JP6286014B2 - Protective film for process - Google Patents
Protective film for process Download PDFInfo
- Publication number
- JP6286014B2 JP6286014B2 JP2016245897A JP2016245897A JP6286014B2 JP 6286014 B2 JP6286014 B2 JP 6286014B2 JP 2016245897 A JP2016245897 A JP 2016245897A JP 2016245897 A JP2016245897 A JP 2016245897A JP 6286014 B2 JP6286014 B2 JP 6286014B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- protective film
- dot
- dots
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、工程用保護フィルムに関する。 The present invention relates to a process protective film.
近年、電子機器部品の小型化が進んだため、その製造において、接着フィルムに各種電子機器部品を仮粘着固定し、各部品の形に打ち抜き加工等を行い、加工終了後に、接着フィルムから各部品を剥離して、使用するという部品の製造方法が行われている。このような接着フィルムは「工程用フィルム」と呼ばれ、セラミックグリーンシートの製造に主として使用されている。 In recent years, electronic device parts have been miniaturized, and in manufacturing, various electronic device parts are temporarily adhesively fixed to an adhesive film, punched into the shape of each part, etc. A method of manufacturing a part is used in which the part is peeled off and used. Such an adhesive film is called a “process film” and is mainly used in the production of ceramic green sheets.
このような工程用フィルムは、プラスチックフィルム等の基材上に、剥離性を有する接着剤層を有する基本構成からなり、例えば、特許文献１及び２のようなものが提案されている。 Such a process film has a basic structure having an adhesive layer having peelability on a base material such as a plastic film. For example, patent documents 1 and 2 have been proposed.
特許文献１は、基材上に、特定の組成からなる接着剤層を設けることにより、適度の接着力を有し、打ち抜き加工性に優れ、ジッピング、糊残り、粉落ちをなくした工程用フィルムを開示している。
特許文献２は、基材上に、特定の物性を有する接着剤層を設けることにより、加工工程後の電子部品の精度が落ちず、また、熱を加えるだけで自己剥離することができる工程用フィルムを開示している。
Patent Document 1 discloses a process film having an appropriate adhesive force, excellent punching workability, and eliminating zipping, adhesive residue, and powder falling by providing an adhesive layer having a specific composition on a substrate. Is disclosed.
Patent Document 2 is for a process in which an adhesive layer having specific physical properties is provided on a base material so that the accuracy of an electronic component after a processing process does not decrease, and self-peeling can be performed only by applying heat. A film is disclosed.
近年、上述したような工程用フィルムは、光拡散フィルム、プリズムシート、偏光フィルム、位相差フィルム、ハードコートフィルム、透明導電性フィルム等の光学フィルムの製造時にも用いられるようになっている。これら光学フィルムは、製造時の傷つき防止のために、打ち抜き加工後も最終工程が完了するまで接着フィルムが貼り合わせられる。したがって、工程用フィルムは、単なる工程用途ではなく、保護機能を兼ね備えた「工程用保護フィルム」として用いられるようになってきた。
光学用フィルムの製造工程では、打ち抜き加工し、工程用保護フィルムを貼りあわせたまま複数枚を積層した後に、各光学フィルムを次の工程に送る場合がある。各光学フィルムを次の工程に送る手段は、例えば、真空吸引で個々の光学フィルムを吸引する手段が挙げられる。
しかし、特許文献１及び２のような従来の工程用フィルムは、この真空吸引の際に、積層した光学フィルムが密着し、複数枚が同時に吸引されてしまうという問題があった。
In recent years, the above-described process films have been used in the production of optical films such as light diffusion films, prism sheets, polarizing films, retardation films, hard coat films, and transparent conductive films. These optical films are bonded to each other until the final process is completed even after punching to prevent damage during manufacturing. Therefore, the process film has been used not only as a process application but as a “process protective film” having a protective function.
In the optical film manufacturing process, after punching and laminating a plurality of sheets with the process protective film bonded together, each optical film may be sent to the next process. Examples of means for sending each optical film to the next step include means for sucking individual optical films by vacuum suction.
However, the conventional process films such as Patent Documents 1 and 2 have a problem in that the laminated optical films are in close contact during vacuum suction, and a plurality of sheets are sucked simultaneously.
上記のような密着を防止するためには、工程用保護フィルムの接着剤層とは反対側の面（背面）に、ケミカルコーティング等でマット層を形成したり、エンボス処理する手段が考えられる。
しかし、光学フィルムには検査や管理のためにＱＲコード（登録商標）やバーコード等の情報が印刷されている場合があり、マット層やエンボス処理した場合には、工程用保護フィルムを介してこれらの情報が読み取れなくなるという問題が生じた。また、エンボス処理した際は、フィルムの平面性が損なわれ、光学フィルムに貼り合わせる際に、気泡が混入する等の不具合が生じるという問題も生じた。
In order to prevent the adhesion as described above, means for forming a mat layer by chemical coating or embossing on the surface (back surface) opposite to the adhesive layer of the process protective film can be considered.
However, information such as QR code (registered trademark) and bar code may be printed on the optical film for inspection and management. When the matte layer or embossing is applied, There arises a problem that such information cannot be read. Moreover, when embossing was performed, the flatness of the film was impaired, and when the film was bonded to the optical film, there was a problem that air bubbles were mixed.
本発明者らは、上記課題を解決すべく鋭意研究した結果、密着防止性と情報の読み取り性を同時に解決し得るための背面形状を見出し、これを解決するに至った。 As a result of intensive studies to solve the above-mentioned problems, the present inventors have found a back surface shape capable of simultaneously solving the adhesion preventing property and the information reading property and have come to solve the problem.
本発明は、以下［１］〜［５］の工程用保護フィルムを提供することを目的とする。
［１］基材上の一方の面に接着剤層を有してなり、前記基材の接着剤層を有する面とは反対側の面にパターン状のドットを有し、前記反対側の面の王研式平滑度が６０秒未満であり、前記反対側の面の全面積に対する前記ドットの占める割合が１０〜６０％である工程用保護フィルム。
［２］前記ドットは、直径が１００〜１２００μｍである上記［１］に記載の工程用保護フィルム。
［３］前記ドットは、高さが２〜１５μｍである上記［１］又は［２］に記載の工程用保護フィルム。
［４］前記反対側の面のドットの密度が５〜１０００個／ｃｍ２である上記［１］〜［３］の何れかに記載の工程用保護フィルム。
［５］光学フィルム用として用いる上記［１］〜［４］の何れかに記載の工程用保護フィルム。
An object of this invention is to provide the protective film for processes of following [1]-[5].
[1] It has an adhesive layer on one surface on the substrate, has a patterned dot on the surface opposite to the surface having the adhesive layer of the substrate, and the surface on the opposite side The Oken type smoothness is less than 60 seconds, and the ratio of the dots to the total area of the opposite surface is 10 to 60%.
[2] The process protective film according to [1], wherein the dot has a diameter of 100 to 1200 μm.
[3] The process protective film according to [1] or [2], wherein the dots have a height of 2 to 15 μm.
[4] The process protective film according to any one of [1] to [3], wherein a density of dots on the opposite surface is 5 to 1000 / cm 2 .
[5] The process protective film according to any one of [1] to [4], which is used for an optical film.
本発明の工程用保護フィルムは、密着防止性に優れつつ、バーコード等の情報の読み取り性を満足することができる。 The protective film for a process of the present invention is excellent in adhesion preventing property and can satisfy information reading properties such as a barcode.
本発明の工程用保護フィルムは、基材上の一方の面に接着剤層を有してなり、前記基材の接着剤層を有する面とは反対側の面にパターン状のドットを有し、前記反対側の面の王研式平滑度が６０秒未満であるものである。以下、本発明の実施の形態を説明する。 The protective film for a process of the present invention has an adhesive layer on one surface on the substrate, and has a pattern-like dot on the surface opposite to the surface having the adhesive layer of the substrate. The Oken-type smoothness of the opposite surface is less than 60 seconds. Embodiments of the present invention will be described below.
［基材］
基材としては、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリカーボネート、ポリエチレン、ポリプロピレン、ポリスチレン、トリアセチルセルロース、ポリ（メタ）アクリレート、ポリ塩化ビニル等のプラスチックフィルムを用いることが好ましい。これらの中でも、延伸加工、特に二軸延伸加工されたポリエチレンテレフタレートフィルムが、機械的強度、寸法安定性及び透明性に優れる点で好ましい。
また、基材表面にコロナ放電処理を施したり、易接着剤層を設ける等の易接着処理を施すことにより、接着剤層又はドットパターンとの密着性を向上させたものも好適に用いられる。
基材の厚みとしては、一般には２５〜５００μｍであるが、取り扱い性の観点から、５０〜３５０μｍであることが好ましい。
[Base material]
As the substrate, it is preferable to use a plastic film such as polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polycarbonate, polyethylene, polypropylene, polystyrene, triacetyl cellulose, poly (meth) acrylate, polyvinyl chloride or the like. Among these, a stretched polyethylene terephthalate film, particularly a biaxially stretched film, is preferable in terms of excellent mechanical strength, dimensional stability, and transparency.
Moreover, what improved the adhesiveness with an adhesive bond layer or a dot pattern by giving corona discharge treatment to the base-material surface, or providing easy adhesive treatment, such as providing an easily adhesive layer, is used suitably.
The thickness of the substrate is generally 25 to 500 μm, but is preferably 50 to 350 μm from the viewpoint of handleability.
［接着剤層］
接着剤層は、光拡散フィルム、プリズムシート、偏光フィルム、位相差フィルム、ハードコートフィルム、透明導電性フィルム等の光学フィルム等の被着体に接着可能であり、かつ工程終了後に剥離可能なものであれば、特に制限することなく使用できる。
接着剤層を構成する接着剤としては、アクリル系接着剤、ポリエステル系接着剤、ウレタン系接着剤、ゴム系接着剤、シリコーン系接着剤等が挙げられ、これらの中でも、接着力、被着体へ汚染性、及びコストの観点から、アクリル系接着剤が好適である。
[Adhesive layer]
The adhesive layer can be adhered to adherends such as light diffusion films, prism sheets, polarizing films, retardation films, hard coat films, transparent conductive films, etc., and can be peeled off after completion of the process. If it is, it can be used without any particular limitation.
Examples of the adhesive constituting the adhesive layer include acrylic adhesives, polyester adhesives, urethane adhesives, rubber adhesives, silicone adhesives, etc. Among these, adhesive strength, adherend Acrylic adhesives are preferred from the standpoint of contamination and cost.
接着剤層の厚みは、１〜１００μｍであることが好ましく、５〜７５μｍであることがより好ましく、１５〜５０μｍであることがさらに好ましい。
なお、接着剤層上には、取り扱い性を向上するために、離型フィルムを積層しておくことが好ましい。離型フィルムとしては、シリコーン等の離型剤で表面処理したフィルムや、ポリエチレンテレフタレートフィルム等が挙げられる。
The thickness of the adhesive layer is preferably 1 to 100 μm, more preferably 5 to 75 μm, and still more preferably 15 to 50 μm.
In addition, it is preferable to laminate | release a release film on an adhesive bond layer in order to improve handleability. Examples of the release film include a film surface-treated with a release agent such as silicone, a polyethylene terephthalate film, and the like.
［パターン状のドット］
パターン状のドットは、基材の接着剤層を有する面とは反対側の面に形成されるものである。基材にケミカルコーティングやエンボス加工を行った場合、凹凸がフィルムの全面に形成されるため、バーコード等の情報の読み取り性が損なわれてしまう。また、エンボス加工ではフィルムの平面性が失われるため、光学フィルムに貼り合わせる際に気泡が混入する等して、貼り合わせ時の作業性が低下してしまう。これに対して、本発明のようにパターン状のドットでは、ドットパターンは部分的に存在するため、情報の読み取り性が損なわれることがない。また、ドットパターンは、ケミカルコーティングやエンボス加工よりも情報の読み取り性に優れつつ、王研式平滑度を低くすることができ、密着を防止することができる。また、基材にドットパターンを形成しても、エンボス加工のように、光学フィルムへの貼り合わせの作業性が低下することもない。
[Pattern dots]
The pattern-like dots are formed on the surface opposite to the surface having the adhesive layer of the substrate. When chemical coating or embossing is performed on the base material, irregularities are formed on the entire surface of the film, so that the readability of information such as barcodes is impaired. Further, since the flatness of the film is lost in the embossing process, air bubbles are mixed when the film is bonded to the optical film, so that workability at the time of bonding is lowered. On the other hand, in the case of pattern-like dots as in the present invention, the dot pattern partially exists, so that the information readability is not impaired. In addition, the dot pattern is superior to chemical coating and embossing in reading information, and can reduce the Oken-type smoothness and prevent adhesion. Moreover, even if a dot pattern is formed on the base material, the workability of bonding to the optical film is not lowered unlike embossing.
本発明では、パターン状のドットを有する側の面の王研式平滑度を６０秒未満とする。王研式平滑度が６０秒以上の場合、光学フィルム等を複数積層した際の密着を防止することができず、真空吸引の際に複数枚が同時に吸引されてしまう。
王研式平滑度は５０秒以下であることが好ましく、３０秒以下であることがより好ましく、２０秒以下であることがさらに好ましい。また、王研式平滑度があまりに小さすぎると、滑り性が高くなり、ロール状態で巻きズレを生じる可能性があるため、王研式平滑度は１０秒以上とすることが好適である。
なお、本発明における王研式平滑度は、ＪＩＳ Ｐ８１５５：２０１０に準じて測定することができる。
In the present invention, the Oken-type smoothness of the surface having the pattern-like dots is set to less than 60 seconds. When the Oken smoothness is 60 seconds or more, it is not possible to prevent adhesion when a plurality of optical films or the like are stacked, and a plurality of sheets are sucked simultaneously during vacuum suction.
The Oken smoothness is preferably 50 seconds or less, more preferably 30 seconds or less, and even more preferably 20 seconds or less. Further, if the Oken type smoothness is too small, the slipperiness becomes high, and there is a possibility that winding deviation occurs in a roll state. Therefore, the Oken type smoothness is preferably 10 seconds or more.
The Oken type smoothness in the present invention can be measured according to JIS P8155: 2010.
ドットの形状は、円形、楕円形、四角形、多角形、不定形等、特に制限されないが、円形が好適である。また、各ドットで形状が異なっていても良いが、面内での密着防止性及び情報の読み取り性を均質化するために、各ドットを同一の形状とすることが好ましい。また、ドットの配置は、ランダムに配置してもよいし、規則性をもってパターン化して配置してもよいが、面内での密着防止性及び情報の読み取り性を均質化するため、規則パターン化して配置することが好ましい。 The shape of the dot is not particularly limited, such as a circle, an ellipse, a rectangle, a polygon, and an indeterminate shape, but a circle is preferable. Each dot may have a different shape, but it is preferable that each dot has the same shape in order to make the in-plane adhesion prevention property and the information readability uniform. In addition, the dots may be arranged randomly or may be arranged in a regular pattern, but in order to make the in-plane adhesion prevention and information readability uniform, a regular pattern is used. Are preferably arranged.
ドットは直径が１００〜１２００μｍであることが好ましく、３００〜１０００μｍであることがより好ましく、４００〜８００μｍであることがさらに好ましい。ドットの直径を１００μｍ以上とすることにより、密着を防止するためのドットの個数を減らすことができ、情報の読み取り性を良好にしやすくできる。また、ドットの大きさを１２００μｍ以下とすることにより、解像性への影響を抑え、情報の読み取り性を良好にしやすくできる。なお、本発明において「直径」とは、ドットの底面の任意の２点を結んだ線分のうち、最も長い線分の長さのことをいう。 The dots preferably have a diameter of 100 to 1200 μm, more preferably 300 to 1000 μm, and still more preferably 400 to 800 μm. By setting the dot diameter to 100 μm or more, the number of dots for preventing adhesion can be reduced, and the information readability can be easily improved. In addition, by setting the dot size to 1200 μm or less, it is possible to suppress the influence on the resolution and easily improve the information readability. In the present invention, “diameter” refers to the length of the longest line segment connecting two arbitrary points on the bottom surface of the dot.
ドットの高さは、２〜１５μｍであることが好ましく、６〜１０μｍであることがより好ましい。ドットの高さを２μｍ以上とすることにより、搬送性を発現できる。また、ドットの高さを１５μｍ以下とすることにより、厚みが薄いまま密着を防止しやすくできる。 The height of the dots is preferably 2 to 15 μm, and more preferably 6 to 10 μm. By setting the height of the dots to 2 μm or more, it is possible to express transportability. Further, by setting the height of the dots to 15 μm or less, it is possible to easily prevent adhesion while the thickness is thin.
ドットを有する側の面の全面積に対するドットの占める割合は、１０〜６０％であることが好ましく、１５〜５０％であることがより好ましく、２０〜４０％であることがさらに好ましい。ドットの占める割合を１０％以上とすることにより、密着を防止しやすくできる。また、ドットの占める割合を６０％以下とすることにより、情報の読み取りを良好にしやすくできる。 The ratio of the dots to the total area of the surface having the dots is preferably 10 to 60%, more preferably 15 to 50%, and still more preferably 20 to 40%. Adhesion can be easily prevented by setting the ratio of dots to 10% or more. Further, by setting the ratio of the dots to 60% or less, it is possible to easily improve the information reading.
ドットの密度は、５〜１０００個／ｃｍ２であることが好ましく、１０〜２００個／ｃｍ２であることがより好ましく、２０〜１５０個／ｃｍ２であることがさらに好ましい。ドットの密度が５個／ｃｍ２以上であることにより重送を防ぐことができ、１０００個／ｃｍ２以下であることにより視認性が損なわれることを防止できる。 The density of the dots is preferably 5 to 1000 / cm 2 , more preferably 10 to 200 / cm 2 , and still more preferably 20 to 150 / cm 2 . When the dot density is 5 / cm 2 or more, double feeding can be prevented, and when it is 1000 / cm 2 or less, visibility can be prevented from being impaired.
ドットパターンは、スクリーン印刷、グラビア印刷等の印刷により形成することが好ましい。また、ドットパターンは、基材上に感光層を形成して、露光、現像により形成することもできる。これらのドットパターンの形成手段の中でも、安価に連続生産が出来るため、量産性の観点からグラビア印刷が好ましい。
ドットパターンは、ポリエステル系樹脂、アクリル系樹脂、アクリルウレタン系樹脂、ポリエステルアクリレート系樹脂、ポリウレタンアクリレート系樹脂、エポキシアクリレート系樹脂、ウレタン系樹脂、エポキシ系樹脂、ポリカーボネート系樹脂、セルロース系樹脂、アセタール系樹脂、ビニル系樹脂、ポリエチレン系樹脂、ポリスチレン系樹脂、ポリプロピレン系樹脂、ポリアミド系樹脂、ポリイミド系樹脂、メラミン系樹脂、フェノール系樹脂、シリコーン系樹脂、フッ素系樹脂等の熱可塑性樹脂、熱硬化性樹脂、電離放射線硬化性樹脂等から形成することが好ましい。これらの樹脂は、単独又は２種以上を混合して使用できる。これらの樹脂の中では、密着防止性を良好にする観点からは、熱硬化性樹脂、電離放射線硬化性樹脂が好適である。また、これら樹脂の中でも、透明性の観点からはアクリル系樹脂が好適であり、その中でも、密着防止性をより良好にする観点から、アクリル系の熱硬化性樹脂、電離放射線硬化性樹脂が好適である。
アクリル系の熱硬化性樹脂としては、アクリルポリオールとイソシアネート系硬化剤との組み合わせが挙げられる。アクリル系の電離放射線硬化性樹脂としては、ポリエステルアクリレート系樹脂、ポリウレタンアクリレート系樹脂及びエポキシアクリレート系樹脂等が挙げられる。
The dot pattern is preferably formed by printing such as screen printing or gravure printing. The dot pattern can also be formed by forming a photosensitive layer on a substrate, and exposing and developing. Among these dot pattern forming means, gravure printing is preferable from the viewpoint of mass productivity because continuous production can be performed at low cost.
Dot pattern is polyester resin, acrylic resin, acrylic urethane resin, polyester acrylate resin, polyurethane acrylate resin, epoxy acrylate resin, urethane resin, epoxy resin, polycarbonate resin, cellulose resin, acetal Resins, vinyl resins, polyethylene resins, polystyrene resins, polypropylene resins, polyamide resins, polyimide resins, melamine resins, phenol resins, silicone resins, fluororesins, and other thermoplastic resins, thermosetting It is preferably formed from a resin, an ionizing radiation curable resin, or the like. These resins can be used alone or in admixture of two or more. Among these resins, thermosetting resins and ionizing radiation curable resins are preferable from the viewpoint of improving adhesion prevention. Among these resins, acrylic resins are preferable from the viewpoint of transparency. Among them, acrylic thermosetting resins and ionizing radiation curable resins are preferable from the viewpoint of improving adhesion prevention. It is.
Examples of the acrylic thermosetting resin include a combination of an acrylic polyol and an isocyanate curing agent. Examples of acrylic ionizing radiation curable resins include polyester acrylate resins, polyurethane acrylate resins, and epoxy acrylate resins.
ドットパターンはマット剤を含有していてもよい。マット剤を含有することにより、密着防止性をより良好にすることができる。
マット剤としては、炭酸カルシウム、炭酸マグネシウム、硫酸バリウム、水酸化アルミニウム、シリカ、カオリン、クレー、タルク等の無機粒子や、アクリル樹脂粒子、ポリスチレン樹脂粒子、ポリウレタン樹脂粒子、ポリエチレン樹脂粒子、ベンゾグアナミン樹脂粒子、エポキシ樹脂粒子等の樹脂粒子があげられる。これらの中でも、分散などの性能とコストのバランスの観点からシリカが好適である。
マット剤の含有量は、ドットパターンの樹脂成分１００質量部に対して、通常１〜２０質量部程度である。また、マット剤の平均粒子径は、通常５〜１５μｍ程度である。
The dot pattern may contain a matting agent. By containing the matting agent, the adhesion preventing property can be improved.
Matting agents include calcium carbonate, magnesium carbonate, barium sulfate, aluminum hydroxide, silica, kaolin, clay, talc and other inorganic particles, acrylic resin particles, polystyrene resin particles, polyurethane resin particles, polyethylene resin particles, benzoguanamine resin particles And resin particles such as epoxy resin particles. Among these, silica is preferable from the viewpoint of balance between performance such as dispersion and cost.
The content of the matting agent is usually about 1 to 20 parts by mass with respect to 100 parts by mass of the resin component of the dot pattern. The average particle size of the matting agent is usually about 5 to 15 μm.
［その他の構成］
接着剤層の表面には、取り扱い性を向上するためにセパレータを貼り合わせておくことが好ましい。セパレータは、上述した基材と同様にプラスチックフィルムを用いることが好ましい。また、セパレータの厚みは通常５〜１００μｍ程度である。
また、基材と接着剤層との間、基材とドットパターンとの間、あるいはドットパターン上に、帯電防止層を形成してもよい。帯電防止層を有することにより、剥離帯電を防止し、作業性を向上させることができる。
[Other configurations]
It is preferable to attach a separator to the surface of the adhesive layer in order to improve handleability. As the separator, a plastic film is preferably used in the same manner as the base material described above. Moreover, the thickness of a separator is about 5-100 micrometers normally.
Further, an antistatic layer may be formed between the substrate and the adhesive layer, between the substrate and the dot pattern, or on the dot pattern. By having the antistatic layer, peeling electrification can be prevented and workability can be improved.
本発明の工程用保護フィルムは、主として電子機器部品を製造する際に、これら部品に貼り合わせる工程用保護フィルムとして用いることができる。特に、本発明の工程用保護フィルムは、光拡散フィルム、プリズムシート、偏光フィルム、位相差フィルム、ハードコートフィルム、透明導電性フィルム等の光学フィルムの打ち抜き、断裁等の加工時、加工後の積層時、積層状態からの真空吸引による搬送工程等の一連の工程において、これら光学フィルムを保護することができ、かつ検査や管理のために印刷されたバーコード等の情報の読み取り性が損なわれることもない。 The protective film for a process of the present invention can be used as a protective film for a process to be bonded to these parts when mainly manufacturing electronic device parts. In particular, the protective film for a process of the present invention is a laminated film after processing at the time of processing such as punching and cutting of an optical film such as a light diffusion film, a prism sheet, a polarizing film, a retardation film, a hard coat film, and a transparent conductive film. Sometimes, these optical films can be protected in a series of processes such as a vacuum suction process from the laminated state, and the readability of information such as barcodes printed for inspection and management is impaired. Nor.
以下、本発明を実施例により具体的に説明するが、本発明は以下の例に限定されるものではない。なお、「部」は特に断りのない限り質量基準とする。 EXAMPLES Hereinafter, although an Example demonstrates this invention concretely, this invention is not limited to the following examples. “Parts” are based on mass unless otherwise specified.
実施例及び比較例で得られた工程用保護フィルムについて下記の評価を行った。結果を表１に示す。
＜王研式平滑度＞
工程用保護フィルムの接着剤層上に厚み１８８μｍのポリエステルフィルム（東レ社製、ルミラーＴ６０）を貼り合わせたサンプルを作製し、該サンプルのドットパターン側（もしくはマット層側）の面を、水柱型王研式透気度試験機（旭精工社製、ＫＹ−５）の測定ヘッド面に押し付け、ＪＩＳ Ｐ８１５５：２０１０に準じて、王研式平滑度を測定した。
The following evaluation was performed about the protective film for processes obtained by the Example and the comparative example. The results are shown in Table 1.
<Oken smoothness>
A sample in which a 188 μm thick polyester film (Lumirror T60, manufactured by Toray Industries, Inc.) is bonded onto the adhesive layer of the protective film for the process is prepared, and the surface on the dot pattern side (or mat layer side) of the sample is a water column type. The Oken type air permeability tester (Asahi Seiko Co., Ltd., KY-5) was pressed against the measuring head surface, and the Oken type smoothness was measured according to JIS P8155: 2010.
＜密着防止＞
光学フィルムの片面に、工程用保護フィルムを貼り合わせたものを１０枚積層し、垂直方向から１００gの圧力を１分間かけた後、積層した状態のまま、バキュームツールを用いて、工程用保護フィルム付きの光学フィルムを１枚ずつ移動させた。この際に、一枚のみ持ち上げることができたものを「〇」、複数枚持ち上がったものを「×」とした。
<Prevention of adhesion>
Laminate 10 sheets of protective film on one side of the optical film, apply a pressure of 100 g from the vertical direction for 1 minute, and then use the vacuum tool to maintain the laminated state. The attached optical films were moved one by one. At this time, “◯” indicates that only one sheet could be lifted, and “×” indicates that several sheets were lifted.
＜情報読み取り性＞
（平面）
透明フィルムにＱＲコード（登録商標）を印刷し、その上に工程用保護フィルムを貼り合わせ、工程用保護フィルムが上を向くように平面上に設置した。１０ｃｍ上方にセットした携帯電話のカメラでＱＲコード（登録商標）の読み取り性を評価した。その結果、瞬時に読み取れたものを「〇」、読み取りに時間がかかったものを「△」、読み取れなかったものを「×」とした。
（曲面）
直径９５ｍｍの筒表面にＱＲコード（登録商標）が印刷された透明フィルムを貼り合わせ、その上に工程用保護フィルムを貼り合わせた。１０ｃｍ離れた箇所から携帯電話のカメラでＱＲコード（登録商標）の読み取り性を評価した。瞬時に読み取れたものを「〇」、読み取りに時間がかかったものを「△」、読み取れなかったものを「×」とした。
<Information readability>
(Plane)
A QR code (registered trademark) was printed on the transparent film, a process protective film was bonded thereon, and the process protective film was placed on a flat surface so that the process protective film faced up. QR code (registered trademark) readability was evaluated with a mobile phone camera set 10 cm above. As a result, “◯” indicates that the reading was instantaneous, “Δ” indicates that the reading took a long time, and “×” indicates that the reading failed.
(curved surface)
A transparent film on which a QR code (registered trademark) was printed was bonded to the surface of a cylinder having a diameter of 95 mm, and a process protective film was bonded thereto. QR code (registered trademark) readability was evaluated with a mobile phone camera from a location 10 cm away. Those that could be read instantly were marked with “◯”, those that took a long time to read were “△”, and those that could not be read were marked with “X”.
［実施例１〜５］、［比較例１］
厚み２５μｍの透明ポリエステルフィルム（東レ社製、ルミラー２５Ｓ１０）の一方の面に、アクリルポリオール（綜研化学社製、サーモラックＥＦ−４３）が１００部、イソシアネート系硬化剤（日本ポリウレタン社製、コロネートＬ）が３部、マット剤（シリカ、平均粒子径９μｍ）が６部、希釈溶剤からなるドットパターン形成用塗布液を調製し、グラビア印刷によりドットパターンを印刷した。なお、実施例１〜４及び比較例１は、ドット中心間の距離が１ｍｍ、ドット密度が１００個／ｃｍ２となる版を使用し、実施例５は、ドット中心間の距離が２ｍｍ、ドット密度が１２．５個／ｃｍ２となる版を使用した。また、ドットの直径及びドットの高さは、ドットパターン形成用塗布液の固形分濃度により、表１の値に調整した。ドットの直径及びドットの高さは、顕微鏡観察により確認した。
次いで、透明ポリエステルフィルムのドットパターンとは反対側の面に、アクリル系接着剤（綜研化学社製、ＳＫダイン１４９１Ｈ）及び希釈溶剤からなる接着剤層塗布液を塗布、乾燥し、厚み１０μｍの接着剤層を形成し、実施例１〜５及び比較例１の工程用保護フィルムを得た。
[Examples 1 to 5], [Comparative Example 1]
On one surface of a transparent polyester film having a thickness of 25 μm (manufactured by Toray Industries, Lumirror 25S10), 100 parts of acrylic polyol (manufactured by Soken Chemical Co., Thermolac EF-43), isocyanate curing agent (manufactured by Nippon Polyurethane Co., Ltd., Coronate L) ) 3 parts, a matting agent (silica, average particle size 9 μm) 6 parts, a coating solution for forming a dot pattern comprising a diluting solvent was prepared, and a dot pattern was printed by gravure printing. In Examples 1 to 4 and Comparative Example 1, a plate in which the distance between the dot centers is 1 mm and the dot density is 100 / cm 2 is used, and in Example 5, the distance between the dot centers is 2 mm. A plate having a density of 12.5 pieces / cm 2 was used. The dot diameter and dot height were adjusted to the values shown in Table 1 depending on the solid content concentration of the dot pattern forming coating solution. The diameter of the dot and the height of the dot were confirmed by microscopic observation.
Next, an adhesive layer coating solution comprising an acrylic adhesive (manufactured by Soken Chemical Co., Ltd., SK Dyne 1491H) and a diluting solvent is applied to the surface opposite to the dot pattern of the transparent polyester film, dried, and bonded with a thickness of 10 μm. An agent layer was formed, and protective films for processes of Examples 1 to 5 and Comparative Example 1 were obtained.
［比較例２］
厚み２５μｍの透明ポリエステルフィルム（東レ社製、ルミラー２５Ｓ１０）の一方の面に、実施例１のドットパターン形成用塗布液を乾燥後の厚みが３μｍとなるように塗布、乾燥し、マット層を形成した。次いで、マット層とは反対側の面に、実施例１と同様の接着剤層を形成し、工程用保護フィルムを得た。
[Comparative Example 2]
On one surface of a 25 μm thick transparent polyester film (Lumirror 25S10, manufactured by Toray Industries, Inc.), the dot pattern forming coating solution of Example 1 was applied and dried to a thickness of 3 μm to form a mat layer. did. Subsequently, the adhesive layer similar to Example 1 was formed in the surface on the opposite side to a mat | matte layer, and the protective film for processes was obtained.
［比較例３］
マット層の厚みを６μｍに変更した以外は、比較例２と同様にして、工程用保護フィルムを得た。
[Comparative Example 3]
A process protective film was obtained in the same manner as in Comparative Example 2 except that the thickness of the mat layer was changed to 6 μm.
［比較例４］
実施例１のドットパターン形成用塗布液に、シリコーンパウダー（信越化学社製、ＫＭＰ−６０１、平均粒子径１２μｍ）を１部添加した以外は、比較例２と同様にして、工程用保護フィルムを得た。
[Comparative Example 4]
A protective film for a process was prepared in the same manner as in Comparative Example 2, except that 1 part of silicone powder (manufactured by Shin-Etsu Chemical Co., Ltd., KMP-601, average particle size: 12 μm) was added to the dot pattern forming coating liquid of Example 1. Obtained.
［比較例５］
実施例１のドットパターン形成用塗布液に、シリコーンパウダー（信越化学社製、ＫＭＰ−６０１、平均粒子径１２μｍ）を３部添加し、乾燥後の厚みが２μｍとなるように塗布、乾燥し、マット層を形成した。次いで、マット層とは反対側の面に、実施例１と同様の接着剤層を形成し、工程用保護フィルムを得た。
[Comparative Example 5]
3 parts of silicone powder (manufactured by Shin-Etsu Chemical Co., Ltd., KMP-601, average particle size 12 μm) is added to the coating liquid for forming the dot pattern of Example 1, and the coating is dried so that the thickness after drying is 2 μm. A mat layer was formed. Subsequently, the adhesive layer similar to Example 1 was formed in the surface on the opposite side to a mat | matte layer, and the protective film for processes was obtained.
［比較例６］
比較例２のマット層上に、帯電防止性コーティング材（三菱化学社製、サフトマー）を溶剤で希釈してなる帯電防止層塗布液を乾燥後の厚みが１μｍとなるように塗布、乾燥し、帯電防止層を形成した以外は、比較例２と同様にして、工程用保護フィルムを得た。
[Comparative Example 6]
On the mat layer of Comparative Example 2, an antistatic coating material (Saftmer manufactured by Mitsubishi Chemical Co., Ltd.) diluted with a solvent was applied and dried so that the thickness after drying was 1 μm. A protective film for a process was obtained in the same manner as in Comparative Example 2 except that an antistatic layer was formed.
表１の結果から明らかなように、実施例１〜５の工程用保護シートは、基材の接着剤層を有する面とは反対側の面に、王研式平滑度が６０秒未満となるドットパターンを有することから、密着防止性に優れつつ、バーコード等の情報の読み取り性を満足できるものであった。特に、実施例１〜４のものは、ドットパターンの直径、高さ、面積割合及び密度が好適な条件であることから、曲面での情報読み取り性も満足できるものであった。
比較例１の工程用保護シートは、実施例と同様にドットパターンを有するものであるが、王研式平滑度が６０秒以上であることから、密着防止性を満足できないものであった。
比較例２、３及び６の工程用保護シートは、王研式平滑度が６０秒以上であるため、密着防止性を満足できないものであった。また、比較例３の工程用保護シートは、ドットパターンではなくマット層を形成したものであるため、凹凸が全面に渡って形成され、情報の読み取り性も満足できないものであった。また、比較例６の工程用保護シートは、帯電防止層を有しているにも関わらず、バキュームツールを用いて工程用保護フィルム付きの光学フィルムを移動させる際に、複数枚持ち上がる結果となっている。このことは、帯電を防止しても工程用保護フィルム付きの光学フィルムの密着を防ぐことはできず、王研式平滑度を小さくすることが密着を防止することに重要であることを示している。
比較例４及び５の工程用保護シートは、王研式平滑度が６０秒未満であるものの、ドットパターンではなくマット層を形成したものであるため、凹凸が全面に渡って形成され、情報の読み取り性を満足できないものであった。
As is clear from the results in Table 1, the process protective sheets of Examples 1 to 5 have Oken-type smoothness of less than 60 seconds on the surface opposite to the surface having the adhesive layer of the base material. Since it had a dot pattern, it was excellent in adhesion preventing properties while satisfying the readability of information such as barcodes. In particular, in Examples 1 to 4, since the diameter, height, area ratio, and density of the dot pattern are suitable conditions, the information readability on a curved surface can be satisfied.
Although the process protective sheet of Comparative Example 1 has a dot pattern as in the Examples, the Oken type smoothness is 60 seconds or more, and thus the adhesion preventing property cannot be satisfied.
The protective sheets for processes of Comparative Examples 2, 3 and 6 were unable to satisfy the adhesion prevention property because the Oken type smoothness was 60 seconds or more. Further, since the process protection sheet of Comparative Example 3 was formed with a mat layer instead of a dot pattern, the unevenness was formed over the entire surface, and the information readability was not satisfactory. In addition, the process protective sheet of Comparative Example 6 has a result that a plurality of sheets are lifted when the optical film with the process protective film is moved using a vacuum tool, despite having the antistatic layer. ing. This indicates that even if charging is prevented, adhesion of the optical film with the process protective film cannot be prevented, and it is important to reduce the Oken type smoothness to prevent adhesion. Yes.
Although the protective sheet for process of Comparative Examples 4 and 5 has an Oken type smoothness of less than 60 seconds, a mat layer is formed instead of a dot pattern. The readability was not satisfactory.
Claims (5)