JP5583649B2 - Golf ball - Google Patents

Description

  The present invention relates to a golf ball. Specifically, the present invention relates to a multi-piece golf ball having a center, an intermediate layer, and a cover.

  Flight performance is important for golf balls. The flight distance correlates with the velocity of the ball immediately after hitting. This speed correlates with the resilience performance. Various proposals have been made regarding resilience performance.

  JP-A-2006-223874 discloses a golf ball having a center, a first intermediate layer, a second intermediate layer, and a cover. The restitution coefficient of the sphere composed of the center and the first intermediate layer is larger than the restitution coefficient of the center. The restitution coefficient of the sphere composed of the center, the first intermediate layer, and the second intermediate layer is larger than the restitution coefficient of the sphere composed of the center and the first intermediate layer. The restitution coefficient of the golf ball is larger than the restitution coefficient of a sphere composed of the center, the first intermediate layer, and the second intermediate layer.

  JP-A-2006-223875 discloses a golf ball having a center, a first intermediate layer, a second intermediate layer, and a cover. The restitution coefficient of the sphere composed of the center, the first intermediate layer, and the second intermediate layer is larger than the restitution coefficient of the golf ball. The restitution coefficient of the sphere composed of the center and the first intermediate layer is larger than the restitution coefficient of the sphere composed of the center, the first intermediate layer, and the second intermediate layer. The restitution coefficient of the center is larger than the restitution coefficient of the sphere composed of the center and the first intermediate layer.

  Japanese Patent Application Laid-Open No. 2006-230661 discloses a golf ball suitable for a golfer having a low head speed. This golf ball includes a core, an intermediate layer, and a cover. In this golf ball, a high resilience material is used for the intermediate layer.

JP 2006-223874 A JP 2006-223875 A JP 2006-230661 A

  The coefficient of restitution correlates with the rigidity of the golf ball. A golf ball having a large rigidity generally has a large coefficient of restitution. However, when a golf ball having high rigidity is hit by a weak golfer, a sufficient flight distance may not be obtained. This is because even if a less powerful golfer, in other words, a golfer with a low head speed hits the golf ball, an appropriate deformation of the golf ball cannot be obtained.

  Less powerful golfers want to improve the flight performance of golf balls. An object of the present invention is to provide a golf ball having excellent flight performance when hit at a low head speed.

The golf ball according to the present invention includes a core and a cover positioned outside the core. The core includes a center and an intermediate layer located outside the center. The center restitution coefficient Ec, the core restitution coefficient Em, and the golf ball restitution coefficient Eb satisfy the following formula (1).
Eb ≧ Ec ≧ Em (1)

Preferably, the golf ball further satisfies the following mathematical formula (2).
Eb−Ec ≧ Ec−Em (2)

  Preferably, the difference (Eb−Ec) between the restitution coefficient Eb and the restitution coefficient Ec is 0.004 or more. Preferably, the difference (Ec−Em) between the restitution coefficient Ec and the restitution coefficient Em is 0.004 or more.

The center may include a first layer and a second layer located outside the first layer. Preferably, the restitution coefficient Ec1 of the first layer and the restitution coefficient Ec of the center satisfy the following formula (3).
Ec> Ec1 (3)
Preferably, this golf ball satisfies the following mathematical formula (4) or (5).
Eb ≧ Ec ≧ Em> Ec1 (4)
Eb ≧ Ec> Em ≧ Ec1 (5)

  Preferably, the intermediate layer has a hardness (Shore D) of less than 35.

  In this golf ball, the core restitution coefficient Em is the lowest among the center restitution coefficient Ec, the core restitution coefficient Em, and the golf ball restitution coefficient Eb. When this golf ball is hit, proper distortion occurs even if the head speed is low. This distortion provides a large flight distance.

FIG. 1 is a schematic cross-sectional view showing a golf ball according to an embodiment of the present invention. FIG. 2 is a schematic cross-sectional view showing a golf ball according to another embodiment of the present invention.

  Hereinafter, the present invention will be described in detail based on preferred embodiments with appropriate reference to the drawings.

  FIG. 1 is a schematic cross-sectional view showing a golf ball 2 according to an embodiment of the present invention. The golf ball 2 includes a spherical core 4 and a cover 6 that covers the core 4. The core 4 includes a spherical center 8 and an intermediate layer 10 that covers the center 8. A large number of dimples 12 are formed on the surface of the cover 6. A portion of the surface of the golf ball 2 other than the dimples 12 is a land 14. The golf ball 2 includes a paint layer and a mark layer outside the cover 6, but these layers are not shown. The golf ball 2 may include a rib positioned on the surface of the center 8.

  The golf ball 2 has a diameter of 40 mm or greater and 45 mm or less. From the viewpoint of satisfying the standards of the US Golf Association (USGA), the diameter is more preferably 42.67 mm or more. In light of suppression of air resistance, the diameter is more preferably equal to or less than 44 mm, and particularly preferably equal to or less than 42.80 mm. The golf ball 2 has a mass of 40 g or more and 50 g or less. In light of attainment of great inertia, the mass is more preferably equal to or greater than 44 g, and particularly preferably equal to or greater than 45.00 g. From the viewpoint that the USGA standard is satisfied, the mass is more preferably 45.93 g or less.

  The center 8 is obtained by crosslinking the rubber composition. Examples of preferable base rubber include polybutadiene, polyisoprene, styrene-butadiene copolymer, ethylene-propylene-diene copolymer, and natural rubber. From the viewpoint of resilience performance, polybutadiene is preferred. When polybutadiene and other rubber are used in combination, it is preferable that polybutadiene is a main component. Specifically, the proportion of polybutadiene in the total base rubber is preferably 50% by mass or more, particularly 80% by mass or more. Polybutadiene having a cis-1,4 bond ratio of 40% or more, particularly 80% or more is preferred.

  For the crosslinking of the center 8, a co-crosslinking agent is preferably used. A preferred co-crosslinking agent from the viewpoint of resilience performance is a monovalent or divalent metal salt of an α, β-unsaturated carboxylic acid having 2 to 8 carbon atoms. Specific examples of preferred co-crosslinking agents include zinc acrylate, magnesium acrylate, zinc methacrylate and magnesium methacrylate. Zinc acrylate and zinc methacrylate are particularly preferable because of high resilience performance.

  As a co-crosslinking agent, an α, β-unsaturated carboxylic acid having 2 to 8 carbon atoms and a metal oxide may be blended. Both react in the rubber composition to obtain a salt. This salt contributes to the crosslinking reaction. Preferred α, β-unsaturated carboxylic acids include acrylic acid and methacrylic acid. Preferred metal oxides include zinc oxide and magnesium oxide.

  From the viewpoint of the resilience performance of the golf ball 2, the compounding amount of the co-crosslinking agent is preferably 10 parts by mass or more and more preferably 15 parts by mass or more with respect to 100 parts by mass of the base rubber. In light of the feel at impact, the amount of the co-crosslinking agent is preferably 50 parts by mass or less, and more preferably 45 parts by mass or less.

  Preferably, the rubber composition of the center 8 includes an organic peroxide together with a co-crosslinking agent. The organic peroxide functions as a crosslinking initiator. Due to the organic peroxide, the excellent resilience performance of the golf ball 2 can be achieved. Suitable organic peroxides include dicumyl peroxide, 1,1-bis (t-butylperoxy) -3,3,5-trimethylcyclohexane, 2,5-dimethyl-2,5-di (t- Butyl peroxy) hexane and di-t-butyl peroxide. A particularly versatile organic peroxide is dicumyl peroxide.

  In light of the resilience performance of the golf ball 2, the organic peroxide is preferably blended in an amount of 0.1 part by weight or more, more preferably 0.3 part by weight or more, based on 100 parts by weight of the base rubber, Part by mass or more is particularly preferable. From the viewpoint of soft feel at impact, the amount of the organic peroxide is preferably 3.0 parts by mass or less, more preferably 2.8 parts by mass or less, and particularly preferably 2.5 parts by mass or less.

  Preferably, the rubber composition of the center 8 includes an organic sulfur compound. Preferred organic sulfur compounds include diphenyl disulfide, bis (4-chlorophenyl) disulfide, bis (3-chlorophenyl) disulfide, bis (4-bromophenyl) disulfide, bis (3-bromophenyl) disulfide, and bis (4-fluorophenyl). ) Monosubstituted products such as disulfide, bis (4-iodophenyl) disulfide, bis (4-cyanophenyl) disulfide; bis (2,5-dichlorophenyl) disulfide, bis (3,5-dichlorophenyl) disulfide, bis (2, 6-dichlorophenyl) disulfide, bis (2,5-dibromophenyl) disulfide, bis (3,5-dibromophenyl) disulfide, bis (2-chloro-5-bromophenyl) disulfide, bis (2-cyano-5-bromophene) Di) disubstituted compounds such as disulfide; trisubstituted compounds such as bis (2,4,6-trichlorophenyl) disulfide and bis (2-cyano-4-chloro-6-bromophenyl) disulfide; Tetra-substituted products such as 5,6-tetrachlorophenyl) disulfide; and bis (2,3,4,5,6-pentachlorophenyl) disulfide, bis (2,3,4,5,6-pentabromophenyl) disulfide, etc. The penta-substituted product is exemplified. With the organic sulfur compound, the excellent resilience performance of the golf ball 2 can be achieved. Particularly preferred organic sulfur compounds are diphenyl disulfide and bis (pentabromophenyl) disulfide.

  In light of the resilience performance of the golf ball 2, the amount of the organic sulfur compound is preferably equal to or greater than 0.1 parts by weight and more preferably equal to or greater than 0.2 parts by weight with respect to 100 parts by weight of the base rubber. In light of the feel at impact, the organic sulfur compound content is preferably equal to or less than 1.50 parts by weight, more preferably equal to or less than 1.0 parts by weight, and particularly preferably equal to or less than 0.8 parts by weight.

  The center 8 may be blended with a filler for the purpose of adjusting specific gravity and the like. Suitable fillers include zinc oxide, barium sulfate, calcium carbonate and magnesium carbonate. As a filler, a powder made of a high specific gravity metal may be blended. Specific examples of the high specific gravity metal include tungsten and molybdenum. The blending amount of the filler is appropriately determined so that the intended specific gravity of the center 8 is achieved. A particularly preferred filler is zinc oxide. Zinc oxide functions not only as a specific gravity adjuster but also as a crosslinking aid. In the center 8, various additives such as sulfur, an antioxidant, a colorant, a plasticizer, and a dispersant are blended in appropriate amounts as necessary. The center 8 may be blended with a crosslinked rubber powder or a synthetic resin powder.

  The diameter of the center 8 is preferably 36 mm or greater and 42 mm or less. Due to the center 8 having a diameter of 36 mm or more, proper deformation of the golf ball 2 can be achieved. In this respect, the diameter is more preferably 37 mm or more. By setting the diameter to 42 mm or less, the intermediate layer 10 and the cover 6 can contribute to durability. In this respect, the diameter is more preferably 41 mm or less.

  The amount of compressive deformation Cc of the center 8 is preferably 2.0 mm or greater and 5.0 mm or less. A soft shot feeling of the golf ball 2 can be achieved by the center 8 having the amount of compressive deformation Cc of 2.0 mm or more. In this respect, the amount of compressive deformation Cc is more preferably equal to or greater than 2.4 mm, and particularly preferably equal to or greater than 2.6 mm. Due to the center 8 having the amount of compressive deformation Cc of 5.0 mm or less, the excellent resilience performance and durability of the golf ball 2 can be achieved. In this respect, the amount of compressive deformation Cc is more preferably equal to or less than 4.3 mm, and particularly preferably equal to or less than 3.5 mm.

  In the measurement of the amount of compressive deformation, a sphere (ie, the center 8, the core 4 or the golf ball 2) is first placed on a metal rigid plate. Next, the metal cylinder gradually descends toward the sphere. The sphere sandwiched between the bottom surface of the cylinder and the rigid plate is deformed. The moving distance of the cylinder from the state where the initial load of 98 N is applied to the sphere to the state where the final load of 1274 N is applied is measured.

  The mid layer 10 is made of a resin composition. Preferred base resins of the resin composition include styrene block-containing thermoplastic elastomers, ionomer resins, thermoplastic polyurethane elastomers, thermoplastic polyester elastomers, and thermoplastic polyamide elastomers.

  A particularly preferred base resin is a styrene block-containing thermoplastic elastomer. This elastomer includes a polystyrene block as a hard segment and a soft segment. A typical soft segment is a diene block. This elastomer includes styrene-butadiene-styrene block copolymer (SBS), styrene-isoprene-styrene block copolymer (SIS), styrene-isoprene-butadiene-styrene block copolymer (SIBS), hydrogenated SBS. Products, SIS hydrogenated products and SIBS hydrogenated products. Examples of the hydrogenated product of SBS include styrene-ethylene-butylene-styrene block copolymer (SEBS). As a hydrogenated product of SIS, styrene-ethylene-propylene-styrene block copolymer (SEPS) can be mentioned. Examples of the hydrogenated product of SIBS include styrene-ethylene-ethylene-propylene-styrene block copolymer (SEEPS).

  In light of the resilience performance of the golf ball 2, the content of the styrene component in the thermoplastic elastomer is preferably 5% by mass or more, more preferably 7% by mass or more, and particularly preferably 10% by mass or more. In light of feel at impact of the golf ball 2, the content is preferably equal to or less than 45% by mass, more preferably equal to or less than 40% by mass, and particularly preferably equal to or less than 45% by mass.

  In the present invention, the styrene block-containing thermoplastic elastomer includes an alloy of one or two or more selected from the group consisting of SBS, SIS, SIBS, SEBS, SEPS and SEEPS, and hydrogenated products thereof, and an olefin. included. The olefin component in the alloy is presumed to contribute to the improvement of compatibility with other base polymers. By using this alloy, the resilience performance of the golf ball 2 is improved. Preferably, an olefin having 2 to 10 carbon atoms is used. Suitable olefins include ethylene, propylene, butene and pentene. Ethylene and propylene are particularly preferred.

  Specific examples of polymer alloys include Mitsubishi Chemical's trade names “Lavalon T3221C”, “Lavalon T3339C”, “Lavalon SJ4400N”, “Lavalon SJ5400N”, “Lavalon SJ6400N”, “Lavalon SJ7400N”, “Lavalon SJ8400N”, “ And “Lavalon SJ9400N” and “Lavalon SR04”. Other specific examples of the styrene block-containing thermoplastic elastomer include Daicel Chemical Industries' trade name “Epofriend A1010” and Kuraray's trade name “Septon HG-252”.

  In light of feel at impact, the material hardness of the styrene block-containing thermoplastic elastomer is preferably less than 8, more preferably less than 6, and particularly preferably less than 5. In the measurement of material hardness, a slab made of a styrene block-containing thermoplastic elastomer is used. In the present invention, unless otherwise specified, a Shore D spring attached to an automatic rubber hardness measuring device (trade name “P1” of Kobunshi Keiki Co., Ltd.) in accordance with the provisions of “ASTM-D 2240-68”. The hardness is measured by a type hardness tester. For the measurement, a slab formed by hot pressing and having a thickness of about 2 mm is used. Prior to measurement, the slab is stored at a temperature of 23 ° C. for 2 weeks. At the time of measurement, three slabs are overlaid. For the measurement of the material hardness of the styrene block-containing thermoplastic elastomer, a slab consisting only of the styrene block-containing thermoplastic elastomer is used. In addition, the material hardness measured with the JIS-A type spring hardness tester is preferably less than 40, more preferably less than 30, and particularly preferably less than 20.

  An ionomer resin, a thermoplastic polyurethane elastomer, a thermoplastic polyester elastomer, or a thermoplastic polyamide elastomer may be used together with the styrene block-containing thermoplastic elastomer. A polymer composition containing a lubricant may be used together with a styrene block-containing thermoplastic elastomer.

  A resin particularly suitable for use in combination with the styrene block-containing thermoplastic elastomer is an ionomer resin. A preferable ionomer resin includes a binary copolymer of an α-olefin and an α, β-unsaturated carboxylic acid having 3 to 8 carbon atoms. Other preferable ionomer resins include ternary α-olefin, α, β-unsaturated carboxylic acid having 3 to 8 carbon atoms and α, β-unsaturated carboxylic acid ester having 2 to 22 carbon atoms. A copolymer is mentioned. In the binary copolymer and ternary copolymer, preferred α-olefins are ethylene and propylene, and preferred α, β-unsaturated carboxylic acids are acrylic acid and methacrylic acid. In the binary copolymer and ternary copolymer, some of the carboxyl groups are neutralized with metal ions. Examples of the metal ions for neutralization include sodium ions, potassium ions, lithium ions, zinc ions, calcium ions, magnesium ions, aluminum ions, and neodymium ions. Neutralization may be performed with two or more metal ions. Particularly suitable metal ions from the viewpoint of resilience performance and durability of the golf ball 2 are sodium ion, zinc ion, lithium ion and magnesium ion.

  A preferable binary copolymer contains 80% by mass or more and 90% by mass or less α-olefin and 10% by mass or more and 20% by mass or less α, β-unsaturated carboxylic acid. This binary copolymer is excellent in resilience performance. Preferred terpolymers are 70% to 85% by weight α-olefin, 5% to 30% by weight α, β-unsaturated carboxylic acid, and 1% to 25% by weight. α, β-unsaturated carboxylic acid ester. This ternary copolymer is excellent in resilience performance. A particularly preferred ionomer resin is a copolymer of ethylene and acrylic acid or methacrylic acid.

  Specific examples of the ionomer resin include Mitsui Dupont Polychemical's trade names “HIMILAN 1555”, “HIMILAN 1557”, “HIMILAN 1605”, “HIMILAN 1706”, “HIMILAN 1707”, “HIMILAN 1856” and “HIMILAN 1855”. "High Milan AM7311", "High Milan AM7315", "High Milan AM7317", "High Milan AM7318" and "High Milan MK7320"; DuPont's trade names "Surlin 6120", "Surlin 6910", "Surlin 7930", "Surlin 7940" , "Surlin 8140", "Surlin 8150", "Surlin 8940", "Surlin 8945", "Surlin 9120", "Surlin 9150", "Surlin 9910", "Surlin 9945" and Phosphorus AD8546 "; and ExxonMobil Chemical Co. under the trade name of" IOTEK7010 "," IOTEK7030 "," IOTEK7510 "," IOTEK7520 "includes" IOTEK8000 "and" IOTEK8030 ". Two or more ionomer resins may be used in combination. An ionomer resin neutralized with a monovalent metal ion and an ionomer resin neutralized with a divalent metal ion may be used in combination.

  From the viewpoint of resilience performance, the material hardness of the ionomer resin is preferably 50 or more, more preferably 53 or more, and particularly preferably 55 or more. In light of feel at impact, the material hardness of the ionomer resin is preferably 70 or less, more preferably 67 or less, and particularly preferably 65 or less. For the measurement of the material hardness of the ionomer resin, a slab made of only the ionomer resin is used.

  When the styrene block-containing thermoplastic elastomer and another resin are used in combination, the ratio of the amount of the styrene block-containing thermoplastic elastomer to the amount of the total base resin is preferably 50% by mass or more, and more preferably 70% by mass or more. The ratio may be 100% by mass.

A filler may be blended in the resin composition of the mid layer 10 for the purpose of adjusting specific gravity and the like. Suitable fillers include zinc oxide, barium sulfate, calcium carbonate and magnesium carbonate. As a filler, a powder made of a high specific gravity metal may be blended. This powder increases the moment of inertia of the golf ball 2. A metal having a specific gravity of 4.5 g / cm ³ or more is preferable, a metal having a specific gravity of 5.0 g / cm ³ or more is more preferable, a metal having a specific gravity of 7 g / cm ³ or more is more preferable, and a specific gravity is 10 g / cm ³ or more. Metal is particularly preferred. Specific examples of the high specific gravity metal include tungsten and molybdenum. The amount of the filler with respect to 100 parts by mass of the base resin is preferably 5 parts by mass or more, more preferably 10 parts by mass or more, and particularly preferably 15 parts by mass or more. The amount of the filler is preferably 30 parts by mass or less. The mid layer 10 may be blended with a colorant, a crosslinked rubber powder, or a synthetic resin powder.

  The hardness (Shore D) of the mid layer 10 is preferably less than 35. With the mid layer 10 having a hardness of less than 35, proper deformation of the golf ball 2 can be achieved. In this respect, the hardness is more preferably 34 or less, and particularly preferably 30 or less. The hardness is preferably 1 or more, particularly preferably 3 or more. For the measurement of hardness, a slab made of the same resin composition as that of the intermediate layer 10 is used. The details of the measurement method are as described above.

  In light of appropriate deformation of the golf ball 2, the mid layer 10 preferably has a thickness of 0.3 mm or greater, and more preferably 0.5 mm or greater. In light of the resilience performance of the golf ball 2, the thickness is preferably equal to or less than 1.2 mm, and more preferably equal to or less than 1.1 mm.

  The cover 6 is made of a resin composition. A preferable base resin of the resin composition is an ionomer resin. An equivalent of the ionomer resin described above with respect to the intermediate layer 10 can be used for the cover 6. The ionomer resin contributes to the resilience performance of the golf ball 2. For the cover 6, a styrene block-containing thermoplastic elastomer, a thermoplastic polyester elastomer, a thermoplastic polyamide elastomer, a thermoplastic polyurethane elastomer, or a thermoplastic polyolefin elastomer may be used. An ionomer resin and another resin may be used in combination. When used in combination, the ionomer resin is preferably the main component from the viewpoint of resilience performance. The ratio of the ionomer resin to the total amount of the base resin is preferably 70% by mass or more, and more preferably 80% by mass or more.

  The cover 6 preferably has a hardness (Shore D) of 55 or more. With this cover 6, the excellent resilience performance of the golf ball 2 can be achieved. In this respect, the hardness is more preferably equal to or greater than 60, and particularly preferably equal to or greater than 65. From the viewpoint of feel at impact, the D hardness is preferably 75 or less, and more preferably 70 or less. For the measurement of hardness, a slab made of the same resin composition as the resin composition of the cover 6 is used. The details of the measurement method are as described above.

  The thickness of the cover 6 is preferably 0.8 mm or greater and 1.4 mm or less. Excellent flight performance and durability can be achieved by the cover 6 having a thickness of 0.8 mm or more. In this respect, the thickness is more preferably equal to or greater than 1.0 mm. Appropriate deformation of the core 4 can be achieved by the cover 6 having a thickness of 1.4 mm or less. In this respect, the thickness is more preferably equal to or less than 1.3 mm. The cover 6 may include two or more layers.

  If necessary, the cover 6 may contain an appropriate amount of a colorant such as titanium dioxide, a filler such as barium sulfate, a dispersant, an antioxidant, an ultraviolet absorber, a light stabilizer, a fluorescent agent, and a fluorescent brightening agent. Blended. For the purpose of adjusting the specific gravity, the cover 6 may be mixed with powder of a high specific gravity metal such as tungsten or molybdenum.

  The compression deformation amount Cb of the golf ball 2 is preferably 2.0 mm or greater and 5.0 mm or less. The golf ball 2 having a compression deformation amount Cb of 2.0 mm or more is excellent in feel at impact. In this respect, the amount of compressive deformation Cb is more preferably equal to or greater than 2.4 mm, and particularly preferably equal to or greater than 2.6 mm. The golf ball 2 having a compression deformation amount Cb of 5.0 mm or less is excellent in durability. In this respect, the amount of compressive deformation Cb is more preferably equal to or less than 4.3 mm, and particularly preferably equal to or less than 3.5 mm.

  In light of resilience performance and durability, the difference (Cc−Cb) between the amount of compressive deformation Cc of the center 8 and the amount of compressive deformation Cb of the golf ball 2 is preferably equal to or greater than 0.4 mm, and particularly preferably equal to or greater than 0.5 mm. In light of feel at impact, the difference (Cc−Cb) is preferably equal to or less than 1.2 mm, and particularly preferably equal to or less than 1.0 mm.

The restitution coefficient Ec of the center 8, the restitution coefficient Em of the core 4, and the restitution coefficient Eb of the golf ball 2 satisfy the following formula (1).
Eb ≧ Ec ≧ Em (1)
In this golf ball 2, the restitution coefficient Ec of the center 8 is the same as or larger than the restitution coefficient Em of the core 4, and the restitution coefficient Eb of the golf ball 2 is the same or larger than the restitution coefficient Ec of the center 8. The gradient of the coefficient of restitution from the center 8 to the core 4 is zero or negative, and the gradient of the coefficient of restitution from the core 4 to the golf ball 2 is zero or positive. When this golf ball 2 is hit, it is greatly distorted even if the head speed is low. Due to this distortion, the center 8 greatly contributes to the initial velocity of the golf ball 2. Moreover, since the coefficient of restitution Ec is equal to or smaller than the coefficient of restitution Eb, the energy loss at the center 8 is large when hit by a driver. Spin is suppressed by a large energy loss. Excellent flight performance is achieved with high initial speed and low spin.

  In the measurement of the coefficient of restitution, an aluminum hollow cylinder having a mass of 200 g is caused to collide with a sphere (golf ball 2, core 4 or center 8) at a speed of 40 m / s. The velocity of the hollow cylinder before and after the collision and the velocity of the sphere after the collision are measured, and the restitution coefficient of the sphere is calculated. Twelve measurement results are averaged.

Preferably, the golf ball 2 satisfies the following formula (6).
Eb>Ec> Em (6)
In the golf ball 2 satisfying the above formula (6), the gradient of the coefficient of restitution from the center 8 to the core 4 is negative, and the gradient of the coefficient of restitution from the core 4 to the golf ball 2 is positive. When this golf ball 2 is hit, it is greatly distorted even if the head speed is low. This golf ball 2 is extremely excellent in flight performance.

Preferably, the golf ball 2 satisfies the following mathematical formula (2).
Eb−Ec ≧ Ec−Em (2)
In this golf ball 2, the cover 6 contributes to the resilience performance. This golf ball 2 is excellent in flight performance. More preferably, the golf ball 2 satisfies the following mathematical formula (7).
Eb-Ec> Ec-Em (7)
The golf ball 2 satisfying the mathematical formula (7) is extremely excellent in flight performance.

  The difference (Eb−Ec) between the restitution coefficient Eb and the restitution coefficient Ec is preferably 0.004 or more. In the golf ball 2 having the difference (Eb−Ec) of 0.004 or more, the cover 6 can contribute to the resilience performance. In this respect, the difference (Eb−Ec) is more preferably equal to or greater than 0.006, and particularly preferably equal to or greater than 0.008. The difference (Eb−Ec) is preferably 0.03 or less.

  The difference (Ec−Em) between the restitution coefficient Ec and the restitution coefficient Em is preferably 0.004 or more. In the golf ball 2 having the difference (Ec−Em) of 0.004 or more, the center 8 can be greatly deformed when hit. In this respect, the difference (Ec−Em) is more preferably equal to or greater than 0.006, and particularly preferably equal to or greater than 0.008. The difference (Ec−Em) is preferably 0.03 or less.

  FIG. 2 is a schematic cross-sectional view showing a golf ball 16 according to another embodiment of the present invention. The golf ball 16 includes a spherical core 18 and a cover 20 that covers the core 18. The core 18 includes a spherical center 22 and an intermediate layer 24 covering the center 22. The center 22 includes a spherical first layer 26 and a second layer 28 positioned outside the first layer 26. A large number of dimples 30 are formed on the surface of the cover 20. A portion of the surface of the golf ball 16 other than the dimple 30 is a land 32. The golf ball 16 includes a paint layer and a mark layer on the outside of the cover 20, but these layers are not shown. The configuration of the mid layer 24 is equivalent to the configuration of the mid layer 10 of the golf ball 2 shown in FIG. The configuration of the cover 20 is equivalent to the configuration of the cover 6 of the golf ball 2 shown in FIG. The golf ball 16 may include a rib positioned on the surface of the first layer 26.

  The first layer 26 and the second layer 28 are obtained by crosslinking the rubber composition. A rubber composition equivalent to the center 8 of the golf ball 2 shown in FIG. 1 can be used for the first layer 26 and the second layer 28. The diameter of the first layer 26 is preferably 5 mm or greater and 30 mm or less. The thickness of the second layer 28 is preferably 4 mm or greater and 16.4 mm or less.

  This golf ball 16 satisfies the above mathematical formula (1). When this golf ball 16 is hit, it is greatly distorted even if the head speed is low. Due to this distortion, the center 22 greatly contributes to the initial velocity of the golf ball 16. Moreover, since the coefficient of restitution Ec is equal to or smaller than the coefficient of restitution Eb, the energy loss at the center 22 is large when hit by a driver. Spin is suppressed by a large energy loss. Excellent flight performance is achieved with high initial speed and low spin. Preferably, the golf ball 16 satisfies the formula (2), (6) or (7).

  The difference (Eb−Ec) between the restitution coefficient Eb and the restitution coefficient Ec is preferably 0.004 or more, more preferably 0.006 or more, and particularly preferably 0.008 or more. The difference (Eb−Ec) is preferably 0.03 or less. The difference (Ec−Em) between the restitution coefficient Ec and the restitution coefficient Em is preferably 0.004 or more, more preferably 0.006 or more, and particularly preferably 0.008 or more. The difference (Ec−Em) is preferably 0.03 or less.

The restitution coefficient Ec1 of the first layer 26 and the restitution coefficient Ec of the center 22 satisfy the following formula (3).
Ec> Ec1 (3)
In the golf ball 16, the center 22 is sufficiently deformed when hit. The golf ball 16 has a high initial velocity when hit at a low head speed. This golf ball 16 is excellent in flight performance.

Preferably, the golf ball 16 satisfies Formula (4) or (5).
Eb ≧ Ec ≧ Em> Ec1 (4)
Eb ≧ Ec> Em ≧ Ec1 (5)
In the golf ball 16 satisfying the mathematical expression (4) or (5), the deformation of the center 22 is extremely large when hit. From the viewpoint of deformation of the center 22, it is more preferable that the golf ball 16 satisfies the following mathematical formula (8).
Eb ≧ Ec>Em> Ec1 (8)

  Hereinafter, the effects of the present invention will be clarified by examples. However, the present invention should not be construed in a limited manner based on the description of the examples.

[Example 1]
100 parts by mass of high-cis polybutadiene (trade name “BR-730” from JSR), 28 parts by mass of zinc acrylate, 10 parts by mass of zinc oxide, an appropriate amount of barium sulfate, 0.3 parts by mass of bis (pentabromo Phenyl) disulfide and 0.7 parts by mass of dicumyl peroxide (Nippon Yushi Co., Ltd.) were kneaded to obtain a rubber composition (a). This rubber composition (a) was put into a mold composed of an upper mold and a lower mold each having a hemispherical cavity and heated at 170 ° C. for 30 minutes to obtain a center having a diameter of 38.3 mm. On the other hand, 20 parts by mass of ionomer resin (“Hi-Milan 1605” from Mitsui DuPont Polychemical), 20 parts by mass of other ionomer resin (“Hi-Milan 1706” from Mitsui DuPont Polychemical), 60 parts by mass of styrene block-containing heat A plastic elastomer (Kreiburg) and 15 parts by mass of tungsten powder were kneaded with a biaxial kneading extruder to obtain a resin composition (f). This resin composition (f) was coated around the center by an injection molding method to obtain a core comprising a center and an intermediate layer. The thickness of the intermediate layer was 1.0 mm. Further, 50 parts by mass of ionomer resin (DuPont's trade name “Surlin 8140”), 50 parts by mass of other ionomer resin (DuPont's trade name “Surlin 9120”) and 2 parts by mass of titanium dioxide are biaxially kneaded. The resin composition (q) was obtained by kneading with an extruder. The core was put into a final mold having a large number of pimples on the inner peripheral surface, and the resin composition (q) was injected around the core by an injection molding method to mold a cover. The cover thickness was 1.2 mm. A large number of dimples having a reversed pimple shape were formed on the cover. A clear paint based on a two-component curable polyurethane was applied to this cover to obtain a golf ball of Example 1 having a diameter of 42.7 mm and a mass of about 45.4 g.

[Examples 2 to 5 and Comparative Examples 1 to 3]
Golf balls of Examples 2 to 5 and Comparative Examples 1 to 3 were obtained in the same manner as in Example 1 except that the specifications of the center, intermediate layer and cover were as shown in Tables 4 and 5 below. Details of the rubber composition of the center are shown in Table 1 below. Details of the resin composition of the intermediate layer are shown in Table 2 below. Details of the resin composition of the cover are shown in Table 3 below.

[Example 6]
100 parts by weight of high-cis polybutadiene (previously referred to as “BR-730”), 19 parts by weight of zinc acrylate, 10 parts by weight of zinc oxide, 0.3 parts by weight of bis (pentabromophenyl) disulfide and 0.7 parts by weight Part of dicumyl peroxide was kneaded to obtain a rubber composition (c). This rubber composition (c) was put into a mold composed of an upper mold and a lower mold each having a hemispherical cavity and heated at 170 ° C. for 30 minutes to obtain a first layer having a diameter of 18.0 mm. . 100 parts by weight of high-cis polybutadiene (previously referred to as “BR-730”), 32 parts by weight of zinc acrylate, 10 parts by weight of zinc oxide, an appropriate amount of barium sulfate, 0.3 parts by weight of bis (pentabromophenyl) disulfide And 0.7 parts by mass of dicumyl peroxide (Nippon Yushi Co., Ltd.) were kneaded to obtain a rubber composition (b). A half shell was molded with this rubber composition (b). The first layer was covered with two half shells. Both the first layer and the half shell were put into a mold composed of an upper mold and a lower mold having a hemispherical cavity and heated at 170 ° C. for 20 minutes to obtain a center having a diameter of 38.3 mm. On the other hand, 20 parts by mass of ionomer resin (previously referred to as “HIMILAN 1605”), 20 parts by mass of other ionomer resin (previously described “HIMILAN 1706”), 60 parts by mass of a styrene block-containing thermoplastic elastomer (Cryburg) and 15 Mass parts of tungsten powder were kneaded with a twin-screw kneading extruder to obtain a resin composition (f). This resin composition (f) was coated around the center by an injection molding method to obtain a core comprising a center and an intermediate layer. The thickness of the intermediate layer was 1.0 mm. Further, 50 parts by mass of ionomer resin (previously “Surlin 8140”), 50 parts by mass of other ionomer resin (previously “Surlin 9120”) and 2 parts by mass of titanium dioxide were kneaded in a twin-screw kneading extruder, A resin composition (q) was obtained. The core was put into a final mold having a large number of pimples on the inner peripheral surface, and the resin composition (q) was injected around the core by an injection molding method to mold a cover. The cover thickness was 1.2 mm. A large number of dimples having a reversed pimple shape were formed on the cover. A clear paint based on a two-component curable polyurethane was applied to this cover to obtain a golf ball of Example 6 having a diameter of 42.7 mm and a mass of about 45.4 g.

[Flight distance test]
A driver equipped with a titanium head (trade name “XXIO” of SRI Sports, shaft hardness: R, loft angle: 11 °) was mounted on a swing machine manufactured by Golf Lab. A golf ball was hit under the condition where the head speed was 40 m / sec, and the distance from the launch point to the rest point was measured. The average values of the data obtained by 12 measurements are shown in Tables 4 and 5 below.

[Evaluation of feel at impact]
Ten golf players hit golf balls with a driver and evaluated the feel at impact. The following ratings were given based on the number of golfers who stated that “the shot feel was good”.
A: 8 or more B: 6 or 7 C: 4 or 5 D: 3 or less The results are shown in Tables 4 and 5 below.

  As shown in Tables 4 and 5, the golf ball of each example has excellent flight performance. From this evaluation result, the superiority of the present invention is clear.

  The golf ball according to the present invention can be used for playing on a golf course or practice in a driving range.

2, 16 ... Golf ball 4, 18 ... Core 6, 20 ... Cover 8, 22 ... Center 10, 24 ... Intermediate layer 12, 30 ... Dimple 14, 32 ... Land 26 ... First layer 28 ... Second layer

Claims (5)

A golf ball comprising a core and a cover located outside the core, the core comprising a center and an intermediate layer located outside the center;
An aluminum hollow cylinder having a mass of 200 g is caused to collide with the sphere at a speed of 40 m / s, and the center repulsion obtained by measuring the speed of the hollow cylinder before and after the collision and the speed of the sphere after the collision. coefficient Ec, resilience coefficient Eb of the resilience coefficient Em, and golf ball core, meets the following formula (6),
The difference (Eb−Ec) between the restitution coefficient Eb and the restitution coefficient Ec is 0.004 or more,
A golf ball having a difference (Ec−Em) between the restitution coefficient Ec and the restitution coefficient Em of 0.006 or more .
Eb>Ec> Em (6) The golf ball according to claim 1, further satisfying the following formula (7) .
Eb-Ec> Ec-Em (7) The center comprises a first layer and a second layer located outside the first layer;
An aluminum hollow cylinder having a mass of 200 g is caused to collide with the sphere at a speed of 40 m / s, and the speed of the hollow cylinder before and after the collision and the speed of the sphere after the collision are measured, and the first layer is obtained. the golf ball according to claim 1 or 2 and the resilience coefficient Ec of the resilience coefficient Ec1 and center satisfies the following equation (3).
Ec> Ec1 (3) The golf ball of claim 3, satisfying the following number of formulas.
Eb>Ec>Em> Ec1 The golf ball according to claim 1 , wherein the mid layer has a hardness (Shore D) of less than 35. 6.