JP6223500B2 - Adhesive, adhesive layer, and adhesive sheet - Google Patents

Description

  The present invention relates to an adhesive capable of realizing a low dielectric constant, an adhesive layer obtained from the adhesive, and an adhesive sheet having such an adhesive layer on at least one side of a support.

  The pressure-sensitive adhesive layer or pressure-sensitive adhesive sheet of the present invention is suitable for optical applications. For example, the pressure-sensitive adhesive layer or pressure-sensitive adhesive sheet of the present invention can be used for the production of image display devices such as liquid crystal display devices, organic EL (electroluminescence) display devices, PDP (plasma display panels), and electronic paper, optical methods, ultrasonic waves, and the like. It can be used suitably for the manufacturing use of input devices, such as a touch panel, such as a system, an electrostatic capacity system, and a resistive film system. In particular, it is suitably used for a capacitive touch panel.

  The pressure-sensitive adhesive sheet of the present invention is useful as a pressure-sensitive adhesive optical member using an optical member as a support. For example, when a transparent conductive film is used as the optical member, the adhesive optical member is used as a transparent conductive film with an adhesive layer. The said transparent conductive film with an adhesive layer is used for the transparent electrode in the said image display apparatus, a touchscreen, etc., after processing is made suitably. In particular, the transparent conductive film with an adhesive layer is suitably used for an electrode substrate of an input device of a capacitive touch panel by patterning a transparent conductive thin film. In addition, the transparent conductive film with the pressure-sensitive adhesive layer is used for antistatic and electromagnetic wave shielding of transparent articles, liquid crystal light control glass, and transparent heaters.

  Moreover, when using an optical film as an optical member, an adhesive optical member is used as an optical film with an adhesive layer. The said optical film with an adhesive layer is used for image display apparatuses, such as a liquid crystal display device and an organic electroluminescence display. As the optical film, a polarizing plate, a phase difference plate, an optical compensation film, a brightness enhancement film, and a film in which these are laminated can be used.

  In recent years, an input device using a combination of an image display device such as a mobile phone or a portable music player and a touch panel has become widespread. In particular, capacitive touch panels are rapidly spreading due to their functionality.

  Currently, many transparent conductive films used for touch panels are known in which a transparent conductive thin film (ITO film) is laminated on a transparent plastic film substrate or glass. A transparent conductive film is laminated | stacked on another member through an adhesive layer. Various types of pressure-sensitive adhesive layers have been proposed (see Patent Documents 1 to 4).

  When the transparent conductive film is used for an electrode substrate of a capacitive touch panel, a film obtained by patterning the transparent conductive thin film is used. A transparent conductive film having such a patterned transparent conductive thin film is used by being laminated with an adhesive layer together with other transparent conductive films and the like. These transparent conductive films are suitably used for multi-touch type input devices that can be operated simultaneously with two or more fingers. In other words, the capacitive touch panel has a mechanism for sensing when the output signal of the position changes when the touch panel is touched with a finger or the like, and the amount of change of the signal exceeds a certain threshold.

JP 2003-238915 A JP 2003-342542 A JP 2004-231723 A JP 2002-363530 A

  As described above, the dielectric constant of the member and film constituting the touch panel is an important numerical value because it relates to the response of the touch panel. On the other hand, with the spread of touch panels in recent years, higher performance is required for touch panels, and high performance is also required for transparent conductive films and pressure-sensitive adhesive layers that are constituent members, and thinning is one of them. is there. However, there is a problem that the designed capacitance value changes if the pressure-sensitive adhesive layer is simply thinned. In order to reduce the thickness of the pressure-sensitive adhesive layer without changing the value of the capacitance value, it is required to lower the dielectric constant of the pressure-sensitive adhesive layer. In addition, in order to improve visibility, an air layer of glass with printing or a film and an optical film or an air layer above the LCD may be filled with an adhesive layer, but on the other hand, If the dielectric constant is high, malfunction may occur. Also from the viewpoint of preventing such malfunction, the adhesive layer is required to have a low dielectric constant. Furthermore, the reduction in the dielectric constant of the pressure-sensitive adhesive layer is expected to improve the response speed and sensitivity of the touch panel.

  Then, an object of this invention is to provide the adhesive which can implement | achieve the adhesive layer of satisfying adhesive performance and a low dielectric constant.

  Moreover, an object of this invention is to provide the adhesive layer formed with the said adhesive, and also to provide the adhesive sheet which has the said adhesive layer.

  As a result of intensive studies to solve the above problems, the present inventors have found the following pressure-sensitive adhesive and have completed the present invention.

  That is, the present invention provides a (meth) acryl obtained by polymerizing a monomer component containing 19 to 99.5% by weight of an alkyl (meth) acrylate having a branched alkyl group having 10 to 24 carbon atoms at the terminal of the ester group. The present invention relates to an adhesive comprising a polymer.

  In the above-mentioned pressure-sensitive adhesive, the monomer component further contains 0.1 to 30% by weight of at least one functional group-containing monomer selected from a carboxyl group-containing monomer, a hydroxyl group-containing monomer, and a monomer having a cyclic ether group. Can do.

  In the above-mentioned pressure-sensitive adhesive, the monomer component further includes an alkyl (meth) acrylate having a branched alkyl group having 3 to 9 carbon atoms at the terminal of the ester group, and a linear alkyl group having 1 to 24 carbon atoms at the terminal of the ester group. 0.5% by weight or more of at least one selected from alkyl methacrylate having a cyclic alkyl group and alkyl (meth) acrylate having a cyclic alkyl group at the terminal of the ester group can be contained.

  In the pressure-sensitive adhesive, the monomer component may further contain 3% by weight or less of a polyfunctional monomer.

  The pressure-sensitive adhesive preferably further contains 0.01 to 5 parts by weight of a crosslinking agent with respect to 100 parts by weight of the (meth) acrylic polymer.

  The said adhesive is suitable as an adhesive for optical members used for an optical member.

  Moreover, this invention relates to the adhesive layer characterized by being obtained from the adhesive in any one of said.

  The pressure-sensitive adhesive layer preferably has a relative dielectric constant of 3.5 or less at a frequency of 100 kHz.

  The pressure-sensitive adhesive layer preferably has a gel fraction of 20 to 98% by weight.

  The pressure-sensitive adhesive layer preferably has a haze of 2% or less when the pressure-sensitive adhesive layer has a thickness of 25 μm.

  The said adhesive layer is suitable as an adhesive layer for optical members used for an optical member.

  The present invention also relates to a pressure-sensitive adhesive sheet, wherein the pressure-sensitive adhesive layer described above is formed on at least one side of a support.

  In the pressure-sensitive adhesive sheet, it is preferable that a 90-degree peel adhesive force (300 mm / min) of the pressure-sensitive adhesive layer to the alkali-free glass is 0.5 N / 20 mm or more.

  The said adhesive sheet is suitable as an adhesive sheet for optical members used for an optical member. Moreover, the said adhesive sheet can be used as an adhesive optical member using the optical member as a support body.

  The (meth) acrylic polymer as the main component in the pressure-sensitive adhesive of the present invention is obtained by polymerizing a monomer component containing a predetermined amount of an alkyl (meth) acrylate having a long-chain branched alkyl group. . According to the pressure-sensitive adhesive of the present invention, a low dielectric constant pressure-sensitive adhesive layer can be realized by the action of the long-chain branched alkyl group, and the adhesive performance can be satisfied. Moreover, even when the air layer is filled with an adhesive layer, malfunction can be prevented because the adhesive layer has a low dielectric constant.

  In order to lower the dielectric constant, it is considered that the molecular dipole moment is reduced and the molar volume is increased from the Clausius-Mossotti equation. Since the alkyl (meth) acrylate related to the main monomer unit constituting the (meth) acrylic polymer as the main component in the pressure-sensitive adhesive of the present invention has a long-chain branched alkyl group, the pressure-sensitive adhesive of the present invention In the obtained pressure-sensitive adhesive layer, the molar volume is increased, and it is considered that the dipole moment is decreased due to the branched alkyl group. Thus, the pressure-sensitive adhesive layer having a balance between the two so that the molar volume is increased and the dipole moment is reduced has a branched alkyl group having 10 to 24 carbon atoms as an alkyl group at the end of the ester group. This is considered to be achieved when alkyl (meth) acrylate is used.

  For example, the pressure-sensitive adhesive layer of the present invention satisfies the low dielectric constant of 3.5 or less at 100 kHz, thereby reducing the thickness of the pressure-sensitive adhesive layer of the present invention and using it for a capacitive touch panel. Even when it is used for an adhesive layer applied to a conductive film, it can be applied without changing the numerical value of the capacitance value designed by a capacitive touch panel.

It is a figure which shows an example of the capacitive touch panel in which the adhesive layer or adhesive sheet of this invention is used.

  The pressure-sensitive adhesive of the present invention was obtained by polymerizing a monomer component containing 19 to 99.5% by weight of an alkyl (meth) acrylate having a branched alkyl group having 10 to 24 carbon atoms at the terminal of the ester group (meta ) Including acrylic polymer. Alkyl (meth) acrylate refers to alkyl acrylate and / or alkyl methacrylate, and (meth) in the present invention has the same meaning.

  The Tg of the homopolymer related to the alkyl (meth) acrylate having a branched alkyl group having 10 to 24 carbon atoms at the end of the ester group is preferably −80 to 0 ° C., more preferably −70 to −10. It is preferable that it is ° C. When the Tg of the homopolymer is −80 ° C. or lower, the elastic modulus of the pressure-sensitive adhesive at room temperature may be excessively lowered, and when it exceeds 0 ° C., the adhesive force may be decreased. The Tg of the homopolymer is a value measured by a differential scanning calorimetry system (DSC). In addition, the branched alkyl group has 10 to 24 carbon atoms from the viewpoint of satisfying a low dielectric constant and an appropriate elastic modulus, but an alkyl having a preferable alkyl group depending on the method for producing a (meth) acrylic polymer. (Meth) acrylate can be selected. For example, when producing a (meth) acrylic polymer by solution polymerization or the like, the alkyl group preferably further has 10 to 18 carbon atoms, more preferably 10 to 16 carbon atoms, and further preferably 10 to 10 carbon atoms. 14 is preferred. When producing a (meth) acrylic polymer by radiation polymerization or the like, the alkyl group preferably further has 12 to 18 carbon atoms, and more preferably 14 to 18 carbon atoms. In addition, even if the Tg of the homopolymer related to the alkyl (meth) acrylate is -80 to 0 ° C., if the alkyl group is linear or the number of carbon atoms is 9 or less, the adhesive layer has a low dielectric constant. The effect is not great.

  Examples of the alkyl (meth) acrylate having a branched alkyl group having 10 to 24 carbon atoms at the end of the ester group include, for example, isodecyl acrylate (carbon number 10, homopolymer Tg = −60 ° C., hereinafter, simply Tg and Abbreviation), isodecyl methacrylate (carbon number 10, Tg = −41 ° C.), isomisticyl acrylate (carbon number 14, Tg = −56 ° C.), isostearyl acrylate (carbon number 18, Tg = −18 ° C.), 2- Examples include propylheptyl acrylate, isoundecyl acrylate, isododecyl acrylate, isotridecyl acrylate, isopentadecyl acrylate, isohexadecyl acrylate, isoheptadecyl acrylate, and the above-mentioned methacrylate monomers. These can be used alone or in combination of two or more.

Further, among the branched alkyl groups having 10 to 24 carbon atoms, those having a t-butyl group, in particular, have a molar volume increased and a dipole moment decreased to obtain a pressure-sensitive adhesive layer having a balance between both. It is preferable at the point considered to be made. Examples of the alkyl (meth) acrylate having a branched alkyl group having 10 to 24 carbon atoms and having a t-butyl group include isostearyl acrylate represented by the following formula.

  In addition, as the alkyl (meth) acrylate having a branched alkyl group having 10 to 24 carbon atoms at the ester end, the alkyl methacrylate is more adhesive than the alkyl acrylate due to an increase in molar volume and a decrease in dipole moment. This is preferable in terms of the effect of reducing the dielectric constant of the layer. On the other hand, alkyl acrylate is more preferable than alkyl methacrylate in that the polymerization time for producing a (meth) acrylic polymer can be shortened and productivity can be improved. In particular, when a (meth) acrylic polymer is produced by radiation polymerization, an alkyl acrylate is preferable.

  In the present invention, the alkyl (meth) acrylate having a branched alkyl group having 10 to 24 carbon atoms at the end of the ester group is 19 to 99.5 with respect to all monomer components forming the (meth) acrylic polymer. %, Preferably 25 to 99.5% by weight, more preferably 35 to 99.5% by weight, still more preferably 40 to 99.5% by weight, still more preferably 45 to 99.5% by weight. %, More preferably 45 to 96% by weight. The use of 19% by weight or more is preferable from the viewpoint of reducing the dielectric constant, and the use of 99.5% by weight or less is preferable from the viewpoint of maintaining adhesive strength.

  The monomer component forming the (meth) acrylic polymer of the present invention further includes at least one functional group-containing monomer selected from a carboxyl group-containing monomer, a hydroxyl group-containing monomer, and a monomer having a cyclic ether group. Can do.

  As the carboxyl group-containing monomer, a monomer having a polymerizable functional group having an unsaturated double bond such as a (meth) acryloyl group or a vinyl group and having a carboxyl group can be used without particular limitation. Examples of the carboxyl group-containing monomer include (meth) acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, itaconic acid, maleic acid, fumaric acid, crotonic acid, and isocrotonic acid. Can be used alone or in combination. These anhydrides can be used for itaconic acid and maleic acid. Among these, acrylic acid and methacrylic acid are preferable, and acrylic acid is particularly preferable. In addition, a carboxyl group-containing monomer can be arbitrarily used for the monomer component used for manufacture of the (meth) acrylic-type polymer of this invention, On the other hand, it is not necessary to use a carboxyl group-containing monomer. A pressure-sensitive adhesive containing a (meth) acrylic polymer obtained from a monomer component not containing a carboxyl group-containing monomer can form a pressure-sensitive adhesive layer in which metal corrosion caused by a carboxyl group is reduced.

As the hydroxyl group-containing monomer, a monomer having a polymerizable functional group having an unsaturated double bond such as a (meth) acryloyl group or a vinyl group and having a hydroxyl group can be used without particular limitation. Examples of the hydroxyl group-containing monomer include 2-hydroxybutyl (meth) acrylate, 3-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, 6-hydroxyhexyl (meth) acrylate, 8-hydroxyoctyl ( Hydroxyalkyl (meth) acrylates such as (meth) acrylate, 10-hydroxydecyl (meth) acrylate, 12-hydroxylauryl (meth) acrylate, etc .; hydroxyalkylcyclos such as (4-hydroxymethylcyclohexyl) methyl (meth) acrylate An alkane (meth) acrylate is mentioned. Other examples include hydroxyethyl (meth) acrylamide, allyl alcohol, 2-hydroxyethyl vinyl ether, 4-hydroxybutyl vinyl ether, diethylene glycol monovinyl ether, and the like. These can be used alone or in combination. Of these, hydroxyalkyl (meth) acrylate is preferred.

  As the monomer having a cyclic ether group, a monomer having a polymerizable functional group having an unsaturated double bond such as a (meth) acryloyl group or a vinyl group and a cyclic ether group such as an epoxy group or an oxetane group. It can be used without particular limitation. Examples of the epoxy group-containing monomer include glycidyl (meth) acrylate, 3,4-epoxycyclohexylmethyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate glycidyl ether, and the like. Examples of the oxetane group-containing monomer include 3-oxetanylmethyl (meth) acrylate, 3-methyl-oxetanylmethyl (meth) acrylate, 3-ethyl-oxetanylmethyl (meth) acrylate, and 3-butyl-oxetanylmethyl (meth) acrylate. , 3-hexyl oxetanylmethyl (meth) acrylate, and the like. These can be used alone or in combination.

  In this invention, it is preferable to use the said functional group containing monomer in the ratio of 0.1 to 30 weight% with respect to all the monomer components which form a (meth) acrylic-type polymer. The functional group-containing monomer is preferably 0.1% by weight or more, more preferably 0.5% by weight or more, and further 0.8% by weight from the viewpoint of enhancing adhesive force and cohesive force. This is preferred. On the other hand, if the amount of the functional group-containing monomer is too large, the pressure-sensitive adhesive layer becomes hard and the adhesive strength may decrease, and the viscosity of the pressure-sensitive adhesive may become too high or gel. The functional group-containing monomer is preferably 30% by weight or less, more preferably 27% by weight or less, and even more preferably 25% by weight or less based on all monomer components forming the (meth) acrylic polymer. preferable.

The monomer component that forms the (meth) acrylic polymer of the present invention may contain a copolymerization monomer other than the functional group-containing monomer. Examples of other copolymerizable monomers include CH ₂ ═C (R ¹ ) COOR ² (wherein R ¹ is hydrogen or a methyl group, R ² is an unsubstituted alkyl group having 1 to 24 carbon atoms or a substituted alkyl group). An alkyl (meth) acrylate represented by the formula (excluding the case of a branched alkyl group having 10 to 24 carbon atoms).

Here, an unsubstituted alkyl group having 1 to 24 carbon atoms (more preferably 1 to 18 carbon atoms) or a substituted alkyl group as R ² is a linear or branched alkyl group or a cyclic cyclo group. This refers to an alkyl group, excluding the case of a branched alkyl group having 10 to 24 carbon atoms. Specific examples of R ² include a branched alkyl group having 3 to 9 carbon atoms and a cyclic alkyl group. In the case of a substituted alkyl group, the substituent is preferably an aryl group having 3 to 8 carbon atoms or an aryloxy group having 3 to 8 carbon atoms. The aryl group is not limited, but is preferably a phenyl group. As the alkyl (meth) acrylate, alkyl methacrylate is preferable to alkyl acrylate in terms of lowering the dielectric constant due to an increase in molar volume and a decrease in dipole moment.

Examples of such a monomer represented by CH ₂ ═C (R ¹ ) COOR ² include methyl (meth) acrylate, ethyl (meth) acrylate, n-butyl (meth) acrylate, and s-butyl (meth) acrylate. , T-butyl (meth) acrylate, isobutyl (meth) acrylate, n-pentyl (meth) acrylate, isopentyl (meth) acrylate, hexyl (meth) acrylate, heptyl (meth) acrylate, isoamyl (meth) acrylate, 2- Ethylhexyl (meth) acrylate, n-octyl (meth) acrylate, isooctyl (meth) acrylate, n-nonyl (meth) acrylate, isononyl (meth) acrylate, phenoxyethyl (meth) acrylate, benzyl (meth) acrylate, cyclohex Sil (meth) acrylate, 3,3,5-trimethylcyclohexyl (meth) acrylate, isobornyl (meth) acrylate, terpenes (meth) acrylate, dicyclopentanyl (meth) acrylate, and the like. These can be used alone or in combination.

In the present invention, the (meth) acrylate represented by CH ₂ ═C (R ¹ ) COOR ² can be used in an amount of 81% by weight or less based on the total monomer components forming the (meth) acrylic polymer. 76% by weight or less is preferable. Further, it is preferably 60% by weight or less, and more preferably 55% by weight or less. The (meth) acrylate represented by CH ₂ ═C (R ¹ ) COOR ² is preferably used in an amount of 5% by weight or more, and more preferably 10% by weight or more from the viewpoint of maintaining adhesive strength.

The (meth) acrylate represented by CH ₂ ═C (R ¹ ) COOR ² can be used in the above ratio, but a preferable ratio can be appropriately selected depending on the method for producing the (meth) acrylic polymer. it can. For example, when a (meth) acrylic polymer is produced by radiation polymerization or the like, the ratio of the (meth) acrylate represented by CH ₂ ═C (R ¹ ) COOR ² to the total monomer components is From the viewpoint, it is preferably more than 0% by weight and 80% by weight or less, and more preferably 20 to 50% by weight. In this case, the proportion of the alkyl (meth) acrylate having a branched alkyl group having 10 to 24 carbon atoms at the ester terminal is preferably 20 to 80% by weight, more preferably 30 to 70% by weight. Is preferred.

  Other copolymer monomers include vinyl monomers such as vinyl acetate, vinyl propionate, styrene, α-methylstyrene, N-vinylcaprolactam, N-vinylpyrrolidone; (meth) acrylic acid polyethylene glycol, (meth) acrylic acid Glycol acrylic ester monomers such as polypropylene glycol, methoxyethylene glycol (meth) acrylate, methoxypolypropylene glycol (meth) acrylate; tetrahydrofurfuryl (meth) acrylate, fluorine (meth) acrylate, silicone (meth) acrylate and 2 -Acrylic acid ester monomers such as methoxyethyl acrylate; amide group-containing monomers, amino group-containing monomers, imide group-containing monomers, N-acryloylmorpholine, vinyl ether mono Chromatography, or the like can also be used.

  Furthermore, the silane type monomer containing a silicon atom, etc. are mentioned. Examples of the silane monomer include 3-acryloxypropyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, 4-vinylbutyltrimethoxysilane, 4-vinylbutyltriethoxysilane, and 8-vinyloctyltrimethoxysilane. , 8-vinyloctyltriethoxysilane, 10-methacryloyloxydecyltrimethoxysilane, 10-acryloyloxydecyltrimethoxysilane, 10-methacryloyloxydecyltriethoxysilane, 10-acryloyloxydecyltriethoxysilane, and the like.

  The monomer component that forms the (meth) acrylic polymer of the present invention contains a polyfunctional monomer as necessary in order to adjust the cohesive strength of the pressure-sensitive adhesive, in addition to the monofunctional monomer exemplified above. be able to.

  The polyfunctional monomer is a monomer having at least two polymerizable functional groups having an unsaturated double bond such as a (meth) acryloyl group or a vinyl group, such as (poly) ethylene glycol di (meth) acrylate, (Poly) propylene glycol di (meth) acrylate, neopentyl glycol di (meth) acrylate, pentaerythritol di (meth) acrylate, pentaerythritol tri (meth) acrylate, dipentaerythritol hexa (meth) acrylate, 1,2-ethylene Glycol di (meth) acrylate, 1,6-hexanediol di (meth) acrylate, 1,12-dodecanediol di (meth) acrylate, trimethylolpropane tri (meth) acrylate, tetramethylol methanetri (meth) acrylate Ester compounds of polyhydric alcohols such as carbonate and (meth) acrylic acid; allyl (meth) acrylate, vinyl (meth) acrylate, divinylbenzene, epoxy acrylate, polyester acrylate, urethane acrylate, butyl di (meth) acrylate, hexyl di ( And (meth) acrylate. Among these, trimethylolpropane tri (meth) acrylate, hexanediol di (meth) acrylate, and dipentaerythritol hexa (meth) acrylate can be preferably used. A polyfunctional monomer can be used individually by 1 type or in combination of 2 or more types.

  The amount of the polyfunctional monomer used varies depending on the molecular weight, the number of functional groups, and the like, but it can be used at 3% by weight or less with respect to all monomer components forming the (meth) acrylic polymer, and 2% by weight or less. More preferably, 1% by weight or less is preferable. When the usage-amount of a polyfunctional monomer exceeds 3 weight%, the cohesion force of an adhesive will become high too much, for example, and adhesive force may fall.

  The (meth) acrylic polymer of the present invention preferably has a Tg of −70 to 0 ° C., more preferably −65 to −10 ° C. By using such a (meth) acrylic polymer, the final pressure-sensitive adhesive obtained can have good heat resistance. The Tg of the (meth) acrylic polymer is a theoretical value calculated from the monomer unit constituting the (meth) acrylic polymer and its ratio by the FOX formula.

  The production of such a (meth) acrylic polymer can be appropriately selected from known production methods such as radiation polymerization such as solution polymerization and UV polymerization, various radical polymerizations such as bulk polymerization and emulsion polymerization. Further, the (meth) acrylic polymer obtained may be any of a random copolymer, a block copolymer, a graft copolymer, and the like.

  The polymerization initiator, chain transfer agent, emulsifier and the like used for radical polymerization are not particularly limited and can be appropriately selected and used. In addition, the weight average molecular weight of a (meth) acrylic-type polymer can be controlled by the usage-amount of a polymerization initiator and a chain transfer agent, and reaction conditions, The usage-amount is suitably adjusted according to these kinds.

  For example, in solution polymerization or the like, for example, ethyl acetate, toluene or the like is used as a polymerization solvent. As a specific example of solution polymerization, the reaction is performed under an inert gas stream such as nitrogen, and a polymerization initiator is added, and the reaction is usually performed at about 50 to 70 ° C. under reaction conditions of about 5 to 30 hours.

  Examples of the thermal polymerization initiator used for solution polymerization include 2,2′-azobisisobutyronitrile, 2,2′-azobis-2-methylbutyronitrile, 2,2′-azobis (2 -Methylpropionic acid) dimethyl, 4,4'-azobis-4-cyanovaleric acid, azobisisovaleronitrile, 2,2'-azobis (2-amidinopropane) dihydrochloride, 2,2'-azobis [2- (5-Methyl-2-imidazolin-2-yl) propane] dihydrochloride, 2,2′-azobis (2-methylpropionamidine) disulfate, 2,2′-azobis (N, N′-dimethyleneisobutyl) Amidine), 2,2′-azobis [N- (2-carboxyethyl) -2-methylpropionamidine] hydrate (manufactured by Wako Pure Chemical Industries, Ltd., VA-057) Any azo initiator, persulfate such as potassium persulfate, ammonium persulfate, di (2-ethylhexyl) peroxydicarbonate, di (4-t-butylcyclohexyl) peroxydicarbonate, di-sec-butylperoxy Dicarbonate, t-butylperoxyneodecanoate, t-hexylperoxypivalate, t-butylperoxypivalate, dilauroyl peroxide, di-n-octanoyl peroxide, 1,1,3,3 -Tetramethylbutylperoxy-2-ethylhexanoate, di (4-methylbenzoyl) peroxide, dibenzoyl peroxide, t-butylperoxyisobutyrate, 1,1-di (t-hexylperoxy) cyclohexane , Peracids such as t-butyl hydroperoxide and hydrogen peroxide Physical initiators, combinations of persulfates and sodium bisulfite, redox initiators combining peroxides and reducing agents, such as combinations of peroxides and sodium ascorbate, etc. It is not limited.

  The polymerization initiator may be used alone or in combination of two or more, but the total content is 0.005 to 1 part by weight with respect to 100 parts by weight of the monomer. Is preferably about 0.02 to 0.5 parts by weight.

  In order to produce the (meth) acrylic polymer having the weight average molecular weight using, for example, 2,2′-azobisisobutyronitrile as the polymerization initiator, the amount of the polymerization initiator used is a monomer. The amount is preferably about 0.06 to 0.2 part by weight, more preferably about 0.08 to 0.175 part by weight with respect to 100 parts by weight of the total amount of the components.

  Examples of the chain transfer agent include lauryl mercaptan, glycidyl mercaptan, mercaptoacetic acid, 2-mercaptoethanol, thioglycolic acid, 2-ethylhexyl thioglycolate, and 2,3-dimercapto-1-propanol. The chain transfer agent may be used alone or in combination of two or more, but the total content is 0.1 parts by weight with respect to 100 parts by weight of the total amount of monomer components. Less than or equal to

  Examples of the emulsifier used in emulsion polymerization include anionic emulsifiers such as sodium lauryl sulfate, ammonium lauryl sulfate, sodium dodecylbenzenesulfonate, ammonium polyoxyethylene alkyl ether sulfate, sodium polyoxyethylene alkyl phenyl ether sulfate, and polyoxy Nonionic emulsifiers such as ethylene alkyl ether, polyoxyethylene alkyl phenyl ether, polyoxyethylene fatty acid ester, and polyoxyethylene-polyoxypropylene block polymer are exemplified. These emulsifiers may be used alone or in combination of two or more.

  Further, as reactive emulsifiers, as emulsifiers into which radical polymerizable functional groups such as propenyl groups and allyl ether groups are introduced, specifically, for example, Aqualon HS-10, HS-20, KH-10, BC-05 BC-10, BC-20 (all of which are manufactured by Daiichi Kogyo Seiyaku Co., Ltd.), Adeka Soap SE10N (manufactured by ADEKA), and the like. Reactive emulsifiers are preferable because they are incorporated into the polymer chain after polymerization and thus have improved water resistance. The amount of the emulsifier used is more preferably 0.3 to 5 parts by weight and 0.5 to 1 part by weight from the viewpoint of polymerization stability and mechanical stability with respect to 100 parts by weight of the total amount of monomer components.

  In addition, when the (meth) acrylic polymer is produced by radiation polymerization, the monomer component can be produced by polymerizing the monomer component by irradiating with radiation such as electron beam or UV. It is not particularly necessary to include a photopolymerization initiator in the monomer component, but when the radiation polymerization is performed by UV polymerization, an advantage that the polymerization time can be shortened, etc. From the above, a photopolymerization initiator can be contained in the monomer component. A photoinitiator can be used individually by 1 type or in combination of 2 or more types.

  The photopolymerization initiator is not particularly limited, but is not particularly limited as long as it initiates photopolymerization, and a commonly used photopolymerization initiator can be used. For example, benzoin ether photopolymerization initiator, acetophenone photopolymerization initiator, α-ketol photopolymerization initiator, aromatic sulfonyl chloride photopolymerization initiator, photoactive oxime photopolymerization initiator, benzoin photopolymerization initiator Agents, benzyl photopolymerization initiators, benzophenone photopolymerization initiators, ketal photopolymerization initiators, thioxanthone photopolymerization initiators, acylphosphine oxide photopolymerization initiators, and the like can be used.

  Specifically, examples of the benzoin ether photopolymerization initiator include benzoin methyl ether, benzoin ethyl ether, benzoin propyl ether, benzoin isopropyl ether, benzoin isobutyl ether, 2,2-dimethoxy-1,2-diphenylethane- 1-one [trade name: Irgacure 651, manufactured by BASF Corporation], anisole methyl ether and the like can be mentioned. Examples of the acetophenone photopolymerization initiator include 1-hydroxycyclohexyl phenyl ketone [trade name: Irgacure 184, manufactured by BASF], 4-phenoxydichloroacetophenone, 4-t-butyl-dichloroacetophenone, 1- [4- ( 2-hydroxyethoxy) -phenyl] -2-hydroxy-2-methyl-1-propan-1-one [trade name: Irgacure 2959, manufactured by BASF Corp.], 2-hydroxy-2-methyl-1-phenyl-propane- 1-one [trade name: Darocur 1173, manufactured by BASF Corporation], methoxyacetophenone, and the like can be given. Examples of the α-ketol photopolymerization initiator include 2-methyl-2-hydroxypropiophenone, 1- [4- (2-hydroxyethyl) -phenyl] -2-hydroxy-2-methylpropane-1- ON etc. are mentioned. Examples of the aromatic sulfonyl chloride photopolymerization initiator include 2-naphthalene sulfonyl chloride. Examples of the photoactive oxime photopolymerization initiator include 1-phenyl-1,1-propanedione-2- (o-ethoxycarbonyl) -oxime.

  The benzoin photopolymerization initiator includes, for example, benzoin. Examples of the benzyl photopolymerization initiator include benzyl. Examples of the benzophenone-based photopolymerization initiator include benzophenone, benzoylbenzoic acid, 3,3′-dimethyl-4-methoxybenzophenone, polyvinylbenzophenone, α-hydroxycyclohexyl phenyl ketone, and the like. Examples of the ketal photopolymerization initiator include benzyl dimethyl ketal. Examples of the thioxanthone photopolymerization initiator include thioxanthone, 2-chlorothioxanthone, 2-methylthioxanthone, 2,4-dimethylthioxanthone, isopropylthioxanthone, 2,4-dichlorothioxanthone, 2,4-diethylthioxanthone, isopropylthioxanthone, 2,4-diisopropylthioxanthone, dodecylthioxanthone and the like are included.

Examples of the acylphosphine photopolymerization initiator include bis (2,6-dimethoxybenzoyl) phenylphosphine oxide, bis (2,6-dimethoxybenzoyl) (2,4,4-trimethylpentyl) phosphine oxide, bis ( 2,6-dimethoxybenzoyl) -n-butylphosphine oxide, bis (2,6-dimethoxybenzoyl)-(2-methylpropan-1-yl) phosphine oxide, bis (2,6-dimethoxybenzoyl)-(1- Methylpropan-1-yl) phosphine oxide, bis (2,6-dimethoxybenzoyl) -t-butylphosphine oxide, bis (2,6-dimethoxybenzoyl) cyclohexylphosphine oxide, bis (2,6-dimethoxybenzoyl) octylphosphine Oxides, bis (2-mes Xylbenzoyl) (2-methylpropan-1-yl) phosphine oxide, bis (2-methoxybenzoyl) (1-methylpropan-1-yl) phosphine oxide, bis (2,6-diethoxybenzoyl) (2-methyl Propan-1-yl) phosphine oxide, bis (2,6-diethoxybenzoyl) (1-methylpropan-1-yl) phosphine oxide, bis (2,6-dibutoxybenzoyl) (2-methylpropane-1- Yl) phosphine oxide, bis (2,4-dimethoxybenzoyl)
(2-methylpropan-1-yl) phosphine oxide, bis (2,4,6-trimethylbenzoyl) (2,4-dipentoxyphenyl) phosphine oxide, bis (2,6-dimethoxybenzoyl) benzylphosphine oxide, Bis (2,6-dimethoxybenzoyl) -2-phenylpropylphosphine oxide, bis (2,6-dimethoxybenzoyl) -2-phenylethylphosphine oxide, bis (2,6-dimethoxybenzoyl) benzylphosphine oxide, bis (2 , 6-Dimethoxybenzoyl) -2-phenylpropylphosphine oxide, bis (2,6-dimethoxybenzoyl) -2-phenylethylphosphine oxide, 2,6-dimethoxybenzoylbenzylbutylphosphine oxide, 2,6-dimethoxybenzo Rubenzyloctylphosphine oxide, bis (2,4,6-trimethylbenzoyl) -2,5-diisopropylphenylphosphine oxide, bis (2,4,6-trimethylbenzoyl) -2-methylphenylphosphine oxide, bis (2, 4,6-trimethylbenzoyl) -4-methylphenylphosphine oxide, bis (2,4,6-trimethylbenzoyl) -2,5-diethylphenylphosphine oxide, bis (2,4,6-trimethylbenzoyl) -2, 3,5,6-tetramethylphenylphosphine oxide, bis (2,4,6-trimethylbenzoyl) -2,4-di-n-butoxyphenylphosphine oxide, 2,4,6-trimethylbenzoyldiphenylphosphine oxide, bis (2,6-dimethoxybenzoyl) -2,4,4- Limethylpentylphosphine oxide, bis (2,4,6-trimethylbenzoyl) isobutylphosphine oxide, 2,6-dimethyloxybenzoyl-2,4,6-trimethylbenzoyl-n-butylphosphine oxide, bis (2,4,4) 6-trimethylbenzoyl) phenylphosphine oxide, bis (2,4,6-trimethylbenzoyl) -2,4-dibutoxyphenylphosphine oxide, 1,10-bis [bis (2,4,6-trimethylbenzoyl) phosphine oxide Decane, tri (2-methylbenzoyl) phosphine oxide, and the like.

  Although the usage-amount of a photoinitiator is not restrict | limited in particular, For example, 0.01-5 weight part with respect to 100 weight part of said monomer components, Preferably it is 0.05-3 weight part, More preferably, it is 0.05- 1.5 parts by weight, more preferably 0.1 to 1 part by weight

  If the amount of the photopolymerization initiator used is less than 0.01 parts by weight, the polymerization reaction may be insufficient. When the usage-amount of a photoinitiator exceeds 5 weight part, a photoinitiator may absorb an ultraviolet-ray and an ultraviolet-ray may not reach the inside of an adhesive layer. In this case, the polymerization rate is lowered, or the molecular weight of the produced polymer is reduced. And thereby, the cohesive force of the pressure-sensitive adhesive layer to be formed becomes low, and when the pressure-sensitive adhesive layer is peeled off from the film, a part of the pressure-sensitive adhesive layer may remain on the film and the film may not be reused. . In addition, a photopolymerization initiator can be used individually by 1 type or in combination of 2 or more types.

  The weight average molecular weight of the (meth) acrylic polymer of the present invention is preferably 400,000 to 2,500,000, more preferably 600,000 to 2,200,000. By making the weight average molecular weight larger than 400,000, it is possible to satisfy the durability of the pressure-sensitive adhesive layer, or to suppress the occurrence of adhesive residue due to the reduced cohesive force of the pressure-sensitive adhesive layer. On the other hand, when the weight average molecular weight is larger than 2.5 million, the bonding property and the adhesive strength tend to be lowered. Furthermore, in the solution system, the viscosity becomes too high, and coating may be difficult. The weight average molecular weight is a value measured by GPC (gel permeation chromatography) and calculated in terms of polystyrene. In addition, it is difficult to measure the molecular weight of the (meth) acrylic polymer obtained by radiation polymerization.

<Measurement of weight average molecular weight>
The weight average molecular weight of the obtained (meth) acrylic polymer was measured by GPC (gel permeation chromatography). The sample used was a filtrate obtained by dissolving the sample in tetrahydrofuran to make a 0.1 wt% solution, which was allowed to stand overnight, and then filtered through a 0.45 μm membrane filter.
・ Analyzer: HLC-8120GPC manufactured by Tosoh Corporation
Column: Tosoh Corporation, (meth) acrylic polymer: GM7000H _XL + GMH _XL + GMH _XL
Aromatic polymer: G3000HXL + 2000HXL + G1000HXL
・ Column size: 7.8mmφ × 30cm each 90cm in total
・ Eluent: Tetrahydrofuran (concentration 0.1% by weight)
・ Flow rate: 0.8 ml / min ・ Inlet pressure: 1.6 MPa
・ Detector: Differential refractometer (RI)
-Column temperature: 40 ° C
・ Injection volume: 100 μl
・ Eluent: Tetrahydrofuran ・ Detector: Differential refractometer ・ Standard sample: Polystyrene

  The pressure-sensitive adhesive of the present invention can contain a crosslinking agent. Examples of crosslinking agents include isocyanate crosslinking agents, epoxy crosslinking agents, silicone crosslinking agents, oxazoline crosslinking agents, aziridine crosslinking agents, silane crosslinking agents, alkyletherified melamine crosslinking agents, metal chelate crosslinking agents, Crosslinkers such as oxides are included. A crosslinking agent can be used alone or in combination of two or more. As said crosslinking agent, an isocyanate type crosslinking agent and an epoxy-type crosslinking agent are used preferably.

  The crosslinking agent may be used alone or in combination of two or more, but the total content is based on 100 parts by weight of the (meth) acrylic polymer. It is preferable to contain the said crosslinking agent in 0.01-5 weight part. The content of the crosslinking agent is preferably 0.01 to 4 parts by weight, more preferably 0.02 to 3 parts by weight.

  The isocyanate-based crosslinking agent refers to a compound having two or more isocyanate groups in a molecule (including isocyanate-regenerating functional groups in which isocyanate groups are temporarily protected by a blocking agent or quantification).

  Examples of the isocyanate-based crosslinking agent include aromatic isocyanates such as tolylene diisocyanate and xylene diisocyanate, alicyclic isocyanates such as isophorone diisocyanate, and aliphatic isocyanates such as hexamethylene diisocyanate.

More specifically, for example, lower aliphatic polyisocyanates such as butylene diisocyanate and hexamethylene diisocyanate, alicyclic isocyanates such as cyclopentylene diisocyanate, cyclohexylene diisocyanate and isophorone diisocyanate, 2,4-tolylene diisocyanate, Aromatic diisocyanates such as 4,4′-diphenylmethane diisocyanate, xylylene diisocyanate, polymethylene polyphenyl isocyanate, trimethylolpropane / tolylene diisocyanate trimer adduct (trade name Coronate L, manufactured by Nippon Polyurethane Industry Co., Ltd.), tri Methylolpropane / hexamethylene diisocyanate trimer adduct (manufactured by Nippon Polyurethane Industry Co., Ltd., trade name Coronate HL), hexamethylene diisocyanate Isocyanurate of anate (made by Nippon Polyurethane Industry Co., Ltd., trade name Coronate HX), etc., xylylene diisocyanate trimethylolpropane adduct (Mitsui Chemicals, trade name D110N), hexamethylene diisocyanate trimethylolpropane Additives (Mitsui Chemicals, trade name D160N); polyether polyisocyanate, polyester polyisocyanate, adducts of these with various polyols, polyfunctionalized polyisocyanate, burette, allophanate, etc. An isocyanate etc. can be mentioned. Of these, it is preferable to use an aliphatic isocyanate because of its high reaction rate.

  The isocyanate-based crosslinking agent may be used alone or in combination of two or more, but the total content is 100 parts by weight of the (meth) acrylic polymer. On the other hand, it is preferable to contain 0.01-5 weight part of the said isocyanate type crosslinking agent, Furthermore, it is preferable to contain 0.01-4 weight part, Furthermore, it is preferable to contain 0.02-3 weight part. . It can be appropriately contained in consideration of cohesive force and prevention of peeling in a durability test.

  In addition, in the aqueous dispersion of the modified (meth) acrylic polymer prepared by emulsion polymerization, it is not necessary to use an isocyanate-based crosslinking agent. However, if necessary, it is blocked because it easily reacts with water. Isocyanate-based crosslinking agents can also be used.

  The said epoxy type crosslinking agent says the polyfunctional epoxy compound which has 2 or more of epoxy groups in 1 molecule. Examples of the epoxy crosslinking agent include bisphenol A, epichlorohydrin type epoxy resin, ethylene glycidyl ether, N, N, N ′, N′-tetraglycidyl-m-xylenediamine, diglycidylaniline, diamine glycidylamine, 1 , 3-bis (N, N-diglycidylaminomethyl) cyclohexane, 1,6-hexanediol diglycidyl ether, neopentyl glycol diglycidyl ether, ethylene glycol diglycidyl ether, propylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether , Polypropylene glycol diglycidyl ether, sorbitol polyglycidyl ether, glycerol polyglycidyl ether, pentaerythritol polyglycidyl ether Glycerin diglycidyl ether, glycerin triglycidyl ether, polyglycerol polyglycidyl ether, sorbitan polyglycidyl ether, trimethylolpropane polyglycidyl ether, adipic acid diglycidyl ester, o-phthalic acid diglycidyl ester, triglycidyl-tris (2-hydroxy Ethyl) isocyanurate, resorcin diglycidyl ether, bisphenol-S-diglycidyl ether, and epoxy resins having two or more epoxy groups in the molecule. Examples of the epoxy-based crosslinking agent include commercially available products such as trade names “Tetrad C” and “Tetrad X” manufactured by Mitsubishi Gas Chemical Company.

  The epoxy crosslinking agent may be used alone or in combination of two or more. However, the total content is 100 parts by weight of the (meth) acrylic polymer. On the other hand, it is preferable to contain 0.01-5 weight part of the said epoxy type crosslinking agent, Furthermore, it is preferable to contain 0.01-4 weight part, Furthermore, it is preferable to contain 0.02-3 weight part. . It can be appropriately contained in consideration of cohesive force and prevention of peeling in a durability test.

  The peroxide crosslinking agent can be used as appropriate as long as it generates radical active species by heating to cause the crosslinking of the base polymer of the pressure-sensitive adhesive, but in consideration of workability and stability, 1 It is preferable to use a peroxide having a minute half-life temperature of 80 ° C to 160 ° C, and it is more preferable to use a peroxide having a temperature of 90 ° C to 140 ° C.

  Examples of peroxides that can be used include di (2-ethylhexyl) peroxydicarbonate (1 minute half-life temperature: 90.6 ° C.), di (4-t-butylcyclohexyl) peroxydicarbonate (1 Minute half-life temperature: 92.1 ° C.), di-sec-butyl peroxydicarbonate (1 minute half-life temperature: 92.4 ° C.), t-butyl peroxyneodecanoate (1 minute half-life temperature: 103 0.5 ° C), t-hexyl peroxypivalate (1 minute half-life temperature: 109.1 ° C), t-butyl peroxypivalate (1 minute half-life temperature: 110.3 ° C), dilauroyl peroxide ( 1 minute half-life temperature: 116.4 ° C.), di-n-octanoyl peroxide (1 minute half-life temperature: 117.4 ° C.), 1,1,3,3-tetramethylbutyl Oxy-2-ethylhexanoate (1 minute half-life temperature: 124.3 ° C), di (4-methylbenzoyl) peroxide (1 minute half-life temperature: 128.2 ° C), dibenzoyl peroxide (half-minute for 1 minute) Period temperature: 130.0 ° C.), t-butyl peroxyisobutyrate (1 minute half-life temperature: 136.1 ° C.), 1,1-di (t-hexylperoxy) cyclohexane (1 minute half-life temperature: 149.2 ° C.). Especially, since the crosslinking reaction efficiency is excellent, di (4-t-butylcyclohexyl) peroxydicarbonate (1 minute half-life temperature: 92.1 ° C.), dilauroyl peroxide (1 minute half-life temperature: 116. 4 ° C), dibenzoyl peroxide (1 minute half-life temperature: 130.0 ° C) and the like are preferably used.

  The peroxide half-life is an index representing the decomposition rate of the peroxide, and means the time until the remaining amount of peroxide is reduced to half. The decomposition temperature for obtaining a half-life at an arbitrary time and the half-life time at an arbitrary temperature are described in the manufacturer catalog, for example, “Organic peroxide catalog 9th edition by Nippon Oil & Fats Co., Ltd.” (May 2003) ".

  The peroxide may be used alone or as a mixture of two or more, but the total content is based on 100 parts by weight of the (meth) acrylic polymer. The peroxide is 0.02 to 2 parts by weight, preferably 0.05 to 1 part by weight. In order to adjust processability, reworkability, cross-linking stability, peelability, and the like, it is appropriately selected within this range.

In addition, as a measuring method of the peroxide decomposition amount remaining after the reaction treatment, for example, HPLC
It can be measured by (high performance liquid chromatography).

  More specifically, for example, about 0.2 g of the pressure-sensitive adhesive after the reaction treatment is taken out, immersed in 10 ml of ethyl acetate, and extracted by shaking at 25 ° C. and 120 rpm for 3 hours with a shaker. Let stand for days. Next, 10 ml of acetonitrile was added, shaken at 120 rpm at 25 ° C. for 30 minutes, and about 10 μl of the extract obtained by filtration through a membrane filter (0.45 μm) was injected into the HPLC for analysis. The amount of peroxide can be set.

  Moreover, you may use together an organic type crosslinking agent and a polyfunctional metal chelate as a crosslinking agent. A polyfunctional metal chelate is one in which a polyvalent metal is covalently or coordinately bonded to an organic compound. Examples of polyvalent metal atoms include Al, Cr, Zr, Co, Cu, Fe, Ni, V, Zn, In, Ca, Mg, Mn, Y, Ce, Sr, Ba, Mo, La, Sn, Ti, and the like. Can be mentioned. Examples of the atom in the organic compound that is covalently bonded or coordinated include an oxygen atom, and examples of the organic compound include an alkyl ester, an alcohol compound, a carboxylic acid compound, an ether compound, and a ketone compound.

  The pressure-sensitive adhesive of the present invention can contain a (meth) acrylic oligomer in order to improve the adhesive force. The (meth) acrylic oligomer is preferably a polymer having a Tg higher than that of the (meth) acrylic polymer of the present invention and a small weight average molecular weight. Such a (meth) acrylic oligomer functions as a tackifying resin and has the advantage of increasing the adhesive force without increasing the dielectric constant.

  The (meth) acrylic oligomer preferably has a Tg of about 0 ° C. or higher and 300 ° C. or lower, preferably about 20 ° C. or higher and 300 ° C. or lower, more preferably about 40 ° C. or higher and 300 ° C. or lower. When the Tg is less than about 0 ° C., the cohesive force of the pressure-sensitive adhesive layer at room temperature or higher is lowered, and the holding characteristics and the adhesiveness at high temperature may be lowered. The Tg of the (meth) acrylic oligomer is a theoretical value calculated based on the Fox equation, similar to the Tg of the (meth) acrylic polymer.

  The weight average molecular weight of the (meth) acrylic oligomer is 1000 or more and less than 30000, preferably 1500 or more and less than 20000, and more preferably 2000 or more and less than 10,000. If the weight average molecular weight is 30000 or more, the effect of improving the adhesive strength may not be sufficiently obtained. On the other hand, if the molecular weight is less than 1000, the molecular weight may be low, which may cause a decrease in adhesive strength and retention characteristics. In this invention, the measurement of the weight average molecular weight of a (meth) acrylic-type oligomer can be calculated | required in polystyrene conversion by GPC method. Specifically, TSKgelGMH-H (20) × 2 columns are used in HPLC 8020 manufactured by Tosoh Corporation, and the measurement is performed with a tetrahydrofuran solvent at a flow rate of about 0.5 ml / min.

  Examples of the monomer constituting the (meth) acrylic oligomer include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, isopropyl (meth) acrylate, butyl (meth) acrylate, and isobutyl (meth) acrylate. , S-butyl (meth) acrylate, t-butyl (meth) acrylate, pentyl (meth) acrylate, isopentyl (meth) acrylate, hexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, heptyl (meth) acrylate, octyl (Meth) acrylate, isooctyl (meth) acrylate, nonyl (meth) acrylate, isononyl (meth) acrylate, decyl (meth) acrylate, isodecyl (meth) acrylate, undeci Alkyl (meth) acrylates such as (meth) acrylate and dodecyl (meth) acrylate; (meth) acrylic acid and alicyclic such as cyclohexyl (meth) acrylate, isobornyl (meth) acrylate and dicyclopentanyl (meth) acrylate An ester with a group alcohol; an aryl (meth) acrylate such as phenyl (meth) acrylate and benzyl (meth) acrylate; a (meth) acrylate obtained from a terpene compound derivative alcohol; and the like. Such (meth) acrylates can be used alone or in combination of two or more.

  Examples of (meth) acrylic oligomers include alkyl (meth) acrylates in which alkyl groups such as isobutyl (meth) acrylate and t-butyl (meth) acrylate have a branched structure; cyclohexyl (meth) acrylate and isobornyl (meth) Esters of (meth) acrylic acid and alicyclic alcohols such as acrylate dicyclopentanyl (meth) acrylate; cyclic structures such as aryl (meth) acrylates such as phenyl (meth) acrylate and benzyl (meth) acrylate It is preferable that an acrylic monomer having a relatively bulky structure represented by (meth) acrylate possessed as a monomer unit. By giving such a bulky structure to the (meth) acrylic oligomer, the adhesiveness of the pressure-sensitive adhesive layer can be further improved. In particular, those having a ring structure in terms of bulkiness are highly effective, and those having a plurality of rings are more effective. In addition, when ultraviolet rays (ultraviolet rays) are employed in the synthesis of the (meth) acrylic oligomer or in the production of the pressure-sensitive adhesive layer, those having a saturated bond are preferred in that they are less likely to cause polymerization inhibition. An alkyl (meth) acrylate having an alkyl group having a branched structure or an ester with an alicyclic alcohol can be suitably used as a monomer constituting the (meth) acrylic oligomer.

From this point, suitable (meth) acrylic oligomers include, for example, a copolymer of cyclohexyl methacrylate (CHMA) and isobutyl methacrylate (IBMA), and a copolymer of cyclohexyl methacrylate (CHMA) and isobornyl methacrylate (IBXMA). Polymer, copolymer of cyclohexyl methacrylate (CHMA) and acryloylmorpholine (ACMO), copolymer of cyclohexyl methacrylate (CHMA) and diethylacrylamide (DEAA), copolymer of 1-adamantyl acrylate (ADA) and methyl methacrylate (MMA) Polymer, copolymer of dicyclopentanyl methacrylate (DCPMA) and isobornyl methacrylate (IBXMA), dicyclopentanyl methacrylate (DCPMA), cyclohexane Xyl methacrylate (CHMA), isobornyl methacrylate (IBXMA), isobornyl acrylate (IBXA), a copolymer of cyclopentanyl methacrylate (DCPMA) and methyl methacrylate (MMA), dicyclopentanyl acrylate (DCPA), 1 -Adamantyl methacrylate (ADMA), 1-adamantyl acrylate (ADA) homopolymers, and the like. In particular, an oligomer containing CHMA as a main component is preferable.

  In the pressure-sensitive adhesive of the present invention, when the (meth) acrylic oligomer is used, the content thereof is not particularly limited, but is preferably 70 parts by weight or less with respect to 100 parts by weight of the (meth) acrylic polymer, Preferably it is 1-70 weight part, More preferably, it is 2-50 weight part, More preferably, it is 3-40 weight part. When the added amount of the (meth) acrylic oligomer exceeds 70 parts by weight, there is a problem that the elastic modulus is increased and the adhesiveness at low temperature is deteriorated. In addition, it is effective from the point of the improvement effect of adhesive force, when mix | blending 1 weight part or more of (meth) acrylic oligomer.

  Furthermore, the pressure-sensitive adhesive of the present invention may contain a silane coupling agent in order to increase the water resistance at the interface when applied to a hydrophilic adherend such as glass of the pressure-sensitive adhesive layer. The amount of the silane coupling agent is preferably 1 part by weight or less, more preferably 0.01 to 1 part by weight, still more preferably 0.02 to 0 parts per 100 parts by weight of the (meth) acrylic polymer. .6 parts by weight. If the amount of the silane coupling agent is too large, the adhesion to the glass increases and the removability is poor, and if it is too small, the durability decreases, which is not preferable.

  Examples of the silane coupling agent that can be preferably used include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropylmethyldiethoxysilane, and 2- (3,4 epoxy cyclohexyl). ) Epoxy group-containing silane coupling agent such as ethyltrimethoxysilane, 3-aminopropyltrimethoxysilane, N-2- (aminoethyl) -3-aminopropylmethyldimethoxysilane, 3-triethoxysilyl-N- (1 , 3-dimethylbutylidene) propylamine, amino group-containing silane coupling agents such as N-phenyl-γ-aminopropyltrimethoxysilane, 3-acryloxypropyltrimethoxysilane, 3-methacryloxypropyltriethoxysilane, etc. (Meta) Acry Group-containing silane coupling agents, such as isocyanate group-containing silane coupling agents such as 3-isocyanate propyl triethoxysilane and the like.

  Furthermore, the pressure-sensitive adhesive of the present invention may contain other known additives, such as powders such as colorants and pigments, dyes, surfactants, plasticizers, tackifiers, surface lubrication. For applications that use agents, leveling agents, softeners, antioxidants, anti-aging agents, light stabilizers, UV absorbers, polymerization inhibitors, inorganic or organic fillers, metal powders, particles, foils, etc. It can be added as appropriate.

  The pressure-sensitive adhesive layer of the present invention is formed from the pressure-sensitive adhesive. The thickness in particular of an adhesive layer is not restrict | limited, For example, it is about 1-400 micrometers. Moreover, the thickness of the said adhesive layer can set a preferable range suitably according to the manufacturing method of the (meth) acrylic-type polymer used for an adhesive. For example, when producing a (meth) acrylic polymer by solution polymerization or the like, the thickness of the pressure-sensitive adhesive layer is preferably 1 to 100 μm, more preferably 2 to 50 μm, still more preferably 2 to 40 μm, More preferably, it is 5-35 micrometers. Moreover, when manufacturing a (meth) acrylic-type polymer by radiation polymerization etc., the thickness of the said adhesive layer has preferable 50-400 micrometers, More preferably, it is 75-300 micrometers, More preferably, it is 100-200 micrometers. .

  The pressure-sensitive adhesive layer of the present invention preferably has a relative dielectric constant of 3.5 or less at a frequency of 100 kHz, more preferably 3.3 or less, and still more preferably 3.2 or less.

  Moreover, it is preferable that the gel fraction of the adhesive layer of this invention is 20 to 98 weight%. The gel fraction of the pressure-sensitive adhesive layer is more preferably 30 to 98% by weight, still more preferably 40 to 95% by weight. When the pressure-sensitive adhesive contains a cross-linking agent, the gel fraction can be controlled by adjusting the addition amount of the entire cross-linking agent and sufficiently considering the influence of the cross-linking temperature and the cross-linking time. When the gel fraction is small, the cohesive force is poor, and when it is too large, the adhesive force may be poor. The pressure-sensitive adhesive layer having such a gel fraction has a very small increase in adhesive force after being applied to an adherend, and exhibits the characteristics that it can be easily re-peeled without any adhesive residue even after being applied for a long time. The

  The pressure-sensitive adhesive layer of the present invention preferably has a haze value of 2% or less when the thickness of the pressure-sensitive adhesive layer is 25 μm. If the haze is 2% or less, the transparency required when the pressure-sensitive adhesive layer is used in an optical member can be satisfied. The haze value is preferably 0 to 1.5%, and more preferably 0 to 1%. In addition, if a haze value is 2% or less, it can be satisfied as an optical use. If the haze value exceeds 2%, white turbidity occurs, which is not preferable for optical film applications.

  The pressure-sensitive adhesive layer can be formed as a pressure-sensitive adhesive sheet by, for example, applying the pressure-sensitive adhesive to a support and drying and removing a polymerization solvent and the like. In applying the adhesive, one or more solvents other than the polymerization solvent may be added as appropriate.

  Various methods are used as a method of applying the adhesive. Specifically, for example, roll coat, kiss roll coat, gravure coat, reverse coat, roll brush, spray coat, dip roll coat, bar coat, knife coat, air knife coat, curtain coat, lip coat, die coater, etc. Examples thereof include an extrusion coating method.

  The heating and drying temperature is preferably 40 ° C to 200 ° C, more preferably 50 ° C to 180 ° C, and particularly preferably 70 ° C to 170 ° C. By setting the heating temperature in the above range, an adhesive layer having excellent adhesive properties can be obtained. As the drying time, an appropriate time can be adopted as appropriate. The drying time is preferably 5 seconds to 20 minutes, more preferably 5 seconds to 10 minutes, and particularly preferably 10 seconds to 5 minutes.

  The pressure-sensitive adhesive layer is formed by manufacturing the (meth) acrylic polymer of the present invention by polymerizing the monomer component by irradiating the monomer component with ultraviolet rays. At the same time, an adhesive layer can be formed. The monomer component can contain a material that can be appropriately blended with the pressure-sensitive adhesive such as a crosslinking agent. As the monomer component, a part of the monomer component previously polymerized into a syrup can be used for ultraviolet irradiation. For ultraviolet irradiation, a high pressure mercury lamp, a low pressure mercury lamp, a metal halide lamp, or the like can be used.

  As the support, for example, a release-treated sheet can be used. A silicone release liner is preferably used as the release-treated sheet.

  When the pressure-sensitive adhesive layer is exposed on the release-treated sheet, the pressure-sensitive adhesive layer may be protected with a release-treated sheet (separator) until practical use. . In practical use, the peeled sheet is peeled off.

  Examples of the constituent material of the separator include, for example, plastic films such as polyethylene, polypropylene, polyethylene terephthalate, and polyester films, porous materials such as paper, cloth, and nonwoven fabric, nets, foam sheets, metal foils, and laminates thereof. Although a thin leaf body etc. can be mentioned, a plastic film is used suitably from the point which is excellent in surface smoothness.

  The plastic film is not particularly limited as long as it can protect the pressure-sensitive adhesive layer. For example, a polyethylene film, a polypropylene film, a polybutene film, a polybutadiene film, a polymethylpentene film, a polyvinyl chloride film, and a vinyl chloride co-polymer are used. Examples thereof include a polymer film, a polyethylene terephthalate film, a polybutylene terephthalate film, a polyurethane film, and an ethylene-vinyl acetate copolymer film.

  The thickness of the separator is usually about 5 to 200 μm, preferably about 5 to 100 μm. For the separator, if necessary, mold release and antifouling treatment with a silicone type, fluorine type, long chain alkyl type or fatty acid amide type release agent, silica powder, etc., coating type, kneading type, vapor deposition type It is also possible to carry out antistatic treatment such as. In particular, when the surface of the separator is appropriately subjected to a release treatment such as silicone treatment, long-chain alkyl treatment, or fluorine treatment, the peelability from the pressure-sensitive adhesive layer can be further improved.

  The pressure-sensitive adhesive layer and pressure-sensitive adhesive sheet of the present invention are preferably applied to optical members, and are preferably used for applications that are applied to metal thin films and metal electrodes, particularly in optical applications. Examples of the metal thin film include a thin film made of a metal, a metal oxide, or a mixture thereof, and are not particularly limited. For example, a thin film of ITO (indium tin oxide), ZnO, SnO, or CTO (cadmium tin oxide) can be given. It is done. The thickness of the metal thin film is not particularly limited, but is about 10 to 200 nm. Usually, metal thin films, such as ITO, are provided on transparent plastic film base materials, such as a polyethylene terephthalate film (especially PET film), and are used as a transparent conductive film, for example. When the above-mentioned pressure-sensitive adhesive sheet of the present invention is attached to a metal thin film, it is preferably used so that the surface on the pressure-sensitive adhesive layer side becomes the pressure-sensitive adhesive surface on the side attached to the metal thin film.

  Further, the metal electrode is not particularly limited as long as it is an electrode made of a metal, a metal oxide, or a mixture thereof, and examples thereof include ITO, silver, copper, and CNT (carbon nanotube) electrodes.

  As an example of the specific use of the adhesive sheet of this invention, the adhesive sheet for touchscreens used for the manufacture use of a touchscreen can be mentioned. For example, in the production of a capacitive touch panel, the pressure-sensitive adhesive sheet for a touch panel includes a transparent conductive film provided with a metal thin film such as ITO, a polymethyl methacrylate resin (PMMA) plate, a hard coat film, a glass lens, and the like. Can be used to paste together. Although the said touch panel is not specifically limited, For example, it is used for a mobile telephone, a tablet computer, a portable information terminal, etc.

  As a more specific example, FIG. 1 shows an example of a capacitive touch panel in which the pressure-sensitive adhesive layer or pressure-sensitive adhesive sheet of the present invention is used. In FIG. 1, 1 is a capacitive touch panel, 11 is a decorative panel, 12 is an adhesive layer or an adhesive sheet, 13 is an ITO film, and 14 is a hard coat film. The decorative panel 11 is preferably a glass plate or a transparent acrylic plate (PMMA plate). The ITO film 13 is preferably a glass plate or a transparent plastic film (particularly a PET film) provided with an ITO film. The hard coat film 14 is preferably a transparent plastic film such as a PET film subjected to a hard coat treatment. The capacitive touch panel 1 uses the pressure-sensitive adhesive layer or pressure-sensitive adhesive sheet of the present invention, so that the thickness can be reduced and the operation stability is excellent. Also, the appearance and visibility are good.

  Moreover, an optical member can be used as a support body of the adhesive sheet of this invention. The pressure-sensitive adhesive layer can be applied directly to the optical member, and the pressure-sensitive adhesive layer can be formed on the optical member by drying and removing the polymerization solvent and the like. In addition, the pressure-sensitive adhesive layer formed on the release-treated separator can be appropriately transferred to an optical member to form a pressure-sensitive adhesive optical member.

  In addition, the sheet | seat which carried out the peeling process used in preparation of said adhesive type optical member can be used as a separator of an adhesive type optical member as it is, and can simplify in the surface of a process.

  Further, in the pressure-sensitive adhesive optical member, when forming the pressure-sensitive adhesive layer, the anchor layer is formed on the surface of the optical member or the pressure-sensitive adhesive layer is formed after various easy-adhesion treatments such as corona treatment and plasma treatment are performed. can do. Moreover, you may perform an easily bonding process on the surface of an adhesive layer.

  The pressure-sensitive adhesive optical member of the present invention can be used as a transparent conductive film with a pressure-sensitive adhesive layer using a transparent conductive film as an optical member. A transparent conductive film has the transparent conductive thin film used as metal thin films, such as said ITO, on one surface of a transparent plastic film base material. The other side of the transparent plastic film substrate has the pressure-sensitive adhesive layer of the present invention. A transparent conductive thin film can be provided on the transparent plastic film substrate via an undercoat layer. A plurality of undercoat layers can be provided. An oligomer migration preventing layer can be provided between the transparent plastic film substrate and the pressure-sensitive adhesive layer.

  Although it does not restrict | limit especially as said transparent plastic film base material, The various plastic film which has transparency is used. The plastic film is formed of a single layer film. For example, the materials include polyester resins such as polyethylene terephthalate and polyethylene naphthalate, acetate resins, polyethersulfone resins, polycarbonate resins, polyamide resins, polyimide resins, polyolefin resins, (meth) acrylic resins. , Polyvinyl chloride resin, polyvinylidene chloride resin, polystyrene resin, polyvinyl alcohol resin, polyarylate resin, polyphenylene sulfide resin, and the like. Of these, polyester resins, polyimide resins and polyethersulfone resins are particularly preferable. The thickness of the film substrate is preferably 15 to 200 μm.

  The film base material is subjected to etching treatment or undercoating treatment such as sputtering, corona discharge, flame, ultraviolet irradiation, electron beam irradiation, chemical conversion, oxidation, etc. on the surface in advance, and a transparent conductive thin film or undercoat provided thereon You may make it improve the adhesiveness with respect to the said film base material of a layer. In addition, before providing the transparent conductive thin film or the undercoat layer, dust may be removed and cleaned by solvent cleaning or ultrasonic cleaning as necessary.

The constituent material and thickness of the transparent conductive thin film are not particularly limited, and are as exemplified in the metal thin film. The undercoat layer can be formed of an inorganic material, an organic material, or a mixture of an inorganic material and an organic material. For example, NaF (1.3), Na ₃ AlF ₆ (1.35), LiF (1.36), MgF ₂ (1.38), CaF ₂ (1.4), BaF ₂ (1. 3), inorganic substances such as SiO ₂ (1.46), LaF ₃ (1.55), CeF ₃ (1.63), Al ₂ O ₃ (1.63) [the values in parentheses for the above materials are Is the refractive index of light. Of these, SiO ₂ , MgF ₂ , A1 ₂ O _{3 and the} like are preferably used. In particular, SiO ₂ is suitable. In addition to the above, a composite oxide containing about 10 to 40 parts by weight of cerium oxide and about 0 to 20 parts by weight of tin oxide with respect to indium oxide can be used.

  Examples of organic substances include acrylic resins, urethane resins, melamine resins, alkyd resins, siloxane polymers, and organic silane condensates. At least one of these organic substances is used. In particular, as the organic substance, it is desirable to use a thermosetting resin made of a mixture of a melamine resin, an alkyd resin, and an organosilane condensate.

  The thickness of the undercoat layer is not particularly limited, but is usually about 1 to 300 nm, preferably 5 to 300 nm, from the viewpoint of optical design and the effect of preventing oligomer generation from the film substrate. .

The said transparent conductive film with an adhesive layer is used in formation of various apparatuses, such as a touch panel and a liquid crystal display. In particular, it can be preferably used as an electrode plate for a touch panel. The touch panel is suitably used for various detection methods (for example, a resistance film method, a capacitance method, etc.).

  In a capacitive touch panel, a transparent conductive film provided with a transparent conductive thin film having a predetermined pattern shape is usually formed on the entire surface of the display unit. The said transparent conductive film with an adhesive layer is laminated | stacked suitably so that an adhesive layer and the patterned transparent conductive thin film may face.

  Moreover, the adhesive optical member of the present invention can be used as an optical film with an adhesive layer using an optical film for an image display device as an optical member.

  As an optical film, what is used for formation of image display apparatuses, such as a liquid crystal display device and an organic electroluminescence display, is used, and the kind in particular is not restrict | limited. For example, a polarizing plate is mentioned as an optical film. A polarizing plate having a transparent protective film on one or both sides of a polarizer is generally used.

  The polarizer is not particularly limited, and various types can be used. Examples of polarizers include dichroic iodine and dichroic dyes on hydrophilic polymer films such as polyvinyl alcohol films, partially formalized polyvinyl alcohol films, and ethylene / vinyl acetate copolymer partially saponified films. Examples thereof include polyene-based oriented films such as those obtained by adsorbing substances and uniaxially stretched, polyvinyl alcohol dehydrated products and polyvinyl chloride dehydrochlorinated products. Among these, a polarizer composed of a polyvinyl alcohol film and a dichroic material such as iodine is preferable. The thickness of these polarizers is not particularly limited, but is generally about 5 to 80 μm.

  A polarizer obtained by dyeing a polyvinyl alcohol film with iodine and uniaxially stretching it can be prepared, for example, by immersing polyvinyl alcohol in an aqueous solution of iodine and stretching it 3 to 7 times the original length. If necessary, it can be immersed in an aqueous solution such as potassium iodide which may contain boric acid, zinc sulfate, zinc chloride or the like. Further, if necessary, the polyvinyl alcohol film may be immersed in water and washed before dyeing. In addition to washing the polyvinyl alcohol film surface with dirt and anti-blocking agents by washing the polyvinyl alcohol film with water, it also has the effect of preventing unevenness such as uneven coloring by swelling the polyvinyl alcohol film. is there. Stretching may be performed after dyeing with iodine, may be performed while dyeing, or may be dyed with iodine after stretching. The film can be stretched even in an aqueous solution such as boric acid or potassium iodide or in a water bath.

  As a material constituting the transparent protective film, for example, a thermoplastic resin excellent in transparency, mechanical strength, thermal stability, moisture barrier property, isotropy and the like is used. Specific examples of such thermoplastic resins include cellulose resins such as triacetyl cellulose, polyester resins, polyethersulfone resins, polysulfone resins, polycarbonate resins, polyamide resins, polyimide resins, polyolefin resins, (meth) acrylic resins, cyclic Examples thereof include polyolefin resins (norbornene resins), polyarylate resins, polystyrene resins, polyvinyl alcohol resins, and mixtures thereof. A transparent protective film is bonded to one side of the polarizer by an adhesive layer. On the other side, as a transparent protective film, (meth) acrylic, urethane-based, acrylurethane-based, epoxy-based, silicone A thermosetting resin such as a system or an ultraviolet curable resin can be used. One or more kinds of arbitrary appropriate additives may be contained in the transparent protective film. Examples of the additive include an ultraviolet absorber, an antioxidant, a lubricant, a plasticizer, a mold release agent, an anti-coloring agent, a flame retardant, a nucleating agent, an antistatic agent, a pigment, and a coloring agent. The content of the thermoplastic resin in the transparent protective film is preferably 50 to 100% by weight, more preferably 50 to 99% by weight, still more preferably 60 to 98% by weight, and particularly preferably 70 to 97% by weight. . When content of the said thermoplastic resin in a transparent protective film is 50 weight% or less, there exists a possibility that the high transparency etc. which a thermoplastic resin originally has cannot fully be expressed.

  Examples of the optical film include liquid crystal display devices such as a reflection plate, an anti-transmission plate, a retardation plate (including wavelength plates such as 1/2 and 1/4), an optical compensation film, a visual compensation film, and a brightness enhancement film. What becomes an optical layer which may be used for formation of is mentioned. These can be used alone as an optical film, or can be laminated on the polarizing plate for practical use and used as one layer or two or more layers.

  An optical film in which the optical layer is laminated on a polarizing plate can be formed by a method of sequentially laminating separately in the manufacturing process of a liquid crystal display device or the like. There is an advantage that the manufacturing process of a liquid crystal display device or the like can be improved because of excellent stability and assembly work. For the lamination, an appropriate adhesive means such as an adhesive layer can be used. When adhering the polarizing plate and the other optical layer, their optical axes can be set at an appropriate arrangement angle in accordance with the target phase difference characteristic.

  The optical film with an adhesive layer of the present invention can be preferably used for forming various image display devices such as a liquid crystal display device. The liquid crystal display device can be formed according to the conventional method. That is, a liquid crystal display device is generally formed by appropriately assembling components such as a liquid crystal cell, an optical film with an adhesive layer, and an illumination system as required, and incorporating a drive circuit. There is no limitation in particular except the point which uses the optical film with an adhesive layer by this invention, and it can apply according to the former. As the liquid crystal cell, any type such as a TN type, STN type, π type, VA type, IPS type, or the like can be used.

  An appropriate liquid crystal display device such as a liquid crystal display device in which an optical film with an adhesive layer is disposed on one side or both sides of a liquid crystal cell, or a backlight system or a reflector used in an illumination system can be formed. In that case, the optical film according to the present invention can be placed on one or both sides of the liquid crystal cell. When optical films are provided on both sides, they may be the same or different. Further, when forming a liquid crystal display device, for example, a single layer or a suitable part such as a diffusing plate, an antiglare layer, an antireflection film, a protective plate, a prism array, a lens array sheet, a light diffusing plate, a backlight, etc. Two or more layers can be arranged.

  EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples. In addition, all the parts and% in each example are based on weight. Evaluation items in Examples and the like were measured as follows.

Example 1
<Preparation of (meth) acrylic polymer>
In a four-necked flask equipped with a stirring blade, a thermometer, a nitrogen gas inlet tube, and a condenser, 100 parts by weight of isodecyl acrylate (IDA), 1 part by weight of 4-hydroxybutyl acrylate (HBA), and 2, as a polymerization initiator After charging 0.1 part by weight of 2′-azobisisobutyronitrile together with 200 parts by weight of ethyl acetate, nitrogen gas was introduced with gentle stirring and the atmosphere was purged with nitrogen for 1 hour, and then the liquid temperature in the flask was changed from 55 ° C. to A polymerization reaction was carried out for 15 hours while maintaining at around 60 ° C. to prepare a (meth) acrylic polymer solution having a weight average molecular weight of 800,000. Tg of the obtained (meth) acrylic polymer was −60 ° C.

  Next, in the (meth) acrylic polymer solution obtained above, a trimethylolpropane adduct of xylylene diisocyanate (trade name D110N, manufactured by Mitsui Chemicals) as a crosslinking agent with respect to 100 parts by weight of the solid content of the polymer. Was added to prepare an adhesive solution.

  Next, the obtained pressure-sensitive adhesive solution is dried on one side of a 38 μm polyethylene terephthalate (PET) film (manufactured by Mitsubishi Chemical Polyester Film Co., Ltd., DIAFOIL MRF38) subjected to silicone treatment, and the thickness of the pressure-sensitive adhesive layer after drying becomes 25 μm. And dried at 130 ° C. for 3 minutes to form a pressure-sensitive adhesive layer, thereby preparing a pressure-sensitive adhesive sheet.

Examples 2-18, Comparative Examples 1-8
Example 1 is the same as Example 1 except that the types and composition ratios of the monomers used for the preparation of the (meth) acrylic polymer and the types and amounts of the crosslinking agents are changed as shown in Table 1. Thus, an adhesive sheet was prepared. Table 1 shows the weight average molecular weight and Tg of the obtained (meth) acrylic polymer.

Example 19
<Preparation of monomer components used for UV polymerization>
48 parts by weight of 2-ethylhexyl acrylate (2EHA), 48 parts by weight of isostearyl acrylate (ISTA), 4 parts by weight of 4-hydroxybutyl acrylate (HBA), two kinds of photopolymerization initiators (trade name: Irgacure 184, manufactured by BASF Corporation) ) 0.05 part by weight and 0.05 part by weight of a photopolymerization initiator (trade name: Irgacure 651, manufactured by BASF) were charged into a four-necked flask to prepare a monomer mixture. Next, the monomer mixture was partially photopolymerized by exposing it to ultraviolet rays under a nitrogen atmosphere to obtain a partially polymerized product (acrylic polymer syrup) having a polymerization rate of about 10% by weight.

  After adding 0.1 parts by weight of trimethylolpropane triacrylate (TMPTA) to 100 parts by weight of the acrylic polymer syrup described above, they were uniformly mixed to prepare a monomer component.

<Preparation of adhesive layer by UV polymerization>
Next, the final thickness of the monomer component adjusted as described above is 100 μm on the release surface of a 38 μm-thick polyester film (trade name: Diafoil MRF, manufactured by Mitsubishi Plastics Co., Ltd.) whose one surface is peeled with silicone. The coating layer was formed by coating as described above. Next, a 38 μm thick polyester film (trade name: Diafoil MRE, manufactured by Mitsubishi Plastics Co., Ltd.) having one surface peeled with silicone on the surface of the applied monomer component, the peel-treated surface of the film is on the coating layer side. It was coated as follows. Thereby, the coating layer of the monomer component was shielded from oxygen. Using a chemical light lamp (manufactured by Toshiba Corporation) on the sheet having the coating layer thus obtained, an ultraviolet ray having an illuminance of 5 mW / cm ² (measured with Topcon UVR-T1 having a maximum sensitivity of about 350 nm) is applied for 360 seconds. Irradiation was performed to cure the coating layer to form an adhesive layer, and an adhesive sheet was prepared. The polyester film coated on both sides of the pressure-sensitive adhesive layer functions as a release liner.

Example 20, Comparative Example 1
In Example 19, the same operation as in Example 1 was performed except that the type and composition ratio of the monofunctional monomer used for the preparation of the monomer component were changed as shown in Table 2, and an adhesive sheet was prepared. .

  The following evaluation was performed about the adhesive sheet (sample) obtained by the said Example and comparative example. The evaluation results are shown in Table 1.

<Measurement of gel fraction>
A predetermined amount (initial weight W1) is taken out from the pressure-sensitive adhesive layer in the pressure-sensitive adhesive sheet, immersed in an ethyl acetate solution and allowed to stand at room temperature for one week. It was calculated as follows.
Gel fraction = (W2 / W1) × 100

<Dielectric constant>
Five pressure-sensitive adhesive layers (those obtained by peeling a PET film subjected to silicone treatment from the pressure-sensitive adhesive sheet) were laminated to form a laminated pressure-sensitive adhesive layer of about 100 μm. The samples having a thickness of 100 μm prepared by UV polymerization in Examples 19 and 20 and Comparative Example 1 were used without being stacked. The laminated adhesive layer (or adhesive layer) was sandwiched between a copper foil and an electrode, and the relative dielectric constant at a frequency of 100 kHz was measured by the following apparatus. Three samples of 30 mm × 30 mm were prepared for measurement, and the average of the measured values of these three samples was taken as the dielectric constant.
The relative dielectric constant of the pressure-sensitive adhesive layer at a frequency of 100 kHz was measured according to JIS K 6911 under the following conditions.
Measurement method: Capacity method (apparatus: using Agilent Technologies 4294A Precision Impedance Analyzer)
Electrode configuration: 12.1 mmφ, 0.5 mm thick aluminum plate Counter electrode: 3 oz copper plate Measurement environment: 23 ± 1 ° C., 52 ± 1% RH

<Adhesive strength>
A sample for evaluation was prepared by attaching a PET film (Lumirror S10, manufactured by Toray Industries, Inc.) having a thickness of 25 μm to the adhesive surface of the samples obtained in Examples and Comparative Examples. After the sample for evaluation was cut into a width of 20 mm and a length of about 100 mm, the PET film was peeled off, and a 2 kg roll reciprocated on a 0.5 mm-thick alkali-free glass plate (Corning Corp., 1737). The film was allowed to stand at room temperature (23 ° C.) for 1 hour, and then peel adhesion was measured at a peel angle of 90 ° and a peel speed of 300 mm / min.

<Measurement of haze and total light transmittance>
The pressure-sensitive adhesive sheets obtained in Examples and Comparative Examples were pasted on one side of an alkali-free glass having a total light transmittance of 93.3% and a haze of 0.1%, and a haze meter (MR-100, manufactured by Murakami Color Research Laboratory) was attached. ) To measure haze and total light transmittance. In measuring with a haze meter, the pressure-sensitive adhesive sheet was placed on the light source side. Since the haze value of the alkali-free glass is 0.1%, the haze value is defined as a value obtained by subtracting 0.1% from the measured value. The measured value was adopted as the total light transmittance (%).

In Tables 1 and 2, IDA is isodecyl acrylate (manufactured by SARTOMER, Tg of homopolymer = -60 ° C.);
IMA is isomistyryl acrylate (Kyoeisha Chemical Co., Tg of homopolymer = −56 ° C.);
ISTA is isostearyl acrylate (manufactured by Osaka Organic Chemical Industry Co., Ltd., homopolymer Tg = −18 ° C.);
ID is isodecyl methacrylate (Kyoeisha Chemical Co., Ltd., homopolymer Tg = −41 ° C.);
TMPTA is trimethylolpropane triacrylate;
i-OA is isooctyl acrylate (manufactured by Osaka Organic Chemical Industry Co., Ltd., homopolymer Tg = −58 ° C.);
i-NA is isononyl acrylate (manufactured by Osaka Organic Chemical Industry Co., Ltd., homopolymer Tg = −58 ° C.);
i-AA is isoamyl acrylate (manufactured by Kyoeisha Chemical Co., Ltd., homopolymer Tg = −45 ° C.);
2EHA is 2-ethylhexyl acrylate (manufactured by Toagosei Co., Ltd., homopolymer Tg = −70 ° C.);
LA is lauryl acrylate (manufactured by Kyoeisha Chemical Co., Ltd., homopolymer Tg = −3 ° C.);
STA is stearyl acrylate (manufactured by Osaka Organic Chemical Industry Co., Ltd., homopolymer Tg = 30 ° C.);
AA is acrylic acid;
HBA is 4-hydroxybutyl acrylate;
BA: butyl acrylate;
MMA: methyl methacrylate CD420: 3,3,5-trimethylcyclohexyl acrylate (manufactured by SARTOMER, homopolymer Tg = 81 ° C.);
OA: octyl acrylate;
DA: decyl acrylate.

Tg was measured by DSC (differential scanning calorimeter) for Tg.
<Conditions>
Apparatus: Q-2000 manufactured by TA Instruments
Average heating rate: 5 ° C / min
Atmospheric gas: Nitrogen (50 ml / min)
Measurement was carried out with about 2.5 mg of homopolymer, and the temperature at which the endothermic peak took an intermediate value was taken as the glass transition point.

D110N is a trimethylolpropane adduct of xylylene diisocyanate (Mitsui Chemicals, trade name D110N);
D140N is a trimethylolpropane adduct of isophorone diisocyanate (trade name D140N, manufactured by Mitsui Chemicals);
TETRAD-C is 1,3-bis (N, N-diglycidylaminomethyl) cyclohexane (manufactured by Mitsubishi Gas Chemical Company, trade name Tetrad C);
TETRAD-X indicates N, N, N ′, N′-tetraglycidyl-m-xylenediamine (manufactured by Mitsubishi Gas Chemical Company, trade name Tetrad X).

DESCRIPTION OF SYMBOLS 1 Capacitive touch panel 11 Decorative panel 12 Adhesive layer or adhesive sheet 13 ITO film 14 Hard coat film

Claims (7)

A pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer formed on at least one side of the support,
The pressure-sensitive adhesive layer comprises 19 to 96% by weight of an alkyl (meth) acrylate having a branched alkyl group having 12 to 24 carbon atoms at the end of the ester group, and a carboxyl group-containing monomer, a hydroxyl group-containing monomer, and a cyclic ether group A pressure-sensitive adhesive containing a (meth) acrylic polymer (excluding an acrylic polymer emulsion) formed from a monomer component containing 0.1 to 30% by weight of at least one functional group-containing monomer selected from monomers having obtained et al are from,
And is a relative dielectric constant of 3.5 or less at a frequency of 100kHz, the gel fraction of the pressure-sensitive adhesive layer is Ri 20-98 wt% der (provided that said (meth) clay mineral with respect to 100 parts by weight of the acrylic polymer Except for the adhesive layer containing 0.5 to 10 parts by weight) ,
The pressure-sensitive adhesive sheet, wherein the support is a transparent conductive film, and the pressure-sensitive adhesive sheet for a transparent conductive film is a transparent conductive film with a pressure-sensitive adhesive layer having a pressure-sensitive adhesive layer on at least one side of the transparent conductive film. The monomer component further includes an alkyl (meth) acrylate having a branched alkyl group having 3 to 9 carbon atoms at the terminal of the ester group, an alkyl methacrylate having a linear alkyl group having 1 to 24 carbon atoms at the terminal of the ester group, and cyclic. The pressure-sensitive adhesive sheet according to claim 1, wherein the pressure-sensitive adhesive sheet is a monomer component containing 0.5% by weight or more of at least one selected from alkyl (meth) acrylates having an alkyl group at the terminal of the ester group. The pressure-sensitive adhesive sheet according to claim 1 or 2, wherein the monomer component is a monomer component further containing 3% by weight or less of a polyfunctional monomer. Furthermore, 0.01-5 weight part of crosslinking agents are contained with respect to 100 weight part of said (meth) acrylic-type polymers, The adhesive sheet of any one of Claims 1-3 characterized by the above-mentioned. The pressure-sensitive adhesive sheet according to any one of claims 1 to 4, wherein a haze when the thickness of the pressure-sensitive adhesive layer is 25 µm is 2% or less. The pressure-sensitive adhesive sheet according to any one of claims 1 to 5, wherein a 90-degree peel adhesive force (300 mm / min) of the pressure-sensitive adhesive layer to the alkali-free glass is 0.5 N / 20 mm or more. The pressure-sensitive adhesive sheet according to any one of claims 1 to 6, wherein the transparent conductive film is a transparent plastic film base material or glass in which a transparent conductive thin film is laminated.