Description

  The present invention relates to a binding tape for a wire harness and a manufacturing method thereof, and more particularly to a binding tape for a wire harness having a laminated structure and a manufacturing method thereof.

Conventionally, what is called a wire harness in which electric wires are bundled in a predetermined shape is used for wiring of an automobile.
Such wire harnesses are usually installed in narrow concealed areas such as in the engine room or between the body and interior materials, and vibrate due to engine vibration or vibration during travel, and contact with surrounding walls. As a result, there is a problem that a hitting sound and a scratching sound are generated.

As this wire harness bundling tape (hereinafter also simply referred to as “bundling tape”), a material based on a polyvinyl chloride tape is generally used. In the present invention, those using a cotton non-woven fabric as a base material are used.
In such a binding tape, by forming the base material layer with a non-woven fabric, it becomes a cushion when the wire harness comes into contact with the surrounding wall or the like, and it is possible to prevent the hitting sound and scratching sound.
Conventionally, the binding tape has been provided to the market in the form of a tape roll that has been wound in the same manner as other adhesive tapes, etc., and the adhesive layer provided on the surface of the base material layer is provided on the inside of the tape. It is offered to the market in a state of being adhered to the back surface of the base material layer.
And when used, it is taken out from the outside and used in the same manner as other adhesive tapes, and is used by being peeled off from the back side of the inner binding tape to which the outer binding tape is bonded.

For this reason, if the base material layer is made of non-woven fabric for the purpose of exerting the silencing function as described above, the binding tape may be removed when the binding tape is taken out depending on the adhesive strength between the pressure-sensitive adhesive layer and the base material layer. There is a risk of causing a phenomenon called “layer cracking” in which the base layer of the inner binding tape to which is adhered is separated into two layers in the thickness direction.
Even if such a “layer crack” does not occur, if the adhesive force between the pressure-sensitive adhesive layer and the base material layer is strong, a strong force is required to take out the binding tape, and it is necessary to bind the wire harness. There is a risk of generating a great deal of labor.

In order to solve such a problem, the following Patent Document 1 describes that a resin layer is provided outside the base material layer, and further a release agent layer is provided outside the resin layer.
In this way, when the binding tape is taken out by providing a release agent layer on the back side, the peelability is improved, so that "layer cracking" can be suppressed and labor required for binding can be reduced. Can be planned.

On the other hand, when tying wire harnesses, the wrapping tape is wound in a winding method called “half wrap” that winds while wrapping about half of the tape width, or the wrapping tape is wound several times. In some cases, simply increasing the peelability of the release agent layer may cause a problem in the binding force of the wire harness.
Therefore, it has been conventionally required to finely adjust the adhesive force acting between the pressure-sensitive adhesive layer and the back surface of the binding tape.

  On the other hand, in the following Patent Document 1, a pressure-sensitive adhesive layer is directly laminated on the surface of a base material layer using a nonwoven fabric, and the base material layer is provided with through holes. Therefore, the pressure-sensitive adhesive easily penetrates between the fibers of the non-woven fabric or this through hole. For example, the pressure-sensitive adhesive penetrates into the non-woven fabric constituting the base material layer depending on the conditions when forming the pressure-sensitive adhesive layer. There is a possibility of changing the thickness of the pressure-sensitive adhesive layer.

If the thickness of the pressure-sensitive adhesive layer changes, it not only affects the adhesive strength between the pressure-sensitive adhesive layer and the back surface of the binding tape, but also affects the adhesive strength to the wire harness.
That is, the conventional binding tape has a problem that it is difficult to stabilize the adhesive force.

Japanese Patent Laid-Open No. 11-335637

  This invention makes it a subject to provide the binding tape which can exhibit the stable adhesive force, and the manufacturing method for manufacturing such a binding tape.

The present invention relating to a binding tape for a wire harness for solving the above-described problem has a laminated structure including a base material layer using a nonwoven fabric and an adhesive layer using an adhesive, A wire harness binding tape in which the pressure-sensitive adhesive layer is arranged on the surface side to be bonded to the wire harness, and a film layer is provided in which a resin film is used between the pressure-sensitive adhesive layer and the base material layer. In addition , a film layer made of a resin film is also provided on the back side of the base material layer .

Moreover, the present invention relating to a method for producing a binding tape for solving the above-mentioned problem is that a laminated structure having a base material layer using a nonwoven fabric and an adhesive layer using an adhesive is formed. A binding tape manufacturing method for manufacturing a wire harness binding tape in which the pressure-sensitive adhesive layer is arranged on the surface side to be bonded to the wire harness, on the surface side and back side of the nonwoven fabric constituting the base material layer, A film layer is formed by laminating resin films, and then the pressure-sensitive adhesive layer is formed by covering the surface of the film layer on the surface side with a pressure-sensitive adhesive.

According to the present invention, since the film layer formed by using the resin film is further provided between the pressure-sensitive adhesive layer and the base material layer, the pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer is the base material layer. It is prevented that the thickness of the pressure-sensitive adhesive layer is changed by entering between the fibers of the nonwoven fabric constituting the same.
Therefore, the stable adhesive force is exhibited by the binding tape for wire harnesses.
Further, when the pressure-sensitive adhesive enters between the fibers of the nonwoven fabric, voids between the fibers may be reduced and the noise reduction effect may be reduced. However, the present invention is also expected to prevent such a noise reduction effect from being reduced. can do.

The a) side view of the binding tape (tape roll) for wire harnesses of one Embodiment, and b) sectional drawing which shows the cross-section of a binding tape. Schematic which shows the formation method (adhesive coating method) of an adhesive layer. Schematic which shows the muffling property evaluation method. Sectional drawing (photograph) which showed a mode that a base material layer (nonwoven fabric) was impregnated with an adhesive. Explanatory drawing of FIG.

A preferred embodiment of the present invention will be described below with reference to FIG.
FIG. 1 a) on the left side of the front view in FIG. 1 shows a tape roll 1 in which a wire harness binding tape 10 of the present embodiment (hereinafter also referred to as “binding tape 10”) is wound around a core 2. FIG. 2 is a side view of the wrapping tape 10 viewed from one side and shows a state in which the binding tape 10 is pulled out from the outside.
On the other hand, FIG. 1 b) on the right side of the front view is a cross-sectional view (enlarged view) taken along the line XX ′ in FIG.

As shown in FIG. 1 a), the binding tape 10 according to the present embodiment has a surface that is bonded to a wire harness that is an adherend and is constituted by an adhesive layer 11. A film layer 12 made of a resin film is provided at a position in contact with the pressure-sensitive adhesive layer 11 on the back side.
Further, the portion in contact with the film layer 12 on the back side of the film layer 12 is a base material layer 13 using a nonwoven fabric, and the film layer 14 using a resin film on the back side of the base material layer 13. Is provided.
That is, the base material layer 13 is sandwiched between two film layers, that is, the film layer 12 on the pressure-sensitive adhesive layer 11 side and the film layer 14 that is the rearmost surface of the binding tape 10. Is provided.

The pressure-sensitive adhesive layer 11 can be formed using a pressure-sensitive adhesive that is used for forming a pressure-sensitive adhesive layer in a general wire harness binding tape.
For example, it can be formed using an acrylic pressure-sensitive adhesive, a rubber-based pressure-sensitive adhesive, or a silicone-based pressure-sensitive adhesive, and can be appropriately selected from the viewpoint of required adhesive strength.
If the thickness of the pressure-sensitive adhesive layer 11 is too thin, there is a possibility of causing a problem in adhesion to the wire harness. If the thickness is excessively thick, protrusion of the tape roll 1 to the side surface or dust on the side surface may occur. May cause problems such as adhesion.
For this reason, the thickness of the pressure-sensitive adhesive layer 11 is usually set in a range of 10 μm to 200 μm, and preferably in a range of 30 μm to 100 μm.

The film layer 12 on the back side of the pressure-sensitive adhesive layer 11 (hereinafter also referred to as “first film layer 12”) and the film layer 14 (hereinafter referred to as “second film layer”) provided on the back side of the base material layer 13 further. The same resin film may be used, or different resin films may be used.
However, these are preferably bonded to the base material layer 13 in a good bonding state, and a film using a thermoplastic resin can be suitably used as a constituent material.
By using such a thermoplastic resin film, a strong adhesive force can be imparted to the nonwoven fabric constituting the base material layer 13 by a general method such as a heat lamination method.

Further, as will be described later, the nonwoven fabric constituting the base material layer 13 is required to be capable of imparting appropriate hand cutting properties (easy tearing) to the binding tape 10.
Therefore, each material is used so that the resin film used for the first film layer 12 and the second film layer 14 does not impair the good hand cutting performance exhibited by the nonwoven fabric constituting the base material layer 13. Preferably, the thickness is selected.
For example, as a material constituting the first film layer 12 and the second film layer 14 in that not only the heat lamination is easy because the melting point is low and the flexibility is high, but also the flexibility of the binding tape 10 can be revealed. Is preferably a polyethylene resin film.
Especially, the film formed with the low density polyethylene resin is suitable irrespective of resin kind, such as a linear low density polyethylene resin and a low density polyethylene resin having a long chain branch formed by a high pressure method.

The thickness is preferably 10 to 50 μm.
That is, the low-density polyethylene resin film is inherently rich in flexibility and has a low risk of damaging the flexibility of the binding tape 10. However, if it is 50 μm or less, the flexibility of the binding tape is more reliably maintained. It can be made.
In addition, a low-density polyethylene resin film having a very thin thickness is difficult to obtain, and a film having a thickness of 10 μm or more can be suitably used because it needs to be handled carefully so as not to be broken.
In addition, the 2nd film layer 14 which comprises the backmost side of the binding tape 10 becomes a part exposed to the surface of the said binding part, when a wire harness is bound.
Therefore, for example, when durability (wear resistance) against abrasion due to vibration or the like is required, the second film layer 14 is preferably formed to a thickness of 35 μm or more, preferably 40 μm or more.

  By using such a polyethylene resin film as a constituent material for the first film layer 12 and the second film layer 14, it is possible to impart cushioning properties to the binding tape 10 and expect a more excellent silencing effect. Can do.

  In the first film layer 12, when the base material layer 13 and the pressure-sensitive adhesive layer 11 are laminated, the pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer 11 enters between the fibers of the nonwoven fabric constituting the base material layer 13. The second film layer 14 is, for example, used for bundling a wire harness, and then the adhesive layer of the outer bundling tape wound by heat in the engine room. The pressure-sensitive adhesive has a function of preventing softening and entering between fibers of the nonwoven fabric constituting the base material layer of the lower binding tape.

That is, in the conventional binding tape, although the resin layer corresponding to the second film layer 14 is provided, nothing is provided in the portion corresponding to the first film layer 12, and the adhesive layer and the base material layer are not adhered. It forms so that it may be in the state which has contacted the agent layer directly.
Therefore, when laminating the base material layer and the pressure-sensitive adhesive layer, the pressure-sensitive adhesive enters between the fibers of the nonwoven fabric constituting the base material layer, and controls the thickness of the pressure-sensitive adhesive layer that affects the adhesion to the wire harness. Is difficult.
Also, for the nonwoven fabric constituting the base material layer, when the pressure-sensitive adhesive is filled in the gaps between the fibers or when pressure is applied in the thickness direction, the back-side fibers enter from the pressure-sensitive adhesive layer side. There is a risk of being adhered to the agent.
Therefore, there exists a possibility that the space | gap part effective for noise reduction may be reduced by filling with an adhesive, or a fiber may adhere | attach in a thickness direction and cushion property may be impaired.
Furthermore, in the conventional binding tape, the adhesive may enter the base material layer from the pressure-sensitive adhesive layer side due to heat in the engine room and reduce the thickness of the binding tape. If the wire harness is fixed at the binding portion by the tape, there is a possibility that the fixing is loosened during the period of use of the automobile.

On the other hand, the binding tape of the present embodiment has the first film layer 12 so that the adhesive enters between the non-woven fibers constituting the base material layer by laminating the base material layer and the adhesive layer. Therefore, the thickness of the pressure-sensitive adhesive layer 11 which is an important factor for controlling the adhesive force can be accurately controlled.
Moreover, even when pressure is applied in the thickness direction, it is easy to restore the original thickness of the nonwoven fabric after the pressure is released because the fibers are less likely to be bonded by the adhesive. Become.

The second film layer 14 is effective as well as the first film layer 12 in terms of the function of maintaining such a silencing performance over a long period of time, but is effective in controlling the thickness of the pressure-sensitive adhesive layer 11. The function of the first film layer 12 is important in that the initial silencing performance and cushioning properties can be made superior to those of conventional binding tapes.
In the present invention, the second film layer 14 is not an indispensable component, but the excellent silencing and cushioning properties exhibited by the first film layer 12 can be achieved through the storage period and binding of the tape roll 1. The second film layer 14 also has an important meaning in that it can maintain the excellent silencing performance and cushioning properties that have been exhibited from the beginning to the stage after the tape 10 is overlaid on the wire harness. Is.

Moreover, since the phenomenon of thickness is prevented by providing this 2nd film layer 14, even if it fixes the wire harness by a bundling part, a possibility that fixation may loosen during use can be suppressed.
In addition, this 2nd film layer 14 can also aim at suppression of a "layer crack" similarly to the conventional binding tape.

The base material layer 13 is, for example, a nonwoven fabric formed by binding filaments having a fineness of 0.5 to 50 dtex with a binder and having a basis weight of 30 to 100 g / m ² and a thickness of 0.2 to 1.0 mm. Can be configured.
Moreover, as said filament, synthetic resin fibers, such as a polyester filament, a polypropylene filament, and a nylon filament; Natural origin fibers, such as cotton, a pulp, a cellulose, and rayon, can be used, and these mixed products can also be used as the said nonwoven fabric.
In addition, in order to suppress problems such as “layer cracking”, a non-woven fabric for forming the base material layer 13 is also a non-woven fabric that has been subjected to a treatment called “heat embossing” or the like interspersed with spot fusion spots. Is available as

Note that the binding tape 10 according to the present embodiment is used for binding a wire harness, and flame retardance is required as an important characteristic in addition to adhesive strength and sound deadening properties.
For example, various flame retardants such as phosphorous flame retardants such as red phosphorus and ammonium phosphate; metal hydrate flame retardants such as magnesium hydroxide and aluminum hydroxide; expanded graphite; In addition, it may be blended with the constituent materials of the first film layer 12, the base material layer 13, and the second film layer 14 so that the binding tape 10 exhibits flame retardancy. For example, it adheres to the surface of the nonwoven fabric fiber constituting the base material layer 13 and carries it, or arranges it in the space between the fibers without adhering and seals it with the film layers 12 and 14 from both sides. For example, the bundling tape 10 may be made to exhibit flame retardancy.

  Although not described in detail here, conventionally known matters such as the material and shape of the binding tape can be used for the binding tape of this embodiment.

Next, an example of the binding tape manufacturing method for manufacturing the above-described binding tape 10 will be described.
First, the base material layer 13 is prepared.
The base material layer 13 may be made of a nonwoven fabric used for the structure by a conventionally known manufacturing method, or a commercially available product suitable for constituting the base material layer 13 may be purchased and used as it is. good.
In addition, if necessary, a hot embossing process or the like may be applied to the nonwoven fabric to form the base material layer 13.

Next, a resin film for constituting the first film layer 12 and the second film layer 14 is heat laminated to the nonwoven fabric constituting the base material layer 13, and the first film layer 12 / base material layer 13 / second A three-layer laminated structure of the film layer 14 is formed.
At this time, two resin films may be heat laminated simultaneously on both sides of the nonwoven fabric to form the first film layer 12 and the two film layers 14 at the same time, and the two resin films are heat laminated one by one. Then, after one of the first film layer 12 and the second film layer 14 is formed first, the other may be formed later.
In addition, adjustment of the adhesive force of the 1st film layer 12 and the base material layer 13 and the adhesive force of the base material layer 13 and the 2nd film layer 14 can be aimed at by the lamination temperature and pressure at this time.
As described above, the second film layer 14 is not an essential component in the present invention.
Therefore, when manufacturing a binding tape that does not have the second film layer 14, the first film layer 12 may be formed by laminating a resin film only on one side of the nonwoven fabric.

Separately from this, the pressure-sensitive adhesive for forming the pressure-sensitive adhesive layer 11 is adjusted, and this pressure-sensitive adhesive is coated on a PET film or the like that has been subjected to a release treatment so as to have a predetermined thickness. By transferring the film onto the surface of the first film layer 12, the binding tape 10 of this embodiment can be obtained.
Moreover, while preparing the nonwoven fabric formed in the elongate strip | belt shape and a resin film, and carrying out the heat lamination of the base material layer 13 and the 1st film layer 12 (2nd film layer 14) continuously, the said adhesive By continuously performing coating and transfer of the above, a long strip-shaped original fabric sheet is produced, the original fabric sheet is wound around a winding core into a roll shape, and slit processing to a predetermined width is performed to produce a tape roll 1 It can be.

In the transfer of the pressure-sensitive adhesive, in the conventional binding tape, the thickness of the pressure-sensitive adhesive layer may be changed due to fluctuations in the transfer pressure. Since the first film layer 12 prevents the nonwoven fabric from being impregnated, the thickness variation of the pressure-sensitive adhesive layer can be prevented.
Therefore, it is possible to suppress the adhesive strength variation from being formed on the binding tape 10.
Moreover, in the binding tape manufacturing method of the present embodiment, the transfer method as exemplified above is not adopted, but the adhesive or the coating liquid obtained by diluting the adhesive component with an organic solvent or the like is used as the first film layer. It is also possible to form the pressure-sensitive adhesive layer 11 by directly coating the surface of 12.
Therefore, in the binding tape manufacturing method of the present embodiment, it is possible to prevent generation of extra materials for once forming a pressure-sensitive adhesive layer such as a PET film subjected to a release treatment.

As described above, according to the binding tape manufacturing method of the present embodiment, an effect that a binding tape capable of exhibiting a stable adhesive force can be easily produced is exhibited.
In addition, regarding the binding tape manufacturing method, conventionally known technical matters can be employed as long as the effects of the present invention are not significantly impaired.

  EXAMPLES Next, although an Example is given and this invention is demonstrated in more detail, this invention is not limited to these.

In order to produce a binding tape, a base material layer was formed using the following nonwoven fabric.
(Nonwoven fabric)
A non-woven fabric in which rayon fibers (about 7 mm in length) having a diameter of about 10 to 20 μm and pulp fibers (about 3 mm in length) are wet-mixed so as to have a mass ratio of 1: 1. Three types of nonwoven fabrics were prepared: ² (nonwoven fabric 1), 58 g / m ² (nonwoven fabric 2), and 60 g / m ² (nonwoven fabric 3).

(Film layer)
Three types of low density polyethylene resin (PE) films having a thickness of 15 μm, 20 μm, and 40 μm were prepared for lamination on the nonwoven fabric.

(Laminated)
No. 1-No. In order to produce 9 binding tapes, a laminated sheet was produced by heat laminating a PE film and a nonwoven fabric so as to have the constitution shown in Table 1 below.
The nip pressure during lamination is also shown in the table below.

A pressure-sensitive adhesive layer is formed on the laminated sheet by reverse coating as shown in FIG. 1-No. 9 binding tapes were produced.
That is, a side dam (not shown) is provided to bring the adhesive AD into contact with the coating roller R1 to form an adhesive reservoir, and the coating roller R1 is rotated to carry the adhesive on the surface, The pressure-sensitive adhesive carried was made uniform by a thickness regulating member B such as a blade and transferred onto the surface of the laminated sheet L to form a pressure-sensitive adhesive layer.
At this time, the carrying amount of the adhesive was adjusted by adjusting the gap (gap G) between the thickness regulating member B and the coating roller R1.

In addition, No. 1-No. For No. 8, the gap G was set so that the pressure-sensitive adhesive had a loading amount of 80 g / m ² . For No. 9, the gap G was set so that the pressure-sensitive adhesive had a loading amount of 55 g / m ² .
In each case, the adhesive adhesion amount per unit area was calculated by subtracting the mass of the laminated sheet from the mass after forming the adhesive layer.
Moreover, the thickness of the adhesive layer was calculated by subtracting the thickness of the laminated sheet from the total thickness including the adhesive layer.
The results are shown in Table 2 below.

  As can be seen from Table 2, the amount of the pressure-sensitive adhesive carried is almost the target value by adjusting the gap G, but no film layer is provided between the pressure-sensitive adhesive layer and the base material layer. No. 1-No. 7 shows that the thickness of the pressure-sensitive adhesive layer is greatly reduced.

(Various evaluations)
No. With respect to the binding tapes 1 to 9 and the commercially available binding tape, the muffling property, end tear resistance, hand cutting property, and adhesive strength to the SUS plate were evaluated.

(Silence)
In addition, about muffling property, evaluation was implemented using the apparatus as shown in FIG.
That is, a hammer HM having an iron ball with a mass of 28 g attached to one end of a stainless steel (SUS) round bar having a length of 31.2 cm and a thickness of about 5 mm is swung in a pendulum shape with the iron ball facing down. In this state, it is supported in a state suspended from the base F, and this is obtained by attaching two binding tapes on the surface of a plate material (ABS plate) made of acrylonitrile / butadiene / styrene copolymer. Set the ABS plate so that the surface to which the binding tape is attached is vertical, and when the previous hammer HM is in the natural state, the binding tape application position is in contact with the iron ball part. The hammer HM is separated from the binding tape attaching position so that the angle from the natural state becomes 10 degrees, and the iron ball is separated from this position without applying extra force. Blow added to S plate (binding tape application position), it was microphone measurements to evaluate the sound deadening qualities and the amount of the impact sound has been set to the position of the front 20cm from the ABS plate.
At this time, a polyvinyl chloride adhesive tape and a paper adhesive tape were wrapped around the iron bar portion of the hammer to prevent reverberation from the hammer.

(End crack resistance)
The end tear resistance (Method B) of JIS C 2151-2006 was determined for workability (hand cutting property) when tearing the tape by hand.
In addition, the tape width of each binding tape was unified to 19 mm and evaluated.

(Hand cutting)
Actually, the binding tape was torn off by hand, and the ease of tearing was evaluated by touch.
Those that could be easily broken by hand were determined as “◯”, and those that were difficult to tear were determined as “Δ”.

About adhesive force, 180 degree | times peeling adhesive force after affixing on a SUS board based on JISZ0237-2000 was measured.
The above evaluation results are shown in Table 3 below together with the thickness of the binding tape.

From this table, the binding tape No. 1 in which a film layer is provided between the pressure-sensitive adhesive layer and the base material layer. 8 and 9 show that high adhesive strength is obtained.
In addition, “commercially available products” are those in which a film layer or the like is not provided between the pressure-sensitive adhesive layer and the base material layer (nonwoven fabric), and are practically used in places where noise reduction is considered. No. The bundling tapes 8 and 9 have the same silencing and adhesive properties as the “commercial product”, but are thinner than the “commercial product” and have low resistance to end tearing.
That is, when one tape of the same length is used, this No. The bundling tapes 8 and 9 can reduce the winding diameter and are excellent in handleability.
Furthermore, since the resistance to tearing is low, the hand cutting property is also good, and the workability in bundling wire harnesses can be improved.

Next, the film layer which consists of a low density PE film was formed on both surfaces with the above "nonwoven fabric 1" and "nonwoven fabric 3", and the laminated sheet of the 3 layer structure of a film layer / base material layer / film layer was produced.
The film layer on the side of the pressure-sensitive adhesive layer had a thickness of 15 μm, and the film layer on the back surface had a thickness shown in Table 4.
An adhesive layer was formed on this laminated sheet by the method shown in FIG. 10-No. 21 binding tapes were produced.
At this time, the gap was adjusted so that the carrying amount of the pressure-sensitive adhesive layer became the “target value” shown in Table 4, and the “carrying amount” almost as the target when the pressure-sensitive adhesive layer was formed was obtained.

In addition, this No. 10-No. Thickness (mm), mass per unit area (g / m ² ), silence (dB), end tear resistance (N / 19 mm), adhesive strength to SUS plate (N / 19 mm) Evaluation was conducted.
Furthermore, this No. 10-No. For the 21 binding tapes, an evaluation of wear resistance was also added.
Specifically, an abrasion test based on ISO-6722-1 was performed using a scrape type abrasion resistance tester manufactured by Swedish TVAB.
A load of 400 g was set on the reciprocating slider, and a wear test was performed with a piano wire having a diameter of 0.25 mm attached to the tip.
Note that the test specimen was a wrapping tape of 19 mm in width wrapped around a metal rod with a diameter of 6 mm, and the evaluation was conducted between the metal rod and the piano wire attached to the tip of the slider. It was done by measuring the number of times until it was observed.
The same evaluation was performed for the above-mentioned “commercially available products”.
The results are shown in Table 5.

  From the above table, it can be seen that by providing a film layer between the pressure-sensitive adhesive layer and the base material layer, the thickness of the pressure-sensitive adhesive layer is stabilized and a stable adhesive force is exhibited.

Next, a non-woven fabric 3 (weight per unit: 60 g / m ² ) having a film layer formed of a low-density polyethylene resin film of 15 μm on the back side was used to form a gap of 170 μm and 200 μm using an apparatus as shown in FIG. Adhesives (viscosity at room temperature: about 7500 mPa) were applied at three coating thicknesses of 290 μm.
Then, the separator for protecting this adhesive layer was laminated | stacked on the surface of the adhesive layer, and the binding tape with a separator was produced.
The obtained binding tape was cut with a semi-cutter, and the cut section was observed with a microscope.

The results are shown in FIG.
In addition, when it demonstrates referring FIG. 5 which showed the mode of each layer in FIG. 4 typically, in this cross-sectional photograph (FIG. 4), a separator, an adhesive layer, a base material layer, a back side in order from the lower layer side. A film layer is observed.
And since the film layer is not provided between the adhesive layer and the base material layer, the area | region (impregnation area | region) which the base material layer impregnated with the adhesive from the adhesive layer side is formed.
Further, from FIG. 4, it is expected to effectively work in silencing as the gap becomes thicker when the adhesive is applied, that is, as the amount of the adhesive carried per unit area increases. It can be seen that non-impregnated regions (regions with voids between fibers that are not impregnated with adhesive) are reduced.
Moreover, the pressure-sensitive adhesive used at this time is impregnated in the nonwoven fabric constituting the base material layer although it has a considerably high viscosity of about 7500 mPa as described above.

  Considering this, in the conventional binding tape, for example, even if the gap is adjusted to increase the thickness of the pressure-sensitive adhesive layer for the purpose of improving the adhesive force, the pressure-sensitive adhesive is impregnated in the base material layer. It can be understood that it is difficult to obtain the desired thickness of the pressure-sensitive adhesive layer, and that there is a risk that the sound deadening property may be lowered in exchange for the improvement of the adhesive force.

That is, according to the present invention, the thickness of the pressure-sensitive adhesive layer can be controlled simply by adjusting the gap, and not only the adhesive force is easily adjusted, but also between the fibers of the nonwoven fabric constituting the base material layer. It can be seen that an excellent sound deadening property is exhibited when the adhesive is not impregnated in the voids.
Furthermore, the adhesive layer is not impregnated in the base material layer, and all of it functions for the adhesiveness (adhesive strength) of the binding tape, so the amount of adhesive used can be reduced and the base material layer is configured more than necessary. It can also be seen that sufficient thickness reduction can be achieved without increasing the thickness of the nonwoven fabric, so that the thickness of the base material layer can be reduced.
Therefore, according to the present invention, it can be seen that the adhesive force is stabilized and the tape roll of the binding tape can be reduced in size and weight.

10: Binding tape, 11: Adhesive layer, 12: Film layer, 13: Base material layer, 14 (Back side) film layer

Claims (4)

A laminated structure having a base material layer using a non-woven fabric and a pressure-sensitive adhesive layer using a pressure-sensitive adhesive is formed, and the wire is provided with the pressure-sensitive adhesive layer on the surface side to be bonded to the wire harness A binding tape for a harness,
A film layer is used in which a resin film is used between the pressure-sensitive adhesive layer and the base material layer, and a film layer in which a resin film is used on the back side of the base material layer is provided , The said film layer is formed by heat-laminating the said resin film on both surfaces of the said nonwoven fabric, The binding tape for wire harnesses characterized by the above-mentioned .   The wire harness binding tape according to claim 1, wherein a film layer between the base material layer and the pressure-sensitive adhesive is composed of a polyethylene resin film. A laminated structure having a base material layer using a non-woven fabric and a pressure-sensitive adhesive layer using a pressure-sensitive adhesive is formed, and the wire is provided with the pressure-sensitive adhesive layer on the surface side to be bonded to the wire harness A binding tape manufacturing method for manufacturing a binding tape for a harness,
After the resin film is laminated by heat lamination on the surface side and the back side of the nonwoven fabric constituting the base material layer to form a film layer, the surface of the film layer on the surface side is coated with an adhesive and the adhesive A method for producing a binding tape, comprising forming an agent layer. Binding tape manufacturing method according to claim 3, wherein the resin film of the surface side is polyethylene resin film.