JP6306878B2 - Adhesive tape - Google Patents

Description

  The present invention relates to an adhesive tape.

  In recent years, electronic devices such as mobile phones, smartphones, mobile terminals, digital cameras, video movies, personal computers, and other home appliances have been downsized. Accordingly, constituent members (for example, a battery used as a power source) inside these electronic devices are also reduced in size and thickness.

  As a component member of an electronic device, an adhesive tape is often used when the end of the component member is fixed. The pressure-sensitive adhesive tape used to fix components inside electronic devices that have been reduced in size and thickness is bent according to the shape of the components to be fixed (for example, bent to 90 ° or 180 °). ) Even if it is affixed, a property (repellency resistance) that is difficult to peel off from the adherend is required.

  In addition, since there is a risk of igniting by heat trapped inside the electronic device, the adhesive tape is also required to have flame retardancy (a property that is difficult to burn).

  Conventionally, as an adhesive sheet having flame retardancy, an adhesive sheet containing a halogen-based flame retardant (Patent Document 1) and an adhesive sheet containing a phosphoric acid-based flame retardant are known (Patent Documents 2 to 4). However, halogen-based flame retardants have problems in environmental safety, and phosphoric acid-based flame retardants have problems such as causing contact failure in electrical and electronic equipment. For this reason, the use of flame retardants other than halogen-based and phosphoric acid-based materials has been studied.

JP 2002-173657 A JP-A-11-1669 JP-A-11-323268 Japanese Patent Application Laid-Open No. 11-189753

  In order to obtain sufficient flame retardancy using a flame retardant other than halogen or phosphoric acid, it is necessary to increase the blending amount of the flame retardant. However, when the ratio of the flame retardant contained in the pressure-sensitive adhesive layer is increased, the pressure-sensitive adhesive force is lowered and the repulsion resistance may be lowered. That is, the present situation is that there is no known pressure-sensitive adhesive tape that uses a flame retardant other than a halogen-based or phosphoric acid-based resin and has excellent flame retardancy and excellent adhesiveness and repulsion resistance.

  Accordingly, an object of the present invention is to provide an adhesive tape having excellent flame retardancy and excellent adhesiveness and repulsion resistance.

  Thus, as a result of intensive studies by the present inventors, an adhesive layer containing an acrylic polymer and a metal hydroxide having a small average particle diameter and / or a hydrated metal compound having a small average particle diameter in a specific ratio is provided. The present inventors have found that the pressure-sensitive adhesive tape is excellent in flame retardancy, and is also excellent in adhesiveness and repulsion resistance.

That is, the pressure-sensitive adhesive tape of the present invention contains an acrylic polymer and a metal hydroxide having an average particle size of 10 μm or less and / or a hydrated metal compound having an average particle size of 10 μm or less, and an average particle size of 10 μm or less. The pressure-sensitive adhesive tape has a pressure-sensitive adhesive layer in which the total content of the metal hydroxide and the hydrated metal compound having an average particle size of 10 μm or less is 20 to 330 parts by weight with respect to 100 parts by weight of the acrylic polymer. In the following bending test, the floating distance of the end portion of the adhesive tape is 0.5 mm or less, and in the flame resistance test of UL94 standard, it has flame resistance of VTM-0 or VTM-1. To do.
Bending test: Adhesive layer surface of adhesive tape (length 20 mm x width 40 mm) is applied to surface A of a polypropylene plate (thickness 2 mm), and a 2 kg roller is attached so that the attached part is 3 mm long x 40 mm wide. 1 reciprocating and bonding, the adhesive tape is folded 180 °, and the remaining part of the adhesive tape is bonded to the other surface B of the polypropylene plate by reciprocating a 2 kg roller once, and kept at 23 ° C. for 24 hours. After standing for 24 hours in an atmosphere of 70 ° C., the distance from the end of the adhesive tape where the adhesive tape lifted from the surface A of the polypropylene plate (the lifting distance of the end of the adhesive tape) was measured. To do.

  It is preferable that the said adhesive tape is used for fixation of the film for battery exterior.

  Since the adhesive tape of this invention has the said structure, it has the outstanding flame retardance and is excellent also in adhesiveness and repulsion resistance.

FIG. 1 is a schematic diagram for explaining a method for measuring a floating distance of an end portion of an adhesive tape.

[Adhesive tape]
The pressure-sensitive adhesive tape of the present invention comprises at least an acrylic polymer and a pressure-sensitive adhesive layer containing a hydrated metal compound having an average particle size of 10 μm or less and / or a metal hydroxide having an average particle size of 10 μm or less (“flame retardant adhesive”). It may be referred to as “agent layer”). That is, the pressure-sensitive adhesive tape of the present invention has at least one flame-retardant pressure-sensitive adhesive layer. The pressure-sensitive adhesive tape of the present invention includes a base material, a pressure-sensitive adhesive layer other than the flame-retardant pressure-sensitive adhesive layer, a release liner, and other layers (for example, an intermediate layer, an undercoat layer, etc.) in addition to the flame-retardant pressure-sensitive adhesive layer. You may have. One layer other than the flame-retardant pressure-sensitive adhesive layer may be provided, or two or more layers may be provided.
In this specification, “adhesive tape” includes the meaning of “adhesive sheet”. That is, in this specification, the pressure-sensitive adhesive tape may be a pressure-sensitive adhesive tape having a sheet shape. Moreover, in this specification, the adhesive composition used when forming the said flame-retardant adhesive layer may be called "a flame-retardant adhesive composition."

  The pressure-sensitive adhesive tape of the present invention may be a single-sided pressure-sensitive adhesive tape in which only one side of the tape is the pressure-sensitive adhesive layer surface (adhesive surface) (that is, the flame-retardant pressure-sensitive adhesive layer surface), It may be a double-sided pressure-sensitive adhesive tape that is the pressure-sensitive adhesive layer surface (adhesive surface). Especially, it is preferable that it is a single-sided adhesive tape from a viewpoint of the handleability at the time of fixing a member.

The pressure-sensitive adhesive tape of the present invention may be a pressure-sensitive adhesive tape having a base material (pressure-sensitive adhesive tape with a base material), or may be a pressure-sensitive adhesive tape having no base material (base material-less pressure-sensitive adhesive tape). As the pressure-sensitive adhesive tape of the present invention, for example, (1) a pressure-sensitive adhesive tape (for example, a group consisting only of a flame-retardant pressure-sensitive adhesive layer) that does not have a base material consisting of only the pressure-sensitive adhesive layer including the flame-retardant pressure-sensitive adhesive layer (2) Adhesive tape having the above flame-retardant adhesive layer on at least one side (both sides or one side) of the substrate (single-sided adhesive tape with substrate, double-sided with substrate) Adhesive tape). Especially, the single-sided adhesive tape with a base material which has only the said flame-retardant adhesive layer on the one surface side of a base material from a viewpoint of handling, workability, and design property is preferable. In the case of a double-sided pressure-sensitive adhesive tape with a base material, it is sufficient that the flame-retardant pressure-sensitive adhesive layer is provided on at least one surface side of the base material, and the flame-retardant side is provided on the other surface side of the base material. A pressure-sensitive adhesive layer (other pressure-sensitive adhesive layer) other than the adhesive pressure-sensitive adhesive layer may be provided.
The “base material” does not include a release liner (separator) that is peeled off when the adhesive tape is used.

{Flame-retardant adhesive layer}
In addition to the acrylic polymer, the metal hydroxide having an average particle size of 10 μm or less and / or the hydrated metal compound having an average particle size of 10 μm or less, the flame retardant pressure-sensitive adhesive layer, if necessary. , Dispersants, fluorosurfactants, crosslinking agents, tackifying resins, acrylic oligomers, silane coupling agents, and the like may be included. That is, the flame retardant pressure-sensitive adhesive composition forming the flame retardant pressure-sensitive adhesive layer is the acrylic polymer, the metal hydroxide having an average particle size of 10 μm or less and / or the average particle size of 10 μm or less. In addition to the hydrated metal compound, a dispersant, a fluorosurfactant, a crosslinking agent, a tackifier resin, an acrylic oligomer, a silane coupling agent, and the like may be included as necessary.
The flame retardant pressure-sensitive adhesive layer may have either a single layer or a multilayer.

(Acrylic polymer)
Although it does not specifically limit as said acrylic polymer, For example, the acrylic polymer comprised from the monomer component which has (meth) acrylic-acid alkylester as a main component is preferable. The monomer component may further contain a polar group-containing monomer, a polyfunctional monomer, and the like.
The above acrylic polymers can be used alone or in combination of two or more.
Note that “(meth) acryl” means “acryl” and / or “methacryl” (one or both of “acryl” and “methacryl”), and the same applies to the following. The “alkyl group” means a linear or branched alkyl group unless otherwise specified.
In the present specification, unless otherwise specified, the polar group-containing monomer refers to a polar group-containing monomer excluding a monomer containing a carboxyl group (a monomer having a polar group excluding a carboxy group in the molecule). To do.

Although it does not specifically limit as said (meth) acrylic-acid alkylester which comprises the said acrylic polymer, For example, (meth) acrylic acid methyl, (meth) acrylic acid ethyl, (meth) acrylic acid propyl, (meth) acrylic Isopropyl acid, butyl (meth) acrylate, isobutyl (meth) acrylate, s-butyl (meth) acrylate, t-butyl (meth) acrylate, pentyl (meth) acrylate, isopentyl (meth) acrylate, ( Hexyl (meth) acrylate, heptyl (meth) acrylate, octyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isooctyl (meth) acrylate, nonyl (meth) acrylate, isononyl (meth) acrylate, Decyl (meth) acrylate, isodecyl (meth) acrylate, (me ) Undecyl acrylate, dodecyl (meth) acrylate, tridecyl (meth) acrylate, tetradecyl (meth) acrylate, pentadecyl (meth) acrylate, hexadecyl (meth) acrylate, heptadecyl (meth) acrylate, (meth) Examples thereof include (meth) acrylic acid alkyl esters having an alkyl group having 1 to 20 carbon atoms, such as octadecyl acrylate, nonadecyl (meth) acrylate, and eicosyl (meth) acrylate. Among these, from the viewpoint of easily balancing the adhesive properties, (meth) acrylic acid alkyl esters having an alkyl group having 2 to 12 carbon atoms are preferred, more preferably having an alkyl group having 4 to 9 carbon atoms (meta ) Acrylic acid alkyl ester.
The said (meth) acrylic-acid alkylester can be used individually or in combination of 2 or more types.

  Although the blending ratio (content) of the (meth) acrylic acid alkyl ester in the monomer component constituting the acrylic polymer is not particularly limited, for example, the total amount of monomer component (100% by weight) constituting the acrylic polymer Is preferably 60% by weight or more (for example, 60 to 99% by weight), more preferably 80% by weight or more (for example, 80 to 98% by weight).

The monomer component constituting the acrylic polymer is not particularly limited, but when the material of the adherend is a metal or the like, from the viewpoint of hardly causing corrosion on the adherend (having corrosion resistance), It is preferable that a carboxyl group-containing monomer is not substantially included. Here, the “carboxyl group-containing monomer” is a monomer having one or more carboxyl groups (may be in the form of anhydrides) in one molecule, such as (meth) acrylic acid, itaconic acid, maleic acid, Examples include fumaric acid, crotonic acid, isocrotonic acid, maleic anhydride, itaconic anhydride and the like.
In addition, “substantially free” means that it is not actively blended unless it is inevitably mixed. Specifically, it contains a carboxyl group in the monomer component constituting the acrylic polymer. The monomer content is preferably 0.1% by weight or less, more preferably less than 0.05% by weight, still more preferably less than 0.01% by weight, based on the total amount of monomer components (100% by weight). Say.

  Even if a carboxyl group-containing monomer is added to the monomer component constituting the acrylic polymer, it is difficult to obtain the effect of improving the adhesive strength. Although the cause of these is not clear, the functional group (for example, hydroxyl group) contained in the metal hydroxide and / or hydrated metal compound reacts with the carboxyl group of the carboxyl group-containing monomer, and the acrylic polymer and the metal hydroxide are reacted. This is considered to be because the fluidity is lowered and the wettability is lowered because the product is in a bonded state. Moreover, since it becomes difficult to show the adhesive force improvement effect by the carboxyl group of a carboxyl group-containing monomer, it is thought that an adhesive characteristic falls.

The monomer component constituting the acrylic polymer may further contain a polar group-containing monomer from the viewpoint that appropriate adhesive strength can be obtained. Examples of the polar group-containing monomer include a nitrogen-containing monomer, a hydroxyl group-containing monomer, a sulfonic acid group-containing monomer, and a phosphoric acid group-containing monomer. Among these, a nitrogen-containing monomer and a hydroxyl group-containing monomer are preferable from the viewpoint that high adhesiveness and holding power can be obtained.
The said polar group containing monomer can be used individually or in combination of 2 or more types.

  Examples of the hydroxyl group-containing monomer include 2-hydroxyethyl (meth) acrylate (2HEA), 3-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate (4HBA / 4HBM), and (meth). 6-hydroxyhexyl acrylate, 8-hydroxyoctyl (meth) acrylate, 10-hydroxydecyl (meth) acrylate, 12-hydroxylauryl (meth) acrylate, (4-hydroxymethylcyclohexyl) methyl methacrylate, etc. Can be mentioned. Of these, 2-hydroxyethyl (meth) acrylate and 4-hydroxybutyl (meth) acrylate are preferable from the viewpoint of good wettability to the adherend.

  Examples of the nitrogen-containing monomer include N- (2-hydroxyethyl) (meth) acrylamide, N- (2-hydroxypropyl) (meth) acrylamide, N- (1-hydroxypropyl) (meth) acrylamide, N- (3-hydroxypropyl) (meth) acrylamide, N- (2-hydroxybutyl) (meth) acrylamide, N- (3-hydroxybutyl) (meth) acrylamide, N- (4-hydroxybutyl) (meth) acrylamide, etc. N-hydroxyalkyl (meth) acrylamides; cyclic (meth) acrylamides such as N- (meth) acryloylmorpholine (ACMO / MCMO), N-acryloylpyrrolidine; (meth) acrylamide, N-substituted (meth) acrylamide (N- Ethyl (meth) acrylamide, N-alkyl (meth) acrylamides such as n-butyl (meth) acrylamide; N, N-dimethyl (meth) acrylamide, N, N-diethyl (meth) acrylamide (DEAA / DEMA), N, N-dipropyl (meth) ) N, N-dialkyl such as acrylamide, N, N-diisopropyl (meth) acrylamide, N, N-di (n-butyl) (meth) acrylamide, N, N-di (t-butyl) (meth) acrylamide ( Acyclic (meth) acrylamides such as (meth) acrylamide); N-vinyl-2-pyrrolidone (NVP), N-vinyl-2-piperidone, N-vinyl-3-morpholinone, N-vinyl-2-caprolactam, N- N-vini such as vinyl-1,3-oxazin-2-one and N-vinyl-3,5-morpholinedione Cyclic amides; monomers having amino groups such as aminoethyl (meth) acrylate, N, N-dimethylaminoethyl (meth) acrylate, N, N-dimethylaminopropyl (meth) acrylate; N-cyclohexylmaleimide, N-phenylmaleimide Monomers having a maleimide skeleton such as N-methylitaconimide, N-ethylitaconimide, N-butylitaconimide, N-2-ethylhexylitaconimide, N-laurylitaconimide, N-cyclohexylitaconimide, etc. And so on. Among these, N-vinyl-2-pyrrolidone, N-hydroxyethyl (meth) acrylamide, N- (meth) acryloylmorpholine, N, N-vinyl-2-pyrrolidone, N-hydroxyethyl (meth) acrylamide, from the viewpoint of good initial stickiness (tack) and adhesion reliability N-diethyl (meth) acrylamide is preferred.

  Examples of the sulfonic acid group-containing monomer include styrene sulfonic acid, allyl sulfonic acid, 2- (meth) acrylamide-2-methylpropane sulfonic acid, (meth) acrylamide propane sulfonic acid, sulfopropyl (meth) acrylate, (meth And acryloyloxynaphthalene sulfonic acid.

  As said phosphate group containing monomer, 2-hydroxyethyl acryloyl phosphate etc. can be mentioned, for example.

  The blending ratio of the polar group-containing monomer in the monomer component constituting the acrylic polymer is not particularly limited. For example, 0.1% with respect to the total amount (100% by weight) of the monomer component constituting the acrylic polymer. It is preferably at least 0.5% by weight, more preferably at least 0.5% by weight, even more preferably at least 1% by weight, even more preferably at least 2% by weight, even more preferably at least 3% by weight, particularly preferably at least 5% by weight. Further, the blending ratio of the polar group-containing monomer is not particularly limited. For example, it is preferably 40% by weight or less, more preferably 30% by weight with respect to the total amount of monomer components (100% by weight) constituting the acrylic polymer. % Or less, more preferably 25% by weight or less, and particularly preferably 20% by weight or less. The blending ratio of the polar group-containing monomer in the monomer component is not particularly limited. For example, it is preferably 0.1 to 40% by weight with respect to the total amount of monomer components (100% by weight) constituting the acrylic polymer. . If the blending ratio is less than the above lower limit, the cohesive strength of the flame retardant pressure-sensitive adhesive layer may be reduced, and high holding power may not be obtained. On the other hand, if the blending ratio of the polar group-containing monomer exceeds the above upper limit, the cohesive force of the flame-retardant pressure-sensitive adhesive layer becomes too high, and the adhesive force may be lowered.

  When a polyfunctional monomer is contained in the monomer component constituting the acrylic polymer, a crosslinked structure can be introduced into the acrylic polymer, and a cohesive force necessary as a flame retardant pressure-sensitive adhesive layer can be obtained.

Although it does not specifically limit as said polyfunctional monomer, For example, hexanediol (meth) acrylate, (poly) ethylene glycol di (meth) acrylate, (poly) propylene glycol di (meth) acrylate, neopentyl glycol di (meth) Acrylate, pentaerythritol di (meth) acrylate, pentaerythritol tri (meth) acrylate, dipentaerythritol hexa (meth) acrylate, trimethylolpropane tri (meth) acrylate, tetramethylolmethane tri (meth) acrylate, allyl (meth) acrylate , Vinyl (meth) acrylate, divinylbenzene, epoxy acrylate, polyester acrylate, urethane acrylate, dibutyl (meth) acrylate, hexidyl (meth ) Such as acrylate, and the like.
The said polyfunctional monomer can be used individually or in combination of 2 or more types.

  The blending ratio of the polyfunctional monomer in the monomer component constituting the acrylic polymer is not particularly limited. For example, it is 2% by weight or less based on the total amount (100% by weight) of the monomer component constituting the acrylic polymer. (For example, 0.01 to 2% by weight) is preferable, and 0.02 to 1% by weight is more preferable. When the blending ratio exceeds 2% by weight, the cohesive force of the pressure-sensitive adhesive layer becomes too high, and the adhesive force may be lowered. Moreover, the cohesion force of an adhesive layer may fall that the said mixture ratio is less than 0.01 weight%.

  The monomer component may contain a monomer (other monomer) other than the (meth) acrylic acid alkyl ester, the polar group-containing monomer, and the polyfunctional monomer. By using the above-mentioned other monomers, various properties of the pressure-sensitive adhesive and the structure of the acrylic polymer can be more appropriately controlled.

Although it does not specifically limit as said other monomer, For example, monomers which have epoxy groups, such as glycidyl (meth) acrylate and allyl glycidyl ether; (meth) acrylate 2-methoxyethyl, (meth) acrylate 3-methoxypropyl Monomers having an alkoxy group such as methoxyethylene glycol (meth) acrylate and methoxypolypropylene glycol (meth) acrylate; monomers having a cyano group such as acrylonitrile and methacrylonitrile; styrene monomers such as styrene and α-methylstyrene Α-olefins such as ethylene, propylene, isoprene, butadiene and isobutylene; modules having an isocyanate group such as 2-isocyanatoethyl acrylate and 2-isocyanatoethyl methacrylate; Nomer; vinyl ester monomers such as vinyl acetate and vinyl propionate; vinyl ether monomers such as vinyl ether; (meth) acrylic acid esters having a heterocyclic ring such as tetrahydrofurfuryl (meth) acrylate; halogens such as fluorine (meth) acrylate Monomers having atoms; Monomers having alkoxysilyl groups such as 3-methacryloxypropyltrimethoxysilane and vinyltrimethoxysilane; Monomers having siloxane bonds such as silicone (meth) acrylate; Alkyls having an alkyl group having 21 or more carbon atoms (Meth) acrylates; cyclopentyl (meth) acrylates, cyclohexyl (meth) acrylates, bornyl (meth) acrylates, isobornyl (meth) acrylates and other alicyclic hydrocarbons (Meth) acrylate having a phenyl group; (meth) acrylate having an aromatic hydrocarbon group such as phenyl (meth) acrylate, benzyl (meth) acrylate, phenoxyethyl (meth) acrylate, phenoxydiethylene glycol (meth) acrylate, etc. . Especially, the monomer (especially 2-methoxyethyl acrylate) which has an alkoxy group from a viewpoint that the wettability of a flame-retardant adhesive layer can be improved is preferable.
These other monomers may be used alone or in combination of two or more.

  The blending ratio of the other monomer in the monomer component constituting the acrylic polymer is not particularly limited. For example, it is 30% by weight or less with respect to the total amount (100% by weight) of the monomer component constituting the acrylic polymer. Is more preferable, and more preferably 20% by weight or less. Especially, when using the monomer which has an alkoxy group, although it does not specifically limit, The compounding ratio is 5 weight% or more (for example, 5 for example) with respect to the monomer component whole quantity (100 weight%) which comprises the said acrylic polymer. -20% by weight), more preferably 8% by weight or more (for example, 8-15% by weight).

  The acrylic polymer can be prepared by polymerizing the monomer component by a known or conventional polymerization method. The polymerization method of the acrylic polymer is not particularly limited, and examples thereof include a solution polymerization method, a bulk polymerization method, an emulsion polymerization method, various radical polymerization methods (active energy ray polymerization methods, etc. Among them, cost and productivity From the viewpoint, a solution polymerization method is preferable.

  The solution polymerization method is not particularly limited, and examples thereof include a method in which the monomer component, the polymerization initiator, etc. are dissolved in a solvent and polymerized by heating to obtain an acrylic polymer solution containing an acrylic polymer. .

  Various common solvents can be used as the solvent used in the solution polymerization method. Examples of such a solvent (polymerization solvent) include aromatic hydrocarbons such as toluene, benzene and xylene; esters such as ethyl acetate and n-butyl acetate; aliphatic carbonization such as n-hexane and n-heptane. Examples of the organic solvents include hydrogens; alicyclic hydrocarbons such as cyclohexane and methylcyclohexane; ketones such as methyl ethyl ketone and methyl isobutyl ketone. The said solvent can be used individually or in combination of 2 or more types.

  Although the blending ratio of the solvent is not particularly limited, for example, it is preferably 10 to 1000 parts by weight, more preferably 50 to 500 parts by weight with respect to the total amount of monomer components (100 parts by weight) constituting the acrylic polymer. is there.

The polymerization initiator used in the solution polymerization method is not particularly limited, and examples thereof include a peroxide polymerization initiator and an azo polymerization initiator. The peroxide-based polymerization initiator is not particularly limited, and examples thereof include peroxycarbonate, ketone peroxide, peroxyketal, hydroperoxide, dialkyl peroxide, diacyl peroxide, and peroxyester. More specifically, benzoyl peroxide, t-butyl hydroperoxide, di-t-butyl peroxide, t-butyl peroxybenzoate, dicumyl peroxide, 1,1-bis (t-butylperoxy)- 3,3,5-trimethylcyclohexane, 1,1-bis (t-butylperoxy) cyclododecane and the like can be mentioned. The azo polymerization initiator is not particularly limited. For example, 2,2′-azobisisobutyronitrile, 2,2′-azobis-2-methylbutyronitrile, 2,2′-azobis (2 , 4-dimethylvaleronitrile), 2,2′-azobis (2-methylpropionic acid) dimethyl, 2,2′-azobis (4-methoxy-2,4-dimethylvaleronitrile), 1,1′-azobis ( Cyclohexane-1-carbonitrile), 2,2'-azobis (2,4,4-trimethylpentane), 4,4'-azobis-4-cyanovaleric acid, 2,2'-azobis (2-amidinopropane) Dihydrochloride, 2,2'-azobis [2- (5-methyl-2-imidazolin-2-yl) propane] dihydrochloride, 2,2'-azobis (2-methylpro Onamidine) disulfate, 2,2'-azobis (N, N'-dimethyleneisobutylamidine) hydrochloride, 2,2'-azobis [N- (2-carboxyethyl) -2-methylpropionamidine] hydrate , Etc.
The said polymerization initiator can be used individually or in combination of 2 or more types.

  The blending ratio of the polymerization initiator is not particularly limited, but is preferably 0.01 to 5 parts by weight, more preferably 0.005 parts by weight with respect to the total amount of monomer components (100 parts by weight) constituting the acrylic polymer. 05 to 3 parts by weight.

  Although it does not specifically limit as heating temperature at the time of superposing | polymerizing by heating with the said solution polymerization method, For example, 50-80 degreeC is mentioned. Although it does not specifically limit as heating time, For example, 1 to 24 hours is mentioned.

Although it does not specifically limit as a viscosity of the acrylic polymer solution containing the said acrylic polymer, For example, 0.1-100 Pa.s is preferable, More preferably, it is 0.5-50 Pa.s. When the viscosity is 0.1 Pa · s or more, it is easy to uniformly mix the metal hydroxide and / or the hydrated metal compound, and a uniform pressure-sensitive adhesive layer is obtained when the pressure-sensitive adhesive layer is applied. Therefore, an adhesive tape having further excellent flame retardancy, adhesiveness, and repulsion resistance can be obtained. When the viscosity is 100 Pa · s or less, the coating property is excellent.
In the present specification, the viscosity means a rotor: No. using a BH viscometer as a viscometer. The viscosity measured under the conditions of 5 rotors, rotation speed: 10 rpm, measurement temperature: 30 ° C.

The glass transition temperature (Tg) of the acrylic polymer is not particularly limited, but is preferably, for example, −10 ° C. or lower (for example, −70 ° C. to −10 ° C.), more preferably −20 ° C. or lower (for example, −70). ° C to -20 ° C). That is, it is preferable to adjust the composition and blending amount of the monomer component so that the Tg of the acrylic polymer falls within the range.
Here, the Tg of the acrylic polymer refers to a value obtained from the Fox equation based on the Tg of the homopolymer of each monomer constituting the monomer component and the weight fraction (copolymerization composition) of the monomer. The value of Tg of the homopolymer can be obtained from various known materials (such as “Adhesion Technology Handbook” of Nikkan Kogyo Shimbun).

(Metal hydroxide, hydrated metal compound)
As the metal hydroxide and the hydrated metal compound is not particularly limited, for example, aluminum hydroxide _{[Al 2 O 3 · 3H 2} O; or Al (OH) _3], boehmite [Al ₂ O ₃ · H ₂ O; or AlOOH], magnesium hydroxide [MgO.H ₂ O; or Mg (OH) ₂ ], calcium hydroxide [CaO.H ₂ O; or Ca (OH) ₂ ], zinc hydroxide [Zn (OH ₂ ), silicic acid [H ₄ SiO ₄ ; or H ₂ SiO ₃ ; or H ₂ Si ₂ O ₅ ], iron hydroxide [Fe ₂ O ₃ .H ₂ O or 2FeO (OH)], copper hydroxide [Cu (OH) ₂ ], barium hydroxide [BaO · H ₂ O; or BaO · 9H ₂ O], zirconium oxide hydrate [ZrO · nH ₂ O], tin oxide hydrate [SnO · H ₂ O], basic magnesium carbonate [3MgCO ₃ · Mg ( _{H) 2 · 3H 2 O]} , hydrotalcite _{[6MgO · Al 2 O 3 ·} H 2 O], dawsonite _{[Na 2 CO 3 · Al 2} O 3 · nH 2 O], borax [Na ₂ O · B ₂ O ₅ .5H ₂ O], zinc borate [2ZnO.3B ₂ O ₅ .3.5H ₂ O] and the like. Of these, aluminum hydroxide and magnesium hydroxide are preferred because excellent flame retardancy can be obtained.
The hydrated metal compound and the metal hydroxide may be used alone or in combination of two or more.

  The shape of the metal hydroxide and the hydrated metal compound is not particularly limited, and may be a bulk shape, a needle shape, a plate shape, or a layer shape. The bulk shape includes, for example, a spherical shape, a rectangular parallelepiped shape, a crushed shape, or a deformed shape thereof.

Generally, it is known that flame retardancy is improved when a metal hydroxide or a hydrated metal compound is contained in the pressure-sensitive adhesive layer. However, as the proportion of the metal hydroxide and hydrated metal compound contained in the pressure-sensitive adhesive layer increases, the flame retardancy improves, but compared to the pressure-sensitive adhesive layer that does not contain the metal hydroxide and hydrated metal compound, It is also known that the adhesive strength decreases. On the other hand, when the ratio of the metal hydroxide and the hydrated metal compound contained in the pressure-sensitive adhesive layer is small, the flame retardancy effect cannot be obtained. That is, it has been recognized that it is difficult to achieve both flame retardancy and adhesiveness using a metal hydroxide and / or a hydrated metal compound.
When the average particle size of the metal hydroxide and / or the hydrated metal compound contained in the flame retardant pressure-sensitive adhesive layer is small (for example, 0.1 to 10 μm, etc.), In addition, the inventors found that the decrease in adhesive strength is small as compared with the case of adding a metal hydroxide and / or a hydrated metal compound having a large average particle diameter. In particular, when the average particle size is 10 μm or less (particularly 8 μm or less), the adhesive strength of the flame retardant pressure-sensitive adhesive layer is higher than the pressure-sensitive adhesive strength of a pressure-sensitive adhesive layer not containing a metal hydroxide and a hydrated metal compound. There is a case. That is, when a metal hydroxide and / or a hydrated metal compound having an average particle size of 10 μm or less (especially 8 μm or less) is used, a pressure-sensitive adhesive formed from a composition containing no metal hydroxide and hydrated metal compound. There are cases where flame retardancy and adhesive strength are superior to the layer.

The average particle diameter (average particle diameter) of the metal hydroxide and the hydrated metal compound is 10 μm or less (for example, 0.1 to 10 μm) from the viewpoint that both flame retardancy and adhesiveness can be achieved. In particular, even when a metal hydroxide and / or a hydrated metal compound is added, the adhesive strength is less likely to be lowered, and the adhesive strength is higher than that of an adhesive layer not containing a metal hydroxide and a hydrated metal compound. From the viewpoint that there is, it is preferably 8 μm or less (for example, 0.1 to 8 μm), and more preferably 1 μm or less (for example, 0.1 to 1 μm).
The average particle size is a volume-based value obtained by a particle size distribution measurement method in the laser scattering method. Specifically, it is calculated | required by measuring D50 value with a laser scattering type particle size distribution system.

  The content (total content) of the metal hydroxide having an average particle diameter of 10 μm or less and / or the hydrated metal compound having an average particle diameter of 10 μm or less is the acrylic polymer in the flame-retardant pressure-sensitive adhesive layer. The amount is 20 to 330 parts by weight, preferably 50 to 300 parts by weight, more preferably 60 to 300 parts by weight, and still more preferably 100 to 300 parts by weight with respect to 100 parts by weight. When the content is 20 parts by weight or more, the flame retardancy is good. When the content is 330 parts by weight or less, the adhesiveness and repulsion resistance are excellent. Moreover, the adhesiveness (tack) at the time of sticking is also excellent. Since the flame-retardant pressure-sensitive adhesive layer is more flammable as the thickness is thinner, when the thickness of the flame-retardant pressure-sensitive adhesive layer is 10 to 80 μm (particularly 10 to 50 μm), for example, the content is 100 to 100 μm. The amount is preferably 300 parts by weight.

  The metal hydroxide and / or the hydrated metal compound has an average particle size of 10 μm or less (preferably 8 μm or less, preferably from the viewpoint of further excellent flame retardancy, further adhesiveness, and further excellent repulsion resistance. More preferably 5 μm or less) metal hydroxide and / or a hydrated metal compound having an average particle size of 10 μm or less (preferably 8 μm or less, more preferably 5 μm or less) is added to the acrylic resin in the flame-retardant pressure-sensitive adhesive layer. It is preferable to contain 20 to 330 parts by weight (preferably 50 to 300 parts by weight, more preferably 100 to 300 parts by weight) with respect to 100 parts by weight of the base polymer.

  The metal hydroxide and the hydrated metal compound may be used in combination of two or more kinds of the metal hydroxide and / or the hydrated metal compound having different average particle diameters. When two or more kinds of the above metal hydroxides and / or hydrated metal compounds having different average particle diameters are used in combination, for example, a combination of particles having an average particle diameter of 5 μm or more and particles having an average particle diameter of less than 5 μm Are preferably used. In this way, by using the metal hydroxide and / or the hydrated metal compound having different average particle sizes in combination, the metal hydroxide and / or the hydrated metal compound in the flame-retardant pressure-sensitive adhesive layer, It can be packed more densely. When the metal hydroxide and / or the hydrated metal compound are densely packed, the fluidity of the pressure-sensitive adhesive layer is increased and the viscosity is decreased, so that the adhesion to the adherend is further improved (adhesive strength) May be further improved). In order to obtain such an effect, for example, the blending ratio (weight ratio) of particles having an average particle diameter of 5 μm or more and particles having an average particle diameter of less than 5 μm is preferably 1:10 to 10: 1, more preferably. Is 1: 5 to 5: 1, more preferably 1: 2 to 2: 1.

  Examples of the metal hydroxide and the hydrated metal compound include a metal hydroxide having an average particle size of 10 μm or less and / or a hydrated metal compound having an average particle size of 10 μm or less and a metal having an average particle size of greater than 10 μm. A hydroxide and / or a hydrated metal compound having an average particle size of more than 10 μm may be used in combination. In this case, from the viewpoint of not impairing the adhesive effect, the ratio of the metal hydroxide having an average particle diameter of 10 μm or less and the hydrated metal compound having an average particle diameter of 10 μm or less is included in the flame retardant adhesive layer. It is preferably 50% by weight or more (for example, 50 to 100% by weight), more preferably 70% by weight or more (for example, 70% by weight) with respect to the total amount (100% by weight) of the metal hydroxide and hydrated metal compound. -100% by weight), more preferably 90% by weight or more (for example, 90-100% by weight).

  As the metal hydroxide having an average particle diameter of 10 μm or less and the hydrated metal compound having an average particle diameter of 10 μm or less, a general commercial product can be used. H-32 ”(average particle size 8 μm, Showa Denko), trade name“ Hijilite H-42 ”(average particle size 1 μm, Showa Denko), trade name“ Heidilite H-43M ”(average particle size) 0.8 μm, manufactured by Showa Denko Co., Ltd.), trade name “B103ST” (average particle diameter 8 μm, manufactured by Nippon Light Metal Co., Ltd.), etc. As magnesium hydroxide, the trade name “KISUMA 5A” (average particle diameter 1 μm, Kyowa Chemical Industry) And a trade name “ECOMAG Z-10” (average particle diameter of 1.4 μm, manufactured by Tateho Chemical Co., Ltd.) can be used.

(Other flame retardants)
In order to further improve the flame retardancy, the flame retardant pressure-sensitive adhesive layer further includes a flame retardant other than the metal hydroxide and the hydrated metal compound (other difficulty A flame retardant). Examples of the other flame retardants include metal carbonates such as magnesium carbonate-calcium carbonate, calcium carbonate, barium carbonate, and dolomite; barium metaborate; magnesium oxide; zinc borate; tin compound; carbon black; Can be mentioned.
These other flame retardants can be used alone or in combination of two or more.

  Although content of the said other flame retardant is not specifically limited, For example, 100 weight part or less (for example, 1-100 weight part) with respect to 100 weight part of said acrylic polymers in the said flame retardant adhesive layer, Or 5 weight part or less is mentioned. When the content of the other flame retardants exceeds 100 parts by weight, the tackiness may be significantly reduced due to the bleeding out of the monomer.

  When the metal hydroxide and / or the hydrated metal compound and the other flame retardant are used in combination, the flame retardant pressure-sensitive adhesive layer includes a total amount thereof (the metal hydroxide, the hydrated metal). Although the total content of the compound and the other flame retardant is not particularly limited, for example, 30 to 350 parts by weight (or 60 to 60 parts by weight) with respect to 100 parts by weight of the acrylic polymer in the flame retardant pressure-sensitive adhesive layer. 310 parts by weight, or 110 to 310 parts by weight). When the total amount is 30 to 350 parts by weight, high flame retardancy can be obtained. On the other hand, when the total amount exceeds 350 parts by weight, the flexibility is lowered, and the adhesive force and holding force may be reduced. If the total amount is lower than 30 parts by weight, sufficient flame retardancy may not be obtained.

  When the metal hydroxide and / or the hydrated metal compound is used in combination with the other flame retardant, the metal hydroxide and / or the average particle size is 10 μm or less. The ratio of the hydrated metal compound is not particularly limited as long as it does not adversely affect the adhesiveness. For example, the total amount of the metal hydroxide, the hydrated metal compound, and the other flame retardant (100 wt. %) Is 50% by weight or more (or 60% by weight or more, or 70% by weight or more).

(Dispersant)
In the flame-retardant pressure-sensitive adhesive layer, a dispersant is further added to stably disperse the metal hydroxide and / or the hydrated metal compound within a range not impairing the effects of the present invention. It may be included.
Although it does not specifically limit as said dispersing agent, For example, phosphate ester is used suitably. Phosphoric acid esters include polyoxyethylene alkyl (or alkylallyl) ether or polyoxyethylene alkyl aryl ether phosphoric acid monoester, polyoxyethylene alkyl ether or polyoxyethylene alkyl aryl ether phosphoric acid diester, phosphoric acid triester Or a derivative thereof. Among these, it is preferable to use a phosphoric acid monoester or a phosphoric acid diester of polyoxyethylene alkyl ether or polyoxyethylene alkyl aryl ether.
The said dispersing agent can be used individually or in combination of 2 or more types.

  Although the content of the dispersant is not particularly limited, for example, 0.01 to 10 parts by weight is preferable with respect to 100 parts by weight of the acrylic polymer in the flame retardant pressure-sensitive adhesive layer, and more preferably 0. 05 to 5 parts by weight, more preferably 0.1 to 3 parts by weight.

  As the dispersant, a general commercial product can be used. For example, a trade name “Plisurf A212E” (Daiichi Kogyo Seiyaku Co., Ltd.), a trade name “Plisurf A210G” (Daiichi Kogyo Seiyaku Co., Ltd.), Name “Plisurf A212C” (Daiichi Kogyo Seiyaku Co., Ltd.), Product Name “Plisurf A210F” (Daiichi Kogyo Seiyaku Co., Ltd.), Product Name “Phosphanol RE610” (Toho Chemical Co., Ltd.) Examples include “Fanol RS710” (manufactured by Toho Chemical Co., Ltd.), trade name “Phosphanol RS610” (manufactured by Toho Chemical Co., Ltd.), and the like.

(Fluorosurfactant)
The flame retardant pressure-sensitive adhesive layer may further contain a fluorine-based surfactant. By using the fluorosurfactant, the degree of adhesion and frictional resistance between the acrylic polymer and the metal hydroxide and / or the hydrated metal compound may be reduced, and the stress dispersibility may be improved. . Therefore, the adhesive tape of the present invention may have higher adhesiveness.

The fluorine-based surfactant is not particularly limited, but for example, a fluorine-based surfactant having an oxy C _2-3 alkylene group and a fluorinated hydrocarbon group in the molecule is preferable. Among these, from the viewpoint of dispersibility with respect to acrylic polymers, the fluorosurfactant is a fluorononionic surfactant having an oxy C _2-3 alkylene group and a fluorinated hydrocarbon group in the molecule. Is preferred.
In addition, the said fluorosurfactant can be used individually or in combination of 2 or more types.

Although it does not restrict | limit especially as said fluorinated hydrocarbon group, For example, a perfluoro group is preferable. The perfluoro group may be monovalent or divalent or higher. The fluorinated hydrocarbon group may have a double bond or a triple bond, and may be a straight chain or a branched structure or a cyclic structure. Although carbon number of the said fluorinated hydrocarbon group is not specifically limited, For example, 1 or 2 or more are preferable, More preferably, it is 3-30, More preferably, it is 4-20. When it has a fluorinated hydrocarbon group, when the said flame-retardant adhesive layer contains a bubble, the effect which improves bubble mixing property and bubble stability is also acquired.
1 type of the said fluorinated hydrocarbon group may be introduce | transduced in the said fluorine-type surfactant molecule | numerator, and 2 or more types may be introduce | transduced.

The oxy C _2-3 alkylene group is represented by the formula: —R—O— (R is a linear or branched alkylene group having 2 or 3 carbon atoms). The oxy C _2-3 alkylene group is not particularly limited, and examples thereof include an oxyethylene group (—CH ₂ CH ₂ O—) and an oxypropylene group [—CH ₂ CH (CH ₃ ) O—]. The oxy C _2-3 alkylene group may be any form such as an alcohol having a hydrogen atom bonded to a terminal oxygen atom, an ether bonded to another hydrocarbon group, or an ester bonded to another hydrocarbon group via a carbonyl group. But you can. Moreover, the form which has this structure in a part of cyclic structure, such as cyclic ethers and lactones, may be sufficient.
One kind of the oxy C _2-3 alkylene group may be introduced into the fluorine-based surfactant molecule, or two or more kinds thereof may be introduced.

The fluorosurfactant is not particularly limited, and is obtained, for example, by polymerizing a monomer component containing a monomer having an oxy C _2-3 alkylene group and a monomer having a fluorinated hydrocarbon group. A copolymer is mentioned. When the fluorosurfactant is a copolymer, it may be, for example, a block copolymer or a graft copolymer.

The block copolymer (copolymer having an oxy C _2-3 alkylene group and a fluorinated hydrocarbon group in the main chain) is not particularly limited, but examples thereof include polyoxyethylene perfluoroalkyl ether, polyoxyethylene peroxy ether, and the like. Fluoroalkylate, polyoxypropylene perfluoroalkyl ether, polyoxyisopropylene perfluoroalkyl ether, polyoxyethylene sorbitan perfluoroalkylate, polyoxyethylene polyoxypropylene block copolymer perfluoroalkylate, polyoxyethylene glycol perfluoroalkyl Chelate etc. are mentioned.

The graft copolymer (a copolymer having an oxy C _2-3 alkylene group and a fluorinated hydrocarbon group in the side chain) is not particularly limited, but for example, a vinyl compound having at least a polyoxyalkylene group and fluorine And a copolymer obtained by polymerizing a monomer component containing a vinyl compound having a functionalized hydrocarbon group, and an acrylic copolymer is particularly preferable. Examples of the vinyl compound having a polyoxyalkylene group include polyoxyalkylene (meth) acrylates such as polyoxyethylene (meth) acrylate, polyoxypropylene (meth) acrylate, and polyoxyethylene polyoxypropylene (meth) acrylate. Is mentioned. Examples of the vinyl compound having a fluorinated hydrocarbon group include perfluoroalkyl (meth) acrylates such as perfluorobutyl (meth) acrylate, perfluoroisobutyl (meth) acrylate, and perfluoropentyl (meth) acrylate. (Meth) acrylic acid ester containing a fluorinated hydrocarbon is mentioned.

In addition to the oxy C _2-3 alkylene group and the fluorinated hydrocarbon group, the above-mentioned fluorosurfactant contains an alicyclic hydrocarbon group, an aromatic group in the molecule within a range that does not impair dispersibility in the acrylic polymer. It may have various functional groups such as an aromatic hydrocarbon group, a carboxyl group, a sulfonic acid group, a cyano group, an amide group, and an amino group. For example, when the fluorosurfactant is a vinyl copolymer, the monomer component can be copolymerized with a vinyl compound having a polyoxyalkylene group and a vinyl compound having a fluorinated hydrocarbon group as a monomer component. May be used.
Such copolymerizable monomers can be used alone or in combination of two or more.

Examples of the copolymerizable monomer component include (meth) acrylic acid C _1-20 alkyl esters such as undecyl (meth) acrylate and dodecyl (meth) acrylate; alicyclic carbonization such as cyclopentyl (meth) acrylate. A (meth) acrylic acid ester having a hydrogen group; a (meth) acrylic acid ester having an aromatic hydrocarbon group such as phenyl (meth) acrylate is preferably used. In addition, carboxyl group-containing monomers such as maleic acid and crotonic acid; sulfonic acid group-containing monomers such as sodium vinyl sulfonate; aromatic vinyl compounds such as styrene and vinyl toluene; olefins and dienes such as ethylene and butadiene Vinyl ethers such as vinyl alkyl ethers; amide group-containing monomers such as acrylamide; amino group-containing monomers such as (meth) acryloylmorpholine; glycidyl group-containing monomers such as methyl glycidyl (meth) acrylate; 2 -Isocyanate group-containing monomers such as methacryloyloxyethyl isocyanate; polyfunctional copolymerizable monomers (polyfunctional monomers) such as dipentaerythritol hexa (meth) acrylate and divinylbenzene.

  The weight average molecular weight of the fluorosurfactant is not particularly limited. For example, when it is less than 20000 (for example, 500 or more and less than 20000), the acrylic polymer, the metal hydroxide and / or the hydration are used. The effect of reducing adhesion between metal compounds and frictional resistance is high. Furthermore, when a fluorosurfactant having a weight average molecular weight of 20000 or more (for example, 20000 to 100000, preferably 22000 to 80000, more preferably 24000 to 60000) is used in combination, the mixing property of the bubbles and the stability of the mixed bubbles are increased. .

  The amount of use (solid content) of the fluorosurfactant is not particularly limited, but is preferably 0.01 to 5 parts by weight with respect to 100 parts by weight of the total monomer components for forming the acrylic polymer, for example. More preferably, it can be selected in the range of 0.02 to 3 parts by weight, more preferably 0.03 to 2 parts by weight. If the amount used is less than 0.01 parts by weight, the stability of the bubbles is difficult to obtain, and if it exceeds 5 parts by weight, the adhesive performance may be lowered.

  The flame-retardant pressure-sensitive adhesive layer has a smaller content than when the dispersant or the fluorosurfactant is used alone, and is stable without aggregation of the metal hydroxide and / or the hydrated metal compound. In view of improving the stress dispersibility of the flame retardant pressure-sensitive adhesive layer and expecting higher adhesiveness, the dispersant and the fluorosurfactant may be used in combination. . When the dispersant and the fluorosurfactant are used in combination, the blending ratio is not particularly limited, but the ratio of the dispersant to the fluorosurfactant (weight ratio) is 1:20 to 20: 0.01 is preferable, More preferably, it is 1: 10-10: 0.01, More preferably, it is 1: 5-5: 0.01.

Specific examples of the fluorosurfactant having an oxy C _2-3 alkylene group and a fluorinated hydrocarbon group and having a weight average molecular weight of less than 20,000 include a trade name “Futgent 251” (manufactured by Neos Co., Ltd.), Name “FTX-218” (manufactured by Neos Co., Ltd.), product name “Megafuck F-477” (manufactured by DIC), product name “Megafuck F-470” (manufactured by DIC), product name “Surflon S-381” (AGC Seimi Chemical Co., Ltd.), trade name “Surflon S-383” (AGC Seimi Chemical Co., Ltd.), trade name “Surflon S-393” (AGC Seimi Chemical Co., Ltd.), trade name “Surflon KH-20” ( AGC Seimi Chemical Co., Ltd.) and trade name “Surflon KH-40” (manufactured by AGC Seimi Chemical Co., Ltd.). Specific examples of the fluorosurfactant having an oxy C _2-3 alkylene group and a fluorinated hydrocarbon group and having a weight average molecular weight of 20000 or more include a trade name “F-top EF-352” (Mitsubishi Materials Electronic Chemicals). Product name “F-top EF-801” (manufactured by Mitsubishi Materials Electronic Chemicals), product name “Unidyne TG-656” (manufactured by Daikin Industries, Ltd.), and the like.

(Crosslinking agent)
The flame retardant pressure-sensitive adhesive layer may further contain a crosslinking agent from the viewpoint that the cohesive force of the flame retardant pressure-sensitive adhesive layer can be adjusted. As the crosslinking agent, a known and commonly used crosslinking agent can be used. For example, epoxy crosslinking agent, isocyanate crosslinking agent, silicone crosslinking agent, oxazoline crosslinking agent, aziridine crosslinking agent, silane crosslinking agent, alkyl Examples include etherified melamine-based crosslinking agents and metal chelate-based crosslinking agents. Of these, isocyanate crosslinking agents and epoxy crosslinking agents are preferred.

  Examples of the isocyanate crosslinking agent include tolylene diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, xylylene diisocyanate, hydrogenated xylylene diisocyanate, diphenylmethane diisocyanate, hydrogenated diphenylmethane diisocyanate, tetramethylxylylene diisocyanate, naphthalene diisocyanate, triphenyl. Examples include methane triisocyanate, polymethylene polyphenyl isocyanate, and adducts of these with polyols such as trimethylolpropane. A compound having at least one isocyanate group and one or more unsaturated bonds in one molecule, specifically, 2-isocyanatoethyl (meth) acrylate or the like can also be used.

  Examples of the epoxy crosslinking agent include bisphenol A, epichlorohydrin type epoxy resin, ethylene glycidyl ether, polyethylene glycol diglycidyl ether, glycerin diglycidyl ether, glycerin triglycidyl ether, 1,6-hexanediol glycidyl ether, Methylolpropane triglycidyl ether, diglycidyl aniline, diamine glycidyl amine, N, N, N ′, N′-tetraglycidyl-m-xylylenediamine and 1,3-bis (N, N′-diamine glycidylaminomethyl) cyclohexane Etc.

  Although content of the said crosslinking agent is not specifically limited, For example, 0.01-5 weight part is preferable with respect to 100 weight part of said acrylic polymers in the said flame-retardant adhesive layer, More preferably, it is 0.00. The amount is from 01 to 3 parts by weight, more preferably from 0.01 to 2 parts by weight. If the content exceeds 5 parts by weight, flexibility may not be obtained, and if it is less than 0.01 parts by weight, cohesion may not be obtained.

(Tackifying resin)
The flame retardant pressure-sensitive adhesive layer may further contain a tackifier resin from the viewpoint of further improving the tackiness. In particular, when the monomer component constituting the acrylic polymer does not contain a carboxyl group-containing monomer and it is difficult to obtain high adhesive strength, the flame-retardant pressure-sensitive adhesive layer is thin (for example, 70 μm or less (particularly 50 μm or less)). In the case of the above, it is preferable that a tackifying resin is contained. The tackifying resin is not particularly limited. However, when an acrylic polymer is obtained by copolymerizing monomer components by irradiating ultraviolet rays, a hydrogenated type adhesive is used because it is difficult to inhibit polymerization even when used together. It is preferable to use an imparting resin. Examples of hydrogenated tackifying resins include derivatives obtained by hydrogenating tackifying resins such as rosin resins, petroleum resins, terpene resins, coumarone-indene resins, styrene resins, alkylphenol resins, xylene resins ( And hydrogenated rosin resins, hydrogenated petroleum resins, hydrogenated terpene resins, and the like. Among these, a hydrogenated rosin resin is preferable. Examples of the hydrogenated rosin-based tackifying resin include modified rosin obtained by modifying unmodified rosin (raw rosin) such as gum rosin, wood rosin and tall oil rosin by hydrogenation.

  Although the softening point of the said tackifying resin is not specifically limited, For example, 80-200 degreeC is preferable, More preferably, it is 90-200 degreeC. When the softening point of the tackifying resin is within the range, the cohesive force is further improved.

  Although content of the said tackifying resin is not specifically limited, 1-50 weight part is preferable with respect to 100 weight part of said acrylic polymers in the said flame-retardant adhesive layer, More preferably, 2-40 weight part More preferably, it is 3 to 30 parts by weight. When the content exceeds 50 parts by weight, the cohesive force may be reduced, and when it is less than 1 part by weight, the effect of improving the adhesive strength may not be obtained.

  As the tackifying resin, a general commercial product can be used. For example, a trade name “Super Ester A-100” (softening point 95 to 105 ° C., manufactured by Arakawa Chemical Industries), a trade name “Super Ester A-125”. Hydrogenated rosin resins such as “(softening point 120 to 130 ° C., manufactured by Arakawa Chemical Industries, Ltd.)” can be used.

(Acrylic oligomer)
The flame retardant pressure-sensitive adhesive layer may further contain an acrylic oligomer from the viewpoint that the adhesiveness is further improved. The acrylic oligomer is a polymer having a glass transition temperature (Tg) higher than that of the acrylic polymer and a small weight average molecular weight, functions as a tackifier resin, and inhibits polymerization during polymerization using ultraviolet rays. It has the advantage of being difficult to wake up.

(Silane coupling agent)
The flame retardant pressure-sensitive adhesive layer has improved adhesion and durability, and improved affinity between the hydrated metal compound and / or the metal hydroxide and the acrylic polymer. From the viewpoint, a silane coupling agent may be further included.

As said silane coupling agent, a well-known thing can be used suitably, for example, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropylmethyldiethoxysilane Epoxy group-containing silane coupling agents such as 2- (3,4-epoxycyclohexyl) ethyltrimethoxysilane; 3-aminopropyltrimethoxysilane, N-2- (aminoethyl) -3-aminopropylmethyldimethoxysilane, Amino group-containing silane coupling agents such as 3-triethoxysilyl-N- (1,3-dimethylbutylidene) propylamine; (methacryloxypropyltrimethoxysilane, 3-methacryloxypropyltriethoxysilane, etc. ) Acrylic group-containing silane coupling Agents; such Inshianeto group-containing silane coupling agents such as 3-isocyanate propyl triethoxysilane and the like.
The silane coupling agent may be used alone or in combination of two or more.

  Although content of the said silane coupling agent is not specifically limited, For example, 0.01-10 weight part is preferable with respect to 100 weight part of said acrylic polymers in the said flame-retardant adhesive layer, More preferably It is 0.02-5 weight part, More preferably, it is 0.05-2 weight part. By using the silane coupling agent in the above range, the cohesive strength and durability are further improved. If the content is less than 0.01 parts by weight, the surface of the hydrated metal compound and / or the metal hydroxide contained in the flame retardant pressure-sensitive adhesive layer cannot be coated, and the affinity may not be improved. is there.

(Bubbles)
The flame-retardant pressure-sensitive adhesive layer may be a flame-retardant pressure-sensitive adhesive layer containing bubbles (sometimes referred to as “bubble-containing flame-retardant pressure-sensitive adhesive layer”). The bubble-containing flame-retardant pressure-sensitive adhesive layer can impart thickness and cushioning properties to the pressure-sensitive adhesive layer, and the performance of filling the unevenness on the surface of the adherend, that is, the unevenness absorbability (unevenness followability) is improved.

(Other additives)
In the flame retardant pressure-sensitive adhesive layer, the acrylic polymer, the hydrated metal compound and / or the metal hydroxide, the dispersant, the other flame retardant, the fluorine-based surfactant, the crosslinking agent, In addition to the tackifying resin, the acrylic oligomer, and the silane coupling agent, other additives may be included depending on the application. As said other additive, a plasticizer, a filler, anti-aging agent, a coloring agent (a pigment, dye, etc.) etc. are mentioned, for example.

  Although the thickness of the said flame-retardant adhesive layer is not specifically limited, For example, 10-250 micrometers is preferable, More preferably, it is 20-200 micrometers, More preferably, it is 30-100 micrometers. If the thickness is less than 10 μm, sufficient adhesive force and holding force may not be obtained. Moreover, sufficient flame retardancy may not be obtained. By setting the thickness to 250 μm or less, the pressure-sensitive adhesive layer becomes flexible, and a pressure-sensitive adhesive tape excellent in repulsion resistance is easily obtained.

  The flame-retardant pressure-sensitive adhesive layer is added as necessary, the acrylic polymer, the metal hydroxide having an average particle size of 10 μm or less, and / or the hydrated metal compound having an average particle size of 10 μm or less. It can be formed from a flame retardant pressure-sensitive adhesive composition in which the above-mentioned dispersant and the like are mixed. Specifically, for example, a monomer solution for forming the acrylic polymer, the polymerization initiator, and a suitable solvent (toluene, ethyl acetate, etc.) are mixed to prepare a monomer solution. A polymer solution containing an acrylic polymer copolymerized with monomer components is prepared by performing a polymerization reaction according to the type of the polymerization initiator on the polymer solution, and then the metal hydroxide and / or the water is added to the polymer solution. A flame retardant pressure-sensitive adhesive composition having a viscosity suitable for coating is prepared by blending a Japanese metal compound and, if necessary, the dispersant described above. When curing by ultraviolet irradiation or the like, a monomer component for forming an acrylic polymer, a photopolymerization initiator, etc. are mixed to prepare a monomer mixture, and the monomer mixture is irradiated with ultraviolet rays. After preparing a composition (syrup) containing a partial polymer obtained by polymerizing only a part of the monomer components, the metal hydroxide and / or the hydrated metal compound is added to the syrup, if necessary, the dispersant, etc. May be blended to prepare a composition having a viscosity suitable for coating, and the composition may be used to form a flame retardant adhesive layer.

  The flame retardant pressure-sensitive adhesive composition preferably has an appropriate viscosity from the viewpoint of excellent coatability. As a viscosity of the said flame-retardant adhesive composition, 5-50 Pa.s is preferable, for example, More preferably, it is 10-40 Pa.s. When the viscosity exceeds 50 Pa · s, the viscosity is too high when the flame-retardant pressure-sensitive adhesive layer is formed, and it becomes difficult to apply the flame-retardant pressure-sensitive adhesive composition.

  The flame retardant pressure-sensitive adhesive composition has a viscosity, for example, a method of blending various polymer components such as acrylic rubber and a thickening additive, a monomer component for forming an acrylic polymer (for example, forming an acrylic polymer) For example, a monomer component such as (meth) acrylic acid ester) is partially polymerized to obtain a partially polymerized product.

{Base material}
The base material is not particularly limited. For example, polyester resins such as polyethylene terephthalate (PET), acrylic resins such as polymethyl methacrylate, polycarbonate, triacetyl cellulose, polysulfone, polyarylate, polyimide, polyvinyl chloride, Examples thereof include plastic films made of materials such as polyvinyl acetate, polyethylene, polypropylene, and ethylene-propylene copolymer. Among these, a polyimide film is preferable from the viewpoint of excellent flame retardancy.
The plastic film material may be one kind or a combination of two or more kinds.

Although the thickness of the said base material is not specifically limited, For example, 5-100 micrometers is preferable, More preferably, it is 10-30 micrometers. By setting the thickness to 30 μm or less, the pressure-sensitive adhesive tape becomes flexible, and a pressure-sensitive adhesive tape excellent in repulsion resistance is easily obtained.
In addition, the said base material may have any form of a single layer and a multilayer. The surface of the base material may be appropriately subjected to known and conventional surface treatments such as physical treatment such as corona discharge treatment and plasma treatment, and chemical treatment such as undercoating treatment.

{Adhesive layer other than flame retardant adhesive layer}
The pressure-sensitive adhesive layer (other pressure-sensitive adhesive layer) other than the flame-retardant pressure-sensitive adhesive layer is not particularly limited as long as the effects of the present invention are not impaired. For example, a urethane-based pressure-sensitive adhesive, an acrylic pressure-sensitive adhesive, and a rubber-based pressure-sensitive adhesive A known and commonly used pressure-sensitive adhesive layer formed from a known pressure-sensitive adhesive such as an adhesive, a silicone-based pressure-sensitive adhesive, a polyester-based pressure-sensitive adhesive, a polyamide-based pressure-sensitive adhesive, an epoxy-based pressure-sensitive adhesive, a vinyl alkyl ether-based pressure-sensitive adhesive, Can be mentioned.
The pressure-sensitive adhesive forming the other pressure-sensitive adhesive layer can be used alone or in combination of two or more.

{Release liner}
The pressure-sensitive adhesive layer surface (pressure-sensitive adhesive surface) of the pressure-sensitive adhesive tape of the present invention may be protected by a release liner until use. When the pressure-sensitive adhesive tape of the present invention is a double-sided pressure-sensitive adhesive tape, each pressure-sensitive adhesive surface may be protected by two separators, respectively, or in a roll shape by one separator whose both surfaces are release surfaces. You may protect in the form wound. The release liner is used as a protective material for the pressure-sensitive adhesive layer, and is peeled off when the pressure-sensitive adhesive tape is attached to an adherend. The release liner also serves as a support for the pressure-sensitive adhesive layer. Note that the release liner is not necessarily provided.

  As the release liner, a conventional release paper or the like can be used. Specifically, for example, in addition to a substrate having a release treatment layer with a release treatment agent on at least one surface, a fluoropolymer (for example, polytetrafluoro Low adhesion substrates made of ethylene, polychlorotrifluoroethylene, polyvinyl fluoride, polyvinylidene fluoride, tetrafluoroethylene-hexafluoropropylene copolymer, chlorofluoroethylene-vinylidene fluoride copolymer, etc. A low adhesive substrate made of a polymer (for example, an olefin resin such as polyethylene or polypropylene) can be used.

  As the release liner, for example, a release liner in which a release treatment layer is formed on at least one surface of a release liner base material can be suitably used. Such release liner substrates include polyester films (polyethylene terephthalate film, etc.), olefin resin films (polyethylene film, polypropylene film, etc.), polyvinyl chloride films, polyimide films, polyamide films (nylon films), rayon films. In addition to plastic base film (synthetic resin film) and papers (quality paper, Japanese paper, kraft paper, glassine paper, synthetic paper, topcoat paper, etc.), etc., these are laminated by laminating or coextrusion. (2-3 layer composite) etc. are mentioned.

  The release treatment agent constituting the release treatment layer is not particularly limited. For example, a silicone release treatment agent, a fluorine release treatment agent, a long-chain alkyl release treatment agent, or the like can be used. The release treatment agents can be used alone or in combination of two or more. The thickness of the release liner, the formation method, etc. are not particularly limited.

The method for producing the pressure-sensitive adhesive tape of the present invention varies depending on the composition of the flame retardant pressure-sensitive adhesive composition and the like, and is not particularly limited. A known forming method can be used. For example, the following (1) to ( 3) and the like.
(1) A monomer component forming the acrylic polymer, a partial polymer of the monomer component, the metal hydroxide having an average particle size of 10 μm or less and / or the hydrated metal compound having an average particle size of 10 μm or less, necessary In accordance with the above, a composition containing the above-described dispersant or the like is applied (coated) on a base material or a separator to form a composition layer, and the composition layer is cured (for example, heat curing, activity such as ultraviolet rays) A method of producing a pressure-sensitive adhesive tape by forming a flame-retardant pressure-sensitive adhesive layer by curing with irradiation of energy rays.
(2) The acrylic polymer (including acrylic polymer solution), the metal hydroxide having an average particle size of 10 μm or less and / or the hydrated metal compound having an average particle size of 10 μm or less, if necessary, A method of producing a pressure-sensitive adhesive tape by applying (coating) a pressure-sensitive adhesive composition (solution) in which the above-mentioned dispersant or the like is uniformly dissolved onto a base material or a separator, and drying to form a flame-retardant pressure-sensitive adhesive layer. .
(3) A method of further drying the pressure-sensitive adhesive tape produced in (1) above.
As the curing method in the above (1) to (3), the method (2) is preferable from the viewpoint of excellent productivity. In addition, since hardening with active energy rays may be inhibited by oxygen in the air, for example, when hardening, oxygen is obtained by bonding a separator on the pressure-sensitive adhesive layer or hardening in a nitrogen atmosphere. Is preferably blocked.

  When obtaining the bubble-containing flame-retardant pressure-sensitive adhesive layer, a bubble-containing flame-retardant pressure-sensitive adhesive composition obtained by introducing and mixing bubbles (bubble-forming gas) into the flame-retardant pressure-sensitive adhesive composition, It can apply | coat on a predetermined surface and a bubble-containing flame-retardant adhesive layer can be formed.

  As a method of applying (coating) the flame retardant pressure-sensitive adhesive composition onto a predetermined surface, a known coating method can be adopted, and it is not particularly limited. For example, roll coating, kiss roll coating, gravure coating , Reverse coat, roll brush, spray coat, dip roll coat, bar coat, knife coat, air knife coat, curtain coat, lip coat, extrusion coat method using a die coater, and the like.

Although the thickness (total thickness) of the adhesive tape of this invention is not specifically limited, For example, 10-100 micrometers is preferable, More preferably, it is 20-80 micrometers, More preferably, it is 30-70 micrometers, Especially preferably, it is 30-60 micrometers. When the thickness is 10 μm or more, the adhesion reliability is excellent. When the thickness is 100 μm or less, the repulsion resistance is further improved.
The thickness (total thickness) of the adhesive tape is the thickness from one adhesive surface to the other adhesive surface, and does not include the thickness of the release liner.

180 ° peel adhesive strength (180 ° peel adhesive strength) of the adhesive tape of the present invention (23 ° C., 50% RH, tensile speed 300 mm / min, peeling condition of 180 ° peeling angle, vs. SUS304 steel plate) is not particularly limited. Is, for example, preferably 2N / 20 mm or more (for example, 2 to 10 N / 20 mm), more preferably 3N / 20 mm or more (for example, 3 to 10 N / 20 mm), and even more preferably 4N / 20 mm or more (for example, 4 to 10 N). / 20 mm). The 180 ° peel adhesive strength of the flame retardant adhesive layer in the adhesive tape of the present invention preferably satisfies the above range. For example, in the case of a double-sided adhesive tape, the 180 ° peel adhesive strength of at least one adhesive surface However, it is preferable to satisfy the above range.
The 180 ° peel adhesive strength can be measured, for example, by the method described in “(1) 180 ° peel adhesive strength” in (Evaluation) described later.

  The pressure-sensitive adhesive tape of the present invention has flame resistance of VTM-0 or VTM-1 in the flame resistance test of UL94 standard. The flame retardancy can be evaluated, for example, by the method described in “(2) Flame retardance” in (Evaluation) described later. It is preferable that only the flame-retardant pressure-sensitive adhesive layer in the pressure-sensitive adhesive tape of the present invention has the above-mentioned flame retardancy. For example, in the case of a double-sided pressure-sensitive adhesive tape, the double-sided pressure-sensitive adhesive surface has the above-mentioned flame retardancy. Is preferred.

In the following bending test, the adhesive tape of the present invention has a floating distance at the end of the adhesive tape of 0.5 mm or less, preferably 0.1 mm or less. When the floating distance is 0.5 mm or less, even if the adhesive tape is bent (for example, bent to 90 ° or 180 °) and attached to the adherend, the adhesive tape is difficult to peel off from the adherend. The floating distance of the adhesive tape end can be measured, for example, by the method described in “(3) Floating distance of tape end (repulsion resistance)” in (Evaluation) described later.
Bending test: Adhesive layer surface of adhesive tape (length 20 mm x width 40 mm) is applied to surface A of a polypropylene plate (thickness 2 mm), and a 2 kg roller is attached so that the attached part is 3 mm long x 40 mm wide. One reciprocal bonding is performed, the adhesive tape is folded 180 ° on the other surface B of the polypropylene plate, and the remaining portion of the adhesive tape is bonded, and left in a 23 ° C. atmosphere for 24 hours, and further in a 70 ° C. atmosphere. After leaving for 24 hours, the distance from the end of the adhesive tape where the adhesive tape is lifted from the surface A of the polypropylene plate (the lifting distance of the end of the adhesive tape) is measured.

  Since the adhesive tape of the present invention is excellent in flame retardancy and adhesiveness, it is a component member used in electronic devices such as mobile phones, smartphones, mobile terminals, digital cameras, video movies, personal computers, and other home appliances ( It can be suitably used in applications such as fixing electronic device components. Among them, the adhesive tape of the present invention has a repulsion resistance that is difficult to peel off from the adherend even if it is bent at 90 ° or 180 °, so that the electronic device is small or thin (for example, 1 to 20 mm in thickness). It can use suitably for the fixation use of a structural member. In particular, the pressure-sensitive adhesive tape of the present invention also has excellent flame retardancy, and therefore an exterior film (for battery exterior use) of a battery (for example, a lithium ion battery) used as a power source of the electronic device that easily generates heat. It is preferably used for the purpose of fixing the film) (for fixing the battery exterior film).

As the lithium ion battery, for example, a laminate type battery (a battery in which a power generation element having a structure in which positive electrodes, negative electrodes, and separators are alternately stacked is covered with a battery exterior material and the periphery is thermally welded), a square battery ( A flat electrolyte membrane is sandwiched between positive and negative electrodes of the same shape, and a plurality of these are stacked via an insulating plate and stored in a square case), a cylindrical battery (a long strip of electrolyte membrane has the same shape) A battery that is wound between a positive electrode and a negative electrode and wound in a cylindrical shape in a cylindrical case, filled with an electrolyte solution, and sealed is known.
The adhesive tape of the present invention is used for fixing an outer film of a laminate type lithium ion battery from the viewpoint of excellent repulsion resistance and flame retardancy (fixing the end of a battery outer film thermally bonded to a laminate type lithium ion battery) Can be used particularly suitably.

  Hereinafter, the present invention will be described more specifically with reference to examples and comparative examples. The present invention is not limited by these.

Example 1
(Preparation of adhesive composition)
As a monomer component of the acrylic polymer, 70 g of 2-ethylhexyl acrylate, 30 g of n-butyl acrylate, 4 g of 2-hydroxyethyl acrylate, and AIBN (trade name “2,2′-azobisisobutyronitrile” as a polymerization initiator, 0.08 g (manufactured by Wako Pure Chemical Industries, Ltd.) and 150 g of ethyl acetate as a polymerization solvent were put into a separable flask, stirred for 2 hours while introducing nitrogen gas, and uniformly dissolved. After removing oxygen in the polymerization system in this way, the temperature was raised to 65 ° C. and reacted for 8 hours to obtain an acrylic polymer solution (solution containing an acrylic polymer) with a solid content concentration of 30% by weight. . The viscosity (BH viscometer, No. 5 rotor, rotation speed 10 rpm, measurement temperature 30 ° C.) of the obtained acrylic polymer solution was about 1.5 Pa · s.
For 100 parts by weight of the acrylic polymer in the acrylic polymer solution, a rosin resin (trade name “Superester A-100”, softening point (ring and ball method) 95 to 105 ° C., Arakawa Chemical Industries, Ltd. as a tackifier resin. 20 parts by weight, trade name "Plisurf A212E" (Daiichi Kogyo Seiyaku Co., Ltd.) 1 part by weight, aluminum hydroxide powder (trade name "Hijilite H-32", shape as metal hydroxide : Crushed, average particle size: 8 μm, 100 parts by weight, manufactured by Showa Denko KK, as a crosslinking agent, isocyanate crosslinking agent (trade name “Coronate L”, tolylene diisocyanate adduct of trimethylolpropane, solid content 75% by mass , Nippon Polyurethane Industry Co., Ltd.) 0.5 parts by weight was added to obtain a pressure-sensitive adhesive composition (flame retardant pressure-sensitive adhesive composition). In addition, the addition amount (weight part) of coronate L is the compounding quantity of coronate L itself (product itself) with respect to 100 weight part of acrylic polymers.
(Preparation of adhesive tape)
The pressure-sensitive adhesive composition was applied to the release-treated surface of a release film (trade name “Diafoil MRF38”, manufactured by Mitsubishi Plastics), dried at 100 ° C. for 2 minutes, and a pressure-sensitive adhesive layer having a thickness of 25 μm ( Flame retardant adhesive layer) was formed. Next, the adhesive layer surface was laminated so as to face the surface of the polyimide film (trade name “Kapton 50H / V”, manufactured by Toray DuPont, thickness 12 μm), and the release film (release liner) / adhesive layer / polyimide An adhesive tape having a film configuration was prepared. The total thickness of the adhesive tape (thickness excluding the release liner) was 37 μm.

(Example 2)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-32” (shape: crushed, average particle size: 8 μm, manufactured by Showa Denko KK) is used with respect to 100 parts by weight of acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 1 except that a pressure-sensitive adhesive composition (a flame-retardant pressure-sensitive adhesive composition) was prepared by adding parts by weight.

(Example 3)
As the metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-32” (shape: crushed, average particle size: 8 μm, manufactured by Showa Denko KK) is used with 300 parts by weight of acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 1 except that a pressure-sensitive adhesive composition (a flame-retardant pressure-sensitive adhesive composition) was prepared by adding parts by weight.

Example 4
A pressure-sensitive adhesive tape was obtained in the same manner as in Example 1, except that a pressure-sensitive adhesive layer (flame-retardant pressure-sensitive adhesive layer) having a thickness of 50 μm was formed. The total thickness of the adhesive tape (thickness excluding the release liner) was 62 μm.

(Example 5)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-32” (shape: crushed, average particle size: 8 μm, manufactured by Showa Denko KK) is used with respect to 100 parts by weight of acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 4, except that a pressure-sensitive adhesive composition (flame retardant pressure-sensitive adhesive composition) was prepared by adding parts by weight.

(Example 6)
As the metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-32” (shape: crushed, average particle size: 8 μm, manufactured by Showa Denko KK) is used with 300 parts by weight of acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 4, except that a pressure-sensitive adhesive composition (flame retardant pressure-sensitive adhesive composition) was prepared by adding parts by weight.

(Comparative Example 1)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-32” (shape: crushed, average particle size: 8 μm, manufactured by Showa Denko KK) is used for 350 parts by weight of acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 1 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 2)
As the metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-32” (shape: crushed, average particle size: 8 μm, manufactured by Showa Denko KK) is 10 A pressure-sensitive adhesive tape was obtained in the same manner as in Example 1 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 3)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-31” (shape: crushed, average particle size: 18 μm, manufactured by Showa Denko KK) is 10 A pressure-sensitive adhesive tape was obtained in the same manner as in Example 1 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 4)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-31” (shape: crushed, average particle size: 18 μm, manufactured by Showa Denko KK), 100 parts by weight with respect to 100 parts by weight of acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 1 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 5)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-31” (shape: crushed, average particle size: 18 μm, manufactured by Showa Denko KK) is used for 350 parts by weight of an acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 1 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 6)
A pressure-sensitive adhesive tape was obtained in the same manner as in Example 1 except that the pressure-sensitive adhesive composition was prepared without adding aluminum hydroxide powder.

(Comparative Example 7)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-32” (shape: crushed, average particle size: 8 μm, manufactured by Showa Denko KK) is used for 350 parts by weight of acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 4 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 8)
As the metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-32” (shape: crushed, average particle size: 8 μm, manufactured by Showa Denko KK) is 10 A pressure-sensitive adhesive tape was obtained in the same manner as in Example 4 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 9)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-31” (shape: crushed, average particle size: 18 μm, manufactured by Showa Denko KK) is 10 A pressure-sensitive adhesive tape was obtained in the same manner as in Example 4 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 10)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-31” (shape: crushed, average particle size: 18 μm, manufactured by Showa Denko KK), 100 parts by weight with respect to 100 parts by weight of acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 4 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 11)
As a metal hydroxide, aluminum hydroxide powder (trade name “Hijilite H-31” (shape: crushed, average particle size: 18 μm, manufactured by Showa Denko KK) is used for 350 parts by weight of an acrylic polymer. A pressure-sensitive adhesive tape was obtained in the same manner as in Example 4 except that the pressure-sensitive adhesive composition was prepared by adding parts by weight.

(Comparative Example 12)
A pressure-sensitive adhesive tape was obtained in the same manner as in Example 4 except that the pressure-sensitive adhesive composition was prepared without adding aluminum hydroxide powder.

(Evaluation)
The following measurement or evaluation was performed about the adhesive tape obtained by the Example and the comparative example. The results are shown in Table 1.

(1) 180 degree peel adhesive force From the adhesive tape obtained by said Example and comparative example, the tape piece of length 100mm and width 20mm was cut out, and the strip-shaped tape piece was produced. In addition, the thickness of each tape piece is the thickness described in said Example and the comparative example.
Next, the release liner is peeled off from the strip-shaped tape piece, and the adhesive surface (measurement surface) is pressure-bonded to the SUS304 steel sheet by reciprocating a 2 kg roller once in a 23 ° C., 50% RH atmosphere. A sample was made.
The measurement sample was allowed to stand for 30 minutes in an atmosphere of 23 ° C. and 50% RH, and then subjected to a 180 ° peel test using a tensile tester (trade name “TCM-1kNB”, manufactured by Minebea Co., Ltd.). 180 ° peel adhesive strength (180 ° peel adhesive strength) (N / 20 mm) was measured. The measurement was performed in an atmosphere of 23 ° C. and 50% RH under conditions of a peeling angle of 180 ° and a tensile speed of 300 mm / min.

(2) Flame retardance The following flame retardancy test was conducted in accordance with the flame retardancy test standard UL94.
Five test pieces having a length of 200 mm and a width of 50 mm were obtained from the pressure-sensitive adhesive tapes obtained in the above Examples and Comparative Examples. In addition, the thickness of each tape piece is the thickness described in said Example and the comparative example.
One end of the test piece was hung vertically. After that, using a burner, flame was applied to the other end for 3 seconds, once separated from the flame, and then the state of the test piece after further flame was applied for 3 seconds. The flame retardancy was evaluated as “VTM-0”, a case satisfying the following standard Y as “VTM-1”, and a case not satisfying the standard X and the standard Y as “bad”.
Criteria X: All the following (1) to (5) are satisfied.
(1) The flammable burning time of each test piece (the total of the burning time after applying the first flame and the burning time after applying the second flame) is within 10 seconds.
(2) The total time of the flammable combustion time of the five test pieces is within 50 seconds.
(3) The total time of the flaming combustion time and the flameless combustion time of each test piece after applying the flame for the second time is within 30 seconds.
(4) Of the five test pieces, there is no test piece in which the combustion drop dropped from the test piece and the cotton disposed below ignited.
(5) All specimens do not burn to the suspended part (upper end part).
Reference Y: satisfying all of the following (1 ′) to (5 ′).
(1 ′) The flammable combustion time (total of the combustion time after applying the first flame and the combustion time after applying the second flame) of each test piece is within 30 seconds.
(2 ') The total time of the flaming combustion time of five test pieces is within 250 seconds.
(3 ') The total time of the flammable combustion time and the flameless combustion time of each test piece after applying the flame for the second time is within 60 seconds.
(4 ′) Of the five test pieces, there is no test piece in which the combustion drop dropped from the test piece and the cotton disposed below ignited.
(5 ') All test pieces do not burn to the suspended part (upper end part).

(3) Floating distance at the end of the adhesive tape (Repulsion resistance)
The “floating distance at the end of the pressure-sensitive adhesive tape” of the pressure-sensitive adhesive tapes obtained in the above Examples and Comparative Examples was measured as follows. In addition, FIG. 1 is the schematic explaining the measuring method of the floating distance of an adhesive tape edge part. (1a) of FIG. 1 is a schematic view showing a state where an adhesive tape (tape piece) and a polypropylene plate are attached, and (1b) is 23 ° C. after attaching the adhesive tape (tape piece). FIG. 4 is a schematic view when the adhesive tape ends are lifted from the polypropylene plate after being left in a 50% RH atmosphere for 24 hours and then in a 70 ° C. atmosphere for 24 hours.
A tape piece having a length of 20 mm and a width of 40 mm was cut out from the pressure-sensitive adhesive tape obtained in the above Examples and Comparative Examples to produce a strip-shaped tape piece. In addition, the thickness of each tape piece is the thickness described in said Example and the comparative example.
Next, the release liner is peeled from the strip-shaped tape piece, and a polypropylene plate (size: length 70 mm, width 70 mm, thickness 2 μm, trade name “Kobe Poly Sheet PP” manufactured by Shin-Kobe Electric Machinery Co., Ltd.) One surface (surface A, 3 in FIG. 1) was pressure-bonded by reciprocating a 2 kg roller once in a 23 ° C., 50% RH atmosphere so that the part to be attached was 3 mm long × 40 mm wide. , Pasted.
Next, the tape piece is bent by 180 °, and the remaining part (length: about 17 mm, width: 40 mm) of the tape piece is placed on the other surface (surface B, 4 in FIG. 1) of the polypropylene plate at 23 ° C. In a 50% RH atmosphere, a 2 kg roller was reciprocated once to be bonded and bonded (FIG. 1 (1a)). Thereafter, it was allowed to stand for 24 hours in an atmosphere of 23 ° C. and 50% RH, and further left for 24 hours in an atmosphere of 70 ° C. and 10% RH (FIG. 1 (1b)).
Measure the distance from the tape piece end of the part (5 in FIG. 1) where the tape piece floated from the surface A of the polypropylene plate (6 in FIG. 1, floating distance at the tape end, unit: mm). The case where the floating distance of the part was 0.5 mm or less was evaluated as “good (◯)”, and the case where it was larger than 0.5 mm was evaluated as “bad” (x).

1 Adhesive tape (tape piece)
2 Polypropylene plate 3 One surface of polypropylene plate (surface A)
4 Other surface of polypropylene plate (surface B)
5 The part where the adhesive tape is lifted from the surface A of the polypropylene plate. 6 The floating distance of the tape end.

Claims (4)

An acrylic polymer and a metal hydroxide having an average particle size of 10 μm or less and / or a hydrated metal compound having an average particle size of 10 μm or less, and the metal hydroxide having an average particle size of 10 μm or less and the average particle size Is a pressure-sensitive adhesive tape having a pressure-sensitive adhesive layer in which the total content of the hydrated metal compound of 10 μm or less is 20 to 330 parts by weight with respect to 100 parts by weight of the acrylic polymer and a base material including a polyimide film. ,
The base material has a thickness of 10 to 30 μm,
The total thickness of the adhesive tape is 20-80 μm,
In the following bending test, the adhesive tape has a floating distance of 0.5 mm or less at the end of the adhesive tape, and has flame retardancy of VTM-0 or VTM-1 in the flame resistance test of UL94 standard. tape.
Bending test: Adhesive layer surface of adhesive tape (length 20 mm x width 40 mm) is applied to surface A of a polypropylene plate (thickness 2 mm), and a 2 kg roller is attached so that the attached part is 3 mm long x 40 mm wide. 1 reciprocating and bonding, the adhesive tape is folded 180 °, and the other part of the adhesive tape is bonded to the other surface B of the polypropylene plate by reciprocating a 2 kg roller once, and the atmosphere is kept at 23 ° C. for 24 hours. After standing for 24 hours in an atmosphere at 70 ° C., the distance from the end of the adhesive tape where the adhesive tape lifted from the surface A of the polypropylene plate (floating distance of the end of the adhesive tape) was measured. To do. The pressure-sensitive adhesive tape according to claim 1, wherein the pressure-sensitive adhesive layer contains a tackifier resin. 2. The content of the carboxyl group-containing monomer in the monomer component constituting the acrylic polymer contained in the pressure-sensitive adhesive layer is 0.1% by weight or less based on the total amount of monomer components (100% by weight). Or the adhesive tape of 2. The adhesive tape of any one of Claims 1-3 used for fixation of the film for battery exteriors.

Images