JP5757884B2 - Method for producing electrode catalyst for fuel cell and use thereof - Google Patents
Method for producing electrode catalyst for fuel cell and use thereof Download PDFInfo
- Publication number
- JP5757884B2 JP5757884B2 JP2011553852A JP2011553852A JP5757884B2 JP 5757884 B2 JP5757884 B2 JP 5757884B2 JP 2011553852 A JP2011553852 A JP 2011553852A JP 2011553852 A JP2011553852 A JP 2011553852A JP 5757884 B2 JP5757884 B2 JP 5757884B2
- Authority
- JP
- Japan
- Prior art keywords
- fuel cell
- catalyst
- nitrogen
- acid
- electrode catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は燃料電池用電極触媒の製造方法、燃料電池用電極触媒およびその用途に関する。 The present invention relates to a method for producing a fuel cell electrode catalyst, a fuel cell electrode catalyst, and uses thereof.
固体高分子型燃料電池は、固体高分子電解質をアノードとカソードとで挟み、アノードに燃料を供給し、カソードに酸素または空気を供給して、カソードで酸素が還元されて電気を取り出す形式を有する燃料電池である。燃料には水素またはメタノールなどが主として用いられる。 A polymer electrolyte fuel cell has a form in which a solid polymer electrolyte is sandwiched between an anode and a cathode, fuel is supplied to the anode, oxygen or air is supplied to the cathode, and oxygen is reduced at the cathode to extract electricity. It is a fuel cell. Hydrogen or methanol is mainly used as the fuel.
従来、燃料電池の反応速度を高め、燃料電池のエネルギー変換効率を高めるために、燃料電池のカソード(空気極)表面やアノード(燃料極)表面には、触媒を含む層(以下「燃料電池用触媒層」とも記す。)が設けられていた。 Conventionally, in order to increase the reaction speed of the fuel cell and increase the energy conversion efficiency of the fuel cell, a layer containing a catalyst (hereinafter referred to as “for fuel cell”) is provided on the cathode (air electrode) surface or anode (fuel electrode) surface of the fuel cell. Also referred to as “catalyst layer”).
この触媒として、一般的に貴金属が用いられており、貴金属の中でも高い電位で安定であり、活性が高い白金、パラジウムなどの貴金属が主として用いられてきた。しかし、これらの貴金属は価格が高く、また資源量が限られていることから、代替可能な触媒の開発が求められていた。 As this catalyst, a noble metal is generally used, and noble metals such as platinum and palladium which are stable at a high potential and have high activity among the noble metals have been mainly used. However, since these noble metals are expensive and have limited resources, development of alternative catalysts has been required.
また、カソード表面に用いる貴金属は酸性雰囲気下では溶解する場合があり、長期間に渡る耐久性が必要な用途には適さないという問題があった。このため酸性雰囲気下で腐食せず、耐久性に優れ、高い酸素還元能を有する触媒の開発が強く求められていた。 In addition, the noble metal used on the cathode surface may be dissolved in an acidic atmosphere, and there is a problem that it is not suitable for applications that require long-term durability. Therefore, there has been a strong demand for the development of a catalyst that does not corrode in an acidic atmosphere, has excellent durability, and has a high oxygen reducing ability.
貴金属代替触媒として、貴金属を一切使わない卑金属炭化物、卑金属酸化物、卑金属炭窒酸化物、カルコゲン化合物及び炭素触媒などが報告されている(例えば、特許文献1〜特許文献4を参照)。これらの材料は白金などの貴金属材料に比べて、安価であり、資源量が豊富である。
Base metal carbides, base metal oxides, base metal carbonitrides, chalcogen compounds, carbon catalysts and the like that do not use any precious metal have been reported as noble metal substitute catalysts (see, for example,
しかしながら、特許文献1及び特許文献2においては、卑金属材料を含むこれらの触媒は実用的に充分な酸素還元能が得られていないという問題点がある。
However, in
また、特許文献3及び特許文献4においては、高い酸素還元触媒活性を示すが、燃料電池運転条件下での触媒の安定性が非常に低いことが問題点である。 Patent Documents 3 and 4 show high oxygen reduction catalytic activity, but the problem is that the stability of the catalyst under fuel cell operating conditions is very low.
このような貴金属代替触媒として、特許文献5及び特許文献6でのNb及びTi炭窒酸化物は上記性能を有効に発現できることから、特に注目されている。 As such a precious metal substitute catalyst, Nb and Ti oxycarbonitrides in Patent Document 5 and Patent Document 6 are attracting particular attention because they can effectively exhibit the above performance.
特許文献5及び特許文献6に開示された触媒は従来の貴金属代替触媒に比べてきわめて高性能であるが、その製造工程の一部において1600℃〜1800℃という高温下での加熱処理が必要であった。(例えば特許文献5 実施例1または特許文献6 実施例1)
このような高温加熱処理は工業的には不可能ではないが困難をともない、設備費の高騰や運転管理の困難を招き、ひいては製造コストが高くなることからより安価に製造出来る方法の開発が望まれていた。The catalysts disclosed in Patent Document 5 and Patent Document 6 have extremely high performance compared to conventional noble metal substitute catalysts, but heat treatment at a high temperature of 1600 ° C. to 1800 ° C. is necessary in a part of the production process. there were. (For example, Patent Document 5 Example 1 or Patent Document 6 Example 1)
Although such high-temperature heat treatment is not impossible industrially, it is difficult, and it leads to a rise in equipment costs and operation management difficulties. It was rare.
本発明に比較的近い先行技術として特許文献7を挙げることができる。特許文献7には炭素、窒素及び酸素を含有するカーボン含有チタンオキシナイトライドの製造に関する技術が報告されている。 Patent Document 7 can be cited as a prior art relatively close to the present invention. Patent Document 7 reports a technique relating to the production of a carbon-containing titanium oxynitride containing carbon, nitrogen and oxygen.
しかしながら、特許文献7に記載されている製造方法では、カーボン含有チタンオキシナイトライドを製造するために、窒素含有有機化合物とチタン前駆体との反応によるチタンオキシナイトライドの製造とフェノール樹脂とチタンオキシナイトライド前駆体との反応によるカーボン含有チタンオキシナイトライド製造の二段階合成が必要であり工程が複雑である。特に、チタンオキシナイトライド前駆体の製造は80℃で、攪拌、過熱、還流、冷却及び減圧濃縮などの複雑な工程が必要であるため、製造コストが高い。 However, in the production method described in Patent Document 7, in order to produce a carbon-containing titanium oxynitride, production of titanium oxynitride by reaction of a nitrogen-containing organic compound and a titanium precursor, and phenol resin and titanium oxynitride. A two-step synthesis of the production of carbon-containing titanium oxynitride by reaction with a nitride precursor is required and the process is complicated. In particular, the production of the titanium oxynitride precursor is at 80 ° C. and requires complicated steps such as stirring, heating, refluxing, cooling, and vacuum concentration, and thus the production cost is high.
また、フェノール樹脂は3次元網目構造を持つ熱硬化性樹脂であるため、金属酸化物と均一に混合して、反応させることが難しい。特に、フェノール樹脂の熱分解温度は400℃〜900℃であるため、1000℃以下の温度で、フェノール樹脂の完全分解による炭化反応が起こりにくい問題点もある。 Further, since the phenol resin is a thermosetting resin having a three-dimensional network structure, it is difficult to uniformly mix and react with the metal oxide. In particular, since the thermal decomposition temperature of the phenol resin is 400 ° C. to 900 ° C., there is a problem that a carbonization reaction due to complete decomposition of the phenol resin hardly occurs at a temperature of 1000 ° C. or less.
さらに、特許文献7には、その用途として太陽光集熱器用の薄膜が記されているだけで、電極触媒として有用性の高い粒状または繊維状などの形状を持つ金属炭窒酸化物の製造方法及びその用途は開示も検討もなされていない。 Furthermore, Patent Document 7 describes a method for producing a metal oxycarbonitride having a granular or fibrous shape that is highly useful as an electrode catalyst only by describing a thin film for a solar collector as its application. And its use has not been disclosed or studied.
本発明はこのような従来技術における問題点の解決を課題とする。
すなわち本発明の目的は、高温での熱処理(焼成)工程を設けることなく、遷移金属(チタン等)を用いた高い触媒活性を有する燃料電池用電極触媒を製造する方法を提供することである。An object of the present invention is to solve such problems in the prior art.
That is, an object of the present invention is to provide a method for producing an electrode catalyst for a fuel cell having a high catalytic activity using a transition metal (titanium or the like) without providing a heat treatment (firing) step at a high temperature.
また、本発明の他の目的は、低コストで、高い触媒活性を有する燃料電池用電極触媒を製造することができる燃料電池用電極触媒の製造方法を提供することである。 Another object of the present invention is to provide a method for producing a fuel cell electrode catalyst capable of producing a fuel cell electrode catalyst having high catalytic activity at low cost.
本発明は、たとえば以下の(1)〜(17)に関する。
(1) 分子中に窒素を含まない有機化合物と分子中に酸素を含む遷移金属含有化合物との混合物を500〜1100℃、窒素ガス含有ガス雰囲気下で熱処理することを特徴とする燃料電池用電極触媒の製造方法。
(2) 分子中に窒素を含まない有機化合物が、アルコール類、ヒドロキシ類、ペルオキシ類、ケトン類、アルデヒド類、エーテル類、カルボキシル類、エステル類、カルボニル類、チオール類、スルホ類、糖類及び窒素を含まない5員及び6員複素環化合物、並びに前記複素環化合物が2つ以上組み合わさってできた環状構造を持つ化合物及び錯体からなる群から選ばれる一種以上であることを特徴とする(1)に記載の燃料電池用電極触媒の製造方法。
(3) 分子中に窒素を含まない有機化合物が、(2)に記載の化合物の重合反応により得られた高分子化合物からなる群から選ばれる一種以上であることを特徴とする(1)に記載の燃料電池用電極触媒の製造方法。
(4) 分子中に窒素を含まない有機化合物が、ポリビニルアルコール、ポリアクリル酸、ポリエチレンオキシド、エチレングリコール、ポリエチレングリコール、クエン酸、リンゴ酸、コハク酸、フマル酸、酒石酸、シュウ酸、グルコース、マンノース、セルロース、フルクトース、ガラクトース、マルトース、スクロース、ラクトース、酪酸、吉草酸、カプロン酸、カプリル酸、ラウリン酸からなる群から選ばれる一種以上であることを特徴とする(1)に記載の燃料電池用電極触媒の製造方法。
(5) 分子中に酸素を含む遷移金属含有化合物が、チタン、バナジウム、クロム、マンガン、鉄、コバルト、ニッケル、銅、亜鉛、ジルコニウム、ニオブ、モリブデン、タンタル及びタングステンからなる群から選ばれる一種以上の金属(以下「金属M」または単に「M」ともいう。2種以上金属を含む場合は「金属M1」または単に「M1」とMの後に数字を記す。)を含む金属酸化物もしくは金属水酸化物または前記金属酸化物及び金属水酸化物の混合物からなることを特徴とする(1)〜(4)のいずれかに記載の燃料電池用電極触媒の製造方法。
(6) 分子中に窒素を含まない有機化合物(2種以上の場合は全ての有機化合物の総和モル数である。高分子化合物の場合はモノマーを基準とする。)と分子中に酸素を含む遷移金属含有化合物(2種以上の場合は全ての金属の総和モル数である。)との混合物における前記有機化合物と前記遷移金属含有化合物の混合割合が、前記有機化合物および前記遷移金属含有化合物のモル数をそれぞれx、yとした場合、0.01≦x/y≦100の範囲であることを特徴とする(1)〜(5)のいずれかに記載の燃料電池用電極触媒の製造方法。
(7) 窒素ガス含有ガス中の窒素ガスの含有量が10〜100体積%であることを特徴とする(1)〜(6)のいずれかに記載の燃料電池用電極触媒の製造方法。
(8) 窒素ガス含有ガスが、さらに、全ガスに対して0.01〜5体積%の水素ガスを含むことを特徴とする(1)〜(7)のいずれかに記載の燃料電池用電極触媒の製造方法。
(9) 窒素ガス含有ガスが、さらに、全ガスに対して0.01〜10体積%の酸素ガスを含むことを特徴とする(1)〜(8)のいずれかに記載の燃料電池用電極触媒の製造方法。
(10) (1)〜(9)のいずれかに記載の燃料電池用電極触媒の製造方法により製造された燃料電池用電極触媒であって、該燃料電池用電極触媒を構成する遷移金属元素、炭素、窒素および酸素の原子数の比(遷移金属元素:炭素:窒素:酸素)を1:x:y:zとした場合に、0<x≦3、0<y≦2、0<z≦3であることを特徴とする燃料電池用電極触媒。
(11) (1)〜(9)のいずれかに記載の燃料電池用電極触媒の製造方法により製造された燃料電池用電極触媒であって、該燃料電池用電極触媒を構成する遷移金属元素M1、遷移金属元素M2(ただし、M1は、チタン、バナジウム、クロム、マンガン、鉄、コバルト、ニッケル、銅、亜鉛、ジルコニウム、ニオブ、モリブデン、タンタル及びタングステンからなる群より選択される1種の金属であり、M2は、前記群より選択されるM1とは異なる少なくとも1種の金属である。)、炭素、窒素および酸素の原子数の比(遷移金属元素M1:遷移金属元素M2:炭素:窒素:酸素)を(1−a):a:x:y:zとした場合に、0<a≦0.5、0<x≦3、0<y≦2、0<z≦3であることを特徴とする燃料電池用電極触媒。
(12) BET法で算出される比表面積が30〜400m2/gであることを特徴とする前記(10)または(11)に記載の燃料電池用電極触媒。
(13) (10)〜(12)のいずれかに記載の燃料電池用電極触媒を含むことを特徴とする燃料電池用触媒層。
(14) さらに電子伝導性物質を含むことを特徴とする(13)に記載の燃料電池用触媒層。
(15) 燃料電池用触媒層と多孔質支持層とを有する電極であって、前記燃料電池用触媒層が(14)に記載の燃料電池用触媒層であることを特徴とする電極。
(16) カソードとアノードと前記カソード及び前記アノードの間に配置された電解質膜とを有する膜電極接合体であって、前記カソード及び/または前記アノードが(15)に記載の電極であることを特徴とする膜電極接合体。
(17) (16)に記載の膜電極接合体を備えることを特徴とする燃料電池。The present invention relates to the following (1) to (17), for example.
(1) A fuel cell electrode characterized by heat-treating a mixture of an organic compound containing no nitrogen in the molecule and a transition metal-containing compound containing oxygen in the molecule at 500 to 1100 ° C. in a nitrogen gas-containing gas atmosphere. A method for producing a catalyst.
(2) Organic compounds containing no nitrogen in the molecule are alcohols, hydroxys, peroxys, ketones, aldehydes, ethers, carboxyls, esters, carbonyls, thiols, sulfos, saccharides and nitrogen 5 or 6-membered heterocyclic compounds not containing any of the above, and one or more selected from the group consisting of compounds and complexes having a cyclic structure formed by combining two or more of the heterocyclic compounds (1 ) For producing a fuel cell electrode catalyst.
(3) The organic compound not containing nitrogen in the molecule is at least one selected from the group consisting of polymer compounds obtained by the polymerization reaction of the compound described in (2). The manufacturing method of the electrode catalyst for fuel cells of description.
(4) Organic compounds that do not contain nitrogen in the molecule are polyvinyl alcohol, polyacrylic acid, polyethylene oxide, ethylene glycol, polyethylene glycol, citric acid, malic acid, succinic acid, fumaric acid, tartaric acid, oxalic acid, glucose, mannose The fuel cell according to (1), which is one or more selected from the group consisting of cellulose, fructose, galactose, maltose, sucrose, lactose, butyric acid, valeric acid, caproic acid, caprylic acid, and lauric acid A method for producing an electrode catalyst.
(5) The transition metal-containing compound containing oxygen in the molecule is one or more selected from the group consisting of titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, zirconium, niobium, molybdenum, tantalum and tungsten A metal oxide or metal water containing a metal (hereinafter also referred to as “metal M” or simply “M”. When two or more metals are included, “metal M1” or simply “M1” followed by a number after M.) The method for producing a fuel cell electrode catalyst according to any one of (1) to (4), comprising an oxide or a mixture of the metal oxide and the metal hydroxide.
(6) Organic compound that does not contain nitrogen in the molecule (in the case of 2 or more, it is the total number of moles of all organic compounds. In the case of polymer compounds, it is based on the monomer) and the molecule contains oxygen. The mixing ratio of the organic compound and the transition metal-containing compound in the mixture with the transition metal-containing compound (in the case of two or more types, the total number of moles of all metals) is the ratio of the organic compound and the transition metal-containing compound. The method for producing an electrode catalyst for a fuel cell according to any one of (1) to (5), wherein the number of moles is x and y, respectively, 0.01 ≦ x / y ≦ 100 .
(7) The method for producing an electrode catalyst for a fuel cell according to any one of (1) to (6), wherein the nitrogen gas content in the nitrogen gas-containing gas is 10 to 100% by volume.
(8) The fuel cell electrode according to any one of (1) to (7), wherein the nitrogen gas-containing gas further contains 0.01 to 5% by volume of hydrogen gas with respect to the total gas. A method for producing a catalyst.
(9) The fuel cell electrode according to any one of (1) to (8), wherein the nitrogen gas-containing gas further contains 0.01 to 10% by volume of oxygen gas with respect to the total gas. A method for producing a catalyst.
(10) A fuel cell electrode catalyst produced by the method for producing a fuel cell electrode catalyst according to any one of (1) to (9), comprising a transition metal element constituting the fuel cell electrode catalyst, When the ratio of the number of atoms of carbon, nitrogen and oxygen (transition metal element: carbon: nitrogen: oxygen) is 1: x: y: z, 0 <x ≦ 3, 0 <y ≦ 2, 0 <z ≦ 3. An electrode catalyst for fuel cells, which is 3.
(11) A fuel cell electrode catalyst produced by the method for producing a fuel cell electrode catalyst according to any one of (1) to (9), wherein the transition metal element M1 constitutes the fuel cell electrode catalyst. Transition metal element M2 (where M1 is one metal selected from the group consisting of titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, zirconium, niobium, molybdenum, tantalum and tungsten) And M2 is at least one metal different from M1 selected from the above group), the ratio of the number of atoms of carbon, nitrogen and oxygen (transition metal element M1: transition metal element M2: carbon: nitrogen: Oxygen) is (1-a): a: x: y: z, 0 <a ≦ 0.5, 0 <x ≦ 3, 0 <y ≦ 2, and 0 <z ≦ 3. A fuel cell electrode catalyst.
(12) The fuel cell electrode catalyst as described in (10) or (11) above, wherein the specific surface area calculated by the BET method is 30 to 400 m 2 / g.
(13) A fuel cell catalyst layer comprising the fuel cell electrode catalyst according to any one of (10) to (12).
(14) The fuel cell catalyst layer according to (13), further comprising an electron conductive substance.
(15) An electrode having a fuel cell catalyst layer and a porous support layer, wherein the fuel cell catalyst layer is the fuel cell catalyst layer according to (14).
(16) A membrane / electrode assembly including a cathode, an anode, and an electrolyte membrane disposed between the cathode and the anode, wherein the cathode and / or the anode is the electrode according to (15). A membrane electrode assembly.
(17) A fuel cell comprising the membrane electrode assembly according to (16).
本発明の燃料電池用電極触媒の製造方法によれば、燃料電池用電極触媒を従来の方法よりも低温で製造することができるので、製造コストを削減することができ、製造工程の安定性を向上させることができる。 According to the method for producing an electrode catalyst for a fuel cell of the present invention, the electrode catalyst for a fuel cell can be produced at a lower temperature than the conventional method, so that production costs can be reduced and the stability of the production process can be reduced. Can be improved.
<燃料電池用電極触媒の製造方法>
本発明の燃料電池用電極触媒の製造方法は、分子中に窒素を含まない有機化合物と分子中に酸素を含む遷移金属含有化合物との混合物を500〜1100℃、窒素ガス含有ガス雰囲気下で熱処理することを特徴とする。<Method for producing electrode catalyst for fuel cell>
The method for producing an electrode catalyst for a fuel cell according to the present invention comprises heat-treating a mixture of an organic compound containing no nitrogen in a molecule and a transition metal-containing compound containing oxygen in the molecule at 500 to 1100 ° C. in a nitrogen gas-containing gas atmosphere. It is characterized by doing.
前記分子中に酸素を含む遷移金属含有化合物は、遷移金属元素として、たとえば、チタン、バナジウム、クロム、マンガン、鉄、コバルト、ニッケル、銅、亜鉛、ジルコニウム、ニオブ、モリブデン、タンタル及びタングステンからなる群から選ばれる一種以上の金属(以下「金属M」または単に「M」ともいう。2種以上金属を含む場合は「金属M1」または単に「M1」とMの後に数字を記す。)を含有する。 The transition metal-containing compound containing oxygen in the molecule includes, for example, a group consisting of titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, zirconium, niobium, molybdenum, tantalum and tungsten as a transition metal element. 1 or more metals selected from the following (hereinafter also referred to as “metal M” or simply “M”. When two or more metals are included, “metal M1” or simply “M1” and a number after M are written). .
これらの中でも、コストおよび得られる触媒の性能の観点から、チタン、ジルコニウム、ニオブおよびタンタルが好ましく、チタンおよびジルコニウムがさらに好ましい。 Among these, titanium, zirconium, niobium, and tantalum are preferable, and titanium and zirconium are more preferable from the viewpoint of cost and performance of the obtained catalyst.
分子中に酸素を含む遷移金属含有化合物としては、前記遷移金属の酸化物または水酸化物を挙げることができ、また酸化物および水酸化物の混合物であってもよい。 Examples of the transition metal-containing compound containing oxygen in the molecule include the oxides or hydroxides of the transition metals, and may be a mixture of oxides and hydroxides.
上記金属の酸化物、水酸化物またはそれらの混合物を合成する手法は特に限定されないが、例えば、上記遷移金属のアルコキシドまたは金属塩を沈殿法または加水分解法を用いることにより合成することができる。また、遷移金属の錯体を形成し、有機化合物を混合した後に、合成してもよい。後者の手法では、得られる酸化物、水酸化物またはそれらの混合物の凝集を抑制することができ、高純度、高均質性を持つ有機化合物との混合物を得ることが可能である。遷移金属の錯体を形成するために用いるものとしては、分子中に窒素を含まなければ特に限定されないが、例えば、アセチルアセトン、エチレングリコールなどが挙げられる。 Although the method of synthesizing the metal oxide, hydroxide or mixture thereof is not particularly limited, for example, the transition metal alkoxide or metal salt can be synthesized by using a precipitation method or a hydrolysis method. Alternatively, a transition metal complex may be formed and mixed with an organic compound, and then synthesized. In the latter method, aggregation of the obtained oxide, hydroxide or mixture thereof can be suppressed, and a mixture with an organic compound having high purity and high homogeneity can be obtained. Although what is used in order to form the complex of a transition metal will not be specifically limited if nitrogen is not included in a molecule | numerator, For example, acetylacetone, ethylene glycol, etc. are mentioned.
前記遷移金属のアルコキシドとしては特に限定されないが、好ましくは前記遷移金属のメトキシド、エトキシド、プロポキシド、イソプロポキシド、ブトキシドおよびイソブトキシドであり、より好ましくはエトキシド、イソプロポキシドおよびブトキシドである。前記遷移金属アルコキシドは、1種のアルコキシ基を有していてもよく、2種以上のアルコキシ基を有していてもよい。 The transition metal alkoxide is not particularly limited, but preferably methoxide, ethoxide, propoxide, isopropoxide, butoxide and isobutoxide of the transition metal, and more preferably ethoxide, isopropoxide and butoxide. The transition metal alkoxide may have one type of alkoxy group or may have two or more types of alkoxy groups.
上記遷移金属の金属塩としては特に限定されないが、上記遷移金属の塩化物、硝酸塩、酢酸塩、炭酸塩、硫化物、シアン化物、ホウ酸塩、リン酸塩、オキソ金属酸塩、臭化物、炭化物、窒化物、またはこれらの混合物が挙げられる。より好ましくは塩化物、硝酸塩および酢酸塩である。 The transition metal metal salt is not particularly limited, but the transition metal chloride, nitrate, acetate, carbonate, sulfide, cyanide, borate, phosphate, oxometalate, bromide, carbide , Nitrides, or mixtures thereof. More preferred are chlorides, nitrates and acetates.
分子中に窒素を含まない有機化合物としては、500℃〜1100℃での熱処理により熱分解しうるものならば特に制限されない。 The organic compound not containing nitrogen in the molecule is not particularly limited as long as it can be thermally decomposed by heat treatment at 500 ° C. to 1100 ° C.
その中でも、ポリビニルアルコール、ポリアクリル酸、ポリエチレンオキシド、エチレングリコール、ポリエチレングリコール、クエン酸、リンゴ酸、コハク酸、フマル酸、酒石酸、シュウ酸、グルコース、マンノース、セルロース、フルクトース、ガラクトース、マルトース、スクロース、ラクトース、酪酸、吉草酸、カプロン酸、カプリル酸、ラウリン酸からなる群から選ばれる一種以上であることが好ましい。また、上記化合物の重合反応により得られた高分子化合物からなる群から選ばれる一種以上であることも好ましい。 Among them, polyvinyl alcohol, polyacrylic acid, polyethylene oxide, ethylene glycol, polyethylene glycol, citric acid, malic acid, succinic acid, fumaric acid, tartaric acid, oxalic acid, glucose, mannose, cellulose, fructose, galactose, maltose, sucrose, It is preferably at least one selected from the group consisting of lactose, butyric acid, valeric acid, caproic acid, caprylic acid and lauric acid. Moreover, it is also preferable that it is 1 or more types chosen from the group which consists of a high molecular compound obtained by the polymerization reaction of the said compound.
さらに上記の中でも、ポリビニルアルコール、ポリアクリル酸、ポリエチレンオキシドなどの水溶性高分子、グルコース、セルロース、フルクトースなどの糖質、クエン酸、リンゴ酸、コハク酸、フマル酸、酒石酸などの有機酸が好ましい。これらの化合物は、2種以上を混合して用いることもできる。 Among the above, water-soluble polymers such as polyvinyl alcohol, polyacrylic acid and polyethylene oxide, carbohydrates such as glucose, cellulose and fructose, and organic acids such as citric acid, malic acid, succinic acid, fumaric acid and tartaric acid are preferable. . These compounds can also be used as a mixture of two or more.
本発明において、分子中に窒素を含まない有機化合物を使用するのは、燃料電池用電極触媒の窒素源を、熱処理雰囲気を形成する窒素ガス含有ガスのみとするためである。従来は窒素雰囲気下で金属または金属化合物を窒素と反応させるには、窒素分子の解離温度である1200℃より高い温度での熱処理が必要であったが、分子中に窒素を含まない有機化合物を使用し、窒素ガス含有ガス中で熱処理することにより、より低温の熱処理温度で金属または金属化合物と窒素とを反応させることが可能となる。 In the present invention, the organic compound containing no nitrogen in the molecule is used because the nitrogen source of the fuel cell electrode catalyst is only the nitrogen gas-containing gas forming the heat treatment atmosphere. Conventionally, in order to react a metal or metal compound with nitrogen in a nitrogen atmosphere, a heat treatment at a temperature higher than 1200 ° C., which is the dissociation temperature of the nitrogen molecule, has been required. When used and heat-treated in a nitrogen gas-containing gas, the metal or metal compound and nitrogen can be reacted at a lower heat treatment temperature.
分子中に窒素を含まない有機化合物と分子中に酸素を含む遷移金属含有化合物とを混合する方法は、それぞれが均一に混合できる方法であれば特に限定されないが、例えば、それぞれを溶媒中に溶解または分散溶媒中に分散させた後に、それぞれを混合し、溶媒または分散溶媒を除去することにより行われる。また、いずれか一方の溶液または分散溶媒に他方を混合した後、溶媒または分散溶媒を除去してもよい。 The method of mixing the organic compound not containing nitrogen in the molecule and the transition metal-containing compound containing oxygen in the molecule is not particularly limited as long as each can be uniformly mixed, but for example, each is dissolved in a solvent. Or after making it disperse | distribute in a dispersion | distribution solvent, each is mixed and it removes a solvent or a dispersion | distribution solvent. Alternatively, the solvent or the dispersion solvent may be removed after mixing one of the solutions or the dispersion solvent with the other.
分子中に窒素を含まない有機化合物(2種以上の場合は全ての有機化合物の総和モル数である。高分子化合物の場合はモノマーを基準とする。)および分子中に酸素を含む遷移金属含有化合物(2種以上の場合は全ての遷移金属の総和モル数である。)のそれぞれのモル数をx、yとし、それらの比をx/yとすると、それぞれの混合割合としては、好ましくは0.01≦x/y≦100であり、より好ましくは0.1≦x/y≦10である。混合割合が前記範囲内であると、熱処理により遷移金属含有化合物に窒素が入りやすい傾向がある。 Organic compounds that do not contain nitrogen in the molecule (in the case of 2 or more, the total number of moles of all organic compounds. In the case of polymer compounds, the monomer is used as a reference) and transition metals containing oxygen in the molecule When the number of moles of a compound (in the case of two or more kinds, the total number of moles of all transition metals) is x and y and the ratio thereof is x / y, the mixing ratio is preferably It is 0.01 <= x / y <= 100, More preferably, it is 0.1 <= x / y <= 10. When the mixing ratio is within the above range, nitrogen tends to easily enter the transition metal-containing compound by heat treatment.
前記混合物の熱処理温度は好ましくは500〜1100℃の範囲であり、より好ましくは800〜1050℃の範囲であり、さらに好ましくは900〜1000℃の範囲である。熱処理温度が前記範囲内であると、得られる燃料電池用電極触媒の結晶性および均一性が良好な点で好ましい。また、製造コストの低減および製造工程の安全性の向上を図ることができる。前記熱処理温度が500℃未満であると、分子中に窒素を含まない有機化合物と分子中に酸素を含む遷移金属含有化合物との混合物である前駆体と焼成ガス中の窒素ガスとの反応性が悪くなり、生成物に窒素が取り込まれにくくなる。1100℃より高いと、粒子径が大きくなり、比表面積が小さくなる傾向がある。さらに、製造コストの低減および製造工程の安定性の向上を図れなくなる。 The heat treatment temperature of the mixture is preferably in the range of 500 to 1100 ° C, more preferably in the range of 800 to 1050 ° C, and still more preferably in the range of 900 to 1000 ° C. When the heat treatment temperature is within the above range, it is preferable in terms of good crystallinity and uniformity of the obtained fuel cell electrode catalyst. Further, the manufacturing cost can be reduced and the safety of the manufacturing process can be improved. When the heat treatment temperature is less than 500 ° C., the reactivity of the precursor, which is a mixture of an organic compound containing no nitrogen in the molecule and a transition metal-containing compound containing oxygen in the molecule, with the nitrogen gas in the firing gas is high. It becomes worse and nitrogen is less likely to be taken into the product. When the temperature is higher than 1100 ° C., the particle diameter tends to increase and the specific surface area tends to decrease. Furthermore, it is impossible to reduce the manufacturing cost and improve the stability of the manufacturing process.
本発明の燃料電池用電極触媒の製造方法においては、上記のように、従来の方法よりも低温での熱処理によって燃料電池用電極触媒を得ることができる。このため、本発明の燃料電池用電極触媒の製造方法においては、安全に、かつ低コストで燃料電池用電極触媒を得ることが可能になる。本発明において、このように低温での熱処理によっても結晶性及び均一性が良好で、活性が高い燃料電池用電極触媒を得ることができるのは、1100℃以下の温度範囲において、有機化合物の熱分解による活性化された炭素および焼成ガス中の窒素が金属酸化物または水酸化物と反応しやすくなり、金属酸化物または水酸化物の一部の酸素と置換することで、好ましい遷移金属元素、炭素、窒素および酸素の組成比を持つ燃料電池用電極触媒を得ることができるためだと考えられる。 In the method for producing a fuel cell electrode catalyst of the present invention, as described above, the fuel cell electrode catalyst can be obtained by heat treatment at a lower temperature than the conventional method. For this reason, in the manufacturing method of the electrode catalyst for fuel cells of this invention, it becomes possible to obtain the electrode catalyst for fuel cells safely and at low cost. In the present invention, an electrode catalyst for a fuel cell having good crystallinity and uniformity and high activity even by heat treatment at such a low temperature can be obtained in the temperature range of 1100 ° C. or less. Activated carbon by decomposition and nitrogen in the calcination gas are more likely to react with the metal oxide or hydroxide, and by replacing the oxygen in the metal oxide or hydroxide, a preferred transition metal element, This is probably because a fuel cell electrode catalyst having a composition ratio of carbon, nitrogen and oxygen can be obtained.
前記混合物の熱処理は、窒素ガス含有ガス雰囲気下で行われる。窒素ガス含有ガス雰囲気下で熱処理することにより原料である遷移金属含有化合物の有機化合物の熱分解に伴う炭化反応が進行すると同時に窒素ガスによる窒化反応が進行する。窒素ガス含有ガスとしては、熱処理により燃料電池用電極触媒が効率的に製造される限り特に制限はなく、窒素ガスの他、窒素ガスと水素ガスとの混合ガスおよび窒素ガスとアルゴンとの混合ガス等が挙げられ、酸素ガスを含んでいてもよい。 The heat treatment of the mixture is performed in a nitrogen gas-containing gas atmosphere. By performing heat treatment in a nitrogen gas-containing gas atmosphere, a carbonization reaction accompanying thermal decomposition of the organic compound of the transition metal-containing compound as a raw material proceeds, and simultaneously, a nitriding reaction with nitrogen gas proceeds. The nitrogen gas-containing gas is not particularly limited as long as the fuel cell electrode catalyst is efficiently produced by heat treatment. In addition to nitrogen gas, a mixed gas of nitrogen gas and hydrogen gas and a mixed gas of nitrogen gas and argon Etc., and oxygen gas may be included.
窒素ガス含有ガス中の窒素ガスの含有量は、好ましくは10〜100体積%であり、より好ましくは50〜100体積%である。 Content of nitrogen gas in nitrogen gas containing gas becomes like this. Preferably it is 10-100 volume%, More preferably, it is 50-100 volume%.
窒素ガス含有ガスが水素ガスを含有する場合、水素ガスの含有量は、0.01〜5体積%であることが好ましい。 When nitrogen gas containing gas contains hydrogen gas, it is preferable that content of hydrogen gas is 0.01-5 volume%.
また窒素ガス含有ガスは、0.01〜10体積%の酸素ガスを含んでいてもよい。 The nitrogen gas-containing gas may contain 0.01 to 10% by volume of oxygen gas.
熱処理雰囲気の圧力は特に限定されず、製造の安定性とコストなどを考慮して、大気圧下で熱処理を行うことができる。 The pressure of the heat treatment atmosphere is not particularly limited, and heat treatment can be performed under atmospheric pressure in consideration of manufacturing stability and cost.
前記混合物の熱処理について、前記記載の焼成温度までの昇温速度は特に限定されないが、例えば、1〜100℃/分が好ましく、より好ましくは5〜50℃/分である。また、昇温後の保持時間は、炭化反応および窒化反応を進行させることができれば特に限定されないが、得られる燃料電池用電極触媒の粒子サイズおよび製造コストなどを考慮すると、10分〜5時間が好ましく、より好ましくは30分〜3時間である。 About the heat processing of the said mixture, although the temperature increase rate to the calcination temperature of the said description is not specifically limited, For example, 1-100 degreeC / min is preferable, More preferably, it is 5-50 degreeC / min. In addition, the holding time after the temperature rise is not particularly limited as long as the carbonization reaction and the nitriding reaction can proceed, but considering the particle size and production cost of the obtained fuel cell electrode catalyst, 10 minutes to 5 hours Preferably, it is 30 minutes to 3 hours.
燃料電池用電極触媒の形状は、好ましい遷移金属元素、炭素、窒素および酸素の組成比を持ち、かつ燃料電池電極触媒としての十分な酸素還元能を有する限り、特に限定はされないが、例えば、粒子状、繊維状、シート状、多孔体構造などが挙げられる。 The shape of the electrode catalyst for a fuel cell is not particularly limited as long as it has a preferable composition ratio of transition metal elements, carbon, nitrogen and oxygen and has a sufficient oxygen reducing ability as a fuel cell electrode catalyst. , Fiber, sheet, and porous structure.
燃料電池用電極触媒は、高い導電性、安定性および高比表面積が要求される。そのため、上記の製造工程中または工程後に燃料電池用電極触媒を担体に担持することもできる。担体としては、導電性および安定性が高く、比表面積が大きいものであれば特に限定されないが、例えば、カーボンブラック、カーボンナノチューブ、カーボンナノファイバー、多孔体カーボン、カーボンナノホーン、フラーレン、グラファイト、グラフェン、黒鉛、導電性セラミックおよび多孔体導電性セラクックなどが挙げられる。担体の形状と大きさは特に限定されないが、担持される燃料電池用電極触媒の触媒活性など考慮すると、担体の粒子径は10〜1000nmが好ましく、より好ましくは10〜100nmである。 Fuel cell electrode catalysts are required to have high conductivity, stability, and high specific surface area. Therefore, the fuel cell electrode catalyst can also be supported on the carrier during or after the above manufacturing process. The carrier is not particularly limited as long as it has high conductivity and stability and a large specific surface area. For example, carbon black, carbon nanotube, carbon nanofiber, porous carbon, carbon nanohorn, fullerene, graphite, graphene, Examples include graphite, conductive ceramics, and porous conductive ceramics. The shape and size of the carrier are not particularly limited, but considering the catalytic activity of the supported fuel cell electrode catalyst, the particle size of the carrier is preferably 10 to 1000 nm, more preferably 10 to 100 nm.
また、前記分子中に窒素を含まない有機化合物または前記分子中に酸素を含む遷移金属含有化合物の性状によっては、熱処理により得られる触媒の凝集状態が不均一であることがある。このような場合に、前記触媒を解砕することにより、微細で、粒径がより均一な触媒を得ることができる。 Further, depending on the properties of the organic compound not containing nitrogen in the molecule or the transition metal-containing compound containing oxygen in the molecule, the agglomerated state of the catalyst obtained by the heat treatment may be uneven. In such a case, by crushing the catalyst, a fine catalyst having a more uniform particle size can be obtained.
燃料電池用電極触媒を解砕する方法としては特に限定されないが、例えば、ロール転動ミル、ボールミル、小径ボールミル(ビーズミル)、媒体撹拌ミル、気流粉砕機、乳鉢、自動混練乳鉢、槽解機およびジェットミルを用いることができ、触媒が少量であれば、好ましくは、乳鉢、自動混練乳鉢、またはバッチ式のボールミルが用いられ、触媒が多量であり連続的な混合、解砕処理を行う場合には、好ましくはジェットミルが用いられる。 The method for crushing the fuel cell electrode catalyst is not particularly limited, and examples thereof include a roll rolling mill, a ball mill, a small-diameter ball mill (bead mill), a medium stirring mill, an airflow crusher, a mortar, an automatic kneading mortar, a tank crusher A jet mill can be used, and if the catalyst is small, preferably a mortar, an automatic kneading mortar, or a batch type ball mill is used, and when a large amount of catalyst is used for continuous mixing and crushing treatment Is preferably a jet mill.
<触媒>
本発明の燃料電池用電極触媒は、上述した本発明の燃料電池用電極触媒の製造方法により製造されることを特徴としている(以下、上述した本発明の燃料電池用電極触媒の製造方法により製造される燃料電池用電極触媒を「触媒(A)」ともいう)。
前記触媒(A)を構成する遷移金属元素、炭素、窒素および酸素の原子数の比を遷移金属元素:炭素:窒素:酸素=1:x:y:zと表すと、好ましくは0<x≦3、0<y≦2、0<z≦3である。<Catalyst>
The fuel cell electrode catalyst of the present invention is manufactured by the above-described method for manufacturing a fuel cell electrode catalyst of the present invention (hereinafter, manufactured by the above-described method for manufacturing a fuel cell electrode catalyst of the present invention). The fuel cell electrode catalyst is also referred to as “catalyst (A)”).
When the ratio of the number of atoms of the transition metal element, carbon, nitrogen and oxygen constituting the catalyst (A) is expressed as transition metal element: carbon: nitrogen: oxygen = 1: x: y: z, preferably 0 <x ≦ 3, 0 <y ≦ 2, 0 <z ≦ 3.
電極触媒の活性が高いことから、xの範囲は、より好ましくは0.3≦x≦2.5、さらに好ましくは0.5≦x≦2.0であり、特に好ましくは0.7≦x≦1.5であり、yの範囲は、より好ましくは0.01≦y≦1.5、さらに好ましくは0.02≦y≦0.5であり、特に好ましくは0.03≦y≦0.4であり、zの範囲は、より好ましくは0.2≦z≦2.5であり、さらに好ましくは0.3≦z≦2.0であり、特に好ましくは0.5≦z≦1.5である。 Since the activity of the electrode catalyst is high, the range of x is more preferably 0.3 ≦ x ≦ 2.5, further preferably 0.5 ≦ x ≦ 2.0, and particularly preferably 0.7 ≦ x. ≦ 1.5, and the range of y is more preferably 0.01 ≦ y ≦ 1.5, still more preferably 0.02 ≦ y ≦ 0.5, and particularly preferably 0.03 ≦ y ≦ 0. The range of z is more preferably 0.2 ≦ z ≦ 2.5, still more preferably 0.3 ≦ z ≦ 2.0, and particularly preferably 0.5 ≦ z ≦ 1. .5.
また、前記触媒(A)が、前記遷移金属元素として、チタン、バナジウム、クロム、マンガン、鉄、コバルト、ニッケル、銅、亜鉛、ジルコニウム、ニオブ、モリブデン、タンタルおよびタングステンからなる群から選択される1種の遷移金属元素M1、および前記群より選択される遷移金属元素M1とは異なる少なくとも1種の遷移金属元素M2を含む場合には、前記触媒(A)を構成する遷移金属元素M1、遷移金属元素M2、炭素、窒素および酸素の原子数の比を、遷移金属元素M1:遷移金属元素M2:炭素:窒素:酸素=(1−a):a:x:y:zと表すと、好ましくは、0<a≦0.5、0<x≦3、0<y≦2、0<z≦3である。前記触媒(A)は、このように遷移金属元素M2を含むと、より性能が高くなる。 The catalyst (A) is selected from the group consisting of titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, zirconium, niobium, molybdenum, tantalum and tungsten as the transition metal element. When including at least one kind of transition metal element M1 selected from the group and a transition metal element M2 selected from the group, the transition metal element M1 and transition metal constituting the catalyst (A) When the ratio of the number of atoms of element M2, carbon, nitrogen and oxygen is expressed as transition metal element M1: transition metal element M2: carbon: nitrogen: oxygen = (1-a): a: x: y: z, 0 <a ≦ 0.5, 0 <x ≦ 3, 0 <y ≦ 2, and 0 <z ≦ 3. When the catalyst (A) contains the transition metal element M2 as described above, the performance becomes higher.
電極触媒の活性が高いことから、x、yおよびzの好ましい範囲は上述のとおりであり、aの範囲は、好ましくは0.01≦a≦0.5、さらに好ましくは0.02≦a≦0.4、特に好ましくは0.03≦a≦0.3である。 Since the activity of the electrode catalyst is high, the preferred ranges of x, y and z are as described above, and the range of a is preferably 0.01 ≦ a ≦ 0.5, more preferably 0.02 ≦ a ≦. 0.4, particularly preferably 0.03 ≦ a ≦ 0.3.
前記a、x、yおよびzの値は、後述する実施例で採用した方法により測定した場合の値である。 The values of a, x, y and z are values measured by the method employed in the examples described later.
<遷移金属元素M2が存在することにより発揮されると予想される効果>
遷移金属元素M2(チタン、バナジウム、クロム、マンガン、鉄、コバルト、ニッケル、銅、亜鉛、ジルコニウム、ニオブ、モリブデン、タンタルおよびタングステンからなる群から選択される遷移金属元素M1とは異なる少なくとも1種の金属元素)が存在することにより予想される効果は以下のとおりである。<Effect expected to be exhibited by the presence of transition metal element M2>
Transition metal element M2 (at least one kind different from transition metal element M1 selected from the group consisting of titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, zirconium, niobium, molybdenum, tantalum and tungsten) The effects expected from the presence of (metal element) are as follows.
(1)遷移金属元素M2または遷移金属元素M2を含む化合物が、電極触媒を合成する際に、遷移金属元素M1原子と窒素原子との結合を形成するための触媒として作用している。 (1) The transition metal element M2 or the compound containing the transition metal element M2 acts as a catalyst for forming a bond between the transition metal element M1 atom and the nitrogen atom when synthesizing the electrode catalyst.
(2)遷移金属元素M1が溶出するような高電位、高酸化性雰囲気下で電極触媒を使用する場合であっても、遷移金属元素M2が不動態化することによって、遷移金属元素M1のさらなる溶出を防ぐ。 (2) Even when the electrode catalyst is used in a high potential, high oxidizing atmosphere where the transition metal element M1 is eluted, the transition metal element M2 is passivated to further increase the transition metal element M1. Prevent elution.
(3)熱処理の際に、熱処理物の焼結、すなわち比表面積の低下を防ぐ。 (3) During heat treatment, sintering of the heat-treated product, that is, reduction in specific surface area is prevented.
(4)電極触媒中に遷移金属元素M1および遷移金属元素M2が存在することにより、双方の金属元素が隣接しあう部位において、電荷の偏りが生じ、金属元素として遷移金属元素M1のみを有する電極触媒ではなしえない、基質の吸着もしくは反応、または生成物の脱離が発生する。 (4) Due to the presence of the transition metal element M1 and the transition metal element M2 in the electrode catalyst, a bias of charge occurs in a portion where both metal elements are adjacent to each other, and the electrode has only the transition metal element M1 as the metal element. Substrate adsorption or reaction, or product desorption, which cannot be achieved with a catalyst, occurs.
本発明の触媒(A)は、好ましくは、遷移金属元素、炭素、窒素および酸素の各原子を有し、前記遷移金属元素の酸化物、炭化物または窒化物単独あるいはこれらのうちの複数の結晶構造を有する。前記触媒(A)に対するX線回折分析による結晶構造解析の結果と、元素分析の結果とから判断すると、前記触媒(A)は、前記遷移金属元素の酸化物構造を有したまま、酸化物構造の酸素原子のサイトを炭素原子または窒素原子で置換した構造、あるいは前記遷移金属元素の炭化物、窒化物または炭窒化物の構造を有したまま、炭素原子または窒素原子のサイトを酸素原子で置換した構造を有するか、あるいはこれらの構造を含む混合物ではないかと推測される。 The catalyst (A) of the present invention preferably has each atom of transition metal element, carbon, nitrogen and oxygen, and oxide, carbide or nitride of the transition metal element alone or a plurality of crystal structures thereof Have Judging from the results of crystal structure analysis by X-ray diffraction analysis on the catalyst (A) and the results of elemental analysis, the catalyst (A) has an oxide structure while having the oxide structure of the transition metal element. The site of the oxygen atom is replaced with a carbon atom or a nitrogen atom, or the site of the carbon atom or nitrogen atom is replaced with an oxygen atom while maintaining the structure of the carbide, nitride or carbonitride of the transition metal element. It is presumed that it has a structure or a mixture containing these structures.
<BET比表面積>
本発明の燃料電池用電極触媒の製造方法によれば、比表面積の大きな燃料電池用電極触媒が製造され、本発明の触媒(A)のBET法で算出される比表面積は、好ましくは30〜400m2/g、より好ましくは50〜350m2/g、さらに好ましくは100〜300m2/gである。<BET specific surface area>
According to the method for producing a fuel cell electrode catalyst of the present invention, a fuel cell electrode catalyst having a large specific surface area is produced, and the specific surface area calculated by the BET method of the catalyst (A) of the present invention is preferably from 30 to 400m 2 / g, more preferably 50~350m 2 / g, more preferably from 100 to 300 m 2 / g.
前記触媒(A)の、下記測定法(A)に従って測定される酸素還元開始電位は、可逆水素電極を基準として好ましくは0.5V(vs.RHE)以上、より好ましくは0.6V(vs.RHE)以上、さらに好ましくは0.7V(vs.RHE)以上である。
〔測定法(A):
電子伝導性物質であるカーボンに分散させた触媒が1質量%となるように、該触媒およびカーボンを溶剤中に入れ、超音波で攪拌し懸濁液を得る。なお、カーボンとしては、カーボンブラック(比表面積:100〜300m2/g)(例えばキャボット社製 XC−72)を用い、触媒とカーボンとが質量比で95:5になるように分散させる。また、溶剤としては、イソプロピルアルコール:水(質量比)=2:1を用いる。The oxygen reduction initiation potential of the catalyst (A) measured according to the following measurement method (A) is preferably 0.5 V (vs. RHE) or more, more preferably 0.6 V (vs. RHE) or more, more preferably 0.7 V (vs. RHE) or more.
[Measurement method (A):
The catalyst and carbon are placed in a solvent so that the amount of the catalyst dispersed in carbon, which is an electron conductive substance, is 1% by mass, and stirred with ultrasonic waves to obtain a suspension. As the carbon, carbon black (specific surface area: 100 to 300 m 2 / g) (for example, XC-72 manufactured by Cabot Corporation) is used, and the catalyst and carbon are dispersed so that the mass ratio is 95: 5. As the solvent, isopropyl alcohol: water (mass ratio) = 2: 1 is used.
前記懸濁液を、超音波をかけながら10μLを採取し、すばやくグラッシーカーボン電極(直径:5.2mm)上に滴下し、120℃で5分間乾燥させる。乾燥することにより触媒を含む燃料電池用触媒層が、グラッシーカーボン電極上に形成される。この滴下および乾燥操作を、カーボン電極表面に1.0mg以上の燃料電池触媒層が形成されるまで行う。 10 μL of the suspension is collected while applying ultrasonic waves, quickly dropped onto a glassy carbon electrode (diameter: 5.2 mm), and dried at 120 ° C. for 5 minutes. By drying, a catalyst layer for a fuel cell containing the catalyst is formed on the glassy carbon electrode. This dropping and drying operation is performed until a fuel cell catalyst layer of 1.0 mg or more is formed on the surface of the carbon electrode.
次いでナフィオン(NAFION(登録商標))(デュポン社 5%NAFION(登録商標)溶液(DE521))をイソプロピルアルコールで10倍に希釈したものを、さらに前記燃料電池用触媒層上に10μL滴下する。これを、120℃で1時間乾燥する。 Next, 10 μL of NAFION (registered trademark) (DuPont 5% NAFION (registered trademark) solution (DE521)) diluted 10-fold with isopropyl alcohol is further dropped on the fuel cell catalyst layer. This is dried at 120 ° C. for 1 hour.
このようにして、得られた電極を用いて、酸素雰囲気および窒素雰囲気で、0.5mol/Lの硫酸水溶液中、30℃の温度で、同濃度の硫酸水溶液中での可逆水素電極を参照電極とし、5mV/秒の電位走査速度で分極することにより電流−電位曲線を測定した際の、酸素雰囲気での還元電流と窒素雰囲気での還元電流とに0.2μA/cm2以上の差が現れ始める電位を酸素還元開始電位とする。〕
本発明において、酸素還元電流密度は、以下のとおり求めることができる。Thus, using the obtained electrode, a reversible hydrogen electrode in a sulfuric acid aqueous solution of the same concentration at a temperature of 30 ° C. in a 0.5 mol / L sulfuric acid aqueous solution in an oxygen atmosphere and a nitrogen atmosphere was used as a reference electrode. And a difference of 0.2 μA / cm 2 or more appears between the reduction current in the oxygen atmosphere and the reduction current in the nitrogen atmosphere when the current-potential curve is measured by polarization at a potential scanning speed of 5 mV / sec. The starting potential is defined as the oxygen reduction starting potential. ]
In the present invention, the oxygen reduction current density can be determined as follows.
まず、上記測定法(A)の結果から、0.65V(vs.RHE)における、酸素雰囲気での還元電流と窒素雰囲気での還元電流との差を算出する。算出した値を、さらに電極面積で除した値を酸素還元電流密度(mA/cm2)とする。First, the difference between the reduction current in the oxygen atmosphere and the reduction current in the nitrogen atmosphere at 0.65 V (vs. RHE) is calculated from the result of the measurement method (A). A value obtained by dividing the calculated value by the electrode area is defined as an oxygen reduction current density (mA / cm 2 ).
また、本発明の燃料電池用電極触媒の酸素還元電流密度は、0.02mA/cm2以上であることが好ましく、0.5mA/cm2以上であることがより好ましく、1.0mA/cm2以上であることが特に好ましい。また、酸素還元電流密度は高い程好ましく、その上限としては、特に制限されないが、100mA/cm2である。The oxygen reduction current density of the fuel cell electrode catalyst of the present invention is preferably 0.02 mA / cm 2 or more, more preferably 0.5 mA / cm 2 or more, 1.0 mA / cm 2 The above is particularly preferable. The oxygen reduction current density is preferably as high as possible, and the upper limit thereof is not particularly limited, but is 100 mA / cm 2 .
<用途>
本発明の触媒(A)は、白金触媒の代替触媒として使用することができる。<Application>
The catalyst (A) of the present invention can be used as an alternative catalyst for a platinum catalyst.
本発明の燃料電池用触媒層は、前記触媒(A)を含むことを特徴としている。 The catalyst layer for a fuel cell according to the present invention includes the catalyst (A).
燃料電池用触媒層には、アノード触媒層、カソード触媒層があるが、前記触媒(A)はいずれにも用いることができる。前記触媒(A)は、耐久性に優れ、酸素還元能が大きいので、カソード触媒層に用いることが好ましい。 The fuel cell catalyst layer includes an anode catalyst layer and a cathode catalyst layer, and the catalyst (A) can be used for both. Since the catalyst (A) is excellent in durability and has a large oxygen reducing ability, it is preferably used for the cathode catalyst layer.
本発明の燃料電池用触媒層には、さらに電子伝導性粉末を含むことが好ましい。前記触媒(A)を含む燃料電池用触媒層がさらに電子伝導性粉末を含む場合には、還元電流をより高めることができる。電子伝導性粉末は、前記触媒(A)に、電気化学的反応を誘起させるための電気的接点を生じさせるため、還元電流を高めると考えられる。 The catalyst layer for a fuel cell of the present invention preferably further contains an electron conductive powder. When the fuel cell catalyst layer containing the catalyst (A) further contains an electron conductive powder, the reduction current can be further increased. The electron conductive powder is considered to increase the reduction current because it generates an electrical contact for inducing an electrochemical reaction in the catalyst (A).
前記電子伝導性粒子は通常、触媒の担体として用いられる。 The electron conductive particles are usually used as a catalyst carrier.
前記触媒(A)はある程度の導電性を有するが、触媒(A)により多くの電子を与える、あるいは、反基質が触媒(A)から多くの電子を受け取るために、触媒(A)に、導電性を付与するための担体粒子を混合してもよい。 The catalyst (A) has a certain degree of conductivity. However, since the catalyst (A) gives more electrons or the anti-substrate receives more electrons from the catalyst (A), the catalyst (A) Carrier particles for imparting properties may be mixed.
電子伝導性粒子の材質としては、炭素、導電性高分子、導電性セラミクス、金属または酸化タングステンもしくは酸化イリジウムなどの導電性無機酸化物が挙げられ、それらを1種単独または組み合わせて用いることができる。特に、炭素からなる電子伝導性粒子は比表面積が大きいため、また、安価に小粒径のものを入手しやすく、耐薬品性、耐高電位性に優れるため、炭素単独または炭素とその他の電子伝導性粒子との混合物が好ましい。すなわち燃料電池用触媒層としては、前記触媒(A)と炭素とを含むことが好ましい。 Examples of the material of the electron conductive particles include carbon, conductive polymer, conductive ceramics, metal, and conductive inorganic oxides such as tungsten oxide or iridium oxide, and these can be used alone or in combination. . In particular, since the electron conductive particles made of carbon have a large specific surface area, and are easily available with a small particle size at low cost, and are excellent in chemical resistance and high potential resistance, carbon alone or carbon and other electrons. A mixture with conductive particles is preferred. That is, the fuel cell catalyst layer preferably contains the catalyst (A) and carbon.
炭素としては、カーボンブラック、グラファイト、黒鉛、活性炭、カーボンナノチューブ、カーボンナノファイバー、カーボンナノホーン、フラーレン、多孔体カーボン、グラフェンなどが挙げられる。炭素からなる電子伝導性粒子の粒径は、小さすぎると電子伝導パスが形成されにくくなり、また大きすぎると燃料電池用触媒層のガス拡散性の低下や触媒の利用率の低下が起こる傾向があるため、5〜1000nmであることが好ましく、10〜100nmであることがよりに好ましい。 Examples of carbon include carbon black, graphite, graphite, activated carbon, carbon nanotube, carbon nanofiber, carbon nanohorn, fullerene, porous carbon, and graphene. If the particle size of the electron conductive particles made of carbon is too small, it becomes difficult to form an electron conduction path. If the particle size is too large, the gas diffusibility of the fuel cell catalyst layer and the catalyst utilization rate tend to decrease. Therefore, the thickness is preferably 5 to 1000 nm, and more preferably 10 to 100 nm.
電子伝導性粒子が炭素からなる場合、前記触媒(A)と電子伝導性粒子との重量比(触媒:電子伝導性粒子)は、好ましくは4:1〜1000:1である。 When the electron conductive particles are made of carbon, the weight ratio of the catalyst (A) to the electron conductive particles (catalyst: electron conductive particles) is preferably 4: 1 to 1000: 1.
前記導電性高分子としては特に限定は無いが、例えばポリアセチレン、ポリ−p−フェニレン、ポリアニリン、ポリアルキルアニリン、ポリピロール、ポリチオフェン、ポリインドール、ポリ−1,5−ジアミノアントラキノン、ポリアミノジフェニル、ポリ(o−フェニレンジアミン)、ポリ(キノリニウム)塩、ポリピリジン、ポリキノキサリン、ポリフェニルキノキサリン等が挙げられる。これらの中でも、ポリピロール、ポリアニリン、ポリチオフェンが好ましく、ポリピロールがより好ましい。 The conductive polymer is not particularly limited. For example, polyacetylene, poly-p-phenylene, polyaniline, polyalkylaniline, polypyrrole, polythiophene, polyindole, poly-1,5-diaminoanthraquinone, polyaminodiphenyl, poly (o -Phenylenediamine), poly (quinolinium) salt, polypyridine, polyquinoxaline, polyphenylquinoxaline and the like. Among these, polypyrrole, polyaniline, and polythiophene are preferable, and polypyrrole is more preferable.
前記高分子電解質としては、燃料電池用触媒層において一般的に用いられているものであれば特に限定されない。具体的には、スルホン酸基を有するパーフルオロカーボン重合体(例えば、ナフィオン(NAFION(登録商標))(デュポン社 5%NAFION(登録商標)溶液(DE521)など)、スルホン酸基を有する炭化水素系高分子化合物、リン酸などの無機酸をドープさせた高分子化合物、一部がプロトン伝導性の官能基で置換された有機/無機ハイブリッドポリマー、高分子マトリックスにリン酸溶液や硫酸溶液を含浸させたプロトン伝導体などが挙げられる。これらの中でも、ナフィオン(NAFION(登録商標))(デュポン社 5%NAFION(登録商標)溶液(DE521))が好ましい。 The polymer electrolyte is not particularly limited as long as it is generally used in a fuel cell catalyst layer. Specifically, a perfluorocarbon polymer having a sulfonic acid group (for example, NAFION (registered trademark) (DuPont 5% NAFION (registered trademark) solution (DE521), etc.), hydrocarbon-based sulfonic acid group Polymer compound, polymer compound doped with inorganic acid such as phosphoric acid, organic / inorganic hybrid polymer partially substituted with proton conductive functional group, polymer matrix impregnated with phosphoric acid solution or sulfuric acid solution Among them, Nafion (NAFION (registered trademark)) (DuPont 5% NAFION (registered trademark) solution (DE521)) is preferable.
本発明の燃料電池用触媒層は、アノード触媒層またはカソード触媒層のいずれにも用いることができる。本発明の燃料電池用触媒層は、高い酸素還元能を有し、酸性電解質中において高電位であっても腐蝕しがたい触媒を含むため、燃料電池のカソードに設けられる触媒層(カソード用触媒層)として有用である。特に固体高分子型燃料電池が備える膜電極接合体のカソードに設けられる触媒層に好適に用いられる。 The catalyst layer for a fuel cell of the present invention can be used for either an anode catalyst layer or a cathode catalyst layer. The catalyst layer for a fuel cell of the present invention includes a catalyst layer (catalyst catalyst for cathode) provided on the cathode of a fuel cell because it contains a catalyst having high oxygen reducing ability and hardly corroded even in a high potential in an acidic electrolyte. Layer). In particular, it is suitably used for a catalyst layer provided on the cathode of a membrane electrode assembly provided in a polymer electrolyte fuel cell.
前記触媒(A)を、担体である前記電子伝導性粒子上に分散させる方法としては、気流分散、液中分散等の方法が挙げられる。液中分散は、溶媒中に触媒(A)および電子伝導性粒子を分散したものを、燃料電池用触媒層形成工程に使用できるため好ましい。液中分散としては、オリフィス収縮流による方法、回転せん断流による方法または超音波による方法等が挙げられる。液中分散の際、使用される溶媒は、触媒(A)や電子伝導性粒子を浸食することがなく、分散できるものであれば特に制限はないが、揮発性の液体有機溶媒または水等が一般に使用される。 Examples of the method for dispersing the catalyst (A) on the electron conductive particles as a support include air flow dispersion and dispersion in liquid. Dispersion in liquid is preferred because a catalyst (A) and electron conductive particles dispersed in a solvent can be used in the fuel cell catalyst layer forming step. Examples of the dispersion in liquid include a method using an orifice contraction flow, a method using a rotating shear flow, and a method using an ultrasonic wave. The solvent used for dispersion in the liquid is not particularly limited as long as it does not erode the catalyst (A) or the electron conductive particles and can be dispersed. However, a volatile liquid organic solvent or water may be used. Generally used.
また、触媒(A)を、前記電子伝導性粒子上に分散させる際、さらに上記電解質と分散剤とを同時に分散させてもよい。 Further, when the catalyst (A) is dispersed on the electron conductive particles, the electrolyte and the dispersant may be further dispersed simultaneously.
燃料電池用触媒層の形成方法としては、特に制限はないが、たとえば、前記触媒(A)と電子伝導性粒子と電解質とを含む懸濁液を、後述する電解質膜またはガス拡散層に塗布する方法が挙げられる。前記塗布する方法としては、ディッピング法、スクリーン印刷法、ロールコーティング法、スプレー法などが挙げられる。また、前記触媒(A)と電子伝導性粒子と電解質とを含む懸濁液を、塗布法またはろ過法により基材に燃料電池用触媒層を形成した後、転写法で電解質膜に燃料電池用触媒層を形成する方法が挙げられる。 The method for forming the fuel cell catalyst layer is not particularly limited. For example, a suspension containing the catalyst (A), electron conductive particles, and an electrolyte is applied to an electrolyte membrane or a gas diffusion layer to be described later. A method is mentioned. Examples of the application method include a dipping method, a screen printing method, a roll coating method, and a spray method. In addition, after forming a catalyst layer for a fuel cell on a base material by a coating method or a filtration method, a suspension containing the catalyst (A), electron conductive particles, and an electrolyte is formed on the electrolyte membrane by a transfer method. The method of forming a catalyst layer is mentioned.
本発明の電極は、前記燃料電池用触媒層と多孔質支持層とを有することを特徴としている。 The electrode of the present invention is characterized by having the fuel cell catalyst layer and a porous support layer.
本発明の電極はカソードまたはアノードのいずれの電極にも用いることができる。本発明の電極は、耐久性に優れ、触媒能が大きいので、カソードに用いるとより産業上の優位性が高い。 The electrode of the present invention can be used as either a cathode or an anode. Since the electrode of the present invention is excellent in durability and has a large catalytic ability, it is more industrially superior when used as a cathode.
多孔質支持層とは、ガスを拡散する層(以下「ガス拡散層」とも記す。)である。ガス拡散層としては、電子伝導性を有し、ガスの拡散性が高く、耐食性の高いものであれば特に限定はされないが、一般的にはカーボンペーパー、カーボンクロスなどの炭素系多孔質材料や、軽量化のためにステンレス、耐食材を被服したアルミニウム箔が用いられる。 The porous support layer is a layer that diffuses gas (hereinafter also referred to as “gas diffusion layer”). The gas diffusion layer is not particularly limited as long as it has electron conductivity, high gas diffusibility, and high corrosion resistance. Generally, carbon-based porous materials such as carbon paper and carbon cloth, In order to reduce the weight, aluminum foil coated with stainless steel and corrosion-resistant material is used.
本発明の膜電極接合体は、カソードとアノードと前記カソードおよび前記アノードの間に配置された電解質膜とを有する膜電極接合体であって、前記カソードおよび/または前記アノードが、前記電極であることを特徴としている。 The membrane electrode assembly of the present invention is a membrane electrode assembly having a cathode, an anode, and an electrolyte membrane disposed between the cathode and the anode, wherein the cathode and / or the anode is the electrode. It is characterized by that.
電解質膜としては、例えば、パーフルオロスルホン酸系を用いた電解質膜または炭化水素系電解質膜などが一般的に用いられるが、高分子微多孔膜に液体電解質を含浸させた膜または多孔質体に高分子電解質を充填させた膜などを用いてもよい。 As the electrolyte membrane, for example, an electrolyte membrane using a perfluorosulfonic acid system or a hydrocarbon electrolyte membrane is generally used. However, a membrane or porous body in which a polymer microporous membrane is impregnated with a liquid electrolyte is used. A membrane filled with a polymer electrolyte may be used.
また本発明の燃料電池は、前記膜電極接合体を備えることを特徴としている。 The fuel cell according to the present invention includes the membrane electrode assembly.
燃料電池の電極反応はいわゆる3相界面(電解質‐電極触媒‐反応ガス)で起こる。燃料電池は、使用される電解質などの違いにより数種類に分類され、溶融炭酸塩型(MCFC)、リン酸型(PAFC)、固体酸化物型(SOFC)、固体高分子型(PEFC)等がある。中でも、本発明の膜電極接合体は、固体高分子型燃料電池に使用することが好ましい。 Fuel cell electrode reactions occur at the so-called three-phase interface (electrolyte-electrode catalyst-reaction gas). Fuel cells are classified into several types depending on the electrolyte used, etc., and include molten carbonate type (MCFC), phosphoric acid type (PAFC), solid oxide type (SOFC), and solid polymer type (PEFC). . Especially, it is preferable to use the membrane electrode assembly of this invention for a polymer electrolyte fuel cell.
本発明の触媒(A)を用いた燃料電池は性能が高く、また、白金を触媒として用いた場合と比較してきわめて安価であるという特徴を持つ。本発明の燃料電池は、発電機能、発光機能、発熱機能、音響発生機能、運動機能、表示機能および充電機能からなる群より選ばれる少なくとも一つの機能を有し燃料電池を備える物品の性能、特に携帯可能な物品の性能を向上させることができる。前記燃料電池は、好ましくは物品の表面または内部に備えられる。 The fuel cell using the catalyst (A) of the present invention has high performance, and is characterized by being extremely inexpensive as compared with the case of using platinum as a catalyst. The fuel cell of the present invention has a power generation function, a light emission function, a heat generation function, a sound generation function, an exercise function, a display function, and a performance of an article provided with a fuel cell having at least one function selected from the group consisting of a charge function, The performance of the portable article can be improved. The fuel cell is preferably provided on the surface or inside of an article.
<本発明の燃料電池を備えた物品の具体例>
本発明の燃料電池を備えることができる前記物品の具体例としては、ビル、家屋、テント等の建築物、蛍光灯、LED等、有機EL、街灯、屋内照明、信号機等の照明器具、機械、車両そのものを含む自動車用機器、家電製品、農業機器、電子機器、携帯電話等を含む携帯情報端末、美容機材、可搬式工具、風呂用品トイレ用品等の衛生機材、家具、玩具、装飾品、掲示板、クーラーボックス、屋外発電機などのアウトドア用品、教材、造花、オブジェ、心臓ペースメーカー用電源、ペルチェ素子を備えた加熱および冷却器用の電源が挙げられる。<Specific example of article provided with fuel cell of the present invention>
Specific examples of the article that can include the fuel cell of the present invention include buildings, houses, buildings such as tents, fluorescent lamps, LEDs, etc., organic EL, street lamps, indoor lighting, lighting fixtures such as traffic lights, machines, Automotive equipment including the vehicle itself, home appliances, agricultural equipment, electronic equipment, portable information terminals including mobile phones, beauty equipment, portable tools, sanitary equipment such as bathroom accessories, furniture, toys, decorations, bulletin boards , Outdoor supplies such as cooler boxes, outdoor generators, teaching materials, artificial flowers, objects, power supplies for cardiac pacemakers, power supplies for heating and cooling devices with Peltier elements.
以下に、本発明を実施例により更に詳細に説明するが、本発明はこれらの実施例に限定されない。 EXAMPLES The present invention will be described below in more detail with reference to examples, but the present invention is not limited to these examples.
また、実施例および比較例における各種測定は、下記の方法により行った。 In addition, various measurements in Examples and Comparative Examples were performed by the following methods.
[分析方法]
1.粉末X線回折
理学電機株式会社製 ロータフレックスを用いて、試料の粉末X線回折を行った。[Analysis method]
1. Powder X-ray diffraction Samples were subjected to powder X-ray diffraction using a rotor flex made by Rigaku Corporation.
各試料の粉末X線回折における回折線ピークの本数は、信号(S)とノイズ(N)の比(S/N)が2以上で検出できるシグナルを1つのピークとしてみなして数えた。 The number of diffraction line peaks in powder X-ray diffraction of each sample was counted by regarding a signal that can be detected at a ratio (S / N) of signal (S) to noise (N) of 2 or more as one peak.
なお、ノイズ(N)は、ベースラインの幅とした。 The noise (N) is the width of the baseline.
2.元素分析
炭素:試料約0.1gを量り取り、堀場製作所 EMIA−110で測定を行った。2. Elemental analysis Carbon: About 0.1 g of a sample was weighed and measured with Horiba EMIA-110.
窒素・酸素:試料約0.1gを量り取り、Ni−Cupに封入後、ON分析装置で測定を行った。 Nitrogen / oxygen: About 0.1 g of a sample was weighed and sealed in Ni-Cup, and then measured with an ON analyzer.
チタン:試料約0.1gを白金皿に量り取り、酸を加えて加熱分解した。この加熱分解物を定容後、希釈し、ICP−MSで定量を行った。 Titanium: About 0.1 g of a sample was weighed into a platinum dish, and acid was added for thermal decomposition. This heat-decomposed product was diluted, diluted, and quantified by ICP-MS.
3.BET比表面積
試料を0.15g採取し、全自動BET比表面積測定装置 マックソーブ((株)マウンテック製)で比表面積測定を行った。前処理時間、前処理温度は、それぞれ30分、200℃に設定した。3. BET specific surface area 0.15 g of a sample was sampled, and the specific surface area was measured with a fully automatic BET specific surface area measuring device Macsorb (manufactured by Mountec Co., Ltd.). The pretreatment time and pretreatment temperature were set at 30 ° C. and 200 ° C., respectively.
[実施例1]
1.触媒の調製
30%硫酸チタン溶液(和光純薬製)18.24gを蒸留水に加え、100mlの溶液を作成した。作成した溶液を28%アンモニア水(和光純薬製)100mlと蒸留水200mlとの混合溶液に滴下し、水酸化チタンの沈殿を得た。得られた水酸化チタンを含む反応液を遠心分離することによりゲル状の水酸化チタンを得た。ポリビニルアルコール(和光純薬製、平均重合度1000)2.008gを蒸留水50mlに溶解させ、得られたゲル状の水酸化チタン6.5gと混合した。その後、溶媒を除去した。得られた混合粉末を管状炉において、1000℃で3時間、窒素ガス雰囲気中で熱処理することにより、燃料電池用電極触媒(以下「触媒(1)」とも記す。)が得られた。[Example 1]
1. Preparation of catalyst 18.24 g of 30% titanium sulfate solution (manufactured by Wako Pure Chemical Industries, Ltd.) was added to distilled water to prepare a 100 ml solution. The prepared solution was dropped into a mixed solution of 28% ammonia water (manufactured by Wako Pure Chemical Industries, Ltd.) 100 ml and distilled
触媒(1)の粉末X線回折スペクトルを図1に示す。立方晶構造を持つチタン化合物およびルチル構造を持つ酸化チタンの回折線ピークが観測された。 The powder X-ray diffraction spectrum of the catalyst (1) is shown in FIG. Diffraction line peaks of titanium compound with cubic structure and titanium oxide with rutile structure were observed.
また、触媒(1)の元素分析結果を表1に示す。炭素、窒素および酸素の存在が確認され、熱処理温度1000℃で窒素が反応し、結晶格子内に入ることが確認された。 In addition, Table 1 shows the results of elemental analysis of the catalyst (1). The presence of carbon, nitrogen and oxygen was confirmed, and it was confirmed that nitrogen reacted at a heat treatment temperature of 1000 ° C. and entered the crystal lattice.
触媒(1)のBET比表面積は213m2/gであった。The BET specific surface area of the catalyst (1) was 213 m 2 / g.
2.燃料電池用電極の製造
触媒(1)0.095gとカーボン(キャボット社製 XC−72)0.005gとを、イソプロピルアルコール:純水=2:1の質量比で混合した溶液10gに入れ、超音波で撹拌、懸濁して混合した。この混合物30μlをグラッシーカーボン電極(東海カーボン社製、直径:5.2mm)に塗布し、120℃で1時間乾燥し、カーボン電極表面に1.0mg以上の燃料電池触媒層が形成された。さらに、ナフィオン(NAFION(登録商標))(デュポン社 5%NAFION(登録商標)溶液(DE521))を10倍にイソプロピルアルコールで希釈したもの10μlを塗布し、120℃で1時間乾燥し、燃料電池用電極(1)を得た。2. Production of Fuel Cell Electrode A catalyst (1) 0.095 g and carbon (Cabot XC-72) 0.005 g were mixed in 10 g of a solution in which the mass ratio of isopropyl alcohol: pure water = 2: 1 was The mixture was stirred and suspended by sonic waves. 30 μl of the mixture was applied to a glassy carbon electrode (Tokai Carbon Co., Ltd., diameter: 5.2 mm) and dried at 120 ° C. for 1 hour to form a fuel cell catalyst layer of 1.0 mg or more on the carbon electrode surface. Furthermore, 10 μl of Nafion (NAFION (registered trademark)) (DuPont 5% NAFION (registered trademark) solution (DE521)) diluted 10-fold with isopropyl alcohol was applied, dried at 120 ° C. for 1 hour, and fuel cell A working electrode (1) was obtained.
3.酸素還元能の評価
作製した燃料電池用電極(1)を、酸素雰囲気および窒素雰囲気で、0.5mol/Lの硫酸水溶液中、30℃、5mV/秒の電位走査速度で分極し、電流−電位曲線を測定した。その際、同濃度の硫酸水溶液中での可逆水素電極を参照電極とした。3. Evaluation of oxygen reduction ability The produced fuel cell electrode (1) was polarized in an oxygen atmosphere and a nitrogen atmosphere in a 0.5 mol / L sulfuric acid aqueous solution at 30 ° C. and a potential scanning speed of 5 mV / sec. The curve was measured. At that time, a reversible hydrogen electrode in an aqueous sulfuric acid solution having the same concentration was used as a reference electrode.
上記測定結果から、酸素雰囲気での還元電流と窒素雰囲気での還元電流とに0.2μA/cm2以上差が現れ始める電位を酸素還元開始電位とした。 また、0.65V(vs.RHE)における、酸素雰囲気での還元電流と窒素雰囲気での還元電流との差を算出した。算出した値を、さらに電極面積で除した値を酸素還元電流密度(mA/cm2)とした。From the above measurement results, a potential at which a difference of 0.2 μA / cm 2 or more began to appear between the reduction current in the oxygen atmosphere and the reduction current in the nitrogen atmosphere was defined as the oxygen reduction start potential. Further, the difference between the reduction current in an oxygen atmosphere and the reduction current in a nitrogen atmosphere at 0.65 V (vs. RHE) was calculated. A value obtained by further dividing the calculated value by the electrode area was defined as an oxygen reduction current density (mA / cm 2 ).
酸素還元開始電位および酸素還元電流密度により、作製した燃料電池用電極(1)の触媒能を評価した。 The catalytic ability of the produced fuel cell electrode (1) was evaluated based on the oxygen reduction starting potential and the oxygen reduction current density.
すなわち、酸素還元開始電位が高いほど、酸素還元電流密度が大きいほど、燃料電池用電極における触媒の触媒能が高いことを示す。 That is, the higher the oxygen reduction start potential and the higher the oxygen reduction current density, the higher the catalytic performance of the catalyst in the fuel cell electrode.
図9に、上記測定により得られた電流−電位曲線を示す。 FIG. 9 shows a current-potential curve obtained by the above measurement.
実施例1で作製した触媒(1)は、酸素還元開始電位が0.83V(vs.RHE)、酸素還元電流密度が0.18mA/cm2であった。The catalyst (1) produced in Example 1 had an oxygen reduction starting potential of 0.83 V (vs. RHE) and an oxygen reduction current density of 0.18 mA / cm 2 .
[実施例2]
1.触媒の調製
30%硫酸チタン溶液18.24g(和光純薬製)を蒸留水に加え、100mlの溶液を作成した。作成した溶液を28%アンモニア水(和光純薬製)100mlと蒸留水200mlとの混合溶液に滴下し、水酸化チタンの沈殿を得た。得られた水酸化チタンを含む反応液を遠心分離することによりゲル状の水酸化チタンを得た。ポリビニルアルコール(和光純薬製、平均重合度1000)2.008gを蒸留水50mlに溶解させ、得られたゲル状の水酸化チタン6.5gと混合した。その後、溶媒を除去した。得られた混合粉末を管状炉において、800℃で3時間、窒素ガス雰囲気中で熱処理することにより、燃料電池用電極触媒(以下「触媒(2)」とも記す。)が得られた。[Example 2]
1. Preparation of catalyst 18.24 g of 30% titanium sulfate solution (manufactured by Wako Pure Chemical Industries, Ltd.) was added to distilled water to prepare a 100 ml solution. The prepared solution was dropped into a mixed solution of 28% ammonia water (manufactured by Wako Pure Chemical Industries, Ltd.) 100 ml and distilled
触媒(2)の粉末X線回折スペクトルを図2に示す。立方晶構造を持つチタン化合物、アナターゼ構造を持つ酸化チタンおよびルチル構造を持つ酸化チタンの回折線ピークが観測された。 The powder X-ray diffraction spectrum of the catalyst (2) is shown in FIG. Diffraction line peaks of a titanium compound having a cubic structure, a titanium oxide having an anatase structure, and a titanium oxide having a rutile structure were observed.
また、触媒(2)の元素分析結果を表1に示す。炭素、窒素および酸素の存在が確認され、熱処理温度800℃で窒素が反応し、結晶格子内に入ることが確認された。 In addition, Table 1 shows the results of elemental analysis of the catalyst (2). The presence of carbon, nitrogen and oxygen was confirmed, and it was confirmed that nitrogen reacted at a heat treatment temperature of 800 ° C. and entered the crystal lattice.
触媒(2)のBET比表面積は243m2/gであった。The BET specific surface area of the catalyst (2) was 243 m 2 / g.
2.燃料電池用電極の製造
前記触媒(2)を用いた以外は実施例1と同様にして燃料電池用電極(2)を得た。2. Production of Fuel Cell Electrode A fuel cell electrode (2) was obtained in the same manner as in Example 1 except that the catalyst (2) was used.
3.酸素還元能の評価
前記燃料電池用電極(2)を用いた以外は実施例1と同様にして触媒能を評価した。3. Evaluation of oxygen reduction ability Catalytic ability was evaluated in the same manner as in Example 1 except that the fuel cell electrode (2) was used.
図10に、上記測定により得られた電流−電位曲線を示す。 FIG. 10 shows a current-potential curve obtained by the above measurement.
実施例2で作製した触媒(2)は、酸素還元開始電位が0.78V(vs.RHE)、酸素還元電流密度が0.08mA/cm2であった。The catalyst (2) produced in Example 2 had an oxygen reduction starting potential of 0.78 V (vs. RHE) and an oxygen reduction current density of 0.08 mA / cm 2 .
[実施例3]
1.触媒の調製
30%硫酸チタン溶液18.24g(和光純薬製)を蒸留水に加え、100mlの溶液を作成した。作成した溶液を28%アンモニア水(和光純薬製)100mlと蒸留水200mlとの混合溶液に滴下し、水酸化チタンの沈殿を得た。得られた水酸化チタンを含む反応液を遠心分離することによりゲル状の水酸化チタンを得た。グルコース(純正化学製)1.396gを蒸留水50mlに溶解させ、得られたゲル状の水酸化チタン6.5gと混合した。その後、溶媒を除去した。得られた混合粉末を管状炉において、1000℃で3時間、窒素ガス雰囲気中で熱処理することにより、燃料電池用電極触媒(以下「触媒(3)」とも記す。)が得られた。[Example 3]
1. Preparation of catalyst 18.24 g of 30% titanium sulfate solution (manufactured by Wako Pure Chemical Industries, Ltd.) was added to distilled water to prepare a 100 ml solution. The prepared solution was dropped into a mixed solution of 28% ammonia water (manufactured by Wako Pure Chemical Industries, Ltd.) 100 ml and distilled
触媒(3)の粉末X線回折スペクトルを図3に示す。立方晶構造を持つチタン化合物およびルチル構造を持つ酸化チタンの回折線ピークが観測された。 The powder X-ray diffraction spectrum of the catalyst (3) is shown in FIG. Diffraction line peaks of titanium compound with cubic structure and titanium oxide with rutile structure were observed.
また、触媒(3)の元素分析結果を表1に示す。炭素、窒素および酸素の存在が確認され、熱処理温度1000℃で窒素が反応し、結晶格子内に入ることが確認された。 In addition, Table 1 shows the results of elemental analysis of the catalyst (3). The presence of carbon, nitrogen and oxygen was confirmed, and it was confirmed that nitrogen reacted at a heat treatment temperature of 1000 ° C. and entered the crystal lattice.
触媒(3)のBET比表面積は223m2/gであった。The BET specific surface area of the catalyst (3) was 223 m 2 / g.
2.燃料電池用電極の製造
前記触媒(3)を用いた以外は実施例1と同様にして燃料電池用電極(3)を得た。2. Production of Fuel Cell Electrode A fuel cell electrode (3) was obtained in the same manner as in Example 1 except that the catalyst (3) was used.
3.酸素還元能の評価
前記燃料電池用電極(3)を用いた以外は実施例1と同様にして触媒能を評価した。3. Evaluation of oxygen reduction ability Catalytic ability was evaluated in the same manner as in Example 1 except that the fuel cell electrode (3) was used.
図11に、上記測定により得られた電流−電位曲線を示す。 FIG. 11 shows a current-potential curve obtained by the above measurement.
実施例3で作製した触媒(3)は、酸素還元開始電位が0.86V(vs.RHE)、酸素還元電流密度が0.59mA/cm2であった。The catalyst (3) produced in Example 3 had an oxygen reduction starting potential of 0.86 V (vs. RHE) and an oxygen reduction current density of 0.59 mA / cm 2 .
[実施例4]
1.触媒の調製
30%硫酸チタン溶液(和光純薬製)18.24gおよび酢酸鉄(Aldrich社製)1.823gを蒸留水に加え、100mlの溶液を作成した。作成した溶液を28%アンモニア水(和光純薬製)100mlと蒸留水200mlとの混合溶液に滴下し、水酸化チタンの沈殿を得た。得られた水酸化チタンを含む反応液を遠心分離することによりゲル状の水酸化チタンを得た。ポリビニルアルコール(和光純薬製、平均重合度1000)2.008gを蒸留水50mlに溶解させ、得られたゲル状の水酸化チタン6.5gと混合した。その後、溶媒を除去した。得られた混合粉末を管状炉において、1000℃で3時間、窒素ガス雰囲気中で熱処理することにより、燃料電池用電極触媒(以下「触媒(4)」とも記す。)が得られた。[Example 4]
1. Preparation of catalyst 18.24 g of 30% titanium sulfate solution (manufactured by Wako Pure Chemical Industries) and 1.823 g of iron acetate (manufactured by Aldrich) were added to distilled water to prepare a 100 ml solution. The prepared solution was dropped into a mixed solution of 28% ammonia water (manufactured by Wako Pure Chemical Industries, Ltd.) 100 ml and distilled
触媒(4)の粉末X線回折スペクトルを図4に示す。立方晶構造を持つチタン化合物およびルチル構造を持つ酸化チタンの回折線ピークが観測された。 The powder X-ray diffraction spectrum of the catalyst (4) is shown in FIG. Diffraction line peaks of titanium compound with cubic structure and titanium oxide with rutile structure were observed.
また、触媒(4)の元素分析結果を表1に示す。炭素、窒素および酸素の存在が確認され、熱処理温度1000℃で窒素が反応し、結晶格子内に入ることが確認された。 In addition, Table 1 shows the elemental analysis results of the catalyst (4). The presence of carbon, nitrogen and oxygen was confirmed, and it was confirmed that nitrogen reacted at a heat treatment temperature of 1000 ° C. and entered the crystal lattice.
触媒(4)のBET比表面積は210m2/gであった。The BET specific surface area of the catalyst (4) was 210 m 2 / g.
2.燃料電池用電極の製造
前記触媒(4)を用いた以外は実施例1と同様にして燃料電池用電極(4)を得た。2. Production of Fuel Cell Electrode A fuel cell electrode (4) was obtained in the same manner as in Example 1 except that the catalyst (4) was used.
3.酸素還元能の評価
前記燃料電池用電極(4)を用いた以外は実施例1と同様にして触媒能を評価した。3. Evaluation of oxygen reduction ability Catalytic ability was evaluated in the same manner as in Example 1 except that the fuel cell electrode (4) was used.
図12に、上記測定により得られた電流−電位曲線を示す。 FIG. 12 shows a current-potential curve obtained by the above measurement.
実施例4で作製した触媒(4)は、酸素還元開始電位が0.83V(vs.RHE)、酸素還元電流密度が0.39mA/cm2であった。The catalyst (4) produced in Example 4 had an oxygen reduction starting potential of 0.83 V (vs. RHE) and an oxygen reduction current density of 0.39 mA / cm 2 .
[比較例1]
1.触媒の調製
30%硫酸チタン溶液(和光純薬製)18.24gを蒸留水に加え、100mlの溶液を作成した。作成した溶液を28%アンモニア水(和光純薬製)100mlと蒸留水200mlとの混合溶液に滴下し、水酸化チタンの沈殿を得た。得られた水酸化チタンを含む反応液を遠心分離することによりゲル状の水酸化チタンを得た。ポリビニルアルコール(和光純薬製、平均重合度1000)2.008gを蒸留水50mlに溶解させ、得られたゲル状の水酸化チタン6.5gと混合した。その後、溶媒を除去した。得られた混合粉末を管状炉において、1000℃で3時間、アルゴン雰囲気中で熱処理することにより、燃料電池用電極触媒(以下「触媒(5)」とも記す。)が得られた。[Comparative Example 1]
1. Preparation of catalyst 18.24 g of 30% titanium sulfate solution (manufactured by Wako Pure Chemical Industries, Ltd.) was added to distilled water to prepare a 100 ml solution. The prepared solution was dropped into a mixed solution of 28% ammonia water (manufactured by Wako Pure Chemical Industries, Ltd.) 100 ml and distilled
触媒(5)の粉末X線回折スペクトルを図5に示す。ルチル構造を持つ酸化チタンの回折線ピークのみが観測された。 The powder X-ray diffraction spectrum of the catalyst (5) is shown in FIG. Only the diffraction line peak of titanium oxide having a rutile structure was observed.
また、触媒(5)の元素分析結果を表1に示す。炭素および酸素の存在が確認された。熱処理雰囲気をアルゴンとすると、窒素源がないため、結晶格子内に窒素が入らないことが確認された。 In addition, Table 1 shows the results of elemental analysis of the catalyst (5). The presence of carbon and oxygen was confirmed. When the heat treatment atmosphere was argon, it was confirmed that nitrogen does not enter the crystal lattice because there is no nitrogen source.
触媒(5)のBET比表面積は187m2/gであった。The BET specific surface area of the catalyst (5) was 187 m 2 / g.
2.燃料電池用電極の製造
前記触媒(5)を用いた以外は実施例1と同様にして燃料電池用電極(5)を得た。2. Production of Fuel Cell Electrode A fuel cell electrode (5) was obtained in the same manner as in Example 1 except that the catalyst (5) was used.
3.酸素還元能の評価
前記燃料電池用電極(5)を用いた以外は実施例1と同様にして触媒能を評価した。3. Evaluation of oxygen reduction ability Catalytic ability was evaluated in the same manner as in Example 1 except that the fuel cell electrode (5) was used.
図13に、上記測定により得られた電流−電位曲線を示す。 FIG. 13 shows a current-potential curve obtained by the above measurement.
比較例1で作製した触媒(5)は、酸素還元開始電位が0.75V(vs.RHE)、酸素還元電流密度が、0.04mA/cm2であり、アルゴン雰囲気中で熱処理した場合は、窒素雰囲気中で熱処理した場合に比べ、触媒能が低いことがわかった。The catalyst (5) produced in Comparative Example 1 has an oxygen reduction starting potential of 0.75 V (vs. RHE), an oxygen reduction current density of 0.04 mA / cm 2 , and when heat-treated in an argon atmosphere, It was found that the catalytic ability was lower than when heat treatment was performed in a nitrogen atmosphere.
[比較例2]
1.触媒の調製
30%硫酸チタン溶液18.24g(和光純薬製)を蒸留水に加え、100mlの溶液を作成した。作成した溶液を28%アンモニア水(和光純薬製)100mlと蒸留水200mlとの混合溶液に滴下し、水酸化チタンの沈殿を得た。得られた水酸化チタンを含む反応液を遠心分離することによりゲル状の水酸化チタンを得た。得られたゲル状の水酸化チタン6.5gを有機化合物と混合せず、80℃で真空乾燥させた。得られた粉末を管状炉において、1000℃で3時間、窒素ガス雰囲気中で熱処理することにより、燃料電池用電極触媒(以下「触媒(6)」とも記す。)が得られた。[Comparative Example 2]
1. Preparation of catalyst 18.24 g of 30% titanium sulfate solution (manufactured by Wako Pure Chemical Industries, Ltd.) was added to distilled water to prepare a 100 ml solution. The prepared solution was dropped into a mixed solution of 28% ammonia water (manufactured by Wako Pure Chemical Industries, Ltd.) 100 ml and distilled
触媒(6)の粉末X線回折スペクトルを図6に示す。ルチル構造を持つ酸化チタンの回折線ピークのみが観測された。 The powder X-ray diffraction spectrum of the catalyst (6) is shown in FIG. Only the diffraction line peak of titanium oxide having a rutile structure was observed.
また、触媒(6)の元素分析結果を表1に示す。酸素の存在のみが確認された。そのため、有機化合物を用いない場合は熱処理雰囲気が窒素でも、窒素とは反応せず、結晶格子内に窒素が入らないことが確認された。 In addition, Table 1 shows the elemental analysis results of the catalyst (6). Only the presence of oxygen was confirmed. Therefore, it was confirmed that when no organic compound was used, even if the heat treatment atmosphere was nitrogen, it did not react with nitrogen and nitrogen did not enter the crystal lattice.
触媒(6)のBET比表面積は12m2/gであった。The BET specific surface area of the catalyst (6) was 12 m 2 / g.
2.燃料電池用電極の製造
前記触媒(6)を用いた以外は実施例1と同様にして燃料電池用電極(6)を得た。2. Production of Fuel Cell Electrode A fuel cell electrode (6) was obtained in the same manner as in Example 1 except that the catalyst (6) was used.
3.酸素還元能の評価
前記燃料電池用電極(6)を用いた以外は実施例1と同様にして触媒能を評価した。3. Evaluation of oxygen reduction ability Catalytic ability was evaluated in the same manner as in Example 1 except that the fuel cell electrode (6) was used.
図14に、上記測定により得られた電流−電位曲線を示す。 FIG. 14 shows a current-potential curve obtained by the above measurement.
比較例2で作製した触媒(6)は、酸素還元開始電位が0.60V(vs.RHE)、酸素還元電流密度が0mA/cm2であり、有機化合物を用いない場合は、有機化合物を用いた場合と比べ、触媒能が非常に低いことがわかった。The catalyst (6) produced in Comparative Example 2 has an oxygen reduction starting potential of 0.60 V (vs. RHE), an oxygen reduction current density of 0 mA / cm 2 , and an organic compound is used when no organic compound is used. It was found that the catalytic ability was very low compared to the case where
[比較例3]
1.触媒の調製
30%硫酸チタン溶液(和光純薬製)18.24gを蒸留水に加え、100mlの溶液を作成した。作成した溶液を28%アンモニア水(和光純薬製)100mlと蒸留水200mlとの混合溶液に滴下し、水酸化チタンの沈殿を得た。得られた水酸化チタンを含む反応液を遠心分離することによりゲル状の水酸化チタンを得た。ポリビニルアルコール(和光純薬製、平均重合度1000)2.008gを蒸留水50mlに溶解させ、得られたゲル状の水酸化チタン6.5gと混合した。その後、溶媒を除去した。得られた混合粉末を管状炉において、1200℃で3時間、窒素ガス雰囲気中で熱処理することにより、燃料電池用電極触媒(以下「触媒(7)」とも記す。)が得られた。[Comparative Example 3]
1. Preparation of catalyst 18.24 g of 30% titanium sulfate solution (manufactured by Wako Pure Chemical Industries, Ltd.) was added to distilled water to prepare a 100 ml solution. The prepared solution was dropped into a mixed solution of 28% ammonia water (manufactured by Wako Pure Chemical Industries, Ltd.) 100 ml and distilled
触媒(7)の粉末X線回折スペクトルを図7に示す。ルチル構造を持つ酸化チタンの回折線ピークは確認されず、立方晶構造を持つチタン炭窒酸化物の回折線ピークのみが観測された。 The powder X-ray diffraction spectrum of the catalyst (7) is shown in FIG. The diffraction line peak of titanium oxide having a rutile structure was not confirmed, and only the diffraction line peak of titanium oxycarbonitride having a cubic structure was observed.
また、触媒(7)の元素分析結果を表1に示す。炭素、窒素および酸素の存在が確認され、熱処理温度が1200℃ではより窒素と反応し、構造内に窒素が多く入り、酸素が少なくなる傾向が確認された。 In addition, Table 1 shows the elemental analysis results of the catalyst (7). The presence of carbon, nitrogen and oxygen was confirmed, and when the heat treatment temperature was 1200 ° C., it reacted more with nitrogen, and a tendency was found that more nitrogen entered the structure and less oxygen.
触媒(7)のBET比表面積は162m2/gであった。The BET specific surface area of the catalyst (7) was 162 m 2 / g.
2.燃料電池用電極の製造
前記触媒(7)を用いた以外は実施例1と同様にして燃料電池用電極(7)を得た。2. Production of Fuel Cell Electrode A fuel cell electrode (7) was obtained in the same manner as in Example 1 except that the catalyst (7) was used.
3.酸素還元能の評価
前記燃料電池用電極(7)を用いた以外は実施例1と同様にして触媒能を評価した。3. Evaluation of oxygen reduction ability Catalytic ability was evaluated in the same manner as in Example 1 except that the fuel cell electrode (7) was used.
図15に、上記測定により得られた電流−電位曲線を示す。 FIG. 15 shows a current-potential curve obtained by the above measurement.
比較例3で作製した触媒(7)は、酸素還元開始電位が0.73V(vs.RHE)、酸素還元電流密度が0mA/cm2であり、熱処理温度を1000℃から1200℃にすることで、触媒能が低下することがわかった。The catalyst (7) produced in Comparative Example 3 has an oxygen reduction starting potential of 0.73 V (vs. RHE), an oxygen reduction current density of 0 mA / cm 2 , and a heat treatment temperature of 1000 ° C. to 1200 ° C. It was found that the catalytic ability was lowered.
[比較例4]
1.触媒の調製
酸化チタン(昭和電工製、スーパータイタニアF6)3.52gとカーボン(キャボット社製、Vulcan72)1.32gとを乳鉢で十分に粉砕して混合した。この混合粉末を管状炉において、1000℃で3時間、窒素雰囲気中で熱処理した。その後、得られた粉末1.0gを管状炉において、1000℃で3時間、2体積%の酸素ガス、4体積%の水素ガスおよび94体積%の窒素ガスからなる窒素ガス含有ガス雰囲気下で熱処理することにより、燃料電池用電極触媒(以下「触媒(8)」とも記す。)が得られた。[Comparative Example 4]
1. Preparation of catalyst 3.52 g of titanium oxide (manufactured by Showa Denko, Super Titania F6) and 1.32 g of carbon (manufactured by Cabot, Vulcan 72) were sufficiently ground and mixed in a mortar. This mixed powder was heat-treated in a tube furnace at 1000 ° C. for 3 hours in a nitrogen atmosphere. Thereafter, 1.0 g of the obtained powder was heat-treated in a tube furnace at 1000 ° C. for 3 hours in a nitrogen gas-containing gas atmosphere composed of 2 volume% oxygen gas, 4 volume% hydrogen gas, and 94 volume% nitrogen gas. As a result, an electrode catalyst for a fuel cell (hereinafter also referred to as “catalyst (8)”) was obtained.
触媒(8)の粉末X線回折スペクトルを図8に示す。ルチル構造を持つ酸化チタンの回折線ピークのみが観測された。 The powder X-ray diffraction spectrum of the catalyst (8) is shown in FIG. Only the diffraction line peak of titanium oxide having a rutile structure was observed.
また、触媒(8)の元素分析結果を表1に示す。酸素の存在のみが確認された。そのため、この合成条件ではカーボンが酸化チタンと反応することはなく、熱処理雰囲気の窒素も構造内に入らないということがわかった。 In addition, Table 1 shows the elemental analysis results of the catalyst (8). Only the presence of oxygen was confirmed. Therefore, it was found that under this synthesis condition, carbon does not react with titanium oxide, and nitrogen in the heat treatment atmosphere does not enter the structure.
触媒(8)のBET比表面積は8m2/gであった。The BET specific surface area of the catalyst (8) was 8 m 2 / g.
2.燃料電池用電極の製造
前記触媒(8)を用いた以外は実施例1と同様にして燃料電池用電極(8)を得た。2. Production of Fuel Cell Electrode A fuel cell electrode (8) was obtained in the same manner as in Example 1 except that the catalyst (8) was used.
3.酸素還元能の評価
前記燃料電池用電極(8)を用いた以外は実施例1と同様にして触媒能を評価した。3. Evaluation of oxygen reduction ability Catalytic ability was evaluated in the same manner as in Example 1 except that the fuel cell electrode (8) was used.
図16に、上記測定により得られた電流−電位曲線を示す。 FIG. 16 shows a current-potential curve obtained by the above measurement.
比較例4で作製した触媒(8)は、酸素還元開始電位が0.66V(vs.RHE)、酸素還元電流密度が0.02mA/cm2であり、この合成条件では触媒としての酸素還元能が非常に低いことがわかった。The catalyst (8) produced in Comparative Example 4 has an oxygen reduction starting potential of 0.66 V (vs. RHE) and an oxygen reduction current density of 0.02 mA / cm 2. Under this synthesis condition, the oxygen reduction ability as a catalyst Was found to be very low.
前記実施例および比較例で得られた燃料電池用電極触媒の酸素還元開始電位および酸素還元電流密度を表2にまとめた。 Table 2 summarizes the oxygen reduction starting potential and the oxygen reduction current density of the fuel cell electrode catalysts obtained in the Examples and Comparative Examples.
本発明の製造方法は、窒化反応を従来より低い反応温度で進行させることができるため、燃料電池用電極触媒の製造コストを削減することができる。 The production method of the present invention can cause the nitriding reaction to proceed at a reaction temperature lower than that of the prior art, and thus can reduce the production cost of the fuel cell electrode catalyst.
Claims (9)