JP6692534B2 - Cutlery and manufacturing method thereof - Google Patents
Cutlery and manufacturing method thereof Download PDFInfo
- Publication number
- JP6692534B2 JP6692534B2 JP2018170384A JP2018170384A JP6692534B2 JP 6692534 B2 JP6692534 B2 JP 6692534B2 JP 2018170384 A JP2018170384 A JP 2018170384A JP 2018170384 A JP2018170384 A JP 2018170384A JP 6692534 B2 JP6692534 B2 JP 6692534B2
- Authority
- JP
- Japan
- Prior art keywords
- cutlery
- decorative material
- laminated
- axial direction
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、カトラリー及びその製造方法に関するものである。 The present invention relates to a cutlery and a manufacturing method thereof.
食卓で使用されるカトラリーの製造方法として、例えば、特許文献１には、スプーンの持ち代に撥水性及び防水性を備える接着剤を含侵させた布地を巻き付ける方法が開示されている。 As a method of manufacturing a cutlery used on a dining table, for example, Patent Document 1 discloses a method of winding a cloth impregnated with an adhesive having water repellency and waterproofness around a holding margin of a spoon.
しかし、前記特許文献１の方法で製造されたカトラリーは、布地に接着剤を含侵させるため、布地が硬化して質感が変化してしまい、布地そのものの質感を生かした装飾効果を得ることができなかった。 However, since the cutlery manufactured by the method of Patent Document 1 impregnates the cloth with the adhesive, the cloth is hardened to change the texture, and a decorative effect utilizing the texture of the cloth itself can be obtained. could not.
一方、特許文献２には、箸本体に布地を巻き付けるステップと、箸本体に布地の両端から延出する長さの熱収縮ラベルを外挿するステップと、熱収縮ラベルを加熱して布地に上から圧接し、布地と熱収縮ラベルとの間に空気を封じ込めるステップと、熱収縮ラベル上に樹脂塗料を塗布するステップと、を備える方法が開示されている。 On the other hand, in Patent Document 2, a step of wrapping the cloth around the chopstick body, a step of extrapolating a heat-shrinkable label of a length extending from both ends of the cloth to the chopstick body, and a step of heating the heat-shrinkable label onto the cloth. A method of compressing air from the fabric and enclosing air between the fabric and the heat shrink label, and applying a resin coating on the heat shrink label.
前記特許文献２の方法で製造されたカトラリーであれば、熱収縮ラベルによって布地を封止するため、熱収縮ラベル越しに布地のそのままの質感を目視することができ、布地の質感を生かした装飾効果を得られる。また、熱収縮ラベル上に樹脂塗料を塗布するため、布地への水の侵入が防止され、カビが発生し難くなる。 In the cutlery manufactured by the method of Patent Document 2, since the cloth is sealed with the heat-shrinkable label, the texture of the cloth can be visually observed through the heat-shrinkable label, and the decoration utilizing the texture of the cloth is utilized. You can get the effect. In addition, since the resin coating is applied on the heat-shrinkable label, water is prevented from entering the fabric and mold is less likely to occur.
しかし、前記特許文献２の方法で製造されたカトラリーは、意図的か否かを問わず、熱収縮時に熱収縮ラベルと布地との間に空気が入り込むため、熱収縮ラベル内に空気が介在している部分と空気が介在していない部分とができ、見栄えが悪くなるという問題があった。さらに、当該カトラリーを使用する場合に、空気が介在している部分が指の押圧によって凹み、これにより、熱収縮ラベル上に塗布された樹脂塗料が撓んで剥がれ易くなり、樹脂塗料が剥がれると、布地へ水が浸入し易くなってカビ等の発生の原因となるという問題がある。 However, in the cutlery manufactured by the method of Patent Document 2, air enters between the heat-shrinkable label and the fabric at the time of heat-shrinking, whether intentionally or not, so that air is present in the heat-shrinkable label. There is a problem that the appearance is bad because there is a part where there is air and a part where air is not present. Furthermore, when using the cutlery, the portion where the air is interposed is depressed by the pressing of the finger, whereby the resin coating applied on the heat-shrinkable label is easily bent and peeled off, and when the resin coating is peeled off, There is a problem that water easily penetrates into the fabric and causes mold and the like.
そこで、本発明は、布地や和紙等の装飾材の質感を生かしつつ、装飾材に対する水の侵入を長期間に亘って防止することができるカトラリー及びその製造方法を提供することを主な課題とするものである。 Therefore, the present invention has a main object to provide a cutlery and a manufacturing method thereof that can prevent the intrusion of water into the decorative material for a long period of time while making the best use of the texture of the decorative material such as cloth or Japanese paper. To do.
すなわち、本発明に係るカトラリーは、カトラリー本体と、前記カトラリー本体の軸方向中間部に積層された装飾材と、前記装飾材の表面に粘着剤を介して貼り付けられた透明フィルムと、前記透明フィルムから露出した前記装飾材の前記軸方向に位置する各端部を封止するように積層された一対の封止帯と、少なくとも前記各封止帯の前記軸方向に位置する各端上に跨るように積層された透明層と、を備えることを特徴とするものである。 That is, the cutlery according to the present invention includes a cutlery body, a decorative material laminated on an axially intermediate portion of the cutlery body, a transparent film attached to the surface of the decorative material via an adhesive, and the transparent material. A pair of sealing bands laminated so as to seal each axially-located end of the decorative material exposed from the film, and at least on each axially-located end of each sealing band. And a transparent layer laminated so as to straddle.
このようなものであれば、布地や和紙等の装飾材に粘着剤を介して透明フィルムを貼り付けているため、装飾材の質感が損なわれず、透明フィルム越しに装飾材の質感を確認することができるようになり、意匠性の高い装飾効果を得ることができる。また、透明フィルムから露出する装飾材の軸方向に位置する各端部を封止するように封止帯を積層し、さらに、その封止帯の軸方向に位置する各端上に樹脂層を積層しているため、装飾材に対する水の浸入を防止できる。その結果、装飾材に対するカビの発生を長期間抑制できる。 If this is the case, a transparent film is attached to a decorative material such as cloth or Japanese paper via an adhesive, so the texture of the decorative material is not impaired, and the texture of the decorative material can be confirmed through the transparent film. It is possible to obtain a decorative effect with high design. Further, a sealing band is laminated so as to seal each end of the decorative material exposed from the transparent film in the axial direction, and a resin layer is further provided on each end of the sealing band in the axial direction. Since they are laminated, water can be prevented from entering the decoration material. As a result, generation of mold on the decorative material can be suppressed for a long period of time.
また、前記透明層が、前記両封止帯の間にさらに積層されたものであってもよい。 Further, the transparent layer may be further laminated between the both sealing bands.
このようなものであれば、透明層のカトラリー本体側に空気を内包され難いため、両封止帯の間に位置する装飾材上に積層された透明層が撓んで剥がれることが防止でき、長期間に亘って透明層による防水効果を維持できる。 With such a structure, since it is difficult for air to be included in the cutlery body side of the transparent layer, it is possible to prevent the transparent layer laminated on the decorative material located between the both sealing bands from being bent and peeled off. The waterproof effect of the transparent layer can be maintained over a period of time.
また、前記カトラリーにおいて、前記装飾材の前記軸方向に位置する各端が隠れるように積層された着色層をさらに備えるものであってもよい。 In addition, the cutlery may further include a coloring layer that is laminated so that each end of the decorative material located in the axial direction is hidden.
このようなものであれば、装飾材の軸方向に位置する各端が隠れるように着色層が積層されているため、見栄えの悪い装飾材の端が外観に現れず、意匠性がさらに向上する。また、カトラリー本体が、木材や竹材等の天然素材によって形成されている場合には、着色層をカトラリー本体の両端にまで伸ばして積層することにより、カトラリー本体自体が露出する部分を着色することができ、意匠性がさらに向上すると共に、カトラリー本体の耐水性を向上させることができる。 In such a case, since the colored layer is laminated so that each end of the decorative material in the axial direction is hidden, the end of the decorative material that does not look good does not appear in the appearance, and the designability is further improved. .. In addition, when the cutlery body is made of a natural material such as wood or bamboo, it is possible to color the exposed portion of the cutlery body by extending the colored layer to both ends of the cutlery body and stacking them. Therefore, the designability can be further improved, and the water resistance of the cutlery body can be improved.
なお、前記装飾材としては、布地や紙を使用すればよい。 Note that cloth or paper may be used as the decoration material.
また、本発明に係るカトラリーの製造方法は、予め表面全体に粘着剤を介して透明フィルムが貼り付けられた装飾材を、カトラリー本体の軸方向中間部に巻き付けて積層させる第１ステップと、前記透明フィルムから露出した前記装飾材の前記軸方向に位置する各端部を封止するように封止帯を密着させる第２ステップと、少なくとも前記各封止帯の前記軸方向に位置する各端上に跨るように透明塗料を塗布して透明層を形成する第３ステップと、を備えることを特徴とするものである。なお、この場合、前記装飾材の前記軸方向に位置する各端上に跨るように有色塗料を塗布して着色層を形成する第４ステップをさらに備えるものであってもよい。 Further, the method of manufacturing a cutlery according to the present invention, a decorative material having a transparent film attached to the entire surface in advance via an adhesive, a first step of winding and stacking the decorative material around an axial middle portion of the cutlery body, A second step of bringing a sealing band into close contact so as to seal each end of the decorative material exposed from the transparent film in the axial direction, and at least each end of the sealing band in the axial direction And a third step of forming a transparent layer by applying a transparent paint so as to extend over the surface. In this case, a fourth step of forming a colored layer by applying a colored paint so as to extend over each end of the decorative material located in the axial direction may be further provided.
また、前記カトラリーの製造方法において、前記封止帯が、筒状の熱収縮ラベルであってもよい。 Further, in the method of manufacturing the cutlery, the sealing band may be a tubular heat shrink label.
このようなものであれば、封止帯の軸方向に位置する各端のみに熱収縮ラベルを密着させればよく、これにより、装飾材を封止するための熱収縮ラベルの幅を短くすることができ、熱収縮時に熱収縮ラベル内へ空気が内包されることを防止できる。 In such a case, the heat-shrinkable label may be adhered only to each end of the sealing band located in the axial direction, thereby shortening the width of the heat-shrinkable label for sealing the decorative material. It is possible to prevent air from being included in the heat-shrinkable label during heat shrinkage.
このように構成した本発明に係るカトラリーによれば、布地等の装飾材の質感を生かしつつ、装飾材に対する水の侵入を長期間に亘って防止することができる。 According to the cutlery according to the present invention having such a configuration, it is possible to prevent water from entering the decorative material for a long period of time while making the most of the texture of the decorative material such as cloth.
以下に、本発明に係るカトラリー及びその製造方法を図面に基づいて説明する。 Hereinafter, a cutlery and a method for manufacturing the same according to the present invention will be described with reference to the drawings.
本発明に係るカトラリーは、食卓で使用される食器であり、具体的には、箸、スプーン、フォーク、ナイフ等が含まれる。なお、以下の実施形態においては、箸について説明する。 The cutlery according to the present invention is a tableware used at a dining table, and specifically includes chopsticks, spoons, forks, knives and the like. In addition, in the following embodiments, chopsticks will be described.
＜実施形態＞ 本実施形態に係る箸１００は、図１〜図３に示すように、箸本体１０と、箸本体１０の持ち代１０ａに積層された布地（装飾材）２０と、布地２０の表面全体に粘着剤を介して積層された透明フィルム３０と、透明フィルム３０から露出した布地２０の持ち代１０ａの軸方向（図１中、矢印方向であり、以下、単に「軸方向」ともいう）に位置する各端部２０ａ，２０ｂを封止するように積層された封止帯４０と、少なくとも封止帯４０の前記軸方向に位置する各端４０ａ，４０ｂ上に跨るように積層された透明層５０と、布地２０の各端部２０ａ，２０ｂを隠すように積層された着色層６０と、を備えている。なお、箸本体１０は、請求項におけるカトラリー本体に対応している。 <Embodiment> As shown in FIGS. 1 to 3, a chopstick 100 according to this embodiment includes a chopstick body 10, a cloth (decorative material) 20 laminated on a holding allowance 10 a of the chopstick body 10, and a cloth 20. The transparent film 30 laminated on the entire surface via an adhesive, and the axial direction of the holding allowance 10a of the fabric 20 exposed from the transparent film 30 (in FIG. 1, the arrow direction, hereinafter also simply referred to as “axial direction”). ) Are laminated so as to seal the respective end portions 20a, 20b located at), and are laminated so as to straddle at least the respective end portions 40a, 40b located in the axial direction of the sealing belt 40. The transparent layer 50 and the colored layer 60 laminated so as to hide the respective end portions 20a and 20b of the fabric 20 are provided. The chopstick body 10 corresponds to the cutlery body in the claims.
前記箸本体１０は、箸の形状に成形された棒状のものである。よって、箸本体１０は、先細り状（テーパー状）になっている。本実施形態においては、箸本体１０の材料として、木材や竹材等の吸水性を有する材料を使用している。なお、木材としては、例えば、マラス、スギヒノキ、エゾ松、又は、シラカバ等を挙げることができる。 The chopstick body 10 is a rod-shaped member formed in the shape of chopsticks. Therefore, the chopstick body 10 is tapered (tapered). In the present embodiment, as the material of the chopstick body 10, a water-absorbing material such as wood or bamboo is used. Examples of wood include maras, Japanese cedar, Japanese pine, and birch.
前記布地２０は、糸を織った織地や糸を編んだ編地であり、各糸が密に組み合わされたもの以外にも、糸が疎に組み合わされたレース状のものも含まれる。そして、布地２０は、箸本体１０の持ち代１０ａに対して周方向に一周巻き付けて積層されている。なお、布地２０には、その表面全体を被覆するように透明フィルム３０が積層されている。なお、布地２０の代わりの装飾材として、和紙等の紙を使用してもよい。すなわち、この装飾材としては、水が染み込むものであって、水によって腐食したり、カビが発生する自然素材からなるシート状のものを使用することが好適である。 The fabric 20 is a woven fabric in which yarns are woven or a knitted fabric in which yarns are knitted, and includes not only those in which the yarns are densely combined but also those in a lace shape in which the yarns are loosely combined. The cloth 20 is wound around the holding allowance 10a of the chopstick body 10 once in the circumferential direction and laminated. A transparent film 30 is laminated on the fabric 20 so as to cover the entire surface thereof. Note that paper such as Japanese paper may be used as a decorative material instead of the cloth 20. That is, as the decorative material, it is preferable to use a sheet-shaped material made of a natural material which is soaked with water and which is corroded by water and causes mold.
前記透明フィルム３０は、耐水性や撥水性を有するフィルムである。具体的には、透明フィルム３０のとしては、ポリ塩化ビニリデン等を素材とするラップフィルムなどを使用することができる。本実施形態では、透明フィルム３０は、粘着剤によって布地２０の表面全体に貼り付けられている。なお、透明フィルム３０は、布地２０の模様が透けて見える程度に透明なものであればよく、無色透明、有色透明、半透明が含まれる。また、粘着剤は、塗布後に硬化しないものを使用すればよい。 The transparent film 30 is a film having water resistance and water repellency. Specifically, as the transparent film 30, a wrap film made of polyvinylidene chloride or the like can be used. In this embodiment, the transparent film 30 is attached to the entire surface of the fabric 20 with an adhesive. The transparent film 30 may be transparent as long as the pattern of the fabric 20 can be seen through, and includes colorless transparent, colored transparent, and semi-transparent. Further, as the pressure-sensitive adhesive, one that does not cure after application may be used.
前記封止帯４０は、熱収縮ラベル（シュリンクラベル）である。熱収縮ラベルは、筒状のものである。具体的には、熱収縮ラベルは、熱収縮前の状態で箸本体１０の布地２０が貼り付けられた持ち代１０ａが余裕をもって挿入できる程度の内径を有しており、熱収縮後に箸本体１０の持ち代１０ａに密着するようになっている。また、封止帯４０は、箸本体１０に巻き付けられた布地２０の軸方向に位置する各端部２０ａ，２０ｂ上に跨るように配置された状態で、その各端２０ａ、２０ｂを封止するように熱収縮して密着している。 The sealing band 40 is a heat shrink label (shrink label). The heat shrink label has a tubular shape. Specifically, the heat-shrinkable label has an inner diameter such that the holding allowance 10a to which the cloth 20 of the chopstick body 10 is attached in a state before the heat-shrinkage can be inserted with a margin, and the heat-shrinkable label can be inserted after the heat-shrinkage. It comes into close contact with the holding margin 10a. In addition, the sealing band 40 seals the ends 20a and 20b of the cloth 20 wound around the chopstick main body 10 while being arranged so as to straddle the ends 20a and 20b located in the axial direction. As it shrinks due to heat, it is in close contact.
前記透明層５０は、耐水性や撥水性を有する透明塗料を塗布して形成された層である。なお、透明層５０は、封止帯４０の軸方向に位置する各端４０ａ，４０ｂ上に跨るように積層されている。これにより、封止帯４０と箸本体１０又は布地２０との間の隙間が封止され、この隙間から水が浸入することを防止できる。なお、本実施形態においては、透明層５０が、箸本体１０全体に積層されている。なお、透明層５０は、布地２０の模様が透けて見える程度の透明性を有するものであればよく、無色透明、有色透明、半透明が含まれる。樹脂塗料としては、例えば、ポリプロピレン、アクリル等を使用すればよい。 The transparent layer 50 is a layer formed by applying a transparent paint having water resistance and water repellency. The transparent layer 50 is laminated so as to straddle the ends 40a and 40b of the sealing band 40 located in the axial direction. As a result, the gap between the sealing band 40 and the chopstick body 10 or the cloth 20 is sealed, and water can be prevented from entering through this gap. In addition, in this embodiment, the transparent layer 50 is laminated on the entire chopstick body 10. The transparent layer 50 may be transparent as long as the pattern of the fabric 20 can be seen through, and includes colorless transparent, colored transparent, and translucent. As the resin paint, for example, polypropylene, acrylic or the like may be used.
前記着色層６０は、耐水性や撥水性を有する有色塗料を塗布して形成された層である。なお、着色層６０は、封止帯４０越しに見える布地２０の各端部２０ａ，２０ｂが隠れるように積層される。これにより、封止帯３０を介して見える見栄えの悪い布地２０の各端部２０ａ，２０ｂを隠すことができる。よって、有色塗料は、透明性を有しないものが好ましい。本実施形態においては、着色層５０が、布地２０の各端２０ａ，２０ｂを隠すように箸本体１０の両端（箸先及び箸頭）まで積層されている。有色塗料としては、例えば、漆等の天然樹脂塗料や合成樹脂塗料を使用すればよい。 The colored layer 60 is a layer formed by applying a colored paint having water resistance and water repellency. The colored layer 60 is laminated so that the end portions 20a and 20b of the fabric 20 that are visible through the sealing band 40 are hidden. This makes it possible to hide the end portions 20a and 20b of the unsightly cloth 20 that is visible through the sealing band 30. Therefore, it is preferable that the colored paint has no transparency. In the present embodiment, the colored layer 50 is laminated up to both ends (chopstick tip and chopstick head) of the chopstick body 10 so as to hide the ends 20a and 20b of the cloth 20. As the colored paint, for example, natural resin paint such as lacquer or synthetic resin paint may be used.
次に、本実施形態に係る箸１００の製造方法を図４及び図５に基づき説明する。 Next, a method of manufacturing the chopsticks 100 according to this embodiment will be described with reference to FIGS. 4 and 5.
先ず、図４（ａ）に示すように、表面全体に粘着剤を塗布して透明フィルム３０を貼り付けた布地２０を製作する。ここで、布地２０は、箸本体１０に対して巻き付ける大きさよりも大きめに製作した後に、持ち代１０ａの幅を有し、かつ、その持ち代１０ａを周方向に一周する長さを有する大きさに切断したものを使用する。そして、図４（ｂ）に示すように、箸本体１０の持ち代１０ａに布地２０を一周巻き付けて粘着剤又は接着剤によって貼り付ける。この状態において、透明フィルム３０が貼り付けられた布地２０の各端部２０ａ，２０ｂ（本実施形態では、布地２０の端面、言い換えれば、透明フィルム３０が貼り付けられた布地２０の切断面）が透明フィルム３０から露出した状態となる。 First, as shown in FIG. 4 (a), an adhesive is applied to the entire surface to fabricate a cloth 20 to which a transparent film 30 is attached. Here, the fabric 20 has a width of the holding allowance 10a after being made larger than a size to be wound around the chopstick body 10, and has a length that makes one turn in the holding allowance 10a in the circumferential direction. Use the one cut into. Then, as shown in FIG. 4 (b), the cloth 20 is wrapped around the holding allowance 10a of the chopstick body 10 once and attached with an adhesive or an adhesive. In this state, the respective end portions 20a and 20b of the cloth 20 to which the transparent film 30 is attached (in the present embodiment, the end surfaces of the cloth 20; in other words, the cut surface of the cloth 20 to which the transparent film 30 is attached) The transparent film 30 is exposed.
次に、箸本体１０の持ち代１０ａに貼り付けられた布地２０の透明フィルム３０から露出する各端部２０ａ，２０ｂを封止帯３０によって封止する。なお、本実施形態では、図４（ｃ）に示すように、先ず、箸本体１０に巻き付けられた布地２０の軸方向に位置する各端部２０ａ，２０ｂに、その端部２０ａ，２０ｂ上に跨るように筒状の熱収縮ラベルを配置し、その後、図４（ｄ）に示すように、熱収縮ラベルを加熱して収縮させることによって封止している。 Next, each end 20a, 20b exposed from the transparent film 30 of the cloth 20 attached to the holding allowance 10a of the chopstick body 10 is sealed by the sealing band 30. In the present embodiment, as shown in FIG. 4 (c), first, at the end portions 20a, 20b located in the axial direction of the cloth 20 wound around the chopstick body 10, the end portions 20a, 20b are placed on the end portions 20a, 20b. A tubular heat-shrinkable label is arranged so as to straddle, and thereafter, as shown in FIG. 4D, the heat-shrinkable label is heated and shrunk to be sealed.
次に、各封止帯４０の軸方向に位置する各端４０ａ，４０ｂ上に跨るように透明の塗料を塗布して透明層５０を形成する。なお、本実施形態においては、図５（ａ）に示すように、箸本体１０全体に透明の塗料を塗布し、各封止帯４０の各端４０ａ，４０ｂ上に跨る透明層５０を形成している。 Next, a transparent coating material is applied so as to straddle the ends 40a and 40b of each sealing band 40 located in the axial direction to form the transparent layer 50. In addition, in this embodiment, as shown in FIG. 5A, a transparent coating material is applied to the entire chopstick body 10 to form a transparent layer 50 extending over the respective ends 40a and 40b of the respective sealing bands 40. ing.
次に、各封止帯４０越しに見える前記布地２０の各端部２０ａ，２０ｂを隠すように有色の塗料を塗布して着色層６０を形成する。なお、本実施形態においては、図５（ｂ）に示すように、箸本体１０の一方の封止帯４０を含む箸頭側までと、箸本体１０の他方の封止帯４０を含む箸先側までと、にそれぞれ有色塗料を塗布し、箸本体１０の両封止帯４０の間の領域を除く箸頭側及び箸先側に着色層６０を形成している。これにより、両封止帯４０の間の領域から布地２０の模様が目視できるようになる。 Next, a colored paint is applied to form the colored layer 60 so as to hide the respective end portions 20a and 20b of the cloth 20 which are visible through the respective sealing bands 40. In addition, in the present embodiment, as shown in FIG. 5B, a chopstick tip including the one sealing band 40 of the chopstick body 10 and the chopstick tip including the other sealing band 40 of the chopstick body 10. The colored layer 60 is formed on the chopstick head side and the chopstick tip side of the chopstick body 10 except for the area between the sealing strips 40 of the chopstick body 10, respectively. This allows the pattern of the fabric 20 to be visually recognized from the area between the two sealing bands 40.
＜その他の実施形態＞ 前記実施形態においては、封止帯４０として筒状の熱収縮ラベルを使用したが、これに限定することなく、封止帯４０として、例えば、透明粘着テープを使用してもよい。 <Other Embodiments> In the above-described embodiment, a tubular heat-shrinkable label is used as the sealing band 40, but the sealing band 40 is not limited to this and, for example, a transparent adhesive tape is used. Good.
また、前記実施形態においては、箸本体１０の一箇所（持ち代１０ａ）に布地２０を巻き付けているが、箸本体１０の複数箇所に布地２０を巻き付けるようにしてもよい。 Further, in the above-described embodiment, the cloth 20 is wound around one portion (holding allowance 10a) of the chopstick body 10, but the cloth 20 may be wrapped around a plurality of portions of the chopstick body 10.
また、前記実施形態においては、箸を例示して説明したが、例えば、フォーク、スプーン、ナイフ等であってもよい。 Further, although the chopsticks have been described as an example in the above embodiment, for example, a fork, a spoon, a knife, or the like may be used.
その他、本発明は前記各実施形態に限られず、その趣旨を逸脱しない範囲で種々の変形が可能であるのは言うまでもない。 In addition, it goes without saying that the present invention is not limited to the above-described embodiments, and various modifications can be made without departing from the spirit of the present invention.
１００ 箸（カトラリー）
１０ 箸本体
２０ 装飾材
３０ 透明フィルム
４０ 封止帯
５０ 樹脂層
６０ 着色層
100 chopsticks
10 Chopstick body 20 Decorative material 30 Transparent film 40 Sealing band 50 Resin layer 60 Colored layer
Claims (7)
前記カトラリー本体の軸方向中間部に積層された装飾材と、
前記装飾材の表面に粘着剤を介して貼り付けられた透明フィルムと、
前記透明フィルムから露出した前記装飾材の前記軸方向に位置する各端部を封止するように積層された一対の封止帯と、
少なくとも前記各封止帯の前記軸方向に位置する各端上に跨るように積層された透明層と、を備えることを特徴とするカトラリー。 With the cutlery body,
A decorative material laminated on an intermediate portion in the axial direction of the cutlery body,
A transparent film attached to the surface of the decorative material via an adhesive,
A pair of sealing bands laminated so as to seal each end portion of the decorative material exposed from the transparent film in the axial direction,
At least a transparent layer laminated so as to extend over each end of the sealing band located in the axial direction, the cutlery.
前記透明フィルムから露出した前記装飾材の前記軸方向に位置する各端部を封止するように封止帯を密着させる第２ステップと、
少なくとも前記各封止帯の前記軸方向に位置する各端上に跨るように透明塗料を塗布して透明層を形成する第３ステップと、を備えることを特徴とするカトラリーの製造方法。 A first step in which a decorative material having a transparent film attached to the entire surface in advance via an adhesive is wrapped around the axially intermediate portion of the cutlery body to be laminated,
A second step of bringing a sealing band into close contact with each other so as to seal each end of the decorative material exposed from the transparent film in the axial direction,
A third step of forming a transparent layer by applying a transparent coating material so as to extend over at least each end of each sealing band located in the axial direction, and a method for manufacturing a cutlery.