JP6085010B2 - Boom welding method - Google Patents

Boom welding method Download PDF

Info

Publication number
JP6085010B2
JP6085010B2 JP2015144528A JP2015144528A JP6085010B2 JP 6085010 B2 JP6085010 B2 JP 6085010B2 JP 2015144528 A JP2015144528 A JP 2015144528A JP 2015144528 A JP2015144528 A JP 2015144528A JP 6085010 B2 JP6085010 B2 JP 6085010B2
Authority
JP
Japan
Prior art keywords
welding
boom
steel plate
metal
welding method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2015144528A
Other languages
Japanese (ja)
Other versions
JP2015212205A (en
Inventor
耕治 山本
耕治 山本
山本 幸生
幸生 山本
拓樹 松尾
拓樹 松尾
雅志 藤澤
雅志 藤澤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tadano Ltd
Original Assignee
Tadano Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tadano Ltd filed Critical Tadano Ltd
Priority to JP2015144528A priority Critical patent/JP6085010B2/en
Publication of JP2015212205A publication Critical patent/JP2015212205A/en
Application granted granted Critical
Publication of JP6085010B2 publication Critical patent/JP6085010B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、ブームの溶接方法に関する。さらに詳しくは、クレーン車や高所作業車、橋梁点検車の構成部品であるブームの溶接による製作技術に関する。 The present invention relates to a method of welding boom. More particularly, cranes and aerial work platforms, related to production technology due to the welding of the boom which is a component of the bridge inspection vehicle.

クレーン車や高所作業車、橋梁点検車の構成部品であるブームは、揚程を高くするため多段のブームに構成され、内蔵している油圧シリンダ等により伸縮可能に構成されるのが一般的である。各段のブームは、長尺鋼板で中空断面に形成された筒形の鋼板構造物であり、その長手方向の長さは数mから10m位のものがある。そして、基端側のブームに中段のブームや先端のブームが順に入れ子状態に挿入されている。   Booms, which are components of crane trucks, aerial work platforms, and bridge inspection vehicles, are generally constructed in a multi-stage boom to increase the lift, and can be extended and retracted by built-in hydraulic cylinders. is there. Each stage boom is a cylindrical steel plate structure formed of a long steel plate and having a hollow cross section, and has a length in the longitudinal direction of several m to 10 m. Then, the middle boom and the distal boom are sequentially inserted into the proximal boom in a nested state.

上記のような鋼板製のブームは、従来より長尺鋼板を溶接により接合して構成されている。
そして、座屈強度を高めたり、使用材料に高張力鋼板の使用が可能となったことから、断面四角形の従来構造から、断面五角形などの多角形構造を経て、近年では上部が角型で下部が円弧状に湾曲した湾曲構造のブームが採用されるに至っている。
しかしながら、いずれの形状のブームであっても、長尺鋼板を溶接により接合する構造であることに変わりはない。
Conventionally, a steel plate boom as described above is formed by joining long steel plates by welding.
And since it has become possible to increase the buckling strength and to use high-strength steel sheets as the material, it has gone from a conventional structure with a square cross section to a polygonal structure such as a pentagonal cross section. A boom having a curved structure in which the arc is curved in an arc shape has been adopted.
However, even if it is a boom of any shape, it does not change that it is the structure which joins a long steel plate by welding.

ところで、特許文献1の従来技術は、ブームを構成する2枚の鋼板、すなわち断面コ形の右側部材と左側部材を上下の接合部で溶接するものであるが、溶接するために鋼板の突合せ継手の裏側に裏当て金を当てて溶接している。この裏当て金を当てるのは溶接接合の信頼性を高めるためと説明されている。   By the way, although the prior art of patent document 1 welds the two steel plates which comprise a boom, ie, the right-side member and left-side member of a cross-sectional U shape, in the up-and-down joining part, in order to weld, the butt joint of a steel plate Welded with a backing metal on the back side. It is explained that this backing metal is applied to improve the reliability of the welded joint.

従来このような裏当て金が必要であった理由を図5に基づき説明する。
図5の(A)は、断面U字形の上鋼板1と断面U字形の下鋼板2を、端縁で溶接して筒形に構成するブームを示している。
上下の鋼板1,2は、平板状の鋼板をプレスで曲げ加工して断面U字形に成形したものであるが、曲げ加工時に生じるスプリングバックや加工歪による変形が端縁形状にも表われる。このため、端縁は一直線にはならず、ブームの幅方向でも微妙なズレが生じ、ブームの上下方向での端縁位置も変位があり、これらのズレや変位がブームの長手方向に連続して発生する。したがって、上鋼板1の端縁と下鋼板2の端縁を図示のように突合せても、その突合せ面には隙間gの寸法が大小に変動しながら続いていく。
The reason why such a backing metal has conventionally been necessary will be described with reference to FIG.
FIG. 5A shows a boom in which a U-shaped upper steel plate 1 and a lower U-shaped lower steel plate 2 are welded at the end edges to form a cylinder.
The upper and lower steel plates 1 and 2 are formed by bending a flat steel plate with a press into a U-shaped cross section. However, deformation due to springback or processing strain that occurs during bending also appears in the edge shape. For this reason, the edges are not straight, and a slight deviation occurs in the width direction of the boom, and the position of the edge in the vertical direction of the boom is also displaced, and these deviations and displacements continue in the longitudinal direction of the boom. Occur. Therefore, even if the end edge of the upper steel plate 1 and the end edge of the lower steel plate 2 are abutted as shown in the drawing, the size of the gap g continues on the abutting surface while fluctuating in size.

このような性状のあることから、図5の(B)に示すように、上鋼板1の端面には開先gvをレ型やV形にとり、溶接には溶着金属wの量を大きくできるアーク溶接が用いられている。アーク溶接は溶接棒あるいは溶接ワイヤ等の溶加材を用いることから溶着金属の増量が可能なので、母材の溶融金属量に溶加材の溶融金属量を加えて突合せ部分に溶着金属を肉盛りできるから、隙間gが多少大きくても溶接が可能だからである。   Because of such properties, as shown in FIG. 5 (B), an arc that can take a groove gv on the end face of the upper steel plate 1 in the shape of a rectangle or V, and can increase the amount of the deposited metal w for welding. Welding is used. Since arc welding uses a filler metal such as a welding rod or welding wire, the amount of weld metal can be increased, so the amount of molten metal in the base metal is added to the amount of molten metal in the base metal, and the weld metal is built up at the butt portion. This is because welding is possible even if the gap g is somewhat large.

とはいっても、上下鋼板の突合せ部分の隙間gが大きすぎたり、溶込み量を多くしようとすると母材が裏面まで溶ける吹き抜けが発生することを意味し、溶接強度は弱くなってしまう。一方、吹き抜けを防止しようとして溶け込みが不足すると、溶融接合部分が少ないことを意味するので、やはり溶接強度は弱くなってしまう。
このような不都合を防止するため、溶接部分の裏側には裏当て金101を当てて、充分な溶け込みを確保しつつ溶接部の吹き抜けを防止していたのである。
However, if the gap g between the butt portions of the upper and lower steel plates is too large, or if the amount of penetration is increased, it means that the base material melts to the back surface, and the welding strength is weakened. On the other hand, if the penetration is insufficient in order to prevent blow-through, it means that there are few fusion-bonded parts, so that the welding strength is also weakened.
In order to prevent such inconvenience, a backing metal 101 is applied to the back side of the welded portion to prevent blowout of the welded portion while ensuring sufficient penetration.

しかるに、アーク溶接によりブームを製作する従来技術では、つぎのような問題があった。
(1)アーク溶接は入熱が大きいため、ブームに溶接歪が発生し、ブームに捩れや歪変形が発生する。このため、溶接作業の前にブーム材を拘束する作業が必要となったり、それでも歪は発生するので、溶接後に歪取りを行う矯正作業が必要となる。このような理由で製造工数が多くなるという欠点がある。
However, the conventional technique for manufacturing a boom by arc welding has the following problems.
(1) Since arc welding has a large heat input, welding distortion occurs in the boom, and twist and distortion deformation occur in the boom. For this reason, an operation of restraining the boom material before the welding operation is necessary, or distortion still occurs, and a correction operation for removing the distortion after welding is necessary. For this reason, there is a drawback that the number of manufacturing steps increases.

(2)既述のごとくブーム側壁の内面には裏当て金があり、かつ製作後のブームの上下面や両側面には矯正しきれなかった歪が残っているので、入れ子式の多段ブームに構成する場合は、各段ブーム間の寸法差を大きくとる必要がある。すなわち、図6に示すように、基端ブームB1と中間ブームB2の間の寸法差D1も、中間ブームB2と先端ブームB3の間の寸法差D2も大きくなる。
この場合、先端側のブームほど断面寸法が小さくなる傾向が強いので充分な強度を確保しにくくなる。逆に先端側のブームに充分な強度を与えようとすると、基端側のブームの断面寸法が大きくなるので、鋼材量を多く使いブーム重量も増え、クレーンの吊上げ性能が低下する。
(2) As mentioned above, there is a backing metal on the inner surface of the boom side wall, and distortion that cannot be corrected remains on the upper and lower surfaces and both sides of the boom after production. When configured, it is necessary to take a large dimensional difference between the booms. That is, as shown in FIG. 6, the dimensional difference D1 between the proximal boom B1 and the intermediate boom B2 and the dimensional difference D2 between the intermediate boom B2 and the distal boom B3 are also increased.
In this case, the boom on the tip side tends to have a smaller cross-sectional dimension, so that it is difficult to ensure sufficient strength. On the other hand, if sufficient strength is given to the boom on the distal end side, the cross-sectional dimension of the boom on the proximal end side increases, so that a large amount of steel is used and the boom weight increases, and the lifting performance of the crane decreases.

特開2003-312996号公報JP2003-312996

本発明は上記事情に鑑み、ブームの軽量化や剛性向上が図れ、溶接前の拘束作業や溶接後の矯正作業等の作業工程が少なくてすむブーム溶接方法を提供することを目的とする。 In view of the above circumstances, weight reduction and improved rigidity of the boom is drawing, and an object thereof is to provide a boom welding method requires less working steps of straightening work or the like after the restraining work and welding of the previous welding.

発明のブームの溶接方法は、断面U字状に曲げ加工した長尺の高張力鋼板である上鋼板と、当該上鋼板よりも大きな曲げ半径で断面U字状に曲げ加工し前記上鋼板よりも板厚が厚い長尺の高張力鋼板である下鋼板を、それぞれ端面で溶接して断面筒型のブームを製作する溶接方法であって、前記上鋼板と前記下鋼板の端縁同士の突合せ接合部分が、裏当て金を用いることなく、アーク溶接が先行しレーザー溶接が後行するハイブリッド溶接で溶接され、先行する前記アーク溶接では、前記上鋼板と前記下鋼板の突合せ表面部を溶融して、母材の溶融金属に溶加材の溶融金属を加え、後行する前記レーザー溶接で前記溶融金属と突合せ接合部分の両方の母材を接合部の深さ方向に溶け込ませることを特徴とする。 The boom welding method according to the first aspect of the present invention includes an upper steel plate that is a long high-strength steel plate bent into a U-shaped section, and the upper steel plate that is bent into a U-shaped section with a larger bending radius than the upper steel plate. It is a welding method of manufacturing a cross-section cylindrical boom by welding the lower steel plate, which is a long high-tensile steel plate having a thicker thickness than the end surface, between the edges of the upper steel plate and the lower steel plate. The butt joint is welded by hybrid welding in which arc welding precedes and laser welding follows without using a backing metal. In the preceding arc welding, the butt surface portions of the upper steel plate and the lower steel plate are melted. to, thereby dissolve the molten metals of the filler added to the molten metals of the base material, both the base material of the joint portion butt and said molten metal in said laser welding of succeeding in the depth direction of the joint It is characterized by.

第1発明によれば、つぎの効果を奏する。
a)溶加材を使用する溶接方法により上下鋼板の突合せ接合部を溶融して、母材の溶融金属量に溶加材の溶融金属量を加えると、たとえ隙間が大きい接合部であっても両方の母材間を溶着金属でつなぐことができる。次いでレーザ溶接Rで加熱すれば、溶融金属と両方の母材を接合部の深さ方向に溶け込ませることができる。このため、隙間が大きくなっている突合せ接合部であっても確実に溶接により接合することができる。
b)溶加材を用いる溶接では表面部を溶融させることでよいので使用熱量は少なくてすみ、レーザ溶接は元々入熱が少ない溶接法なので、溶接後のブームに捩れや歪が生じにくい。したがって、溶接前のブームの拘束作業や溶接後の矯正作業を削減することができる。
c)レーザ溶接はビームの指向制御が容易なので、溶接部の吹き抜けが生じにくく、熱影響範囲を極めて小さくして溶接ができる。このため、裏当て金を用いる必要もない。この裏当て金を用いないことと、上下鋼板に発生する捩れや歪みが少ないことから、多段入れ子式のブームの寸法差を小さくできるので、先端側のブームの断面寸法を大きくし剛性を向上させることができる。
According to the first shot bright, the effects of the following.
a) When the butt joints of the upper and lower steel plates are melted by a welding method using a filler material and the molten metal amount of the filler material is added to the molten metal amount of the base material, even if the joint portion has a large gap Both base materials can be connected by weld metal. Next, when heated by laser welding R, the molten metal and both base materials can be melted in the depth direction of the joint. For this reason, even if it is a butt | jointing junction part with which the clearance gap is large, it can join reliably by welding.
b) In welding using a filler material, the surface portion may be melted, so that the amount of heat used is small, and laser welding is originally a welding method with little heat input, so that the boom after welding is less likely to be twisted or distorted. Accordingly, it is possible to reduce the boom restraining work before welding and the straightening work after welding.
c) Since laser beam directing control of the beam is easy, it is difficult for the weld to blow through, and welding can be performed with a very small heat-affected range. For this reason, it is not necessary to use a backing metal. Since this backing metal is not used and the torsion and distortion generated in the upper and lower steel plates are small, the dimensional difference of the multistage telescopic boom can be reduced, so that the cross-sectional dimension of the boom on the tip side is increased and the rigidity is improved. be able to.

(A)は本発明が適用されるブームの部分斜視図、(B)は本発明の溶接法の説明図である。(A) is the fragmentary perspective view of the boom to which this invention is applied, (B) is explanatory drawing of the welding method of this invention. 本発明で用いられるハイブリッド溶接法における二形態の説明図である。It is explanatory drawing of two forms in the hybrid welding method used by this invention. 本発明のハイブリッド溶接法による溶接断面の説明図である。It is explanatory drawing of the welding cross section by the hybrid welding method of this invention. 本発明に係る多段式ブームの一例の断面図である。It is sectional drawing of an example of the multistage boom which concerns on this invention. 従来の溶接法の説明図であって、(A)はブームの斜視図、(B)はアーク溶接による溶接断面の説明図である。It is explanatory drawing of the conventional welding method, Comprising: (A) is a perspective view of a boom, (B) is explanatory drawing of the welding cross section by arc welding. 従来の溶接法で作成された多段式ブームの一例の断面図である。It is sectional drawing of an example of the multistage boom produced with the conventional welding method.

つぎに、本発明の実施形態を図面に基づき説明する。
本発明の溶接法で製作されるブームは、クレーンや高所作業車、橋梁点検車などに用いられる長尺の鋼板製筒状構造物であり、作業時には大きな曲げ負荷が作用する部材である。
このブームの材料は、一般的には高張力鋼板が主に使用される板材であって、厚さが4〜12mm程度の中厚鋼板が用いられる。自動車用薄板鋼板は厚さが0.6〜6mm位であり、種々の用途に用いられる厚板鋼板は厚さが6〜150mm位であるが、それらの中間位の厚さの鋼板が用いられる点が特徴である。
Next, an embodiment of the present invention will be described with reference to the drawings.
The boom manufactured by the welding method of the present invention is a long steel tubular structure used for a crane, an aerial work vehicle, a bridge inspection vehicle, and the like, and is a member to which a large bending load acts during work.
The material of the boom is generally a plate material mainly using a high-tensile steel plate, and a medium-thickness steel plate having a thickness of about 4 to 12 mm is used. The sheet steel plate for automobiles has a thickness of about 0.6 to 6 mm, and the plate steel plate used for various applications has a thickness of about 6 to 150 mm. It is a feature.

本発明は種々の断面形状のブームに適用できるが、以下では図1に示す湾曲断面のブームに係る実施形態について説明する。
図1の(A)に示すブームは断面U字状に曲げ加工した長尺鋼板である上鋼板1と下鋼板2を、それぞれの端縁で突合せている。裏当て金は全く用いていない。その理由は後述する。
上鋼板1と下鋼板2は曲げ加工されて断面U字状に形成されているが、このように曲げ加工された鋼板はスプリングバックが生じたり、曲げ加工時に生じた歪によって、突合せ端縁は綺麗に揃っていない。このため、端縁同士が接触している部分もあるが隙間gが生じている部分もある。隙間gの大きさは各位で変動するが、大きな部分は4〜5mm位に達する。
Although the present invention can be applied to booms having various cross-sectional shapes, an embodiment relating to a boom having a curved cross section shown in FIG. 1 will be described below.
The boom shown in FIG. 1 (A) has an upper steel plate 1 and a lower steel plate 2, which are long steel plates bent into a U-shaped cross section, butted at their respective edges. No backing gold is used. The reason will be described later.
The upper steel plate 1 and the lower steel plate 2 are bent and formed into a U-shaped cross section. However, the butt edge is caused by a springback or a strain generated during the bending process. It is not neatly arranged. For this reason, there are portions where the edges are in contact with each other, but there are also portions where the gap g is generated. The size of the gap g varies from place to place, but the large portion reaches about 4 to 5 mm.

上記のような突合せ部分を溶接するのに、本発明では図1(B)に示すように、溶加材を用いる溶接法Aとレーザ溶接Rからなるハイブリッド溶接Hを用いる。溶接機の配置順序は、溶接方向において溶加材を用いる溶接機Aが先行し、レーザ溶接機Rが後行する位置関係となるが、その理由は後述する。   In order to weld the butt portion as described above, in the present invention, as shown in FIG. 1B, a hybrid welding H composed of a welding method A using a filler metal and a laser welding R is used. The arrangement order of the welding machines is a positional relationship in which the welding machine A using the filler material precedes and the laser welding machine R follows in the welding direction, and the reason will be described later.

図2に示すように、溶加材を用いる溶接法Aとしては、アーク溶接a1のほかホットワイヤ供給溶接a2などがある。アーク溶接機a1は、ノズル11の中に、電極ワイヤ12を送給ローラ13で送り込み、ノズル11からはシールドガスを噴出させる公知の溶接機である。アーク溶接a1には、消耗電極式ガスシールドアーク溶接法、ノンガスシールドアーク溶接法、ディグ溶接法などがある。
ホットワイヤ供給溶接機a2は、ノズル11の中に電極ワイヤ12を送給ローラ13で送り込む点は、アーク溶接機a1と同様であるが、アークを出さない点で異なっている。これも公知の溶接機である。
As shown in FIG. 2, as the welding method A using a filler metal, there are hot wire supply welding a2 in addition to arc welding a1. The arc welding machine a1 is a known welding machine that feeds an electrode wire 12 into a nozzle 11 with a feeding roller 13 and ejects a shielding gas from the nozzle 11. The arc welding a1 includes a consumable electrode type gas shielded arc welding method, a non-gas shielded arc welding method, a dig welding method, and the like.
The hot wire supply welder a2 is similar to the arc welder a1 in that the electrode wire 12 is fed into the nozzle 11 by the feed roller 13, but is different in that no arc is emitted. This is also a known welding machine.

アーク溶接機a1やホットワイヤ供給溶接機a2は、溶加材としての電極ワイヤ12を用いるものであり、溶接中に電極ワイヤ12の溶融金属を母材由来の溶融金属に加え、溶着金属を肉盛りできる点に特徴がある。また溶加材の溶融量を母材の溶融とは独立に制御できる特徴がある。本発明では、この肉盛りできる溶融金属を隙間gの埋め込み等に使う点が特徴である。   The arc welding machine a1 and the hot wire supply welding machine a2 use an electrode wire 12 as a filler material, and during welding, the molten metal of the electrode wire 12 is added to the molten metal derived from the base material, and the deposited metal is added to the metal. The feature is that it can be served. In addition, the melting amount of the filler material can be controlled independently of the melting of the base material. The present invention is characterized in that the molten metal that can be built up is used for filling the gap g.

レーザ溶接機Rは、レーザ光の収束ビームを熱源とし、高エネルギー密度を有している。溶融特性は非常に狭くて深い溶融部が得られ、かつビームの指向制御が容易という特徴がある。また、アーク溶接のような大きな電流を流さないので、母材への入熱が少なくてすむという利点がある。   The laser welding machine R uses a convergent beam of laser light as a heat source and has a high energy density. The melting characteristics are very narrow and a deep melting part can be obtained, and the beam directing control is easy. In addition, since a large current is not passed as in arc welding, there is an advantage that heat input to the base material can be reduced.

本発明の溶接方法は、上記2種類の溶接方法を組み合わせたハイブリッド方式にあり、
図1(B)や図2に示すように、溶加材を用いるアーク溶接a1やホットワイヤ供給溶接a2を先行させて溶接を行い、その直後の溶融金属が固化する前にレーザー溶接Rを行うものである。
The welding method of the present invention is a hybrid method combining the above two types of welding methods,
As shown in FIG. 1 (B) and FIG. 2, arc welding a1 using a filler metal and hot wire supply welding a2 are performed in advance, and laser welding R is performed before the molten metal immediately after that is solidified. Is.

上記ハイブリット溶接Hの利点は、つぎのとおりである。
(1)溶加材を使用するアーク溶接a1やホットワイヤ供給溶接a2で鋼板の突合せ接合部を溶融して、母材の溶融金属量に溶加材の溶融金属量を加えると、たとえ隙間が大きい接合部であっても両方の母材間を溶着金属でつなぐことができる。次いでレーザ溶接Rで加熱すれば、溶融金属と両方の母材を接合部の深さ方向に溶け込ませることができる。このため、隙間が大きくなっている突合せ接合部であっても確実に溶接により接合することができる。図3に基づき溶接断面を説明すると、m1はアーク溶接a1による肉盛り部分であり、m2はレーザ溶接Rによる深い溶け込み部分である。このように、表面部に肉盛りした溶融金属m1をレーザ光によって狭い範囲で縦深方向に押し込むことが可能なので、表面部をアーク溶接で、深さ方向の溶け込みをレーザー溶接Rで分担させることで、確実な溶接が行えるのである。
The advantages of the hybrid welding H are as follows.
(1) When the butt joint of a steel plate is melted by arc welding a1 or hot wire supply welding a2 using a filler metal, and the molten metal amount of the filler material is added to the molten metal amount of the base material, even if a gap is formed Even in a large joint, both base materials can be connected by a weld metal. Next, when heated by laser welding R, the molten metal and both base materials can be melted in the depth direction of the joint. For this reason, even if it is a butt | jointing junction part with which the clearance gap is large, it can join reliably by welding. Referring to FIG. 3, the welding cross section will be described. M1 is a build-up portion by arc welding a1, and m2 is a deep penetration portion by laser welding R. Thus, since the molten metal m1 piled up on the surface portion can be pushed in the vertical depth direction with a laser beam in a narrow range, the surface portion is shared by arc welding and the penetration in the depth direction is shared by laser welding R. Thus, reliable welding can be performed.

(2)上記のように、アーク溶接a1は表面部を溶融させることでよいので使用熱量は少なくてすみ、レーザ溶接Rは元々入熱が少ない溶接法なので、溶接後のブームに捩れや歪が生じにくい。したがって、溶接前のブームの拘束作業や溶接後の矯正作業を削減することができる。
(3)レーザ溶接Rはビームの指向制御が容易なので、溶接部の吹き抜けが生じにくく、熱影響範囲を極めて小さくして溶接ができる。このため、裏当て金を用いる必要もない。この裏当て金を用いないことと、上下鋼板1,2に発生する捩れや歪みが少ないことから、多段入れ子式のブームの寸法差を小さくできるので、先端側のブームの断面寸法を大きくし剛性を向上させることができる。
(2) As described above, the arc welding a1 only needs to melt the surface portion, so the amount of heat used is small, and the laser welding R is originally a welding method with little heat input, so that the boom after welding is twisted or distorted. Hard to occur. Accordingly, it is possible to reduce the boom restraining work before welding and the straightening work after welding.
(3) Since laser beam welding R is easy to control the beam direction, it is difficult for the weld to blow through, and welding can be performed with an extremely small heat-affected range. For this reason, it is not necessary to use a backing metal. Since this backing metal is not used and the twist and distortion generated in the upper and lower steel plates 1 and 2 are small, the dimensional difference of the multistage telescopic boom can be reduced. Can be improved.

本発明の溶接法で製造されたブームの一例を図4に示す。
図4から明らかなように、基端ブームB1と中間ブームB2との間の寸法差D1も、中間ブームB2と先端ブームB3の間の寸法差D2も小さくなる。この場合、図6の従来構造と比べてみると、基端ブームB1の寸法が同じとすれば、中間ブームB2や先端ブームB3の寸法を大きくできることを意味する。したがって、ブームの剛性を向上させることができる。
換言すれば、先端ブームB3に所望の強度を発揮する寸法を与えた場合、中間ブームB2や基端ブームB1を必要以上に大きくしなくてよいので、ブームの軽量化を図ることができる。
An example of a boom manufactured by the welding method of the present invention is shown in FIG.
As apparent from FIG. 4, the dimensional difference D1 between the proximal boom B1 and the intermediate boom B2 and the dimensional difference D2 between the intermediate boom B2 and the distal boom B3 are reduced. In this case, when compared with the conventional structure of FIG. 6, if the dimensions of the proximal boom B1 are the same, it means that the dimensions of the intermediate boom B2 and the distal boom B3 can be increased. Therefore, the rigidity of the boom can be improved.
In other words, when the end boom B3 is given a dimension that exhibits a desired strength, the intermediate boom B2 and the base end boom B1 do not have to be enlarged more than necessary, so that the weight of the boom can be reduced.

1 上鋼板
2 鋼板
A 溶接機
a1 アーク溶接
a2 ホットワイヤ溶接
H ハイブリッド溶接
R レーザ溶接
1 Upper steel plate 2 Steel plate A Welding machine a1 Arc welding a2 Hot wire welding H Hybrid welding R Laser welding

Claims (1)

断面U字状に曲げ加工した長尺の高張力鋼板である上鋼板と、当該上鋼板よりも大きな曲げ半径で断面U字状に曲げ加工し前記上鋼板よりも板厚が厚い長尺の高張力鋼板である下鋼板を、それぞれ端面で溶接して断面筒型のブームを製作する溶接方法であって、
前記上鋼板と前記下鋼板の端縁同士の突合せ接合部分が、裏当て金を用いることなく、アーク溶接が先行しレーザー溶接が後行するハイブリッド溶接で溶接され、
先行する前記アーク溶接では、前記上鋼板と前記下鋼板の突合せ表面部を溶融して、母材の溶融金属に溶加材の溶融金属を加え、
後行する前記レーザー溶接で前記溶融金属と突合せ接合部分の両方の母材を接合部の深さ方向に溶け込ませる
ことを特徴とするブームの溶接方法。
An upper steel plate, which is a long high-tensile steel sheet bent into a U-shaped section, and a long, high-thickness steel plate that is bent into a U-shaped section with a larger bending radius than the upper steel sheet and is thicker than the upper steel sheet A welding method in which a lower steel plate, which is a tensile steel plate, is welded at each end face to produce a cross-section cylindrical boom,
The butt joint between the edges of the upper steel plate and the lower steel plate is welded by hybrid welding in which arc welding precedes and laser welding follows without using a backing metal,
In the arc welding the preceding, by melting the butt surface portion of the lower steel plate and the upper steel plate, the melting metals of filler added to the molten metals of the base material,
A boom welding method, wherein the base metal of both the molten metal and the butt joint is melted in the depth direction of the joint by the subsequent laser welding.
JP2015144528A 2015-07-22 2015-07-22 Boom welding method Active JP6085010B2 (en)