JP6198316B2 - Composite filler and dental composition - Google Patents
Composite filler and dental composition Download PDFInfo
- Publication number
- JP6198316B2 JP6198316B2 JP2013211084A JP2013211084A JP6198316B2 JP 6198316 B2 JP6198316 B2 JP 6198316B2 JP 2013211084 A JP2013211084 A JP 2013211084A JP 2013211084 A JP2013211084 A JP 2013211084A JP 6198316 B2 JP6198316 B2 JP 6198316B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- weight
- acrylate
- group
- monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、複合充填材及び歯科用組成物に関する。さらに詳しくは、歯科用セメント、歯科用ボンディング材などの歯科用接着性組成物に使用可能な及び覆髄材あるいは根管充填材として使用可能な複合充填材ならびにそれを含有する歯科用組成物に関する。 The present invention relates to a composite filler and a dental composition. More particularly, the present invention relates to a composite filler that can be used for a dental adhesive composition such as dental cement and a dental bonding material, and can be used as a pulp capping material or a root canal filling material, and a dental composition containing the same. .
生物活性セメントが、様々な歯科用途における硬組織の治療を容易にする機能を有していることが証明されている。ここで、生物活性セメントとは、バイオガラス、リン酸カルシウム系セメント、水酸化カルシウム、ヒドロキシアパタイト、ポルトランドセメント等の生体親和性および組織誘導能を有する材料のことである。これらのセメント材料は、これまでに硬組織などの生体組織に対して使用されてきたカルシウム系生体材料である。
例えば、ポルトランドセメントでは歯科組成物としてＭＴＡ（Ｍｉｎｅｒａｌ Ｔｒｉｏｘｉｄｅ Ａｇｇｒｅｇａｔｅ）と称される歯科用ポルトランドセメントが市販されている。この硬化体は優れた生体親和性及び硬組織誘導能を有し、歯髄や歯根歯周組織に新生硬組織形成を伴う治療を導くとの報告もされている。これらのセメント材料の具体的な歯科用途としては、例えば、象牙質・歯髄の保護としての間接、直接覆髄及び暫間的間接覆髄で使用される覆髄材、根管充填材などが挙げられる。
これらの材料としては、酸性、中性又は塩基性の水性環境中で反応し硬化することでセメント系構造体を形成することができる水系セメントである。これらのセメント材料は、水性環境中で反応し硬化するため、反応速度が遅く、完全硬化までに数日を必要とするものもある。そのため、適用直後ではその強度が弱く、溶解度も高くなる傾向があり、さらに湿潤環境である口腔内では感水による硬化不良も懸念されることから、臨床使用での操作性に問題があった。
Bioactive cement has proven to have the ability to facilitate the treatment of hard tissue in a variety of dental applications. Here, the bioactive cement is a material having biocompatibility and tissue inducing ability such as bioglass, calcium phosphate cement, calcium hydroxide, hydroxyapatite, and Portland cement. These cement materials are calcium-based biomaterials that have been used for biological tissues such as hard tissues.
For example, in Portland cement, dental Portland cement called MTA (Mineral Trioxide Aggregate) is commercially available as a dental composition. It has been reported that this hardened body has excellent biocompatibility and hard tissue inducing ability, and leads to treatment with new hard tissue formation in the pulp and root periodontal tissue. Specific dental applications of these cement materials include, for example, indirect as a means of protecting dentin and pulp, directly capping, and capping material used for temporary indirect capping, root canal filling material, etc. It is done.
These materials are water-based cements that can form a cement-based structure by reacting and curing in an acidic, neutral or basic aqueous environment. Since these cement materials react and harden in an aqueous environment, the reaction rate is slow, and some cement materials require several days for complete hardening. Therefore, immediately after application, the strength tends to be weak and the solubility tends to be high, and in addition, there is a concern about poor curing due to water sensitivity in the oral cavity, which is a moist environment.
そこで、特許文献１では、ＭＴＡと称される歯科用ポルトランドセメントをポリマー湿潤構造体とすることで反応速度や適用直後の強度及び溶解度などの問題を解決する手段が提案されている。また、特許文献２では、ＭＴＡに機械的物性、さらに接着促進モノマーによる接着性とシール性を付与することで、より効果的な硬組織誘導が可能な歯科用組成物が提案されている。
しかしながら、これらの手法は、セメント粒子をポリマー材料若しくは重合性組成物とただ単に混合しているだけで、それらを含んだ組成物の混和泥中では、セメント粒子はポリマー材料若しくは重合性組成物とは馴染まず、意図する操作性が達成できない。また、それらを含んだ組成物の重合後の硬化体内では、セメント粒子とポリマー材料若しくは重合性組成物とが接する界面で化学的な結合は期待できないため、硬化体に外力が加われば、その界面を基点として破壊し機械的物性が低下する虞がある。
このため、優れた操作性と機械的物性を有すると共に、歯牙への接着性とシール性が達成され、且つ硬組織などの生体組織に対して有益に作用する歯科用組成物の開発が望まれている。
Therefore, Patent Document 1 proposes a means for solving problems such as reaction rate, strength immediately after application, and solubility by using dental Portland cement called MTA as a polymer wet structure. Further, Patent Document 2 proposes a dental composition capable of more effective hard tissue induction by imparting mechanical properties to MTA, as well as adhesion and sealing properties with an adhesion promoting monomer.
However, these techniques merely mix the cement particles with the polymer material or polymerizable composition, and in the mixed mud of the composition containing them, the cement particles are separated from the polymer material or polymerizable composition. Is unfamiliar and the intended operability cannot be achieved. In addition, in the cured body after polymerization of the composition containing them, chemical bonding cannot be expected at the interface between the cement particles and the polymer material or the polymerizable composition. Therefore, if an external force is applied to the cured body, the interface There is a risk that the mechanical properties will be degraded due to the breakage.
For this reason, it is desired to develop a dental composition that has excellent operability and mechanical properties, achieves adhesion and sealability to teeth, and acts beneficially on living tissues such as hard tissues. ing.
本発明は、硬組織などの生体組織に対して有益に作用する生物活性セメント成分を重合性組成物で内包し、重合体とした後粉末化することで、マトリックスとなる重合体との馴染みが良好になり、優れた操作性と機械的物性の向上が達成でき、且つ接着促進モノマーによる硬組織への接着性とシール性の付与と同時に、生物活性セメント由来の硬組織などの生体組織に対して有益な作用を達成できる、より効果的な歯科用組成物を提供することを目的としている。 In the present invention, a bioactive cement component that has a beneficial effect on a living tissue such as a hard tissue is encapsulated with a polymerizable composition, and is made into a polymer and then pulverized so that it can be used with a polymer as a matrix. It improves the operability and mechanical properties, and gives adhesion and sealing properties to hard tissues with adhesion promoting monomers, and at the same time for biological tissues such as hard tissues derived from bioactive cement. It is an object of the present invention to provide a more effective dental composition that can achieve beneficial effects.
本発明によれば、本発明の上記目的は、
（α）生物活性セメントの微粒子と、
（β）（β１）単官能重合性単量体を含有する単量体組成物からなる混合物の重合硬化体の粉砕物
よりなる歯科用複合充填材
により達成される。
According to the present invention, the above object of the present invention is
(Α) fine particles of bioactive cement;
(Β) (β1) This is achieved by a dental composite filler comprising a pulverized product of a polymerized cured product of a mixture comprising a monomer composition containing a monofunctional polymerizable monomer.
これらの組み合せによって良好な操作性及び機械的物性を有し、硬組織への接着性とシール性が付与され、硬組織などの生体組織に対しての有用能を達成する歯科用組成物を提供できる。 Providing a dental composition that has good operability and mechanical properties by combining these materials, provides adhesion to hard tissues and sealability, and achieves useful functions for living tissues such as hard tissues. it can.
本発明の複合充填材及び歯科用組成物によれば、硬組織などの生体組織に有用とされる生物活性セメント成分を、重合性組成物で内包し、重合体とした後粉末化することで複合充填材とし、その複合充填材を含む歯科用組成物を患部へ適用することで、複合充填材に含まれる生物活性セメント成分の有用性と共に、マトリックスとなる重合体との馴染みが良くなることにより優れた操作性と機械的物性が付与され、更に歯牙への接着性とシール性の付与で、歯冠側からの微小漏洩（コロナルリーケージ）により細菌や唾液及び食物残渣などの侵入を抑制して、より効果的な歯科用組成物を提供することができる。 According to the composite filler and dental composition of the present invention, a bioactive cement component that is useful for living tissue such as hard tissue is encapsulated with a polymerizable composition to form a polymer and then pulverized. By applying a dental composition containing the composite filler to the affected area as a composite filler, the bioactive cement component contained in the composite filler is useful and familiar with the polymer as a matrix. Superior operability and mechanical properties are added to the teeth, and adhesion and sealability to the teeth are further reduced, and microleakage from the crown side (coronal leakage cage) suppresses the invasion of bacteria, saliva and food residues. Thus, a more effective dental composition can be provided.
次に本発明の複合充填材及び歯科用組成物について具体的に説明する。
なお、以下の説明において、好適な数値範囲等の記載で「好ましくはＸＸ〜ＹＹ」とあるは、「好ましくはＸＸ以上および／またはＹＹ以下」を意味するものとする。
Next, the composite filler and dental composition of the present invention will be specifically described.
In the following description, “preferably XX to YY” in a description of a suitable numerical range or the like means “preferably XX or more and / or YY or less”.
本発明の複合充填材は、硬組織などの生体組織に有用とされる生物活性セメントを重合性組成物で内包し粉末化した充填材であり、本発明の歯科用組成物は前記複合充填材を含んだ歯科用組成物である。
本発明の複合充填材及び歯科用組成物を患部に適用すると、複合充填材に含有された生物活性セメントが硬組織などの生体組織に対して有益な作用を達成すると同時に、硬組織との接着性とシール性を付与することで、歯冠側からの微小漏洩を低減し、患部の汚染を防止する。
（（β）単官能重合性単量体を含有する単量体組成物の重合体）
（β１）単官能重合性単量体を含有する単量体組成物は、構成する単量体１００重量％に基づいて、単官能重合性単量体が、好ましくは、３２重量％以上、より好ましくは、５６重量％以上、更に好ましくは、８３重量％以上である単量体組成物の重合体である。また、構成する単量体１００重量％に基づいて、（β１’）２官能以上の多官能重合性単量体が、好ましくは１０重量％以下、より好ましくは、４．６重量％以下、更に好ましくは、０重量％である。前記数値範囲を満たさない場合、単量体組成物の生物活性セメントとの馴染みが低下して好ましくない場合がある。
The composite filler of the present invention is a filler obtained by encapsulating a bioactive cement useful for living tissue such as a hard tissue with a polymerizable composition, and pulverizing the dental composition of the present invention. A dental composition containing
When the composite filler and the dental composition of the present invention are applied to an affected area, the bioactive cement contained in the composite filler achieves a beneficial effect on a living tissue such as a hard tissue and at the same time adheres to the hard tissue. By providing the seal and the sealing property, the minute leakage from the crown side is reduced and the contamination of the affected part is prevented.
((Β) Polymer of Monomer Composition Containing Monofunctional Polymerizable Monomer)
(Β1) The monomer composition containing the monofunctional polymerizable monomer is preferably a monofunctional polymerizable monomer based on 100% by weight of the constituent monomer, preferably 32% by weight or more. The polymer of the monomer composition is preferably 56% by weight or more, more preferably 83% by weight or more. Further, based on 100% by weight of the constituting monomer, the polyfunctional polymerizable monomer having (β1 ′) bifunctional or higher is preferably 10% by weight or less, more preferably 4.6% by weight or less, Preferably, it is 0% by weight. When the numerical value range is not satisfied, the compatibility of the monomer composition with the bioactive cement may be unfavorable.
なお、単量体組成物中の多官能重合性単量体の含有比率の簡便な判別方法として、ゲル分率測定法があげられる。この方法は単量体組成物を公知の重合法により重合させて得られた硬化体を、適当な溶媒（アセトンなど）で溶解させることで、その硬化体の溶解前後の重量差の百分率（＝ゲル分率）を求めるというものである。但し、本発明の充填材は無機成分を含有するので、最終的には、残余のゲル分と無機成分を分別する必要があるが、前記の残余のゲル分と無機成分の混合物について、強力な溶媒にて溶脱したり、高温にて焼却することにてゲル分を除去して、無機成分を精密に秤量してもよいし、この測定をゲル分率測定にかけた試料と同重量の充填材にて行なって推算しても良い。この測定方法によるゲル分率は、本発明における上記重合体について好ましくは、１２重量％以下、より好ましくは、８重量％以下、更に好ましくは、４重量％以下である。 In addition, a gel fraction measuring method is mention | raise | lifted as a simple discrimination | determination method of the content rate of the polyfunctional polymerizable monomer in a monomer composition. In this method, the cured product obtained by polymerizing the monomer composition by a known polymerization method is dissolved in an appropriate solvent (such as acetone), whereby the percentage of the weight difference before and after the dissolution of the cured product (= Gel fraction). However, since the filler of the present invention contains an inorganic component, it is necessary to finally separate the remaining gel component from the inorganic component. However, the mixture of the remaining gel component and the inorganic component is powerful. Gels may be removed by leaching with a solvent or incineration at a high temperature, and the inorganic component may be precisely weighed, or the same weight as the sample subjected to the gel fraction measurement. It is also possible to estimate by performing the above. The gel fraction by this measuring method is preferably 12% by weight or less, more preferably 8% by weight or less, and still more preferably 4% by weight or less for the polymer in the present invention.
また、（β）単官能重合性単量体を含有する単量体組成物の重合体重量平均の分子量は、好ましくは、１０，０００〜１，０００，０００、より好ましくは、１００，０００〜８００，０００、更に好ましくは、１５０，０００〜６００，０００である。前記数値範囲の下限値を下回ると重合硬化物としての形態を維持することが困難となり、一方、上限値を上回ると組成物での使用で化合物との馴染みが低下することとなり、何れも好ましくない場合がある。
又、単官能重合性単量体を含有する単量体組成物を構成する単量体は、比較的生体安全性に優れるため（メタ）アクリレート系が好ましく、更に組成物中の化合物との馴染みが比較的良好となるのでメタクリレート系であることがより好ましい。
歯科用複合充填材の重合体乃至は重合体相（１００重量％とする）に、（β）単官能重合性単量体を含有する単量体組成物の重合体以外の成分は本発明の効果に支障がない限り、若干含まれてもよいが、その含有量は、好ましくは、５．０重量％以下、より好ましくは、２．０重量％以下、更に好ましくは、１．０重量％以下である。かかる成分としては、顔料、色素、抗菌剤等の無機成分や非高分子系有機成分（数平均分子量１０，０００未満）が挙げられる。
Moreover, the polymer weight average molecular weight of the monomer composition containing the (β) monofunctional polymerizable monomer is preferably 10,000 to 1,000,000, more preferably 100,000 to 800,000, more preferably 150,000 to 600,000. If the value falls below the lower limit of the numerical range, it becomes difficult to maintain the form as a polymerized cured product. On the other hand, if the value exceeds the upper limit, the familiarity with the compound decreases due to use in the composition, which is not preferable. There is a case.
In addition, the monomer constituting the monomer composition containing the monofunctional polymerizable monomer is preferably (meth) acrylate type because it is relatively excellent in biological safety, and is more familiar with the compound in the composition. Is more preferable because it is relatively good.
Components other than the polymer of the monomer composition containing the (β) monofunctional polymerizable monomer in the polymer or polymer phase (100% by weight) of the dental composite filler As long as there is no hindrance to the effect, it may be included slightly, but its content is preferably 5.0% by weight or less, more preferably 2.0% by weight or less, and still more preferably 1.0% by weight. It is as follows. Examples of such components include inorganic components such as pigments, dyes, and antibacterial agents, and non-polymeric organic components (number average molecular weight of less than 10,000).
（β１）単官能重合性単量体
（β１ａ）分子内に酸性基と重合性基を有する化合物
本発明で用いられる（β１）単官能重合性単量体には、（β１ａ）分子内に酸性基と重合性基を有する化合物が含まれることが好ましい。この（β１ａ）成分中にある重合性基としては、ラジカル重合性基が好ましく、例えばビニル基、シアン化ビニル基、アクリロイル基、メタアクリロイル基、アクリルアミド基、メタアクリルアミド基などを挙げることができる。また、酸性基としては、例えばカルボシキル基、リン酸基、チオリン酸基、スルホン酸基、スルフィン酸基あるいはカルボキシル基の酸無水基のように、実用条件において容易に加水・分解して前記酸性基になるなど、実質上酸性基として機能するものも、酸性基として挙げることができる。酸性基と重合性基のそれぞれは分子内に１つまたは２つ以上あってもよい。
(Β1) Monofunctional polymerizable monomer (β1a) Compound having acidic group and polymerizable group in molecule (β1) Monofunctional polymerizable monomer used in the present invention is (β1a) acidic in the molecule A compound having a group and a polymerizable group is preferably included. The polymerizable group in the (β1a) component is preferably a radical polymerizable group, and examples thereof include a vinyl group, a vinyl cyanide group, an acryloyl group, a methacryloyl group, an acrylamide group, and a methacrylamide group. Examples of the acidic group include a hydroxyl group, a phosphoric acid group, a thiophosphoric acid group, a sulfonic acid group, a sulfinic acid group, or an acid anhydride group such as a carboxyl group, which is easily hydrolyzed and decomposed under practical conditions. Those that substantially function as an acidic group, such as, can also be cited as acidic groups. One or two or more acidic groups and polymerizable groups may be present in the molecule.
本発明において、（β１ａ）成分の具体的な例であるカルボキシル基を有する重合性化合物の例としては、（メタ）アクリル酸（以下、アクリル酸とメタアクリル酸の総称として（メタ）アクリル酸と記載する。）、マレイン酸等のα−不飽和カルボン酸；４−ビニル安息香酸等のビニル芳香環化合物；１１−（メタ）アクリロイルオキシ−１，１−ウンデカンジカルボン酸（以下、アクリロイルとメタアクリロイルの総称として（メタ）アクリロイルと記載する。）等の（メタ）アクリロイルオキシ基とカルボン酸基の間に直鎖炭化水素基が存在するカルボン酸化合物；６−（メタ）アクリロイルオキシエチルナフタレン−１，２，６−トリカルボン酸等の（メタ）アクリロイルオキシアルキルナフタレン（ポリ）カルボン酸；４−（メタ）アクリロイルオキシメチルトリメリット酸、４−（メタ）アクリロイルオキシエチルトリメリット酸、４−（メタ）アクリロイルオキシブチルトリメリット酸等といった（メタ）アクリロイルオキシアルキルトリメリット酸；４−［２−ヒドロキシ−３−（メタ）アクリロイルオキシ］ブチルトリメリット酸等のさらに水酸基を含有する化合物；２，３−ビス（３，４−ジカルボキシベンゾイルオキシ）プロピル（メタ）アクリレート（以下、アクリレートとメタアクリレートの総称として（メタ）アクリレートと記載する）等のカルボキシベンゾイルオキシを有する化合物；Ｎ，Ｏ−ジ（メタ）アクリルチロシン、Ｏ−（メタ）アクリルチロシン、Ｎ−（メタ）アクリルチロシン、Ｎ−（メタ）アクリルフェニルアラニン、Ｏ−（メタ）アクリルフェニルアラニン、Ｎ，Ｏ−ジ（メタ）アクリルフェニルアラニン等のＮ−及び／又はＯ−位置換のモノ又はジ（メタ）アクリルアミノ酸；Ｎ−（メタ）アクリル−４−アミノ安息香酸、Ｎ−（メタ）アクリル−５−アミノ安息香酸、２−又は３−又は４−（メタ）アクリロイルオキシ安息香酸、４−又は５−（メタ）アクリロイルアミノサリチル酸等の官能性置換基を有する安息香酸の（メタ）アクリロイル化合物；２−ヒドロキシエチル（メタ）アクリレートとピロメリット酸二無水物の付加生成物、２−ヒドロキシエチル（メタ）アクリレ−トと無水マレイン酸又は３，３’，４，４’−ベンゾフェノンテトラカルボン酸二無水物又は３，３’，４，４’−ビフェニルテトラカルボン酸二無水物の付加反応物等のヒドロキシアルキル（メタ）アクリレートと不飽和ポリカルボン酸無水物の付加反応物；２−（３，４−ジカルボキシベンゾイルオキシ）−１，３−ジ（メタ）アクリロイルオキシプロパン、Ｎ−フェニルグリシン又はＮ−トリルグリシンとグリシジル（メタ）アクリレ−トとの付加物、４−［（２−ヒドロキシ−３−（メタ）アクリロイルオキシプロピル）アミノ］フタル酸、３−又は４−［Ｎ−メチル−Ｎ−（２−ヒドロキシ−３−（メタ）アクリロイルオキシプロピル）アミノ］フタル酸などのポリカルボキシベンゾイルオキシと（メタ）アクリロイルオキシを有する化合物などを挙げることができる。これらのうち、１１−（メタ）アクリロイルオキシ−１，１−ウンデカンジカルボン酸及び４−（メタ）アクリロイルオキシエチルトリメリット酸が好ましく用いられる。 In the present invention, examples of the polymerizable compound having a carboxyl group, which is a specific example of the (β1a) component, include (meth) acrylic acid (hereinafter referred to as (meth) acrylic acid as a generic term for acrylic acid and methacrylic acid). Α-unsaturated carboxylic acids such as maleic acid; vinyl aromatic ring compounds such as 4-vinylbenzoic acid; 11- (meth) acryloyloxy-1,1-undecanedicarboxylic acid (hereinafter referred to as acryloyl and methacryloyl) A carboxylic acid compound in which a linear hydrocarbon group is present between the (meth) acryloyloxy group and the carboxylic acid group, such as 6- (meth) acryloyloxyethylnaphthalene-1 (Meth) acryloyloxyalkylnaphthalene (poly) carboxylic acid such as 1,2,6-tricarboxylic acid; 4- (meth) (Meth) acryloyloxyalkyl trimellitic acid such as acryloyloxymethyl trimellitic acid, 4- (meth) acryloyloxyethyl trimellitic acid, 4- (meth) acryloyloxybutyl trimellitic acid; 4- [2-hydroxy-3 -(Meth) acryloyloxy] butyl trimellitic acid and other compounds further containing a hydroxyl group; 2,3-bis (3,4-dicarboxybenzoyloxy) propyl (meth) acrylate (hereinafter, a generic term for acrylate and methacrylate) Compounds having carboxybenzoyloxy such as (meth) acrylate); N, O-di (meth) acryl tyrosine, O- (meth) acryl tyrosine, N- (meth) acryl tyrosine, N- (meth) acryl Phenylalanine, O- (meth) a N- and / or O-substituted mono- or di (meth) acrylic amino acids such as rylphenylalanine, N, O-di (meth) acrylphenylalanine; N- (meth) acryl-4-aminobenzoic acid, N- ( (Meth) acryl-5-aminobenzoic acid, 2- or 3- or 4- (meth) acryloyloxybenzoic acid, 4- or 5- (meth) acryloylaminosalicylic acid and other benzoic acid (meth) ) Acrylyl compound; addition product of 2-hydroxyethyl (meth) acrylate and pyromellitic dianhydride, 2-hydroxyethyl (meth) acrylate and maleic anhydride or 3,3 ′, 4,4′-benzophenone Hydroxyalkyl such as tetracarboxylic dianhydride or addition reaction product of 3,3 ′, 4,4′-biphenyltetracarboxylic dianhydride Addition reaction product of ru (meth) acrylate and unsaturated polycarboxylic acid anhydride; 2- (3,4-dicarboxybenzoyloxy) -1,3-di (meth) acryloyloxypropane, N-phenylglycine or N- Adduct of tolylglycine and glycidyl (meth) acrylate, 4-[(2-hydroxy-3- (meth) acryloyloxypropyl) amino] phthalic acid, 3- or 4- [N-methyl-N- ( And 2-hydroxy-3- (meth) acryloyloxypropyl) amino] phthalic acid and other compounds having polycarboxybenzoyloxy and (meth) acryloyloxy. Of these, 11- (meth) acryloyloxy-1,1-undecanedicarboxylic acid and 4- (meth) acryloyloxyethyl trimellitic acid are preferably used.
リン酸基としては、少なくとも１個の水酸基がリン原子に結合している基及び水中で容易に水酸基に変換し得る官能基としての例えばリン酸エステル基を１個又は２個有する基を好ましく例示することができる。このような基を有する重合性単量体としては、例えば２−（メタ）アクリロイルオキシエチルアシドホスフェート、２−及び／又は３−（メタ） アクリロイルオキシプロピルアシドホスフェート、４−（メタ）アクリロイルオキシブチルアシドホスフェート、６−（メタ）アクリロイルオキシヘキシルアシドホスフェート、８−（メタ）アクリロイルオキシオクチルアシドホスフェート、１０−（メタ）アクリロイルオキシデシルアシドホスフェート、１２−（メタ）アクリロイルオキシドデシルアシドホスフェート等の（メタ）アクリロイルオキシアルキルアシドホスフェート；ビス［２−（メタ）アクリロイルオキシエチル］アシドホスフェート、ビス［２−又は３−（メタ）アクリロイルオキシプロピル］アシドホスフェート等の２つ以上の（メタ）アクリロイルオキシアルキル基を有するアシドホスフェート；２−（メタ）アクリロイルオキシエチルフェニルアシドホスフェート、２−（メタ）アクリロイルオキシエチル−ｐ−メトキシフェニルアシドホスフェート等の（メタ）アクリロイルオキシアルキル基とフェニレン基などの芳香環やさらには酸素原子などのヘテロ原子を介して有するアシドホスフェートなどを挙げることができる。これらの化合物におけるリン酸基を、チオリン酸基に置き換えた化合物も例示することができる。これらのうち、２−（メタ）アクリロイルオキシエチルアシドホスフェートを好ましく使用することができる。 Preferred examples of the phosphoric acid group include a group in which at least one hydroxyl group is bonded to a phosphorus atom and a group having one or two phosphate ester groups as a functional group that can be easily converted into a hydroxyl group in water. can do. Examples of the polymerizable monomer having such a group include 2- (meth) acryloyloxyethyl acid phosphate, 2- and / or 3- (meth) acryloyloxypropyl acid phosphate, 4- (meth) acryloyloxybutyl. (Meta) such as acid phosphate, 6- (meth) acryloyloxyhexyl acid phosphate, 8- (meth) acryloyloxyoctyl acid phosphate, 10- (meth) acryloyloxydecyl acid phosphate, 12- (meth) acryloyl oxide decyl acid phosphate 2) acryloyloxyalkyl acid phosphate; bis [2- (meth) acryloyloxyethyl] acid phosphate, bis [2- or 3- (meth) acryloyloxypropyl] acid phosphate, etc. (Meth) acryloyloxyalkyl groups such as the above (meth) acryloyloxyalkyl group-containing acid phosphates; 2- (meth) acryloyloxyethylphenyl acid phosphate, 2- (meth) acryloyloxyethyl-p-methoxyphenyl acid phosphate, etc. And an acid phosphate having an aromatic ring such as a phenylene group or a heteroatom such as an oxygen atom. The compound which substituted the phosphate group in these compounds by the thiophosphate group can also be illustrated. Of these, 2- (meth) acryloyloxyethyl acid phosphate can be preferably used.
スルホン酸基あるいはスルホン酸基に容易に水中で変換し得る官能基を有する重合性単量体として、例えば２−スルホエチル（メタ）アクリレート、２−又は１−スルホ−１−又は２−プロピル（メタ）アクリレート、１−又は３−スルホ−２−ブチル（メタ）アクリレート等のスルホアルキル（メタ）アクリレート；３−ブロモ−２−スルホ−２−プロピル（メタ）アクリレート、３−メトキシ−１−スルホ−２−プロピル（メタ）アクリレート等の前記のアルキル部にハロゲンや酸素などのヘテロ原子を含む原子団を有する化合物；１，１−ジメチル−２−スルホエチル（メタ）アクリルアミド、２−メチル−２−（メタ）アクリルアミドプロパンスルホン酸等の前記アクリレートに換えてアクリルアミドである化合物など；さらには４−スチレンスルホン酸、４−（プロプ−１−エン−２−イル）ベンゼンスルホン酸などのビニルアリールスルホン酸などを挙げることができる。これらのうち、４−スチレンスルホン酸を好ましく使用することができる。（β１ａ）成分の上記単量体は単独であるいは２種以上組み合わせて使用することができる。 Examples of polymerizable monomers having a sulfonic acid group or a functional group that can be easily converted into a sulfonic acid group in water include 2-sulfoethyl (meth) acrylate, 2- or 1-sulfo-1- or 2-propyl (meta ) Sulfoalkyl (meth) acrylates such as acrylate, 1- or 3-sulfo-2-butyl (meth) acrylate; 3-bromo-2-sulfo-2-propyl (meth) acrylate, 3-methoxy-1-sulfo- Compounds having an atomic group containing a hetero atom such as halogen or oxygen in the alkyl part such as 2-propyl (meth) acrylate; 1,1-dimethyl-2-sulfoethyl (meth) acrylamide, 2-methyl-2- ( A compound that is acrylamide instead of the acrylate such as meth) acrylamide propane sulfonic acid; Styrene sulfonic acid and vinyl aryl sulfonic acids such as 4- (prop-1-en-2-yl) benzenesulfonic acid. Of these, 4-styrenesulfonic acid can be preferably used. The above monomers of the (β1a) component can be used alone or in combination of two or more.
上記（β１ａ）分子内に酸性基と重合性基を有する単量体は、（β１）単官能重合性単量体を含有する単量体組成物１００重量％に対して、好ましくは６〜７０重量％、より好ましくは１１〜４６重量％、更に好ましくは１７〜３４重量％の範囲で使用される。このような量で（β１ａ）分子内に酸性基と重合性基を有する単量体を使用することにより、本発明の複合充填材及び歯科用組成物は、被着体である歯質に代表される硬組織に対して良好な接着性を示すようになる。 The (β1a) monomer having an acidic group and a polymerizable group in the molecule is preferably 6 to 70 with respect to 100 wt% of the monomer composition containing the (β1) monofunctional polymerizable monomer. It is used in the range of wt%, more preferably 11 to 46 wt%, still more preferably 17 to 34 wt%. By using a monomer having an acidic group and a polymerizable group in the molecule (β1a) in such an amount, the composite filler and the dental composition of the present invention are represented by a dentin as an adherend. Good adhesion to the hard tissue.
（β１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物
本発明で用いられる（β１ｂ）成分は、分子内に１つの重合性基を有し、酸性基を有しない化合物である。このような（β１ｂ）成分として使用できる化合物の例としては、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ｎ−プロピル（メタ）アクリレート、ｎ−ブチル（メタ）アクリレートなどのアルキル（メタ）アクリレート類；２−ハイドロキシエチル（メタ）アクリレート、３−ハイドロキシプロピル（メタ）アクリレートなどのハイドロキシアルキル（メタ）アクリレート類；２−（２−メトキシエトキシ）エチル（メタ）アクリレート、２−（２−（２−（２−メトキシエトキシ）エトキシ）エトキシ）エチル（メタ）アクリレートなどのポリアルキレングリコールアルキルエーテルの（メタ）アクリレート類（Ｒ１−（−Ｏ−Ｒ２−）ｎ−Ｏ−ＣＯＣＨ（Ｒ３）＝ＣＨ２（Ｒ１：アルキル基、Ｒ２：アルキレン基、Ｒ３：水素又はメチル原子団）；アセトアセトキシエチル（メタ）アクリレート；シクロブチル（メタ）アクリレート、シクロヘキシル（メタ）アクリレートなどのシクロアルキル（メタ）アクリレート類；（テトラハイドロフラン−２−イル）（メタ）アクリレートなどのヘテロ原子を含む環状アルキル（メタ）アクリレート類；パーフルオロオクチル（メタ）アクリレート及びヘキサフルオロイソプロピル（メタ）アクリレートなどの（メタ）アクリル酸のフルオロアルキルエステル；３−（トリメトキシシリル）プロピル（メタ）アクリレートなどの（メタ）アクリロキシアルキル基を有するシラン化合物などを挙げることができる。これら（β１ｂ）成分の単量体は単独であるいは２種以上併用して重合に用いられる。
(Β1b) Compound having one polymerizable group in the molecule and not having an acidic group (β1b) component used in the present invention is a compound having one polymerizable group in the molecule and not having an acidic group It is. Examples of such compounds that can be used as the (β1b) component include alkyl (meth) acrylates such as methyl (meth) acrylate, ethyl (meth) acrylate, n-propyl (meth) acrylate, and n-butyl (meth) acrylate. 2-hydroxyethyl (meth) acrylate, hydroxyalkyl (meth) acrylates such as 3-hydroxypropyl (meth) acrylate; 2- (2-methoxyethoxy) ethyl (meth) acrylate, 2- (2- (2 (Meth) acrylates of polyalkylene glycol alkyl ethers such as — (2-methoxyethoxy) ethoxy) ethoxy) ethyl (meth) acrylate (R 1 — (— O—R 2 —) n —O—COCH (R 3 ) = CH 2 (R 1 : alkyl group, R 2 : alkyle Group, R 3 : hydrogen or methyl atom group); acetoacetoxyethyl (meth) acrylate; cycloalkyl (meth) acrylates such as cyclobutyl (meth) acrylate and cyclohexyl (meth) acrylate; (tetrahydrofuran-2-yl ) Cyclic alkyl (meth) acrylates containing heteroatoms such as (meth) acrylate; fluoroalkyl esters of (meth) acrylic acid such as perfluorooctyl (meth) acrylate and hexafluoroisopropyl (meth) acrylate; 3- (tri Examples thereof include silane compounds having a (meth) acryloxyalkyl group such as methoxysilyl) propyl (meth) acrylate, etc. These (β1b) component monomers are used alone or in combination of two or more for polymerization. It is done.
また、（β１ｂ）成分として、歯質など硬組織に対する高い接着力を得るために、歯質などとの接着界面へのモノマーの拡散に低分子量モノマー、例えば分子量が３００以下の低分子量モノマーを使用することが好ましい。このような低分子量モノマーとしては、例えば、メチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、エチレングリコールモノメチルエーテル（メタ）アクリレートを挙げることができる。本発明においては、重合性単量体である（β１ｂ）成分としてこのような低分子量モノマーも使用することもできる。
特に本発明では分子内に１つの重合性基を有し、酸性基を有しない化合物（（β１ｂ）として、人体への刺激性が比較的低いメタアクリレートが特に好ましく使用される。
また、本発明で使用する（β１ｂ）成分としては、酸性基を有する上記（β１ａ）成分を室温で溶解可能な化合物であることが好ましい。
上記（β１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物は、（β１）単官能重合性単量体を含有する単量体組成物１００重量％に対して、好ましくは１１〜８４重量％、より好ましくは２９〜７６重量％、更に好ましくは５０〜６８重量％の範囲で使用される。本発明で使用される（β１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物は、本発明の複合充填材及び歯科用組成物の有する優れた特性を発現させるための基礎となるモノマーであり、上記範囲内で使用することによって本発明の複合充填材及び歯科用組成物の物性に関する基礎的特性が確立する。
In addition, as a component (β1b), a low molecular weight monomer, for example, a low molecular weight monomer having a molecular weight of 300 or less is used for the diffusion of the monomer to the adhesive interface with the tooth structure, etc., in order to obtain a high adhesive force to the hard tissue such as the tooth structure. It is preferable to do. Examples of such low molecular weight monomers include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, and ethylene glycol monomethyl ether (meth) acrylate. In the present invention, such a low molecular weight monomer can also be used as the component (β1b) which is a polymerizable monomer.
In particular, in the present invention, as a compound having one polymerizable group in the molecule and not having an acidic group ((β1b)), a methacrylate having a relatively low irritation to the human body is particularly preferably used.
In addition, the (β1b) component used in the present invention is preferably a compound that can dissolve the (β1a) component having an acidic group at room temperature.
The compound (β1b) having one polymerizable group in the molecule and not having an acidic group is preferably based on 100% by weight of the monomer composition containing (β1) monofunctional polymerizable monomer. Is used in the range of 11 to 84% by weight, more preferably 29 to 76% by weight, and still more preferably 50 to 68% by weight. The compound having one polymerizable group in the molecule (β1b) used in the present invention and not having an acidic group is used for developing the excellent properties of the composite filler and the dental composition of the present invention. It is a basic monomer, and when used within the above range, basic characteristics relating to the physical properties of the composite filler and dental composition of the present invention are established.
（β２）ポリ（（メタ）アクリレート）系重合体粒子からなる充填材
本発明に配合される（β２）成分は、予め別に重合させておいた重合体であり、これ以外の成分を重合させる際に混合するものであり、例えば、ポリ（（メタ）アクリレート）粒子等からなる充填材である。このポリマー粒子を形成するモノマーとしては、例えばメチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、ブチル（メタ）アクリレートなどのアルキル（メタ）アクリレート、シクロヘキシル（メタ）アクリレートなどのシクロアルキル（メタ）アクリレート、ベンジル（メタ）アクリレートなど芳香族（メタ）アクリレートなどのような（メタ）アクリレート系モノマーを挙げることができる。また、本発明のポリ（（メタ）アクリレート）系重合体には、必要に応じて少量の架橋性モノマーを共重合させることができる。架橋性モノマーとしては、例えばエチレングリコールジ（メタ）アクリレート、トリエチレングリコールジ（メタ）アクリレート、ブタジエンなどの多官能モノマーを挙げることができる。
（β２）成分１００重量％中、前記架橋性モノマーは、好ましくは５０重量％以下、より好ましくは３５重量％以下、更に好ましくは２０重量％以下の範囲で使用される。前記数値範囲の上限値を上回ると（β２）ポリ（（メタ）アクリレート）系重合体粒子からなる充填材が硬くなることがあり、（β１ａ）分子内に酸性基と重合性基を有する化合物、及び（β１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物との馴染みが低下し易くなるので、所望の物性を発揮することができにくくなり、好ましくない。
また、（β２）成分中には、少量ならば（メタ）アクリレート系成分以外の単量体や重合体が、共重合や混合していてもよい。（メタ）アクリレート系成分以外の成分としては、スチレン、ブタジエンなどのビニル化合物等が挙げられる。前記（メタ）アクリレート系成分以外の成分は、好ましくは５０重量％以下、より好ましくは４０重量％以下、更に好ましくは３０重量％以下の範囲で使用される。
本発明で充填材（β２）として好適に使用されるポリ（（メタ）アクリレート）系重合体粒子の重合体重量平均分子量は、５万〜６０万の範囲内にあることが好ましい。
また、本発明において、これらの充填材（β２）は、単独であるいは組み合わせて使用することができる。
(Β2) Filler Composed of Poly ((meth) acrylate) Polymer Particles The (β2) component blended in the present invention is a polymer that has been polymerized separately in advance, and other components are polymerized. For example, it is a filler made of poly ((meth) acrylate) particles or the like. Examples of monomers that form the polymer particles include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, alkyl (meth) acrylate such as butyl (meth) acrylate, and cyclohexane such as cyclohexyl (meth) acrylate. (Meth) acrylate monomers such as aromatic (meth) acrylates such as alkyl (meth) acrylates and benzyl (meth) acrylates may be mentioned. The poly ((meth) acrylate) -based polymer of the present invention can be copolymerized with a small amount of a crosslinkable monomer as required. Examples of the crosslinkable monomer include polyfunctional monomers such as ethylene glycol di (meth) acrylate, triethylene glycol di (meth) acrylate, and butadiene.
In 100% by weight of the component (β2), the crosslinkable monomer is preferably used in an amount of 50% by weight or less, more preferably 35% by weight or less, and still more preferably 20% by weight or less. When the upper limit of the numerical range is exceeded, the filler composed of (β2) poly ((meth) acrylate) polymer particles may be hardened, and (β1a) a compound having an acidic group and a polymerizable group in the molecule, And (β1b) Since it becomes easy to decrease conformity with a compound having one polymerizable group in the molecule and not having an acidic group, it becomes difficult to exhibit desired physical properties, which is not preferable.
Further, in the (β2) component, a monomer or a polymer other than the (meth) acrylate-based component may be copolymerized or mixed as long as the amount is small. Examples of components other than the (meth) acrylate component include vinyl compounds such as styrene and butadiene. Components other than the (meth) acrylate component are preferably used in the range of 50% by weight or less, more preferably 40% by weight or less, and still more preferably 30% by weight or less.
The polymer weight average molecular weight of the poly ((meth) acrylate) polymer particles suitably used as the filler (β2) in the present invention is preferably in the range of 50,000 to 600,000.
In the present invention, these fillers (β2) can be used alone or in combination.
本発明において、（β１ａ）成分と（β１ｂ）成分と後述する（β３）成分との馴染みを向上させるためには、上記充填材（β２）の粒子の平均粒子径は、０．００１〜６０μｍの範囲内にあることが好ましく、さらに、０．０１〜５０μｍの範囲内にあることが特に好ましい。
上記（β２）ポリ（（メタ）アクリレート）系重合体粒子からなる充填材は、（β１）単官能重合性単量体を含有する単量体組成物の、（β２）以外の成分１００重量％に対して、好ましくは０〜１８５重量％、より好ましくは８．６〜７１重量％、更に好ましくは１７〜２１重量％の範囲で使用される。
前記数値範囲の下限値以上であると、歯科用複合充填材としての形態を維持でき、好ましい。一方、前記数値範囲の上限値を上回ると、本発明の複合充填材に含有する（α）成分の性能が発揮され難くなり、所望する複合充填材及び歯科用組成物硬化体が得られなくなり好ましくない。
In the present invention, in order to improve the familiarity of the (β1a) component, the (β1b) component, and the (β3) component described later, the average particle diameter of the particles of the filler (β2) is 0.001 to 60 μm. It is preferably within the range, and more preferably within the range of 0.01 to 50 μm.
The filler comprising the (β2) poly ((meth) acrylate) polymer particles is 100% by weight of components other than (β2) of the monomer composition containing the (β1) monofunctional polymerizable monomer. Is preferably 0 to 185% by weight, more preferably 8.6 to 71% by weight, and still more preferably 17 to 21% by weight.
It is preferable if it is equal to or more than the lower limit of the numerical range because the form as a dental composite filler can be maintained. On the other hand, when the value exceeds the upper limit of the numerical range, the performance of the component (α) contained in the composite filler of the present invention is hardly exhibited, and the desired composite filler and a cured dental composition cannot be obtained. Absent.
（β３）重合開始剤
本発明に配合される（β３）成分は、重合開始剤である。重合開始剤（β３）としては、例えば有機ホウ素化合物、有機過酸化物、無機化酸化物を挙げることができる。有機ホウ素化合物としては、例えばトリエチルホウ素、トリ（ｎ−プロピル）ホウ素、トリイソプロピルホウ素、トリ（ｎ−ブチル）ホウ素、トリ（ｓ−ブチル）ホウ素、トリイソブチルホウ素、トリペンチルホウ素、トリヘキシルホウ素、トリオクチルホウ素、トリデシルホウ素、トリドデシルホウ素、トリシクロペンチルホウ素、トリシクロヘキシルホウ素、ブチルジシクロヘキシルボランなどのトリアルキルホウ素；ブトキシジブチルホウ素などのアルコキシアルキルホウ素；ジイソアミルボラン、９−ボラビシクロ［３．３．１］ノナンなどのジアルキルボラン；テトラフェニルホウ素ナトリウム、テトラフェニルホウ素トリエタノールアミン塩、テトラフェニルホウ素ジメチル−ｐ−トルイジン塩、テトラフェニルホウ素ジメチルアミノ安息香酸エチルなどのアリールボレート化合物；部分酸化トリブチルホウ素などの部分酸化トリアルキルホウ素などを挙げることができる。なお、トリアルキルホウ素とそれより誘導される部分酸化トリアルキルホウ素などを併せてトリアルキルホウ素化合物という。
(Β3) Polymerization Initiator The (β3) component blended in the present invention is a polymerization initiator. Examples of the polymerization initiator (β3) include organic boron compounds, organic peroxides, and inorganic oxides. Examples of the organoboron compound include triethylboron, tri (n-propyl) boron, triisopropylboron, tri (n-butyl) boron, tri (s-butyl) boron, triisobutylboron, tripentylboron, trihexylboron, Trialkylboron such as trioctylboron, tridecylboron, tridodecylboron, tricyclopentylboron, tricyclohexylboron, butyldicyclohexylborane; alkoxyalkylboron such as butoxydibutylboron; diisoamylborane, 9-borabicyclo [3.3. 1] Dialkylborane such as nonane; tetraphenyl boron sodium, tetraphenyl boron triethanolamine salt, tetraphenyl boron dimethyl-p-toluidine salt, tetraphenyl boron dimethyl Aryl borate compounds such as amino ethyl benzoate; and partially oxidized trialkyl boron such as partial oxidation tributylboron can be exemplified. Trialkyl boron and partially oxidized trialkyl boron derived therefrom are collectively referred to as a trialkyl boron compound.
有機過酸化物としては、例えばジアセチルパーオキサイド、ジプロピルパーオキサイド、ジブチルパーオキサイド、ジカプロルパーオキサイド、ジラウリルパーオキサイド、ベンゾイルパーオキサイド、ｐ，ｐ’−ジクロルベンゾイルパ−オキサイド、ｐ，ｐ’−ジメトキシベンゾイルパーオキサイド、ｐ，ｐ’−ジメチルベンゾイルパーオキサイド及びｐ，ｐ’−ジニトロジベンゾイルパーオキサイドなどを挙げることができる。
無機過酸化物としては、例えば過硫酸アンモニウム、過硫酸カリウム、塩素酸カリウム、臭素酸カリウムおよび過リン酸カリウムなどを挙げることができる。酸化還元性金属化合物としては、例えば銅、鉄、コバルトなど遷移金属の硝酸塩、塩化塩、アセチルアセト塩などを挙げることができる。
これらの中では、トリブチルホウ素あるいは部分酸化トリブチルホウ素を用いることが好ましく、さらに最も好ましい有機ホウ素化合物は部分酸化トリブチルホウ素である。これらの（β３）成分は単独であるいは２種以上組み合わせで使用することができる。
Examples of the organic peroxide include diacetyl peroxide, dipropyl peroxide, dibutyl peroxide, dicaprol peroxide, dilauryl peroxide, benzoyl peroxide, p, p′-dichlorobenzoyl peroxide, p, p. Examples include '-dimethoxybenzoyl peroxide, p, p'-dimethylbenzoyl peroxide, and p, p'-dinitrodibenzoyl peroxide.
Examples of inorganic peroxides include ammonium persulfate, potassium persulfate, potassium chlorate, potassium bromate, and potassium perphosphate. Examples of the redox metal compound include nitrates, chlorides, and acetylacetates of transition metals such as copper, iron, and cobalt.
Among these, it is preferable to use tributyl boron or partially oxidized tributyl boron, and the most preferable organic boron compound is partially oxidized tributyl boron. These (β3) components can be used alone or in combination of two or more.
さらに本発明の歯科用組成物において硬化剤の助剤として本発明の目的を損なわない限り、光重合開始剤を配合されていてもよい。光重合開始剤としては、可視光線を照射することによって重合性モノマーの重合を開始しうるものが好ましく使用され、例えばベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテルなどのベンゾイン類；ベンジル、４，４’−ジクロロベンジル、ジアセチル、α−シクロヘキサンジオン、ｄ，１−カンファキノン（ＣＱ）、カンファキノン−１０−スルホン酸、カンファキノン−１０−カルボン酸などのα−ジケトン；ベンゾフェノン、ベンゾイル安息香酸メチル、ヒドロキシベンゾフェノンなどのジフェニルモノケトン類；２，４−ジエチルチオキサントン、２−イソプロピルチオキサントンなどのチオキサントン類；２，４，６−トリメチルベンゾイルジフェニルホスフィンオキサイドなどのアシルホスフィンオキサイド類などの光増感剤を挙げることができる。
これらの中ではｄ，１−カンファキノン、カンファキノン−１０−カルボン酸、２，４，６−トリメチルベンゾイルジフェニルホスフィンオキサイドが特に好ましい。これら光重合開始剤は単独であるいは組み合わせて使用することができる。
Furthermore, in the dental composition of the present invention, a photopolymerization initiator may be blended as long as the object of the present invention is not impaired as an auxiliary of the curing agent. As the photopolymerization initiator, those capable of initiating polymerization of a polymerizable monomer by irradiation with visible light are preferably used. For example, benzoins such as benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether; benzyl, Α-diketones such as 4,4′-dichlorobenzyl, diacetyl, α-cyclohexanedione, d, 1-camphorquinone (CQ), camphorquinone-10-sulfonic acid, camphorquinone-10-carboxylic acid; benzophenone, benzoylbenzoic acid Diphenyl monoketones such as methyl acid and hydroxybenzophenone; thioxanthones such as 2,4-diethylthioxanthone and 2-isopropylthioxanthone; 2,4,6-trimethylbenzoyldiphenylphosphine oxide Photosensitizer such as acylphosphine oxides of the like.
Among these, d, 1-camphorquinone, camphorquinone-10-carboxylic acid, and 2,4,6-trimethylbenzoyldiphenylphosphine oxide are particularly preferable. These photopolymerization initiators can be used alone or in combination.
加えて、上記光重合開始剤の重合開始効果を向上するため、有機ホウ素化合物の触媒効果に悪影響を及ぼさない還元性化合物の併用も可能である。例えば、Ｎ，Ｎ−ジメチルアニリン、Ｎ，Ｎ−ジメチル−ｐ−トルイジン、Ｎ，Ｎ−ジエチル−ｐ−トルイジン、Ｎ，Ｎ−ジエタノール−ｐ−トルイジン、Ｎ，Ｎ−ジメチル−ｐ−ｔ−ブチルアニリン、Ｎ，Ｎ−ジメチルアニシジン、Ｎ，Ｎ−ジメチル−ｐ−クロルアニリン、Ｎ，Ｎ−ジメチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ−ジエチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ−ジメチルアミノ安息香酸およびそのアルキルエステル及びそれらの塩、Ｎ，Ｎ−ジエチルアミノ安息香酸およびそのアルキルエステルおよびそれらの塩、Ｎ，Ｎ−ジメチルアミノベンズアルデヒド、Ｎ−フェニルグリシン及びその塩、Ｎ−トリルグリシンおよびその塩、Ｎ，Ｎ−（３−（メタ）アクリロイルオキシ−２−ヒドロキシプロピル）フェニルグリシンおよびその塩などの有機還元性化合物を挙げることができる。 In addition, in order to improve the polymerization initiation effect of the photopolymerization initiator, it is possible to use a reducing compound that does not adversely affect the catalytic effect of the organoboron compound. For example, N, N-dimethylaniline, N, N-dimethyl-p-toluidine, N, N-diethyl-p-toluidine, N, N-diethanol-p-toluidine, N, N-dimethyl-pt-butyl Aniline, N, N-dimethylanisidine, N, N-dimethyl-p-chloroaniline, N, N-dimethylaminoethyl (meth) acrylate, N, N-diethylaminoethyl (meth) acrylate, N, N-dimethylamino Benzoic acid and alkyl esters thereof and salts thereof, N, N-diethylaminobenzoic acid and alkyl esters thereof and salts thereof, N, N-dimethylaminobenzaldehyde, N-phenylglycine and salts thereof, N-tolylglycine and salts thereof N, N- (3- (meth) acryloyloxy-2-hydroxypropyl) It can be mentioned Nirugurishin and organic reducing compounds such as salts thereof.
上記（β３）重合開始剤は、（β１）単官能重合性単量体を含有する単量体組成物１００重量％に対して、好ましくは０．５〜１０重量％、更に好ましくは１〜１０重量％の範囲で使用される。また、本発明で光重合開始剤を使用する場合、有機ホウ素化合物の使用量を１００重量％に対して、好ましくは０．１〜１０重量％、更に好ましくは０．２〜５重量％の範囲で使用される。さらに、還元性化合物の配合量は、通常は使用される光重合開始剤の０．５〜３．０倍の範囲で使用される。
前記数値範囲の下限値を下回るとレジン系組成物が硬化することなく重合が終了してしまい所望する物性を得ることができなくなり、一方、上限値を上回ると重合に関与できなかった重合開始剤がレジン系組成物硬化体の物性に影響を及ぼし、基礎的特性が損なわれるおそれがあり、何れも好ましくない。
The (β3) polymerization initiator is preferably 0.5 to 10% by weight, more preferably 1 to 10%, based on 100% by weight of the monomer composition containing the (β1) monofunctional polymerizable monomer. Used in the range of% by weight. Moreover, when using a photoinitiator by this invention, Preferably the usage-amount of an organic boron compound is 0.1-10 weight% with respect to 100 weight%, More preferably, it is the range of 0.2-5 weight%. Used in. Furthermore, the compounding quantity of a reducing compound is normally used in the range of 0.5-3.0 times of the photoinitiator used.
If the lower limit of the numerical range is not reached, the polymerization is completed without curing the resin-based composition, and the desired physical properties cannot be obtained. On the other hand, if the upper limit is exceeded, the polymerization initiator cannot be involved in the polymerization. Affects the physical properties of the cured resin-based composition, and the basic characteristics may be impaired.
（α）生物活性セメント成分
本発明に使用される（α）成分は、生物活性セメント成分である。この（α）成分とは、硬組織などの生体組織に対して有益な作用を達成できるカルシウム系生体材料である。適した生物活性セメントとしては、特に限定されるわけではないが、例えばバイオガラス、リン酸カルシウム系セメント、水酸化カルシウム系セメント、ヒドロキシアパタイト系材料、アルミン酸カルシウム系セメント及びポルトランドセメント等が挙げられる。
バイオガラスとしては、例えばＳｉＯ２−ＣａＯ−Ｎａ２Ｏ−Ｐ２Ｏ５系ガラス、ＳｉＯ２−ＣａＯ−Ｎａ２Ｏ−Ｐ２Ｏ５−Ｋ２Ｏ−ＭｇＯ系ガラス、ＳｉＯ２−ＣａＯ−Ａｌ２Ｏ３−Ｐ２Ｏ５系ガラス（アパタイトウォラストナイト結晶化ガラスとも称する）及びＣａＯ−Ａｌ２Ｏ３−Ｐ２Ｏ５系ガラス等が挙げられる。
(Α) Bioactive cement component The (α) component used in the present invention is a bioactive cement component. This (α) component is a calcium-based biomaterial that can achieve a beneficial effect on a living tissue such as a hard tissue. Suitable bioactive cements are not particularly limited, and examples include bioglass, calcium phosphate cement, calcium hydroxide cement, hydroxyapatite material, calcium aluminate cement, and Portland cement.
Examples of bioglass include SiO 2 —CaO—Na 2 O—P 2 O 5 glass, SiO 2 —CaO—Na 2 O—P 2 O 5 —K 2 O—MgO glass, and SiO 2 —CaO—Al. Examples thereof include 2 O 3 —P 2 O 5 glass (also referred to as apatite wollastonite crystallized glass) and CaO—Al 2 O 3 —P 2 O 5 glass.
リン酸カルシウム系セメントとしては、例えばα型第３リン酸カルシウム単独；第４リン酸カルシウム単独；α型第３リン酸カルシウムと第４リン酸カルシウムとの混合物；α型第３リン酸カルシウムと第２リン酸カルシウム及び／又は第１リン酸カルシウムとの混合物（即ちα型第３リン酸カルシウムと第２リン酸カルシウムとの混合物、α型第３リン酸カルシウムと第１リン酸カルシウムとの混合物、α型第３リン酸カルシウムと第２リン酸カルシウムと第１リン酸カルシウムとの混合物）；第４リン酸カルシウムと第２リン酸カルシウム及び／又は第１リン酸カルシウムとの混合物（即ち、第４リン酸カルシウムと第２リン酸カルシウムとの混合物、第４リン酸カルシウムと第１リン酸カルシウムとの混合物、第４リン酸カルシウムと第２リン酸カルシウムと第１リン酸カルシウムとの混合物）；若しくはα型第３リン酸カルシウムと第４リン酸カルシウムと第２リン酸カルシウム及び／又は第１リン酸カルシウムとの混合物（即ちα型第３リン酸カルシウムと第４リン酸カルシウムと第２リン酸カルシウムとの混合物、α型第３リン酸カルシウムと第４リン酸カルシウムと第１リン酸カルシウムとの混合物、α型第３リン酸カルシウムと第４リン酸カルシウムと第２リン酸カルシウムと第１リン酸カルシウムとの混合物）等を挙げることができる。 Examples of calcium phosphate cements include α-type tricalcium phosphate alone; quaternary calcium phosphate alone; a mixture of α-type third calcium phosphate and fourth calcium phosphate; a mixture of α-type third calcium phosphate and dibasic calcium phosphate and / or first calcium phosphate. (That is, a mixture of α-type tricalcium phosphate and dicalcium phosphate, a mixture of α-type tricalcium phosphate and first calcium phosphate, a mixture of α-type tricalcium phosphate, second calcium phosphate and first calcium phosphate); fourth calcium phosphate and A mixture of second calcium phosphate and / or first calcium phosphate (ie, a mixture of fourth calcium phosphate and second calcium phosphate, a mixture of fourth calcium phosphate and first calcium phosphate, fourth calcium phosphate and second A mixture of calcium phosphate and primary calcium phosphate); or a mixture of α-type third calcium phosphate, fourth calcium phosphate, second calcium phosphate and / or first calcium phosphate (ie α-type third calcium phosphate, fourth calcium phosphate and second calcium phosphate). A mixture of α-type tricalcium phosphate, a fourth calcium phosphate and a first calcium phosphate, a mixture of α-type third calcium phosphate, a fourth calcium phosphate, a second calcium phosphate and a first calcium phosphate).
ポルトランドセメントしては、一般的に土木建築用途に用いられているポルトランドセメントを適宜リファインして、歯科用途に適用したものである。
ポルトランドセメントは、カルシウムの酸化物とケイ素の酸化物を主体として、少量の硫酸カルシウムやアルミニウムの酸化物と、必要に応じて鉄等の遷移金属やその他のアルカリ金属元素やアルカリ土類元素の酸化物や塩を少量含有してなるものであり、好適には固溶体などの形態を有する。特に限定されるものではないが、通常よく知られているポルトランドセメントの一般的組成としては、各元素の酸化物にて換算して、
ＣａＯは、好ましく４〜８５重量％、より好ましく４０〜８５重量％、更に好ましくは５５〜７５重量％、特に好ましくは６０〜７０重量％、ＳｉＯ２は、好ましく１０〜９５重量％、より好ましく１０〜５０重量％、更に好ましくは１５〜４０重量％、更に好ましくは１８〜３２重量％、Ａｌ２Ｏ３は、好ましく０〜１７重量％、より好ましく０〜１５重量％、更に好ましくは１．５〜８重量％、特に好ましくは２．５〜６重量％、ＳＯ３は、好ましく０．０２〜６重量％、より好ましく０．２〜６重量％、更に好ましくは０．５〜３重量％、特に好ましくは０．６〜２重量％、Ｆｅ２Ｏ３は、好ましく０〜４．７重量％、より好ましく０〜４．５重量％、更に好ましくは０．２〜２重量％、特に好ましくは０．５〜１重量％、ＭｇＯは、好ましく０．０２〜５重量％、より好ましく０．２〜５重量％、更に好ましくは０．７〜３重量％、特に好ましくは０．８〜２重量％、上記の残余が、上記以外の遷移金属（原子番号順にバナジウムから銅）やその他のアルカリ金属元素等である。
As Portland cement, Portland cement generally used for civil engineering and building applications is appropriately refined and applied to dental applications.
Portland cement is mainly composed of oxides of calcium and silicon, with a small amount of calcium sulfate and aluminum oxide, and, if necessary, oxidation of transition metals such as iron and other alkali metal elements and alkaline earth elements. It contains a small amount of product or salt, and preferably has a form such as a solid solution. Although it is not particularly limited, as a general composition of Portland cement that is usually well known, in terms of oxides of each element,
CaO is preferably 4 to 85% by weight, more preferably 40 to 85% by weight, still more preferably 55 to 75% by weight, particularly preferably 60 to 70% by weight, and SiO 2 is preferably 10 to 95% by weight, more preferably 10%. 50 wt%, more preferably 15 to 40 wt%, more preferably 18 to 32 wt%, Al 2 O 3 is preferably 0 to 17 wt%, more preferably from 0 to 15 wt%, more preferably 1.5 8% by weight, particularly preferably from 2.5 to 6 wt%, SO 3 is preferably 0.02 to 6 wt%, more preferably from 0.2 to 6 wt%, more preferably 0.5 to 3 wt%, Particularly preferably 0.6 to 2 % by weight, Fe 2 O 3 is preferably 0 to 4.7% by weight, more preferably 0 to 4.5% by weight, still more preferably 0.2 to 2% by weight, particularly preferably. 0.5-1% by weight, Mg Is preferably 0.02 to 5% by weight, more preferably 0.2 to 5% by weight, still more preferably 0.7 to 3% by weight, particularly preferably 0.8 to 2% by weight. Transition metals (vanadium to copper in the order of atomic number) and other alkali metal elements.
但し、酸化物にて換算するとは、対象となる全体の実測重量Ｗｏを１００重量％として、そこに含まれる分析対象の元素のモル数ｎを分析測定し、当該モル数ｎの当該元素を酸化して、指定した形態の酸化物乃至は常温常圧下で最安定の酸化物にした場合の酸化物重量Ｗｘを割り出して、その重量％（１００＊Ｗｘ／Ｗｏ）を求めたものである。
従って、当該元素が当該酸化物形態にて含有されると限定されるものではないし、実際に含有されている当該元素の化合物形態が当該酸化物形態と相違すれば、その化合物の重量％が前記酸化物換算値と一致しないことも当然あり得る。
また、ケイ素成分として、ヒュームドシリカのような、アモルファス形態、ナノサイズ、乃至は球状の二酸化ケイ素がポルトランドセメント成分として含まれていてもよい。
However, in terms of oxide, the total measured weight Wo of the target is 100% by weight, the number of moles n of the element to be analyzed contained therein is analyzed and measured, and the number of moles n of the element is oxidized. Then, the oxide weight Wx of the designated form of oxide or the oxide most stable under normal temperature and normal pressure was determined, and the weight% (100 * Wx / Wo) was obtained.
Therefore, it is not limited that the element is contained in the oxide form. If the compound form of the element actually contained is different from the oxide form, the weight percent of the compound is Naturally, it may not match the oxide equivalent value.
Further, as the silicon component, amorphous form, nano-sized or spherical silicon dioxide such as fumed silica may be contained as the Portland cement component.
但し、ポルトランドセメントでは、これらの成分がそれぞれ単独で粉末乃至は粒子として存在していることは殆ど無く、複数の成分が混合された固溶体で存在している。
ポルトランドセメント（生セメント）は、石灰石、粘土、珪石、酸化鉄等を微粉砕混合し、例えばロータリーキルン等を用いて、最高１４５０℃に焼成し、１２００℃までは徐冷、それ以降は急冷してクリンカーを作製し、これに石膏３〜４重量％を加えて微粉砕して得ることができる。クリンカーは、酸化カルシウム、二酸化ケイ素、酸化アルミニウム及び酸化鉄などを主成分とする固溶体の粉末を主としてなり、例えば、
エーライト相としてケイ酸三カルシウム（３ＣａＯ・ＳｉＯ２）系固溶体、
ビーライト相としてケイ酸二カルシウム（２ＣａＯ・ＳｉＯ２）系固溶体、
アルミネート相としてカルシウムアルミネート（３ＣａＯ・Ａｌ２Ｏ３）系固溶体及び、
フェライト相としてカルシウムアルミノフェライト（３ＣａＯ・Ａｌ２Ｏ３・Ｆｅ２Ｏ３）
系固溶体を有しており、それぞれ、２０〜６５重量％、１０〜５５重量％、５〜１０重量％、９〜１５重量％含まれるものであり、その他、ガラス質の混合相を有することもある。
However, in Portland cement, these components rarely exist as powders or particles, respectively, and exist as a solid solution in which a plurality of components are mixed.
Portland cement (raw cement) is pulverized and mixed with limestone, clay, silica, iron oxide, etc., for example, using a rotary kiln, etc., fired to a maximum of 1450 ° C, gradually cooled to 1200 ° C, and then rapidly cooled A clinker is prepared, and 3-4% by weight of gypsum is added to the clinker and pulverized. The clinker is mainly composed of a solid solution powder mainly composed of calcium oxide, silicon dioxide, aluminum oxide, iron oxide, and the like.
Tricalcium silicate (3CaO.SiO 2 ) solid solution as alite phase,
Dicalcium silicate (2CaO.SiO 2 ) solid solution as belite phase,
Calcium aluminate (3CaO · Al 2 O 3 ) solid solution as the aluminate phase;
Calcium aluminoferrite (3CaO.Al 2 O 3 .Fe 2 O 3 ) as the ferrite phase
It has a solid solution of 20 to 65% by weight, 10 to 55% by weight, 5 to 10% by weight and 9 to 15% by weight, respectively, and may have a glassy mixed phase. is there.
歯科用途としては、審美性の観点から、着色を抑えるために鉄等の含有を適宜削減することが好ましい。また、粘度調整などの為にヒュームドシリカ等が添加される場合があり、必ずしも上記の通りの組成にて各固溶体が含まれるものではない。本発明の組成物ではエーライト相としてケイ酸三カルシウム（３ＣａＯ・ＳｉＯ２）系固溶体：ビーライト相としてケイ酸二カルシウム（２ＣａＯ・ＳｉＯ２）系固溶体：アルミネート相としてカルシウムアルミネート（３ＣａＯ・Ａｌ２Ｏ３）系固溶体＝２０〜６５：１０〜５５：５〜１０の重量比にて含まれていることが好ましい。 For dental use, from the viewpoint of aesthetics, it is preferable to appropriately reduce the content of iron or the like in order to suppress coloring. Moreover, fumed silica etc. may be added for viscosity adjustment etc., and each solid solution is not necessarily contained by the above composition. Tricalcium silicate as alite phase in the compositions of the present invention (3CaO · SiO 2) based solid solution: belite phase as dicalcium silicate (2CaO · SiO 2) based solid solution: Calcium as aluminate phase aluminate (3CaO · Al 2 O 3 ) -based solid solution is preferably contained in a weight ratio of 20 to 65:10 to 55: 5 to 10.
なお、生物活性セメントがポルトランドセメントのような水硬性セメントの場合には、水等と反応して硬化反応可能な状態（未硬化状態）にて複合充填材粒子を形成してもよいし、予め反応させて、もはや反応しない状態（硬化状態）にて複合充填材粒子を形成してもよい。或いは、不完全に反応させた状態（半硬化状態）であったり、それらの任意の混合物であってもよい。更には複合充填材粒子を形成してから、反応させたもの（複合後硬化状態）であってもよい。なお、未硬化状態では、反応性は良いという利点が有り、硬化状態では保存安定性や低発熱であるなどの低為害性を有するという利点が有り、半硬化状態や混合物では、その中間の特性を有するものである。また、複合後硬化状態では、生物活性セメント粒子は、複合充填材粒子表面は専ら硬化状態であり、内部の方は未硬化状態であるので、反応がゆるやかに進む利点がある。
前記の酸化カルシウム、二酸化ケイ素、酸化アルミニウム及び酸化鉄などの金属酸化物粉末を主成分とする粉末と硫酸カルシウムの他に、その他の粉末成分として、例えば、炭酸カルシウムなどの金属塩粉末、シリカガラス、アルミニウム含有ガラスなどのガラスフィラーなどを有する無機物を含むことができる。
In the case where the bioactive cement is a hydraulic cement such as Portland cement, the composite filler particles may be formed in a state capable of undergoing a curing reaction by reacting with water or the like (uncured state). You may make it react and may form a composite filler particle in the state (hardened state) which no longer reacts. Alternatively, it may be in an incompletely reacted state (semi-cured state) or any mixture thereof. Further, the composite filler particles may be formed and then reacted (composited post-cured state). In the uncured state, there is an advantage that the reactivity is good, and in the cured state, there is an advantage that it has low adverse effects such as storage stability and low heat generation. It is what has. Moreover, in the post-composite cured state, the bioactive cement particles have an advantage that the reaction proceeds slowly because the surface of the composite filler particles is exclusively cured and the inside is uncured.
In addition to the powders mainly composed of metal oxide powders such as calcium oxide, silicon dioxide, aluminum oxide and iron oxide and calcium sulfate, as other powder components, for example, metal salt powder such as calcium carbonate, silica glass An inorganic substance having a glass filler such as aluminum-containing glass can be included.
本発明における生物活性セメントのカルシウム含有率は、好ましくは５〜９０重量％、より好ましくは、１０〜８０重量％、更に好ましくは、３０〜６０重量％である。前記数値範囲の下限値を下回ると生物活性セメントの生体組織への効果が低下することとなり、一方、上限値を上回ると水和硬化後の機械的物性が低下することとなり、何れも好ましくない場合がある。本発明における生物活性セメントのリン含有率は、好ましくは２０〜９０重量％、より好ましくは、３０〜８０重量％、更に好ましくは、４０〜７０重量％である。前記数値範囲の下限値を下回ると構造体の機械的強度が低下することとなり、一方、上限値を上回ると構造体としての形態を維持することが困難となり、何れも好ましくない場合がある。
これら生物活性セメントは、適宜製造しても、市販品を用いてもよく、例えばリン酸カルシウム系セメントは、湿式法、乾式法若しくは水熱法等により、製造した合成リン酸カルシウム系セメントを用いてもよく、又は骨若しくは歯等から分離された天然のリン酸カルシウム系セメントを用いてもよい。
これら生物活性セメントは単独であるいは２種以上組み合わせて使用することができる。
The calcium content of the bioactive cement in the present invention is preferably 5 to 90% by weight, more preferably 10 to 80% by weight, and still more preferably 30 to 60% by weight. If the lower limit of the numerical range is not reached, the effect on the biological tissue of the bioactive cement will be reduced, whereas if the upper limit is exceeded, the mechanical properties after hydration will be reduced, both of which are not preferred There is. The phosphorus content of the bioactive cement in the present invention is preferably 20 to 90% by weight, more preferably 30 to 80% by weight, and still more preferably 40 to 70% by weight. If the value falls below the lower limit of the numerical range, the mechanical strength of the structure is lowered. On the other hand, if the value exceeds the upper limit, it is difficult to maintain the form of the structure, and either may not be preferable.
These bioactive cements may be produced as appropriate, or commercially available products may be used. For example, calcium phosphate cement may be a synthetic calcium phosphate cement produced by a wet method, a dry method or a hydrothermal method, Alternatively, natural calcium phosphate cement separated from bone or teeth may be used.
These bioactive cements can be used alone or in combination of two or more.
本発明に用いられる（α）成分の別の実施形態では、（β）重合体と混合する前に、セメント硬化体を形成し、その硬化体を規定のサイズ及び／若しくは形状の粒子に縮小、粉末化させて使用することも可能である。
（α）成分の形態としては、特に限定されるものではないが、例えば充填材のような粒子形状であることが好ましい。この場合に粒径はメッシュパスにて好ましくは１００μｍ以下、より好ましくは５０μｍ以下、さらに好ましくは３０μｍ以下の範囲内にある。なお、下限値については特に限定するものではないが、好ましくは０．００１μｍ以上、より好ましくは０．０１μｍ以上、さらに好ましくは０．５μｍ以上の範囲である。
なお、（α）成分が、例えば充填材のような粒子形状にて、（β）（β１）単官能重合性単量体を含有する単量体組成物の重合体の粒子中に分散して複合充填材粒子を形成している場合には、α）成分の粒子直径／当該複合粒子の直径の比率は、好ましくは１：１０００００〜１：１．００１、より好ましくは１：１０００〜１：１．０１、更に好ましくは１：１５〜１：２．５の範囲である。前記数値範囲の上限値を上回ると複合充填材としての形態を維持できないこととなり、いずれも好ましくない。
前記数値範囲の上限を上回ると、前記（β１ａ）、（β１ｂ）、（β２）、（β３）成分と均一に分散せず偏析してしまい、後述する複合充填材作製において（α）成分が前記（β１ａ）、（β１ｂ）、（β２）、（β３）成分で構成される重合性組成物に内包されずに粉末化されてしまうおそれがある。
In another embodiment of the component (α) used in the present invention, a cement hardened body is formed before mixing with the (β) polymer, and the hardened body is reduced to particles of a prescribed size and / or shape, It is also possible to use it in powder form.
The form of the component (α) is not particularly limited, but it is preferably a particle shape such as a filler. In this case, the particle size is preferably 100 μm or less, more preferably 50 μm or less, and even more preferably 30 μm or less by mesh pass. In addition, although it does not specifically limit about a lower limit, Preferably it is 0.001 micrometer or more, More preferably, it is 0.01 micrometer or more, More preferably, it is the range of 0.5 micrometer or more.
In addition, the (α) component is dispersed in the polymer particles of the monomer composition containing the (β) (β1) monofunctional polymerizable monomer in a particle shape such as a filler, for example. When composite filler particles are formed, the ratio of α) component particle diameter / composite particle diameter is preferably 1: 100000-1: 1.001, more preferably 1: 1000-1: The range is 1.01, more preferably in the range of 1:15 to 1: 2.5. If the value exceeds the upper limit of the numerical range, the form as a composite filler cannot be maintained, which is not preferable.
If the upper limit of the numerical range is exceeded, the (β1a), (β1b), (β2), and (β3) components are segregated without being uniformly dispersed, and in the composite filler preparation described later, the (α) component is There is a possibility that it may be powdered without being encapsulated in the polymerizable composition composed of the components (β1a), (β1b), (β2), and (β3).
上記（α）生物活性セメントは、（β１ａ）分子内に酸性基と重合性基を有する化合物、（β１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物、および（β３）重合開始剤の合計１００重量％に対して、好ましくは３３６〜１５重量％、より好ましくは２７０〜４０重量％、更に好ましくは２０３〜６５重量％の範囲で使用される。
前記数値範囲の下限を下回ると、硬組織などの生体組織に対する有益な作用が低下することとなり、一方、上限値を上回ると後述する本発明の複合充填材の作製が困難になることとなり、何れも好ましくない。
The (α) bioactive cement includes (β1a) a compound having an acidic group and a polymerizable group in the molecule, (β1b) a compound having one polymerizable group in the molecule and having no acidic group, and (β3 ) It is preferably used in the range of 336 to 15% by weight, more preferably 270 to 40% by weight, still more preferably 203 to 65% by weight, based on 100% by weight of the polymerization initiator.
If the lower limit of the numerical range is not reached, beneficial effects on living tissue such as hard tissue will be reduced, while if the upper limit is exceeded, it will be difficult to produce the composite filler of the present invention described later. Is also not preferred.
又、カルシウム原子は、（β１ａ）分子内に酸性基と重合性基を有する化合物、（β１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物、および（β３）重合開始剤の合計１００重量％に対して、好ましくは０．０１〜６０重量％、より好ましくは１〜５０重量％、更に好ましくは１０〜４０重量％の範囲で使用される。
前記数値範囲の下限を下回ると、硬組織などの生体組織に対する有益な作用が低下することとなり、一方、上限値を上回ると複合充填材の作製及びその形態維持が困難となることとなり、何れも好ましくない。
なお、前記数値範囲を満たすならば、例えば、（α）生物活性セメント粒子以外にカルシウム原子を有しない無機粒子も本発明の歯科用複合充填材に含有されていても差し支えない。
In addition, the calcium atom is (β1a) a compound having an acidic group and a polymerizable group in the molecule, (β1b) a compound having one polymerizable group in the molecule and having no acidic group, and (β3) polymerization initiation. It is preferably used in the range of 0.01 to 60% by weight, more preferably 1 to 50% by weight, and still more preferably 10 to 40% by weight with respect to 100% by weight of the agent.
If the lower limit of the numerical range is not reached, beneficial effects on living tissue such as hard tissue will be reduced, while if the upper limit is exceeded, it will be difficult to produce a composite filler and maintain its form, It is not preferable.
As long as the numerical range is satisfied, for example, (α) inorganic particles having no calcium atom other than the bioactive cement particles may be contained in the dental composite filler of the present invention.
本発明の複合充填材の調製方法
本発明の複合充填材は、前記（β１ａ）、（β１ｂ）、（β２）、（β３）、（α）成分の混合物を公知の重合法、例えば溶液重合、塊状重合、乳化重合、光重合等の重合法により重合させた後、粉砕して作製することができる。
重合法の好ましい一例を示すと、予め粉末成分である（β２）ポリ（（メタ）アクリレート）系重合体粒子からなる充填材及び（α）生物活性セメント成分とを所望の重量比で混合させ、得られたその混合粉末と（β１ａ）分子内に酸性基と重合性基を有する化合物、（β１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物及び（β２）重合開始剤で構成される液成分とを所望の重量比で混和させペースト化する。得られたそのペーストを硬化する前に金型に充填・圧接し、室温以上の環境下に放置することで硬化体が得られる。
Preparation method of composite filler of the present invention The composite filler of the present invention comprises a mixture of the above (β1a), (β1b), (β2), (β3), (α) components by a known polymerization method such as solution polymerization, It can be produced by polymerizing by a polymerization method such as bulk polymerization, emulsion polymerization, or photopolymerization and then pulverizing.
As a preferred example of the polymerization method, a filler composed of (β2) poly ((meth) acrylate) polymer particles as a powder component and (α) a bioactive cement component are mixed in a desired weight ratio in advance. The obtained mixed powder and (β1a) a compound having an acidic group and a polymerizable group in the molecule, (β1b) a compound having one polymerizable group in the molecule and having no acidic group, and (β2) initiation of polymerization The liquid component composed of the agent is mixed at a desired weight ratio to form a paste. Before the obtained paste is cured, the mold is filled and pressed, and left in an environment of room temperature or higher to obtain a cured product.
得られた硬化体の粉砕は、予め５ｍｍ程度の大きさに粗粉砕した後、ボールミル、ローラーミル、摩砕ミル及びジェットミル等の乾式粉砕機、又はコロイドミル等の湿式粉砕機を用いて行われる。湿式粉砕では溶媒を除去、乾燥する必要があるので、乾式粉砕の方が好ましい。さらに、得られた硬化体が軟質で通常の粉砕が困難な場合は、液体窒素などを用いた凍結粉砕により粉砕してもよい。
粒子形状は球状体であっても不定形体であってもよく、所望の粒子径になるまで実施される。また、粉砕後は篩いやエアジェット分級機等で所望の粒子径や粒子分布を有する粉体を得ることもできる。
The obtained cured product is pulverized in advance to a size of about 5 mm, and then using a dry pulverizer such as a ball mill, a roller mill, an attrition mill and a jet mill, or a wet pulverizer such as a colloid mill. Is called. Since wet pulverization requires removal of the solvent and drying, dry pulverization is preferred. Furthermore, when the obtained cured product is soft and difficult to pulverize normally, it may be pulverized by freeze pulverization using liquid nitrogen or the like.
The particle shape may be a spherical body or an indeterminate shape, and is carried out until a desired particle diameter is obtained. Further, after pulverization, a powder having a desired particle size and particle distribution can be obtained with a sieve, an air jet classifier or the like.
本発明における複合充填材中の（α）成分の活性を極力効率よく発現させるためには、塊状に固まらずになるべく分散されていることが好ましいから、本発明における複合充填材の粒径は、メッシュパスを準用して好ましくは１００μｍ以下、より好ましくは５０μｍ以下、さらに好ましくは３０μｍ以下の範囲である。但し、通常メッシュパスでは、その上限値粒径より大きい粒子は一切含まれないのが標準であるが、本発明の準用では、前記の各上限値以下の粒径の複合充填材を１００重量％とした際に、（α）成分として、各上限値粒径を超えて各上限値粒径の１．３倍以下の粒径の複合充填材は、２０重量％以下含まれていても良いが、各上限値粒径の１．３倍を超える粒径の複合充填材は、０．５重量％以下であるものとする。なお、下限値については特に限定するものではないが、好ましくは０．００１μｍ以上、より好ましくは０．０１μｍ以上、さらに好ましくは０．５μｍ以上の範囲である。 In order to express the activity of the component (α) in the composite filler in the present invention as efficiently as possible, it is preferable that the composite filler in the present invention is dispersed as much as possible without being consolidated into a lump. The mesh path is applied mutatis mutandis, preferably in the range of 100 μm or less, more preferably 50 μm or less, and further preferably 30 μm or less. However, in the normal mesh pass, it is standard that no particles larger than the upper limit particle diameter are included, but in the quasi-application of the present invention, 100% by weight of the composite filler having a particle diameter equal to or less than each of the upper limit values described above. In this case, as the component (α), the composite filler having a particle size that exceeds each upper limit particle size and is 1.3 times or less of each upper limit particle size may be contained in an amount of 20% by weight or less. The composite filler having a particle size exceeding 1.3 times the upper limit particle size is 0.5% by weight or less. In addition, although it does not specifically limit about a lower limit, Preferably it is 0.001 micrometer or more, More preferably, it is 0.01 micrometer or more, More preferably, it is the range of 0.5 micrometer or more.
本発明の複合充填材の作製に使用される（β１ａ）及び（β１ｂ）成分の混合物自体が熱重合するものであれば、（β２）重合開始剤を含まない前駆体をそのまま公知の方法で加熱重合して複合充填材を作製してもよい。
また、複合充填材は後述の表面処理剤や処理方法で疎水化処理して使用しても差し支えない。表面処理剤の好ましい処理量としては、複合充填材１００重量部に対して表面処理剤が、好ましくは０．１〜２０重量％、より好ましくは０．１〜１５重量％であり、更に好ましくは０．１〜１０重量％である。
本発明の充填材は、有機成分を多く含むため比重が軽く、無機成分も含むため親水性を有する。そのため、水中に投ずると１日以上の間、水中に浮遊する。これに対して、重合体のみからなるフィラーや撥水処理した無機フィラーは、撥水性のため水面に浮き、無処理の無機フィラーは、親水性と高比重のために水底に没するという違いが有るので、これらのフィラーと本発明の充填材は容易に区別することが可能である。
If the mixture of the components (β1a) and (β1b) used for the production of the composite filler of the present invention is thermally polymerized, the precursor containing no (β2) polymerization initiator is heated as it is by a known method. A composite filler may be produced by polymerization.
Further, the composite filler may be used after being hydrophobized by the surface treatment agent or treatment method described later. As a preferable treatment amount of the surface treatment agent, the surface treatment agent is preferably 0.1 to 20% by weight, more preferably 0.1 to 15% by weight, further preferably 100 parts by weight of the composite filler. 0.1 to 10% by weight.
The filler of the present invention has a low specific gravity because it contains a lot of organic components, and has hydrophilicity because it also contains inorganic components. Therefore, when it is thrown into water, it floats in water for more than a day. On the other hand, fillers consisting only of polymers and water-repellent treated inorganic fillers float on the water surface due to water repellency, while untreated inorganic fillers are submerged in the water bottom due to hydrophilicity and high specific gravity. Thus, these fillers and the filler of the present invention can be easily distinguished.
本発明の歯科用組成物
本発明の歯科用組成物は、前記の複合充填材を含有し、好ましくはそれに加えて、（γ１ａ）分子内に酸性基と重合性基を有する化合物、（γ１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物、（γ２）ポリ（（メタ）アクリレート）系重合体粒子からなる充填材、（γ３）重合開始剤及び上記の複合充填材を含むことを特徴とする。また、これらの配合量は、使用目的等に応じて適宜選択される。これらの（γ１ａ）分子内に酸性基と重合性基を有する化合物、（γ１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物、（γ２）ポリ（（メタ）アクリレート）系重合体粒子からなる充填材、（γ３）重合開始剤は、それぞれ、前記の（β１ａ）分子内に酸性基と重合性基を有する化合物、（β１ｂ）分子内に１つの重合性基を有し、酸性基を有しない化合物、（β２）ポリ（（メタ）アクリレート）系重合体粒子からなる充填材、（β３）重合開始剤と同様のものを同様の組成比率にて用いることが可能である。
なお、本発明の複合充填材を含有した歯科用組成物の重量を１００重量％とした際、当該複合充填材の含有比率は、好ましくは８０〜２０重量％、より好ましくは７０〜３０重量％、更に好ましくは６０〜４０重量％である。
本発明の歯科用組成物における前記複充填材の配合形態乃至保存形態としては、特に限定されるものではないが、（β２）ポリ（（メタ）アクリレート）系重合体粒子からなる充填材や後述する（γ５’）無機フィラー、（γ６）色素及び／又は顔料等の乾燥粉末成分に混合乃至は複合されている保存形態が好ましい。
本発明の歯科用組成物における（γ２）ポリ（（メタ）アクリレート）系重合体粒子からなる充填材は、（γ１ａ）、（γ１ｂ）、（γ３）成分と前記複合充填材の混合物で重合硬化し、所望の物性が達成される場合、本発明の歯科用組成物に含まなくてもよい。
Dental composition of the present invention The dental composition of the present invention contains the above-mentioned composite filler, preferably (γ1a) a compound having an acidic group and a polymerizable group in the molecule, (γ1b) Compound having one polymerizable group in the molecule and not having acidic group, filler comprising (γ2) poly ((meth) acrylate) polymer particles, (γ3) polymerization initiator and the above composite filler It is characterized by including. Moreover, these compounding quantities are suitably selected according to a use purpose etc. These (γ1a) compounds having an acidic group and a polymerizable group in the molecule, (γ1b) compounds having one polymerizable group in the molecule and having no acidic group, (γ2) poly ((meth) acrylate) The filler composed of polymer particles (γ3) and the polymerization initiator (β1a) each have an acidic group and a polymerizable group in the molecule (β1b) and one polymerizable group in the molecule. In addition, it is possible to use a compound having no acidic group, a filler made of (β2) poly ((meth) acrylate) polymer particles, and the same one as (β3) polymerization initiator at the same composition ratio. is there.
In addition, when the weight of the dental composition containing the composite filler of the present invention is 100% by weight, the content ratio of the composite filler is preferably 80 to 20% by weight, more preferably 70 to 30% by weight. More preferably, it is 60 to 40% by weight.
The compounding form or storage form of the double filler in the dental composition of the present invention is not particularly limited, but is a filler composed of (β2) poly ((meth) acrylate) polymer particles, which will be described later. The storage form is preferably mixed or combined with dry powder components such as (γ5 ′) inorganic filler, (γ6) dye and / or pigment.
The filler comprising the (γ2) poly ((meth) acrylate) polymer particles in the dental composition of the present invention is polymerized and cured by a mixture of the (γ1a), (γ1b), (γ3) components and the composite filler. If the desired physical properties are achieved, the dental composition of the present invention may not be included.
（γ４）安定剤
本発明は所望により（γ４）成分の安定剤を使用することができる。（γ４）成分としては、例えば２−ヒドロキシ−４−メチルベンゾフェノンのような紫外線吸収剤、ハイドロキノン、ハイドロキノンモノメチルエーテル、２，５−ジターシャリーブチル−４−メチルフェノール等の重合禁止剤、変色防止剤、抗菌材、着色顔料その他の従来公知の添加剤等の成分を、必要に応じて任意に添加できる。
（γ１’）多官能（メタ）アクリレート化合物
本発明は所望により（γ１’）成分の多官能（メタ）アクリレート化合物を使用することができる。（γ１’）成分としては、例えばグリセロールジ（メタ）アクリレート；トリメチロールプロパンなどのブタントリオールのジ（メタ）アクリレート；メソ−エリスリトールなどのブタンテトラオールのジ（メタ）アクリレート又はトリ（メタ）アクリレート；ペンタントリオールのジ（メタ）アクリレート；テトラメチロールメタンなどのペンタンテトラオールのジ（メタ）アクリレート又はトリ（メタ）アクリレート；キシリトール及びその異性体の水酸基を１〜２個有する多官能（メタ）アクリレート；ヘキサントリオールのジ（メタ）アクリレート；ヘキサンテトラオールのジ（メタ）アクリレート又はトリ（メタ）アクリレート；ヘキサンペンタオールの水酸基を１〜２個有する多官能（メタ）アクリレート；ヘキサンヘキサオールの水酸基を１〜２個有する多官能（メタ）アクリレート；あるいは下記式（１）
(Γ4) Stabilizer In the present invention, a stabilizer of the (γ4) component can be used as desired. Examples of the component (γ4) include UV absorbers such as 2-hydroxy-4-methylbenzophenone, polymerization inhibitors such as hydroquinone, hydroquinone monomethyl ether, and 2,5-ditertiary butyl-4-methylphenol, and discoloration inhibitors. Components such as antibacterial materials, color pigments and other conventionally known additives can be optionally added as necessary.
(Γ1 ′) polyfunctional (meth) acrylate compound In the present invention, a polyfunctional (meth) acrylate compound of the component (γ1 ′) can be used as desired. Examples of the (γ1 ′) component include glycerol di (meth) acrylate; di (meth) acrylate of butanetriol such as trimethylolpropane; di (meth) acrylate or tri (meth) acrylate of butanetetraol such as meso-erythritol Di (meth) acrylate of pentanetriol; di (meth) acrylate or tri (meth) acrylate of pentanetetraol such as tetramethylolmethane; polyfunctional (meth) acrylate having 1 to 2 hydroxyl groups of xylitol and its isomer Hexanetriol di (meth) acrylate; hexanetetraol di (meth) acrylate or tri (meth) acrylate; polyfunctional (meth) acrylate having 1 to 2 hydroxyl groups of hexanepentaol; hexanehexaol Polyfunctional having 1-2 hydroxyl groups (meth) acrylate; or formula (1)
［式（１）中、Ｒ１は少なくとも１個の芳香族環を有しかつ分子中に酸素原子又は硫黄原子を有していてもよい２価の芳香族残基あるいはシクロアルキル残基、好ましくは下記式（２） [In the formula (1), R 1 is a divalent aromatic residue or cycloalkyl residue which has at least one aromatic ring and may have an oxygen atom or a sulfur atom in the molecule, preferably Is the following formula (2)
から選択されるいずれかを示し、Ｒ２及びＲ３は互いに独立して水素原子又はメチル基を示し、ｎ及びｍは正の整数を示す］で示される多官能（メタ）アクリレートなどを挙げることができる。これら多官能（メタ）アクリレートは、官能基の数が２〜３個のものが好ましく用いられ、２個（２官能）のものがより好ましい。官能基数が多い場合には、添加量によって組成物の硬化体の架橋度が高くなり、組成物の硬化体の柔軟性を損なわれ、歯質や歯科用金属への接着性を低下させる傾向がある。
なお、多官能（メタ）アクリレート化合物である（γ１’）成分は通常、酸性基を有しないものとするのが好ましい。
And R 2 and R 3 each independently represent a hydrogen atom or a methyl group, and n and m each represent a positive integer.] Can do. As these polyfunctional (meth) acrylates, those having 2 to 3 functional groups are preferably used, and those having 2 (bifunctional) are more preferred. When the number of functional groups is large, the degree of cross-linking of the cured product of the composition increases depending on the amount added, the flexibility of the cured product of the composition is impaired, and the adhesiveness to the tooth or dental metal tends to be reduced. is there.
In addition, it is preferable that the (γ1 ′) component which is a polyfunctional (meth) acrylate compound usually has no acidic group.
上記（γ１’）多官能（メタ）アクリレート化合物は、（γ）（γ１）単官能重合性単量体を含有する単量体組成物の重合体１００重量％に対して、好ましくは１〜２０重量％、更に好ましくは２〜９重量％の範囲内の量で含有させることができる。前記数値範囲の上限を上回ると、歯科用組成物硬化体の架橋度が高くなり、歯科用組成物硬化体の柔軟性を損なう傾向があり、好ましくない。
（γ５’）無機フィラー
本発明は所望により（γ５’）成分の無機フィラーを使用することができる。無機フィラーの例としては、ジルコニウム酸化物、ビスマス酸化物、チタン酸化物、酸化亜鉛及び酸化アルミニウム粒子などの金属酸化物粉末、炭酸カルシウム、炭酸ビスマス、リン酸ジルコニウム及び硫酸バリウムなどの金属塩粉末、シリカガラス、アルミニウム含有ガラス、バリウム含有ガラス、ストロンチウム含有ガラス及びジルコニウムシリケートガラスなどのガラスフィラー、銀徐放性を有するフィラー、フッ素徐放性を有するフィラーなどを挙げることができる。これら無機フィラーは単独であるいは組み合わせて使用することができる。
また、無機フィラーと樹脂間に強固な結合を得るには、シラン処理、ポリマーコートなどの表面処理を施した無機フィラーを使用することが好ましい。
これらの無機フィラーは、単独であるいは組み合わせて使用することができる。
上記（γ５’）無機フィラーは、（γ）（γ１）単官能重合性単量体を含有する単量体組成物の重合体１００重量％に対して、好ましくは１５〜８５重量％、より好ましくは２０〜８０重量％、更に好ましくは２５〜７５重量％の範囲内の量で使用される。前記数値範囲の上限を上回ると、歯科用組成物硬化体の柔軟性を損なう傾向があり、好ましくない。
The (γ1 ′) polyfunctional (meth) acrylate compound is preferably 1 to 20 with respect to 100% by weight of the polymer of the monomer composition containing the (γ) (γ1) monofunctional polymerizable monomer. It can be contained in an amount in the range of 2% by weight, more preferably 2-9% by weight. If the upper limit of the numerical range is exceeded, the degree of cross-linking of the cured dental composition is increased, which tends to impair the flexibility of the cured dental composition, which is not preferable.
(Γ5 ′) Inorganic Filler In the present invention, an inorganic filler of the (γ5 ′) component can be used as desired. Examples of inorganic fillers include metal oxide powders such as zirconium oxide, bismuth oxide, titanium oxide, zinc oxide and aluminum oxide particles, metal salt powders such as calcium carbonate, bismuth carbonate, zirconium phosphate and barium sulfate, Examples thereof include glass fillers such as silica glass, aluminum-containing glass, barium-containing glass, strontium-containing glass, and zirconium silicate glass, a filler having a silver sustained release property, and a filler having a fluorine sustained release property. These inorganic fillers can be used alone or in combination.
In order to obtain a strong bond between the inorganic filler and the resin, it is preferable to use an inorganic filler that has been subjected to a surface treatment such as silane treatment or polymer coating.
These inorganic fillers can be used alone or in combination.
The (γ5 ′) inorganic filler is preferably 15 to 85% by weight, more preferably 100% by weight of the polymer of the monomer composition containing the (γ) (γ1) monofunctional polymerizable monomer. Is used in an amount in the range of 20 to 80% by weight, more preferably 25 to 75% by weight. Exceeding the upper limit of the above numerical range is not preferable because it tends to impair the flexibility of the cured dental composition.
（γ６）色素及び／又は顔料
本発明は所望により（γ６）成分色素及び／又は顔料を添加してもよい。かかる色素及び／又は顔料としては、例えばフロキシンＢＫ、アシッドレッド、ファストアッシドマゼンダ、フロキシンＢ、ファストグリーンＦＣＦ、ローダミンＢ、塩基性フクシン、酸性フクシン、エオシン、エチスロシン、サフラニン、ローズベンガル、ベーメル、ゲンチアナ紫、銅クロロフィルソーダ、ラッカイン酸、フルオレセインナトリウム、コチニール及びシソシン、タルク、チタンホワイトなどを挙げることができる。これらの色素及び／又は顔料は単独であるいは２種以上組み合わせて使用することができる。
本発明の歯科用組成物のエッチングなしでの人歯象牙質微小引張接着強さは、好ましくは１〜３０ＭＰａ、より好ましくは５〜２５ＭＰａ、更に好ましくは２．５〜２０ＭＰａである。
(Γ6) Dye and / or Pigment In the present invention, a (γ6) component dye and / or pigment may be added as desired. Examples of such dyes and / or pigments include phloxine BK, acid red, fast acid magenta, phloxine B, fast green FCF, rhodamine B, basic fuchsin, acidic fuchsin, eosin, ethysulosin, safranin, rose bengal, bemel, gentian Examples include purple, copper chlorophyll soda, laccaic acid, sodium fluorescein, cochineal and perilla, talc, titanium white and the like. These dyes and / or pigments can be used alone or in combination of two or more.
The human dental dentin microtensile bond strength without etching of the dental composition of the present invention is preferably 1 to 30 MPa, more preferably 5 to 25 MPa, and still more preferably 2.5 to 20 MPa.
以下、本発明を実施例により具体的に説明するが、本発明はこれらの実施例に限定されるものではない。本実施例は歯科における露髄部に適用する直接覆髄材としての使用を想定している。そのため、直接覆髄材として一般的に使用されている水酸化カルシウム製剤（ダイカル デンツプライ三金株式会社）を比較するために使用した。
（ポルトランドセメント含有粉材の調製）
ポルトランドセメント（ホワイトセメント 太平洋セメント株式会社、以下ＰＬＣ）を水（ＰＬＣ／蒸留水＝７４．１ｇ／２５．９ｇ）で混練し、８０×８０×１ｍｍのテフロン（登録商標）製の型枠に流し込み、室温で一晩放置し硬化させた。
EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples. The present embodiment assumes use as a direct pulp capping material applied to the exposed pulp portion in dentistry. Therefore, it was used to compare calcium hydroxide preparations (Daikar Dentsu Ply Sankin Co., Ltd.), which is commonly used as a direct pulp capping material.
(Preparation of powder containing Portland cement)
Portland cement (White Cement Taiheiyo Cement Co., Ltd., hereinafter referred to as PLC) is kneaded with water (PLC / distilled water = 74.1 g / 25.9 g) and poured into a 80 × 80 × 1 mm Teflon (registered trademark) formwork And allowed to cure overnight at room temperature.
硬化後のＰＬＣを遊星回転ボールミル（実験用遊星回転ポットミル ＬＰ−１株式会社伊藤製作所）により粉砕し、篩（１００メッシュ）を通過させた粉材（以下、Ｒ−ＰＬＣ）とスーパーボンドポリマー粉末クリア（サンメディカル株式会社、以下ＳＢＣ）を重量比（Ｒ−ＰＬＣ：ＳＢＣ＝９：１）で混合し、ターブラーミキサー（ＴＵＲＢＵＬＡ Ｔ２Ｆ Ｗｉｌｌｙ Ａ Ｂａｃｈｏｆｅｎ ＡＧ）で撹拌させ粉材を均一化させた（以下Ｒ−ＰＬＣ／ＳＢＣ）。
このＲ−ＰＬＣ／ＳＢＣ粉材とスーパーボンドクイックモノマー液（サンメディカル株式会社）、スーパーボンドキャタリスト（サンメディカル株式会社）を重量比（Ｒ−ＰＬＣ／ＳＢＣ：スーパーボンドクイックモノマー液：スーパーボンドキャタリスト＝０．１９５１ｇ：０．１０ｇ：０．００５４ｇ）で混和泥を作製し、２０×２０×１ｍｍのテフロン製の型枠に充填し、２３℃で３日間放置した。
３日後、硬化した試料を１ｍｍ四方のペレット状に砕き、遊星回転ボールミル（実験用遊星回転ポットミル ＬＰ−１ 株式会社伊藤製作所）にて粉砕し、篩（２８０メッシュ）を通過させることで、ポルトランド含有粉材（以下ＲＣＰ）を得た。
The cured PLC was pulverized with a planetary rotating ball mill (experimental planetary rotating pot mill LP-1 Ito Seisakusho) and passed through a sieve (100 mesh) (hereinafter referred to as R-PLC) and superbond polymer powder clear. (Sun Medical Co., Ltd., hereinafter referred to as SBC) was mixed at a weight ratio (R-PLC: SBC = 9: 1), and stirred with a tumbler mixer (TURBULA T2F Willy A Bachofen AG) to homogenize the powder material (hereinafter referred to as “SBC”). R-PLC / SBC).
This R-PLC / SBC powder, Superbond Quick Monomer Liquid (Sun Medical Co., Ltd.) and Super Bond Catalyst (Sun Medical Co., Ltd.) are in a weight ratio (R-PLC / SBC: Super Bond Quick Monomer Liquid: Super Bond Catalyst). (List = 0.1951 g: 0.10 g: 0.0054 g), a mixed mud was prepared, filled in a 20 × 20 × 1 mm Teflon mold, and allowed to stand at 23 ° C. for 3 days.
Three days later, the cured sample was crushed into 1 mm square pellets, ground with a planetary rotating ball mill (experimental planetary rotating pot mill LP-1 Ito Seisakusho Co., Ltd.), and passed through a sieve (280 mesh). A contained powder material (hereinafter RCP) was obtained.
（人歯象牙質微小引張接着強さ測定）
人歯健全大臼歯を咬合面から注水下で＃６００の耐水研磨紙で研磨し、健全な象牙質を露出させた。
露出象牙質面に対し、下記実施例１又は比較例１に従って、上記ＲＣＰを適用し、適用直後にボンドフィルＳＢ（サンメディカル株式会社）を製造者指示通りに適用し、適用直後に厚さ５ｍｍのアクリル板で圧接した。
その状態で、１５分間室温で放置した後、圧を取り除き３７℃、１晩、水中浸漬した。
水中浸漬後、硬組織精密低速切断機（Ｉｓｏｍｅｔ ｌｏｗ ｓｐｅｅｄ ｓａｗ，Ｂｕｅｈｌｅｒ Ｌｔｄ）を用いて接着界面に垂直に厚さ１ｍｍの連続切片に切り出し、更に切片を接着面積が１×１ｍｍの短冊状になるように切り分け、小型卓上試験機（ＥＺ Ｔｅｓｔ 島津製作所）にて、クロスヘッドスピード１ｍｍ／ｍｉｎで微小引張接着強さ測定を行った。
(Measurement of human dental dentin micro-tension adhesive strength)
A healthy human molar was polished with # 600 water-resistant abrasive paper under water injection from the occlusal surface to expose a healthy dentin.
In accordance with Example 1 or Comparative Example 1 described below, the RCP is applied to the exposed dentin surface, and bond fill SB (Sun Medical Co., Ltd.) is applied as directed by the manufacturer immediately after application, and the thickness is 5 mm immediately after application. Pressure-welded with an acrylic plate.
In that state, the mixture was left at room temperature for 15 minutes, and then the pressure was removed, and it was immersed in water at 37 ° C. overnight.
After immersion in water, cut into 1 mm thick continuous sections perpendicular to the bonding interface using a hard tissue precision low speed cutting machine (Isomet low speed saw, Buehler Ltd), and further cut the sections into strips with a bonding area of 1 × 1 mm In this way, the micro-tension adhesive strength was measured at a crosshead speed of 1 mm / min with a small desktop testing machine (EZ Test Shimadzu Corporation).
実施例１
上記の微小引張接着強さ測定に従って、上記ポルトランド含有粉材ＲＣＰを、スーパーボンドモノマー液（サンメディカル株式会社）：スーパーボンドキャタリスト＝０．１０ｇ：０．００５４ｇの活性化液で露出象牙質面に筆積法（製造業者推奨方法）により適用した。
Example 1
In accordance with the above measurement of the micro-tension adhesive strength, the Portland-containing powder material RCP is exposed to the dentin exposed with the activation liquid of Superbond monomer liquid (Sun Medical Co., Ltd.): Superbond catalyst = 0.10 g: 0.0054 g. The surface was applied by the writing method (manufacturer recommended method).
比較例１
実施例１において、ＲＣＰをダイカル（水酸化カルシウム製剤）を替えた以外は、実施例１と同様に行った。
Comparative Example 1
In Example 1, RCP was performed in the same manner as in Example 1 except that dical (calcium hydroxide preparation) was changed.
結果を表１に示す。 The results are shown in Table 1.
表１の結果から、一般的に直接覆髄材として使用されている水酸化カルシウム製剤（ダイカル）は歯質と接着せず、それに伴うシール性は期待できないことが示唆された。また、ＲＣＰは歯質と接着し、それに伴うシール性が期待できると考えられることから、従来の覆髄材と比較して接着性およびそれに伴うシール性が向上したことで、細菌や唾液などの侵入を抑制することが可能となり、より効率的に生物活性セメント成分の使用が可能となった。 From the results in Table 1, it was suggested that the calcium hydroxide preparation (Dical), which is generally used directly as a pulp-capping material, does not adhere to the tooth and cannot be expected to have a sealing property. In addition, since RCP is considered to adhere to the tooth substance and can be expected to have a sealing property associated therewith, the adhesive property and the sealing property associated therewith have been improved as compared with conventional pulp-capping materials, such as bacteria and saliva. It has become possible to suppress intrusion and more efficiently use bioactive cement components.
Claims (7)
（β）（β１）単官能重合性単量体を含有する単量体組成物からなる混合物の重合硬化体の粉砕物
よりなる歯科用複合充填材。 (Α) fine particles of bioactive cement;
(Β) (β1) A dental composite filler comprising a pulverized product of a polymerized cured product of a mixture comprising a monomer composition containing a monofunctional polymerizable monomer.
（β１ａ）分子内に少なくとも１つの酸性基を有する単量体
が含まれている請求項１記載の歯科用複合充填材。 (Β) In the monomer composition,
The dental composite filler according to claim 1, wherein (β1a) a monomer having at least one acidic group in the molecule is contained.
（β１ｂ）分子内に酸性基を有しない単量体
が含まれている請求項１記載の歯科用複合充填材。 (Β) In the monomer composition,
The dental composite filler according to claim 1, wherein (β1b) a monomer having no acidic group is contained in the molecule.
（β２）ポリ（メタ）アクリレート系重合体粒子
が含まれている請求項１記載の歯科用複合充填材。 (Β) In the monomer composition,
The dental composite filler according to claim 1, wherein (β2) poly (meth) acrylate polymer particles are contained.
（β）（β１）単官能重合性単量体を含有する単量体組成物の混合物を重合硬化せしめ、得られた重合硬化体を粉砕することを特徴とする歯科用複合充填材の製造法。 It is characterized by polymerizing and curing a mixture of (α) bioactive cement fine particles and (β) (β1) a monomer composition containing a monofunctional polymerizable monomer , and pulverizing the resulting polymerized cured product. A method of manufacturing a dental composite filler .