-trifluoroethyl (meth)acrylate,
2,2,3,3-tetrafluoropropyl (meth)acrylate,
1,1,1,3,3,3-hexafluoroisopropyl (meth)acrylate,
2,2,3,3,3-pentafluoropropyl (meth)acrylate,
2,2,3,4,4,4-hexafluorobutyl (meth)acrylate,
2,2,3,3,4,4,4-heptafluorobutyl (meth)acrylate,
1H,1H,5H-octafluoropentyl (meth)acrylate,
1H,1H,2H,2H-nonafluorohexyl (meth)acrylate,
1H,1H,2H,2H-tridecafluoro-n-octyl (meth)acrylate,
1H,1H-pentadecafluoro-n-octyl (meth)acrylate,
1H,1H,2H,2H-tridecafluoro-n-octyl (meth)acrylate,
2,2,3,3,4,4,5,5,6,6,7,7-dodecafluoroheptyl (meth)acrylate,
(meth)acrylate compounds having a fluorinated alkyl group having 1 to 20 carbon atoms, such as 1H, 1H, 2H, 2H-heptafluorodecyl (meth)acrylate;
(meth)acrylate compound having a fluorinated aryl group having 6 to 20 carbon atoms;
(meth)acrylate compounds having a fluorinated aralkyl group having 7 to 20 carbon atoms, such as pentafluorobenzyl (meth)acrylate;
Fluorinated styrenes such as 2,3,4,5,6-pentafluorostyrene;
etc.

Examples of the monomer A-2 include a reaction product (ester compound) of (meth)acrylic acid and a diol compound having a fluorine atom.
Diol compounds having fluorine atoms include 1,3-bis(hexafluoro-α-hydroxyisopropyl)benzene, 2,2,3,3,4,4,5,5,6,6,7,7-dodeca fluoro-1,8-octanediol, 2,2,3,3,4,4-hexafluoro-1,5-pentanediol, 1H,1H,10H,10H-hexadecafluoro-1,10-decanediol, Hexafluoro-2,3-bis(trifluoromethyl)-2,3-butanediol, 2,2,3,3,4,4,5,5-octafluoro-1,6-hexanediol, 2,2 , 3,3-tetrafluoro-1,4-butanediol, 2,3,5,6-tetrafluoro-1,4-benzenedimethanol and the like.

From the viewpoint of further improving the adhesion and abrasion resistance of the image over time, the monomer A includes:
A polymerizable monomer (more preferably a radically polymerizable monomer) having 6 or more fluorine atoms is preferred,
A (meth)acrylate compound having 6 or more fluorine atoms is more preferable,
A (meth)acrylate compound having a fluorinated alkyl group having 3 to 20 carbon atoms and 6 to 43 fluorine atoms is more preferable,
A (meth)acrylate compound having a fluorinated alkyl group having 4 to 12 carbon atoms and 6 to 25 fluorine atoms is more preferable,
2,2,3,4,4,4-hexafluorobutyl (meth)acrylate,
2,2,3,3,4,4,4-heptafluorobutyl (meth)acrylate,
1H,1H,5H-octafluoropentyl (meth)acrylate,
1H,1H,2H,2H-nonafluorohexyl (meth)acrylate,
1H,1H,2H,2H-tridecafluoro-n-octyl (meth)acrylate,
1H,1H-pentadecafluoro-n-octyl (meth)acrylate,
1H,1H,2H,2H-tridecafluoro-n-octyl (meth)acrylate,
2,2,3,3,4,4,5,5,6,6,7,7-dodecafluoroheptyl (meth)acrylate, or
More preferred is 1H,1H,2H,2H-heptafluorodecyl (meth)acrylate.

The content of the monomer A is preferably 1% by mass to 60% by mass, more preferably 1% by mass to 20% by mass, and even more preferably 1% by mass to 10% by mass, relative to the total amount of the ink.

Further, the ratio of the content mass of monomer A to the total content mass of all polymerizable monomers contained in the ink (hereinafter also referred to as "monomer A/total monomer ratio") is preferably 0.001 to 0.9. 0.002 to 0.5 is more preferred, 0.05 to 0.5 is still more preferred, and 0.05 to 0.4 is even more preferred.

The preferred range of the ratio of the content mass of the monomer A to the total content mass of all the radically polymerizable monomers contained in the ink is the same as the preferred range of the monomer A/total monomer ratio described above.

<(Meth)acrylate compound having an aromatic ring and not having a fluorine atom (monomer B)>
The ink of the present disclosure further contains at least one monomer B, which is a (meth)acrylate compound having an aromatic ring and no fluorine atom, from the viewpoint of further improving the abrasion resistance of the image over time. is preferred.
Monomer B is a radically polymerizable monomer.
When the ink of the present disclosure contains monomer B, monomer A described above is also preferably a radically polymerizable monomer.
Here, the aromatic ring includes a benzene ring, a naphthalene ring and the like, preferably a benzene ring.

The molecular weight of the monomer B is preferably 1000 or less, more preferably 500 or less, even more preferably 400 or less.

Monomer B may be a monofunctional (meth)acrylate compound having an aromatic ring and having no fluorine atom (hereinafter also simply referred to as "monomer B-1"), having an aromatic ring, and A di- or higher-functional (meth)acrylate compound having no fluorine atom (hereinafter also simply referred to as “monomer B-2”) may also be used.

Examples of the monomer B-1 include phenoxyethyl (meth)acrylate, benzyl (meth)acrylate and the like.

Examples of the monomer B-2 include reaction products of 1,4-bis(2-hydroxyethoxy)benzene and (meth)acrylic acid.

From the viewpoint of further improving the abrasion resistance of the image over time, the ink of the present disclosure preferably contains the monomer B-1, and contains phenoxyethyl (meth)acrylate (that is, phenoxyethyl acrylate and phenoxyethyl methacrylate). including at least one) is more preferred.

When the ink of the present disclosure contains the monomer B, the content of the monomer B is preferably 1% by mass to 50% by mass, more preferably 5% by mass to 45% by mass, and 10% by mass, relative to the total amount of the ink. ~40% by mass is more preferred.

In addition, from the viewpoint of further improving the abrasion resistance of the image over time, the ratio of the content mass of monomer B to the total content mass of all polymerizable monomers contained in the ink (hereinafter also referred to as "monomer B/total monomer ratio") ) is preferably 0.001 to 0.9, more preferably 0.002 to 0.5, still more preferably 0.01 to 0.5, and still more preferably 0.05 to 0.4.

The preferable range of the ratio of the mass content of monomer B to the total mass content of all radically polymerizable monomers contained in the ink is the same as the preferred range of the ratio of monomer B/total monomers described above.

<N-vinylcaprolactam (monomer C)>
The ink of the present disclosure preferably contains the monomer C, which is N-vinylcaprolactam, from the viewpoint of further improving the abrasion resistance of the image over time.
Monomer C is a radically polymerizable monomer.
When the ink of the present disclosure contains monomer C, monomer A described above is also preferably a radically polymerizable monomer.

When the ink of the present disclosure contains monomer C, the content of monomer C is preferably 1% by mass to 40% by mass, more preferably 3% by mass to 35% by mass, and 5% by mass, relative to the total amount of the ink. ~30% by mass is more preferred.

From the viewpoint of further improving the abrasion resistance of an image over time, the ratio of the content mass of monomer C to the total content mass of all polymerizable monomers contained in the ink (hereinafter also referred to as "monomer C/total monomer ratio") is , is preferably 0.001 to 0.9, more preferably 0.002 to 0.5, still more preferably 0.01 to 0.5, even more preferably 0.05 to 0.4.

The preferred range of the ratio of the content mass of the monomer C to the total content mass of all the radical polymerizable monomers contained in the ink is the same as the preferred range of the monomer C/total monomer ratio described above.

When the ink of the present disclosure contains at least one (preferably both) of monomer B and monomer C, the ratio of the content mass of monomer B to the total content mass of monomer B and monomer C (hereinafter referred to as "monomer B/(monomer B + Monomer C) ratio”) is preferably from 0.1 to 1, more preferably from 0.2 to 0.9, from the viewpoint of further improving the abrasion resistance of the image over time. More preferably 3 to 0.8.

Further, when the ink of the present disclosure contains at least one (preferably both) of the monomer B and the monomer C, the ratio of the content mass of the monomer A to the total content mass of the monomer B and the monomer C (hereinafter referred to as "monomer A/( Monomer B + monomer C) ratio") is preferably 0.002 to 5, more preferably 0.004 to 1, still more preferably 0.004 to 0.8, even more preferably 0.004 to 0.6 .
When the monomer A/(monomer B+monomer C) ratio is 0.002 or more, the adhesion and abrasion resistance of the image over time are further improved.
When the monomer A/(monomer B+monomer C) ratio is 5 or less, the image has improved abrasion resistance over time.

In addition, from the viewpoint of further improving the adhesion and abrasion resistance of the image over time, the ratio of the mass content of monomer A, monomer B, and monomer C to the total mass content of all polymerizable monomers contained in the ink (hereinafter referred to as , Also referred to as “(monomer A + monomer B + monomer C)/total monomer ratio”) is preferably 0.3 or more, more preferably 0.4 or more, still more preferably 0.5 or more, and further Preferably it is 0.6 or more.
The (monomer A+monomer B+monomer C)/total monomer ratio may be 1 or less than 1.

The preferable range of the ratio of the total mass content of monomer C to the total mass content of all radically polymerizable monomers contained in the ink is the same as the preferred range of the ratio of (monomer A+monomer B+monomer C)/total monomer ratio described above. be.

<Polymerizable Monomer Having Aliphatic Cyclic Structure and Not Having Fluorine Atom (Monomer D)>
The ink of the present disclosure may contain a monomer D, which is a polymerizable monomer having an aliphatic cyclic structure and no fluorine atoms, from the viewpoint of further improving the abrasion resistance of the image over time.
When the ink of the present disclosure contains monomer D, both monomer A and monomer D contained in the ink are preferably radically polymerizable monomers.

The number of carbon atoms in the aliphatic cyclic structure in the monomer D is preferably 4-20, more preferably 4-16, still more preferably 4-12.
The number of carbon atoms in the aliphatic cyclic structure in the monomer D is preferably 4-20, more preferably 4-16, still more preferably 4-12.
The aliphatic cyclic structure in monomer D may have a heteroatom in the cyclic structure.
As the aliphatic cyclic structure in the monomer D, a cycloalkyl group or a heterocycloalkyl group is preferred.
The number of heteroatoms in the heterocycloalkyl group is preferably 1 or 2. The heteroatom in the cyclic structure of the heterocycloalkyl group is preferably an oxygen atom, a sulfur atom or a nitrogen atom, more preferably an oxygen atom.
As the heterocycloalkyl group, a 5- to 6-membered heterocycloalkyl group is preferred.

Monomer D is preferably a (meth)acrylate compound having an aliphatic cyclic structure and no aromatic ring.
As the monomer D, a (meth)acrylate compound having an aliphatic cyclic structure and having neither a basic group containing a nitrogen atom nor an aromatic ring is more preferable.

When the monomer D is a radically polymerizable monomer, the monomer D may be a monofunctional radically polymerizable monomer (hereinafter also simply referred to as "monomer D-1"), or a bifunctional or higher radically polymerizable monomer. (hereinafter simply referred to as "monomer D-2"), but monomer D-1 is more preferable from the viewpoints of image adhesion and availability.

The molecular weight of the monomer D is preferably 1000 or less, more preferably 500 or less, even more preferably 300 or less.

Monomer D-1 includes cyclic trimethylolpropane formal (meth)acrylate, cyclohexyl (meth)acrylate, isobornyl (meth)acrylate, 2-methyladamantan-2-yl (meth)acrylate, and 2-(meth)acrylate. ethyladamantan-2-yl, 1-(meth)acryloyloxy-3-hydroxyadamantane, and the like.
Monomer D-2 includes 1,3-bis-(meth)acryloyloxy-adamantane and the like.

When the ink of the present disclosure contains monomer D, the content of monomer D is preferably 1% by mass to 20% by mass, more preferably 3% by mass to 15% by mass, and 5% by mass, relative to the total amount of the ink. ~10% by mass is more preferred.

Further, when the ink of the present disclosure contains monomer D, the ratio of the content mass of monomer D to the total content mass of all polymerizable monomers contained in the ink (hereinafter also referred to as "monomer D/total monomer ratio" ) is preferably 0.01 to 0.3, more preferably 0.02 to 0.2.

The preferable range of the ratio of the content mass of the monomer D to the total content mass of all the radical polymerizable monomers contained in the ink is the same as the preferred range of the monomer D/total monomer ratio described above.

<Compound H>
The ink of the present disclosure is at least one selected from the group consisting of an organic solvent, an alkyl (meth)acrylate having an alkyl group having 1 to 4 carbon atoms, and styrene which may have a substituent other than a fluorine atom. It is preferable to contain compound H.
When the ink of the present disclosure contains compound H, the adhesion of the image over time is further improved.
Although the reason why such an effect is exhibited is not clear, when the ink is applied onto the building material, the compound H in the ink dissolves or swells the building material. It is presumed that this is because the adhesiveness (adhesion before aging) is improved, and this adhesion before aging is maintained even when the image is aged in an outdoor environment.
When the ink of the present disclosure contains the compound H, the adhesion of the image over time is further improved, and the adhesion of the image over time may also be further improved.

(Organic solvent as compound H)
The organic solvent as the compound H is not particularly limited, but examples thereof include ketone compounds, ester compounds, alcohol compounds, ether compounds, hydrocarbon compounds, aromatic compounds, cellosolve compounds and the like.

Examples of ketone compounds include aliphatic ketones and aromatic ketones.
Aliphatic ketones include acetone, cyclohexanone, diisopropyl ketone, methyl ethyl ketone, diethyl ketone and the like.
Acetophenone etc. are mentioned as an aromatic ketone.

Ester compounds include acetic esters, acetoacetic esters, aromatic carboxylic acid esters, and the like. Ester compounds are distinguished from the above ketone compounds by not having a ketone group in the molecule.
Acetates include methyl acetate, ethyl acetate, isopropyl acetate, propyl acetate, butyl acetate, pentyl acetate, cellosolve acetate, 3-methoxybutyl acetate and the like.
Ethyl acetoacetate etc. are mentioned as acetoacetate.
Dibutyl phthalate etc. are mentioned as aromatic carboxylic acid ester.

Alcohol compounds include alcohol compounds having an aliphatic cyclic structure. Alcohol compounds are distinguished from the above ketone compounds and ester compounds by having no ketone group or ester group in the molecule.
Cyclohexanol etc. are mentioned as an alcohol compound which has an aliphatic cyclic structure.

Ether compounds include cyclic ether compounds, cellosolve compounds, and the like. Ether compounds are distinguished from the above ketone compounds, ester compounds and alcohol compounds in that they do not contain ketone groups, ester groups and alcoholic hydroxyl groups in their molecules.
Cyclic ether compounds include tetrahydrofuran, dioxane, furan, and the like.
Cellosolve compounds include butyl cellosolve, ethyl cellosolve, and the like.

The hydrocarbon compound may be either an aliphatic hydrocarbon compound or an aromatic hydrocarbon compound. Hydrocarbon compounds are distinguished from the above ketone compounds, ester compounds, alcohol compounds and ether compounds in that they do not have ketone groups, ester groups, alcoholic hydroxyl groups and ether bonds in their molecules.

Examples of aliphatic hydrocarbon compounds include cyclohexane and pinene.
Examples of aromatic hydrocarbon compounds include ethylbenzene, toluene, and xylene.

Alkyl (meth)acrylates having an alkyl group having 1 to 4 carbon atoms as Compound H include methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, and (meth)acrylic acid. isopropyl, butyl (meth)acrylate, isobutyl (meth)acrylate, and the like.

Examples of the styrene which may have a substituent other than fluorine as the compound H include styrene and methylstyrene.

When the ink of the present disclosure contains compound H, the content of compound H is preferably 0.01% by mass to 30% by mass, more preferably 0.05% by mass to 25% by mass, relative to the total amount of the ink. , more preferably 0.05% by mass to 20% by mass.

When the ink of the present disclosure contains Compound H, the content of Compound H is 0.01% by mass to 50% by mass with respect to the total content of all polymerizable monomers contained in the ink. preferably 0.05% by mass to 40% by mass, more preferably 0.05% by mass to 35% by mass, even more preferably 0.05% by mass to 25% by mass, and 0.05% by mass to 20% by mass % is particularly preferred.
When the content of compound H is 0.01% by mass or more relative to the total content of all polymerizable monomers, the adhesion of the image over time is further improved.
When the content of compound H is 50% by mass or less with respect to the total content of all polymerizable monomers, the abrasion resistance of the image over time is further improved.

The preferred range of the content of compound H with respect to the total content of all radically polymerizable monomers contained in the ink is also the above-described content of compound H with respect to the total content of all polymerizable monomers contained in the ink. Same as quantity.

<Other polymerizable monomers>
The inks of the present disclosure may contain other polymerizable monomers other than the monomers mentioned above.
As other polymerizable monomers, radically polymerizable monomers are preferred, and ethylenically unsaturated compounds are more preferred.
Radically polymerizable monomers (hereinafter also referred to as "other radically polymerizable monomers") as other polymerizable monomers may be known radically polymerizable monomers such as (meth)acrylate compounds, (meth)acrylamide compounds, vinyl ether compounds, allyl compounds, N-vinyl compounds, unsaturated carboxylic acids and the like.
Other polymerizable monomers include radically polymerizable monomers described in JP-A-2009-221414, radically polymerizable compounds described in JP-A-2009-209289, and ethylenic compounds described in JP-A-2009-191183. An unsaturated compound or the like may also be used.
The other radically polymerizable monomer is preferably a (meth)acrylate compound, more preferably an acrylate compound.

Other radically polymerizable monomers may be monofunctional radically polymerizable monomers or bifunctional or higher radically polymerizable monomers.
The ink of the present disclosure preferably contains a difunctional or higher radically polymerizable monomer as another radically polymerizable monomer, and more preferably contains a bifunctional or trifunctional radically polymerizable monomer. It is more preferable to contain a radically polymerizable monomer.

Specific examples of other radically polymerizable monomers include;
monofunctional (meth)acrylate compounds such as alkyl (meth)acrylate compounds having an alkyl group having 5 or more carbon atoms;
Bifunctional (meth)acrylate compounds such as 1,6-hexanediol di(meth)acrylate, dipropylene glycol di(meth)acrylate, propylene oxide (PO)-modified neopentyl glycol di(meth)acrylate;
Trifunctional (meth)acrylate compounds such as tris(2-hydroxyethyl)isocyanurate tri(meth)acrylate and ethylene oxide (EO)-modified trimethylolpropane tri(meth)acrylate;
etc.

Further, specific examples of other radically polymerizable monomers include (meth)acrylate compounds having a basic group having a nitrogen atom (eg, tertiary amino group, nitrogen-containing heterocyclic group, etc.).
As the basic group having a nitrogen atom, a tertiary amino group is preferable, and a tertiary amino group which is an aliphatic amino group is more preferable.
The tertiary amino group, which is an aliphatic amino group, preferably has 2 to 12 carbon atoms, more preferably 2 to 8 carbon atoms.
A tertiary amino group which is an aliphatic amino group includes a dimethylamino group, a diethylamino group, a morpholino group, a piperidino group, a pyrrolidino group, a piperazino group having a substituent on a nitrogen atom, and the like.
As a (meth)acrylate compound having a basic group having a nitrogen atom;
Dimethylaminoethyl (meth)acrylate, diethylaminoethyl (meth)acrylate, N-phenylaminoethyl (meth)acrylate, 2-N-morpholinoethyl (meth)acrylate, 2-piperidinoethyl (meth)acrylate, 2-pyrrolidinoethyl ( Monofunctional (meth)acrylate compounds such as meth)acrylates;
Bifunctional or higher (meth)acrylate compounds such as reaction products of N-methyldiethanolamine and (meth)acrylic acid, and reaction products of piperazine-1,4-bisethanolamine and (meth)acrylic acid;
etc.

Further, specific examples of other radically polymerizable monomers include radically polymerizable monomers having at least one of an epoxy ring and an oxetane ring.
Specific examples of radically polymerizable monomers having at least one of an epoxy ring and an oxetane ring include glycidyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate glycidyl ether, 3,4-epoxycyclohexylmethyl (meth)acrylate, allyl Glycidyl ether, (3-ethyloxetan-3-yl)methyl (meth)acrylate, (meth)acryl for one of the epoxy groups in a compound having two or more epoxy groups (e.g., bisphenol A type epoxy resin) compounds to which acids are added, and the like.

Examples of other radically polymerizable monomers include unsaturated carboxylic acids such as acrylic acid, methacrylic acid, itaconic acid, crotonic acid, isocrotonic acid, and maleic acid, salts thereof, and anhydrides having an ethylenically unsaturated group. , acrylonitrile, styrene, as well as various unsaturated polyesters, unsaturated polyethers, unsaturated polyamides, unsaturated urethanes, and the like.

More specifically, Shinzo Yamashita, "Crosslinking Agent Handbook" (1981, Taiseisha); Kiyomi Kato, "UV/EB Curing Handbook (Raw Materials)" (1985, Kobunshi Publishing Association); Ed. "Application and Market of UV/EB Curing Technology", page 79 (1989, CMC Publishing Co., Ltd.); Eiichiro Takiyama, "Polyester Resin Handbook" (1988, Nikkan Kogyo Shimbun), etc. Radically polymerizable monomers, oligomers and polymers known in the art can be used.

The molecular weight of the other radically polymerizable monomer is preferably 80-1,000, more preferably 80-800, even more preferably 80-500.

In the ink of the present disclosure, the total content of polymerizable monomers is preferably 50% by mass or more, more preferably 55% by mass or more, and even more preferably 60% by mass or more, relative to the total amount of the ink.
Although the upper limit of the polymerizable monomer is not particularly limited, examples thereof include 95% by mass and 90% by mass.

Examples of the preferred range and upper limit of the total content of the radically polymerizable monomers in the ink of the present disclosure are the same as the examples of the preferred range and the upper limit of the total content of the polymerizable monomers in the ink of the present disclosure, respectively. .

In the ink of the present disclosure, the total content of the monofunctional radically polymerizable monomer and the bifunctional radically polymerizable monomer is preferably 50% by mass or more, more preferably 55% by mass or more, more preferably 60% by mass, based on the total amount of the ink. % or more is more preferable.
The upper limit of the total content of monofunctional radically polymerizable monomers and bifunctional radically polymerizable monomers is not particularly limited, but examples thereof include 95% by mass and 90% by mass.

In the ink of the present disclosure, the ratio of the monofunctional radically polymerizable monomer to the total radically polymerizable monomer is preferably 60% by mass or more, more preferably 65% by mass or more, and even more preferably 70% by mass or more.
The upper limit of the ratio of the monofunctional radically polymerizable monomer in all the radically polymerizable monomers is not particularly limited, but examples thereof include 100% by mass, 95% by mass, and 90% by mass.

<Photoinitiator>
The ink of the present disclosure preferably contains a photopolymerization initiator.
When the ink of the present disclosure contains a photopolymerization initiator, the number of photopolymerization initiators contained may be one or more.
As the photopolymerization initiator, a known photopolymerization initiator that absorbs light (that is, active energy ray) and generates radicals that are polymerization initiation species can be used.

Preferred photopolymerization initiators include (a) carbonyl compounds such as aromatic ketones, (b) acylphosphine oxide compounds, (c) aromatic onium salt compounds, (d) organic peroxides, (e) thio compounds, (f) hexaarylbiimidazole compound, (g) ketoxime ester compound, (h) borate compound, (i) azinium compound, (j) metallocene compound, (k) active ester compound, (l) having a carbon-halogen bond compounds, (m) alkylamine compounds, and the like.

As for these photopolymerization initiators, the above compounds (a) to (m) may be used singly or in combination of two or more.

As the photopolymerization initiator, the above (a), (b) and (e) are more preferable.

Preferable examples of (a) a carbonyl compound, (b) an acylphosphine oxide compound, and (e) a thio compound are described in "RADIATION CURING IN POLYMER SCIENCE AND TECHNOLOGY", J. Am. P. FOUASSIER, J.; F. RABEK (1993), pp. and compounds having a benzophenone skeleton or a thioxanthone skeleton described in pp. 77-117.
More preferred examples include α-thiobenzophenone compounds described in JP-B-47-6416, benzoin ether compounds described in JP-B-47-3981, α-substituted benzoin compounds described in JP-B-47-22326, Benzoin derivatives described in JP-B-47-23664, aroyl phosphonate esters described in JP-B-57-30704, dialkoxybenzophenone described in JP-B-60-26483, JP-B-60-26403, JP-A-60 Benzoin ethers described in JP-B-1-34242, US Pat. p-di(dimethylaminobenzoyl)benzene described in JP-A-61-194062, thio-substituted aromatic ketone described in JP-B-2-9597, acylphosphine sulfide described in JP-B-2-9596 acylphosphines described in JP-B-63-61950, thioxanthones described in JP-B-59-42864, and the like.
Moreover, the polymerization initiators described in JP-A-2008-105379 and JP-A-2009-114290 are also preferred.

Among these photopolymerization initiators, (a) carbonyl compounds or (b) acylphosphine oxide compounds are more preferable, and specifically, bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide (eg, BASF IRGACURE® 819 from BASF), 2-(dimethylamine)-1-(4-morpholinophenyl)-2-benzyl-1-butanone (for example IRGACURE® 369 from BASF), 2 -methyl-1-(4-methylthiophenyl)-2-morpholinopropan-1-one (e.g. IRGACURE® 907 from BASF), 1-hydroxy-cyclohexyl-phenyl-ketone (e.g. BASF) manufactured by IRGACURE (registered trademark) 184), 2,4,6-trimethylbenzoyl-diphenyl-phosphine oxide (for example, DAROCUR (registered trademark) TPO, LUCIRIN (registered trademark) TPO (both manufactured by BASF)), etc. mentioned.
Among these, the photopolymerization initiator (b) is preferably an acylphosphine oxide compound, and a monoacylphosphine oxide compound (especially preferably 2,4 ,6-trimethylbenzoyl-diphenyl-phosphine oxide) or bisacylphosphine oxide compounds (particularly preferably bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide) are more preferred.

When the ink of the present disclosure contains a photopolymerization initiator, the content of the photopolymerization initiator is preferably 1.0% by mass to 25.0% by mass, and 2.0% by mass to 2.0% by mass, based on the total amount of the ink. 20.0% by mass is more preferable, and 3.0% by mass to 15.0% by mass is even more preferable.

<Sensitizer>
The ink of the present disclosure preferably contains a sensitizer.
When the ink of the present disclosure contains a sensitizer, the sensitizers may be contained either alone or in combination of two or more.
Here, the sensitizer is a substance that absorbs a specific actinic energy ray and enters an electronically excited state. The sensitizer in an electronically excited state comes into contact with a photopolymerization initiator to produce actions such as electron transfer, energy transfer and heat generation. This promotes chemical changes in the photopolymerization initiator, ie decomposition, generation of radicals, acids or bases, and the like.

Examples of sensitizers include ethyl 4-(dimethylamino)benzoate (EDB), anthraquinone, 3-acylmarine derivatives, terphenyl, styryl ketone, 3-(aroylmethylene)thiazoline, camphorquinone, eosin, and rhodamine. , erythrosine and the like.
Further, as the sensitizer, compounds represented by the general formula (i) described in JP-A-2010-24276, compounds represented by the general formula (I) described in JP-A-6-107718 can also be preferably used.
Among the above, the sensitizer is at least selected from thioxanthone, isopropylthioxanthone, ethyl 4-(dimethylamino)benzoate, and benzophenone from the viewpoint of compatibility with LED light and reactivity with a photopolymerization initiator. One is preferred.

When the ink of the present disclosure contains a sensitizer, the content of the sensitizer is preferably 0.5% by mass to 10% by mass, more preferably 1.0% by mass to 7.0% by mass. 0% to 6.0% by weight is particularly preferred.

<Surfactant>
The inks of the present disclosure may contain surfactants.
Examples of surfactants include surfactants described in JP-A-62-173463 and JP-A-62-183457. For example, dialkylsulfosuccinates, alkylnaphthalenesulfonates, anionic surfactants such as fatty acid salts, polyoxyethylene alkyl ethers, polyoxyethylene alkylallyl ethers, acetylene glycol, polyoxyethylene/polyoxypropylene block copolymers, modified Examples include nonionic surfactants such as silicones such as polydimethylsiloxane, cationic surfactants such as alkylamine salts and quaternary ammonium salts, and betaine surfactants such as carbobetaine and sulfobetaine.
An organic fluoro compound having no polymerizable group may be used instead of the surfactant. Preferably, the organic fluoro compound is hydrophobic. Examples of organic fluoro compounds include fluorine-containing surfactants, oily fluorine-containing compounds (e.g., fluorine oils) and solid fluorine compound resins (e.g., tetrafluoroethylene resins), which are disclosed in JP-B-57-9053. (columns 8 to 17) and compounds described in JP-A-62-135826.

When the ink of the present disclosure contains a surfactant, the content of the surfactant is preferably 0.01% by mass to 5.0% by mass, more preferably 0.1% by mass to 3.0% by mass, based on the total amount of the ink. % by mass is more preferred, and 0.3% by mass to 2.0% by mass is particularly preferred.

(Polymerization inhibitor)
The ink of the present disclosure may contain a polymerization inhibitor.
Polymerization inhibitors include p-methoxyphenol, quinones (e.g., hydroquinone, benzoquinone, methoxybenzoquinone, etc.), phenothiazine, catechols, alkylphenols (e.g., dibutylhydroxytoluene (BHT), etc.), alkylbisphenols, dimethyldithiocarbamine. zinc acid, copper dimethyldithiocarbamate, copper dibutyldithiocarbamate, copper salicylate, thiodipropionates, mercaptobenzimidazole, phosphites, 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO), 2,2,6,6-tetramethyl-4-hydroxypiperidine-1-oxyl (TEMPOL), tris(N-nitroso-N-phenylhydroxylamine) aluminum salt (alias: cupferron Al) and the like.
Among these, at least one selected from p-methoxyphenol, catechols, quinones, alkylphenols, TEMPO, TEMPOL, and tris(N-nitroso-N-phenylhydroxylamine) aluminum salts is preferable, and p-methoxyphenol , hydroquinone, benzoquinone, BHT, TEMPO, TEMPOL, and tris(N-nitroso-N-phenylhydroxylamine) aluminum salt is more preferred.

When the ink of the present disclosure contains a polymerization inhibitor, the content of the polymerization inhibitor is preferably 0.01% by mass to 2.0% by mass, more preferably 0.02% by mass to 1.0% by mass, based on the total amount of the ink. % by mass is more preferred, and 0.03% by mass to 0.5% by mass is particularly preferred.

<Resin>
The ink of the present disclosure may contain at least one resin.
As the resin, a resin having no polymerizable group is preferable.

Examples of resins include epoxy resins, vinyl chloride resins, vinyl acetate resins, polyesters, (meth)acrylic resins, chlorinated polyolefins, and polyketones.

Commercially available vinyl chloride resins include Uker Solution vinyl resins VYHD, VYHH, VMCA, VROH, and VYLF-X manufactured by Dow Chemicals; Solbin resins CL, CNL, C5R, and TA5R manufactured by Nisshin Kagaku Kogyo; VINNOL® E15/40, E15/45, H14/36, H15/42, H15/50, H11/59, H40/43, H40/50, H40/55, H40/60, H15/45M, E15/45M, E15/40A; and the like.

Examples of (meth)acrylic resins include copolymers of methyl methacrylate and n-butyl methacrylate.
Commercially available (meth)acrylic resins include Elvacite 2013 (copolymer of methyl methacrylate and n-butyl methacrylate, Mw = 34000) and Elvacite 2014 (methyl methacrylate and n-butyl methacrylate) from Lucite International. copolymer, Mw = 119000), Elvacite 4099 (copolymer of methyl methacrylate and n-butyl methacrylate, Mw = 15000); Mitsubishi Chemical Corporation Dianal (registered trademark) BR-113 ( butyl methacrylate resin, Mw=30000), and the like.

Commercially available polyester products include polyester resin (“TEGO (registered trademark) addbond LTH”; Mw=3000) available from Evonik Japan Co., Ltd., and the like.
Commercially available chlorinated polyolefins include Superchron (registered trademark) 814HS from Nippon Paper Industries Co., Ltd. Commercially available polyketones include TEGO (registered trademark) VARIPLUS AP, CA, SK, etc. from Evonik. mentioned

The weight average molecular weight (Mw) of the resin is preferably 3,000 to 200,000, more preferably 5,000 to 200,000, still more preferably 10,000 to 150,000, still more preferably 10,000 to 100,000, and 10,000 to 50,000. is particularly preferred.

When the ink contains a resin, the content of the resin is preferably 1% by mass to 10% by mass, more preferably 1.5% by mass to 10% by mass, based on the total amount of the ink. Particularly preferred is 2% by mass to 6% by mass.

<Water>
The inks of the present disclosure may contain small amounts of water.
Specifically, the water content relative to the total amount of the ink of the present disclosure is preferably 3% by mass or less, more preferably 2% by mass or less, and particularly preferably 1% by mass or less.
The inks of the present disclosure are preferably non-aqueous inks that contain substantially no water.

<Other ingredients>
The ink of the present disclosure may contain other components than those mentioned above.
Other components include ultraviolet absorbers, co-sensitizers, antioxidants, anti-fading agents, conductive salts and the like.
For other components, known documents such as JP-A-2011-225848 and JP-A-2009-209352 can be referred to as appropriate.

<Preferred physical properties of ink>
There is no particular limitation on the viscosity of the inks of the present disclosure.
The ink of the present disclosure preferably has a viscosity at 25° C. of 10 mPa·s to 50 mPa·s, more preferably 10 mPa·s to 30 mPa·s, and further preferably 10 mPa·s to 25 mPa·s. preferable. The viscosity of the ink can be adjusted, for example, by adjusting the composition ratio of each component contained.
The viscosity here is a value measured using a viscometer: VISCOMETER RE-85L (manufactured by Toki Sangyo Co., Ltd.).
When the viscosity of the ink is within the preferred range, the ejection stability can be further improved.

There is no particular limit to the surface tension of the inks of the present disclosure.
The ink of the present disclosure preferably has a surface tension of 20 mN/m to 30 mN/m at 30° C., more preferably 23 mN/m to 28 mN/m. 30 mN/m or less is preferable in terms of wettability, and 20 mN/m or more is preferable in terms of bleeding suppression and permeability.
The surface tension here is a value measured using a surface tensiometer DY-700 (manufactured by Kyowa Interface Science Co., Ltd.).

[Image recording method]
The image recording method of the present disclosure comprises a step of applying the ink of the present disclosure onto a building material by an inkjet method (hereinafter also referred to as an “application step”), and applying an active energy ray (i.e., and a step of irradiating (hereinafter also referred to as an “irradiation step”) with “light” as used herein.
According to the image recording method of the present disclosure, it is possible to record an image excellent in abrasion resistance over time and curability over time on a building material.

－Building materials－
Specific examples of building materials (building materials) in the present disclosure include floor materials (e.g., plate materials such as solid boards and plywood; tiles such as natural stone, glass, ceramics, stainless steel, and metal; cork floors; sheet floors such as linoleum and vinyl) ; paving materials such as stones, blocks, and bricks), wall materials (e.g., composite metal siding materials, ceramic siding materials, wooden siding materials, resin siding materials (e.g., polyvinyl chloride siding materials); siding materials such as exterior wood, Exterior materials such as sheet building materials, exterior film materials, exterior wall finishing materials, and exterior finishing materials; Interior materials such as interior finishing materials, design materials, veneers, and wooden interior materials; Exterior louvers, such as blind louvers, screens, and decorative louvers; Fences Exterior walls such as wood and blocks; wallpaper, shoji, fusuma), roofing materials (clay tiles, metal tiles, aluminum, asphalt shingles, copper plates, etc.), ceiling materials, and the like. Among them, building materials that require weather resistance are preferred, wall materials are more preferred, and siding materials are even more preferred.
In addition, the siding material may be embossed, draw-formed, or the like to have irregularities such as tile, brick, or wood grain, or may be pre-coated by precoating or the like.
Preferable building materials include polyvinyl chloride, polyvinylidene chloride, polyethylene, polypropylene, polyethylene terephthalate, polyethylene naphthalate, EPDM (Ethylene Propylene Diene Terpolymer), and other building materials containing resins such as engineering plastics (more preferably wall materials, more preferably is a resin siding material).

In the image recording method of the present disclosure, polyvinyl chloride building materials are preferably used.
Here, the polyvinyl chloride building material means a building material containing polyvinyl chloride as a raw material.
As the polyvinyl chloride building material, a hard polyvinyl chloride building material is preferable from the viewpoint of use as a building material.
Here, the rigid polyvinyl chloride building material means a polyvinyl chloride building material having a polyvinyl chloride content of 70% by mass or more relative to the total amount of the building material.
The rigid polyvinyl chloride building material does not contain a plasticizer (e.g., bis-2-ethylhexyl phthalate, etc.), or if it contains a plasticizer, the content of the plasticizer is less than 10% by mass (more than preferably less than 5% by weight) are preferred.

A siding material is mentioned as an example of building materials.
In this case, by recording an image on the siding material by the image recording method of the present disclosure, it is possible to improve the design of the siding material. Moreover, as described above, the recorded image is excellent in adhesion over time and abrasion resistance over time.

(Addition process)
The application step is a step of applying the ink of the present disclosure onto a building material by an inkjet method.

Application of ink by an inkjet method can be performed using a known inkjet recording apparatus.
The inkjet recording apparatus is not particularly limited, and any known inkjet recording apparatus capable of achieving the desired resolution can be selected and used. That is, a known inkjet recording device including commercially available products can be used.

The inkjet recording apparatus includes, for example, an apparatus including an ink supply system, temperature sensor, and heating means.
The ink supply system includes, for example, a primary tank containing ink, a supply pipe, an ink supply tank immediately before the inkjet head, a filter, and a piezoelectric inkjet head. The piezo-type inkjet head is preferably 1 pL to 100 pL, more preferably 8 pL to 30 pL multi-size dots, preferably 320 dpi (dot per inch) × 320 dpi to 4000 dpi × 4000 dpi (dot per inch), more preferably 400 dpi × It can be driven to eject at a resolution of 400 dpi to 1600 dpi×1600 dpi, more preferably 720 dpi×720 dpi to 1600 dpi×1600 dpi.
Note that dpi represents the number of dots per 2.54 cm (1 inch).

(Irradiation process)
The irradiation step is a step of irradiating the ink applied on the building material with active energy rays.
By irradiating the ink applied on the building material with an active energy ray, the polymerization reaction of the polymerizable monomer in the ink proceeds. As a result, the image can be fixed and the hardness of the image can be improved.

Examples of active energy rays that can be used in the irradiation step include ultraviolet rays (UV light), visible rays, electron beams, and the like, and among these, UV light is preferred.

The peak wavelength of the active energy ray is preferably 200 nm to 405 nm, more preferably 220 nm to 390 nm, even more preferably 220 nm to 385 nm.
It is also preferably 200 nm to 310 nm, and more preferably 200 nm to 280 nm.

The exposure energy when the active energy ray is applied is, for example, 10 mJ/cm ² to 2000 mJ/cm ² , preferably 20 mJ/cm ² to 1000 mJ/cm ² .

Mercury lamps, metal halide lamps, UV fluorescent lamps, gas lasers, solid-state lasers, and the like are widely known as sources for generating active energy rays.
Also, the replacement of the light sources exemplified above with semiconductor ultraviolet light emitting devices is very useful both industrially and environmentally.
Among semiconductor ultraviolet light emitting devices, LEDs (Light Emitting Diodes) and LDs (Laser Diodes) are small, have a long life, are highly efficient, and are low in cost, and are expected as light sources.
The light source is preferably a metal halide lamp, an ultra-high pressure mercury lamp, a high pressure mercury lamp, a medium pressure mercury lamp, a low pressure mercury lamp, an LED, or a blue-violet laser.
Among these, when a sensitizer and a photopolymerization initiator are used in combination, an ultrahigh-pressure mercury lamp capable of irradiating light with a wavelength of 365 nm, 405 nm, or 436 nm, or a light irradiation with a wavelength of 365 nm, 405 nm, or 436 nm is possible. A high-pressure mercury lamp or an LED capable of emitting light with a wavelength of 355 nm, 365 nm, 385 nm, 395 nm, or 405 nm is more preferable, and an LED capable of emitting light with a wavelength of 355 nm, 365 nm, 385 nm, 395 nm, or 405 nm is most preferable.

In the irradiation step, the irradiation time of the active energy ray to the ink applied on the building material is, for example, 0.01 seconds to 120 seconds, preferably 0.1 seconds to 90 seconds.
As for the irradiation conditions and the basic irradiation method, the irradiation conditions and irradiation method disclosed in JP-A-60-132767 can be similarly applied.
As a method of irradiating the active energy ray, specifically, a method in which light sources are provided on both sides of a head unit including an ink ejection device, and the head unit and the light source are scanned by a so-called shuttle method, or a separate light source without driving is used. A method of irradiating with an active energy ray is preferred.
Irradiation with active energy rays is preferably carried out after a certain period of time (for example, 0.01 to 120 seconds, preferably 0.01 to 60 seconds) after the ink is landed and dried by heating.

(Heat drying process)
The image recording method may further include a heat drying step after the application step and before the irradiation step, if necessary.
The heating means is not particularly limited, but includes a heat drum, warm air, an infrared lamp, a heat oven, heat plate heating, and the like.
The heating temperature is preferably 40°C or higher, more preferably about 40°C to 150°C, even more preferably about 40°C to 80°C.
Note that the heating time can be appropriately set in consideration of the composition of the ink and the printing speed.

<Image recording>
The image recorded matter of the present disclosure includes a building material (preferably polyvinyl chloride building material) and an image, which is a cured product of the ink of the present disclosure, placed on the building material.
Therefore, the image recorded matter of the present disclosure is excellent in adhesion over time and abrasion resistance over time.
An example of the image recorded matter of the present disclosure is a siding material with an image.

In the image recorded matter of the present disclosure, the image, which is the cured product of the ink of the present disclosure, contains a polymer containing a structural unit derived from the monomer A and the specific inorganic pigment described above.
Here, the structural unit derived from the monomer A means a structural unit obtained by polymerization of the monomer A.
For the preferable content of the structural unit derived from the monomer A in the polymer, the monomer A/total monomer ratio in the ink section described above can be appropriately referred to.
The polymer may contain structural units other than the structural units derived from the monomer A.
In addition, the image, which is the cured product of the ink of the present disclosure, may contain components other than the specific inorganic pigment and the polymer.
For other structural units and other components, the section on the ink described above can be referred to as appropriate.

Examples of the present disclosure are shown below, but the present disclosure is not limited to the following examples.

<Preparation of cyan mill base>
Each material in the following composition was mixed and stirred for 10 minutes at 2,500 rpm using a mixer (L4R manufactured by Silverson) to obtain a mixture. After that, the obtained mixture is placed in a bead mill dispersing machine DISPERMAT LS (manufactured by VMA) and dispersed at 2,500 rpm for 6 hours using YTZ balls (manufactured by Nikkato Co., Ltd.) having a diameter of 0.65 mm. A cyan mill base having the following composition was obtained as an inorganic pigment dispersion.

- Composition of cyan mill base -
・ Sicopal Blue K 6310 ... 40 parts by mass (cyan pigment (specific inorganic pigment); C.I. Pigment Blue 28, manufactured by BASF)
・ Solsperse 32000 ... 10 parts by mass (polymer dispersant, manufactured by Lubrizol Japan Co., Ltd.)
・ SR339A ... 49 parts by mass (monomer B; 2-phenoxyethyl acrylate (PEA), manufactured by Sartomer Japan Co., Ltd.)
・FLORSTAB UV12 ... 1.0 parts by mass (polymerization inhibitor; Cuperon Al, manufactured by Kromachem)

<Preparation of magenta mill base>
A magenta mill base having the following composition was prepared in the same manner as the cyan mill base, except that some of the materials were changed.

-Magenta Mil Base Composition-
・ Sicotrans Red L 2818 ... 30 parts by mass (magenta pigment (specific inorganic pigment); C.I. Pigment Red 101, manufactured by BASF)
・Solsperse 32000...10 parts by mass ・SR339A...59 parts by mass ・FLORSTAB UV12...1.0 parts by mass

<Preparation of yellow mill base 1>
A yellow millbase 1 having the following composition was prepared in the same manner as the cyan millbase except that some of the materials were changed.

- Composition of yellow mill base 1 -
・ Sicotrans Gelb L 1915 ... 30 parts by mass (yellow pigment (specific inorganic pigment); CI Pigment Yellow 42, manufactured by BASF)
・Solsperse 32000...10 parts by mass ・SR339A...59 parts by mass ・FLORSTAB UV12...1.0 parts by mass

<Preparation of yellow mill base 2>
A yellow millbase 2 having the following composition was prepared in the same manner as the cyan millbase except that some of the materials were changed.

-Composition of Yellow Mill Base 2-
・Lysopac Yellow 6615B ... 40 parts by mass (yellow pigment (specific inorganic pigment); CI Pigment Yellow 184, manufactured by Cappelle Pigments NVF)
・Solsperse 32000...10 parts by mass ・SR339A...49 parts by mass ・FLORSTAB UV12...1.0 parts by mass

<Preparation of white mill base>
A white mill base having the following composition was prepared in the same manner as the cyan mill base, except that some of the materials were changed.

-Composition of white mill base-
・KRONOS 2300 ... 40 parts by mass (white pigment (specific inorganic pigment); C.I. Pigment White 6, manufactured by KRONOS)
・Solsperse 32000...10 parts by mass ・SR339A...49 parts by mass ・FLORSTAB UV12...1.0 parts by mass

<Preparation of black mill base>
A black mill base having the following composition was prepared in the same manner as in the preparation of the cyan mill base, except that some of the materials were changed.

-Composition of black mill base-
・ SPECIAL BLACK 250 ... 40 parts by mass (black pigment (specific inorganic pigment); CI Pigment Black 7, manufactured by BASF)
・Solsperse 32000...10 parts by mass ・SR339A...49 parts by mass ・FLORSTAB UV12...1.0 parts by mass

[Example 1]
<Ink preparation>
An ink was prepared by mixing each component of the following composition.

-Ink composition-
・The above cyanyl base... 25.0 parts by mass ・2,2,3,3-Tetrafluoropropyl acrylate (hereinafter also referred to as "TFPA") (monomer A)... 56.0 parts by mass ・SPEEDCURE BP... 1.2 Parts by mass (photopolymerization initiator, benzophenone, manufactured by Lambson)
· Lucirin TPO ... 5.2 parts by mass (photopolymerization initiator, 2,4,6-trimethylbenzoyldiphenylphosphine oxide, manufactured by BASF)
・SPEEDCURE ITX ... 1.4 parts by mass (photopolymerization initiator, isopropylthioxanthone, manufactured by Lambson)
・SPEEDCURE EDB ... 1.7 parts by mass (sensitizer, 4-(dimethylamino) ethyl benzoate, manufactured by Lambson)
・ FLORSTAB UV12 ... 0.1 parts by mass (polymerization inhibitor, manufactured by Kromachem)
· Dianal BR-113 ... 1.4 parts by mass (acrylic resin, Tg = 78 ° C., manufactured by Mitsubishi Rayon Co., Ltd.)
· BYK-307 ... 0.2 parts by mass (silicone surfactant, manufactured by BYK-Chemie)

<Image recording>
The ink was applied onto a polyvinyl chloride building material by an inkjet method, and an image was recorded by irradiating the applied ink with UV light to obtain an image record.
Images were recorded using a UV ink jet printer LuxelJet UV550GTW manufactured by Fuji Film Co., Ltd. under the conditions of production mode and lamp 7 .
Kaidak (registered trademark) Milky Ivory SKDG1200 manufactured by Sumitomo Bakelite Co., Ltd. was used as the polyvinyl chloride building material. This polyvinyl chloride building material is a rigid polyvinyl chloride building material that does not contain a plasticizer.
The recorded image was a solid image of A2 size.

<Evaluation>
Using the above-described image recorded matter, the adhesion of the image over time and the abrasion resistance of the image over time were evaluated.
Table 1 shows the results.

(Image adhesion over time)
The image recorded matter was subjected to an accelerated weather resistance test for 2000 hours in accordance with ISO4892-2 using Weatherometer Ci4000 manufactured by Atlas.
After the 2000-hour accelerated weather resistance test, the images in the image recordings were subjected to a cross-hatch test in accordance with ISO2409 (cross-cut method), and the adhesion over time of the images was evaluated according to the following evaluation criteria.
In the following evaluation criteria, "A" is the most excellent rank in adhesion over time of the image.
In this cross-hatch test, the cut interval was set to 1 mm, and 25 square lattices of 1 mm square were formed.
In the following evaluation criteria, the ratio (%) of peeling of the grid is a value obtained by the following formula. The total number of grids in the equation below is 25.
Percentage of grid peeling (%) = [(number of grids with peeling) / (total number of grids)] × 100

-Evaluation Criteria for Image Adhesion over Time-
A: The ratio (%) of peeling of the lattice was 0% or more and 5% or less.
B: The rate (%) of peeling of the lattice was more than 5% and 15% or less.
C: The ratio (%) of peeling of the lattice was more than 15% and 35% or less.
D: The ratio (%) of peeling of the lattice was more than 35% and 65% or less.
E: The ratio (%) of peeling of the lattice was over 65%.

(Image scratch resistance over time)
Using the recorded image after the 2000-hour accelerated weather resistance test, the abrasion resistance of the image over time was evaluated as follows.
Two paperweights weighing 200g (width 1.5cm x thickness 1.5cm x length 12cm) are stacked and fixed in the thickness direction, and canvas (12.5cm x 5.5cm) is attached to the bottom and sides of the lower paperweight. fixed to cover the
The paperweight with the canvas fixed was placed canvas down on the image in the image recording after the 2000 hour accelerated weathering test described above. In this state, the paperweight to which the canvas was fixed was subjected to a rubbing operation in which the paperweight was reciprocated 50 times at a distance of 12 cm in the longitudinal direction of the paperweight. Hereinafter, this rubbing operation is referred to as 50 rubbing operations.
During the rubbing operation 50 times, the color transfer from the image recorded matter to the canvas was appropriately observed visually, and the rubbing resistance of the image over time was evaluated according to the following evaluation criteria. In the following evaluation criteria, "A" is the most excellent rank in abrasion resistance.

-Evaluation Criteria for Image Scratch Resistance over Time-
A: At the time when 50 rubbing operations were completed, no color transfer from the image to the canvas was visually observed.
B: When the rubbing operation was completed 50 times, the color transfer from the image to the rubbing paper was visually observed, but when the rubbing operation was completed 30 times, the color transfer from the image to the rubbing paper was not visually observed. rice field.
C: When the rubbing operation was completed 30 times, the color transfer from the image to the rubbing paper was visually observed, but when the rubbing operation was completed 15 times, the color transfer from the image to the rubbing paper was not visually observed. rice field.
D: When the rubbing operation was completed 15 times, the color transfer from the image to the rubbing paper was visually observed, but when the rubbing operation was completed 5 times, the color transfer from the image to the rubbing paper was not visually observed. rice field.
E: When the rubbing operation was completed 5 times, color transfer from the image to the rubbing paper was visually observed.

[Examples 2 to 25 and Comparative Example 1]
The same operation as in Example 1 was performed except that the monomer A (TFPA: 56.0 parts by mass) in the composition of the ink was changed to the combination of each monomer and compound H shown in Table 1 or Table 2.
Examples 1 to 15 and Comparative Example 1 are examples containing no compound H, and Examples 16 to 25 are examples containing compound H.
The results are shown in Table 1 or Table 2.

[Examples 26 to 30]
The same operation as in Example 25 was performed except that the cyan mill base as the pigment dispersion was changed to the pigment dispersion shown in Table 2.
Table 2 shows the results.

[Examples 31 to 36]
The same operation as in Example 1 was performed except that the monomer A (TFPA: 56.0 parts by mass) in the composition of the ink was changed to the combination of each monomer and compound H shown in Table 3.
Examples 31-36 are examples containing Compound H.
Table 3 shows the results.

-Description of Tables 1 to 3-
・In each table, only the inorganic pigment dispersion, the polymerizable monomer, and the compound H are shown in the composition of the ink. , acrylic resin, and silicone surfactant) are omitted.
- The numerical value in each component means a mass part.
・A blank in the table means that the corresponding component is not contained.
- The total monomer (parts by mass) in the ink means the total content (parts by mass) of all polymerizable monomers contained in the ink. All monomers in the ink also include monomers in the inorganic pigment dispersion (specifically 2-phenoxyethyl acrylate as monomer B).
The monomer A/total monomer ratio means the ratio of the content mass of monomer A to the total content mass of all polymerizable monomers contained in the ink.
- The ratio of monomer A/(monomer B+monomer C) means the ratio of the mass content of monomer A to the total mass content of monomer B and monomer C.
The content (% by mass) of compound H relative to all monomers means the content (% by mass) of compound H relative to the total content of all polymerizable monomers contained in the ink.
- Monomer A is a polymerizable monomer having a fluorine atom,
Monomer B is a (meth)acrylate compound having an aromatic ring and no fluorine atom,
Monomer C is N-vinylcaprolactam,
Monomer D is a polymerizable monomer having an aliphatic cyclic structure and no fluorine atom,
Compound H is at least one selected from the group consisting of an organic solvent, an alkyl (meth)acrylate having an alkyl group of 1 to 4 carbon atoms, and styrene which may have a substituent other than a fluorine atom.

- Abbreviations in Tables 1 to 3 -
・TFPA: 2,2,3,3-tetrafluoropropyl acrylate ・PFPMA: 2,2,3,3,3-pentafluoropropyl methacrylate ・HXFBA: 2,2,3,4,4,4 acrylic acid -Hexafluorobutyl HPFBMA: 2,2,3,3,4,4,4-heptafluorobutyl methacrylate PEA: 2-phenoxyethyl acrylate NVC: N-vinylcaprolactam CHA: cyclohexyl acrylate CTFA: cyclic Trimethylolpropane formal acrylate IBOA: isobornyl acrylate LA: lauryl acrylate TDA: tridecyl acrylate HDDA: 1,6-hexanediol diacrylate 3-MBA: 3-methoxybutyl acetate

As shown in Tables 1 to 3, an inorganic monomer containing fluorine-containing polymerizable monomer A and at least one element selected from the group consisting of cobalt, aluminum, iron, bismuth, vanadium, titanium and carbon In each example using the ink containing the pigment, the image was excellent in adhesion over time and abrasion resistance over time.
Compared to each example, Comparative Example 1 containing no monomer A was inferior in image adhesion over time and abrasion resistance over time.

From the results of Examples 1 to 6, the ink contains monomer B, which is a (meth)acrylate compound having an aromatic ring, and monomer C, which is N-vinylcaprolactam, and the monomer A/(monomer B+monomer C) ratio is It can be seen that when it is 0.004 to 1 (Examples 3 to 6), the adhesion and abrasion resistance of the image over time are further improved.

From the results of Examples 7 and 11 to 13, when the ink contains monomer D, which is a polymerizable monomer having an aliphatic cyclic structure and no fluorine atom (Examples 11 to 13), It can be seen that the abrasion resistance of the image over time is further improved.

From the results of Examples 7 and 16 to 25, the ink is selected from the group consisting of an organic solvent, an alkyl (meth)acrylate having an alkyl group having 1 to 4 carbon atoms, and styrene which may have a substituent other than a fluorine atom. It can be seen that when at least one selected compound H is contained (Examples 16 to 25), the adhesion of the image over time is further improved.

Claims (11)

a monomer A which is a polymerizable monomer having a fluorine atom and a (meth)acryloyl group ;
an inorganic pigment containing at least one element selected from the group consisting of cobalt, aluminum, iron, bismuth, vanadium, titanium and carbon;
contains
The content of the monomer A is 1% by mass to 60% by mass with respect to the total amount of the ink,
The total content of polymerizable monomers is 50% by mass or more with respect to the total amount of the ink.
An inkjet ink composition for polyvinyl chloride building materials. The inorganic pigment is C.I. I. Pigment Blue 28, C.I. I. Pigment Red 101, C.I. I. Pigment Yellow 42, C.I. I. Pigment Yellow 184, C.I. I. Pigment White 6 and C.I. I. 2. The inkjet ink composition for polyvinyl chloride building materials according to claim 1, which is at least one selected from the group consisting of Pigment Black 7. 3. The inkjet ink composition for polyvinyl chloride building materials according to claim 1, further comprising a monomer B which is a (meth)acrylate compound having an aromatic ring and not having a fluorine atom. 4. The inkjet ink composition for polyvinyl chloride building materials according to any one of claims 1 to 3, further comprising a monomer C which is N-vinylcaprolactam. Furthermore, it contains a monomer B that is a (meth)acrylate compound having an aromatic ring and does not have a fluorine atom, and a monomer C that is N-vinylcaprolactam,
3. The inkjet ink composition for polyvinyl chloride building materials according to claim 1, wherein the ratio of the content of the monomer A to the total content of the monomer B and the monomer C is 0.004 to 1. 6. The inkjet ink for polyvinyl chloride building materials according to any one of claims 1 to 5, further comprising a monomer D which is a radically polymerizable monomer having an alicyclic structure and having no fluorine atom. Composition. Furthermore, it contains at least one compound H selected from the group consisting of an organic solvent, an alkyl (meth)acrylate having an alkyl group having 1 to 4 carbon atoms, and styrene which may have a substituent other than a fluorine atom. The inkjet ink composition for polyvinyl chloride building materials according to any one of claims 1 to 6. 8. The polychloride according to claim 7, wherein the content of the compound H is 0.05% by mass to 35% by mass with respect to the total content of all polymerizable monomers contained in the inkjet ink composition for building materials. An inkjet ink composition for vinyl building materials. 9. The inkjet ink composition for polyvinyl chloride building materials according to any one of claims 1 to 8, further comprising a photopolymerization initiator. A step of applying the inkjet ink composition for polyvinyl chloride building materials according to any one of claims 1 to 9 onto a polyvinyl chloride building material by an inkjet method;
a step of irradiating the inkjet ink composition for polyvinyl chloride building materials applied onto the building material with an active energy ray;
An image recording method comprising: a polyvinyl chloride building material;
an image, which is a cured product of the inkjet ink composition for polyvinyl chloride building materials according to any one of claims 1 to 9 , placed on the building material;
image recording.