JP5506291B2 - Decorative sheet - Google Patents
Decorative sheet Download PDFInfo
- Publication number
- JP5506291B2 JP5506291B2 JP2009195251A JP2009195251A JP5506291B2 JP 5506291 B2 JP5506291 B2 JP 5506291B2 JP 2009195251 A JP2009195251 A JP 2009195251A JP 2009195251 A JP2009195251 A JP 2009195251A JP 5506291 B2 JP5506291 B2 JP 5506291B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- synthetic resin
- decorative sheet
- resin layer
- capsule
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、バックスキンやスエードのようなソフトな触感や高級感があり、しかも温感性に優れ、水周りでの使用も可能な装飾シートに関する。 The present invention relates to a decorative sheet that has a soft touch and a high-class feeling such as a back skin and suede, is excellent in warm feeling, and can be used around water.
装飾シートとしては、例えば、畳、カーペット、フローリング、クッションフロアなど家庭用の床材などがある。
それらの中でも、塩化ビニル樹脂製のクッションフロアが、水や汚れ等を簡単に拭き取れるので、手入れがしやすく、多用な意匠（模様）を実現できることから、良く使われていたことがあった。しかし、近年では、低価格化されてきたフローリングが急速に普及する一方、フローリングに比べると高級感にやや劣るクッションフロアは、家庭床面積の中に占める割合が減少し、使用される場所としては、水周りの限られた所しか使われなくなってきている。
Examples of the decorative sheet include home floor materials such as tatami mats, carpets, flooring, and cushion floors.
Among them, the cushion floor made of vinyl chloride resin has been often used because it can easily wipe off water and dirt, etc., and is easy to care for and can realize a variety of designs (patterns). However, in recent years, flooring, which has been priced down, has spread rapidly, while cushion floors, which are slightly inferior in quality compared to flooring, have a smaller share in the home floor area and are used as places where they are used. Only a limited area around the water is being used.
ところが、これらフローリングやクッションフロアは共に、寒い冬季などに、その表面を「冷たい」と感じることから、床暖房の設置をする、その上にホットカーペットあるいは布製マットを敷く、などの対策が取られることが多い。
ちなみに、人が物に触れたとき、それぞれが同じ温度であるにもかかわらず、フローリングやクッションフロアは「冷たい」、畳やカーペットは「暖かい」と感じる傾向がある。このような皮膚感覚は、接触冷温感と呼ばれ、人の皮膚から物への熱の移動量の差によって変化するものであり、その物を構成する「素材」だけでなく、「毛羽立ち具合」や「凹凸等の表面形状」も影響するといわれている。
However, both of these flooring and cushion floors feel that the surface is “cold” in the cold winter season, so measures such as installing floor heating and laying hot carpets or cloth mats on them are taken. There are many cases.
By the way, when people touch things, they tend to feel that flooring and cushion floors are “cold” and tatami mats and carpets are “warm” even though they are at the same temperature. This kind of skin sensation is called a feeling of cold contact and changes depending on the amount of heat transferred from the person's skin to the object, and not only the “material” that makes up the object, but also the “fuzziness” It is said that "surface shape such as irregularities" also affects.
他方、このように温感性（冷たく感じない）には優れている畳やカーペットは、水や汚れが浸透しやすいので、上記フローリングやクッションフロアに比べ、清掃性に劣る欠点がある。 On the other hand, tatami mats and carpets, which are excellent in warm feeling (not feeling cold), have a drawback that they are inferior in cleanability as compared with the above flooring and cushion floor because water and dirt are likely to penetrate.
本発明は、畳やカーペットのような温感性（冷たく感じない）とフローリングやクッションフロアのような清掃性との機能を併せ持ち、また、バックスキンやスエードのようなソフトな触感や高級感を有する床材や壁材などの装飾シートの提供を課題とする。 The present invention combines the functions of warm feeling (not feeling cold) such as tatami mats and carpets with cleanability such as flooring and cushion floor, and also has soft touch and luxury like backskin and suede. The issue is to provide decorative sheets such as flooring and wall materials.
本発明の装飾シートは、基材層、合成樹脂層、意匠層、透明合成樹脂層、表面層とからなる装飾シートであって、前記表面層が熱膨張カプセルを含み、
表面層を構成する塗料の固形分１００重量部に対して熱膨張カプセルの含有量が１０〜９０重量部であり、該表面層の目付け量（塗料固形分と熱膨張カプセルを合わせた量）が乾燥状態で２〜１０ｇ／ｍ2であることを特徴とする。
また、本発明の装飾シートでは、合成樹脂層が発泡した発泡合成樹脂層であってもよい。
さらに、本発明の装飾シートは、表面層に異なる２種以上の熱膨張カプセルを使用することができる。
Decorative sheet of the present invention, the base material layer, a synthetic resin layer, design layer, a transparent synthetic resin layer, a decorative sheet comprising a surface layer, said surface layer is observed containing a thermal expansion capsules,
A content of the thermal expansion capsules with respect to 100 parts by weight of the solid content of the coating constituting the surface layer is 10 to 90 parts by weight, the basis weight of the surface layer (the combined amount of paint solids and thermal expansion capsules) are characterized in that in a dry state is 2 to 10 g / m 2.
In the decorative sheet of the present invention, the synthetic resin layer may be a foamed synthetic resin layer.
Furthermore, the decorative sheet of the present invention can use two or more different thermally expanded capsules for the surface layer.
本発明者は、先に、布製敷物の素材感と温か味を持ちながら、清掃の手軽さを兼ね備えた床化粧シートを開発している（特許文献１参照）。
これに対し、本発明の装飾シートでは、透明合成樹脂層の上に設けられる表面層が熱膨張カプセルを含むことが重要である。
熱膨張カプセルが加熱工程により膨張し、柔らかく薄い殻で構成されたセルが装飾シート表面に存在することで、表面に起毛感が発現し、先願の床化粧シートにはないバックスキンやスエードのようなソフトな感触が得られる。
また、このように、各セルには空気が内包されているので、人の皮膚から装飾シートへの熱伝導がこの空気に阻害され、熱が伝わりにくくなり、装飾シート表面に接触した例えば素足などから熱の奪われる量が減少する結果、冷たく感じず、優れた温感性を発現することができる。
The present inventor has previously developed a floor decorative sheet that combines the ease of cleaning with the texture and warm taste of a cloth rug (see Patent Document 1).
On the other hand, in the decorative sheet of the present invention, it is important that the surface layer provided on the transparent synthetic resin layer includes a thermally expanded capsule.
The thermal expansion capsule expands by the heating process, and the cells composed of soft and thin shells are present on the surface of the decorative sheet. A soft feel like this is obtained.
In addition, since air is contained in each cell in this way, heat conduction from the human skin to the decorative sheet is hindered by the air, making it difficult for heat to be transmitted, such as bare feet touching the decorative sheet surface, etc. As a result of the decrease in the amount of heat taken away, it does not feel cold and can exhibit excellent warmth.
本発明の装飾シートは、フローリングやクッションフロアのように水周りでの使用が可能で清掃性に優れていながら、塩化ビニル樹脂製クッションフロア特有の触感（ベタツキ感）は一切無く、バックスキンやスエードのようなソフトな感触や高級感を有するので、これまで畳やカーペット、フローリングが占めいていた場所にも使いたくなるものであり、従来のクッションフロアより用途面積が広い。
しかも、フローリングだと、寒い冬季などに冷たさを感じることから、床暖房やホットカーペットを使用し暖を取ることが多いのに対し、本発明の装飾シートは、接触した例えば素足などから熱の奪われる量が少なく、温感性（冷たく感じ難い）に非常に優れているので、床暖房やホットカーペットを必要とせず、家庭内でのエネルギー使用量の削減（エコ）に繋がるものである。
The decorative sheet of the present invention can be used around water like flooring and cushion floors, and has excellent cleanability, but has no peculiar feeling (stickiness) peculiar to vinyl chloride resin cushion floors. Because of its soft feel and high-class feel, it would be desirable to use it in places where tatami mats, carpets, and flooring had previously occupied, and has a wider application area than conventional cushion floors.
In addition, the flooring often feels cold in cold winter seasons, so it is often warmed by using floor heating or hot carpets, whereas the decorative sheet of the present invention is heated from bare feet, for example. Since the amount taken is small and the thermal sensitivity (it is hard to feel cold) is excellent, it does not require floor heating or hot carpeting, leading to a reduction in energy consumption in the home (eco).
本発明の装飾シートの実施形態を、図１，２に示す概念図、および図３に示す写真により説明する。
本発明の一実施形態例を示す図１において、装飾シート１０は、基材層１、非発泡の合成樹脂層２、意匠層３、透明合成樹脂層４、表面層５とからなり、表面層５が熱膨張カプセル６を含む。また、図２，３は、基材層１と意匠層３との間に発泡合成樹脂層２'が設けられた、本発明の他の実施形態例を示すものである。図１〜２において共通あるいは同一の部分は同じ符号で示している。
An embodiment of the decorative sheet of the present invention will be described with reference to conceptual diagrams shown in FIGS. 1 and 2 and a photograph shown in FIG.
In FIG. 1 showing an embodiment of the present invention, a decorative sheet 10 includes a base layer 1, a non-foamed synthetic resin layer 2, a design layer 3, a transparent synthetic resin layer 4, and a surface layer 5, 5 includes a thermally expanded capsule 6. 2 and 3 show another embodiment of the present invention in which a foamed synthetic resin layer 2 ′ is provided between the base material layer 1 and the design layer 3. 1 and 2, common or identical parts are denoted by the same reference numerals.
基材層１は、装飾シート１０，２０の最下層に設けられる。
基材層１としては、装飾シートの基材として一般的に使用されているものであれば特に限定されず、例えば、繊維に合成樹脂を含浸硬化させたものなどが挙げられる。具体的には、合成繊維、天然繊維、無機繊維の少なくとも１種以上からなる不織布、編布または織布、あるいは、合成樹脂バインダーと各種繊維、パルプ素材とを混抄した混抄紙とすることができる。合成樹脂バインダーとしては、アクリル樹脂、スチレンブタジエンゴムなどが挙げられる。
基材層１は、複数の層から構成されても良く、例えば、合成繊維の織布または不織布と、ガラス繊維の不織布とを積層させてもよい。
The base material layer 1 is provided in the lowermost layer of the decorative sheets 10 and 20.
The base material layer 1 is not particularly limited as long as it is generally used as a base material for a decorative sheet, and examples thereof include a fiber in which a synthetic resin is impregnated and cured. Specifically, it can be a non-woven fabric, knitted fabric or woven fabric composed of at least one of synthetic fibers, natural fibers, and inorganic fibers, or a mixed paper obtained by mixing a synthetic resin binder with various fibers and pulp materials. . Examples of the synthetic resin binder include acrylic resin and styrene butadiene rubber.
The base material layer 1 may be composed of a plurality of layers. For example, a synthetic fiber woven fabric or nonwoven fabric and a glass fiber nonwoven fabric may be laminated.
合成樹脂層２としては、ポリエチレン、ポリプロピレン、エチレン酢酸ビニル樹脂（ＥＶＡ）、エチレンアクリル共重合系樹脂（ＥＭＡ、ＥＭＭＡ、ＥＥＡなど）などのポリオレフィン系樹脂、塩化ビニル系樹脂、アクリル酸エステル共重合樹脂、ウレタン系樹脂、ウレタンアクリレート系樹脂の少なくとも１種以上からなる熱可塑性樹脂が挙げられる。
また、本発明の装飾シートでは、上記合成樹脂層２が発泡した発泡合成樹脂層２’であってもよい。
発泡方法としては、機械発泡でもよく、発泡剤を用いたケミカル発泡でもよい。ケミカル発泡に使用される発泡剤としては、マイクロカプセル等の熱膨張型発泡剤、アゾジカルボン酸（ＡＤＣＡ）、ジニトロソ・ペンタメチレン・テトラミン（ＤＰＩ）、オキシビスベンゼン・スルホニルヒドラジド（ＯＢＳＨ）等の熱分解型発泡剤のいずれも使用できる。樹脂層２’の発泡成形時の加熱温度や加熱時間は、選択される製造方法や樹脂等の材質により適宜選択され得る。
The synthetic resin layer 2 includes polyolefin resins such as polyethylene, polypropylene, ethylene vinyl acetate resin (EVA), and ethylene acrylic copolymer resins (EMA, EMMA, EEA, etc.), vinyl chloride resins, and acrylate copolymer resins. , A thermoplastic resin comprising at least one of a urethane resin and a urethane acrylate resin.
In the decorative sheet of the present invention, the synthetic resin layer 2 may be a foamed synthetic resin layer 2 ′.
The foaming method may be mechanical foaming or chemical foaming using a foaming agent. As foaming agents used for chemical foaming, thermal expansion foaming agents such as microcapsules, heat such as azodicarboxylic acid (ADCA), dinitroso / pentamethylene / tetramine (DPI), oxybisbenzene / sulfonyl hydrazide (OBSH), etc. Any of the decomposable foaming agents can be used. The heating temperature and heating time at the time of foam molding of the resin layer 2 ′ can be appropriately selected depending on the selected manufacturing method and material such as resin.
意匠層３は、例えば、上記合成樹脂層２又は発泡合成樹脂層２'の表面上、または下記で示す透明合成樹脂層４の裏面に、インクジェットプリント、グラビアプリント、スクリーンプリント、オフセットプリント、フレキソプリントなどの一般的なプリント方法を用いて形成することができる。このとき使用されるインクは、酢酸ビニル系、アクリル系、ウレタン系など一般に使用される極性のあるインクを用いればよいが、意匠層３を形成させる層に対して接着性を有するインクであることが好ましい。このインクには、発泡剤を含有させ、意匠層３を発泡させることもできる。
あるいは、合成樹脂層２又は発泡合成樹脂層２’の表面、または透明合成樹脂層４の裏面に、染色を施したり、柄織布、柄編布などを積層したりすることで、意匠層３を構成してもよい。
The design layer 3 is, for example, an inkjet print, a gravure print, a screen print, an offset print, or a flexographic print on the surface of the synthetic resin layer 2 or the foamed synthetic resin layer 2 ′ or the back surface of the transparent synthetic resin layer 4 shown below. It can be formed using a general printing method such as. The ink used at this time may be a commonly used polar ink such as vinyl acetate, acrylic, urethane, etc., but is an ink having adhesiveness to the layer on which the design layer 3 is formed. Is preferred. The ink may contain a foaming agent to foam the design layer 3.
Alternatively, the design layer 3 can be obtained by dyeing or laminating a patterned woven fabric, a patterned knitted fabric, or the like on the surface of the synthetic resin layer 2 or the foamed synthetic resin layer 2 ′ or the back surface of the transparent synthetic resin layer 4. May be configured.
透明合成樹脂層４は、その下層にある意匠層３の意匠を視認できるものであれば、透明な樹脂に限定されず、半透明な樹脂であってもよく、顔料や染料によって着色されたものであってもよい。透明合成樹脂層４の厚みは、通常０．０５〜０．５０ｍｍ程度である。
透明合成樹脂層４を構成する樹脂としては、ポリオレフィン系樹脂、塩化ビニル系樹脂、アクリル酸エステル共重合樹脂、ウレタン系樹脂、ウレタンアクリレート系樹脂等の少なくとも１種の熱可塑性樹脂からなることが好ましく、それら熱可塑性樹脂は、エマルジョンタイプであっても、溶剤タイプであってもよい。
なお、製造後の装飾シート１０，２０の表面に折りしわが付くことを防止したり、表面のベタツキ感を防止したりするために、透明合成樹脂層４の表面上に、ロータリースクリーンプリント（ＲＳＰ）やメカニカルエンボスなどで凹凸を設けておくこともできる。
The transparent synthetic resin layer 4 is not limited to a transparent resin as long as the design of the design layer 3 in the lower layer can be visually recognized. The transparent synthetic resin layer 4 may be a translucent resin and is colored with a pigment or a dye. It may be. The thickness of the transparent synthetic resin layer 4 is usually about 0.05 to 0.50 mm.
The resin constituting the transparent synthetic resin layer 4 is preferably made of at least one thermoplastic resin such as polyolefin resin, vinyl chloride resin, acrylate copolymer resin, urethane resin, or urethane acrylate resin. These thermoplastic resins may be an emulsion type or a solvent type.
In addition, in order to prevent the surface of the decorative sheets 10 and 20 after manufacture from being wrinkled or to prevent the surface from becoming sticky, a rotary screen print (RSP) is provided on the surface of the transparent synthetic resin layer 4. ) Or mechanical embossing.
表面層５は、上記のような透明合成樹脂層４の上に設けられ、装飾シート１０，２０の最上層を構成する。本発明では、表面層５が熱膨張カプセル６を含むことが重要である。
表面層５は、例えば、塗料に熱膨張カプセル６を分散した処理液を、ロールコーター、グラビアコーター、グラビア・オフセットロールコーターなどの薄膜塗布装置にて、所定の目付け量で塗布し、熱風乾燥機、ヒーター加熱装置、誘電加熱装置などで加熱（乾燥）処理し、塗料を乾燥させ、かつ熱膨張カプセル６を膨張させることで設けることができる。
上記目付け量は、透明合成樹脂層４の厚みによっても左右されるが、少なすぎると、本発明が目的とする所望の効果（ソフト感や温感）が十分に得られず、多すぎれば、下層にある意匠層３の意匠を視認しづらくなるばかりか、カプセルの付着量が過剰となり表面凹凸が増え水周り使用適正が損なわれる傾向（水などが滲みやすい、ふき取りにくい）にあるので、乾燥状態で２〜１０ｇ／ｍ2であることが好ましく、より好ましくは３〜７ｇ／ｍ2である。
The surface layer 5 is provided on the transparent synthetic resin layer 4 as described above, and constitutes the uppermost layer of the decorative sheets 10 and 20. In the present invention, it is important that the surface layer 5 includes the thermal expansion capsule 6.
The surface layer 5 is, for example, coated with a treatment liquid in which the thermally expanded capsule 6 is dispersed in a coating material with a predetermined basis weight using a thin film coating apparatus such as a roll coater, a gravure coater, or a gravure / offset roll coater. It can be provided by heating (drying) treatment with a heater heating device, dielectric heating device or the like, drying the paint, and expanding the thermally expandable capsule 6.
The weight per unit area depends on the thickness of the transparent synthetic resin layer 4, but if it is too small, the desired effect of the present invention (soft feeling and warm feeling) cannot be obtained sufficiently, and if it is too much, Not only is it difficult to visually recognize the design of the design layer 3 in the lower layer, but the amount of capsules attached becomes excessive, surface irregularities increase, and the water use suitability tends to be impaired (water is likely to bleed and difficult to wipe off). It is preferable that it is 2-10 g / m < 2 > in a state, More preferably, it is 3-7 g / m < 2 >.
熱膨張カプセル６としては、例えば、液状の低沸点炭化水素（イソブタン、イソペンタンなど）を熱可塑性樹脂（アクリル系共重合体樹脂など）の殻内に封入したもので、加熱処理により２０〜７０倍程度（体積）に膨張するものであればよく、一般に市販されているものをそのまま用いることができる。
熱膨張カプセルのサイズについては、小さすぎると、本発明が目的とする所望の効果（ソフト感や温感）が十分に得られず、大きすぎると、透明合成樹脂層４上に付着し難くなるので、膨張前の平均粒子径が５〜５０μｍ程度のものが好ましい。
As the thermal expansion capsule 6, for example, a liquid low boiling point hydrocarbon (isobutane, isopentane, etc.) is enclosed in a shell of a thermoplastic resin (acrylic copolymer resin, etc.), which is 20 to 70 times larger by heat treatment. What expand | swells to a grade (volume) should just be used, and what is generally marketed can be used as it is.
If the size of the thermal expansion capsule is too small, the desired effect (soft feeling and warm feeling) intended by the present invention cannot be obtained sufficiently, and if it is too large, it is difficult to adhere to the transparent synthetic resin layer 4. Therefore, the thing of the average particle diameter before expansion | swelling about 5-50 micrometers is preferable.
熱膨張カプセルを膨張させるための加熱処理条件（温度や時間など）は、発泡層の有無をはじめとして各層の構成素材などにしたがって適宜選択される。
例えば、図２に示すように発泡合成樹脂層２’が設けられる場合、加熱処理温度が１５０〜１８０℃、加熱処理時間が２０〜６０秒とすることが好ましい。熱量（加熱処理温度×加熱処理時間）が高すぎると、発泡合成樹脂層２’が２次発泡を起こし、製品とならないからである。
したがって、熱膨張カプセルの膨張開始温度や最大膨張温度については、加熱処理条件にもよるため一概には決められないが、一般には、膨張開始温度は９０〜１５０℃程度、最大膨張温度は１１０〜１８０℃程度のものを用いればよい。なお、膨張開始温度が７０℃以下のカプセルでは、装飾シートを使用する段階で直射日光などで床面が温まった際に熱膨張してしまう虞がある。
The heat treatment conditions (temperature, time, etc.) for expanding the thermally expanded capsule are appropriately selected according to the constituent materials of each layer, including the presence or absence of the foamed layer.
For example, when the foamed synthetic resin layer 2 ′ is provided as shown in FIG. 2, the heat treatment temperature is preferably 150 to 180 ° C. and the heat treatment time is 20 to 60 seconds. This is because if the amount of heat (heat treatment temperature × heat treatment time) is too high, the foamed synthetic resin layer 2 ′ undergoes secondary foaming and does not become a product.
Therefore, the expansion start temperature and the maximum expansion temperature of the thermally expanded capsule cannot be determined unconditionally because they depend on the heat treatment conditions. In general, the expansion start temperature is about 90 to 150 ° C., and the maximum expansion temperature is 110 to 110 ° C. What is about 180 degreeC should just be used. For capsules having an expansion start temperature of 70 ° C. or lower, there is a risk of thermal expansion when the floor surface is warmed by direct sunlight at the stage of using the decorative sheet.
本発明では、装飾シートの意匠性や、熱膨張カプセルの付着性を高めるために、色や粒径、膨張開始温度、膨張率、構成材などにおいて異なる熱膨張カプセルを２種以上組み合わせて用いることもできる。
このとき、複数種の熱膨張カプセルを処理液中に分散混合させた塗料を塗布してもよいし、種類の異なるカプセル毎に分散させる処理液を分けて、重ね塗りすることもできる。
In the present invention, in order to enhance the design properties of the decorative sheet and the adhesiveness of the thermal expansion capsule, two or more types of thermal expansion capsules different in color, particle size, expansion start temperature, expansion rate, constituent material, etc. are used in combination. You can also.
At this time, a coating material in which a plurality of types of thermally expanded capsules are dispersed and mixed in the processing liquid may be applied, or the processing liquids to be dispersed for different types of capsules may be divided and overcoated.
このような熱膨張カプセルを分散させる処理液については、熱膨張カプセル６と透明合成樹脂層４との両方に密着性が良いものを選択すればよい。具体的には、ウレタン系樹脂、ウレタンアクリレート系樹脂、アクリル系樹脂などのバインダー樹脂を、一般的な溶剤に固形分５〜４０％で配合したものなどが挙げられる。また、環境や（熱膨張カプセルを分散した後の）保存安定性などを考慮すると、溶剤の代わりに水を用いてもよい。
なお、より確実にソフトな感触を得るために、硬度の低いバインダー樹脂を選択することが好ましい。
As for the treatment liquid in which such thermally expanded capsules are dispersed, a liquid having good adhesion to both the thermally expanded capsule 6 and the transparent synthetic resin layer 4 may be selected. Specifically, what blended binder resin, such as urethane type resin, urethane acrylate type resin, and acrylic resin, in a general solvent with a solid content of 5 to 40%, etc. are mentioned. In consideration of the environment and storage stability (after dispersing the thermally expanded capsule), water may be used instead of the solvent.
In order to obtain a soft feel more surely, it is preferable to select a binder resin having a low hardness.
上記処理液において、塗料の固形分１００重量部に対する熱膨張カプセルの含有量は１０〜９０重量部が好適である。
塗料の固形分に対して、熱膨張カプセルの配合量が少なすぎると、本発明が目的とする所望の効果（ソフト感や温感）が十分に得られず、多すぎると、下層にある意匠層３の意匠の視認性が阻害されるばかりか、装飾シートとしての使用時にカプセルの脱落が生じやすい。
このように、塗料中のバインダー樹脂分にて、加熱により膨らんだ熱膨張カプセル６が、装飾シート１０，２０の透明合成樹脂層４に固着される。本発明では、図３（Ａ）及び（Ｂ）に示すように、熱膨張カプセルの加熱処理条件などにより、熱膨張カプセル６の発泡度合いが異なるので、要求されるソフト感、又は基材や熱膨張カプセル等の種類によって、適した加熱処理条件を選択することが好ましい。
In the treatment liquid, the content of the thermally expanded capsule is preferably 10 to 90 parts by weight with respect to 100 parts by weight of the solid content of the paint.
If the amount of the thermally expanded capsule is too small relative to the solid content of the paint, the desired effect (soft feeling and warm feeling) intended by the present invention cannot be obtained sufficiently. Not only is the visibility of the design of the layer 3 impaired, but the capsule is likely to fall off when used as a decorative sheet.
In this way, the thermally expandable capsule 6 swelled by heating with the binder resin content in the paint is fixed to the transparent synthetic resin layer 4 of the decorative sheets 10 and 20. In the present invention, as shown in FIGS. 3A and 3B, the degree of foaming of the thermally expandable capsule 6 varies depending on the heat treatment conditions of the thermally expandable capsule. It is preferable to select suitable heat treatment conditions depending on the type of the expanded capsule or the like.
本発明では、必要に応じて、本発明の特性を損なわない範囲で、基材層１、合成樹脂層２又は発泡合成樹脂層２’、意匠層３、透明合成樹脂層４、表面層５において、無機充填剤、安定剤、帯電防止剤、滑剤、殺菌剤、防虫剤、着色剤などの各種添加剤を適宜添加することができる。
これらの添加剤としては、通常の装飾シートに配合する通常のものが使用できる。
In this invention, in the range which does not impair the characteristic of this invention as needed, in base material layer 1, synthetic resin layer 2 or foaming synthetic resin layer 2 ', design layer 3, transparent synthetic resin layer 4, and surface layer 5, Various additives such as inorganic fillers, stabilizers, antistatic agents, lubricants, bactericides, insect repellents, and coloring agents can be appropriately added.
As these additives, ordinary additives blended in an ordinary decorative sheet can be used.
本発明の装飾シート１０，２０の全厚みは、１．０〜５．０ｍｍ程度であり、好ましくは１．５〜３．０ｍｍである。 The total thickness of the decorative sheets 10 and 20 of the present invention is about 1.0 to 5.0 mm, preferably 1.5 to 3.0 mm.
以上のような本発明の装飾シート１０（発泡層を含まない）の製造方法は、例えば、以下のような手順で行うことができる。
１）基材層１上に非発泡の樹脂層２を塗布加熱成形し、その上に意匠層３を設け、さらに透明合成樹脂層４を塗布加熱形成する。
２）必要に応じて、透明合成樹脂層４の表面上に、ロータリースクリーンプリント（ＲＳＰ）またはメカニカルエンボス、或いは両方で凹凸を設ける。
３）続いて、透明合成樹脂層４上に、熱膨張カプセル６を含む表面層５を設ける。
The method for producing the decorative sheet 10 (not including the foamed layer) of the present invention as described above can be performed, for example, by the following procedure.
1) A non-foamed resin layer 2 is applied and heat-molded on the base material layer 1, a design layer 3 is provided thereon, and a transparent synthetic resin layer 4 is further applied and heated.
2) If necessary, unevenness is provided on the surface of the transparent synthetic resin layer 4 by rotary screen printing (RSP), mechanical embossing, or both.
3) Subsequently, the surface layer 5 including the thermal expansion capsule 6 is provided on the transparent synthetic resin layer 4.
また、本発明の装飾シート２０（発泡層を含む）の製造方法は、例えば、以下のような手順で行うことができる。
１）基材層１上に、発泡剤を含有した樹脂層２’を塗布加熱形成（非発泡で）し、その上に意匠層３を設け、さらに透明合成樹脂層４を塗布加熱形成し、さらに樹脂層２’を加熱発泡する。
２）必要に応じて、透明合成樹脂層４の表面上に、ロータリースクリーンプリント（ＲＳＰ）またはメカニカルエンボス、或いは両方で凹凸を設ける。ただし、ＲＳＰの場合は、上記１）の加熱発泡前に塗布する。
３）続いて、透明合成樹脂層４上に、熱膨張カプセル６を含む表面層５を設ける。
Moreover, the manufacturing method of the decoration sheet | seat 20 (a foaming layer is included) of this invention can be performed in the following procedures, for example.
1) A resin layer 2 ′ containing a foaming agent is applied and heated (non-foamed) on the base material layer 1, a design layer 3 is provided thereon, and a transparent synthetic resin layer 4 is further applied and heated. Further, the resin layer 2 ′ is heated and foamed.
2) If necessary, unevenness is provided on the surface of the transparent synthetic resin layer 4 by rotary screen printing (RSP), mechanical embossing, or both. However, in the case of RSP, it is applied before heating and foaming in 1) above.
3) Subsequently, the surface layer 5 including the thermal expansion capsule 6 is provided on the transparent synthetic resin layer 4.
〔塗料に熱膨張カプセルを分散した処理液の調製〕
調製例１
溶剤系塗料（大日精化社製 商品名“ダイプラコート ワニス ＥＳＣ−７３９７”）の固形分１００重量部に対し、熱膨張カプセル（同社製 商品名“ダイフォーム Ｍ４３０Ｄ”）を５９重量部配合して、固形分２５％の処理液Ａを調製した。
[Preparation of treatment liquid with thermally expanded capsules dispersed in paint]
Preparation Example 1
59 parts by weight of thermal expansion capsule (trade name “Daifoam M430D” manufactured by the company) is added to 100 parts by weight of the solid content of solvent-based paint (trade name “Daipla Coat Varnish ESC-7397” manufactured by Dainichi Seika Co., Ltd.) A treatment liquid A having a solid content of 25% was prepared.
調製例２
調製例１と同じ溶剤系塗料の固形分１００重量部に対し、膨張開始温度の異なる２種の熱膨張カプセル（同社製 商品名“ダイフォーム Ｍ４３０Ｄ”：同社製 商品名“同 Ｈ７５０Ｄ”＝１：１の割合）を５９重量部配合して、固形分２５％の処理液Ｂを調製した。
Preparation Example 2
Two types of thermal expansion capsules having different expansion start temperatures with respect to 100 parts by weight of the solid content of the same solvent-based paint as in Preparation Example 1 (trade name “Daifoam M430D” manufactured by the same company: product name “H750D” manufactured by the same company = 1) 1 part) was mixed in an amount of 59 parts by weight to prepare a treatment liquid B having a solid content of 25%.
〔（発泡層を含まない）装飾シートの製造〕
実施例２〜７，９、比較例５，６
厚さ０．２ｍｍのガラス混抄紙である基材層の上に、厚さ１．５ｍｍの塩化ビニル樹脂層を形成（ペースト加工にて）し、更にグラビアプリント機にて印刷を施すことで意匠層を形成し、その上に厚さ０．３ｍｍの塩化ビニル系樹脂製の透明合成樹脂層を形成（ペースト加工にて）し、加熱キュアした後に、表面加熱し押し型にてエンボス加工を施した（第１工程品）。
次に、第１工程品の表面（透明合成樹脂層側）に、表１に示す処理液を表面処理装置（グラビアロールコーター）にて、表１に示す目付け量（ｇ／ｍ2）にて塗布した。
続いて、熱風乾燥機にて、加熱処理（１７０℃×３０秒）を施し、処理液の溶媒を乾燥させつつ、熱膨張カプセルを膨らませ、本体（第１工程品）に固着させ、厚さがおよそ２ｍｍの装飾シートを得た。
[Manufacture of decorative sheet (not including foam layer)]
Examples 2-7, 9 and Comparative Examples 5, 6
Design by forming a vinyl chloride resin layer with a thickness of 1.5 mm on the base material layer, which is a glass mixed paper with a thickness of 0.2 mm (by pasting), and then printing with a gravure printing machine A transparent synthetic resin layer made of vinyl chloride resin with a thickness of 0.3 mm is formed on it (by paste processing), and after heat curing, the surface is heated and embossed with a pressing die. (First step product).
Next, on the surface of the first step product (transparent synthetic resin layer side), the treatment liquid shown in Table 1 is applied with a surface treatment device (gravure roll coater), and the basis weight (g / m 2 ) shown in Table 1. Applied.
Subsequently, in a hot air dryer, heat treatment (170 ° C. × 30 seconds) is performed, the solvent of the treatment liquid is dried, the thermal expansion capsule is expanded, and is fixed to the main body (first process product). An approximately 2 mm decorative sheet was obtained.
参考例１〜３
家庭用の装飾シートとして一般的に用いられているフローリングを参考例１、畳を参考例２、カーペットを参考例３とした。
Reference Examples 1-3
The flooring generally used as a decorative sheet for home use was set as Reference Example 1, the tatami mat as Reference Example 2, and the carpet as Reference Example 3.
得られた装飾シートについて、（Ａ）表面のソフト感、（Ｂ）水周りでの使用適性、（Ｃ）温感性、および（Ｄ）意匠性を下記の評価方法で評価した。なお、参考例１〜３については、（Ａ）、（Ｂ）、（Ｃ）のみ評価を行った。結果を併せて表１に示す。 About the obtained decorative sheet, (A) soft feeling of the surface, (B) suitability for use around water, (C) warm sensitivity, and (D) designability were evaluated by the following evaluation methods. For Reference Examples 1 to 3, only (A), (B), and (C) were evaluated. The results are also shown in Table 1.
（Ａ）表面のソフト感について、以下の基準で手の触感により評価した。
スエードやバックスキンのような優れた柔らかさがある：◎
柔らかさがある：○
カプセルの脱落が多少あり、柔らかさにやや劣る：△
従来の塩化ビニル樹脂製クッションフロアと大差無し：×
（Ｂ）水周りでの使用適性について、コップ１杯の水をこぼした直後の表面を雑巾で拭き、以下の基準で評価した。
こぼれた水が滲むことなく拭き取れる：◎
こぼれた水が滲むことはないが、拭き取りにくい：○
こぼれた水が少々滲み、僅かにしみとして残る：△
こぼれた水が滲み、しみがとれない：×
（Ｃ）温感性について、室温５℃の部屋の中で各々の表面上に素足で立ち、以下の基準で評価した。
冷たく感じない：◎
あまり冷たく感じない：○
やや冷たく感じる：△
冷たく感じる：×
（Ｄ）意匠性について、表面層を設けることによる意匠層の視認度合いを、表面層を設けない場合と比較して、以下の基準で評価した。
表面層を設けない場合と同程度に、意匠層が視認できる：◎
表面層を設けない場合よりも若干劣るが、意匠層が問題なく視認できる：○
表面層を設けない場合よりも劣り、意匠層が視認し難い：△
意匠層が視認できない：×
(A) About the soft feeling of the surface, it evaluated by the touch feeling of the hand on the following references | standards.
Excellent softness like suede and backskin: ◎
There is softness: ○
There is some dropout of the capsule, and it is slightly inferior in softness: △
No significant difference from conventional vinyl chloride resin cushion floor: ×
(B) About the suitability for use around water, the surface immediately after spilling a glass of water was wiped with a rag and evaluated according to the following criteria.
The spilled water can be wiped off without bleeding: ◎
Spilled water will not bleed, but difficult to wipe off: ○
Spilled water slightly blots and remains as a slight stain: △
Spilled water bleeds and stains cannot be removed: ×
(C) About temperature sensitivity, it stood on each surface in the room | chamber temperature of 5 degreeC with bare feet, and evaluated by the following references | standards.
Does not feel cold: ◎
Does not feel too cold: ○
Feel slightly cold: △
Feel cold: ×
(D) About the design property, the visual recognition degree of the design layer by providing a surface layer was evaluated on the following criteria compared with the case where a surface layer was not provided.
The design layer is visible as much as when no surface layer is provided:
Although slightly inferior to the case where no surface layer is provided, the design layer can be visually recognized without problems:
It is inferior to the case where no surface layer is provided, and the design layer is difficult to visually recognize: Δ
The design layer is not visible: ×
表１に示すとおり、実施例３〜６の装飾シートは、上記（Ａ）〜（Ｃ）については全て「◎」の評価が得られ、かつ（Ｄ）意匠性も「○」又は「◎」と、特に優れるものであった。
また、実施例９の装飾シートは、意匠が他の実施例よりも立体的に見えるものであった。
As shown in Table 1, the decorative sheets of Examples 3 to 6 are all evaluated as “◎” for the above (A) to (C), and (D) the design properties are also “◯” or “」 ”. And it was particularly excellent.
In the decorative sheet of Example 9, the design looks more three-dimensional than the other examples.
〔（発泡層を含む）装飾シートの製造〕
実施例１０−１〜１０−１９
厚さ０．２ｍｍのガラス混抄紙である基材層の上に、厚さ０．３ｍｍの発泡剤（ＡＤＣＡ）を含んだ塩化ビニル樹脂ペーストを積層し加熱ゲル化してシートを形成し、更にグラビアプリント機にて印刷を施すことで意匠層を形成し、その上に厚さ０．１５ｍｍの塩化ビニル系樹脂製の透明合成樹脂層を形成（ペースト加工にて）し、更にその上に塩化ビニル樹脂ペーストをロータリースクリーンプリントで塗布し、表面凹凸意匠を形成した後、発泡ベース層を加熱発泡した（第１工程品）。
次に、第１工程品の表面（透明合成樹脂層側）に、調製例１で得た処理液Ａをグラビアロールコーターにて、目付け量５ｇ／ｍ2（乾燥状態）にて塗布した。
続いて、熱風乾燥機にて、表２に示す温度および時間（秒）にて加熱処理を施し、処理液の溶媒を乾燥させつつ、熱膨張カプセルを膨らませ、本体（第１工程品）に固着させ、厚さがおよそ１．８ｍｍの装飾シートを得た。
[Manufacture of decorative sheet (including foam layer)]
Examples 10-1 to 10-19
A vinyl chloride resin paste containing a foaming agent (ADCA) with a thickness of 0.3 mm is laminated on a base material layer, which is a glass mixed paper with a thickness of 0.2 mm, and heated to gel to form a sheet. A design layer is formed by printing on a printing machine, a transparent synthetic resin layer made of a vinyl chloride resin having a thickness of 0.15 mm is formed thereon (by paste processing), and further vinyl chloride is formed thereon. The resin paste was applied by rotary screen printing to form a surface asperity design, and then the foamed base layer was heated and foamed (first process product).
Next, the treatment liquid A obtained in Preparation Example 1 was applied to the surface of the first step product (transparent synthetic resin layer side) with a gravure roll coater at a basis weight of 5 g / m 2 (dry state).
Subsequently, heat treatment was performed at a temperature and time (seconds) shown in Table 2 with a hot air dryer, and the thermally expanded capsule was expanded while drying the solvent of the treatment liquid, and fixed to the main body (first process product). A decorative sheet having a thickness of about 1.8 mm was obtained.
得られた各装飾シートについて、前述と同様の評価方法に基づき、（Ｂ）水周りでの使用適性、（Ｃ）温感性、および（Ｄ）意匠性について評価した。結果を併せて表２に示す。
なお、「（Ａ）表面のソフト感」の代わりに「（Ａ'）熱膨張カプセルの発泡状態」について、以下の基準で評価した。
所望の膨張倍率が得られ、（スエードやバックスキンのような）起毛感が得られた：◎
膨張が不十分なものもあるが、起毛感は得られた：○
膨張が不十分なものが多く、起毛感があまり得られなかった：△
殆ど膨張していない状態で、起毛感が全く得られなかった（従来の塩化ビニル樹脂製クッションフロアの触感と大差無し）：×
About each obtained decoration sheet, based on the evaluation method similar to the above-mentioned , (B) Usability around water, (C) Warmth sensitivity, and (D) Designability were evaluated. The results are also shown in Table 2.
In addition, instead of “(A) surface soft feeling”, “(A ′) foamed state of thermally expanded capsule” was evaluated according to the following criteria.
The desired expansion ratio was obtained, and a raised feeling (like suede or backskin) was obtained:
Although some of the swelling was insufficient, a feeling of brushing was obtained: ○
There were many things with insufficient expansion, and the feeling of raising was not obtained so much:
In the almost unexpanded state, no brushed feeling was obtained (no significant difference from the tactile feel of the conventional vinyl chloride resin cushion floor): ×
表２に示すとおり、実施例１０−２，３，６，７，９，１０，１１，１３，１６の装飾シートは全て（Ａ'）〜（Ｄ）の評価項目において「◎」であった。
また、実施例１０−１０、１０−１１で得られた装飾シートの表面について一部拡大した写真を、図３（Ａ）、図３（Ｂ）にそれぞれ示す。これら写真から、実施例１０−１１では、実施例１０−１０に比べて、熱膨張カプセルが発泡していることがわかる。
As shown in Table 2, all the decorative sheets of Examples 10-2, 3, 6, 7, 9, 10, 11, 13, and 16 were “◎” in the evaluation items (A ′) to (D). .
Moreover, the photograph which expanded partially about the surface of the decoration sheet obtained in Example 10-10, 10-11 is shown to FIG. 3 (A) and FIG. 3 (B), respectively. From these photographs, it can be seen that in Example 10-11, the thermally expanded capsule is foamed as compared to Example 10-10.
実施例１１
処理液Ｂを用いた以外は、実施例１０−１０と同様にして厚さが１．８ｍｍの装飾シートを得た。
Example 11
A decorative sheet having a thickness of 1.8 mm was obtained in the same manner as in Example 10-10 except that the treatment liquid B was used.
比較例１〜３
比較例５における第１工程品を比較例１、実施例１０における第１工程品を比較例２とした。
実施例１０における表面凹凸意匠の形成を、ロータリースクリーンプリントではなくメカニカルエンボスにて施した第１工程品を比較例３とした。
Comparative Examples 1-3
The first process product in Comparative Example 5 was designated as Comparative Example 1, and the first process product in Example 10 was designated as Comparative Example 2.
The first step product in which the formation of the surface unevenness design in Example 10 was performed by mechanical embossing instead of rotary screen printing was referred to as Comparative Example 3.
比較例４
実施例１０の第１工程において、凹凸加工を施すためのロータリースクリーンプリント（ＲＳＰ）に用いる塩化ビニル樹脂ペーストに熱膨張カプセルを混入し、発泡ベース層を発泡させる際に熱膨張カプセルをも膨張させ、比較例４とした。なお、塩化ビニル樹脂ペーストへの熱膨張カプセルの添加量は、塩化ビニル樹脂ペースト１００重量部に対して１０重量部とした。
Comparative Example 4
In the first step of Example 10, the thermally expandable capsule is mixed with the vinyl chloride resin paste used for the rotary screen print (RSP) for roughening, and the thermally expanded capsule is also expanded when foaming the foam base layer. Comparative Example 4 was obtained. The amount of thermally expanded capsule added to the vinyl chloride resin paste was 10 parts by weight with respect to 100 parts by weight of the vinyl chloride resin paste.
実施例１１および比較例１〜４の装飾シートについて、（Ａ）表面のソフト感、（Ｂ）水周りでの使用適性、（Ｃ）温感性、および（Ｄ）意匠性を前述と同様の評価方法で評価した。結果を表３に示す。 About the decorative sheet of Example 11 and Comparative Examples 1-4, (A) soft feeling of the surface, (B) suitability for use around water, (C) warmth sensitivity, and (D) designability as described above The method was evaluated. The results are shown in Table 3.
表１より、目付け量が少なすぎると、所望とするソフト感を得られるだけの効果が出せず、また、多すぎると、下の意匠が見え難く或いは見えなくなるばかりでなく、カプセルの固着が弱くなり、脱落するので、結果として表面のソフト感が得られ難く、適切な量を設定する必要があった。
また、表２より、実施例１０のように発泡層を有するシートへの加工の場合は、処理液の乾燥（加熱処理）条件にも制限され、発泡が不十分な状態（加工温度が低い、短時間の加熱）では、ソフト感や温感性が得られない傾向にある。また過発泡状態までの加熱（加工温度が高い、長時間の加熱）でもソフト感や温感性を得られない傾向にある。
結果、熱膨張カプセルを混入する処理液の処方としては「塗料の固形分」１００重量部に対して熱膨張カプセルが１０〜９０重量部であり、処理液の目付けが「乾燥状態で２〜１０ｇ／ｍ2」望ましくは「３〜７ｇ／ｍ2」であることがわかった。また、本処方での実施例においては、実用上の問題はないものであった。
From Table 1, if the basis weight is too small, an effect sufficient to obtain a desired soft feeling cannot be obtained, and if it is too large, not only the design below is difficult to see or disappear, but also the capsule is weakly fixed. As a result, it is difficult to obtain a soft feeling of the surface, and it is necessary to set an appropriate amount.
Further, from Table 2, in the case of processing into a sheet having a foamed layer as in Example 10, it is also limited to the drying (heat treatment) conditions of the treatment liquid, and foaming is insufficient (processing temperature is low, In short heating, there is a tendency that a soft feeling and warm feeling cannot be obtained. In addition, even when heated to an excessively foamed state (processing temperature is high, heating for a long time), there is a tendency that a soft feeling and warm feeling cannot be obtained.
As a result, the prescription of the treatment liquid in which the thermally expanded capsule is mixed is 10 to 90 parts by weight of the thermally expanded capsule with respect to 100 parts by weight of “solid content of paint”, and the basis weight of the treatment liquid is “2 to 10 g in a dry state” / M 2 ”, preferably“ 3-7 g / m 2 ”. Moreover, in the Example by this prescription, there was no problem in practical use.
本発明の装飾シートは、ソフトな触感や高級感を有するうえ、温感性があり、しかも水や汚れを拭き掃除で簡単に除去できるものである。
このため、本発明による装飾シートは、従来のクッションフロアのように台所、トイレ、洗面所等の水周りに使用できると共に、スエードやバックスキンのような高級感のある敷物として使用することもできる。また、施工を伴わないものなので、トイレや洗面所などの床タイル、ダイニングや居間、子供部屋などのフローリング、寝室や客間の畳など様々な箇所に置き敷くことができるものである。
さらに、温感性に優れているので、基材層を耐水性のものとすることで、寒い冬季に浴室の洗い場に敷くことも有益である。
The decorative sheet of the present invention has a soft tactile sensation and a high-class feeling, is warm, and can easily remove water and dirt by wiping and cleaning.
For this reason, the decorative sheet according to the present invention can be used around the water in kitchens, toilets, washrooms, etc. like a conventional cushion floor, and can also be used as a high-quality rug such as a suede or a back skin. . In addition, because it does not involve construction, it can be laid in various places such as floor tiles such as toilets and washrooms, dining and living rooms, flooring in children's rooms, and tatami mats between bedrooms and guests.
Furthermore, since it is excellent in temperature sensitivity, it is also beneficial to make the base material layer water-resistant so that it is laid in a bathroom washing place in the cold winter season.
１ 基材層
２ 合成樹脂層
２’ 発泡合成樹脂層
３ 意匠層
４ 透明合成樹脂層
５ 表面層
６ 熱膨張カプセル
１０，２０ 装飾シート
DESCRIPTION OF SYMBOLS 1 Base material layer 2 Synthetic resin layer 2 'Foamed synthetic resin layer 3 Design layer 4 Transparent synthetic resin layer 5 Surface layer 6 Thermal expansion capsule 10,20 Decoration sheet
Claims (3)