JP6554210B1 - Rugs and bats - Google Patents
Rugs and bats Download PDFInfo
- Publication number
- JP6554210B1 JP6554210B1 JP2018104147A JP2018104147A JP6554210B1 JP 6554210 B1 JP6554210 B1 JP 6554210B1 JP 2018104147 A JP2018104147 A JP 2018104147A JP 2018104147 A JP2018104147 A JP 2018104147A JP 6554210 B1 JP6554210 B1 JP 6554210B1
- Authority
- JP
- Japan
- Prior art keywords
- wool
- tourmaline
- weight
- skin
- intermediate layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】ムートンの品質低下を防止し、かつムートンを利用したトルマリン効果を最大限に発揮できる敷物及び蒲団を提供する。【解決手段】ムートン体12は、羊毛12A1が密集した羊毛部12Aと、羊毛12A1が一度も切り離されない皮12B1で構成された皮部12Bと、を有し、中間層16に、Al2O3、TiO3、BaO、BaTiO2の1種類又は2種類以上からなる焼結粉粒体とトルマリンの粉粒体とが、焼結粉粒体と前記トルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%となるように混入され、皮12B1から一度も切り離されないことに伴う羊毛12A1の表面に形成された微細な隙間の開閉作用を利用して、トルマリンからのマイナスイオンを羊毛12A1の隙間から大気中に放出させる。【選択図】 図1[Problem] To provide a rug and a straw mat which can prevent the deterioration of the quality of a mouton and can maximize the tourmaline effect using the mouton. A mouton body 12 has a wool part 12A in which wool 12A1 is dense and a skin part 12B composed of a skin 12B1 in which the wool 12A1 is never cut, and an intermediate layer 16 has Al2O3 and TiO3. , BaO, BaTiO2 sintered powder particles consisting of one or more types and tourmaline powder particles, the blending ratio of the sintered powder particles and the tourmaline is 60 to 40 weight sintered powder particles. %: Tourmaline negative ions from tourmaline using the opening and closing action of fine gaps formed on the surface of the wool 12A1 that are mixed so as to be 40-60% by weight and never cut off from the skin 12B1 Are released into the atmosphere from the gap between the wool 12A1. [Selection] Figure 1
Description
本発明は、ムートン(羊又は子羊の毛皮)とトルマリンを含んだ敷物及び蒲団に関する。 The present invention relates to rugs and bats comprising mutton (fleece or lamb fur) and tourmaline.
従来からムートンを用いた敷物が知られている。一例として、特許文献1には、羊毛が密集した羊毛部と、羊毛部が密着固定された羊毛固定部と、を有するムートン体と、流体が通過可能な大きさの開口部を有するネット又はメッシュ生地と、を備えるムートンを用いた敷物が開示されている。 Conventionally, rugs using moutons are known. As an example, Patent Document 1 discloses a net or mesh having an opening having a size through which fluid can pass, and a muton body having a wool part densely packed with wool and a wool fixing part to which the wool part is closely fixed. A rug using a mutton comprising a fabric is disclosed.
上記発明は、天然又は人工のムートンからなる敷物を使って就寝するときに、安眠・リラックス効果が得られるように、温熱板やマイナスイオン発生シートや備長炭シートやゲルマニウムシート等の健康補助器材を天然又は人工のムートンの敷物の下に配置して天然又は人工のムートンと併用したいという要望があることの着眼点に基づき、皮部の裏面側にマイナスイオン発生機能を持った粉体を塗布することによって、毛皮にマイナスイオン発生機能を付与した場合の課題を解決するものである。 The above invention uses health aids such as thermal plates, negative ion generation sheets, bincho charcoal sheets, germanium sheets, etc. so that sleep and relaxation effects can be obtained when going to bed using natural or artificial rugons. Apply powder with function to generate negative ions on the back side of skin based on the point of view that there is a demand to be placed under the cover of natural or artificial mutton and to be used together with natural or artificial mutton It solves the problem in the case of giving a negative ion generating function to the fur.
具体的には、課題は、天然ムートンの皮部や人工ムートンの裏地層等は通気性を有していないために、熱やマイナスイオン等の健康補助成分を含んだ流体が皮部や裏地層等を通過して羊毛側(表面側)に流出することが遮断される。天然又は人工のムートンでは、皮部や裏地層等の流体遮蔽効果によって、皮部や裏地層等というムートンの裏面側で発生したマイナスイオンをムートンの表面側に運ぶことができないために、所望の健康補助効果を得ることができない。 Specifically, the problem is that the skin of natural mutons and the lining layer of artificial mutons do not have breathability, so fluids containing health aids such as heat and anions are the skin and lining layers Flow out to the wool side (surface side) through the In natural or artificial Moutons, the fluid shielding effect of skins and lining layers can not carry negative ions generated on the back side of the skins, such as skins and lining layers, to the surface side of the Moutons. Cannot get health benefits.
ムートンは羊毛が密集したフサフサとした羊毛部を備えていることを特徴とするものであるので、ムートンに小さな通気穴を設けたくらいでは、ムートンのフサフサとした羊毛部によって通気穴が覆い隠される。そのために、小さな通気穴で十分な通気性を確保することは困難である。 Mouton is characterized by having a fuzzy wool part where wool is densely packed. Therefore, if a small vent hole is provided in the mouton, the vent hole is covered by the fuzzy wool part of the mouton. . Therefore, it is difficult to ensure sufficient ventilation with small vent holes.
そこで、上記特許文献1に記載された発明によれば、流体が通過可能な通り道(path)がネット又はメッシュ生地によって明確に確保されているので、ネット又はメッシュ生地の開口部を通じて流体が通過することができる。 Therefore, according to the invention described in Patent Document 1, since a path through which fluid can pass is clearly secured by the net or mesh fabric, the fluid passes through the opening of the net or mesh fabric. be able to.
したがって、ネット又はメッシュ生地の開口部を介して、ムートン体の裏面側に配置された健康補助器材からのオゾン、熱、マイナスイオンあるいは水分等の健康補助成分を含んだ有益な流体が流通することができるので、敷物の高機能化を図ることができる。
しかしながら、上記特許文献1に記載された発明によれば、流体が通過可能な通り道(path)がネット又はメッシュの部位が形成されているため、かかる部位の形成工程が必要になるとともに、敷物自体の強度が低下する問題がある。 However, according to the invention described in the above-mentioned patent document 1, since a path through which fluid can pass is a net or mesh site, the process of forming such site is required, and the rug itself There is a problem that the strength of the material is lowered.
また、ネット又はメッシュ生地の開口部を通じて流体が通過するため、開口部以外の部位では効果的に放出されず、流体による効果が半減する問題がある。 In addition, since the fluid passes through the opening of the net or mesh fabric, there is a problem that the effect by the fluid is halved because the fluid is not effectively released at a portion other than the opening.
詳細には、特許文献1によれば、特開2000−17300号公報を先行技術文献として紹介し、かかる先行技術文献に対して、特許文献1の段落(0007)に『しかしながら、天然ムートンの皮部や人工ムートンの裏地層等は、通気性を有していないために、熱やマイナスイオン等の健康補助成分を含んだ流体が皮部や裏地層等を通過して羊毛側(表面側)に流出することが遮断されてしまう。したがって、天然又は人工のムートンでは、皮部や裏地層等の流体遮蔽効果によって、皮部や裏地層等というムートンの裏面側で発生したマイナスイオンをムートンの表面側に運ぶことができないために、所望の健康補助効果を得ることができないという問題がある。』という問題乃至課題を指摘したうえで、特許文献1に記載された発明の『したがって、本発明の解決すべき技術的課題は、流体が通過可能な、ムートンを用いた敷物を提供することであり、さらに、天然ムートンの皮部や人工ムートンの裏地層の側に配置された健康補助器材からのオゾン、熱、マイナスイオンあるいは水分等の健康補助成分を含んだ有益な流体がムートンの羊毛側に提供されることによって高機能化が図られる、ムートンを用いた敷物を提供することである(引用文献1の段落(0008))。』に至り、特許文献1に記載された発明が完成している。 In detail, according to Patent Document 1, Japanese Patent Laid-Open No. 2000-17300 is introduced as a prior art document, and in the paragraph (0007) of Patent Document 1, “However, the skin of natural mouton” Since the back layer of the artificial muon or the like has no air permeability, the fluid containing health aid components such as heat and negative ions passes through the skin and the back layer, etc. and is on the wool side (surface side) It will be blocked from flowing out. Therefore, with natural or artificial Moutons, negative ions generated on the back side of the skin such as skins and lining layers can not be transported to the surface side of the Moutons by the fluid shielding effect of the skins and lining layers, etc. There is a problem that the desired health support effect can not be obtained. After pointing out the problem or the problem, “the technical problem to be solved by the present invention of the invention described in Patent Document 1 is to provide a rug using a mouton through which a fluid can pass. There is also a useful fluid containing health aids such as ozone, heat, negative ions or moisture from health aids placed on the side of natural mutton skin or artificial mutton lining layer, the wool side of the mutton It is an object of the present invention to provide a rug using a rug which can be enhanced in functionality by being provided to the above (paragraph (0008) of reference 1). The invention described in Patent Document 1 is completed.
かかる特許文献1の発明に至る過程を参酌すれば、開口部がない場合にはマイナスイオン効果(有益な流体)がムートン体の羊毛側に流動しないことが従来の問題点としてあげられており、それに対して開口部を積極的に設けるように発明されているため、特許文献1では『開口部を有すること』が発明の必須となる特徴的技術(本質的部分ないし発明の前提)を意味するものである。 If the process leading to the invention of Patent Document 1 is taken into consideration, the conventional problem is that the negative ion effect (beneficial fluid) does not flow to the wool side of the Muton body when there is no opening, On the other hand, in the patent document 1, "having an opening" means an essential characteristic technique (essential part or premise of the invention) of the invention since it is invented to provide the opening positively. It is a thing.
よって、特許文献1に発明された発明では、開口部位の形成工程が必須になるとともに、開口部を形成する分だけ敷物自体の強度が低下する問題を避けることができず、致命的な問題となる。 Therefore, in the invention invented in Patent Document 1, the formation process of the opening portion is essential, and the problem that the strength of the rug itself is reduced by the amount of forming the opening cannot be avoided, and this is a fatal problem. Become.
特許文献2及び特許文献3には、マイナスイオン発生による効果が高い繊維シートが開示されているが、かかる繊維シートを内在させた敷物では、敷物内部にマイナスイオンが留まり、敷物の表面から外部への発散効果が制限される。
そこで、本発明においては、上記の様々な課題を解決し、ムートンの品質低下を防止し、かつムートンの拡散効果を利用したトルマリンによるマイナスイオン効果を最大限に発揮できる敷物及び蒲団を提供することを目的とする。 Therefore, in the present invention, it is an object of the present invention to solve the various problems described above, to prevent the deterioration of the Mouton, and to provide a rug and a carpet capable of maximizing the negative ion effect by the tourmaline utilizing the diffusion effect of the Mouton. With the goal.
第1の発明は、開口部を有さないムートン体と、ベース材と、前記ムートン体と前記ベース材との間に介在された中間層と、が積層され、縁部において縫製により各層間が密着固定されて形成される敷物であって、前記ムートン体は、羊毛が密集した羊毛部と、前記羊毛が一度も切り離されない皮で構成された皮部と、を有し、前記中間層に、Al2O3、TiO3、BaO、BaTiO2の1種類又は2種類以上からなる焼結粉粒体とトルマリンの粉粒体とが、前記焼結粉粒体と前記トルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%となるように混入され、前記皮から一度も切り離されないことに伴う前記羊毛の表面に形成された微細な隙間の開閉作用を利用して、前記トルマリンからのマイナスイオンを前記羊毛の前記隙間から大気中に放出させることを特徴とする。
In the first invention, a Muton body having no opening, a base material, and an intermediate layer interposed between the Muton body and the base material are laminated, and each layer is sewn at the edge by sewing. The mouton body has a wool part in which wool is dense and a skin part composed of a skin from which the wool is never separated, and is formed in the intermediate layer. , Al 2 O 3 , TiO 3 , BaO, BaTiO 2 , sintered powder particles consisting of two or more types and tourmaline powder particles, the mixing ratio of the sintered powder particles and the tourmaline is , Sintered
第2の発明は、開口部を有さないムートン体と、ベース材と、前記ムートン体と前記ベース材との間に介在された中間層と、が積層され、縁部において縫製により各層間が密着固定されて形成される蒲団であって、前記ムートン体は、羊毛が密集した羊毛部と、前記羊毛が一度も切り離されない皮で構成された皮部と、を有し、前記中間層に、Al2O3、TiO3、BaO、BaTiO2の1種類又は2種類以上からなる焼結粉粒体とトルマリンの粉粒体とが、前記焼結粉粒体と前記トルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%となるように混入され、前記皮から一度も切り離されないことに伴う前記羊毛の表面に形成された微細な隙間の開閉作用を利用して、前記トルマリンからのマイナスイオンを前記羊毛の前記隙間から大気中に放出させることを特徴とする。
In the second invention, a Muton body not having an opening, a base material, and an intermediate layer interposed between the Muton body and the base material are laminated, and the respective layers are sewn at the edge by sewing. A mushroom formed by being closely fixed , the mouton body having a wool part in which wool is dense and a skin part composed of a skin from which the wool is never separated, and in the intermediate layer , Al 2 O 3 , TiO 3 , BaO, BaTiO 2 , sintered powder particles consisting of two or more types and tourmaline powder particles, the mixing ratio of the sintered powder particles and the tourmaline is , Sintered
第3の発明は、開口部を有さないムートン体と、ベース材と、前記ムートン体と前記ベース材との間に介在された中間層と、が積層され、縁部において縫製により各層間が密着固定されて形成される敷物であって、前記ムートン体は、羊毛が密集した羊毛部と、前記羊毛が一度も切り離されない皮で構成された皮部と、を有し、前記中間層は、Al2O3、TiO3、及びBaOを主成分とする焼結粉粒体とトルマリンの粉粒体とを含有するレーヨン繊維と、綿糸との混紡糸からなり、前記焼結粉粒体と前記トルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%であり、混紡糸の配合比率が、レーヨン繊維20〜40重量%;綿糸80〜60重量%であり、前記皮から一度も切り離されないことに伴う前記羊毛の表面に形成された微細な隙間の開閉作用を利用して、前記トルマリンからのマイナスイオンを前記羊毛の前記隙間から大気中に放出させることを特徴とする。 A third invention is a Mouton having no opening, and the base member, and an intermediate layer interposed between the Mouton body and the base material, are stacked, the respective layers by sewing at the edge The mouton body has a wool part in which wool is dense and a skin part composed of a skin from which the wool is never separated, and the intermediate layer is a rug formed by being closely fixed. , Comprising a blended yarn of rayon fiber containing a sintered powder body mainly composed of Al 2 O 3 , TiO 3 , and BaO and a tourmaline powder body, and cotton yarn, and the sintered powder body, The compounding ratio with the tourmaline is 60 to 40% by weight of sintered powder particles; 40 to 60% by weight of tourmaline; the compounding ratio of mixed spinning is 20 to 40% by weight of rayon fiber; 80 to 60% by weight of cotton yarn Yes, with no separation from the skin By utilizing the opening and closing action of the minute gaps formed on the surface of serial wool, characterized in that to release into the atmosphere of negative ions from the tourmaline from the gap of the wool.
第4の発明は、開口部を有さないムートン体と、ベース材と、前記ムートン体と前記ベース材との間に介在された中間層と、が積層され、縁部において縫製により各層間が密着固定されて形成される蒲団であって、前記ムートン体は、羊毛が密集した羊毛部と、前記羊毛が一度も切り離されない皮で構成された皮部と、を有し、前記中間層は、Al2O3、TiO3、及びBaOを主成分とする焼結粉粒体とトルマリンの粉粒体とを含有するレーヨン繊維と、綿糸との混紡糸からなり、前記焼結粉粒体と前記トルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%であり、混紡糸の配合比率が、レーヨン繊維20〜40重量%;綿糸80〜60重量%であり、前記皮から一度も切り離されないことに伴う前記羊毛の表面に形成された微細な隙間の開閉作用を利用して、前記トルマリンからのマイナスイオンを前記羊毛の前記隙間から大気中に放出させることを特徴とする。 According to a fourth aspect of the present invention, a mouton body having no opening, a base material, and an intermediate layer interposed between the mouton body and the base material are laminated, and each layer is sewn by sewing at an edge. A mushroom formed by being closely fixed , wherein the mouton body has a wool part in which wool is dense and a skin part composed of a skin from which the wool is never separated, and the intermediate layer is , Comprising a blended yarn of rayon fiber containing a sintered powder body mainly composed of Al 2 O 3 , TiO 3 , and BaO and a tourmaline powder body, and cotton yarn, and the sintered powder body, The compounding ratio with the tourmaline is 60 to 40% by weight of sintered powder particles; 40 to 60% by weight of tourmaline; the compounding ratio of mixed spinning is 20 to 40% by weight of rayon fiber; 80 to 60% by weight of cotton yarn Yes, with no separation from the skin By utilizing the opening and closing action of the minute gaps formed on the surface of serial wool, characterized in that to release into the atmosphere of negative ions from the tourmaline from the gap of the wool.
第1の発明によれば、ムートン体を身体の敷物とすることにより、ムートン体の吸湿性により身体からの汗(水分)が羊毛から吸収される。羊毛から吸収された汗(水分)は羊毛の内部で保持される。そして、羊毛の微細な隙間の開閉作用により羊毛内の水分が外部へ適宜放出される。これにより、ムートン体の羊毛の表面に形成された微細な隙間の開閉作用に伴う吸湿・発散作用を利用して、ムートン体の羊毛に蓄積された湿度が一定に維持され、ムートン体の清潔性及び耐久性が向上する。 According to the first aspect of the invention, by making the mutton body a covering of the body, sweat (water) from the body is absorbed from the wool by the hygroscopicity of the mutton body. Sweat (moisture) absorbed from the wool is retained inside the wool. Then, the moisture in the wool is appropriately released to the outside by the opening and closing action of the fine gaps of the wool. As a result, the moisture accumulated in the wool of the mutton body is maintained at a constant level by utilizing the hygroscopic and emanating actions associated with the opening and closing action of the fine gap formed on the surface of the mutton wool, and the cleanliness of the mutton body is maintained. And durability is improved.
なお、ムートン体では羊毛と皮とが一度も切り離されずに一体となって取得される。これにより、羊毛の微細な隙間の開閉作用が生じる。そして、後述するように、羊毛の微細な隙間の開閉作用により内部のマイナスイオン等が敷物の外部へ放出され、マイナスイオン等の放射効果が著しく高くなる。本明細書では、「ムートン体では羊毛と皮とが一度も切り離されずに一体となって取得される結果、羊毛の微細な隙間の開閉作用」を説明の便宜上、『羊毛の呼吸』と表現する。 In the case of the mutton body, wool and skin are obtained as one without being separated. Thereby, the opening and closing action of the minute gap of the wool occurs. Then, as described later, the internal negative ions and the like are discharged to the outside of the rug by the opening and closing action of the fine gaps of the wool, and the radiation effect of the negative ions and the like becomes extremely high. In the present specification, “the wool and the skin are obtained as one unit without being separated in the mutton body, and hence the opening and closing action of the fine gaps of the wool” is expressed as “respiration of the wool” for convenience of explanation. .
また、羊毛が弾性力を有するらせん状構造を有しているため、使用者の身体の重さを羊毛で均等に支持することができ、身体に対する負担が軽減する。また、羊毛のラノリン効果により人肌に良い影響(美容効果)を与えることができる。 In addition, since the wool has a helical structure having elasticity, the weight of the user's body can be evenly supported by the wool and the burden on the body is reduced. In addition, the lanolin effect of wool can have a positive effect (cosmetic effect) on human skin.
ムートン体と、ベース材と、トルマリンを含んだ中間層と、が積層されて一体に形成されているため、トルマリンから放出されたマイナスイオンは敷物の内部に保持されるため、敷物の内部におけるマイナスイオンの濃度が高くなる。羊毛の放湿性を利用して、羊毛を介して高濃度のマイナスイオンを効率良く、外部へ放出させることができる。 Since the Muton body, the base material, and the intermediate layer containing tourmaline are laminated and integrally formed, the negative ions released from the tourmaline are retained inside the rug, so the minus inside the rug The concentration of ions increases. By using the moisture releasing property of wool, high concentration negative ions can be efficiently released to the outside through the wool.
ここで、発明者らは、トルマリンからのマイナスイオンの発生をより効果的にするため、以下のように考えた。すなわち、敷物の中間層に、アルミニウム、チタン、バリウム系化合物の1種類又は2種類以上からなる焼結粉粒体と、トルマリンの粉粒体とを混入している。 Here, in order to make generation of the negative ion from tourmaline more effective, the inventors considered as follows. That is, in the intermediate layer of the rug, sintered powder particles consisting of one or more kinds of aluminum, titanium and barium compounds and powder particles of tourmaline are mixed.
上記焼結粉粒体とトルマリン粉粒体との混合体は、トルマリン単体の場合に比べ誘電率が大となって、高い電気的刺激効果が得られる。特に、熱や圧力を加えることにより、分極現象が高められる。よって、上記混合体を混入した敷物は、人体と接触・使用されることにより、誘電率が大となって、人体への電気的刺激効果が高められる。 The mixture of the sintered powder particles and the tourmaline powder particles has a large dielectric constant as compared with the case of tourmaline alone, and a high electrical stimulation effect is obtained. In particular, the polarization phenomenon is enhanced by applying heat or pressure. Therefore, the carpet mixed with the above mixture has a high dielectric constant by being in contact with and used by the human body, and the electrical stimulation effect on the human body is enhanced.
また、上記焼結粉粒体は、人体が吸収し易い波長領域における赤外線のエネルギー放射率が高いので、血行が良くなって良好な保温効果が得られる。 Moreover, since the sintered powder particles have high infrared energy emissivity in a wavelength region that is easily absorbed by the human body, blood circulation is improved and a good heat retaining effect is obtained.
さらに、上記焼結粉粒体は、人体の活性化に有効なマイナスイオンを発生するので、身体全体の電気の流れが良好となって回復に寄与する。 Furthermore, since the sintered powder particles generate negative ions effective for activating the human body, the flow of electricity in the entire body is improved and contributes to recovery.
しかも、上記焼結粉粒体とトルマリン粉粒体との混合体は、消臭作用があり、特にアンモニア系成分に対して優れた消臭効果を発揮し、また抗菌作用も有している。 In addition, a mixture of the above-mentioned sintered powder and tourmaline powder has a deodorizing action, in particular, exerts an excellent deodorizing effect on ammonia-based components, and also has an antibacterial action.
このとき、トルマリンおよび焼結粉粒体としては、粒径0.2〜20μm程度のものが好適に使用される。この粒径のものは、原料中に混入して繊維の紡糸が容易に行える。また、上記粒径のものは、トルマリンと焼結粉粒体が具有する上記各作用を効果的に発揮する。これらトルマリンおよび焼結粉粒体の粉砕化は、湿式または乾式など周知の方法で任意に行うことができる。 At this time, as the tourmaline and the sintered powder particles, those having a particle diameter of about 0.2 to 20 μm are suitably used. Those having this particle size can be easily mixed in the raw material and fiber spinning. Moreover, the said particle size thing exhibits the said each effect which tourmaline and a sintered powder body have. Pulverization of these tourmaline and sintered powder particles can be optionally performed by a known method such as wet or dry.
そして、以上のような混合体を中綿の繊維に混入することにより、健康保持又は健康増進効果が得られ、病院や一般家庭等で使用する敷物として最適となる。特に、上記混合体を混入したことにより敷物の全体が重量感に富むものとなって、使用時に身体に密着し、最適なものとなる。 And, by mixing the above-mentioned mixture into the fiber of batt, health maintenance or health promotion effect can be obtained, and it becomes optimum as a rug used in a hospital or general household. In particular, by mixing the above mixture, the entire rug becomes rich in weight, and is in close contact with the body during use, which is optimal.
なお、中間層として、アルミニウム、チタン、バリウム系化合物の1種類又は2種類以上からなる焼結粉粒体と、トルマリンの粉粒体とが混入された繊維からなる放射層を不織布などのシートを設け、このシートを布帛内に介入させてもよい。 In addition, as an intermediate layer, a sheet of a nonwoven fabric or the like is used as a radiation layer made of fibers mixed with sintered powder particles made of one or more of aluminum, titanium and barium compounds and tourmaline powder particles. It may be provided and this sheet intervenes in the fabric.
このような敷物によっても、シートに設けた放射層により、上記と同様な作用効果が得られる。また、この場合、既成の敷物内にシートを組み込むことにより、健康保持又は健康増進効果に優れた敷物に容易に変えられる。さらに、布帛と中綿となる羽毛との間にシートを介入させることにより、羽毛独特の感触を損なうことなく、健康保持又は健康増進効果に優れた敷物とすることができる。つまり、第1発明のように焼結粉粒体とトルマリン粉粒体の混合体が混入された繊維を用い、これを羽毛間に介入させると、上記したような混合体による作用効果は得られるが、使用者が違和感をいだくおそれがある。 With such a covering, the same effects as those described above can be obtained by the radiation layer provided on the sheet. Also, in this case, by incorporating the sheet in the existing rug, it can be easily converted into a rug excellent in health maintenance or health promotion effect. Furthermore, by interposing a sheet between the fabric and the feathers used as the batting, it is possible to obtain a rug excellent in health maintenance or health promotion effect without impairing the unique feel of feathers. That is, when using a fiber in which a mixture of sintered powder and tourmaline powder is mixed as in the first invention and intervening between the feathers, the effect of the mixture as described above can be obtained. However, the user may feel uncomfortable.
上記各発明で用いる焼結粉粒体は、Al2O3、TiO3、BaO、BaTiO2の1種類又は2種類以上とすることが好ましい。このような焼結粉粒体よれば、電気的刺激効果や赤外線効果が高められ、またマイナスイオンの発生率も高められて、健康保持又は健康増進効果に優れた敷物が得られる。 The sintered granular material used in each of the above inventions is preferably one or more of Al 2 O 3 , TiO 3 , BaO, and BaTiO 2 . According to such a sintered powder, the electrical stimulation effect and the infrared effect are enhanced, and the generation rate of negative ions is also enhanced, and a covering excellent in health maintenance or health promotion effect can be obtained.
また、上記混合体の配合比率は、焼結粉粒体60〜40重量%;トルマリン40〜60重量%とすることが好ましい。このような配合比率とすれば、焼結粉粒体のトルマリンによる分極現象つまり誘電率が高められる。仮に、上記範囲を逸脱すると、十分な電気的刺激効果が得られず、また赤外線効果やマイナスイオンの発生効果も十分には得られず、健康保持又は健康増進用の敷物として最適な使用が行えなくなる。また、上記混合体は、繊維を紡糸し得る範囲で繊維中に自由に配合することができるが、繊維を容易に紡糸し、かつ繊維中の混合体の量を出来るだけ増大させて、所期の目的を十分に達成するためには、繊維に対する混合体の添加比率を、5〜15重量%程度とすることが好ましい。本願発明は、中間層には不織布からなる薄いシートが介装され、該シートの一面若しくは両面に、Al2O3、TiO3、BaO、BaTiO2の1種類又は2種類以上からなる焼結粉粒体とトルマリンの粉粒体とが、焼結粉粒体とトルマリンとの配合比率を、焼結粉粒体60〜40重量%;トルマリン40〜60重量%として混入された繊維からなる格子状開口を持つシート状の放射層が接合一体化されて設けられていることを特徴とする敷物である。
Moreover, it is preferable that the mixture ratio of the said mixture shall be sintered
第2の発明の蒲団についても、第1の発明の敷物と同様の作用効果を得る。 Also in the group of the second invention, the same function and effect as the rug of the first invention are obtained.
第3の発明によれば、ムートン体と、ベース材と、トルマリンを含んだ中間層と、が積層されて一体に形成されているため、トルマリンから放出されたマイナスイオンは敷物の内部に保持されるため、敷物の内部におけるマイナスイオンの濃度が高くなる。羊毛の放湿性を利用して、羊毛を介して高濃度のマイナスイオンを効率良く、外部へ放出させることができる。 According to the third invention, since the Muton body, the base material, and the intermediate layer containing tourmaline are laminated and integrally formed, the negative ions released from the tourmaline are held inside the rug. Therefore, the negative ion concentration in the interior of the rug increases. By using the moisture releasing property of wool, high concentration negative ions can be efficiently released to the outside through the wool.
特に、中間層は、Al2O3、TiO3、及びBaOを主成分とする焼結粉粒体とトルマリンの粉粒体とを含有するレーヨン繊維と、綿糸との混紡糸からなり、焼結粉粒体とトルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%であり、混紡糸の配合比率が、レーヨン繊維20〜40重量%;綿糸80〜60重量%である敷物である。 In particular, the intermediate layer is made of a blended yarn of rayon fibers containing sintered powder particles mainly composed of Al 2 O 3 , TiO 3 , and BaO and tourmaline particles, and cotton yarn, and sintered. The blending ratio of the powder and the tourmaline is 60 to 40% by weight of the sintered powder; 40 to 60% by weight of the tourmaline, and the blending ratio of mixed spinning is 20 to 40% by weight of rayon fiber; It is a rug which is% by weight.
上記焼結粉粒体は、Al2O3、TiO3、及びBaOの3種類を主成分とすることが好ましい。このような焼結粉粒体によれば、電気的刺激効果や遠赤外線効果が高められ、またマイナスイオンの発生率も高められて、十分な治癒効果が得られる。 It said sintered powder particle body, Al 2 O 3, TiO 3 , and it is preferable that a main component three BaO. According to such a sintered powder particle, the electrical stimulation effect and the far infrared effect are enhanced, and the generation rate of negative ions is also enhanced, so that a sufficient healing effect can be obtained.
上記混合体の配合比率は、焼結粉粒体60〜40重量%;トルマリン40〜60重量%とすることが好ましい。このような配合比率とすれば、焼結粉粒体のトルマリンによる分極現象つまり誘電率が高められる。仮に、上記範囲を逸脱すると、十分な電気的刺激効果が得られず、また遠赤外線効果やマイナスイオンの発生効果も十分には得られず、毛布や敷物又はサポータなどとして最適な使用が行えなくなる。また、上記混合体は、繊維を紡糸し得る範囲で自由に配合することができるが、繊維を容易に紡糸し、かつ繊維中のトルマリンおよび焼結粉粒体の量を出来るだけ増大させて、所期の目的を十分に達成するためには、繊維に対する混合体の添加比率を、5〜15重量%程度とすることが好ましい。 It is preferable that the compounding ratio of the said mixture sets to 60 to 40 weight% of sinter powder particles; and 40 to 60 weight% of tourmaline. With such a blending ratio, the polarization phenomenon of the sintered powder particles by tourmaline, that is, the dielectric constant can be enhanced. If it deviates from the above range, sufficient electrical stimulation effect can not be obtained, and far infrared effect and negative ion generation effect can not be sufficiently obtained, and the optimum use as a blanket, a cover or a supporter can not be performed. . Further, the above mixture can be freely blended within a range in which the fiber can be spun, but the fiber is easily spun and the amount of tourmaline and sintered powder in the fiber is increased as much as possible. In order to sufficiently achieve the intended purpose, the addition ratio of the mixture to the fibers is preferably about 5 to 15% by weight.
第3の発明は、Al2O3、TiO3、及びBaOの3種類を主成分とする焼結粉粒体とトルマリンの粉粒体を混入した繊維と、綿糸との混紡糸から形成している。 A third invention is formed from a blended yarn of a cotton yarn and a fiber mixed with sintered powder particles mainly composed of Al 2 O 3 , TiO 3 , and BaO, and tourmaline powder particles. There is.
以上のような混紡糸で敷物を作ることにより、上記の優れた効果が得られながら、敷物全体の肌ざわり感が良好となって、最適なものとなる。 By making the rug by mixed spinning as described above, while the above-mentioned excellent effects are obtained, the texture of the entire rug becomes good and becomes optimum.
なお、より最適なものとするためには、混紡糸の配合比率を、焼結粉粒体とトルマリンの混入繊維20〜40重量%;綿糸80〜60重量%とする。このとき、混入繊維の配合比率を20重量%以下とし、綿糸の配合比率を80重量%以上にすると、肌ざわり感は良好となるものの、トルマリンと焼結粉粒体を添加したことによる所期の目的が得られ難くなる。一方、混入繊維の配合比率を40重量%以上とし、綿糸の配合比率を60重量%以下にすると、トルマリンと焼結粉粒体による効果は向上するものの、肌ざわり感が悪くなってしまう。 In addition, in order to make it more optimal, the compounding ratio of mixed spinning is made into 20 to 40 weight% of mixed powder of sinter powder and tourmaline, and 80 to 60 weight% of cotton yarn. At this time, if the blending ratio of the mixed fiber is 20% by weight or less and the blending ratio of the cotton yarn is 80% by weight or more, the feeling of feeling on the skin becomes good, but the expected due to the addition of tourmaline and sintered powder particles. It becomes difficult to obtain the purpose. On the other hand, when the mixing ratio of the mixed fiber is 40% by weight or more and the mixing ratio of the cotton yarn is 60% by weight or less, although the effects of tourmaline and sintered powder particles are improved, the feeling of rough skin is deteriorated.
第4の発明の蒲団についても、第3の発明の敷物と同様の作用効果を得る。 Also in the group of the fourth invention, the same function and effect as the rug of the third invention are obtained.
以下、本発明の一実施形態に係る敷物について、図面を参照しつつ詳細に説明する。なお、敷物として、「トルマリン素材含有敷物」を一例にあげて、説明する。 Hereinafter, a rug according to an embodiment of the present invention will be described in detail with reference to the drawings. In addition, as a rug, "a tourmaline material-containing rug" is mentioned as an example, and is demonstrated.
本発明の「敷物」とは、座布団、シート、カバー、足ふきなどとして、身体の一部に敷くもの、又は身体にかけるものの用途で用いる意味である。 "Rug" of the present invention is used as a cushion, a sheet, a cover, a foot towel, etc. in the application of what is put on a part of the body, or what is put on the body.
本発明は、蒲団の用途で用いることもできる。蒲団の説明については、用途が異なるだけの敷物と同じになるため、省略する。 The present invention can also be used in brigade applications. The explanation of the band is omitted because it is the same as the rug that has a different purpose.
[1.トルマリン素材含有敷物の全体構成]
図1に示すように、本発明のトルマリン素材含有敷物10は、ムートン体12と、ベース材14と、ムートン体12とベース材14との間に介在されトルマリン素材16A1を含んだ中間層16と、が積層されるとともに周囲の縁部付近における縫製等により、例えば一体に形成されている。なお、中間層16は、ベース材14と同じ材質又は異なる材質のもので一体的に形成されていてもよい。
[1. Overall configuration of tourmaline material-containing rug]
As shown in FIG. 1, a tourmaline material-containing
換言すれば、トルマリン素材含有敷物10は、ムートン体12とベース材14と中間層16の3層が縫製により縫い部18で一体に形成されている。
In other words, in the tourmaline material-containing
ムートン体12は、天然のものであり、複数本の羊毛12A1が密集した羊毛部12Aと、羊毛12A1が一度も切り離されない皮12B1で構成された皮部12Bと、を有している。このため、本発明のムートン体12は、羊毛12A1と皮12B1とが一度分離された後、相互に縫い合わされて人工的に形成されたムートン体とは明確に異なり、羊毛12A1と皮12B1との境界の細胞が分断されず、天然のままで維持される。
The
なお、ムートン体12は、特許文献1に示すような開口部を有しておらず、連続的かつ一体的なものとなる。
In addition, the
羊毛12A1と皮12B1は、両者を切り離さずに羊又は子羊から取得したものである。ゆえに羊毛12A1と皮12B1との間は分断されておらず、細胞が連続したものとなっている。これは羊毛12A1の毛根がいわゆる生きた状態と表現することもでき、羊毛12A1のいわゆる呼吸が維持されているともいえる。 The wool 12A1 and the skin 12B1 are obtained from sheep or lambs without separating them. Therefore, the area between wool 12A1 and skin 12B1 is not divided, and the cells are continuous. This can also be expressed as a so-called live state of the hair roots of the wool 12A1, and it can be said that the so-called breathing of the wool 12A1 is maintained.
換言すれば、羊毛12A1の表面には微細な隙間が複数形成されている。毛根がいわゆる生きた状態であるからこそ、羊毛12A1の微細な隙間の開閉作用が維持される。これにより、大気中の水分が羊毛12A1に吸湿され、または羊毛12A1の内部の水分が大気中に放出される。なお、羊毛12A1の微細な隙間の開閉作用の詳細については後述する。 In other words, a plurality of fine gaps are formed on the surface of the wool 12A1. Because the hair roots are in a so-called live state, the opening and closing action of the fine gaps of the wool 12A1 is maintained. Thereby, moisture in the atmosphere is absorbed by the wool 12A1, or moisture inside the wool 12A1 is released into the atmosphere. The details of the opening and closing action of the minute gap of the wool 12A1 will be described later.
ベース材14は、シート状に形成された裏地であり、ポリビニル、ポリアミド、ポリエステルなどの素材、あるいはそれらの混合素材等、既知の合成樹脂素材や天然素材を使用することができる。
The
中間層16は、トルマリン素材16A1を含んでいる。詳細には、中間層16は、トルマリン素材16A1を含むトルマリンシート16Aが綿16B1で構成された綿シート16Bに縫製され、縫い部18において一体に形成されている。
The
ここで、トルマリン素材16A1が綿シート16B上に平面視にてほぼ均一に分布するように配置されている。綿シート16B上にトルマリン素材16A1を敷き詰めた層である。
Here, the tourmaline material 16A1 is arranged on the
トルマリン素材16A1は、各種の素材を採用することができるが、好ましい一例としては、トルマリン鉱石を混在させた繊維状または薄幕状の素材からなるものである。 Although various materials can be adopted as the tourmaline material 16A1, as a preferable example, it is made of a fibrous or thin film-like material mixed with tourmaline ore.
なお、図2に示すように、トルマリン素材含有敷物10は、所定の寸法に形成された方形状のものであるが、複数のトルマリン素材含有敷物10をマジックテープ(登録商標)等の連結手段で連結させて大きさを調整することができる。このため、トルマリン素材含有敷物10は、座布団、寝具としての蒲団、敷布団、足マットなど様々な用途に利用することができる。
In addition, as shown in FIG. 2, although the tourmaline material-containing
トルマリン素材16A1は、縫い部18を基準として内面側に位置していることが好ましい。これにより、トルマリン素材16A1から発生したマイナスイオンが縫い部18を基準として内側(内部側)に充満する。この結果、トルマリン素材含有敷物10の内部に充満されたマイナスイオンの濃度が高くなり、高濃度のマイナスイオンが羊毛12A1の微細な隙間から大気中へ放出され、マイナスイオン効果が高くなる。
It is preferable that the tourmaline material 16A1 be positioned on the inner side with respect to the sewn
また、トルマリン素材16A1は、羊毛12A1の毛根(図示省略)の近傍、詳細には羊毛12A1の毛根の鉛直下方側に配置されていることが好ましい。これにより、トルマリン素材16A1から発生したマイナスイオンが羊毛12A1の毛根に浸入し易くなり、この結果、羊毛12A1の表面の微細な隙間から大気中に拡散され易くなる。 Further, it is preferable that the tourmaline material 16A1 is disposed in the vicinity of the hair root (not shown) of the wool 12A1, specifically, vertically below the hair root of the wool 12A1. As a result, negative ions generated from the tourmaline material 16A1 easily enter the hair roots of the wool 12A1, and as a result, they are easily diffused into the air from the fine gaps on the surface of the wool 12A1.
[2.トルマリン素材含有敷物の作用効果]
次に、本発明の敷物の一実施形態に係るトルマリン素材含有敷物10の作用について説明する。
[2. Effects of tourmaline material-containing rugs]
Next, the operation of the tourmaline material-containing
図1に示すように、トルマリン素材含有敷物10を利用することにより、使用者は、ムートンによる効果が得られる。すなわち、ムートン体12の吸湿性と放湿性により肌触りの良い感覚を使用者に与えることができる。使用者の身体から出た汗(水分)は、ムートン体12の羊毛12A1から吸湿される。これにより、使用者は、爽やかな使用感が得られる。
As shown in FIG. 1, by using the tourmaline material-containing
羊毛12A1から吸収された汗(水分)は、羊毛12A1の微細な隙間の開閉作用により、複数の隙間を通して、適宜、羊毛12A1(の内部)から大気中に放出される。このため、羊毛12A1内の湿度が一定に維持され、耐久性が向上する。このように、羊毛12A1の吸湿性と放湿性により、トルマリン素材含有敷物10の使用時における心地良さと耐久性が向上する。また、トルマリン素材含有敷物10の肌触りが良くなり、清潔性が増す。
The sweat (moisture) absorbed from the wool 12A1 is released from (the inside of) the wool 12A1 into the atmosphere as appropriate through the openings of the fine gaps of the wool 12A1. For this reason, the humidity in the wool 12A1 is kept constant, and the durability is improved. Thus, the comfort and durability at the time of use of the tourmaline material-containing
また、羊毛12A1がらせん状に巻回されているため、使用者の身体がバランス良く均等に支持される。これにより、使用者の身体に対する負担が軽減され、使用感が高くなる。また、羊毛12A1のラノリン効果により人肌に良い影響を与えることができる。 Further, since the wool 12A1 is spirally wound, the user's body is supported in a balanced and equal manner. This reduces the burden on the user's body and enhances the feeling of use. Further, the human skin can be positively affected by the lanolin effect of the wool 12A1.
さらに、トルマリン素材含有敷物10は、トルマリン素材16A1から発生するマイナスイオン効果を使用者に与えることができる。ここで、ムートン体12の羊毛12A1は皮12B1と切離さずに一体となっている。このため、大気の湿度に応じて、羊毛12A1の表面上にある隣接したキューティクル間から微細な隙間が開き、羊毛12A1内に保持された水分が大気中に放出され、または大気中の水分が羊毛12A1の内部に浸入する。この羊毛12A1の呼吸現象により、羊毛12A1の吸湿性と放湿性が機能にして羊毛12A1内の湿度が一定に維持される。
Furthermore, the tourmaline material-containing
[2−1.羊毛の表面状態]
詳細には、図4に示すように、羊毛12A1は、我々の皮膚やツメと同じように蛋白質の細胞からできており、1本の繊維の断面を拡大すれば、表皮部と、皮質部(コルテックス)から成り立っている。羊毛12A1の表皮部は、屋根瓦のようにウロコ状に重なり合っている。このウロコをスケールといい、スケールは規則正しく毛先の方向に突出している。
[2-1. Surface condition of wool]
In detail, as shown in FIG. 4, the wool 12A1 is made of protein cells like our skin and claws. When the cross section of one fiber is enlarged, the epidermis and cortex ( Cortex)). The skin of wool 12A1 overlaps with each other like a roof tile. This scale is called a scale, and the scale regularly protrudes in the direction of the hair tips.
図4の右側は、皮膚などから発生する汗(水分)にウールが反応してスケールが開いた状態である。外部の湿度に応じて、スケールが自在に開閉し、外部の湿気を吸収したり、又は内部の湿気を放出することができる。このように、スケールの開閉動作を羊毛12A1の呼吸といい、これは血流が動力源となって発生しているものではなく、羊毛12A1と皮12B1を一度も切断・分離させたことがない状態において奏されるスケールの開閉動作に基づくものである。 The right side of FIG. 4 shows a state in which the scale is opened by the reaction of the wool with sweat (moisture) generated from the skin or the like. Depending on the external humidity, the scale can freely open and close to absorb the external moisture or release the internal moisture. Thus, the opening and closing movement of the scale is called respiration of the wool 12A1, which is not generated by the blood flow as a power source, and the wool 12A1 and the skin 12B1 have never been cut and separated once This is based on the scale opening / closing operation performed in the state.
[2−2.羊毛表面の詳細構造]
図5に示すように、1本の羊毛(ウール)12A1を拡大すれば、異なる細胞から成る2種類の領域(AコルテックスとBコルテックス)を張り合わせたような構造になっており、双方の性質の違いが、ウールの縮れと弾力性を生んでいる。
[2-2. Detailed structure of wool surface]
As shown in FIG. 5, when one wool (wool) 12A1 is enlarged, it has a structure in which two types of regions (A cortex and B cortex) composed of different cells are bonded together. The difference in properties gives rise to the shrinkage and elasticity of wool.
[2−3.羊毛表面の微細な隙間の開閉原理]
図6に示すように、羊毛12A1の場合、スケール間に微細な隙間があり、血流の有無ではなく、外部の湿度等の環境条件に応じてスケールが反応することで微細な隙間が開閉する。これにより、表皮部では、湿気は微細な隙間を通過して内部に浸入することができるが、水滴は微細な隙間から浸入することはできず、弾かれる。これも羊毛12A1の性質である。
[2-3. Principle of opening and closing fine gaps on the surface of wool
As shown in FIG. 6, in the case of wool 12A1, there is a fine gap between the scales, and the fine gap opens and closes when the scale reacts according to environmental conditions such as external humidity, not the presence or absence of blood flow. . Thus, in the skin portion, moisture can pass through the fine gap and infiltrate into the inside, but the water droplet can not penetrate from the fine gap and is repelled. This is also the nature of wool 12A1.
[2−4.特有の効果]
図1、図4、図5及び図6に示すように、トルマリン素材16A1から発生したマイナスイオンは、羊毛12A1の微細な隙間の開閉動作に伴って、羊毛12A1の表面の微細な隙間から大気中に放出される。すなわち、トルマリン素材16A1から発生したマイナスイオンは、各羊毛12A1の隙間の開閉作用に合わせて、羊毛12A1の内部から大気中へ放出される。
[2-4. Specific effects]
As shown in FIG. 1, FIG. 4, FIG. 5 and FIG. 6, the negative ions generated from the tourmaline material 16A1 are released into the atmosphere from the minute gaps on the surface of the wool 12A1 as the minute gaps of the wool 12A1 are opened and closed. Released into That is, negative ions generated from the tourmaline material 16A1 are released from the inside of the wool 12A1 to the atmosphere in accordance with the opening and closing action of the gaps of the wool 12A1.
特に、羊毛12A1が複数本存在し、各羊毛12A1には複数の微細な隙間が自在に開閉するため、各羊毛12A1の隙間の開閉作用によりマイナスイオンの高い拡散効果が実現される。 In particular, since a plurality of wools 12A1 exist and a plurality of fine gaps freely open and close in each wool 12A1, a high diffusion effect of negative ions is realized by the opening and closing action of the gaps in each wool 12A1.
ここで、使用者がトルマリン素材含有敷物10を敷いている場合には、羊毛12A1が使用者の身体に絡みついて接触又は密着し、その接触面積が大きくなる。マイナスイオンは、羊毛12A1と身体との接触を介してより効率的に身体の内部に取り込まれるため、使用者により多くのマイナスイオンを供給することができる。
Here, when the user lays the tourmaline material-containing
これに対して、例えば特開2008−295850号公報に記載された発明では、羊毛ではなく、開口部を有するネット又はメッシュ生地からマイナスイオンが放出されることを意図しているため、使用者の身体が羊毛で支持された構成では、ネット又はメッシュ生地の部位が身体には接触しない。このため、マイナスイオンがネット又はメッシュ生地から大気中に放出されてしまう問題がある。 On the other hand, for example, in the invention described in Japanese Patent Application Laid-Open No. 2008-295850, it is intended that negative ions are released not from wool but from a net or mesh fabric having an opening. In the configuration where the body is supported by wool, portions of the net or mesh fabric do not touch the body. Therefore, there is a problem that negative ions are released from the net or mesh fabric to the atmosphere.
マイナスイオンが大気中に放出され大気中のマイナスイオンが身体に及ぼす影響と、羊毛と身体とが接触して羊毛から身体にマイナスイオンが直接供給される影響と、を比較すれば、後者の身体に対するマイナスイオンの吸収率が格段に高くなる。本願は、羊毛12A1の微細な隙間の開閉作用を利用してマイナスイオンが放出される構成を採ることで、使用者がトルマリン素材含有敷物10を敷いている場合には、身体に対するマイナスイオンの吸収率を高める格別の効果がある。
Comparing the effects of negative ions released into the atmosphere and negative ions in the atmosphere on the body and the effects of direct contact of wool with the body and negative ions supplied from the wool to the body, the latter's body The rate of absorption of negative ions to In the present application, negative ions are released by utilizing the opening and closing action of the fine gaps of the wool 12A1, so that when the user lays the tourmaline material-containing
また、例えば特開2008−295850号公報に記載された発明のように、布等によるマイナスイオンの遮断を阻止しマイナスイオンを放出し易くするという目的のために、開口部を有するネット又はメッシュ生地を設けた構成では、耐久性が低下するばかりか、敷物内部に充満するマイナスイオンがネット又はメッシュ生地から大気中に逃げてしまい、敷物内部におけるマイナスイオンの濃度が低下する問題がある。 Also, as in the invention described in, for example, Japanese Patent Application Laid-Open No. 2008-295850, a net or mesh fabric having an opening for the purpose of blocking the blocking of negative ions by cloth or the like and facilitating the release of negative ions. Not only does the durability decrease, but also the negative ions filling the interior of the rug escape from the net or mesh fabric to the atmosphere, resulting in a problem that the concentration of negative ions in the interior of the rug decreases.
これに対して、本願は、ムートン体12とベース材14と中間層16とが積層され縫製により一体的に形成されているため、中間層16に含まれているトルマリン素材16A1から発生したマイナスイオンが各層12、14、16と縫い部18により形成された領域に閉じ込められる。このため、トルマリン素材含有敷物10の内部のマイナスイオン濃度が極大化する。そして、高濃度のマイナスイオンは、羊毛12A1の微細な隙間の開閉動作を介して羊毛12A1の内部から外部に放出される。このため、羊毛12A1と使用者の身体が接触していれば、羊毛12A1から高濃度のマイナスイオンが使用者の身体内に効率良く取り込まれるため、マイナスイオン効果が極めて高くなる。
On the other hand, in the present application, since the
また、トルマリン素材含有敷物10の中間層16は、トルマリン素材16A1を含んだトルマリンシート16Aが綿シート16Bに縫い部18により固定されて構成されているため、トルマリンシート16Aが綿シート16Bに対して位置ずれしない。このため、トルマリン素材16A1が綿シート16B上に平面視にて均一に分布された状態が維持され、マイナスイオンの放出むらを防止できる。
In addition, the
また、トルマリン素材含有敷物10の平面視における縁部には縫い部18により各層間において密着固定されているため、トルマリン素材16A1から発生したマイナスイオンは、トルマリン素材含有敷物10の各積層面から外部に漏えいし難い。換言すれば、トルマリン素材含有敷物10の内部には、マイナスイオンが高濃度で充満している。このマイナスイオンは、羊毛12A1の毛根から羊毛12A1の内部に浸入し、羊毛12A1の微細な隙間の開閉作用に伴って羊毛12A1の表面の微細な隙間から放出されるため、マイナスイオンの放出量が極大化する。
In addition, since the sealing portions of the tourmaline material-containing
特に、羊毛12A1は複数本の束になっているため、各羊毛12A1から大気中にマイナスイオンが放出されると、マイナスイオンの拡散効果が得られ、トルマリン素材含有敷物10の使用者に対して大量のマイナスイオンが供給される。 In particular, since the wool 12A1 is a bundle of a plurality of strands, when negative ions are released from the wool 12A1 to the atmosphere, the diffusion effect of the negative ions is obtained, and for the user of the tourmaline material-containing rug 10 A large amount of negative ions are supplied.
ここで、羊毛12A1内に水分が保持されている場合には、マイナスイオンが水分と共に羊毛12A1から大気中に放出される。これにより、適度な湿度の環境下において、ミスト効果とマイナスイオン効果が得られ、爽快感と美容効果が実現される。 Here, when moisture is held in the wool 12A1, negative ions are released from the wool 12A1 together with moisture into the atmosphere. As a result, in an environment of appropriate humidity, a mist effect and a negative ion effect can be obtained, and a refreshing sensation and a beauty effect can be realized.
特に、羊毛12A1から吸収された使用者の汗がトルマリン素材16A1と反応してヒドロキシルイオンというマイナスイオンが生成され、このマイナスイオンが使用者の皮膚や呼吸によって体内に吸収される。また、人体の皮膚の中でも特に誘電性の高い「ツボ」の部分から血液などの体液に吸収される。これにより、マイナスイオン効果が高くなる。 In particular, the user's sweat absorbed from the wool 12A1 reacts with the tourmaline material 16A1 to form a negative ion called hydroxyl ion, and this negative ion is absorbed into the body by the skin of the user and by respiration. In addition, it is absorbed into body fluid such as blood from the portion of the "bar" which is particularly high in the skin of the human body. This increases the negative ion effect.
また、皮12B1を通してもマイナスイオンが放出され、羊毛12A1からのマイナスイオンの拡散効果と相まってマイナスイオンの供給量が大幅に増大する。これによっても、マイナスイオン効果が高くなる。 In addition, negative ions are also released through the skin 12B1, and the supply amount of negative ions is significantly increased in combination with the diffusion effect of the negative ions from the wool 12A1. This also increases the negative ion effect.
また、トルマリン素材16A1は、独特な結晶構造から乾電池のようにプラスとマイナスの電極を持ち、微弱電流が発生する。この電流は、0.06ミリアンペアであり、人体に流れている生体電流と同じである。これにより、使用者の身体の細胞を活性化させることができる。 In addition, the tourmaline material 16A1 has positive and negative electrodes like a dry cell because of its unique crystal structure, and a weak current is generated. This current is 0.06 milliamps, which is the same as the biocurrent flowing in the human body. Thereby, the cell of a user's body can be activated.
トルマリン素材16A1から6ミクロン〜14ミクロンの波長の遠赤外線が放出される。これにより、使用者の身体を深部から暖めることができる。 Far infrared rays having a wavelength of 6 microns to 14 microns are emitted from the tourmaline material 16A1. Thereby, a user's body can be warmed from the deep part.
さらに、トルマリン素材含有敷物10の製造方法によれば、羊毛12A1の呼吸を利用してトルマリン素材16A1からのマイナスイオンを羊毛12A1の表面の微細な隙間から大気中に放出させるように、ムートン体12と中間層16とベース材14とが積層されて縫製により一体に形成されるため、マイナスイオンの放出効果を向上させつつ、トルマリン素材含有敷物10を容易に製造できる。
Furthermore, according to the method of manufacturing the tourmaline material-containing
詳細には、ムートン体12とトルマリン素材16A1を含んだ中間層16とベース材14とが積層されて縫製により一体に形成されることにより、トルマリン素材16A1がムートン体12の下面側に位置し、固定される。これにより、羊毛12A1の毛根の近傍にトルマリン素材16A1が位置するため、トルマリン素材16A1から発生したマイナスイオンが羊毛12A1の毛根から羊毛12A1の内部に浸入し、羊毛12A1の微細な隙間の開閉作用により、水分とともに大気中に放出・拡散される。このように、トルマリン素材含有敷物10を容易に製造できるとともに、マイナスイオンの拡散効果を高めることができる。
In detail, the
[3.トルマリン素材含有敷物の積層構造の変形例]
次に、本発明の一実施形態に係るトルマリン素材含有敷物の積層構造の変形例について説明する。なお、上記実施形態のトルマリン素材含有敷物と重複する構成には同符号を付し、その説明を適宜省略する。
[3. Modification of laminated structure of tourmaline-containing rug]
Next, a modification of the laminated structure of the tourmaline material-containing covering according to the embodiment of the present invention will be described. In addition, the same code | symbol is attached | subjected to the structure which overlaps with the tourmaline material containing rug of the said embodiment, and the description is abbreviate | omitted suitably.
図3に示すように、変形例に係るトルマリン素材含有敷物10は、ムートン体12の皮部12Bの下面に、ラジウムシート20と、トルマリンシート16Aと、ウレタン層22と、固わた層24と、ベース材14とが順に積層された構成である。
As shown in FIG. 3, the tourmaline material-containing
なお、トルマリン素材含有敷物10の各層は、縫製により縫い部18において一体に形成されている。
The layers of the tourmaline material-containing
本発明の「中間材」は、変形例において、ラジウムシート20と、トルマリンシート16Aと、ウレタン層22と、固わた層24と、を含めた概念である。
The “intermediate material” of the present invention is a concept including, in a modification, a
変形例のトルマリン素材含有敷物10においても、各層が縫製により一体に形成されている。
Also in the tourmaline material-containing
変形例によれば、トルマリン素材含有敷物10にラジウムシート20が含まれているため、ラジウムシート20から放出される微量放射線が身体に細胞の活性化に機能し若返り効果、あるいは所謂ホルミシス効果が得られる。
According to the modification, since the
[4.トルマリン素材含有敷物の中間層の変形例]
次に、本発明の一実施形態に係るトルマリン素材含有敷物の中間層の変形例について説明する。なお、上記実施形態のトルマリン素材含有敷物と重複する構成には同符号を付し、その説明を適宜省略する。
[4. Modification of intermediate layer of rugs containing tourmaline material]
Next, the modification of the middle class of the tourmaline material content covering concerning one embodiment of the present invention is explained. In addition, the same numerals are given to the structure which overlaps with the tourmaline material content covering of the above-mentioned embodiment, and the explanation is omitted suitably.
[4−1.トルマリン素材含有敷物の中間層の第1変形例]
中間層16として、例えば繊維径1.5〜6.0デニールで繊維長38〜60mmのポリエステル繊維を用いる。そして、上記中間層16を、下記する各実施例のようにして作る。なお、中間層16の周囲を布帛(図示省略)により包み込んでいる。
[4-1. First modification of intermediate layer of tourmaline material-containing rug]
As the
実施例1;トルマリン(粒径5μm)の40重量%と、BaTiO2を主成分とする焼結粉粒体(粒径5μm)の60重量%とからなる混合体を、原料中に5重量%混入してポリエステル繊維を紡糸し、これにより、上記中間層16を作った。
Example 1 5% by weight of a mixture of 40% by weight of tourmaline (
実施例2;トルマリン(粒径15μm)の50重量%と、Al2O3、TiO3、BaOを主成分とする焼結粉粒体(粒径15μm)の50重量%とからなる混合体を、原料中に15重量%混入してポリエステル繊維を紡糸し、これにより、上記中間層16を作った。
Example 2: A mixture comprising 50% by weight of tourmaline (
実施例3;トルマリン(粒径8μm)の60重量%と、BaTiO2を主成分とする焼結粉粒体(粒径8μm)の40重量%とからなる混合体を、原料中に10重量%混入してポリエステル繊維を紡糸し、これにより、上記中間層16を作った。
Example 3 10% by weight of a mixture comprising 60% by weight of tourmaline (
なお、上記実施例1〜3においては、トルマリンとして、ショール(Schorl)を用いた。 In Examples 1 to 3, a shawl was used as tourmaline.
次に、上記実施例1〜3で使用した混合体の作用効果を調べるため、この混合体とその比較例であるトルマリン単体について、それぞれ誘電率、誘電正接、放射率(全エネルギーと全放射率)、赤外線放射量を測定した。その結果は、図7に示す。なお、図7は、実施例2の混合体を使用したときのデータである。また、実施例1、3の混合体を使用する場合も、図7とほぼ同一の作用効果が得られる。 Next, in order to investigate the function and effect of the mixture used in the above Examples 1 to 3, the dielectric constant, the dielectric loss tangent, and the emissivity (total energy and total emissivity, respectively, for this mixture and the tourmaline alone as a comparative example thereof ), The amount of infrared radiation was measured. The result is shown in FIG. FIG. 7 shows data when the mixture of Example 2 is used. In addition, when the mixture of Examples 1 and 3 is used, substantially the same operational effects as in FIG. 7 can be obtained.
図7に示すように、本発明で用いる混合体は、トルマリン単体に比べて、誘電率と誘電正接及び赤外線放射量の何れもが優れている。また、放射率については、混合体とトルマリン単体との差は殆どないが、後述するように、放射の発生領域が異なり、混合体の場合は、人体が吸収し易い領域で放射量が多くなる。 As shown in FIG. 7, the mixture used in the present invention is superior in all of dielectric constant, dielectric loss tangent and infrared radiation amount as compared with tourmaline alone. As for emissivity, there is almost no difference between the mixture and tourmaline alone, but as described later, the radiation generation region is different, and in the case of a mixture, the amount of radiation increases in a region that is easily absorbed by the human body. .
ここで、誘電率と誘電正接についての測定試験は、混合体とトルマリン単体を20mmφ、2mm厚に圧縮成形して試験片として用いた。また、試験は、インピーダンス/ゲイン・フェイズアナライザー4194A(HEWLEFTT PAKARD社製)を用い、電極外径20mmφ、測定周波数1MHZ、試験温湿度23℃、50%RHで行った。 Here, in the measurement test for the dielectric constant and the dielectric loss tangent, the mixture and the tourmaline alone were compression-molded to a thickness of 20 mm and a thickness of 2 mm and used as a test piece. The test was conducted using an impedance / gain phase analyzer 4194A (manufactured by HEWLEFTT PAKARD) at an electrode outer diameter of 20 mmφ, a measurement frequency of 1 MHZ, and a test temperature and humidity of 23 ° C. and 50% RH.
エネルギーの放射率についての測定試験は、混合体とトルマリン単体を20mmφ、2mm厚に圧縮成形して試験片として用いた。また、試験は、IFS−113V(Bruker社製 FT−1R)を用い、波長領域2〜100μ、試験温度40℃で行った。なお、図7の放射率の項目には、理想黒体のデータも示している。 In the measurement test for the emissivity of energy, the mixture and tourmaline alone were compression-molded to a thickness of 20 mm and a thickness of 2 mm and used as a test piece. The test was conducted using IFS-113V (FT-1R manufactured by Bruker) at a wavelength range of 2 to 100 μ and a test temperature of 40 ° C. The item of emissivity in FIG. 7 also shows data of an ideal black body.
赤外線放射量(ファブリック)についての試験は、混合体とトルマリン単体を50×50mmの両面テープに接合して試験片として用いた。また、試験は、サーモグラフィー(NEC三栄社製)を用い、与熱時間15分、温度36℃、検出波長8〜13μ、試験温湿度23℃、50%RHで行った。 In the test for the amount of infrared radiation (fabric), the mixture and tourmaline alone were bonded to a 50 × 50 mm double-sided tape and used as a test piece. The test was conducted using thermography (manufactured by NEC San-ei Co., Ltd.) with a heating time of 15 minutes, a temperature of 36 ° C., a detection wavelength of 8 to 13 μ, and a test temperature and humidity of 23 ° C. and 50% RH.
図8は、縦軸にRelative emissivity(放射率、%)を、横軸にWavelength(波長、μm)をとった上記混合体の放射率スペクトルを示している。また、図9は、比較例としてトルマリン単体の放射率スペクトルを示している。これらの各図から明らかなように、人体が吸収し易い7〜12μm領域での放射率スペクトルが高い。 FIG. 8 shows the emissivity spectrum of the above mixture, where the vertical axis represents relative emission (emissivity,%) and the horizontal axis represents Wavelength (wavelength, μm). Further, FIG. 9 shows an emissivity spectrum of tourmaline alone as a comparative example. As apparent from each of these figures, the emissivity spectrum in the 7 to 12 μm region where the human body is likely to absorb is high.
図10は、縦軸にWatt×m-2×μm-1(熱エネルギー)を、横軸にWavelength(波長、μm)をとった上記混合体と理想黒体の発光エネルギー分布を示している。また、図11は、比較例としてトルマリン単体と理想黒体の発光エネルギー分布を示している。これらの各図から明らかなように、人体が吸収し易い7〜12μm領域において、発光エネルギー分布の曲線が理想黒体の曲線に近づき、上記領域での発生エネルギー量が多い。 FIG. 10 shows emission energy distributions of the above mixture and the ideal black body, in which the ordinate is Watt × m −2 × μm −1 (heat energy) and the abscissa is Wavelength (wavelength, μm). Further, FIG. 11 shows the light emission energy distribution of the tourmaline alone and the ideal black body as a comparative example. As is apparent from these figures, in the 7 to 12 μm region where the human body easily absorbs, the curve of the light emission energy distribution approaches the curve of the ideal black body, and the amount of generated energy in the above region is large.
以上のことから、上記各実施例による中間層16を使用した場合、その内部に混入したアルミニウム、チタン、バリウム系化合物を主成分とする焼結粉粒体とトルマリン粉粒体との混合体により、人体が吸収し易い波長領域でのエネルギー放射率が高い赤外線特性を具有していることが理解できる。つまり、波長7〜12μmの領域において、約30〜36Watt×m-2×μm-1のエネルギーを放射する赤外線特性を具有する。よって、上記中間層16を用いた敷物10とすることにより、血行が良くなって良好な保温効果が得られる。
From the above, when the
また、上記中間層16は、誘電率及び誘電正接が大きいので、高い電気的刺激効果が得られる。特に、敷物10を使用するとき、これが人体により加温されたり、又は圧力が加えられると、誘電率がさらに高められるので、人体への電気的刺激効果がより高められる。
Further, since the
さらに、上記混合体はマイナスイオンを発生するので、これが混入された中間層16ひいては敷物10を使用することにより、身体全体の電気の流れが良好となって人体の活性化に有効となる。しかも、上記混合体は、アンモニア系成分に対して優れた消臭効果を発揮し、また抗菌作用も有しているので、これが混入された中間層16ひいては敷物10は、家庭だけではなく、病院などで看護用として使用するものとして最適となる。
Furthermore, since the mixture generates negative ions, the use of the
中間層16とその表面を覆う布帛との間に例えば綿、レーヨン、アセテート、ナイロン、ポリエステルなどの不織布からなる薄いシートを介装してもよい。そして、このシートの一方側表面には、上記各実施例で用いた焼結粉粒体とトルマリン粉粒体の混合体が混入された繊維からなる格子状開口をもつシート状の放射層(図示省略)を接合一体化させる。この放射層は、例えば上記シートと同様に不織布により形成する。このようにすれば、シートと放射層の強固な接合一体化が容易に行える。上記放射層は、全面を盲状としてシートの全面に接合してもよく、また放射層は、シートの表裏両面に接合させてもよい。さらに、放射層は、片状としてシートの表裏両面又は一方の面に点在状に設けることもできる。また、シートは、不織布に限らず布などを用いることもできる。
A thin sheet of non-woven fabric such as cotton, rayon, acetate, nylon, polyester or the like may be interposed between the
これによれば、中間層16とその表面の布帛との間に上記シートを介装させることにより、健康保持又は健康増進効果に優れたものに容易に変えられる。
According to this, by interposing the above-mentioned sheet between the
[4−2.トルマリン素材含有敷物の中間層の第2変形例]
実施例4;先ず、トルマリン(平均粒径0.9μm)の40重量%と、BaTiO2を主成分とする焼結粉粒体(平均粒径0.5μm)の60重量%とからなる混合体を、原料セルロースに対し10重量%混入してレーヨン繊維を紡糸した。次に、上記で得られた繊維の20重量%と綿糸80重量%の混紡糸を作製し、この混紡糸を用いて中間層16を製造した。
[4-2. Second modified example of intermediate layer of tourmaline material-containing rug]
Example 4 First, a mixture comprising 40% by weight of tourmaline (average particle diameter 0.9 μm) and 60% by weight sintered powder particles (average particle diameter 0.5 μm) mainly composed of BaTiO 2 Was mixed with 10% by weight of the raw material cellulose to spin a rayon fiber. Next, a blended yarn of 20% by weight of the fiber obtained above and 80% by weight of cotton yarn was produced, and an
実施例5;先ず、トルマリン(平均粒径0.9μm)の50重量%と、Al2O3、TiO3、BaOを主成分とする焼結粉粒体(平均粒径0.9μm)の50重量%とからなる混合体を、原料セルロースに対し10重量%混入してレーヨン繊維を紡糸した。次に、上記で得られた繊維の40重量%と綿糸60重量%の混紡糸を作製し、この混紡糸で中間層16を製造した。
Example 5 First, 50% by weight of tourmaline (average particle diameter 0.9 μm) and 50 of sintered powder particles (average particle diameter 0.9 μm) mainly composed of Al 2 O 3 , TiO 3 and BaO A mixture of 10% by weight and 10% by weight of the raw material cellulose was mixed to spin a rayon fiber. Next, a blended yarn of 40% by weight of the fiber obtained above and 60% by weight of cotton yarn was produced, and the
実施例6;先ず、トルマリン(平均粒径0.9μm)の60重量%と、BaTiO2を主成分とする焼結粉粒体(粒径1μm)の40重量%とからなる混合体を、原料セルロースに対し10重量%混入してレーヨン繊維を紡糸した。次に、上記で得られた繊維の30重量%と綿糸70重量%の混紡糸を作製し、この混紡糸で中間層16を作った。
Example 6 First, a mixture of 60% by weight of tourmaline (average particle size 0.9 μm) and 40% by weight of sintered powder particles (particle size 1 μm) mainly composed of BaTiO 2 is used as a raw material. Rayon fibers were spun in 10% by weight with respect to cellulose. Next, a blended yarn of 30% by weight of the fiber obtained above and 70% by weight of cotton yarn was produced, and the
なお、上記実施例4〜6においては、トルマリンとして、ショール(Schorl)を用いた。 In Examples 4 to 6, a shawl was used as tourmaline.
次に、上記実施例4〜6で使用した混合体の作用効果を調べるため、この混合体とその比較例であるトルマリン単体について、それぞれ誘電率、誘電正接、放射率(全エネルギーと全放射率)、遠赤外線放射量を測定した。その結果は、図7に示す。なお、図7は、実施例5の混合体を使用したときのデータである。また、実施例4、6の混合体を使用する場合も、図7とほぼ同一の作用効果が得られる。 Next, in order to investigate the function and effect of the mixtures used in the above Examples 4 to 6, the dielectric constant, the dielectric loss tangent, and the emissivity (total energy and total emissivity, respectively, for this mixture and the tourmaline alone as a comparative example thereof ), Far infrared radiation was measured. The result is shown in FIG. FIG. 7 shows data when the mixture of Example 5 is used. Also in the case of using the mixture of Examples 4 and 6, substantially the same effect as that of FIG. 7 can be obtained.
図7から明らかなように、本発明で用いる混合体は、トルマリン単体に比べて、誘電率と誘電正接及び遠赤外線放射量の何れもが優れている。また、放射率については、混合体とトルマリン単体との差は殆どないが、後述するように、放射量の発生領域が異なり、混合体の場合は、人体が吸収し易い領域で多量の放射量が発生する。 As is clear from FIG. 7, the mixture used in the present invention is superior in all of dielectric constant, dielectric loss tangent and far-infrared radiation amount as compared with tourmaline alone. As for emissivity, there is almost no difference between the mixture and tourmaline alone. However, as will be described later, the radiation generation region is different. Occurs.
ここで、誘電率と誘電正接についての測定試験は、混合体とトルマリン単体を20mmφ、2mm厚に圧縮成形して試験片として用いた。また、試験は、インピーダンス/ゲイン・フェイズアナライザー4194A(HEWLEFTT PAKARD社製)を用い、電極外径20mmφ、測定周波数1MHZ、試験温湿度23℃、50%RHで行った。 Here, in the measurement test for the dielectric constant and the dielectric loss tangent, the mixture and the tourmaline alone were compression-molded to a thickness of 20 mm and a thickness of 2 mm and used as a test piece. The test was conducted using an impedance / gain phase analyzer 4194A (manufactured by HEWLEFTT PAKARD) at an electrode outer diameter of 20 mmφ, a measurement frequency of 1 MHZ, and a test temperature and humidity of 23 ° C. and 50% RH.
エネルギーの放射率についての測定試験は、混合体とトルマリン単体を20mmφ、2mm厚に圧縮成形して試験片として用いた。また、試験は、IFS−113V(Bruker社製 FT−1R)を用い、波長領域2〜100μ、試験温度40℃で行った。なお、図7の放射率の項目には、理想黒体のデータも示している。 In the measurement test for the emissivity of energy, the mixture and tourmaline alone were compression-molded to a thickness of 20 mm and a thickness of 2 mm and used as a test piece. The test was conducted using IFS-113V (FT-1R manufactured by Bruker) at a wavelength range of 2 to 100 μ and a test temperature of 40 ° C. The item of emissivity in FIG. 7 also shows data of an ideal black body.
遠赤外線放射量(ファブリック)についての試験は、混合体とトルマリン単体を50×50mmの両面テープに貼り付けて試験片として用いた。また、試験は、サーモグラフィー(NEC三栄社製)を用い、与熱時間15分、温度36℃、検出波長8〜13μ、試験温湿度23℃、50%RHで行った。 In the test for far-infrared radiation (fabric), the mixture and tourmaline alone were attached to a 50 × 50 mm double-sided tape and used as a test piece. The test was conducted using thermography (manufactured by NEC San-ei Co., Ltd.) with a heating time of 15 minutes, a temperature of 36 ° C., a detection wavelength of 8 to 13 μ, and a test temperature and humidity of 23 ° C. and 50% RH.
図8は、縦軸にRelative emissivity(放射率、%)を、横軸にWavelength(波長、μm)をとった上記混合体の放射率スペクトルを示している。また、図9は、比較例としてトルマリン単体の放射率スペクトルを示している。これらの各図から明らかなように、人体が吸収し易い7〜12μm領域での放射率スペクトルが高い。 FIG. 8 shows the emissivity spectrum of the above mixture, where the vertical axis represents relative emission (emissivity,%) and the horizontal axis represents Wavelength (wavelength, μm). Further, FIG. 9 shows an emissivity spectrum of tourmaline alone as a comparative example. As apparent from each of these figures, the emissivity spectrum in the 7 to 12 μm region where the human body is likely to absorb is high.
図10は、縦軸にWatt×m-2×μm-1(熱エネルギー)を、横軸にWavelength(波長、μm)をとった上記混合体と理想黒体の発光エネルギー分布を示している。また、図11は、比較例としてトルマリン単体と理想黒体の発光エネルギー分布を示している。これらの各図から明らかなように、人体が吸収し易い7〜12μm領域において、発光エネルギー分布の曲線が理想黒体の曲線に近づき、上記領域での発生エネルギー量が多い。 FIG. 10 shows emission energy distributions of the above mixture and the ideal black body, in which the ordinate is Watt × m −2 × μm −1 (heat energy) and the abscissa is Wavelength (wavelength, μm). Further, FIG. 11 shows the light emission energy distribution of the tourmaline alone and the ideal black body as a comparative example. As is apparent from these figures, in the 7 to 12 μm region where the human body easily absorbs, the curve of the light emission energy distribution approaches the curve of the ideal black body, and the amount of generated energy in the above region is large.
以上のことから、上記各実施例による中間層16を用いた場合、これに混入したアルミナ、チタン、バリウム系化合物を主成分とする焼結粉粒体とトルマリン粉粒体との混合体により、人体が吸収し易い波長領域でのエネルギー放射率が高い遠赤外線特性を具有していることが理解できる。つまり、波長7〜12μmの領域において、約30〜36Watt×m-2×μm-1のエネルギーを放射する遠赤外線特性を具有する。よって、上記敷物10を使用することにより、血行が良くなって良好な保温効果が得られる。
From the above, when the
また、上記各中間層16は、誘電率が大きくて、高い電気的刺激効果が得られる。特に、敷物10を使用したとき、これが人体により加温されたり、又は圧力が加えられると、誘電率がさらに高められるので、人体への電気的刺激効果がより高められる。
Further, each of the
さらに、上記混合体はマイナスイオンを発生するので、これを混入した各敷物10を使用することにより、身体全体の電気の流れが良好となって人体の活性化に有効となる。しかも、上記混合体は、アンモニア系成分に対して優れた消臭効果を発揮し、また抗菌作用も有しているので、これを混入した敷物10は病院などで使用するものとして最適となる。
Furthermore, since the above mixture generates negative ions, the use of each of the
なお、上記説明したトルマリン素材含有敷物10の各構成要素は、本発明の一形態を例示したものに過ぎず、当業者が容易に想到できる程度の変形等は、本発明の範囲に含まれるものである。
The constituent elements of the tourmaline material-containing
10 トルマリン素材含有敷物
12 ムートン体
12A 羊毛部
12A1 羊毛
12B 皮部
12B1 皮
14 ベース材
16 中間層
16A トルマリンシート
16A1 トルマリン素材
16B 綿シート
16B1 綿
18 縫い部
20 ラジウムシート
22 ウレタン層
24 固わた層
DESCRIPTION OF
Claims (4)
前記ムートン体は、羊毛が密集した羊毛部と、前記羊毛が一度も切り離されない皮で構成された皮部と、を有し、
前記中間層に、Al2O3、TiO3、BaO、BaTiO2の1種類又は2種類以上からなる焼結粉粒体とトルマリンの粉粒体とが、前記焼結粉粒体と前記トルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%となるように混入され、
前記皮から一度も切り離されないことに伴う前記羊毛の表面に形成された微細な隙間の開閉作用を利用して、前記トルマリンからのマイナスイオンを前記羊毛の前記隙間から大気中に放出させることを特徴とする敷物。 A mouton body that does not have an opening, a base material, and an intermediate layer interposed between the mouton body and the base material are laminated, and the respective layers are formed in close contact by sewing at the edge. Rug, which
The Muton body has a wool section densely packed with wool and a skin section composed of a skin from which the wool is never separated.
In the intermediate layer, Al 2 O 3 , TiO 3 , BaO, BaTiO 2 , one or more sintered powder particles and tourmaline particles, and the tourmaline, The mixing ratio of the powder is 60 to 40% by weight of sintered powdery particles; 40 to 60% by weight of tourmaline,
Using the opening and closing action of a minute gap formed on the surface of the wool that is never separated from the skin, the negative ions from the tourmaline are released into the atmosphere from the gap of the wool. Characterized rugs.
前記ムートン体は、羊毛が密集した羊毛部と、前記羊毛が一度も切り離されない皮で構成された皮部と、を有し、
前記中間層に、Al2O3、TiO3、BaO、BaTiO2の1種類又は2種類以上からなる焼結粉粒体とトルマリンの粉粒体とが、前記焼結粉粒体と前記トルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%となるように混入され、
前記皮から一度も切り離されないことに伴う前記羊毛の表面に形成された微細な隙間の開閉作用を利用して、前記トルマリンからのマイナスイオンを前記羊毛の前記隙間から大気中に放出させることを特徴とする蒲団。 A mouton body that does not have an opening, a base material, and an intermediate layer interposed between the mouton body and the base material are laminated, and the respective layers are formed in close contact by sewing at the edge. The group is
The Muton body has a wool section densely packed with wool and a skin section composed of a skin from which the wool is never separated.
In the intermediate layer, Al 2 O 3 , TiO 3 , BaO, BaTiO 2 , one or more sintered powder particles and tourmaline particles, and the tourmaline, The mixing ratio of the powder is 60 to 40% by weight of sintered powdery particles; 40 to 60% by weight of tourmaline,
Using the opening and closing action of a minute gap formed on the surface of the wool that is never separated from the skin, the negative ions from the tourmaline are released into the atmosphere from the gap of the wool. A group to feature.
前記ムートン体は、羊毛が密集した羊毛部と、前記羊毛が一度も切り離されない皮で構成された皮部と、を有し、
前記中間層は、Al2O3、TiO3、及びBaOを主成分とする焼結粉粒体とトルマリンの粉粒体とを含有するレーヨン繊維と、綿糸との混紡糸からなり、前記焼結粉粒体と前記トルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%であり、混紡糸の配合比率が、レーヨン繊維20〜40重量%;綿糸80〜60重量%であり、
前記皮から一度も切り離されないことに伴う前記羊毛の表面に形成された微細な隙間の開閉作用を利用して、前記トルマリンからのマイナスイオンを前記羊毛の前記隙間から大気中に放出させることを特徴とする敷物。 A mouton body that does not have an opening, a base material, and an intermediate layer interposed between the mouton body and the base material are laminated, and the respective layers are formed in close contact by sewing at the edge. Rug, which
The Muton body has a wool section densely packed with wool and a skin section composed of a skin from which the wool is never separated.
The intermediate layer is composed of a blended yarn of rayon fiber containing a sintered powder body mainly composed of Al 2 O 3 , TiO 3 , and BaO and a tourmaline powder body, and cotton yarn, and the sintered body The blending ratio of the powder and the tourmaline is 60 to 40% by weight of the sintered powder; 40 to 60% by weight of the tourmaline, and the blending ratio of mixed spinning is 20 to 40% by weight of rayon fiber; 60% by weight,
Using the opening and closing action of the fine gap formed on the surface of the wool associated with never being separated from the skin, to release negative ions from the tourmaline to the atmosphere from the gap of the wool Characterized rugs.
前記ムートン体は、羊毛が密集した羊毛部と、前記羊毛が一度も切り離されない皮で構成された皮部と、を有し、
前記中間層は、Al2O3、TiO3、及びBaOを主成分とする焼結粉粒体とトルマリンの粉粒体とを含有するレーヨン繊維と、綿糸との混紡糸からなり、前記焼結粉粒体と前記トルマリンとの配合比率が、焼結粉粒体60〜40重量%;トルマリン40〜60重量%であり、混紡糸の配合比率が、レーヨン繊維20〜40重量%;綿糸80〜60重量%であり、
前記皮から一度も切り離されないことに伴う前記羊毛の表面に形成された微細な隙間の開閉作用を利用して、前記トルマリンからのマイナスイオンを前記羊毛の前記隙間から大気中に放出させることを特徴とする蒲団。 A mouton body that does not have an opening, a base material, and an intermediate layer interposed between the mouton body and the base material are laminated, and the respective layers are formed in close contact by sewing at the edge. The group is
The Muton body has a wool section densely packed with wool and a skin section composed of a skin from which the wool is never separated.
The intermediate layer is composed of a blended yarn of rayon fiber containing a sintered powder body mainly composed of Al 2 O 3 , TiO 3 , and BaO and a tourmaline powder body, and cotton yarn, and the sintered body The blending ratio of the powder and the tourmaline is 60 to 40% by weight of the sintered powder; 40 to 60% by weight of the tourmaline, and the blending ratio of mixed spinning is 20 to 40% by weight of rayon fiber; 60% by weight,
Using the opening and closing action of a minute gap formed on the surface of the wool that is never separated from the skin, the negative ions from the tourmaline are released into the atmosphere from the gap of the wool. A group to feature.