JP6494083B2 - Nonwoven sheet for interpersonal wiping - Google Patents
Nonwoven sheet for interpersonal wiping Download PDFInfo
- Publication number
- JP6494083B2 JP6494083B2 JP2014240484A JP2014240484A JP6494083B2 JP 6494083 B2 JP6494083 B2 JP 6494083B2 JP 2014240484 A JP2014240484 A JP 2014240484A JP 2014240484 A JP2014240484 A JP 2014240484A JP 6494083 B2 JP6494083 B2 JP 6494083B2
- Authority
- JP
- Japan
- Prior art keywords
- region
- nonwoven fabric
- wiping
- interpersonal
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、対人ワイピング用不織布シートに関する。 The present invention relates to a nonwoven fabric sheet for interpersonal wiping.
対人ワイピング用途で使用される不織布には適度な強度、保水性及び柔らかさが要求される。病院施設等老人介護において、オムツ交換時の下拭き用途では、多くの場合、レンタルのリネンタオルが使用されている。リネンタオルは専用の洗浄液（水+洗浄成分）を含浸して温めて下拭きの用に供される。リネンタオルは厚みの有る綿タオル地素材であり、吸水性と温めた後の保温性に優れており、下拭き用途に適した性能を有している。 Nonwoven fabrics used for interpersonal wiping are required to have appropriate strength, water retention and softness. In elderly care such as hospital facilities, rental linen towels are often used for wiping the diaper. Linen towels are impregnated with a special cleaning solution (water + cleaning components), warmed and used for wiping. Linen towel is a thick cotton towel material, has excellent water absorbency and heat retention after warming, and has performance suitable for wiping.
しかし、リネンタオルは専門業者による回収、洗浄してリユースされることが前提となっており、洗浄によりＢａｃｉｌｌｕｓ属等芽胞を形成する菌を完全に消毒することは困難であり、院内感染の原因となるリスクを内包していることも事実である。これらの問題に鑑み、使い捨てのレーヨンスパンレース不織布ワイパーが提案されている（特許文献１参照）。 However, it is assumed that linen towels are collected and washed by specialists and reused, and it is difficult to completely disinfect bacteria that form spores such as Bacillus genus by washing. It is also true that it contains a risk. In view of these problems, a disposable rayon spunlace nonwoven wiper has been proposed (see Patent Document 1).
しかしながら、上記使い捨てのレーヨンスパンレース不織布ワイパーのような一般的な不織布では、下拭き時に重要となる軟便の拭き取り性が劣るという問題がある。 However, a general nonwoven fabric such as the disposable rayon spunlace nonwoven wiper has a problem that the wiping property of soft stool, which is important at the time of wiping under, is inferior.
そこで、本発明の目的は上記課題を解決するために、衛生的で、拭き取り性能の良い使い捨て可能な対人ワイピング用不織布シートを提供することを目的とする。 Accordingly, an object of the present invention is to provide a disposable nonwoven fabric sheet for interpersonal wiping that is hygienic and has good wiping performance in order to solve the above-mentioned problems.
上記課題を解決するために、（１）本発明は、対人ワイピング用不織布シートであって、５０重量％以上のレーヨンと、ポリプロピレン、ポリエチレンテレフタレートおよびポリエチレンから選ばれる材質を含む単一又は複合繊維と、を含み、乾式スパンレース法によって形成され、所定の繊維量を有する第１領域と、前記第１領域より少ない繊維量を有する第２領域と、が全面にわたって選択的に形成されている。 In order to solve the above-mentioned problems, (1) the present invention is a nonwoven fabric sheet for interpersonal wiping, comprising 50% by weight or more of rayon and a single or composite fiber containing a material selected from polypropylene, polyethylene terephthalate and polyethylene The first region having a predetermined fiber amount and the second region having a smaller fiber amount than the first region are selectively formed over the entire surface.
（２）上記（１）において、坪量が６０ｇ／ｍ２〜１００ｇ／ｍ２である。
（３）上記（１）又は（２）において、前記第２領域が前記不織布シートの面積の３０％〜７０％の範囲で設けられている。
（４）上記（１）〜（３）のいずれか１において、前記第１領域と、前記第２領域は、一方方向に沿って、ストライプ状に交互に形成される。
(2) In the above (1), a basis weight of 60g / m 2 ~100g / m 2 .
(3) In the above (1) or (2), the second region is provided in a range of 30% to 70% of the area of the nonwoven fabric sheet.
(4) In any one of the above (1) to (3), the first region and the second region are alternately formed in a stripe shape along one direction.
（５）上記（１）〜（４）において、前記第２領域の平均坪量は、前記不織布シートの平均坪量の３０％〜７０％である。
（６）上記（１）〜（５）のいずれか１において、前記第２領域は、前記第２領域の平均坪量よりもさらに繊維量の少ない第３領域を有する。
（７）上記（１）〜（６）において、前記第３領域の平均坪量は、前記不織布シートの平均坪量の５％〜３０％である。
(5) In the above (1) to (4), the average basis weight of the second region is 30% to 70% of the average basis weight of the nonwoven fabric sheet.
(6) In any one of the above (1) to (5), the second region has a third region having a smaller fiber amount than the average basis weight of the second region.
(7) In the above (1) to (6), the average basis weight of the third region is 5% to 30% of the average basis weight of the nonwoven fabric sheet.
（８）上記（１）〜（７）において、ＴＳＡソフトネス指数によるＴＳ７５０値が１５ｄＢＶ2ｒｍｓ〜３５ｄＢＶ2ｒｍｓである。
（９）上記（１）〜（８）において、ＴＳＡソフトネス指数によるＴＳ７値が５ｄＢＶ2ｒｍｓ〜１２ｄＢＶ2ｒｍｓである。
（１０）上記（１）〜（９）において、ＴＳＡソフトネス指数による剛性Ｄ値が１．０ｍｍ／Ｎ〜３．５ｍｍ／Ｎである。
(8) In the above (1) ~ (7), TS750 value by TSA softness index is 15dBV 2 rms~35dBV 2 rms.
(9) In the above (1) ~ (8), TS7 value by TSA softness index is 5dBV 2 rms~12dBV 2 rms.
(10) In the above (1) to (9), the stiffness D value according to the TSA softness index is 1.0 mm / N to 3.5 mm / N.
本発明によれば、衛生的で、拭き取り性能の良い使い捨て可能な対人ワイピング用不織布シートを提供できる。 According to the present invention, a disposable nonwoven fabric sheet for interpersonal wiping that is hygienic and has good wiping performance can be provided.
以下、添付図面を参照して、本発明を実施するための形態（以下、「実施形態」と称する）について詳細に説明する。実施形態の説明の全体を通して同じ要素には同じ番号を付している。 DESCRIPTION OF EMBODIMENTS Hereinafter, embodiments for carrying out the present invention (hereinafter referred to as “embodiments”) will be described in detail with reference to the accompanying drawings. The same number is attached | subjected to the same element through the whole description of embodiment.
図１は、第１領域と第２領域を一方方向に沿ってストライプ状に交互に形成した不織布シートの一例を示す図である。
本発明の実施形態に係る対人ワイピング用不織布シート（以下、「不織布シート」と称す）１００は、５０重量％以上のレーヨンと、ポリプロピレン（ＰＰ）、ポリエチレンテレフタレート（ＰＥＴ）およびポリエチレン（ＰＥ）から選ばれる材質を含む単一又は複合繊維と、を含み、乾式スパンレース法によって形成される不織布シートである。
不織布シート１００は、乾式スパンレース法によって、レーヨンなどの天然系素材と、ＰＰ、ＰＥＴ、ＰＥなどを材質とする合成繊維を高圧水流によって繊維同士を絡合させて形成される。
FIG. 1 is a diagram illustrating an example of a nonwoven fabric sheet in which first regions and second regions are alternately formed in a stripe shape along one direction.
The nonwoven fabric sheet for interpersonal wiping (hereinafter referred to as “nonwoven fabric sheet”) 100 according to the embodiment of the present invention is selected from rayon of 50% by weight or more, polypropylene (PP), polyethylene terephthalate (PET), and polyethylene (PE). And a non-woven sheet formed by a dry spunlace method.
The nonwoven fabric sheet 100 is formed by intertwining fibers with a natural material such as rayon and a synthetic fiber made of PP, PET, PE or the like by a high-pressure water stream by a dry spunlace method.
レーヨンを５０重量％以上含有することで対人ワイピングに適した吸水性を得ることが出来る。また合成繊維は、材質をＰＰ、ＰＥＴ、ＰＥの中からいずれか１つを選んだ単一繊維でもよいし、複数の材質を選んだ複合繊維でもよい。 By containing 50% by weight or more of rayon, water absorption suitable for interpersonal wiping can be obtained. The synthetic fiber may be a single fiber selected from PP, PET, PE, or a composite fiber selected from a plurality of materials.
図１に示すように、不織布シート１００は、所定の繊維量を有する第１領域１０１と、第１領域１０１より少ない繊維量を有する第２領域１０２が不織布シートの全面にわたって選択的に形成されている。この構成により下拭き作業において軟便を拭取る際、繊維量の少ない第２領域１０２によって軟便を迅速に収容し、きれいにふき取ることができる。 As shown in FIG. 1, the nonwoven fabric sheet 100 is formed by selectively forming a first region 101 having a predetermined fiber amount and a second region 102 having a fiber amount smaller than the first region 101 over the entire surface of the nonwoven fabric sheet. Yes. With this configuration, when soft stool is wiped in the lower wiping operation, the soft stool can be quickly accommodated and wiped cleanly by the second region 102 having a small amount of fibers.
不織布シート１００の坪量は、ＪＩＳ Ｐ ８１２４に準拠した方法で測定し、坪量が６０ｇ／ｍ２〜１００ｇ／ｍ２であるのが好ましい。坪量が１００ｇ／ｍ２を超えると、厚くなりすぎ、シワやヒダの隙間に入った汚れを綺麗に拭き取ることが出来ない。また、坪量が６０ｇ／ｍ２を下回るとシートが薄く、使用時に不安感を覚えるとともに洗浄液の保持量が少なく拭き取りにくい。 The basis weight of the nonwoven fabric sheet 100 is measured by a method conforming to JIS P 8124, preferably the basis weight is 60g / m 2 ~100g / m 2 . If the basis weight exceeds 100 g / m 2 , it will be too thick and it will not be possible to clean off dirt that has entered wrinkles and creases. On the other hand, when the basis weight is less than 60 g / m 2 , the sheet is thin, anxiety is felt at the time of use, and the amount of the cleaning liquid is small and it is difficult to wipe off.
第１領域１０１は、第２領域１０２の繊維量との関係から、不織布シートの平均坪量より繊維量が多いことが好ましい。 From the relationship with the fiber amount of the 2nd area | region 102, it is preferable that the 1st area | region 101 has more fiber amounts than the average basic weight of a nonwoven fabric sheet.
第２領域１０２が不織布シート１００の全面にわたって多数形成されていることによって、下拭き作業において軟便を拭き取る際、当該第２領域１０２が軟便を迅速に繊維間隙に収容するため、きれいに拭き取ることができる。
第２領域１０２は、不織布シート１００の平均坪量より繊維量が少なく、不織布シートの面積の３０％〜７０％であることが好ましい。第２領域１０２が３０％より少ない場合、軟便の拭き取り性能が低くなってしまう。また、第２領域１０２が７０％より多い場合、不織布シートの平均坪量より繊維量が多い第１領域１０１の面積少なくなることから、第１領域１０１の厚みが大きくなりすぎる結果、不織布シートの凹凸差が激しい、触感の悪い不織布シートとなってしまう。
Since the second region 102 is formed in large numbers over the entire surface of the nonwoven fabric sheet 100, when the soft stool is wiped off in the lower wiping operation, the second region 102 quickly accommodates the soft stool in the fiber gap, so that it can be wiped cleanly. .
The second region 102 has less fiber than the average basis weight of the nonwoven fabric sheet 100, and is preferably 30% to 70% of the area of the nonwoven fabric sheet. When the second area 102 is less than 30%, the wiping performance of soft stool is lowered. In addition, when the second region 102 is more than 70%, the area of the first region 101 having a larger fiber amount than the average basis weight of the nonwoven fabric sheet is reduced, and as a result, the thickness of the first region 101 becomes too large. This results in a nonwoven fabric sheet with a large unevenness difference and a poor tactile feel.
第２領域１０２の平均坪量は、不織布シート全体の平均坪量の３０％〜７０％であることが好ましい。３０％未満の繊維量では、十分な量の軟便を有効に保持することが出来ない。また、７０％を超える繊維量では、軟便を収容する繊維間隙が小さくなることから迅速かつ十分な量の軟便を保持することが出来ない。 The average basis weight of the second region 102 is preferably 30% to 70% of the average basis weight of the entire nonwoven fabric sheet. If the fiber amount is less than 30%, a sufficient amount of soft stool cannot be effectively retained. On the other hand, if the amount of fiber exceeds 70%, the fiber gap for accommodating loose stool becomes small, so that a quick and sufficient amount of loose stool cannot be held.
ところで、図１に示すように、第１領域１０１と、第２領域１０２は一方方向に沿って、ストライプ状に交互に形成されることが好ましい。第１領域１０１および第２領域１０２がそれぞれ線上に延びる方向は、乾式スパンレース法における乾式カード工程およびスパンレース工程の流れ方向と同一である。これにより、不織布シートの製造および加工工程における必要な強度を維持することができる。 By the way, as shown in FIG. 1, it is preferable that the 1st area | region 101 and the 2nd area | region 102 are alternately formed in stripe form along one direction. The direction in which each of the first region 101 and the second region 102 extends on the line is the same as the flow direction of the dry card process and the spun lace process in the dry spunlace method. Thereby, the required intensity | strength in manufacture and a process of a nonwoven fabric sheet can be maintained.
図２は、第２領域が第３領域を有する不織布シートの変形例を示す図である。図２に示すように、不織布シート１１０は、第２領域１０２内に第２領域１０２の平均坪量よりさらに繊維量の少ない第３領域１０３が形成されている。図２に示す例では、第３領域１０３が所定の間隔を空けて楕円形状に形成されている。また、隣り合う第２領域１０２間で重ならない領域に第２領域が形成されている。このように第３領域１０３を形成することによって、比較的粘度が高めの軟便に対して有効に作用することができる。 FIG. 2 is a view showing a modification of the nonwoven fabric sheet in which the second region has the third region. As shown in FIG. 2, in the nonwoven fabric sheet 110, a third region 103 having a smaller fiber amount than the average basis weight of the second region 102 is formed in the second region 102. In the example shown in FIG. 2, the third region 103 is formed in an elliptical shape with a predetermined interval. Further, the second region is formed in a region that does not overlap between the adjacent second regions 102. By forming the third region 103 in this way, it is possible to effectively act on soft stool having a relatively high viscosity.
また、第３領域１０３の平均坪量は、不織布シート全体の平均坪量の５％〜３０％であることが好ましい。５％未満の繊維量では、粘度の低い緩めの軟便が不織布シートの裏に抜けてしまい、手が汚れてしまう。また、３０％を超える繊維量では、粘度が高めの軟便に対して有効に作用しない。 Moreover, it is preferable that the average basic weight of the 3rd area | region 103 is 5 to 30% of the average basic weight of the whole nonwoven fabric sheet. If the amount of fiber is less than 5%, loose soft stool having a low viscosity falls out to the back of the nonwoven fabric sheet, and the hands become dirty. In addition, when the amount of fibers exceeds 30%, it does not act effectively on soft stool having a high viscosity.
（ＴＳ７５０値）
（ＴＳ７値）
本発明の実施形態に係る不織布シートは、ＴＳＡ（Tissue Softness Analyzer、日本ルフト株式会社製）ソフトネス指数によるＴＳ７５０値が不織布シートは、ＴＳ７５０値が１５〜３５ｄＢＶ2ｒｍｓであるのが好ましい。
本実施形態に係る不織布シートは、ＴＳＡソフトネス指数によるＴＳ７値が５〜１２ｄＢＶ2ｒｍｓであるのが好ましい。
(TS750 value)
(TS7 value)
The nonwoven fabric sheet according to the embodiment of the present invention preferably has a TS750 value according to TSA (Tissue Softness Analyzer, Nippon Luft Co., Ltd.) softness index, and the nonwoven fabric sheet has a TS750 value of 15 to 35 dBV 2 rms.
The nonwoven fabric sheet according to this embodiment preferably has a TS7 value according to the TSA softness index of 5 to 12 dBV 2 rms.
ＴＳＡソフトネス指数によるＴＳ７５０値は、ソフトネス測定装置ＴＳＡにより、試料台に設置した不織布シートのサンプルに対し、ブレード付きロータを１００ｍＮの押し込み圧力として上から押し込んだ後に回転数２．０（／ｓｅｃ）で回転させ、試料台の振動を振動センサで測定したとき、ＴＳＡ上のソフトウェアにて自動的に取得した、低周波数側からの最初のスペクトルの極大ピークの強度で表される。ＴＳＡソフトネス指数によるＴＳ７値は、６５００Ｈｚを含むスペクトルの極大ピークの強度で表される。 The TS750 value according to the TSA softness index is calculated by using a softness measuring apparatus TSA to push a bladed rotor from the top to a non-woven sheet sample placed on a sample table from the top with a pushing pressure of 100 mN, and the rotation speed is 2.0 (/ sec. ), And the vibration of the sample stage is measured by a vibration sensor, and is represented by the intensity of the maximum peak of the first spectrum from the low frequency side automatically obtained by software on the TSA. The TS7 value according to the TSA softness index is represented by the intensity of the maximum peak of the spectrum including 6500 Hz.
ＴＳ７５０値が１５より低いと平滑性が高すぎて、汚れを掻き落とす機能が低くなる。ＴＳ７５０値が３５より高いとザラザラとした触感が不快に感じられる。ＴＳ７値が５より低いと柔らかさが際立ち不安感を与えるとともに、拭きにくい。ＴＳ７値が１２より高いと硬い触感となる。 When the TS750 value is lower than 15, the smoothness is too high and the function of scraping off the dirt is lowered. If the TS750 value is higher than 35, the rough texture is uncomfortable. When the TS7 value is lower than 5, the softness stands out and gives anxiety and is difficult to wipe. When the TS7 value is higher than 12, a hard tactile sensation is obtained.
（剛性Ｄ）
本実施形態に係る不織布シートは、ＴＳＡソフトネス指数による剛性Ｄが１〜３．５ｍｍ／Ｎであるのが好ましい。ＴＳＡソフトネス指数による剛性Ｄの測定値は、ソフトネス測定装置ＴＳＡにより、試料台に設置した不織布のサンプルに対し、ブレード付きロータを回転させずに１００ｍＮと６００ｍＮの押し込み圧力でそれぞれ上から押し込んだとき、それぞれ押し込み圧力１００ｍＮと６００ｍＮの間でのサンプルの上下方向の変形変位量で表される。
(Rigidity D)
The nonwoven fabric sheet according to this embodiment preferably has a stiffness D according to the TSA softness index of 1 to 3.5 mm / N. The measured value of stiffness D by the TSA softness index was pushed from above with a pushing force of 100 mN and 600 mN without rotating the bladed rotor with respect to the nonwoven fabric sample placed on the sample table by the softness measuring device TSA. Is expressed by the amount of deformation in the vertical direction of the sample between the pressing pressures of 100 mN and 600 mN, respectively.
（ＴＳＡ）
ここで、図３に示すように、ソフトネス測定装置ＴＳＡ２１０は、不織布シート試料（サンプル）２０６の上から、回転したブレード付きロータ２０４を押付けたときの各種センサで検知した振動データを、振動解析してパラメータ化（ＴＳ値）することにより、不織布のソフトネス（手触り感）を定量評価するものであり、ドイツのエムテック（Emtec Electronic GmbH、日本代理店は日本ルフト株式会社）社製の商品名である。
(TSA)
Here, as shown in FIG. 3, the softness measuring device TSA 210 performs vibration analysis on vibration data detected by various sensors when the rotated bladed rotor 204 is pressed on the nonwoven fabric sheet sample (sample) 206. By parameterizing (TS value), the softness (feel of touch) of the nonwoven fabric is quantitatively evaluated. The product name of Emtec Electronic GmbH of Germany (Japan distributor is Japan Luft Co., Ltd.) It is.
ＴＳＡを用いた具体的な測定は、(i)円形の試料台２０５を外側から覆うようサンプル２０６（ｅｍｔｅｃ社のサンプルパンチを使用して直径が約１１２．８ｍｍの円形に加工したサンプル）を設置し、サンプル２０６の外周をサンプル固定リング２０８で保持し、(ii)ブレード付きロータ２０４を１００ｍＮの押し込み圧力でサンプル２０６の上から押し込んだ後、ロータ２０４を回転数２．０（／ｓｅｃ）で回転させ、(iii)試料台２０５の振動を、試料台２０５内部に設置した振動センサ２０３で測定し、振動周波数を解析する。(iv)次に、押し込み圧力１００ｍＮと６００ｍＮで、ロータ２０４を回転させずにそれぞれサンプル２０６を変形させたときの上下方向の変形変位量（ｍｍ/Ｎ、剛性Ｄ）を計測する。
(i)〜(iv)の手順により、不織布シートの総合的なハンドフィール値の要素（滑らかさ、しなやかさ、ボリューム感）が各々数値化できる。
For specific measurement using TSA, (i) Install sample 206 (sample processed into a circular shape with a diameter of about 112.8 mm using emtec's sample punch) to cover the circular sample stage 205 from the outside. The outer periphery of the sample 206 is held by the sample fixing ring 208. (ii) After the bladed rotor 204 is pushed from above the sample 206 with a pushing pressure of 100 mN, the rotor 204 is rotated at a rotation speed of 2.0 (/ sec). (Iii) The vibration of the sample stage 205 is measured by the vibration sensor 203 installed in the sample stage 205, and the vibration frequency is analyzed. (iv) Next, when the indentation pressure is 100 mN and 600 mN, the deformation amount (mm / N, rigidity D) in the vertical direction when the sample 206 is deformed without rotating the rotor 204 is measured.
By the procedures (i) to (iv), the elements (smoothness, suppleness, volume feeling) of the overall hand feel value of the nonwoven fabric sheet can be quantified.
測定は１サンプルについて表裏５回ずつ繰り返し、平均化する。なお、表裏とは、不織布シートの両面を意味する。試料台２０５はベースプレート２０１上に設置され、試料台２０５とベースプレート２０１の間には、力センサ２０２が配置されている。そして、力センサ２０２の検出値により、ブレード付きロータ２０４の押し込み圧力を制御する。又、ブレード付きロータ２０４はモータ２０９によって回転する。又、振動解析してパラメータ化（ＴＳ値）するソフトウェアは、emtec measurement systemを用いる。本ソフトウェアには、各種アルゴリズム（例えば、Base Tissue、Facial、TP等）が備えられ、ＴＳ７、ＴＳ７５０、Ｄをソフトウェア上で自動的に取得し、これらＴＳ７、ＴＳ７５０、Ｄ値が計算される。本発明では、ＴＳ７、ＴＳ７５０、Ｄのみを規定しており、上記測定条件を満たせば、アルゴリズムは何を使用しても良く、ＴＳ７、ＴＳ７５０、Ｄの値はアルゴリズムの種類によって変わることはない。 The measurement is repeated 5 times for each sample and averaged. In addition, front and back mean both surfaces of a nonwoven fabric sheet. The sample stage 205 is installed on the base plate 201, and a force sensor 202 is disposed between the sample stage 205 and the base plate 201. Then, the pushing pressure of the bladed rotor 204 is controlled by the detection value of the force sensor 202. The bladed rotor 204 is rotated by a motor 209. In addition, emtec measurement system is used as software for analyzing vibration and parameterizing (TS value). This software includes various algorithms (for example, Base Tissue, Facial, TP, etc.), and TS7, TS750, and D are automatically acquired on the software, and these TS7, TS750, and D values are calculated. In the present invention, only TS7, TS750, and D are defined, and any algorithm can be used as long as the above measurement conditions are satisfied, and the values of TS7, TS750, and D do not vary depending on the type of algorithm.
図４は、ＴＳＡによる不織布シート試料サンプルの振動周波数の解析結果の一例を示す。低周波数側からの最初のスペクトルの極大ピークＡの強度をＴＳ７５０とし、６５００Ｈｚを含む（６５００Ｈｚの前後の）スペクトルの極大ピークＢの強度をＴＳ７とする。極大ピークＢは、通常、約６５００Ｈｚに位置する。 FIG. 4 shows an example of the analysis result of the vibration frequency of the nonwoven fabric sheet sample sample by TSA. The intensity of the maximum peak A of the first spectrum from the low frequency side is TS750, and the intensity of the maximum peak B of the spectrum including 6500 Hz (around 6500 Hz) is TS7. The maximum peak B is usually located at about 6500 Hz.
図５は、ＴＳＡによる不織布シート試料サンプルの剛性Ｄの測定方法を示す。不織布シート試料サンプルの振動周波数は、不織布シートの構造及びロータ２０４の回転数に依存し、振幅（スペクトルの強度）は、不織布シートの構造の高さに依存する。そして、スペクトルの最初のピーク（図２のＡ）であるＴＳ７５０は滑らかさ、粗さを表す。一方、ＴＳ７が現れる周波数（５０００〜８０００Ｈｚの範囲、通常は６５００Ｈｚ近傍）は、ロータ２０４の共振周波数であり、水平振動となって不織布シート表面を進むときに繊維による瞬間的な遮断とロータ２０４の振動に起因する。剛性Ｄは、紙の剛性（引張強度）に相関する。ＴＳ７の値が低いほど、ふんわり感（表面ソフトネスおよびバルクソフトネス）に優れ、ＴＳ７５０の値が低いほど、滑らかさに優れる。又、Ｄの値が大きいほど、しなやかさに優れる。 FIG. 5 shows a method for measuring the rigidity D of the nonwoven fabric sheet sample sample by TSA. The vibration frequency of the nonwoven sheet sample sample depends on the structure of the nonwoven sheet and the number of rotations of the rotor 204, and the amplitude (spectrum intensity) depends on the height of the structure of the nonwoven sheet. TS750, which is the first peak of the spectrum (A in FIG. 2), represents smoothness and roughness. On the other hand, the frequency at which TS7 appears (in the range of 5000 to 8000 Hz, usually around 6500 Hz) is the resonance frequency of the rotor 204. Due to vibration. The rigidity D correlates with the rigidity (tensile strength) of the paper. The lower the TS7 value, the better the soft feeling (surface softness and bulk softness), and the lower the TS750 value, the better the smoothness. Moreover, the greater the value of D, the more flexible.
以下に、実施例及び比較例を挙げて本発明をさらに具体的に説明する。なお、本発明はその要旨を超えない限り、以下の実施例の記載に限定されるものではない。 Hereinafter, the present invention will be described more specifically with reference to examples and comparative examples. In addition, this invention is not limited to description of a following example, unless the summary is exceeded.
（実施例１）
実施例１では、１．７ｄｔｅｘのレーヨン繊維（ホープ、オーミケンシ株式会社製）８０重量％、２．２ｄｔｅｘのＰＥＴ／ＰＥ芯鞘複合繊維（テトロン、帝人ファイバー株式会社製）２０重量％を均一に混綿し、ＣＡＤ（カード機）でセミランダムウェブを作製した。次いで、スパンレース工程において、平織りの全体に平坦なネット支持体にウェブを載置して連続的に移送するとともに、高圧水流を噴射して交絡処理を行ない、ネットの凹凸を不織布表面に転写するように調整した。第１領域１０１の面積、第２領域１０２の面積、第２領域１０２の平均坪量、第３領域１０３の平均坪量、ＴＳ７５０、ＴＳ７、Ｄ値は表１に示すとおりである。
Example 1
In Example 1, 80% by weight of 1.7 dtex rayon fiber (Hope, manufactured by Omikenshi Co., Ltd.) and 20% by weight of 2.2 dtex PET / PE core-sheath composite fiber (Tetron, manufactured by Teijin Fibers Limited) were uniformly mixed. Then, a semi-random web was produced with a CAD (card machine). Next, in the spunlace process, the web is placed on a flat net support on the entire plain weave and continuously transferred, and entangled with a high-pressure water stream to transfer the unevenness of the net to the nonwoven fabric surface. Adjusted as follows. The area of the first region 101, the area of the second region 102, the average basis weight of the second region 102, the average basis weight of the third region 103, TS750, TS7, and the D value are as shown in Table 1.
（実施例２〜３）
実施例２および実施例３については、表１に示すとおりとし、実施例１とまったく同様にして不織布シートを作成した。
(Examples 2-3)
About Example 2 and Example 3, it was as having shown in Table 1, and it carried out similarly to Example 1, and created the nonwoven fabric sheet.
（比較例１）
比較例１については、表１に示すとおり第３領域を設けず、実施例１とまったく同様にして不織布シートを作成した。第１領域１０１の面積、第２領域１０２の面積、第２領域１０２の平均坪量、ＴＳ７５０、ＴＳ７、Ｄ値は表１に示すとおりである。比較例１では第１領域の繊維量が多いため、軟便をうまく拭き取ることができなかった。
(Comparative Example 1)
For Comparative Example 1, a non-woven sheet was prepared in the same manner as in Example 1 without providing the third region as shown in Table 1. Table 1 shows the area of the first region 101, the area of the second region 102, the average basis weight of the second region 102, TS750, TS7, and the D value. In Comparative Example 1, since the amount of fibers in the first region was large, soft stools could not be wiped off.
（比較例２）
比較例２については、実施例１とまったく同様にして不織布シートを作成した。第１領域１０１の面積、第２領域１０２の面積、第２領域１０２の平均坪量、第３領域１０３の平均坪量、ＴＳ７５０、ＴＳ７、Ｄ値は表１に示すとおりである。比較例２では第２領域の面積が小さく、十分な量の軟便をうまく拭き取ることができなかった。
(Comparative Example 2)
For Comparative Example 2, a non-woven sheet was prepared in exactly the same manner as in Example 1. The area of the first region 101, the area of the second region 102, the average basis weight of the second region 102, the average basis weight of the third region 103, TS750, TS7, and the D value are as shown in Table 1. In Comparative Example 2, the area of the second region was small, and a sufficient amount of soft stool could not be wiped off.
（比較例３）
比較例３については、実施例１とまったく同様にして不織布シートを作成した。第１領域１０１の面積、第２領域１０２の面積、第２領域１０２の平均坪量、第３領域１０３の平均坪量、ＴＳ７５０、ＴＳ７、Ｄ値は表１に示すとおりである。比較例３では第１領域１０１が非常に厚くなり、デコボコとして触感が非常に悪くなった。
(Comparative Example 3)
For Comparative Example 3, a nonwoven fabric sheet was prepared in exactly the same manner as in Example 1. The area of the first region 101, the area of the second region 102, the average basis weight of the second region 102, the average basis weight of the third region 103, TS750, TS7, and the D value are as shown in Table 1. In the comparative example 3, the 1st area | region 101 became very thick and the tactile sensation became very bad as a bump.
以上、実施形態を用いて本発明を説明したが、本発明の技術的範囲は上記の実施形態に記載の範囲には限定されないことは言うまでもない。上記実施形態に、多様な変更又は改良を加えることが可能であることが当業者に明らかである。また、そのような変更又は改良を加えた形態も本発明の技術的範囲に含まれ得ることが、特許請求の範囲の記載から明らかである。 As mentioned above, although this invention was demonstrated using embodiment, it cannot be overemphasized that the technical scope of this invention is not limited to the range as described in said embodiment. It will be apparent to those skilled in the art that various modifications or improvements can be added to the above embodiment. Further, it is apparent from the scope of the claims that embodiments with such changes or improvements can also be included in the technical scope of the present invention.
１０１ 第１領域
１０２ 第２領域
１０３ 第３領域
２０１ ベースプレート
２０２ 力センサ
２０３ 振動センサ
２０４ ロータ
２０５ 試料台
２０６ サンプル
２０８ サンプル固定リング
２０９ モータ
DESCRIPTION OF SYMBOLS 101 1st area | region 102 2nd area | region 103 3rd area | region 201 Base plate 202 Force sensor 203 Vibration sensor 204 Rotor 205 Sample stand 206 Sample 208 Sample fixing ring 209 Motor
Claims (9)
５０重量％以上のレーヨンと、
ポリプロピレン、ポリエチレンテレフタレートおよびポリエチレンから選ばれる材質を含む単一又は複合繊維と、を含み、
所定の繊維量を有する第１領域と、
前記第１領域より少ない繊維量を有する第２領域と、が全面にわたって選択的に形成されており、
前記第２領域は、前記第２領域の平均坪量よりもさらに繊維量の少ない第３領域を有することを特徴とする対人ワイピング用不織布シート。 A spunlace nonwoven sheet for interpersonal wiping,
50% or more by weight of rayon,
A single or composite fiber comprising a material selected from polypropylene, polyethylene terephthalate and polyethylene ,
A first region having a predetermined fiber amount;
A second region having a fiber amount less than the first region is selectively formed over the entire surface ,
The nonwoven fabric sheet for interpersonal wiping , wherein the second region has a third region having a smaller amount of fibers than the average basis weight of the second region .
The nonwoven fabric sheet for interpersonal wiping according to any one of claims 1 to 8 , wherein a stiffness D value according to a TSA softness index is 1.0 mm / N to 3.5 mm / N.