JP5500570B2 - Pressure sensitive transfer adhesive tape for personal information protection - Google Patents
Pressure sensitive transfer adhesive tape for personal information protection Download PDFInfo
- Publication number
- JP5500570B2 JP5500570B2 JP2009008471A JP2009008471A JP5500570B2 JP 5500570 B2 JP5500570 B2 JP 5500570B2 JP 2009008471 A JP2009008471 A JP 2009008471A JP 2009008471 A JP2009008471 A JP 2009008471A JP 5500570 B2 JP5500570 B2 JP 5500570B2
- Authority
- JP
- Japan
- Prior art keywords
- adhesive layer
- adhesive
- pressure
- sensitive
- transfer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、基材に接着層を形成し、塗膜転写具を用いて圧力で基材から剥離させて接着層を転写させる感圧転写接着テープに関し、特に接着層を濃色にして、個人情報などの文字が記載された紙などに転写することで、個人情報などが判読できない個人情報保護用感圧転写接着テープに関するものである。 The present invention relates to a pressure-sensitive transfer adhesive tape in which an adhesive layer is formed on a substrate, and peeled off from the substrate with pressure using a coating film transfer tool to transfer the adhesive layer. The present invention relates to a pressure sensitive transfer adhesive tape for personal information protection in which personal information or the like cannot be read by transferring it to paper or the like on which characters such as information are written.
近年、企業や一般家庭において個人情報保護の重要性に関する認識が高まってきている中、名前や住所などの個人情報が記載された紙（書類、封筒、はがき）などを廃棄するときに、第三者に個人情報を判読できない状態にしてから廃棄することが望まれており、個人情報保護に関する商品が多く販売されるようになった。 In recent years, the recognition of the importance of protecting personal information in corporations and general households has increased. When paper (documents, envelopes, postcards) with personal information such as names and addresses is discarded, It has been desired to dispose of personal information after it has been unreadable by the consumer, and many products related to personal information protection have been sold.
廃棄するときに、記載された個人情報などが判読できなくする方法としては、個人情報が記載された紙（書類、封筒、はがき）などを細かく裁断する方法がある。そのような裁断機いわゆるシュレッダーは、すでに商品として販売されており、電動式のものや手動式のものなどがある。手動式のものとして、鋏形状で裁断可能な「シュレッダーはさみ」というものもある。 As a method of making the personal information described in the document unreadable when discarded, there is a method of finely cutting a paper (document, envelope, postcard) or the like on which the personal information is described. Such a cutting machine, a so-called shredder, is already sold as a product, and there are an electric type and a manual type. As a manual type, there is also a “shredder scissors” that can be cut in a bowl shape.
細かく裁断する方法以外で、個人情報などが判読できなくする方法として、特開２００４−２７２１７７号公報のように、遮蔽層を構成したシールで個人情報を隠す方法があり、マーカーで塗りつぶす方法、スタンプで個人情報を隠す方法などもある。スタンプも、ベタ柄のだけでなく、意匠登録第１３３５７１３号公報のように、スタンプ画像（スタンプ印面）を工夫して、スタンプ画像の文字や画像によって、個人情報などが判読することを困難にしている「個人情報保護用スタンプ」も販売されている。これらはその手軽さから、多くのユーザーに支持されている。 Other than the method of finely cutting, as a method of making personal information unreadable, there is a method of hiding personal information with a seal comprising a shielding layer as disclosed in Japanese Patent Application Laid-Open No. 2004-272177, a method of painting with a marker, a stamp There is also a method of hiding personal information. The stamp is not only a solid pattern, but also a design of the stamp image (stamp stamp face) as in Design Registration No. 1335713, making it difficult to read personal information by the characters and images of the stamp image. The “personal information protection stamp” is also on sale. These are supported by many users because of their simplicity.
このように、個人情報が記載された紙（書類、封筒、はがき）などを廃棄するときに、第三者に個人情報が読み取られることを困難にする方法としては、個人情報が記載された紙などを細かく裁断する方法と、個人情報をシールやスタンプで隠す方法がある。 In this way, when disposing of paper (documents, envelopes, postcards, etc.) on which personal information is written, as a method to make it difficult for a third party to read the personal information, paper on which personal information is written There are a method of finely cutting such information and a method of hiding personal information with a sticker or stamp.
細かく裁断する方法として、電動式のシュレッダーは装置自体が大きいため、設置場所が必要であり、価格も高いという問題がある。手動式のものは、人が労力を費やす必要があり、裁断するのに手間隙がかかるという問題がある。 As a method of finely cutting, an electric shredder has a problem that the apparatus itself is large, so an installation place is required and the price is high. In the manual type, there is a problem that it is necessary for a person to spend labor, and it takes time to cut.
隠す方法として、シールは、剥離紙などの余分な廃棄物が出てしまい、昨今の環境問題に合っていない。マーカーやベタ柄のスタンプは、インクが紙に染み込み、個人情報の文字がレーザプリンタなどで印刷したわずかな厚さを有する文字であると、厚みの差による凹凸で、文字が読み取られてしまうことがある。 As a concealment method, the sticker generates excess waste such as release paper, which is not suitable for recent environmental problems. Markers and solid pattern stamps can be read with unevenness due to thickness differences if the ink soaks into the paper and the personal information characters are printed with a laser printer or the like. There is.
そのようにならないように、意匠登録第１３３５７１３号公報のように、スタンプ画像（スタンプ印面）を工夫して、個人情報などが判読されることを困難にしているものもあるが、スタンプという商品であるため、使い方によってはスタンプした画像のインク濃度にムラが出ることがあり、インク濃度が薄くなった場合は、隠したい個人情報が判読されてしまう。また、個人情報である文字のフォント、サイズ、色などによっては、スタンプ画像では隠しきれずに、判読されてしまうということもある。 To prevent this from happening, there are some products such as Design Registration No. 1335713 that devise a stamp image (stamp stamp face) to make it difficult for personal information to be read. Therefore, depending on the usage, the ink density of the stamped image may become uneven, and when the ink density becomes low, personal information to be hidden is read. Also, depending on the font, size, color, etc. of the characters that are personal information, the stamp image may not be hidden and may be read.
本発明が解決しようとする課題は、誰でも簡単に使用でき、廃棄するときに、隠したい個人情報が判読されてしまうことがない個人情報保護用感圧転写接着テープを提供することである。また、これを使用する塗膜転写具は、感圧転写接着テープであってもうまく感圧転写できる構成のものである。 The problem to be solved by the present invention is to provide a pressure-sensitive transfer adhesive tape for personal information protection that can be easily used by anyone, and that does not read personal information to be hidden when discarded. Moreover, the coating film transfer tool using this is a structure which can perform a pressure-sensitive transfer well even if it is a pressure-sensitive transfer adhesive tape.
本発明の個人情報保護用感圧転写接着テープは、基材に接着層を形成し、塗膜転写具を用いて圧力で基材から剥離させて接着層を転写させる感圧転写接着テープにおいて、接着層全体が均一の濃色であることを特徴とするものである。また、濃色の接着層の透過濃度が１．０以上であることを特徴とするものであり、さらに、濃色の接着層の接着力が３Ｎ／２５ｍｍ〜３０Ｎ／２５ｍｍであることを特徴とするものである。 The pressure-sensitive transfer adhesive tape for personal information protection of the present invention is a pressure-sensitive transfer adhesive tape in which an adhesive layer is formed on a substrate, and the adhesive layer is transferred by peeling off the substrate with pressure using a coating film transfer tool. The entire adhesive layer has a uniform dark color. Further, the transmission density of the dark color adhesive layer is 1.0 or more, and the adhesive force of the dark color adhesive layer is 3 N / 25 mm to 30 N / 25 mm. To do.
本発明によって、塗膜転写具を用いて圧力で基材から剥離させて接着層を転写させることができるため、誰でも簡単に使用できる個人情報保護用感圧転写接着テープとなった。 According to the present invention, since the adhesive layer can be transferred by peeling off from the substrate with pressure using a coating film transfer tool, a pressure-sensitive transfer adhesive tape for protecting personal information can be easily used by anyone.
感圧転写型の接着層なので、転写された接着層は厚さがあり、レーザプリンタで印刷した文字の厚さによる凹凸が接着層表面上に現れることがなく、文字が判読されてしまうことはない。また、接着層全体が均一の濃色であるため、隠したい文字上に転写するだけでも、文字が判読できなくなる。そして、接着層であるため、その上に不透明なものを貼り合わせて捨てることができる。これにより、文字の部分が貼り合わされた内側に隠れた状態となり、より一層の安心感を使用者に与えられる。不透明なものは、別のものでも、接着層を転写した紙などを折り曲げた部分でもよい。さらに、このようにして貼り合わせて捨てられた紙を第三者が貼り合せた部分を無理やり開こうとしても、紙自体が破けてしまうものである。 Because it is a pressure-sensitive transfer type adhesive layer, the transferred adhesive layer has a thickness, and the unevenness due to the thickness of the characters printed by the laser printer does not appear on the surface of the adhesive layer, so that the characters can be read Absent. In addition, since the entire adhesive layer has a uniform dark color, the characters cannot be read even if they are simply transferred onto the characters to be hidden. And since it is an contact bonding layer, an opaque thing can be bonded together and thrown away. Thereby, it will be in the state hidden in the inner side where the character part was bonded together, and a further relief will be given to a user. The opaque thing may be another thing, or the part which bent the paper etc. which transferred the adhesive layer may be sufficient. Furthermore, even if an attempt is made to forcibly open a portion where the third party has pasted the paper that has been stuck and discarded in this manner, the paper itself is torn.
本発明の個人情報保護用感圧転写接着テープは、塗膜転写具を用いて圧力で基材から剥離させて接着層を転写させて使用するものであり、基材に接着層を形成するものである。 The pressure-sensitive transfer adhesive tape for personal information protection of the present invention is used by peeling the adhesive layer from the substrate with pressure using a coating film transfer tool, and transferring the adhesive layer to form the adhesive layer on the substrate. It is.
図１は、本発明の使用例を示した説明図である。個人情報として、架空の住所を図に示している。図１（ａ）のような「住所：大阪府特許市出願町１０−６」という文字２の上に、接着層１を感圧転写させたものが図１（ｂ）である。このように接着層１が濃色であるために、判読することができなくなる。
FIG. 1 is an explanatory view showing an example of use of the present invention. As personal information, a fictitious address is shown in the figure. FIG. 1B is a diagram in which the
図２は、本発明の構成を示した説明図である。基材４に濃色の接着層１を形成した構成である。基材４に、接着層塗工液をいわゆるコーターなどで塗布して、加熱乾燥して接着層１を形成して、細い幅にスリットして感圧転写接着テープ３を製造する。
FIG. 2 is an explanatory diagram showing the configuration of the present invention. In this configuration, the dark
接着層塗工液は、接着剤とフィラーと着色剤および溶媒とからなる。接着剤は、いわゆる粘着剤に、粘着付与剤と硬化剤を含んだものである。これは、接着層に感圧転写性能を出すため、つまり、接着性能を有しながら、感圧転写性能を出すためである。フィラーは、感圧転写の切れ性能を出すためであり、着色剤は、濃色にするためである。 The adhesive layer coating liquid is composed of an adhesive, a filler, a colorant, and a solvent. The adhesive is a so-called pressure-sensitive adhesive containing a tackifier and a curing agent. This is to provide pressure-sensitive transfer performance to the adhesive layer, that is, to provide pressure-sensitive transfer performance while having adhesive performance. This is because the filler is used for producing pressure-sensitive transfer cutting performance, and the colorant is used for making the color darker.
コーターは、ロールコーター、リバースロールコーター、グラビアコーターなど、接着層が形成できるものであればよい。 The coater may be any one that can form an adhesive layer, such as a roll coater, a reverse roll coater, or a gravure coater.
この感圧転写接着テープ３を繰出しリールに小巻にして、転写ヘッドと巻取りリールに巻き回して塗膜転写具に装填して使用するものである。
This pressure-sensitive transfer
図３は、塗膜転写具１１を用いた感圧転写を示した説明図である。塗膜転写具１１の転写ヘッドはローラーヘッド１２であり、図にはローラーヘッド１２の回転軸１３も見えている。
FIG. 3 is an explanatory view showing pressure-sensitive transfer using the coating
ローラーヘッド１２にて感圧転写接着テープ３を紙５の文字上に押さえつけて圧力を与えながら図面左から右方向へ塗膜転写具１１を引いて、接着層１を紙５に感圧転写している。接着層１が剥離された基材４は、塗膜転写具１１内部に巻き取られている。
The pressure-sensitive transfer
転写ヘッドがローラーヘッド１２であるのは、粘着という特性を有する接着層を感圧転写させるのにはローラーという形態が好ましいからである。修正テープに使用するような、ローラーではない動かない固定されたヘッドであると、そのような接着層をうまく転写できない。
The reason why the transfer head is the
塗膜転写具１１には、感圧転写接着テープ３の使用量が目視できるように、窓１５が設けられている。これにより、繰出しリールに巻かれている感圧転写接着テープ３が見えるようになっている。図において、窓１５の中に見える黒い部分が感圧転写接着テープ３である。
The coating
この塗膜転写具１１では、窓１５は２つからなる。２つあることにより、使い初めと使い終わりが目視できるようになっている。図において、右上側のひとつの窓１５にて使い始めが、左下側のもうひとつの窓１５にて使い終わりが、目視できるものである。
In the coating
また、塗膜転写具１１には、キャップ１４が設置されている。この図では、キャップ１４はほとんど隠れている。
A
図４は、塗膜転写具１１にキャップ１４をした状態を示した説明図である。このようにして、接着層１の接着面にごみや埃が付着したり、他の何かに接着層１がふいに接触したりするのを防いでいる。このようにキャップをして、持ち運びしたり、保管したりできるようにしている。
FIG. 4 is an explanatory view showing a state in which the
図５は、透明な筐体の塗膜転写具で、内部構成を示した説明図である。繰出しリール１６から繰り出された感圧転写接着テープ３は、ローラーヘッド１２にて、接着層が感圧転写されて、基材４が巻取りリール１７に巻き取られる構成である。基材４を整えながら巻き取るために、巻取りリール１７にはフランジがあり、フランジの外側（図で見えている側）がローレット形状のフランジ１８である。繰出しリール１６と巻取りリール１７には連動機構があり、この塗膜転写具１１では連動機構としてギア１９を用いている。
FIG. 5 is an explanatory diagram showing an internal configuration of a transparent film-transfer tool. The pressure-sensitive transfer
巻取りリール１７にローレット形状のフランジ１８を設けているのは、塗膜転写具１１の内部に、繰出しリール１６や巻取りリール１７や連動機構などを組み込んだ後に、感圧転写接着テープ３の弛みなどを調整するためである。この調整により、使い始めから不具合なく使用できる状態にすることができる。
A
また、感圧転写接着テープ３の接着面が塗膜転写具１１の筐体の内壁に引っ付いてしまわないように、筐体の内壁に突起物２０を設けており、図では８つの突起物２０が見えている。筐体の内壁に引っ付いてしまうと、テープが動かなくなってうまく転写できなくなったり、接着層１が部分的にはがれて、転写できたとしても本来の目的を果たさなくなったりすることが起こる。このように複数個の突起物２０を設けることにより、それを防ぐことができる。
Further,
転写ヘッドがローラーヘッド１２であり、筐体に２つの窓１５があり、筐体の内壁に突起物２０がある塗膜転写具１１であるので、感圧転写テープが感圧転写接着テープであっても、うまく感圧転写できる構成となっている。
Since the transfer head is the
接着層を転写して、文字を判読することができなくするためには、接着層が濃色であればよい。濃色とは、濃い色のことであり、色の種類に関係なく、色の濃度が濃いものである。色の濃度が薄く、透明で薄く色づいているようなものは淡色である。濃色であり、感圧転写接着テープにおける接着層の厚さが、一般的な１０〜１００μｍの範囲であれば、好ましくは１５〜３０μｍの範囲であれば、文字を判読することができなくなる。 In order to transfer the adhesive layer so that the characters cannot be read, the adhesive layer may be dark. A dark color is a dark color and has a high color density regardless of the type of color. The color density is light, transparent and lightly colored. If it is a dark color and the thickness of the adhesive layer in the pressure-sensitive transfer adhesive tape is in the general range of 10 to 100 μm, preferably in the range of 15 to 30 μm, the characters cannot be read.
このような接着層であっても、転写した紙などの裏面から強い光を当てると、文字が透けて判読されてしまう場合がある。そのため、濃色の接着層の透過濃度が１．０以上であることが好ましい。 Even with such an adhesive layer, when strong light is applied from the back side of the transferred paper or the like, characters may be seen through and read. Therefore, the transmission density of the dark color adhesive layer is preferably 1.0 or more.
この透過濃度は、厚さ２５μｍの透明ＰＥＴフィルムに感圧転写した接着層の上に、さらに厚さ２５μｍの透明ＰＥＴフィルムを貼り合せたものを試料として、マクベス濃度計ＴＲ−９２７を使用して測定したものである。濃色の接着層の透過濃度は、１．０以上であればよく、文字を判読することができなくなる。また、１．４以上であれば好ましく、２．０以上であればより好ましい。 This transmission density was measured using a Macbeth densitometer TR-927 with a sample obtained by laminating a 25 μm thick transparent PET film on an adhesive layer that was pressure-sensitively transferred to a 25 μm thick transparent PET film. It is measured. The transmission density of the dark color adhesive layer may be 1.0 or more, and the characters cannot be read. Further, it is preferably 1.4 or more, and more preferably 2.0 or more.
このようなものであれば、レーザプリンタで上質紙に印刷した文字の上に、塗膜転写具を用いて感圧転写接着テープの接着層を転写させて、文字のない上質紙の部分を折り曲げて、接着層の上に重ねて、上質紙同士を貼り合わせて、上質紙の背面に１５ワットの蛍光灯を接触させて、接着層で貼り合わせた文字付近に蛍光灯の光を透過させて、文字が判読することができないものになる。 If this is the case, transfer the adhesive layer of the pressure-sensitive transfer adhesive tape onto the characters printed on the high-quality paper with a laser printer, and then fold the portion of the high-quality paper without the characters. Then, superimpose them on the adhesive layer, paste the high-quality paper together, bring a 15-watt fluorescent lamp into contact with the back of the high-quality paper, and transmit the light from the fluorescent lamp near the letters pasted together on the adhesive layer , The characters become unreadable.
一方で、紙などに感圧転写した接着層の上に紙を重ねて貼り合せて、その後に剥がすと、紙自体が破けてしまう（紙破壊が起こる）方が、使用者にさらに安心感を与えるものである。それだけの十分な接着力があるのが好ましい。 On the other hand, if the paper is overlaid on the adhesive layer that has been pressure-sensitively transferred to the paper, and then peeled off, the paper itself will be torn (paper breaks), giving the user a greater sense of security. Give. It is preferable that the adhesive strength is sufficient.
しかしながら、濃色でありながら、それだけの接着力を発揮させる感圧転写型の接着層とすることは難しかった。研究を重ねた結果、接着剤、フィラー、着色剤が、下記のような構成からなる接着層塗工液により形成した接着層であれば可能となった。ここで接着剤とは、粘着剤、粘着付与剤、硬化剤を含んだものである。 However, it has been difficult to obtain a pressure-sensitive transfer type adhesive layer that exhibits a sufficient adhesive strength while being dark. As a result of repeated research, it has become possible for the adhesive, filler, and colorant to be an adhesive layer formed by an adhesive layer coating liquid having the following constitution. Here, the adhesive includes an adhesive, a tackifier, and a curing agent.
粘着剤は、アクリル系、ゴム系、ウレタン系、オレフィン系、シリコン系などの一般的な粘着剤を用いることができる。実施例では、汎用性、価格、種類の多さなどから、アクリル系粘着剤を用いた。固形分比で、６０〜８０重量％であればよい。 As the pressure-sensitive adhesive, general pressure-sensitive adhesives such as acrylic, rubber-based, urethane-based, olefin-based, and silicon-based materials can be used. In the examples, an acrylic pressure-sensitive adhesive was used because of its versatility, price, and variety. The solid content ratio may be 60 to 80% by weight.
粘着付与剤は、ロジン、ロジン誘導体、ポリテルペン、テルペンフェノール樹脂、石油樹脂などが使用できる。実施例では、アクリル系粘着剤と相溶性がよく、高い粘着力を得られるテルペンフェノール樹脂を用いた。固形分比で、５〜２０重量％であればよい。 As the tackifier, rosin, rosin derivative, polyterpene, terpene phenol resin, petroleum resin and the like can be used. In the examples, a terpene phenol resin having good compatibility with an acrylic pressure-sensitive adhesive and capable of obtaining high adhesive strength was used. The solid content ratio may be 5 to 20% by weight.
硬化剤は、接着層の凝集力を高め、表面のべたつきを抑え、保持力を向上させる効果があり、これにより、接着性能を有しながら、感圧転写性能を出している。イソシアネート系硬化剤、エポキシ系硬化剤、メラミン系硬化剤などが使用できる。実施例では、イソシアネート系硬化剤を用いた。固形分比で、０．１〜２重量％であればよい。 The curing agent has the effect of increasing the cohesive force of the adhesive layer, suppressing the stickiness of the surface, and improving the holding power, thereby providing pressure-sensitive transfer performance while having adhesive performance. An isocyanate curing agent, an epoxy curing agent, a melamine curing agent, and the like can be used. In the examples, an isocyanate curing agent was used. The solid content ratio may be 0.1 to 2% by weight.
ここで、粘着剤、粘着付与剤、硬化剤を含んだ接着剤としては、固形分比で、６５〜９７重量％であればよく、８０〜９０重量％が好ましい。 Here, as an adhesive containing a pressure-sensitive adhesive, a tackifier, and a curing agent, the solid content ratio may be 65 to 97% by weight, and preferably 80 to 90% by weight.
フィラーは、感圧転写の切れ性能を出すために、用いている。このフィラーによって、感圧転写を終わらせる時、つまり、紙から塗膜転写具を持ち上げて圧力を抜いた時、接着層が切れずに糸引き状態になるのを軽減させ、接着層の切れ性能を良くすることができる。フィラーの形状には、球状、針状、板状、燐片状など様々な形状がある。材質も、ガラス、シリカ、樹脂などがある。これらを単独もしくは混合して用いることができる。しかしながら、フィラーの添加量が多すぎると、接着力が著しく低下することがあるので、多すぎても良くない。切れ性能が良く、接着力を低下させないためには、添加量は固形分比で、１〜２０重量％がよく、１〜１０重量％が好ましく、４〜６重量％がさらに好ましい。 The filler is used for achieving pressure-sensitive transfer cutting performance. With this filler, when the pressure-sensitive transfer ends, that is, when the pressure is released by lifting the coating film transfer tool from the paper, the adhesive layer is less likely to be threaded without being cut, and the adhesive layer cutting performance Can be improved. The filler has various shapes such as a spherical shape, a needle shape, a plate shape, and a flake shape. There are also materials such as glass, silica, and resin. These can be used alone or in combination. However, if the amount of filler added is too large, the adhesive strength may be significantly reduced. In order to improve the cutting performance and not lower the adhesive strength, the addition amount is 1 to 20% by weight, preferably 1 to 10% by weight, and more preferably 4 to 6% by weight in terms of solid content.
着色剤は、一般的な着色剤が使用可能であり、無機顔料や有機顔料などを用いることができる。無機顔料としては、カーボンブラック、アイボリーブラック、コバルトブルー、チタンイエロー、酸化チタン、黄鉛、酸化鉄などがあげられ、有機顔料としては、アゾ顔料系、フタロシアニン顔料系、レーキ顔料系、ジオキサジン顔料系などがあげられる。また、染料、金粉やアルミニウム粉などを用いることができる。着色剤は、濃色になればよいが、固形分比で、３重量％以上であればよく、６重量％以上であれば好ましく、１０重量％以上であればより好ましい。 As the colorant, a general colorant can be used, and an inorganic pigment, an organic pigment, or the like can be used. Examples of inorganic pigments include carbon black, ivory black, cobalt blue, titanium yellow, titanium oxide, yellow lead, and iron oxide. Organic pigments include azo pigments, phthalocyanine pigments, lake pigments, and dioxazine pigments. Etc. Moreover, dye, gold powder, aluminum powder, etc. can be used. The colorant may be dark, but it may be 3% by weight or more, preferably 6% by weight or more, and more preferably 10% by weight or more in terms of solid content.
基材は、ポリエチレンテレフタレ−ト（ＰＥＴ）、ポリエチレンナフタート、ポリプロピレンなどのプラスチックフィルムや、３０〜６０ｇ／ｍ２程度のグラシン紙などの薄葉紙を用いることができる。基材の厚さは３〜５０μｍ程度が好ましいが、この限りではない。基材によっては離型加工した方がよい。離型加工は、シリコン樹脂やフッ素樹脂などで加工することができ、微粒子などの添加剤を使用してもよい。基材の両面に離型加工するのが好ましいが、離型加工せずとも圧力で接着層を剥離することができる基材であれば、接着層を形成する面とは反対の基材背面に離型加工するだけでよい。これは、コーターを用いてロール状で接着層を形成するため、そのような基材であれば、基材背面に接着層が引っ付いてしまうのを防ぐだけでよいからである。つまり、基材両面に、もしくは、接着層を形成する面とは反対の基材背面に、離型加工した基材を用いるのが好ましい。 As the substrate, plastic films such as polyethylene terephthalate (PET), polyethylene naphthalate, and polypropylene, and thin paper such as glassine paper of about 30 to 60 g / m 2 can be used. The thickness of the substrate is preferably about 3 to 50 μm, but is not limited thereto. Depending on the substrate, it is better to release the mold. The mold release process can be performed with a silicon resin or a fluorine resin, and an additive such as fine particles may be used. It is preferable to perform release processing on both surfaces of the base material, but if the base material can be peeled off by pressure without release processing, the back surface of the base material opposite to the surface on which the adhesive layer is formed is provided. It is only necessary to release the mold. This is because the adhesive layer is formed in a roll shape using a coater, so that it is only necessary to prevent the adhesive layer from sticking to the back surface of the base material if it is such a base material. That is, it is preferable to use a release-treated substrate on both sides of the substrate or on the back of the substrate opposite to the surface on which the adhesive layer is formed.
接着層塗工液として、これら粘着剤、粘着付与剤、硬化剤、フィラー、着色剤を溶媒とともに攪拌機等で均一に混合し作製する。これを、例えばリバースロールコーターにより塗布し、加熱乾燥により、所定の厚さに形成する。接着層の厚さは、１０〜１００μｍであれば良いが、１５〜３０μｍが好ましい。 As the adhesive layer coating liquid, these pressure-sensitive adhesive, tackifier, curing agent, filler, and colorant are uniformly mixed with a solvent with a stirrer or the like. This is applied by, for example, a reverse roll coater, and formed into a predetermined thickness by heat drying. The thickness of the adhesive layer may be 10 to 100 μm, but preferably 15 to 30 μm.
このような接着層塗工液の構成であり、形成された接着層の接着力が３Ｎ／２５ｍｍ〜３０Ｎ／２５ｍｍであれば、ロール状に巻いた時に、基材背面に接着層が引っ付いてしまう、ブロッキング現象が生じることなく、紙破壊が起こることを見出した。接着力が３Ｎ／２５ｍｍより小さいと、紙を貼り合わせて剥がそうとしても、紙破壊せずに剥がせてしまう。接着力が３０Ｎ／２５ｍｍより大きいとブロッキング現象が生じてしまう。 If the adhesive force of the formed adhesive layer is 3 N / 25 mm to 30 N / 25 mm, the adhesive layer is attracted to the back surface of the substrate when wound in a roll shape. It was found that paper breakage occurred without causing a blocking phenomenon. If the adhesive strength is less than 3 N / 25 mm, even if the paper is pasted and peeled off, the paper is peeled off without breaking the paper. If the adhesive force is greater than 30 N / 25 mm, a blocking phenomenon occurs.
接着力は、ＪＩＳＺ０２３７に定める「試験板に対する１８０度引き剥がし粘着力」測定方法に準じて測定したものである。接着力は、３Ｎ／２５ｍｍ〜３０Ｎ／２５ｍｍであればよく、５Ｎ／２５ｍｍ〜２０Ｎ／２５ｍｍであれば好ましい。 The adhesive strength is measured in accordance with the “180 degree peel adhesion to the test plate” measuring method defined in JISZ0237. The adhesive force may be 3N / 25 mm to 30 N / 25 mm, and preferably 5 N / 25 mm to 20 N / 25 mm.
このようなものであれば、レーザプリンタで上質紙に印刷した文字の上に、塗膜転写具を用いて感圧転写接着テープの接着層を転写させて、文字のない上質紙の部分を折り曲げて、接着層の上に重ねて、上質紙同士を貼り合わせて、２４時間室温で放置後、上質紙同士を引き剥がすと、上質紙が破れるものになる。 If this is the case, transfer the adhesive layer of the pressure-sensitive transfer adhesive tape onto the characters printed on the high-quality paper with a laser printer, and then fold the portion of the high-quality paper without the characters. Then, when the high quality papers are laminated on top of each other and bonded together, left at room temperature for 24 hours, and then peeled off, the high quality papers are torn.
以下に本発明における実施例により詳細に説明する。ただし本発明はこれらの実施例に限定されるものではない。 Hereinafter, the present invention will be described in detail by way of examples. However, the present invention is not limited to these examples.
実施例１の接着層塗工液は、粘着剤、粘着付与剤、硬化剤、フィラー、着色剤として次のような固形分比での重量％となるように、溶媒としてトルエンを用いて攪拌機で均一に混合し作製した。 The adhesive layer coating liquid of Example 1 is a stirrer using toluene as a solvent so as to have a weight percentage in the following solid content ratio as a pressure-sensitive adhesive, a tackifier, a curing agent, a filler, and a colorant. It was prepared by mixing uniformly.
粘着剤として、アクリル系粘着剤「ＳＫダイン１９０６Ｈ」（綜研化学株式会社製）を固形分比で７０重量％、粘着付与剤として、テルペンフェノール樹脂（「ＹＳポリスターＵ１１５」（ヤスハラケミカル株式会社製）を固形分比で１４．７重量％、硬化剤として、イソシアネート系硬化剤「Ｌ−４５」（綜研化学株式会社製）を固形分比で０．３重量％、フィラーとして、「マイクログラスサーフェストランドＲＥＶ１」（エヌエスジー・ヴェトロテックス株式会社製）を固形分比で５重量％、着色剤として、ボールミルで分散処理したカーボンブラック「Ｒａｖｅｎ１０８０」（コロンビアカーボン社製）を固形分比で１０重量％となるように、作製した。 As an adhesive, acrylic adhesive “SK Dyne 1906H” (manufactured by Soken Chemical Co., Ltd.) in a solid content ratio of 70% by weight, and as a tackifier, terpene phenol resin (“YS Polystar U115” (manufactured by Yasuhara Chemical Co., Ltd.)) The solid content ratio is 14.7% by weight, the curing agent is an isocyanate curing agent “L-45” (manufactured by Soken Chemical Co., Ltd.), the solid content ratio is 0.3% by weight, and the filler is “Microglass Surface Land REV1”. "NV Vetrotex Co., Ltd." is 5% by weight in terms of solid content, and carbon black "Raven 1080" (produced by Columbia Carbon Co., Ltd.) dispersed in a ball mill as a colorant is 10% by weight in terms of solid content. As shown in FIG.
この実施例１の接着層塗工液を、基材として厚さ１２μｍの両面離型加工したＰＥＴフィルムを用いて、リバースロールコーターで塗布して、加熱乾燥して、厚さ１８μｍになるように実施例１の接着層を形成した。 The adhesive layer coating solution of Example 1 was coated with a reverse roll coater using a PET film having a thickness of 12 μm on both sides as a substrate, and dried by heating to a thickness of 18 μm. The adhesive layer of Example 1 was formed.
実施例１の接着層塗工液を用いて、厚さ２４μｍになるように実施例２の接着層を形成した。これ以外は、実施例１と同じである。 Using the adhesive layer coating liquid of Example 1, the adhesive layer of Example 2 was formed to a thickness of 24 μm. Other than this, the second embodiment is the same as the first embodiment.
実施例１の接着層塗工液を用いて、厚さ３０μｍになるように実施例３の接着層を形成した。これ以外は、実施例１と同じである。 Using the adhesive layer coating solution of Example 1, the adhesive layer of Example 3 was formed to a thickness of 30 μm. Other than this, the second embodiment is the same as the first embodiment.
実施例１の接着層塗工液において、粘着剤を固形分比で７４重量％、着色剤を固形分比で６重量％に変更して、これら以外は実施例１と同様にして、実施例４の接着層を形成した。 In the adhesive layer coating liquid of Example 1, the pressure-sensitive adhesive was changed to 74% by weight in the solid content ratio, and the colorant was changed to 6% by weight in the solid content ratio. 4 adhesive layers were formed.
実施例１の接着層塗工液において、粘着剤を固形分比で７７重量％、着色剤を固形分比で３重量％に変更して、これら以外は実施例１と同様にして、実施例５の接着層を形成した。 In the adhesive layer coating solution of Example 1, the pressure-sensitive adhesive was changed to 77% by weight in the solid content ratio, and the colorant was changed to 3% by weight in the solid content ratio. 5 adhesive layers were formed.
実施例１の接着層塗工液において、粘着剤としてアクリル系粘着剤「ＳＫダイン１７２０」（綜研化学株式会社製）を固形分比で７７重量％、着色剤を固形分比で３重量％に変更して、これら以外は実施例１と同様にして、実施例６の接着層を形成した。 In the adhesive layer coating liquid of Example 1, acrylic pressure-sensitive adhesive “SK Dyne 1720” (manufactured by Soken Chemical Co., Ltd.) as the pressure-sensitive adhesive was 77 wt% in solid content ratio, and the colorant was 3 wt% in solid content ratio. The adhesive layer of Example 6 was formed in the same manner as Example 1 except that these were changed.
実施例１の接着層塗工液において、粘着剤としてアクリル系粘着剤「ＳＫダイン１６０４Ｎ」（綜研化学株式会社製）を固形分比で７７重量％、着色剤を固形分比で３重量％に変更して、これら以外は実施例１と同様にして、実施例７の接着層を形成した。 In the adhesive layer coating liquid of Example 1, acrylic pressure-sensitive adhesive “SK Dyne 1604N” (manufactured by Soken Chemical Co., Ltd.) as a pressure-sensitive adhesive was 77% by weight, and the colorant was 3% by weight. The adhesive layer of Example 7 was formed in the same manner as Example 1 except that these were changed.
（比較例１）実施例１の接着層塗工液において、粘着剤を固形分比で７９．５重量％、着色剤を固形分比で０．５重量％に変更して、これら以外は実施例１と同様にして、比較例１の接着層を形成した。 (Comparative Example 1) In the adhesive layer coating solution of Example 1, the pressure-sensitive adhesive was changed to 79.5% by weight in the solid content ratio, and the colorant was changed to 0.5% by weight in the solid content ratio. In the same manner as in Example 1, the adhesive layer of Comparative Example 1 was formed.
実施例と比較例において、実施例すべては濃色の接着層となり、比較例は淡色の接着層となった。 In the examples and comparative examples, all of the examples were dark color adhesive layers, and the comparative example was a light color adhesive layer.
これら実施例と比較例の基材に形成した接着層を、基材ごと細い幅にスリットしてそれぞれの個人情報保護用感圧転写接着テープとした。これらを繰出しリールに小巻にして、転写ヘッドと巻取りリールに巻き回して、塗膜転写具「グルーラミニ」（ユニオンケミカー社製）の筐体に装填して使用可能な状態にした。 The adhesive layers formed on the base materials of these examples and comparative examples were slit into thin widths together with the base materials to form pressure-sensitive transfer adhesive tapes for personal information protection. These were made into a small volume on a pay-out reel, wound around a transfer head and a take-up reel, and loaded into a case of a coating film transfer tool “Gura Mini” (manufactured by Union Chemika) to be ready for use.
なお、この塗膜転写具は、転写ヘッドがローラーヘッド１２であり、筐体に２つの窓１５があり、筐体の内壁に突起物２０があり、感圧転写テープが感圧転写接着テープであっても、うまく感圧転写できる構成のものである。
In this coating film transfer tool, the transfer head is a
実施例と比較例の透過濃度は、厚さ２５μｍの透明ＰＥＴフィルムに感圧転写した接着層の上に、さらに厚さ２５μｍの透明ＰＥＴフィルムを貼り合せたものを試料として、マクベス濃度計ＴＲ−９２７を使用して測定した。実施例と比較例の接着力は、ＪＩＳＺ０２３７に基づいて測定した。これらの測定結果は、表１に記載している。 The transmission density of the examples and comparative examples is a Macbeth densitometer TR- using a sample obtained by laminating a 25 μm thick transparent PET film on a pressure sensitive transfer adhesive layer onto a 25 μm thick transparent PET film. 927. The adhesive strengths of Examples and Comparative Examples were measured based on JISZ0237. These measurement results are listed in Table 1.
判読性と紙破壊性は、以下の評価のように行った。これらの評価結果も、表１に記載している。 The legibility and paper breakability were evaluated as follows. These evaluation results are also shown in Table 1.
判読性は、レーザプリンタで上質紙に印刷した文字の上に、塗膜転写具を用いて実施例と比較例のそれぞれの接着層を転写させて、文字のない上質紙の部分を折り曲げて、接着層の上に重ねて、上質紙同士を貼り合わせて、上質紙の背面に１５ワットの蛍光灯を接触させて、接着層で貼り合わせた文字付近に蛍光灯の光を透過させて、文字が判読することができるかどうかを評価した。判読できない場合は○、判読できる場合は×とした。 For legibility, on the characters printed on the high-quality paper with a laser printer, the adhesive layers of the examples and comparative examples are transferred using a coating film transfer tool, and the portion of the high-quality paper without characters is bent. Overlaid on the adhesive layer, the high-quality papers are bonded together, a 15-watt fluorescent lamp is brought into contact with the back of the high-quality paper, and the light from the fluorescent lamp is transmitted in the vicinity of the characters bonded together in the adhesive layer. Evaluated whether can be read. When it was not readable, it was marked as ◯.
紙破壊性は、レーザプリンタで上質紙に印刷した文字の上に、塗膜転写具を用いて感圧転写接着テープの接着層を転写させて、文字のない上質紙の部分を折り曲げて、接着層の上に重ねて、上質紙同士を貼り合わせて、２４時間室温で放置後、上質紙同士を引き剥がすと、上質紙が破れるかどうかを評価した。破れる場合は○、破れない場合は×とした。 Paper breakability is achieved by transferring the adhesive layer of pressure-sensitive transfer adhesive tape onto the characters printed on high-quality paper with a laser printer, and then folding the portion of the high-quality paper with no characters on it. Overlaid on the layers, the high quality papers were pasted together, left to stand at room temperature for 24 hours, and then peeled off the high quality papers to evaluate whether the high quality papers were torn. When it was torn, it was marked as ◯, and when it was not broken, it was marked as x.
以上の内容を表１に記載した。なお、接着層塗工液である粘着剤、粘着付与剤、硬化剤、フィラー、着色剤の数値の単位は、固形分比における重量％である。また、粘着剤Ａは「ＳＫダイン１９０６Ｈ」（綜研化学株式会社製）であり、粘着剤Bは「ＳＫダイン１７２０」（綜研化学株式会社製）であり、粘着剤Cは「ＳＫダイン１６０４Ｎ」（綜研化学株式会社製）である。 The above contents are shown in Table 1. In addition, the unit of the numerical value of the adhesive, the tackifier, the curing agent, the filler, and the colorant, which are the adhesive layer coating solution, is wt% in the solid content ratio. Adhesive A is “SK Dyne 1906H” (manufactured by Soken Chemical Co., Ltd.), Adhesive B is “SK Dyne 1720” (manufactured by Soken Chemical Co., Ltd.), and Adhesive C is “SK Dyne 1604N” ( Soken Chemical Co., Ltd.).
１ 濃色の接着層
２ 文字
３ 個人情報保護用感圧転写接着テープ
４ 基材
５ 紙
１１ 塗膜転写具
１２ ローラーヘッド
１３ ローラーヘッドの回転軸
１４ キャップ
１５ 窓
１６ 繰出しリール
１７ 巻取りリール
１８ ローレット形状のフランジ
１９ ギア
２０ 突起物
DESCRIPTION OF
Claims (1)
これを使用する塗膜転写具は、感圧転写接着テープであってもうまく感圧転写できる構成のものであり、転写ヘッドがローラーヘッドであり、キャップを設置しており、感圧転写接着テープの接着面が塗膜転写具の筐体の内壁に引っ付いてしまわないように、塗膜転写具の筐体の内壁に複数個の突起物を設けてあって、
接着層は、基材に接着層塗工液を塗布して加熱乾燥して形成するものであり、接着層塗工液は、接着剤とフィラーと着色剤および溶媒とからなり、接着剤は、粘着剤、粘着付与剤、硬化剤を含んでおり、フィラーの添加量は、固形分比で１〜２０重量％であって、
接着層全体が均一の濃色であり、濃色の接着層の透過濃度が１．０以上であり、濃色の接着層の接着力が３Ｎ／２５ｍｍ〜３０Ｎ／２５ｍｍであることを特徴とする個人情報保護用感圧転写接着テープ。 In pressure-sensitive transfer adhesive tape that forms an adhesive layer on a substrate and peels it from the substrate with pressure using a coating film transfer tool to transfer the adhesive layer,
The coating film transfer tool that uses this is a structure that can perform pressure-sensitive transfer well even if it is a pressure-sensitive transfer adhesive tape, the transfer head is a roller head, a cap is installed, and pressure-sensitive transfer adhesive tape In order to prevent the adhesive surface from sticking to the inner wall of the coating film transfer tool housing, a plurality of protrusions are provided on the inner wall of the coating film transfer tool housing,
The adhesive layer is formed by applying an adhesive layer coating solution on a substrate and drying by heating. The adhesive layer coating solution is composed of an adhesive, a filler, a colorant, and a solvent. It contains a pressure-sensitive adhesive, a tackifier, and a curing agent, and the amount of filler added is 1 to 20% by weight in terms of solid content,
The entire adhesive layer has a uniform dark color, the transmission density of the dark adhesive layer is 1.0 or more, and the adhesive strength of the dark adhesive layer is 3 N / 25 mm to 30 N / 25 mm. Pressure sensitive transfer adhesive tape for personal information protection.