JP6567790B1 - Comforter - Google Patents
Comforter Download PDFInfo
- Publication number
- JP6567790B1 JP6567790B1 JP2019040369A JP2019040369A JP6567790B1 JP 6567790 B1 JP6567790 B1 JP 6567790B1 JP 2019040369 A JP2019040369 A JP 2019040369A JP 2019040369 A JP2019040369 A JP 2019040369A JP 6567790 B1 JP6567790 B1 JP 6567790B1
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- comforter
- low
- present
- foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】良好に保温性、放湿性及び軽量性を発現できる掛け布団を提供する。【解決手段】袋状に形成された外側生地の内部に、シート状の中綿とシート状のポリウレタンフォームを積層する。シート状の中綿として、綿、羽毛、麻、真綿、ウール、合成繊維綿等を使用することができる。シート状のポリウレタンフォームは、袋状に形成された外側生地の肌に接する側に積層されていることが好ましく、更にシート状の低反発ウレタンを採用すれば、良好に身体にフィットさせることが可能である。【選択図】図１Disclosed is a comforter that can exhibit good heat retention, moisture release and light weight. A sheet-like batting and a sheet-like polyurethane foam are laminated inside an outer fabric formed in a bag shape. Cotton, feathers, hemp, cotton, wool, synthetic fiber cotton, etc. can be used as the sheet-like filling. The sheet-like polyurethane foam is preferably laminated on the side of the outer fabric that is formed in the shape of a bag and touches the skin. Furthermore, if a sheet-like low-resilience urethane is used, the body can fit well. It is. [Selection] Figure 1
Description
本発明は掛け布団に関する。 The present invention relates to a comforter.
掛け布団用の詰め物として、羽毛、羊毛、真綿、綿等の天然繊維素材やポリエステル綿、アクリル繊維等の合成繊維素材が使用されている。 As stuffing for comforters, natural fiber materials such as feathers, wool, cotton and cotton, and synthetic fiber materials such as polyester cotton and acrylic fibers are used.
また、掛け布団用詰め物として、ポリウレタンフォームを使用することが知られている（特許文献１）。この技術は、毛布や羽毛布団に代わる技術であり、ボリューム感を求める技術である。この技術は、保温性、放湿性及び軽量性について、改善の余地が有る。 In addition, it is known to use polyurethane foam as a quilt filling (Patent Document 1). This technology replaces blankets and duvets, and is a technology that requires a sense of volume. This technology has room for improvement in terms of heat retention, moisture release and light weight.
本発明は、従来技術に比べて、良好に保温性、放湿性及び軽量性を発現できる掛け布団を提供することを目的とする。 An object of this invention is to provide the comforter which can express heat retention, moisture release, and lightweight property compared with a prior art.
本発明者は、特定の構造を備える掛け布団が上記目的を達成できることを見出した。 The present inventor has found that a comforter having a specific structure can achieve the above object.
即ち、本発明は、下記の掛け布団である。 That is, this invention is the following comforter.
項１．
袋状に形成された外側生地の内部に、シート状の中綿とシート状のポリウレタンフォームとが積層されていることを特徴とする掛け布団。
Item 1.
A comforter characterized in that a sheet-like batting and a sheet-like polyurethane foam are laminated inside a bag-like outer fabric.
項２．
前記シート状のポリウレタンフォームは、前記袋状に形成された外側生地の肌に接する側に積層されていることを特徴とする、前記項1に記載の掛け布団。
Item 2.
Item 2. The comforter according to Item 1, wherein the sheet-like polyurethane foam is laminated on the side of the bag-like outer fabric that contacts the skin.
項３．
前記シート状のポリウレタンフォームは、低反発ウレタンシートであることを特徴とする、前記項1又は2に記載の掛け布団。
Item 3.
Item 3. The comforter according to Item 1 or 2, wherein the sheet-like polyurethane foam is a low-resilience urethane sheet.
本発明の掛け布団は、良好に保温性、放湿性及び軽量性を発現することができる。 The comforter of the present invention can exhibit good heat retention, moisture release and light weight.
以下に本発明を詳細に説明する。 The present invention is described in detail below.
本発明の掛け布団は、袋状に形成された外側生地の内部に、シート状の中綿とシート状のポリウレタンフォームとが積層されていることを特徴とする。 The comforter of the present invention is characterized in that a sheet-like batting and a sheet-like polyurethane foam are laminated inside an outer fabric formed in a bag shape.
本発明の掛け布団では、前記シート状のポリウレタンフォームは、前記袋状に形成された外側生地の肌に接する側に積層されていることが好ましい。 In the comforter of the present invention, it is preferable that the sheet-like polyurethane foam is laminated on the side of the outer fabric formed in the bag shape in contact with the skin.
本発明の掛け布団は、保温性、放湿性及び軽量性に優れる。 The comforter of the present invention is excellent in heat retention, moisture release and light weight.
（１）袋状に形成された外側生地
本発明の掛け布団は、袋状に形成された外側生地で包まれており、平面視格子状を成す格子状キルト線に沿って、生地材の表裏を縫い合わせるキルティング加工が施されていることが好ましい。本発明の掛け布団は、このキルティング加工により複数の区画が形成されることで、袋状に形成された外側生地の内部で、シート状の中綿とシート状のポリウレタンフォームとの積層構造が偏ってしまうことを防止することが可能である。
(1) Outer fabric formed in a bag shape The comforter of the present invention is wrapped in an outer fabric formed in a bag shape, and covers the front and back of the fabric material along a lattice-shaped quilt line that forms a lattice shape in plan view. It is preferable that the quilting process to sew is given. In the comforter of the present invention, a plurality of sections are formed by this quilting process, so that the laminated structure of the sheet-like batting and the sheet-like polyurethane foam is biased inside the bag-shaped outer fabric. It is possible to prevent this.
本発明の掛け布団では、キルティング加工は、例えば40cm×40cmの格子状にすることが好ましい。 In the comforter of the present invention, the quilting is preferably performed in a lattice shape of, for example, 40 cm × 40 cm.
（２）シート状の中綿
本発明の掛け布団は、シート状の中綿として、綿、羽毛、麻、真綿、ウール、合成繊維綿等を使用することができる。合成繊維綿として、公知の合成繊維綿を使用することができ、例えば、ポリエチレン綿、ポリエステル繊維綿等を好ましく使用することができる。中空繊維を使用した合成繊維綿を使用することも可能である。
(2) Sheet-like batting The comforter of the present invention can use cotton, feathers, hemp, true cotton, wool, synthetic fiber cotton, etc. as the sheet-like batting. As synthetic fiber cotton, well-known synthetic fiber cotton can be used, for example, polyethylene cotton, polyester fiber cotton, etc. can be used preferably. It is also possible to use synthetic fiber cotton using hollow fibers.
（３）シート状のポリウレタンフォーム
本発明の掛け布団は、袋状に形成された外側生地の内部に、シート状の中綿に加えて、シート状のポリウレタンフォームが積層されていることにより、保温性、放湿性及び軽量性に優れる。
(3) Sheet-like polyurethane foam The comforter of the present invention has a heat-retaining property by laminating a sheet-like polyurethane foam in addition to the sheet-like batting inside the bag-shaped outer fabric. Excellent moisture release and light weight.
本発明の掛け布団は、シート状のポリウレタンフォームとして、公知のポリウレタンフォームを使用することができる。具体的には、ポリエーテルポリオール化合物、発泡剤、整泡剤及び触媒を含むポリオール組成物とポリイソシアネート化合物とを反応させることにより製造されたポリウレタンフォームである。 In the comforter of the present invention, a known polyurethane foam can be used as the sheet-like polyurethane foam. Specifically, it is a polyurethane foam produced by reacting a polyol composition containing a polyether polyol compound, a foaming agent, a foam stabilizer and a catalyst with a polyisocyanate compound.
本発明の掛け布団は、前記シート状のポリウレタンフォームは、前記袋状に形成された外側生地の肌に接する側に積層されていることが好ましい。本発明の掛け布団は、この特徴を有することで、ウレタンの重力を利用して、良好に身体にフィットさせることが可能である。 In the comforter of the present invention, it is preferable that the sheet-like polyurethane foam is laminated on the side of the outer fabric formed in the bag shape in contact with the skin. Since the comforter of the present invention has this feature, it can fit the body satisfactorily using the gravity of urethane.
本発明の掛け布団は、シート状のポリウレタンフォームとして、シート状の低反発ウレタン（ウレタンフォーム等とも記す）を使用することが好ましい。低反発ウレタン（低反発弾性フォーム、又は低反発フォーム等とも記す）は、特殊な分子構造に設計され、「弾性」を抑え「粘性」を上げたフォームで、ヒステリシスロス率（JIS K 6400-2）)の大き
い衝撃吸収性フォームの特性を有する。低反発ウレタン（低反発弾性フォーム）は、気泡が連通し、圧縮した後に外力を取り除いた際、ゆっくりと元に戻る性質があり、一般フォームに比較して反発弾性率が15%程度以下（JIS K 6400-3)と非常に小さい特徴を有している。
The comforter of the present invention preferably uses a sheet-like low-resilience urethane (also referred to as urethane foam or the like) as a sheet-like polyurethane foam. Low resilience urethane (also referred to as low resilience foam or low resilience foam, etc.) is a foam with a special molecular structure that suppresses elasticity and increases viscosity. Hysteresis loss rate (JIS K 6400-2 )) Large shock-absorbing foam characteristics. Low resilience urethane (low resilience foam) has the property that air bubbles communicate with each other and return slowly when external force is removed after compression. Rebound resilience is about 15% or less compared to general foam (JIS K 6400-3) and very small features.
本発明の掛け布団は、シート状の低反発ウレタン（低反発弾性フォーム）を使用することで、感触が良く、局部的な圧迫が少なく、体圧が全体に分散されるので、血流阻害や床擦れ防止に効果的である。 The comforter of the present invention uses a sheet-like low-resilience urethane (low-resilience elastic foam), so it feels good, there is little local compression, and body pressure is dispersed throughout, so blood flow inhibition and floor rubbing It is effective for prevention.
先行技術文献として挙げた特許文献1の技術は、袋状に形成された外側生地の内部に、
密度が12〜25kg／m3の軟質ポリウレタンフォームを使用しており、この技術が使用するウレタンは低反発ウレタンではない。特許文献1の技術に見られる通り、一般に、軟質ウレ
タンフォームの密度は16kg/m3程度である。
The technology of Patent Document 1 cited as the prior art document is the inside of the outer fabric formed in a bag shape,
A flexible polyurethane foam having a density of 12 to 25 kg / m 3 is used, and the urethane used in this technology is not a low-resilience urethane. As seen in the technique of Patent Document 1, the density of flexible urethane foam is generally about 16 kg / m 3 .
本発明の掛け布団は、シート状のポリウレタンフォームとして、シート状の低反発ウレタン（ウレタンフォーム）を使用することが好ましい。本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、その密度は30kg/m3以上が好ましく、40kg/m3以上がより好ましい。また、その密度は60kg/m3以上であっても良い。本発明の掛
け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、その密度は、特に設ける必要は無く、例えば100kg/m3程度以下が好ましく、80kg/m3程度以下がより好ま
しい。本発明の掛け布団は、この特徴を有することで、ウレタンの重力を利用して、良好に身体にフィットさせることが可能である。
The comforter of the present invention preferably uses a sheet-like low-resilience urethane (urethane foam) as the sheet-like polyurethane foam. The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention has a density of preferably 30 kg / m 3 or more, more preferably 40 kg / m 3 or more. The density may be 60 kg / m 3 or more. Sheet Foam which quilt uses of the present invention (low impact resilience foam), the density is not necessary to particularly specify, for example, 100 kg / m 3 approximately or less, more preferably about 80 kg / m 3 . Since the comforter of the present invention has this feature, it can fit the body satisfactorily using the gravity of urethane.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、密度（ISO 845規格）は、±43kg/m3程度が好ましい。 The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention preferably has a density (ISO 845 standard) of about ± 43 kg / m 3 .
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、多孔質化したウレタンを使用することが好ましい。本発明の掛け布団は、この特徴を有することで、優れた通気性を保持することが可能である。 The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention is preferably a porous urethane. Since the comforter of the present invention has this feature, it is possible to maintain excellent air permeability.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、多孔質化したウレタンの中でも、ウレタンフォームの気泡にあるフィルム状の膜を取り除き、空気や水を通り易くした無膜ウレタンフォームであることが好ましい。通常のウレタンフォームの気泡には、フィルム状の膜が有るが、これを取り除いたものが無膜ウレタンフォームである。膜が無いことで、空気や水を通りが良い無膜ウレタンフォームとなり、通気性が高く水洗いも可能になる。 The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention is a non-porous urethane film that removes a film-like film in the foam of the urethane foam and facilitates passage of air and water. A membrane urethane foam is preferred. A normal urethane foam has a film-like film, and a film without the film is a non-film urethane foam. Due to the absence of a membrane, it becomes a non-film urethane foam that allows air and water to pass through, and is highly breathable and can be washed with water.
本発明の掛け布団は、使用する低反発ウレタン（低反発弾性フォーム）を無膜化することにより、ムレ難くなり、水洗いも可能となる。本発明の掛け布団は、無膜ウレタンフォームを使用することで、通気性が良く、通水性が良くなる。 In the comforter of the present invention, by making the low-resilience urethane (low-resilience elastic foam) to be used film-free, it becomes difficult to sag and can be washed with water. The comforter of the present invention has good breathability and good water permeability by using non-film urethane foam.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、その硬さは、20N〜100N程度が好ましく、25N〜90N程度がより好ましい。硬さ（JIS K 6400-2）は、製品から50×380×380mmの試験片を切り出して垂直方向に始めの厚さの75%まで押し込んだ後、直ちに荷重を除き、再び直ちに始めの厚さの25%まで押し込み、静止後、20
秒経過した時の荷重を読み取る。
The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention preferably has a hardness of about 20N to 100N, more preferably about 25N to 90N. The hardness (JIS K 6400-2) was determined by cutting out a 50 x 380 x 380 mm test piece from the product and pushing it vertically to 75% of the initial thickness. Push down to 25% of the
Read the load when 2 seconds have passed.
また、本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、硬さ（25%圧縮）(ISO 2439規格)は、70N程度以上が好ましい。本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、硬さ（40%圧縮）(ISO 2439規格)は、100N程度以上が好ましい。本発明の掛け布団が使用するシート状の低反発ウレ
タン（低反発弾性フォーム）は、硬さ（65%圧縮）(ISO 2439規格)は、170N程度以上が好
ましい。
Further, the sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention preferably has a hardness (25% compression) (ISO 2439 standard) of about 70 N or more. The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention preferably has a hardness (40% compression) (ISO 2439 standard) of about 100 N or more. The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention preferably has a hardness (65% compression) (ISO 2439 standard) of about 170 N or more.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、その反発弾性は、1%〜40%が好ましく、1%〜30%がより好まく、2%〜10%が更に好ましい。反
発弾性（JIS K 6400-3)は、製品から50×100×100mm以上の試験片を切り出し、試験片の
上面より500mmの高さから直径16mm、質量16gの鋼球を落下させ、跳ね返った最高の高さを落下高さ（500mm）の百分率（パーセント）で表す。
The sheet-like low resilience urethane (low resilience foam) used by the comforter of the present invention preferably has a resilience of 1% to 40%, more preferably 1% to 30%, and 2% to 10%. Further preferred. The rebound resilience (JIS K 6400-3) is the highest bounced by cutting a test piece of 50 x 100 x 100 mm or more from the product, dropping a steel ball with a diameter of 16 mm and a mass of 16 g from a height of 500 mm from the top surface of the test piece. Is expressed as a percentage of the fall height (500 mm).
また、本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、ボール試験（反発弾性）（ISO 8307規格)は、4%以上が好ましい。 The sheet-like low-rebound urethane (low-rebound resilience foam) used by the comforter of the present invention preferably has a ball test (rebound resilience) (ISO 8307 standard) of 4% or more.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、その圧縮たわみ試験（ヒステリシスロス）は、50%〜80%が好ましく、52%〜70%がより好まく、55%〜68%が更に好ましい。圧縮たわみ試験（JIS K 6400-2）は、製品から50×380×380mmの試験片を切り出して垂直方向に始めの厚さの75%まで押し込んだ後、加圧板を戻して3〜5分間放置し、再び、加圧板を始めの厚さの75%まで押し込んだ後、同じ速さで加圧板を戻して、その時の履歴をグラフにする。 The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention has a compression deflection test (hysteresis loss) of preferably 50% to 80%, more preferably 52% to 70%. 55 % To 68% is more preferable. In the compression deflection test (JIS K 6400-2), a 50 x 380 x 380 mm test piece is cut out from the product and pushed to 75% of the initial thickness in the vertical direction, and then the pressure plate is returned and left for 3 to 5 minutes. Then, after pressing the pressure plate again to 75% of the initial thickness, the pressure plate is returned at the same speed, and the history at that time is graphed.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、表面硬さ（JIS K6301A規格）は、±45-50程度が好ましい。 The sheet-like low resilience urethane (low resilience foam) used by the comforter of the present invention preferably has a surface hardness (JIS K6301A standard) of about ± 45-50.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、一般的なウレタンフォームと同様に、ポリオールとポリイソシアネ―トを主成分として発泡剤、整泡剤、触媒等を撹拌混合して発泡させることで調製できる。この低反発ウレタンには、必要に応じて着色剤や難燃剤等の添加剤が使用される。低反発弾性フォームの原料としては、ポリオールの構造等に特徴を持たせることで、圧縮後にゆっくりとした復元性を持ち、エネルギー吸収性能を高めるために粘弾性的にポリウレタン樹脂組成を変性している。この低反発ウレタン（低反発弾性フォーム）は、素材はポリウレタン樹脂を組成とした連通気泡の発泡体である。 The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention is a foam, a foam stabilizer, a catalyst and the like, which are mainly composed of polyol and polyisocyanate, as in the case of general urethane foam. It can be prepared by mixing and foaming. Additives such as colorants and flame retardants are used for the low-resilience urethane as necessary. As a raw material for low resilience foam, the polyurethane resin composition is viscoelastically modified to enhance energy absorption performance, by providing a characteristic of the structure of the polyol, etc., and having a slow recovery after compression. . This low-resilience urethane (low-resilience elastic foam) is an open-cell foam having a polyurethane resin composition.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、軽くて、衝撃吸収性、制振性、体圧分散性、吸音性、断熱性能等が良く、着色自由度が広い等の特長が発揮される。 The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention is light, has good shock absorption, vibration damping, body pressure dispersibility, sound absorption, heat insulation, etc., and has a high degree of coloring freedom. Features such as wide.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、掛け布団に使用することで、腰、尻等の体の形や動きにフィットしながら、低反発フォームの形状が変化して体圧が局部に集中せずに分散する。本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、快適・健康クッションとして有効に使用できる。 The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention changes the shape of the low-resilience foam while fitting to the shape and movement of the waist, hips, etc. And body pressure is dispersed without concentrating locally. The sheet-like low-resilience urethane (low-resilience elastic foam) used by the comforter of the present invention can be effectively used as a comfort / health cushion.
本発明の掛け布団が使用するシート状の低反発ウレタン（低反発弾性フォーム）は、復元性として、低反発弾性フォームの場合、ゆっくりと元の状態に戻る性質が有る。一方、一般的な、軟質ウレタンフォームは圧縮した後に、外力を除くと瞬時に復元する。 The sheet-like low-resilience urethane (low-resilience foam) used by the comforter of the present invention has a property of slowly returning to the original state in the case of the low-resilience foam. On the other hand, a general, flexible urethane foam is instantly restored after compressing and then removing external force.
本発明の掛け布団は、シート状のポリウレタンフォームとして、略5mm厚（厚みが5mm程度）のシートを使用することが好ましい。本発明の掛け布団は、シート状のポリウレタンフォームとして、低反発ウレタンを使用し、略5mm厚（厚みが5mm程度）のシートを使用することで、体に良好にフィットする。 The comforter of the present invention preferably uses a sheet having a thickness of about 5 mm (thickness is about 5 mm) as a sheet-like polyurethane foam. The comforter of the present invention uses a low-resilience urethane as a sheet-like polyurethane foam, and fits well to the body by using a sheet having a thickness of about 5 mm (thickness is about 5 mm).
本発明の掛け布団は、シート状のポリウレタンフォームの硬さは、例えばフォームを構成するポリウレタン重合体におけるイソシアネート化合物単位の重量比率により調整することができ、密度は発泡剤の添加量により調整することができる。 In the comforter of the present invention, the hardness of the sheet-like polyurethane foam can be adjusted by, for example, the weight ratio of isocyanate compound units in the polyurethane polymer constituting the foam, and the density can be adjusted by the amount of foaming agent added. it can.
本発明の掛け布団は、シート状の低反発ウレタン（低反発弾性フォーム）を使用することで、その密度は30kg/m3以上が好ましく、また多孔質化したウレタンを使用することと
で、ウレタンの重力を利用して、良好に身体にフィットさせることが可能であり、優れた通気性を保持することが可能である。
The comforter of the present invention uses a sheet-like low-resilience urethane (low-resilience elastic foam), and its density is preferably 30 kg / m 3 or more, and by using porous urethane, It is possible to fit the body satisfactorily using gravity, and it is possible to maintain excellent breathability.
（４）掛け布団
本発明の掛け布団は、袋状に形成された外側生地の内部に、シート状の中綿とシート状のポリウレタンフォームとが積層されている。
(4) Comforter In the comforter of the present invention, a sheet-like batting and a sheet-like polyurethane foam are laminated inside an outer fabric formed in a bag shape.
本発明の掛け布団では、シート状のポリウレタンフォームとシート状の中綿との積層は公知の方法により行うことができ、例えば糸を使用して縫い合わせる方法や、接着剤を使用してスポット的に接着する方法等を好ましく採用することができる。 In the comforter of the present invention, lamination of the sheet-like polyurethane foam and the sheet-like batting can be performed by a known method, for example, a method of sewing using a thread or a spot bonding using an adhesive. A method or the like can be preferably employed.
本発明の掛け布団では、シート状のポリウレタンフォームの厚さは、掛け布団の形状、詰め物の重量、シート状のポリウレタンフォームとシート状の中綿との重量比、ポリウレタンフォームの密度に応じて決定される。 In the comforter of the present invention, the thickness of the sheet-like polyurethane foam is determined according to the shape of the comforter, the weight of the filling, the weight ratio of the sheet-like polyurethane foam to the sheet-like padding, and the density of the polyurethane foam.
本発明の掛け布団では、シート状の中綿とシート状のポリウレタンフォームとの積層構造は2層が好ましい。また、その積層構造は、シート状の中綿／シート状のポリウレタン
フォーム／シート状の中綿、シート状のポリウレタンフォーム／シート状の中綿／シート状のポリウレタンフォーム等の3層構造やより多層の構造であっても良い。
In the comforter of the present invention, the laminated structure of the sheet-like batting and the sheet-like polyurethane foam is preferably two layers. The laminated structure is a three-layer structure such as sheet-like batting / sheet-like polyurethane foam / sheet-like batting, sheet-like polyurethane foam / sheet-like batting / sheet-like polyurethane foam, or a multilayer structure. There may be.
本発明の掛け布団では、前記シート状のポリウレタンフォームは、前記袋状に形成された外側生地の肌に接する側に積層されていることが好ましい。 In the comforter of the present invention, it is preferable that the sheet-like polyurethane foam is laminated on the side of the outer fabric formed in the bag shape in contact with the skin.
以下、実施例の掛け布団を例に本発明を説明する。 Hereinafter, the present invention will be described taking the comforter of the example as an example.
実施例の掛け布団
本発明として、袋状に形成された外側生地の内部に、シート状の中綿とシート状のポリウレタンフォームとが積層し、本発明の掛け布団を作製した。
As an embodiment of the present invention, a sheet-like batting and a sheet-like polyurethane foam are laminated inside a bag-like outer fabric to produce the comforter of the present invention.
参考例として、市販品のアクリル毛布を使用した。 As a reference example, a commercially available acrylic blanket was used.
本発明の掛け布団及び市販品のアクリル毛布について、（1）保温性試験、（2）寝床内シミュレーション、及び（3）耐洗濯性試験を行い、掛け布団の性能を評価した。 The comforter of the present invention and the commercially available acrylic blanket were subjected to (1) heat retention test, (2) in-bed simulation, and (3) washing resistance test to evaluate the comforter performance.
（1）保温性試験（サーマルマネキン法）
前処理
20℃65%RHの環境室に、本発明の掛け布団及び市販品のアクリル毛布の各試料を一晩リ
ラックスさせた。
(1) Thermal insulation test (thermal mannequin method)
Preprocessing
Each sample of the comforter of the present invention and a commercial acrylic blanket was relaxed overnight in an environmental room at 20 ° C. and 65% RH.
試験方法
＜１＞20℃65%RHに設置された木製ベッドの上に敷き布団及び枕をセットし、36℃に制
御したサーマルマネキン（インテック株式会社製）を仰向けに寝かせた。＜２＞サーマルマネキンの上に、本発明の掛け布団及び市販品のアクリル毛布の各試料を自然に掛けた。＜３＞約2時間後から3回連続して測定して平均値を出した。
Test Method <1> A futon and a pillow were set on a wooden bed set at 20 ° C. and 65% RH, and a thermal manikin (manufactured by Intec Corporation) controlled at 36 ° C. was laid on its back. <2> Each sample of the comforter of the present invention and a commercially available acrylic blanket was naturally hung on the thermal mannequin. <3> About 3 hours after about 2 hours, the average value was obtained.
使用寝具
枕、敷き布団(中綿ポリエステル100%、3.1kg)
測定時間
1回1時間を3回連続測定
試験結果
表1の数値は、1以上が良く、温かみが有ることを表す。
Use bedding pillow, mattress (100% batting polyester, 3.1 kg)
Measurement time
3 times a time for 1 hour
The numerical value in the test result table 1 should be 1 or more, indicating that it is warm.
表1の結果より、本発明の掛け布団（重量：1.6kg）は、市販品のアクリル毛布（重量：2.5kg）に比べて、軽量であるにもかかわらず、より温かみを感じる（保温性に優れる）
掛け布団であることを評価できた。
From the results in Table 1, the comforter of the present invention (weight: 1.6 kg) feels warmer (excellent in heat retention), although it is lighter than the commercially available acrylic blanket (weight: 2.5 kg). )
We were able to evaluate that it was a comforter.
（2）寝床内シミュレーション（寝床内湿度変化）
試験方法
＜１＞36℃に低温制御したサーモラボ熱板に、約150%湿潤状態のろ紙を置き、スペーサー（厚さ5mm）を設置した。＜２＞安定後、本発明の掛け布団及び市販品のアクリル毛布
の各試料を設置すると同時に寝床内湿度を経時的に測定した。
(2) In-bed simulation (change in humidity in bed)
Test Method <1> A filter paper in a wet state of about 150% was placed on a thermolab hot plate controlled at a low temperature of 36 ° C., and a spacer (thickness 5 mm) was installed. <2> After stabilization, each sample of the comforter of the present invention and a commercially available acrylic blanket was installed, and simultaneously the humidity in the bed was measured over time.
測定環境
20℃40%RH
熱板温度及び熱板サイズ
36℃、10cm×10cm
試験結果
Measurement environment
20 ℃ 40% RH
Hot plate temperature and hot plate size
36 ℃, 10cm × 10cm
Test results
表2及び図2の結果より、本発明の掛け布団は、市販品のアクリル毛布に比べて、最大湿度差時の湿度が低く、良好な放湿性を示す掛け布団であることを評価できた。 From the results shown in Table 2 and FIG. 2, it was possible to evaluate that the comforter of the present invention is a comforter having a low humidity at the time of maximum humidity difference and exhibiting good moisture-releasing properties compared to a commercially available acrylic blanket.
（3）耐洗濯性試験
本発明の掛け布団（ウレタン入りケット）について、JIS-L-1930 C4M吊干に従って、耐洗濯性を評価した。
(3) Washing resistance test Washing resistance of the comforter (urethane-containing ket) according to the present invention was evaluated according to JIS-L-1930 C4M suspension.
試験結果Test results
表3の結果より、本発明の掛け布団は、良好な耐洗濯性を示す掛け布団であることを評
価できた。本発明の掛け布団は、シート状のポリウレタンフォームは劣化せず、通常の毛布と同様に洗濯することが可能である。
From the results shown in Table 3, it can be evaluated that the comforter of the present invention is a comforter having good washing resistance. The comforter of the present invention does not deteriorate the sheet-like polyurethane foam and can be washed in the same manner as a normal blanket.
本発明の掛け布団は、袋状に形成された外側生地の内部に、シート状の中綿とシート状のポリウレタンフォームとが積層されていることで、良好に保温性、放湿性及び軽量性を発現することができる。本発明の掛け布団は、保温性が有るので熱を保持する性能を有し、放湿性が有るので蒸し蒸ししない掛け布団である。本発明の掛け布団は、特に、シート状のポリウレタンフォームを含むことで、体に良好にフィットする。 The comforter of the present invention has good heat retention, moisture release and lightness by laminating a sheet-like batting and a sheet-like polyurethane foam inside a bag-like outer fabric. be able to. The comforter of the present invention is a comforter that has heat retention because it has heat retention and does not steam due to its moisture release. The comforter of the present invention includes a sheet-like polyurethane foam and fits well to the body.
Claims (2)
前記シート状のポリウレタンフォームは、低反発ウレタンシートである、
ことを特徴とする掛け布団。 Inside the outer fabric formed in a bag shape, a sheet-like batting and a sheet-like polyurethane foam are laminated ,
The sheet-like polyurethane foam is a low-resilience urethane sheet,
A comforter characterized by that.