JP6603602B2 - Resin holding base material for internal repair of piping and repair method using the base material - Google Patents
Resin holding base material for internal repair of piping and repair method using the base material Download PDFInfo
- Publication number
- JP6603602B2 JP6603602B2 JP2016056315A JP2016056315A JP6603602B2 JP 6603602 B2 JP6603602 B2 JP 6603602B2 JP 2016056315 A JP2016056315 A JP 2016056315A JP 2016056315 A JP2016056315 A JP 2016056315A JP 6603602 B2 JP6603602 B2 JP 6603602B2
- Authority
- JP
- Japan
- Prior art keywords
- substrate
- pipe
- base material
- resin holding
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、主として、本管に接続された取付管の内面を補修して、樹脂被覆するための樹脂保持基材およびそれを用いた補修方法に関する。 The present invention mainly relates to a resin holding base material for repairing an inner surface of a mounting pipe connected to a main pipe and coating the resin, and a repair method using the same.
本出願人は既に、下記特許文献１に記載の既設取付管の補修方法を提案している。
この発明は、長尺で筒状の軟質なインナーフィルムとアウターフィルムと、両フィルム間に介装された未硬化の樹脂付き補修基材とを具備し、内部に気体を供給して樹脂を硬化させるものである。
これは、アウターフィルムとインナーフィルムとの間にガラスパイルを配置すると共に、耐食性の優れたエポキシアクリレート樹脂をそのパイルに十分に付着させる。そして、エアーを供給すると共に、光硬化装置を内部に挿入して樹脂材を光硬化させるものである。
The present applicant has already proposed a method for repairing an existing mounting pipe described in Patent Document 1 below.
The present invention comprises a long and cylindrical soft inner film and an outer film, and an uncured resin-equipped repair base material interposed between the two films, and supplies the gas therein to cure the resin. It is something to be made.
This arrange | positions a glass pile between an outer film and an inner film, and fully adheres the epoxy acrylate resin excellent in corrosion resistance to the pile. And while supplying air, a photocuring apparatus is inserted in an inside and a resin material is photocured.
従来の配管内面の補修用の樹脂保持基材は、縦糸と横糸をクロスさせ、それに樹脂を付着させ、光硬化又は熱硬化により、配管内面を被覆するものである。
ところが、従来の樹脂保持基材では、特に配管の曲り部において、皺が生じ、そこに盛り上がりが形成される。すると、その曲り部で流体の流通を阻害するおそれがある。
そこで、本発明は、配管の曲り部で皺ができ難く、その被覆層の内面を可及的に平滑にできる配管の内面補修用の樹脂保持基材およびそれを用いた補修方法を提供することを課題とする。
A conventional resin holding base material for repairing the inner surface of a pipe is one in which warp and weft are crossed, a resin is adhered thereto, and the inner surface of the pipe is covered by photocuring or thermosetting.
However, in the conventional resin-holding substrate, wrinkles are generated particularly at the bent portion of the pipe, and a bulge is formed there. Then, there exists a possibility that the distribution | circulation of the fluid may be inhibited at the bent part.
Accordingly, the present invention provides a resin holding base material for repairing the inner surface of a pipe that is difficult to cause wrinkles at the bent portion of the pipe and makes the inner surface of the coating layer as smooth as possible, and a repair method using the same. Is an issue.
請求項１に記載の発明は、ガラス繊維またはポリエステル繊維の経編みニットであって、その繊維の繊度が１００ＴＥＸ〜４００ＴＥＸのものであり、
鎖編みの編目列（Ｌ４）と横振りの挿入糸（Ｌ５、Ｌ６）との角目状の組織（Ｌ４、Ｌ５、Ｌ６）である裏素地（２）と、その裏素地（２）に対向して菱目状または亀甲状の組織（Ｌ１、Ｌ２）である表素地（１）と、両素地（１、２）間を連結する連結糸（３）とにより立体構造ネットの組織を有している配管の内面補修用の樹脂保持基材である。
The invention according to claim 1 is a warp knitted knit of glass fiber or polyester fiber, and the fiber has a fineness of 100 TEX to 400 TEX,
A lining substrate (2) that is a square-shaped structure (L4, L5, L6) of a chain stitch stitch row (L4) and a laterally inserted insertion yarn (L5, L6), and facing the lining substrate (2) And a surface structure (1) which is a rhombus-shaped or turtle-shaped structure (L1, L2) and a connecting thread (3) which connects both the structures (1, 2), and has a three-dimensional structure net structure. It is a resin holding base material for repairing the inner surface of the pipe.
請求項２に記載の発明は、請求項１に記載の配管の内面補修用の樹脂保持基材であって、
前記繊維のコース（２．５４ｃｍ（＝１インチ）間の網目を縦方向に数えた数値）が、２．３６回／ｃｍ（＝６．０回／インチ）〜４．７２回／ｃｍ（＝１２．０回／インチ）であり、
前記繊維のウェール（２．５４ｃｍ（＝１インチ）間の網目を横方向に数えた数値） が、３．５４回／ｃｍ（＝９．０回／インチ）〜７．０８回／ｃｍ（＝１８．０回／インチ）である配管の内面補修用の樹脂保持基材である。
Invention of Claim 2 is the resin holding base material for inner surface repair of piping of Claim 1, Comprising:
The fiber course (numerical value counted in the longitudinal direction of the mesh between 2.54 cm (= 1 inch) ) is from 2.36 times / cm (= 6.0 times / inch) to 4.72 times / cm (= 12.0 times / inch)
The fiber wales (numerical values counted in the horizontal direction between meshes of 2.54 cm (= 1 inch) ) are from 3.54 times / cm (= 9.0 times / inch) to 7.08 times / cm (= 18.0 times / inch) is a resin holding base material for repairing the inner surface of a pipe.
請求項３に記載の発明は、請求項１または請求項２に記載の配管の内面補修用の樹脂保持基材において、
前記裏素地２と表素地１とを連結する連結糸３の構造をストレート構造とした配管の内面補修用の樹脂保持基材である。
The invention according to claim 3 is the resin holding substrate for repairing the inner surface of the pipe according to claim 1 or 2,
This is a resin holding base material for repairing the inner surface of a pipe in which the structure of the connecting yarn 3 that connects the backing substrate 2 and the front substrate 1 is a straight structure.
請求項４に記載の発明は、請求項１〜請求項３のいずれかに記載の配管の内面補修用の樹脂保持基材において、
前記立体構造ネットの厚みが２ｍｍ〜１２ｍｍである配管の内面補修用の樹脂保持基材である。
Invention of Claim 4 in the resin holding base material for inner surface repair of piping in any one of Claims 1-3,
It is a resin holding base material for repairing the inner surface of a pipe whose thickness of the three-dimensional structure net is 2 mm to 12 mm.
請求項５に記載の発明は、請求項１〜請求項４のいずれかに記載の配管の内面補修用の樹脂保持基材を用いた配管の内面補修方法において、
その樹脂保持基材８に光硬化性または熱硬化性の樹脂材を含浸する工程と、
その樹脂保持基材８の前記裏素地２側にアウターフィルム５を被着し、前記表素地１側にインナーフィルム４を被着して、その表素地１の網目の縦方向が既設取付管９の軸方向と一致させる工程と、
そのインナーフィルム４の内部に流体を供給して、膨張させながら、その樹脂保持基材８の裏素地２側を既設取付管９の内面にアウターフィルム５を介して圧着する工程と、
次いでインナーフィルム４内に樹脂硬化用の補修機を挿入し、前記樹脂保持基材８を硬化する工程と、
を具備する配管の内面補修方法である。
The invention according to claim 5 is a pipe inner surface repair method using a resin holding base material for pipe inner surface repair according to any one of claims 1 to 4,
Impregnating the resin holding substrate 8 with a photocurable or thermosetting resin material;
An outer film 5 is attached to the back substrate 2 side of the resin holding base material 8, an inner film 4 is attached to the front substrate 1 side, and the vertical direction of the mesh of the surface substrate 1 is the existing attachment tube 9. The step of matching with the axial direction of
A step of pressure bonding the inner surface of the existing mounting pipe 9 to the inner surface of the existing mounting tube 9 while supplying a fluid into the inner film 4 and expanding the fluid;
Next, a step of inserting a resin curing repair machine into the inner film 4 and curing the resin holding substrate 8;
It is the inner surface repair method of piping which comprises.
請求項１に記載の発明は、比較的屈曲に弱いガラス繊維を用いても、その繊維の繊度が１００ＴＥＸ〜４００ＴＥＸの範囲であるため、基材を経編みニットの立体構造とすることができ、その基材に十分な樹脂を含浸できる。特に、表素地と裏素地との間を連結する連結糸の存在により、樹脂の空間保持率を高めて、そこに樹脂を保持し、配管の内面に形成する樹脂層を厚くできる。即ち、配管の内面に十分厚みのある補修層を形成でき、耐久性の高い配管内面となる。
なお、繊維を１００ＴＥＸ以下とすると、空隙部が多くなり必要な強度が得られなくなる。また、４００ＴＥＸを以上太い繊維を使用すると、ガラス繊維を小さな半径で屈曲させて網目を形成することができなくなる。
In the invention according to claim 1, even if glass fibers that are relatively weak to bending are used, the fineness of the fibers is in the range of 100 TEX to 400 TEX, so that the base material can have a three-dimensional structure of warp knitting knit, The substrate can be impregnated with sufficient resin. In particular, the presence of the connecting yarn that connects the front substrate and the back substrate increases the space retention rate of the resin, holds the resin therein, and thickens the resin layer formed on the inner surface of the pipe. That is, a sufficiently thick repair layer can be formed on the inner surface of the pipe, resulting in a highly durable pipe inner surface.
If the fiber is 100 TEX or less, the voids increase and the required strength cannot be obtained. Further, when a fiber having a thickness of 400 TEX or more is used, it becomes impossible to form a network by bending the glass fiber with a small radius.
次に、この樹脂保持基材は、裏素地（被補修管に接する内面側）が、鎖編みの編目列Ｌ４と横振りの挿入糸Ｌ５、Ｌ６からなる角目状の組織として構成されており、表素地（裏素地に対向して配管の軸線側に配置される素地）は網目のように編成される菱目または亀甲状の組織Ｌ１、Ｌ２として構成されており、両素地間を連結糸で連結した立体構造ネットを構成している。
配管の内面側に配置される裏素地を角目状の組織としたことにより、その角目組織が軸方向にも円周方向へも延び易くい構造となっているため、配管の屈曲部に追随することができ、樹脂保持基材が配管内面にフィットすることができる。
一方で、表素地を網目のように編成される菱目または亀甲状の組織としたことにより、一定の伸縮性を保ちながら、軸方向には伸び難くく、円周方向に伸び易い構造となっている。そのため、配管に圧着して硬化したときには、配管の軸線側に皺が出来にくくなり、 素地表面の凹凸を少なくして樹脂硬化後の表面を平滑にして、管内の流水性をよくし、体裁のよい内面を形成できる。即ち、配管の屈曲部での内部流体の流通を促進できる。
また、この表素地の構造により、連結糸を補強して樹脂材の厚みを保持することができる。
Next, in this resin holding base material, the backing base (the inner surface side in contact with the pipe to be repaired) is configured as a square-shaped structure comprising a chain stitch L4 and lateral insertion yarns L5 and L6. The front substrate (the substrate arranged on the axis side of the pipe facing the back substrate) is configured as a rhombus or turtle-like structure L1, L2 knitted like a mesh, and a connecting yarn between the two substrates The three-dimensional structure net connected with is constructed.
By making the backing substrate arranged on the inner surface side of the pipe into a square-shaped structure, the square structure is easy to extend both in the axial direction and in the circumferential direction. The resin holding base material can be fitted to the inner surface of the pipe.
On the other hand, the surface substrate is a rhombus or turtle shell-like structure that is knitted like a mesh, making it difficult to stretch in the axial direction and easily stretch in the circumferential direction while maintaining a certain stretchability. ing. For this reason, when it is hardened by pressure bonding to the pipe, it becomes difficult to wrinkle on the axis side of the pipe, the surface of the substrate surface is reduced to smoothen the surface after resin hardening, improve the water flow in the pipe, and improve the appearance. A good inner surface can be formed. That is, it is possible to promote the flow of the internal fluid at the bent portion of the pipe.
Further, the structure of the surface substrate can reinforce the connecting yarn and maintain the thickness of the resin material.
請求項２に記載のように、繊維のコースが６．０〜１２．０回／インチであり、繊維のウェールが９．０〜１８．０回／インチである場合には、良好な編み組織となる。
繊維のコースが６．０回／インチ以下または１２．０回／インチ以上だと、編み機の能力的な困難を伴う。繊維のウェールが９．０〜１８．０回／インチとしたのは、９．０回／インチよりも網目列の間隔があくと、成形後に表面に凹凸ができ、１８．０回／インチより緻密になると、伸縮性が得られなくなることが分かったからである。
A good knitting structure when the fiber course is 6.0 to 12.0 times / inch and the wale of the fibers is 9.0 to 18.0 times / inch. It becomes.
When the fiber course is 6.0 times / inch or less or 12.0 times / inch or more, the knitting machine has a difficult ability. The fiber wale was set to 9.0 to 18.0 times / inch because if the mesh rows were spaced apart from the 9.0 times / inch, the surface was uneven after molding, and from 18.0 times / inch This is because it has been found that when it becomes dense, stretchability cannot be obtained.
請求項３に記載の発明のように、裏素地２と表素地１とを連結する連結糸３の構造をストレート構造とした場合には、連結糸の糸量が大きくなるのを抑制して、生産効率を上げることができる。 When the structure of the connecting yarn 3 that connects the backing substrate 2 and the front substrate 1 is a straight structure as in the invention described in claim 3, it is possible to suppress an increase in the yarn amount of the connecting yarn, Production efficiency can be increased.
請求項４に記載の発明のように、前記立体構造ネットの厚みを２ｍｍ〜１２ｍｍとすると、ダブルラッセル編み機で、伸縮性のよいダブルラッセル構造を容易に編むことができ、本樹脂保持材を容易に製造することができる。 When the thickness of the three-dimensional structure net is 2 mm to 12 mm as in the invention described in claim 4, a double raschel knitting machine can be easily knitted with a double raschel knitting machine, and the resin holding material can be easily obtained. Can be manufactured.
請求項５に記載の配管の内面補修方法によれば、上記いずれかの内面補修用の樹脂保持基材を用いて、配管内面に十分に厚い被覆層を形成することができる。そして、表素地の編み目状の菱目または亀甲状の組織のコース（１インチ間の網目を縦方向に数えた数値）の方向を軸線方向に一致させる。
実験によれば、その表素地の縦方向を配管の軸線方向に一致させることにより、一定の伸縮性を保ちながら、軸方向には伸びにくく、円周方向に伸び易くなり、皺が出来にくくなる。即ち、表素地の編み目状の菱目または亀甲状の組織のコース（１インチ間の網目を縦方向に数えた数値）の方向を軸線方向に一致させる。
According to the method for repairing the inner surface of the pipe according to claim 5, a sufficiently thick coating layer can be formed on the inner surface of the pipe by using any one of the resin retaining base materials for inner surface repair. Then, the direction of the course (the numerical value counted in the vertical direction of the meshes between 1 inch) of the stitch-like rhombus or turtle shell-like structure of the surface substrate is made to coincide with the axial direction.
According to the experiment, by making the vertical direction of the surface substrate coincide with the axial direction of the pipe, it is difficult to stretch in the axial direction, easily stretch in the circumferential direction, and difficult to wrinkle while maintaining a certain stretchability. . That is, the direction of the course (the numerical value counted in the vertical direction of the mesh between 1 inch) of the stitch-like rhombus or turtle shell-like texture of the surface substrate is made to coincide with the axial direction.
なお、上記の裏素地と表素地との配置を配管内で逆にすると、配管の内面側に凹凸が生じ、流水の流れを妨げることが分かった。即ち、鎖状に編成される角目状の組織の裏素地を配管の中心側に配置すると、その内面が平滑にならないことが、実験により明らかになった。 In addition, it turned out that an unevenness | corrugation will arise in the inner surface side of piping, and the flow of flowing water will be disturbed if arrangement | positioning of said backing base material and surface base material is reversed in piping. In other words, it has been clarified through experiments that the inner surface of the lining of a square-shaped structure knitted in a chain is not smooth when it is arranged on the center side of the pipe.
次に、図面に基づいて本発明の樹脂保持基材およびそれを用いた補修方法につき、説明する。図１は、本発明の樹脂保持基材の説明図であり、図２は、それを構成する各糸Ｌ１〜Ｌ６を示す。
（樹脂保持基材の構造）
この配管の内面補修用の樹脂保持基材８は、それに熱硬化性又は光硬化性の樹脂を含浸するものであり、流体圧により既設取付管９の内面に圧着し、光硬化又は熱硬化により樹脂を硬化して、その取付管９の内面を補修するためのものである。
Next, the resin holding substrate of the present invention and the repair method using the same will be described with reference to the drawings. FIG. 1 is an explanatory view of the resin holding base material of the present invention, and FIG. 2 shows the respective yarns L1 to L6 constituting the same.
(Structure of resin holding substrate)
The resin holding base material 8 for repairing the inner surface of the pipe is impregnated with a thermosetting or photocurable resin, and is pressure-bonded to the inner surface of the existing mounting tube 9 by fluid pressure, and is cured by photocuring or thermosetting. This is for curing the resin and repairing the inner surface of the mounting tube 9.
この樹脂保持基材８は、ガラス繊維又はポリエステル繊維の経編みニットである。また、その繊維の太さ（繊度）が１００ＴＥＸ〜４００ＴＥＸであって、図１に示す如く、立体構造ネットの組織を有している。
即ち、その立体構造ネット状の組織は、表素地１と裏素地２と、両素地の間を架け渡す連結糸３とからなる。
The resin holding substrate 8 is a warp knitted knit made of glass fiber or polyester fiber. Further, the thickness (fineness) of the fibers is 100 TEX to 400 TEX, and as shown in FIG.
That is, the structure of the three-dimensional structure net is composed of a front substrate 1, a backing substrate 2, and a connecting thread 3 that bridges between the substrates.
表素地１は、図２の糸Ｌ１と糸Ｌ２とにより網目状に編成される菱目状または亀甲状の組織であり、裏素地２は、図２の鎖状の編目列糸Ｌ４と、これに横ぶり挿入される挿入糸Ｌ５、挿入糸Ｌ６とにより角目状の組織であり、図１に示す如く、これらの表素地１と裏素地２とが連結糸３（図２の糸Ｌ３からなる）により立体構造ネット状の構造をしている。
この例では図１の如く、連結糸３は表素地１と裏素地２の間を接続するものであり、その繊維は表素地１、裏素地２の素地に直行（ストレート状）して架け渡すように編み込まれる構造をしている。ただし、連結糸３を用いた連結構造は、ストレート状の構造に限定されるものではない。
The front substrate 1 is a rhombus or turtle shell-like structure knitted in a mesh pattern by the yarn L1 and the yarn L2 in FIG. 2, and the backing substrate 2 is a chain-like stitch row yarn L4 in FIG. The insertion thread L5 and the insertion thread L6 are inserted into the horizontal direction to form a square structure. As shown in FIG. 1, the front substrate 1 and the back substrate 2 are connected to the connecting yarn 3 (from the yarn L3 in FIG. 2). To have a three-dimensional net structure.
In this example, as shown in FIG. 1, the connecting yarn 3 connects between the front substrate 1 and the back substrate 2, and the fibers are passed straight (straight) to the substrate of the front substrate 1 and the back substrate 2. The structure is knitted like this. However, the connection structure using the connection yarn 3 is not limited to a straight structure.
図６は、その裏素地２の拡大図であり、図７は、表素地１の平面拡大図である。
図６および図７において、繊維の繊度は１００ＴＥＸ〜４００ＴＥＸである。
繊維を１００ＴＥＸ以下とすると空隙部が大きくなり、必要な強度が得られなくなる。また、４００ＴＥＸ以上太い繊維を用いるとガラス繊維を小さな半径で屈曲させて、編目を形成することができなくなる。
FIG. 6 is an enlarged view of the backing substrate 2, and FIG. 7 is an enlarged plan view of the front substrate 1.
6 and 7, the fineness of the fiber is 100 TEX to 400 TEX.
If the fiber is 100 TEX or less, the gap becomes large and the required strength cannot be obtained. Further, when a fiber thicker than 400 TEX is used, it is impossible to form a stitch by bending the glass fiber with a small radius.
また、表素地１、裏素地２の繊維のコース（１インチ間の網目を縦方向に数えた数値）は６．０〜１２．０回／インチであり、繊維のウェール（１インチ間の網目を横方向に数えた数値）は、９．０〜１８．０回／インチとすることが好ましい。
コースを６．０回／インチ以下または１２．０回／インチ以上にすると、この樹脂保持基材を作成するためのダブルラッセル機で編成することが難しい。また、ウェールを９．０回／インチよりも編目列の間隔をあけると、成形後に表面に凹凸ができる。また、１８．０回／インチより緻密になると伸縮性が得られなくなることが発明者の実験により分かった。この条件は、設計により変更可能である。
Also, the fiber course of the front substrate 1 and the back substrate 2 (the numerical value counted in the vertical direction of the mesh between 1 inch) is 6.0 to 12.0 times / inch, and the fiber wale (the mesh between 1 inch) Is a value in the range of 9.0 to 18.0 times / inch.
If the course is 6.0 times / inch or less or 12.0 times / inch or more, it is difficult to knit with a double Russell machine for producing the resin holding substrate. Further, when the wales are spaced apart by a stitch row more than 9.0 times / inch, the surface becomes uneven after molding. Further, it has been found by the inventors' experiment that when the density becomes denser than 18.0 times / inch, stretchability cannot be obtained. This condition can be changed by design.
また、表素地１と裏素地２の間を連結糸３によりストレート状に接続する構造にすることが好ましく、そうすることにより、連結糸の糸量が大きくなることを抑制して、生産効率を上げることができる。この条件は、設計により変更可能である。
このような立体構造ネットの組織からなる基材は、その厚みが２ｍｍ〜１２ｍｍとすることが好ましい。この条件は、設計により変更可能である。
Moreover, it is preferable to make it the structure which connects between the surface base material 1 and the back base material 2 with the connection thread | yarn 3 in a straight form, and by doing so, it suppresses that the thread quantity of a connection thread | yarn becomes large, and increases production efficiency. Can be raised. This condition can be changed by design.
The base material made of such a three-dimensional structure net structure preferably has a thickness of 2 mm to 12 mm. This condition can be changed by design.
（樹脂保持基材の製造方法）
このような樹脂保持基材は、ダブルラッセル編み機により製造することができる。
このダブルラッセル編み機は、生地を編成する２列の針床（ニードルヘッド）を有している。この編み機によって編成される生地は、表素地と裏素地を別々に編む（組織は表素地と裏素地を変えて編むことも可能である）ことができ、表素地と裏素地の全部または一部を連結糸で連結して編むことができる。厚みのある立体的なシート状や円筒状の基材を製造することができる。
この編み機により、伸縮性のよいダブルラッセル構造（本発明の樹脂保持基材に適用される編み構造の上位概念）を容易に編むことができ、本発明の樹脂保持基材を容易に製造することができる。
(Method for producing resin holding substrate)
Such a resin holding substrate can be manufactured by a double Russell knitting machine.
This double raschel knitting machine has two rows of needle beds (needle heads) for knitting the fabric. The fabric knitted by this knitting machine can knit the front and back substrates separately (the organization can also knit by changing the front and back substrates), and all or part of the front and back substrates Can be connected and knitted with connecting yarns. A thick three-dimensional sheet-like or cylindrical base material can be manufactured.
With this knitting machine, it is possible to easily knit a double raschel structure with good stretchability (superior concept of the knitting structure applied to the resin holding substrate of the present invention), and to easily manufacture the resin holding substrate of the present invention. Can do.
（本発明の樹脂保持基材を用いた配管の補修方法）
次に、本発明の樹脂保持基材による配管の補修方法につき説明する。
先ず、樹脂保持基材８に光硬化性または熱硬化性の樹脂材を含浸する。この樹脂保持基材８は、通常、筒状に加工されたものを用いる（シート状のものを丸めた状態にしたものを使用してもよい）。
次に、図４に示す如く、その樹脂保持基材８の前記裏素地２（角目状の組織）の側にアウターフィルム５を配置し、表素地１（菱目状または亀甲状の組織）の側にインナーフィルム４（インナーフィルム５は、その先端に取付けられたボビン６により袋状に形成されている。）を配置する。その際、樹脂保持基材８の表素地１（菱目状または亀甲状の組織）の編目の縦方向（コースの方向）が既設取付管９の軸Ｏの方向と一致するように、反転機（図示しない）に取付ける。反転機（圧縮空気などの流体をインナーフィルム４内に送り込むもの）は公知のものを用いることができる。
(Piping repair method using the resin holding substrate of the present invention)
Next, the pipe repairing method using the resin holding substrate of the present invention will be described.
First, the resin holding substrate 8 is impregnated with a photocurable or thermosetting resin material. The resin holding substrate 8 is usually a cylindrically processed one (a sheet-like one rolled up may be used).
Next, as shown in FIG. 4, the outer film 5 is arranged on the side of the backing substrate 2 (square-shaped structure) of the resin holding base material 8, and the surface substrate 1 (rhombus-shaped or turtle-shaped structure). The inner film 4 (the inner film 5 is formed in a bag shape by a bobbin 6 attached to the tip thereof) is disposed on the side of the inner side. At that time, a reversing machine is used so that the longitudinal direction (course direction) of the stitch of the surface substrate 1 (rhombus-shaped or turtle shell-shaped structure) of the resin holding base material 8 coincides with the direction of the axis O of the existing mounting tube 9. Attach to (not shown). A known reversing machine (that feeds fluid such as compressed air into the inner film 4) can be used.
次いで、そのインナーフィルム４の内部に反転機から圧縮流体を供給することにより、インナーフィルム４を膨張させ、各フィルム４、５と共に樹脂保持基材８を反転しながら既設取付管９の内面に沿って侵入させる。
図３は、樹脂保持基材８がアウターフィルム５を介して既設取付管９の内面に圧着されている状態を示している。
そして、図３に示す如く、樹脂保持基材８の裏素地２（角目状の組織）の側がアウターフィルム５を介して既設取付管９の内面に圧着させる。なお、図３に示す如く、インナーフィルム４は、既設取付管９から既設本管７内に突出した状態となっている。
Subsequently, the inner film 4 is expanded by supplying compressed fluid from the reversing machine to the inside of the inner film 4, and along the inner surface of the existing mounting tube 9 while reversing the resin holding substrate 8 together with the films 4 and 5. To invade.
FIG. 3 shows a state in which the resin holding substrate 8 is pressure-bonded to the inner surface of the existing mounting tube 9 via the outer film 5.
Then, as shown in FIG. 3, the side of the backing base 2 (cornered structure) of the resin holding base material 8 is pressed against the inner surface of the existing mounting tube 9 via the outer film 5. As shown in FIG. 3, the inner film 4 is in a state of protruding from the existing mounting pipe 9 into the existing main pipe 7.
この樹脂保持基材８の裏素地２の角目組織は、その角目組織が軸方向にも円周方向へも延び易い構造となっているため、既設取付管９の屈曲部に追随することができ、樹脂保持基材８を既設取付管９の曲り部の内面にフィットさせることができる。
一方、表素地１を菱目または亀甲状の組織としたことにより、一定の伸縮性を保ちながら、軸方向には伸び難く、円周方向に伸び易い構造となっている。そのため、配管の屈曲部で皺が出来にくくなる。
上記樹脂保持基材の特性を生かすため、アウターフィルム５および樹脂保持基材８は、反転機に固定されている端の反対側は、図３の如く、フリーな状態にすることが、好ましい。
The corner structure of the backing substrate 2 of the resin holding substrate 8 has a structure in which the corner structure easily extends both in the axial direction and in the circumferential direction, and therefore follows the bent portion of the existing mounting tube 9. The resin holding base material 8 can be fitted to the inner surface of the bent portion of the existing mounting tube 9.
On the other hand, the surface substrate 1 has a rhombus or turtle shell-like structure, so that it has a structure that hardly stretches in the axial direction and easily stretches in the circumferential direction while maintaining a certain stretchability. Therefore, it becomes difficult to make wrinkles at the bent part of the pipe.
In order to take advantage of the characteristics of the resin-holding substrate, it is preferable that the outer film 5 and the resin-holding substrate 8 be in a free state as shown in FIG.
次いで、インナーフィルム４の内部に図示しない樹脂硬化用の補修機を挿入し、インナーフィルム４内を移動させて、樹脂保持基材８を硬化させる。そして、既設取付管９の内面を補修する。
次いで、インナーフィルム４を取り除くことにより、既設取付管９の内面の補修を完成する。後処理として、その取付管９から既設本管７に突出したアウターフィルム５および樹脂保持基材８の部分をカットすると良い。
Next, a resin curing repair machine (not shown) is inserted into the inner film 4 and moved in the inner film 4 to cure the resin holding substrate 8. Then, the inner surface of the existing mounting tube 9 is repaired.
Next, the inner film 4 is removed to complete the repair of the inner surface of the existing mounting tube 9. As a post-treatment, the outer film 5 and the resin holding base material 8 that protrude from the attachment pipe 9 to the existing main pipe 7 may be cut.
既設取付管９のライニングされた内面は、図５に示す如く、既設取付管９の内面側から、アウターフィルム５、樹脂保持基材８の裏素地２（角目状の組織）、連結糸３、表素地１（菱目状または亀甲状の組織）の補修層の構造となっている。
樹脂保持基材８の表素地１の構造は、連結糸３の層の強度を補強して、樹脂保持基材８の厚みを保持することができ構造となっているため、基材の硬化後は、強固なライニング構造とすることができる。
その補修層は、既設取付管の内面に接する側（裏素地側）が図８の如く形成され、既設取付管の中心側（表素地側）に位置するのは、図９の如く形成される。配管の中心側が図９の如く滑らかに形成されることにより、内部を流通する流体が円滑に導かれる。
As shown in FIG. 5, the inner surface of the existing mounting tube 9 lined from the inner surface side of the existing mounting tube 9 is the outer film 5, the backing substrate 2 (corner-like structure) of the resin holding substrate 8, and the connecting yarn 3. The structure of the repair layer of the surface substrate 1 (rhomboid or turtle shell-like structure) is formed.
The structure of the surface substrate 1 of the resin holding base material 8 is a structure that can reinforce the strength of the layers of the connecting yarns 3 and hold the thickness of the resin holding base material 8. Can have a strong lining structure.
The repair layer is formed as shown in FIG. 8 on the side contacting the inner surface of the existing mounting pipe (back base side) as shown in FIG. 8, and located on the center side (surface base side) of the existing mounting pipe as shown in FIG. . By smoothly forming the center side of the pipe as shown in FIG. 9, the fluid flowing inside is smoothly guided.
１ 表素地
２ 裏素地
Ｌ１〜Ｌ６ 糸
３ 連結糸
４ インナーフィルム
５ アウターフィルム
６ ボビン
７ 既設本管
８ 樹脂保持基材
９ 既設取付管
DESCRIPTION OF SYMBOLS 1 Surface base material 2 Lining base material L1-L6 Yarn 3 Connection thread 4 Inner film 5 Outer film 6 Bobbin 7 Existing main pipe 8 Resin holding base material 9 Existing installation pipe
Claims (5)
鎖編みの編目列（Ｌ４）と横振りの挿入糸（Ｌ５、Ｌ６）との角目状の組織（Ｌ４、Ｌ５、Ｌ６）である裏素地（２）と、その裏素地（２）に対向して菱目状または亀甲状の組織（Ｌ１、Ｌ２）である表素地（１）と、両素地（１、２）間を連結する連結糸（３）とにより立体構造ネットの組織を有している配管の内面補修用の樹脂保持基材。 A warp knitting of glass fiber or polyester fiber, and the fineness of the fiber is 100 TEX to 400 TEX,
A lining substrate (2) that is a square-shaped structure (L4, L5, L6) of a chain stitch stitch row (L4) and a laterally inserted insertion yarn (L5, L6), and facing the lining substrate (2) And a surface structure (1) which is a rhombus-shaped or turtle-shaped structure (L1, L2) and a connecting thread (3) which connects both the structures (1, 2), and has a three-dimensional structure net structure. Resin holding base material for internal repair of pipes.
前記繊維のコース（２．５４ｃｍ（＝１インチ）間の網目を縦方向に数えた数値）が、２．３６回／ｃｍ（＝６．０回／インチ）〜４．７２回／ｃｍ（＝１２．０回／インチ）であり、
前記繊維のウェール（２．５４ｃｍ（＝１インチ）間の網目を横方向に数えた数値） が、３．５４回／ｃｍ（＝９．０回／インチ）〜７．０８回／ｃｍ（＝１８．０回／インチ）である配管の内面補修用の樹脂保持基材。 A resin holding base material for repairing the inner surface of the pipe according to claim 1,
The fiber course (numerical value counted in the longitudinal direction of the mesh between 2.54 cm (= 1 inch) ) is from 2.36 times / cm (= 6.0 times / inch) to 4.72 times / cm (= 12.0 times / inch)
The fiber wales (numbers counted in the horizontal direction between the meshes of 2.54 cm (= 1 inch) ) are 3.54 times / cm (= 9.0 times / inch) to 7.08 times / cm (= (18.0 times / inch) A resin holding base material for repairing the inner surface of a pipe.
前記裏素地（２）と表素地（１）とを連結する連結糸（３）の構造をストレート構造とした配管の内面補修用の樹脂保持基材。 In the resin holding base material for repairing the inner surface of the pipe according to claim 1 or 2,
A resin holding base material for repairing the inner surface of a pipe, wherein the connecting yarn (3) connecting the backing substrate (2) and the front substrate (1) has a straight structure.
前記立体構造ネットの厚みが２ｍｍ〜１２ｍｍである配管の内面補修用の樹脂保持基材。 In the resin holding substrate for repairing the inner surface of the pipe according to any one of claims 1 to 3,
A resin holding base material for repairing the inner surface of a pipe whose thickness of the three-dimensional structure net is 2 mm to 12 mm.
その樹脂保持基材（８）に光硬化性または熱硬化性の樹脂材を含浸する工程と、
その樹脂保持基材（８）の前記裏素地（２）側にアウターフィルム（５）を被着し、前記表素地（１）側にインナーフィルム（４）を被着して、その表素地（１）の網目の縦方向が既設取付管（９）の軸方向と一致させる工程と、
そのインナーフィルム（４）の内部に流体を供給して、膨張させながら、その樹脂保持基材（８）の裏素地（２）側を既設取付管（９）の内面にアウターフィルム（５）を介して圧着する工程と、
次いでインナーフィルム（４）内に樹脂硬化用の補修機を挿入し、前記樹脂保持基材（８）を硬化する工程と、
を具備する配管の内面補修方法。 In the pipe inner surface repair method using the resin holding base material for inner pipe repair according to any one of claims 1 to 4,
Impregnating the resin holding substrate (8) with a photo-curable or thermosetting resin material;
An outer film (5) is attached to the back substrate (2) side of the resin holding substrate (8), an inner film (4) is attached to the front substrate (1) side, and the surface substrate ( 1) the step of causing the vertical direction of the mesh to coincide with the axial direction of the existing mounting pipe (9);
While the fluid is supplied to the inside of the inner film (4) and expanded, the back base (2) side of the resin holding substrate (8) is placed on the inner surface of the existing mounting pipe (9). Crimping via, and
Next, a step of inserting a resin curing repair machine into the inner film (4) and curing the resin holding substrate (8);
A method for repairing the inner surface of a pipe comprising: