JP6734463B1

JP6734463B1 - shoes

Info

Publication number: JP6734463B1
Application number: JP2019238154A
Authority: JP
Inventors: 一元大山
Original assignee: 一元大山
Priority date: 2019-12-27
Filing date: 2019-12-27
Publication date: 2020-08-05
Anticipated expiration: 2039-12-27
Also published as: JP2021104312A

Abstract

【課題】装飾物等の脱着が容易であるにもかかわらず、装着時に容易に外れてしまうことがなく、さらに前記装飾物等を外した状態においても外観が良好な状態とすることが可能となる磁着シート部材、それを用いた皮革製品および靴を提供する。【解決手段】軟磁性体金属粉末とエラストマーとを含む層を有しているシート部材であって、前記層における前記軟磁性金属粉末の含有量が、７０重量％以上９５重量％以下の範囲内であり、前記層における前記エラストマーの含有量が、５重量％以上３０重量％以下の範囲内であり、前記シート部材の厚みが０．２ｍｍ以上２．０ｍｍ以下の範囲内であることを特徴とする磁着シート部材３。磁着シート部材３は外観に影響を及ぼしにくいため、靴１は、装飾物５を取り付けた状態においても取り外した状態においても、違和感なく履くことができる。【選択図】図２PROBLEM TO BE SOLVED: To easily attach and detach a decoration or the like, but never easily come off at the time of mounting, and to make a good appearance even when the decoration or the like is removed. Provided is a magnetically adhered sheet member, a leather product using the same, and shoes. A sheet member having a layer containing a soft magnetic metal powder and an elastomer, wherein the content of the soft magnetic metal powder in the layer is in the range of 70% by weight to 95% by weight. The content of the elastomer in the layer is in the range of 5% by weight or more and 30% by weight or less, and the thickness of the sheet member is in the range of 0.2 mm or more and 2.0 mm or less. The magnetically adhered sheet member 3. Since the porcelain sheet member 3 is unlikely to affect the appearance, the shoe 1 can be worn without discomfort when the ornament 5 is attached or detached. [Selection diagram] Figure 2

Description

本発明は、靴に関する。 The present invention relates to shoes .

靴等の履物や衣類、鞄等に、装飾物を取り付けたり、必要に応じて取り外したりすることが行われている（例えば、特許文献１、２参照）。前記文献１には装飾物を取り外し自由に取り替えできるとした靴・履物が開示されている。この履物はアッパー部、ベルト部などに小孔をあけて磁石の吸着ハトメを設け、装飾品の下部に磁石を設けてハトメに挿着するというものである。磁石同士を吸着させるために取り外しも簡単にできるものであるが、そのためには履物側に小孔を開ける必要がある。そのため、製造に手間がかかるうえに、装飾物を取り付けないと小孔が露出してしまうため、装飾物を取り外した状態では外見に問題がある。また、特許文献２には、履物本体に装飾物を取り付けることのできる脱着可能な装飾物付き履物が開示されている。前記文献に開示された履物は、履物本体と装飾物が、導電性部材である金属箔の両面に熱可塑性接着剤を塗布して構成された三層構造の接着層を介して接合されたものであることを特徴としている。装飾物が脱着可能となるように、接着層は履物本体と装飾物が分離解体できるように構成されているが、装飾物を取り外すには、接着層の加熱手段を用意することが必要であるため、気軽に脱着することは困難である。 BACKGROUND ART Decorations are attached to or removed from footwear such as shoes, clothes, bags, and the like as needed (for example, see Patent Documents 1 and 2). The document 1 discloses shoes and footwear in which ornaments can be removed and replaced freely. In this footwear, a small hole is made in the upper part, the belt part, etc. to provide a magnet adsorbing eyelet, and a magnet is provided below the ornament to be attached to the eyelet. It can be easily removed because the magnets are attracted to each other, but for that purpose it is necessary to make a small hole in the footwear side. Therefore, it takes time to manufacture, and if the ornament is not attached, the small hole is exposed. Therefore, there is a problem in appearance when the ornament is removed. In addition, Patent Document 2 discloses a removable footwear with a decorative material that can be attached to the footwear body. The footwear disclosed in the above-mentioned literature is one in which the footwear body and the decoration are joined via a three-layered adhesive layer formed by applying a thermoplastic adhesive to both surfaces of a metal foil which is a conductive member. It is characterized by being. The adhesive layer is configured so that the main body of the footwear and the ornament can be separated and dismantled so that the ornament can be detached, but it is necessary to prepare a heating means for the adhesive layer to remove the ornament. Therefore, it is difficult to easily remove it.

特開２０１１−１２５６４７号公報JP, 2011-125647, A 実用新案登録第３１９１９７６号公報Utility model registration No. 3191976

本発明は上記課題を解決するものであり、装飾物等の脱着が容易であるにもかかわらず、装着時に容易に外れてしまうことがなく、さらに前記装飾物等を外した状態においても外観が良好な状態とすることが可能となる靴を提供することを目的とする。 The present invention is to solve the above-mentioned problems, and even though it is easy to attach and detach a decoration or the like, it does not easily come off during mounting, and the appearance is even when the decoration or the like is removed. an object of the present invention is to provide a Do that shoes can be a good state.

本発明の靴は、軟磁性体金属粉末とエラストマーとを含む層を有している磁着シート部材が、アッパーの甲部分、踵部分およびサイド部分の少なくとも一箇所に内蔵されており、前記磁着シート部材は、前記層における前記軟磁性金属粉末の含有量が、７０重量％以上９５重量％以下の範囲内であり、前記層における前記エラストマーの含有量が、５重量％以上３０重量％以下の範囲内であり、前記磁着シート部材の厚みが０．２ｍｍ以上２．０ｍｍ以下の範囲内にあることを特徴とする。 Shoes of the invention, magnetically attracted sheet member having a layer containing a soft magnetic metal powder and elastomer instep of the upper, are incorporated in at least one position of the heel part and side part, the magnetic landing sheet member, the content of the soft magnetic metal powder in the layer is in the range of 70 wt% to 95 wt% or less, the content of the elastomer in the layer is 30% or less 5 wt% or more And the thickness of the magnetic sheet member is within a range of 0.2 mm or more and 2.0 mm or less.

本発明の靴における磁着シート部材において、前記軟磁性体金属粉末が、鉄、ニッケル、コバルト、および、これらのいずれかを含む合金の粉末からなる群より選ばれる少なくとも１種であることが好ましい。 In the porcelain sheet member of the shoe of the present invention, it is preferable that the soft magnetic metal powder is at least one selected from the group consisting of iron, nickel, cobalt, and an alloy powder containing any of these. ..

本発明の靴における磁着シート部材において、前記軟磁性金属粉末は、外気から遮断される状態で保持されていることが好ましい。 In the magnetic sheet member of the shoe of the present invention, it is preferable that the soft magnetic metal powder is held in a state of being shielded from the outside air.

本発明の靴における磁着シート部材において、前記軟磁性体金属粉末とエラストマーとを含む層が、不織布上に設けられていることが好ましい。 In the magnetically adhered sheet member of the shoe of the present invention, it is preferable that the layer containing the soft magnetic metal powder and the elastomer is provided on the nonwoven fabric.

本発明の靴における磁着シート部材において、前記エラストマーが天然ゴムを含むことが好ましい。 In the magnetic sheet member of the shoe of the present invention, it is preferable that the elastomer contains natural rubber.

本発明によれば、装飾物等の脱着が容易であるにもかかわらず、装着時に容易に外れてしまうことがなく、さらに前記装飾物等を外した状態においても外観が良好な状態とすることが可能となる靴を提供することができる。 ADVANTAGE OF THE INVENTION According to the present invention, it is possible to easily attach and detach a decoration or the like, but it does not easily come off during mounting, and further, the appearance is good even when the decoration or the like is removed. it is possible to provide a can and Do that shoes.

図１は、本発明にかかる磁着シート部材を内蔵した靴の一例の斜視図である。FIG. 1 is a perspective view of an example of a shoe incorporating a magnetically adhered sheet member according to the present invention. 図２は、本発明にかかる磁着シート部材の使用状態を説明する斜視図である。FIG. 2 is a perspective view illustrating a usage state of the magnetically-adhesive sheet member according to the present invention.

以下、本発明をさらに具体的に述べる。本発明の磁着シート部材は、それ自体が砂鉄等を磁着するような磁力を有さずに、磁石には強固に磁着することのできる部材であり、前記磁着シートを設けておくことで、磁石を有する装飾物等の他部材を装着し、また容易に取り外すことが可能となる。 Hereinafter, the present invention will be described more specifically. The magnetically-adhesive sheet member of the present invention is a member that does not have a magnetic force to magnetically attach sand iron or the like, but can be strongly magnetically attached to a magnet. As a result, other members such as ornaments having magnets can be attached and easily removed.

前記磁着シート部材は、軟磁性体金属粉末とエラストマーとを含む層を有しているシート部材である。軟磁性体とは磁力を保持する力が小さく、透磁性が大きい材料であり、磁場の影響下では強く磁化されるが、磁場が存在しない場合は磁力を持たない性質を持つものである。前記磁着シート部材に軟磁性体金属粉末を用いることで、磁石には磁着するが、磁石から離れると、比較的簡単に磁極が消えるシート部材とすることができる。したがって、磁着することで装飾物を装着可能な靴の場合、前記磁着シート部材を、例えば、靴の側に使用すると、装飾物を取り外した状態で、地面にある砂鉄や金属片等を引き寄せてしまうという問題は生じにくくなる。 The magnetically adhered sheet member is a sheet member having a layer containing a soft magnetic metal powder and an elastomer. A soft magnetic material is a material that has a small force for holding a magnetic force and a large magnetic permeability, and is strongly magnetized under the influence of a magnetic field, but has the property of not having a magnetic force in the absence of a magnetic field. By using the soft magnetic metal powder for the magnetically-adhesive sheet member, the magnetic member can be magnetically attached to the magnet, but the magnetic pole can be relatively easily erased when the magnetic member is separated from the magnet. Therefore, in the case of a shoe that can be attached with a decoration by magnetic attachment, if the magnetic attachment sheet member is used on the side of the shoe, for example, sand iron or metal pieces on the ground can be removed with the decoration removed. The problem of attracting is less likely to occur.

本発明においては、前記軟磁性体金属粉末が、鉄、ニッケル、コバルト、および、これらのいずれかを含む合金の粉末からなる群より選ばれる少なくとも１種であることが好ましい。 In the present invention, the soft magnetic metal powder is preferably at least one selected from the group consisting of powders of iron, nickel, cobalt, and alloys containing any of these.

前記シート部材は、前記層における軟磁性金属粉末の含有量は、７０重量％以上９５重量％以下の範囲内であり、前記層における前記エラストマーの含有量は、５重量％以上３０重量％以下の範囲内であり、前記シート部材の厚みは０．２ｍｍ以上２．０ｍｍ以下の範囲内である。前記軟磁性金属粉末の含有量が、９０重量％以上であると、磁着力をより強くすることができ、好ましい。前記軟磁性金属粉末および前記エラストマーが、所定の厚みを有する前記シート部材において前記範囲の含有量であることで、前記シート部材の使用時において、厚すぎることにより外観に影響を及ぼすことがなく、かつ、シートとしての形状を維持しつつ十分な磁着力を得ることができる。 In the sheet member, the soft magnetic metal powder content in the layer is in the range of 70% by weight to 95% by weight, and the elastomer content in the layer is 5% to 30% by weight. It is in the range, and the thickness of the sheet member is in the range of 0.2 mm or more and 2.0 mm or less. When the content of the soft magnetic metal powder is 90% by weight or more, the magnetic force can be further increased, which is preferable. The soft magnetic metal powder and the elastomer, by the content of the range in the sheet member having a predetermined thickness, when using the sheet member, without affecting the appearance by being too thick, Moreover, it is possible to obtain a sufficient magnetic force while maintaining the shape of the sheet.

前記エラストマーとしては、天然ゴム、合成ゴム、熱硬化性樹脂系エラストマー等の熱硬化性エラストマー、熱可塑性エラストマーをあげることができる。硬化性樹脂系エラストマーとしては、ウレタンゴム、シリコーンゴム、フッ素ゴム等があげられる。熱硬化性エラストマーは、ある一定の温度範囲において、熱を加えても軟化することの無い、比較的耐熱性の高いタイプのエラストマーであり、耐熱性を要する用途に適するものである。熱可塑性エラストマーは、熱を加えると軟化して流動性を示し、冷却すればゴム状に戻る性質を持ったエラストマーであり、材料を加熱して射出成形することによって迅速に成型加工を行なえる利点がある。前記シート部材を、後述する靴に内蔵して用いる場合には、靴の製造工程の先芯蒸器での成型時に加熱圧縮を行うことから、前記エラストマーとしては天然ゴムを含んだものを用いることが好ましい。加熱圧縮することで、シート部材が延ばされるので、内蔵される対象の製品の外側から、前記シート部材を見えにくくすることができる。なお、前記軟磁性体金属粉末が、さびやすい材料である場合には、前記エラストマーは塩分を含まない材料であることが好ましい。 Examples of the elastomer include natural rubber, synthetic rubber, thermosetting elastomer such as thermosetting resin elastomer, and thermoplastic elastomer. Examples of the curable resin elastomer include urethane rubber, silicone rubber, fluororubber and the like. The thermosetting elastomer is an elastomer of a relatively high heat resistance type that does not soften even when heat is applied within a certain temperature range, and is suitable for applications requiring heat resistance. Thermoplastic elastomer is an elastomer that softens and shows fluidity when heat is applied, and returns to a rubber-like property when cooled, and the advantage of rapid molding by heating the material and injection molding There is. When the above-mentioned sheet member is used by incorporating it into a shoe described later, since it is heated and compressed during molding in a toe box steamer in the shoe manufacturing process, it is preferable to use one containing natural rubber as the elastomer. preferable. Since the sheet member is expanded by heating and compressing, the sheet member can be made difficult to see from the outside of the product to be incorporated. When the soft magnetic metal powder is a material that easily rusts, the elastomer is preferably a material containing no salt.

本発明の磁着シート部材において、前記軟磁性金属粉末は、外気から遮断される状態で保持されていることが好ましい。前記軟磁性金属粉末が、外気から遮断される状態で保持されていることで、前記軟磁性金属粉末のさび（酸化）を防止しやすくなり、磁着力を維持しやすくなる。外気から遮断される状態とするには、例えば、前記軟磁性金属粉末を前記エラストマーで覆うようにして、前記磁着シート部材を形成することもできる。あるいは、前記軟磁性金属粉末と前記エラストマーとを含む層を、例えば、水分透過率や酸素透過率の低いラップフィルム等で覆って前記磁着シート部材を形成することもできる。 In the magnetically adhered sheet member of the present invention, it is preferable that the soft magnetic metal powder is held in a state of being shielded from the outside air. Since the soft magnetic metal powder is held in a state of being shielded from the outside air, it is easy to prevent rust (oxidation) of the soft magnetic metal powder, and it is easy to maintain the magnetic force. In order to be in a state of being shielded from the outside air, for example, the soft magnetic metal powder may be covered with the elastomer to form the magnetically adhered sheet member. Alternatively, the layer containing the soft magnetic metal powder and the elastomer may be covered with, for example, a wrap film having a low water permeability or a low oxygen permeability to form the magnetic sheet member.

本発明の磁着シート部材において、前記軟磁性体金属粉末とエラストマーとを含む層が、不織布上に設けられていることが好ましい。不織布上に前記軟磁性体金属粉末とエラストマーとを含む層を設けることで、他部材への取付けを容易に行うことができる。前記不織布は、前記軟磁性体金属粉末とエラストマーとを含む層の反対面に、例えば、剥離紙付きの粘着層あるいは接着層を有していてもよく、その場合は前記剥離紙を剥がして、所望の場所に容易に固着させることが可能である。 In the magnetically adhered sheet member of the present invention, it is preferable that a layer containing the soft magnetic metal powder and the elastomer is provided on the nonwoven fabric. By providing a layer containing the soft magnetic metal powder and the elastomer on the non-woven fabric, it can be easily attached to another member. The non-woven fabric, on the opposite surface of the layer containing the soft magnetic metal powder and the elastomer, for example, may have a pressure-sensitive adhesive layer or adhesive layer with release paper, in which case, peel off the release paper, It can be easily fixed to a desired place.

本発明の磁着シート部材において、前記エラストマーが天然ゴムを含むことが好ましい。例えば、前記軟磁性体金属粉末として鉄粉を用いた場合、エラエストマーとして天然ゴムを用いると、柔軟性が高い磁着シート部材を得ることができる。 In the magnetic sheet member according to the present invention, it is preferable that the elastomer contains natural rubber. For example, when iron powder is used as the soft magnetic metal powder and natural rubber is used as the elastomer, a magnetically flexible sheet member having high flexibility can be obtained.

本発明の磁着シート部材は、デニム等の布帛を用いた布帛製品、皮革製品等の各種製品に内蔵されて好適に用いることができる。前記磁着シート部材は、薄く、柔軟性に富むため、柔らかい素材の内側に装着しても、違和感が少なく、また、外観に与える影響も少なくすることができる。前記磁着シート部材を装着することで、前記の各種製品の前記磁着シート部材装着部分において、磁石を有する装飾物等の他部材を装着して、デザインのバリエーションを楽しむことができる。あるいは、磁着により着脱可能な留め具を設けることができる。前記皮革製品としては、天然の皮革から製造された製品に限定されるものではなく、合成皮革や皮調の素材から製造された製品であってもよい。 The magnetically adhered sheet member of the present invention can be suitably used by being incorporated in various products such as cloth products using leather such as denim and leather products. Since the magnetically-adhesive sheet member is thin and highly flexible, even if it is attached to the inside of a soft material, there is little discomfort and the influence on the appearance can be reduced. By mounting the magnetic sticking sheet member, other members such as ornaments having magnets can be mounted in the magnetic sticking sheet member mounting portion of the various products to enjoy design variations. Alternatively, a removable fastener can be provided by magnetic attachment. The leather product is not limited to a product manufactured from natural leather, and may be a product manufactured from synthetic leather or a leather-like material.

靴、特にパンプス等の婦人靴においては、アッパーの甲部分、踵部分およびサイド部分の少なくとも一箇所に前記磁着シート部材を内蔵することで、磁石を有する装飾物を容易に着脱することができる。前記磁着シート部材は薄く、柔軟であるため、靴の製造工程における先芯蒸器での成型時に加熱圧縮を行った後に、前記装飾物を装着していない状態（プレーンなパンプスの状態）でも、前記磁着シート部材が表面に浮き出して見えることのないように調整することが可能である。図１は、磁着シート部材３を内蔵した靴１の一例の斜視図である。同図においては、本発明の磁着シート部材３が、一例としてアッパーの甲部分に内蔵されている靴１を示している。図２は、本発明の磁着シート部材３の使用状態を説明する斜視図である。靴１に装飾物５を取り付けたい場合、装飾物５の裏面に磁石７を固着させておくことで、装飾物５を靴１の磁着シート部材３の配置箇所に磁着させることができる。磁着シート部材３は外観に影響を及ぼしにくいため、靴１は、装飾物５を取り付けた状態においても取り外した状態においても、違和感なく履くことができる。装飾物５に替えて、他の装飾を行うことも容易である。その場合には、磁石が固着された装飾物であれば、任意のものを用いることができる。 In women's shoes such as shoes, particularly pumps, the magnetized sheet member can be easily attached/detached by incorporating the magnetic sheet member in at least one of the upper part, the heel part and the side part of the upper. .. Since the porcelain sheet member is thin and flexible, even after the heating and compression at the time of molding in the toe box steamer in the manufacturing process of shoes, even in a state where the ornament is not attached (state of plain pumps), It is possible to make adjustments so that the magnetically-adhesive sheet member does not appear to stand out on the surface. FIG. 1 is a perspective view of an example of a shoe 1 having a magnetically attached sheet member 3 incorporated therein. In the same figure, a shoe 1 in which the magnetically adhered sheet member 3 of the present invention is built in the upper instep portion is shown as an example. FIG. 2 is a perspective view illustrating a usage state of the magnetically adhered sheet member 3 of the present invention. When it is desired to attach the ornament 5 to the shoe 1, the magnet 5 can be fixed to the back surface of the ornament 5 to magnetically attach the ornament 5 to the place where the magnetized sheet member 3 of the shoe 1 is arranged. Since the magnetic attachment sheet member 3 is unlikely to affect the outer appearance, the shoe 1 can be worn without a sense of discomfort when the ornament 5 is attached or detached. It is also easy to replace the ornament 5 with other ornaments. In that case, any ornament can be used as long as it is an ornament to which a magnet is fixed.

衣類、鞄等においては、ボタンやホック等で係合する部分に、前記ボタンや前記ホック等に替えて、前記磁石シート部材と磁石とを使用することで、確実に係合させることができるとともに、容易に（例えば、片手でも）着脱を行うことが可能となる。 In clothes, bags, etc., by using the magnet sheet member and a magnet in place of the buttons, the hooks, etc., in the part that engages with the buttons, the hooks, etc., it is possible to ensure engagement. It becomes possible to easily attach and detach (for example, with one hand).

本発明の磁着シート部材は、厚みが０．２ｍｍ以上２．０ｍｍ以下の範囲内にあることが好ましく、より好ましくは０．３ｍｍ以上１．５ｍｍ以下の範囲にあることが好ましい。前記磁着シート部材は、厚くなるとシート部材が丈夫になり破れにくくなるが、厚すぎると、配置された部分において違和感が生じやすい。厚みが薄すぎると取り扱いしにくく、また、貼付時の耐性が不十分となりやすい。 The magnetic sheet member of the present invention preferably has a thickness of 0.2 mm or more and 2.0 mm or less, and more preferably 0.3 mm or more and 1.5 mm or less. When the thickness of the magnetically-adhesive sheet member is increased, the sheet member becomes strong and is less likely to be torn, but when it is too thick, a discomfort is likely to occur in the arranged portion. If the thickness is too thin, it will be difficult to handle, and the resistance when applied will tend to be insufficient.

本発明の磁着シート部材には、本発明で得られる特性を損なわない範囲で、例えば、可塑剤、増量剤、着色剤、安定剤等の添加物を含有させることも可能である。 The magnetically adhered sheet member of the present invention may contain additives such as plasticizers, extenders, colorants, stabilizers, etc. within a range that does not impair the properties obtained in the present invention.

以下、本発明を実施例により具体的に説明する。 Hereinafter, the present invention will be specifically described with reference to examples.

［実施例１］
実施例１は、不織布上に軟磁性体金属粉末とエラストマーとを含む層を有している磁着シート部材であり、軟磁性体金属粉末として鉄粉（＃２００、協和純薬工業株式会社製）を、エラストマーとして天然ゴム（「ＲＵＢＢＥＲＣＥＭＥＮＴ８８０」、オリエント化成工業株式会社製）を用いた。厚さ０．６ｍｍの不織布上に、鉄粉と天然ゴムとの混合割合（重量比）が、９１：９である層を形成した。天然ゴムが乾燥するまで、約１日放置して、本実施例の磁着シート部材を得た。乾燥後に厚さを測定したところ、磁着シート部材全体の厚さは１．０ｍｍであり、前記層の厚さは０．４ｍｍであった。前記不織布は、５５ｍｍ×４０ｍｍでの重さが、約０．５ｇであり、塗布後の重さ（磁着シート部材の重さ）は、約２．７ｇであった。得られた磁着シート部材をパンプス用の皮革で挟み込み、その上から磁石を近づけたところ、強固に磁着し、磁石を持ち上げたり振ったりしても、容易には外れなかった。 [Example 1]
Example 1 is a magnetic sticking sheet member having a layer containing a soft magnetic metal powder and an elastomer on a non-woven fabric, and an iron powder (#200, manufactured by Kyowa Pure Chemical Industries, Ltd.) as the soft magnetic metal powder. ) Was used as an elastomer for natural rubber (“RUBBER CEMENT 880”, manufactured by Orient Kasei Kogyo Co., Ltd.). A layer having a mixing ratio (weight ratio) of iron powder and natural rubber of 91:9 was formed on a nonwoven fabric having a thickness of 0.6 mm. The magnetic sheet was left for about 1 day until the natural rubber was dried to obtain a magnetically adhered sheet member of this example. When the thickness was measured after drying, the thickness of the entire magnetically-coated sheet member was 1.0 mm, and the thickness of the layer was 0.4 mm. The non-woven fabric had a weight of 55 mm×40 mm of about 0.5 g, and a weight after application (weight of the magnetically adhered sheet member) was about 2.7 g. The obtained magnetically-adhered sheet member was sandwiched by leather for pumps, and when a magnet was brought close to it, it was strongly magnetically adhered and could not be easily removed even if the magnet was lifted or shaken.

［実施例２］
実施例１と同じ材料を用い、磁着シート部材を作製した。本実施例においては、不織布上に天然ゴムと鉄粉を面方向に交互に層状に重ねて配置させて固着させて、軟磁性体金属粉末とエラストマーとを含む層を形成した。まず、不織布に、天然ゴムを塗布した。次いで、天然ゴムの塗布面に鉄粉を散布した。そして、鉄粉の散布面の上から天然ゴムを再度塗布した。これを繰り返し、鉄粉の散布層を３層形成し、最後に天然ゴムを塗布して、軟磁性体金属粉末とエラストマーとを含む層を形成したところ、実施例１とほぼ同一の厚さおよび重量比の層が得られた。エラストマーに対する軟磁性体金属粉末の比率が大きくなると、混合時にダマになるなど、容易な混合は難しくなる傾向にあり、また、混合後に放置すると沈殿してしまうため、常に撹拌が必要であるが、本実施例での方法によると、鉄粉と天然ゴムを均一に混合させる工程を省くことができるにもかかわらず、均一な層を容易に得ることができる。 [Example 2]
Using the same material as in Example 1, a magnetically adhered sheet member was produced. In the present example, natural rubber and iron powder were alternately arranged in layers in the surface direction on a non-woven fabric and fixed to form a layer containing soft magnetic metal powder and elastomer. First, natural rubber was applied to the nonwoven fabric. Next, iron powder was sprinkled on the coated surface of the natural rubber. Then, the natural rubber was applied again from above the surface of the iron powder. Repeating this, three layers of iron powder were formed, and finally, natural rubber was applied to form a layer containing the soft magnetic metal powder and the elastomer. A layer by weight ratio was obtained. When the ratio of the soft magnetic metal powder to the elastomer becomes large, easy mixing tends to be difficult, such as lumps at the time of mixing, and since precipitation occurs if left after mixing, it is always necessary to stir, According to the method of this embodiment, a uniform layer can be easily obtained although the step of uniformly mixing the iron powder and the natural rubber can be omitted.

得られた磁着シート部材を用い、靴（パンプス）を作製した。５５ｍｍ×４０ｍｍの前記磁着シート部材の不織布側を、靴の表革の甲部分の裏面に貼り付けた。その上から、磁着シート部材の端部を含む全体をコーティングするように、天然ゴムを塗布して約５分放置し、鉄粉が外気から遮断されるようにした。得られた磁着シート部材付きの表革を用い、ライニングで磁着シート部材を挟み込み、通常の工程と同様に、先芯蒸器での成型を行った。成型後の靴では、磁着シート部材が内蔵されている箇所が外観からは容易にわからない状態となっていた。なお、磁着部材としてステンレス板（厚さ約０．１ｍｍ）を挟み成型すると、成型後にステンレス板の部分が表面に浮き出るようになった。それに対し、本実施例の磁着シート部材を用いた場合には、表面の意匠に影響を及ぼすことがなかった。得られた磁着シート部材内蔵の靴の上から磁石を近づけたところ、磁着シート部材の配置箇所には強固に磁着した。磁石を持ち上げたり振ったりしても、容易には外れなかった。磁石を持ち上げると、靴も持ち上がり、磁石は靴から外れなかった。 A shoe (pumps) was produced using the obtained magnetically adhered sheet member. The non-woven fabric side of the 55 mm×40 mm porcelain sheet member was attached to the back surface of the upper portion of the front leather of the shoe. From above, natural rubber was applied so as to coat the entire portion including the end portion of the magnetically adhered sheet member and left for about 5 minutes so that the iron powder was shielded from the outside air. Using the obtained surface leather with a magnetically-adhesive sheet member, the magnetically-adhesive sheet member was sandwiched by linings, and molding was performed in a toecap steamer in the same manner as in a normal process. In the molded shoe, the portion where the magnetically-adhesive sheet member was incorporated was in a state where it was difficult to see from the appearance. When a stainless plate (thickness: about 0.1 mm) was sandwiched and formed as the magnetically-adhesive member, the portion of the stainless plate came out to the surface after molding. On the other hand, when the magnetic sheet member of this example was used, the surface design was not affected. When a magnet was brought close to the obtained shoe having a built-in magnetically-adhesive sheet member, it was strongly magnetically attached to the position where the magnetically-attached sheet member was arranged. Even if the magnet was lifted or shaken, it did not come off easily. When I lifted the magnet, the shoe lifted and the magnet did not come off the shoe.

［実施例３］
実施例２と同様にして、鉄粉の散布層を５層形成し、最後に天然ゴムを塗布して、軟磁性体金属粉末とエラストマーとを含む層を形成した。得られた磁着シート部材の厚さは１．３ｍｍであり、軟磁性体金属粉末とエラストマーとを含む層における鉄粉と天然ゴムとの重量比は、９１：９であった。 [Example 3]
In the same manner as in Example 2, five iron powder dispersion layers were formed, and finally, natural rubber was applied to form a layer containing the soft magnetic metal powder and the elastomer. The thickness of the obtained magnetically adhered sheet member was 1.3 mm, and the weight ratio of the iron powder and the natural rubber in the layer containing the soft magnetic metal powder and the elastomer was 91:9.

得られた磁着シート部材を用い、実施例２と同様に靴（パンプス）を作製した。成型後の靴では、磁着シート部材が内蔵されている箇所が外観からは容易にわからない状態となっていた。本発明の磁着シート部材を用いた場合には、鉄粉の散布層が５層の場合でも、表面の意匠に影響を及ぼすことがなかった。得られた磁着シート部材内蔵の靴の上から磁石を近づけたところ、磁着シート部材の配置箇所には、実施例２に比べてより強固に磁着した。磁石を持ち上げたり振ったりしても、容易には外れなかった。磁石を持ち上げると、靴も持ち上がり、磁石は靴から外れなかった。 A shoe (pumps) was produced in the same manner as in Example 2 using the obtained magnetically adhered sheet member. In the molded shoe, the portion where the magnetically-adhesive sheet member was incorporated was in a state where it was difficult to see from the appearance. When the magnetically adhered sheet member of the present invention was used, the design of the surface was not affected even when the iron powder dispersion layer was five layers. When a magnet was brought close to the obtained shoe with the built-in magnetically-adhesive sheet member, it was more strongly magnetically attached to the place where the magnetically-attached sheet member was arranged as compared with Example 2. Even if the magnet was lifted or shaken, it did not come off easily. When I lifted the magnet, the shoe lifted and the magnet did not come off the shoe.

［実施例４］
実施例４は、不織布を用いず、軟磁性体金属粉末とエラストマーとを含む層のみからなる磁着シート部材である。実施例１と同様に、軟磁性体金属粉末として鉄粉（＃２００、協和純薬工業株式会社製）を、エラストマーとして天然ゴム（「ＲＵＢＢＥＲＣＥＭＥＮＴ８８０」、オリエント化成工業株式会社製）を用いた。市販のクリアファイル（ポリプロピレンシート）上に、実施例２と同様に、天然ゴムを塗布した。次いで、天然ゴムの塗布面に鉄粉を散布した。そして、鉄粉の散布面の上から天然ゴムを再度塗布した。これを繰り返し、鉄粉の散布層を３層形成し、最後に天然ゴムを塗布して、軟磁性体金属粉末とエラストマーとを含む層を形成した。天然ゴムが乾燥するまで、よく乾かした後、ポリプロピレンシートから前記層を剥がし、本実施例の磁着シート部材を得た。 [Example 4]
Example 4 is a magnetic sticking sheet member which does not use a non-woven fabric and is composed of only a layer containing a soft magnetic metal powder and an elastomer. As in Example 1, iron powder (#200, manufactured by Kyowa Pure Chemical Industries, Ltd.) was used as the soft magnetic metal powder, and natural rubber (“RUBBER CEMENT 880”, manufactured by Orient Kasei Co., Ltd.) was used as the elastomer. .. Natural rubber was applied onto a commercially available clear file (polypropylene sheet) in the same manner as in Example 2. Next, iron powder was sprinkled on the coated surface of the natural rubber. Then, the natural rubber was applied again from above the surface of the iron powder. This was repeated to form three iron powder dispersion layers, and finally, natural rubber was applied to form a layer containing the soft magnetic metal powder and the elastomer. After the natural rubber was thoroughly dried, the layer was peeled off from the polypropylene sheet to obtain a magnetically adhered sheet member of this example.

得られた磁着シート部材を用い、実施例２と同様にして磁着シート部材が内蔵された靴を作製した。本実施例の磁着シート部材は、実施例１および実施例２で得られた磁着シート部材よりも、不織布がない分だけ薄くすることができ、より違和感なく製品に内蔵させることができた。 Using the obtained magnetically-adhered sheet member, a shoe having the magnetically-attached sheet member built therein was produced in the same manner as in Example 2. The magnetically adhered sheet member of this example can be made thinner than the magnetically adhered sheet members obtained in Examples 1 and 2 because there is no non-woven fabric, and the magnetically adhered sheet member can be incorporated in the product more comfortably. ..

［実施例５］
実施例４で得られた磁着シート部材に含まれる鉄粉を、外気からより遮断した状態とするために、ラップフィルム（ポリ塩化ビニリデンフィルム「ＮＥＷクレラップ」、株式会社クレハ製）を用いた。ラップフィルムを１５ｃｍ×２０ｃｍにカットし、天然ゴムを塗布した。天然ゴムの塗布面に実施例４で得られた磁着シート部材を置き、上からさらに天然ゴムをコートするように塗布した。約５分間放置した後に、ラップフィルムで磁着シート部材を、中の空気を抜くようにしながら包んだ。ヒートシーラーを用いて、ラップフィルムを溶着させて磁着シート部材を密封するとともに、余分なラップフィルムをカットして、本実施例の磁着シート部材を得た。 [Example 5]
A wrap film (polyvinylidene chloride film "NEW Kurerap", manufactured by Kureha Co., Ltd.) was used to keep the iron powder contained in the magnetically-coated sheet member obtained in Example 4 in a state of being more shielded from the outside air. The wrap film was cut into 15 cm×20 cm, and natural rubber was applied. The magnetic sheet member obtained in Example 4 was placed on the coated surface of the natural rubber, and the coating was performed so that the natural rubber was further coated from above. After leaving it for about 5 minutes, the magnetically adhered sheet member was wrapped with a wrap film so that the air therein was removed. Using a heat sealer, the wrap film was welded to seal the magnetically adhered sheet member, and the excess wrap film was cut to obtain the magnetically adhered sheet member of this example.

得られた磁着シート部材を、室温で水中に入れて放置したところ、約１か月経過後においても、鉄粉がさびた様子は見られなかった（赤色への変色は見られなかった）。 When the obtained magnetically adhered sheet member was placed in water at room temperature and allowed to stand, no rusting of iron powder was observed even after about 1 month (discoloration to red was not observed).

また、得られた磁着シート部材を用い、靴（パンプス）を作製した。５５ｍｍ×４０ｍｍの前記磁着シート部材を、両面テープを用いて靴の表革の甲部分の裏面に貼り付けた。本実施例の磁着シート部材を用いると、製品に内蔵する際に、天然ゴム等の塗布を行わずに、磁着シート部材を防水状態で固定することができる。得られた磁着シート部材付きの表革を用い、ライニングで磁着シート部材を挟み込み、通常の工程と同様に、先芯蒸器での成型を行った。成型後の靴では、磁着シート部材が内蔵されている箇所が外観からは容易にわからない状態となっていた。 In addition, shoes (pumps) were produced using the obtained magnetically adhered sheet member. The 55 mm x 40 mm porcelain sheet member was attached to the back surface of the upper part of the outer leather of the shoe using a double-sided tape. When the magnetic sheet member of this embodiment is used, the magnetic sheet member can be fixed in a waterproof state when it is built into a product without applying natural rubber or the like. Using the obtained surface leather with a magnetically-adhesive sheet member, the magnetically-adhesive sheet member was sandwiched by linings, and molding was performed in a toecap steamer in the same manner as in a normal process. In the molded shoe, the portion where the magnetically-adhesive sheet member was incorporated was in a state where it was difficult to see from the appearance.

以上のように、本発明では、装飾物等の脱着が容易であるにもかかわらず、装着時に容易に外れてしまうことがなく、さらに前記装飾物等を外した状態においても外観が良好な状態とすることが可能となる磁着シート部材、それを用いた皮革製品および靴が得られることがわかる。 As described above, in the present invention, it is easy to attach and detach a decoration or the like, but does not easily come off during mounting, and the appearance is good even when the decoration or the like is removed. It can be seen that a porcelain sheet member, a leather product and shoes using the same can be obtained.

１…靴（皮革製品）
３…磁着シート部材
５…装飾物
７…磁石 1…Shoes (leather products)
3... Magnetic sheet member 5... Ornament 7... Magnet

Claims

A magnetized sheet member having a layer containing a soft magnetic metal powder and an elastomer , the upper part of the upper, the heel part and the side part is built in at least one place,
The magnetic sheet member,
The content of the soft magnetic metal powder in the layer is in the range of 70% by weight or more and 95% by weight or less,
The content of the elastomer in the layer is in the range of 5% by weight or more and 30% by weight or less,
The shoe, wherein the thickness of the magnetically- adhesive sheet member is in the range of 0.2 mm or more and 2.0 mm or less.