JP5455335B2 - Manufacturing method of resin foam molding - Google Patents

Description

  The present invention relates to a method for producing a resin foam molded body by performing so-called core back molding.

Conventionally, a resin foam molded article having a predetermined expansion ratio can be formed by filling a cavity formed between a fixed mold and a movable mold with a molten resin and retracting the movable mold with respect to the fixed mold. Has been done. For example, in the method for producing a thermoplastic resin foam molded article disclosed in Patent Document 1, a step of injecting an inert gas in advance into a mold having a movable core whose cavity volume is variable, and a molten resin kneaded with a chemical foaming agent Injecting the supercritical fluid into the mold and filling the molten resin into the mold, and retreating the movable core in the direction of increasing the cavity volume when the molten resin is filled in the mold. Foam molded body is molded. Thereby, it is excellent in the surface external appearance quality of a molded object, and a highly uniform foaming cell diameter can be obtained stably.
Patent Document 2 discloses that two specific types of ABS resins are blended with a polycarbonate resin in order to obtain a thermoplastic resin composition having improved heat resistance, impact resistance, and thinner resistance. Has been.

JP 2007-15231 A JP 2001-131398 A

However, the strength of the resin foam molded body is generally lower than that of the resin molded body that is not foamed. Therefore, in order to suppress a decrease in strength due to foaming of the resin, further contrivance is required. Further, in a resin foam molded article obtained by foam molding of a thermoplastic resin, further ingenuity is required in order to make the cell diameter by foaming more uniform and to suppress deterioration in appearance and strength.
Moreover, in patent document 2, only the composition excellent in the predetermined characteristic is disclosed, and the device for aiming at the deterioration of an external appearance and the fall of intensity | strength is not made | formed.

The present invention was made in view of such conventional problems, and by forming a stable skin layer, the strength of the resin foam molded body to be molded can be improved, and the cell diameter by foaming can be made more uniform, it is intended to provide a method for producing a resin foam molded article that can suppress the appearance of the resin expanded molded article is deteriorated.

The first invention uses a first mold part and a second mold part movable relative to the first mold part, and is formed between the second mold part and the first mold part. A filling step of filling a molten resin obtained by kneading a chemical foaming agent into a thermoplastic resin composition in the cavity, and the first mold part and the second mold part in a separation direction in which the volume of the cavity is increased. In a method of manufacturing a resin foam molded article by performing a movable step of relatively moving,
The content of the chemical foaming agent is 0.05 to 5 parts by mass with respect to 100 parts by mass of the thermoplastic resin composition.
The thermoplastic resin composition contains the polycarbonate resin (A) and the rubber-reinforced vinyl resin (B) in such a ratio that (A) is 20 to 80% by mass and (B) is 80 to 20% by mass. And
The rubber-reinforced vinyl resin (B) is a graft copolymer (B1) obtained by polymerizing a vinyl monomer (b2) containing an aromatic vinyl compound in the presence of a rubbery polymer (b1). Or a mixture of the vinyl monomer (b3) copolymer (B2) and the graft copolymer (B1). .

In the method for producing a resin foam molded article of the present invention, when the resin foam molded article is produced by performing the filling step and the movable step, in particular, the material constituting the thermoplastic resin composition is devised.
Specifically, the thermoplastic resin composition of the present invention comprises the polycarbonate resin (A) and the rubber-reinforced vinyl resin (B), wherein (A) is 20 to 80% by mass and (B) is 80 to 80%. It is contained at a ratio of 20% by mass. The rubber-reinforced vinyl resin (B) is a graft copolymer (B1) obtained by polymerizing a vinyl monomer (b2) containing an aromatic vinyl compound in the presence of the rubbery polymer (b1). ) Or a mixture of the copolymer (B2) of the vinyl monomer (b3) and the graft copolymer (B1).

As a result, when the volume of the cavity filled with the molten resin obtained by kneading the chemical foaming agent with the thermoplastic resin composition is expanded as the movable step, the molten resin is stably placed on the portion that contacts the surface of the cavity. It is possible to form a skin layer (an almost unfoamed surface layer formed by curing a portion of the molten resin in contact with the surface of the cavity earlier than a portion of the molten resin located therein). Therefore, the strength of the resin foam molding to be molded can be improved by forming a stable skin layer.
Further, when the volume of the cavity is expanded by using the thermoplastic resin composition, a foam layer is formed inside the molten resin, and the cell diameter by foaming is made more uniform in the resin foam molded body to be molded. It can suppress that the external appearance of a resin foaming molding deteriorates.

  In the present invention, the cell diameter by foaming can be made as uniform as possible by the presence of the polycarbonate resin (A) having a high viscosity at a predetermined temperature at which resin molding is performed, and the appearance of the resin foam molding is improved. be able to. Further, at a predetermined temperature at which resin molding is performed, the presence of the rubber-reinforced vinyl resin (B) having a viscosity lower than that of the polycarbonate resin (A) can stably form a skin layer on the surface of the resin foam molded body. it can.

  Therefore, according to the method for producing a resin foam molded article of the present invention, by forming a stable skin layer, the strength of the resin foam molded article to be molded can be improved, the cell diameter by foaming is made more uniform, It can suppress that the external appearance of a resin foaming molding deteriorates.

A second reference invention is a resin foam molded article obtained by the method for producing a resin foam molded article .
According to the resin foam molded article of the present invention, the strength can be improved by forming a stable skin layer, the cell diameter by foaming can be made more uniform, and deterioration of the appearance can be suppressed.

The preferred embodiments of the first invention and the second reference invention described above will be described.
1st invention WHEREIN: When content of the said chemical foaming agent with respect to 100 mass parts of said thermoplastic resin compositions is less than 0.05 mass part, there is little content of a chemical foaming agent, and each cell of foaming It becomes difficult to make the diameter uniform. On the other hand, when the content of the chemical foaming agent with respect to 100 parts by mass of the thermoplastic resin composition exceeds 5 parts by mass, the content of the chemical foaming agent is large and mold contamination due to the residue of the chemical foaming agent occurs. It is difficult to obtain a resin foam molded article having an excellent appearance.
The expansion ratio of the volume of the cavity due to relative movement between the first mold part and the second mold part may be 1.1 to 1.6 times. This enlargement ratio is the expansion ratio of the resin foam molding.

In addition to the polycarbonate resin (A) and the rubber-reinforced vinyl resin (B), the thermoplastic resin composition can be configured to contain other resin components. This other resin component can be contained, for example, within 5% by mass relative to the total of the component (A) and the component (B).
Other resin components are not particularly limited, but excluding component (B), styrene resins, acrylic resins, vinyl chloride resins, polyamide resins (PA), polyester resins, olefin resins, ethylene resins A copolymer etc. are mentioned. These can be used individually by 1 type and can also be used in combination of 2 or more type.

The thermoplastic resin composition preferably contains 50 to 70% by mass of the aromatic polycarbonate resin as the polycarbonate resin (A), and the balance is made of the rubber-reinforced vinyl resin (B). 2).
In this case, in the thermoplastic resin composition, since the content of the aromatic polycarbonate resin (A) is larger than the content of the rubber-reinforced vinyl resin (B), on the surface of the resin foam molded article, A skin layer can be formed more stably.

  Further, the second mold part is provided with a cavity forming convex part disposed in a cavity forming concave part provided in the first mold part, and the first mold part and the second mold part are provided in the cavity forming concave part. A filling gap for filling the molten resin is communicated with the cavity between the inner side surface formed in parallel with the movable direction and the outer side surface formed in the cavity forming convex portion in parallel with the movable direction. In the filling step, the molten resin is filled into the cavity and the filling gap is filled, and in the movable step, the molten resin is filled into the cavity and the filling gap. After filling, it is preferable that the first mold part and the second mold part are relatively movable in the separation direction.

In this case, in the filling step, a skin layer obtained by curing the molten resin to be filled almost without foaming is formed not only on the portion of the molten resin that contacts the surface of the cavity, but also in the filling gap. Also, it can be formed on the portion of the molten resin that contacts the inner surface of the cavity forming recess of the first mold part and the outer surface of the cavity forming protrusion of the second mold part. Thereby, in the movable step, when the first mold part and the second mold part are relatively moved in the separation direction, a foamed layer in which the molten resin is foamed is formed inside the resin foam molded body, and resin foam molding is performed. A skin layer can be formed on the entire surface of the body.
Therefore, the skin layer can be stably formed on the entire circumferential surface of the resin foam molded article by the idea of forming the filling gap.

In the filling step, the molten resin is filled into the entire cavity and the filling gap, and the molten resin is semi-cured to form an unfoamed skin layer. The first mold part and the second mold part are moved relative to each other in the separation direction, and a foam layer in which the molten resin is foamed is formed on an inner part with respect to the skin layer. It is preferable to manufacture (claim 4).
In this case, in the filling step, the skin layer is more stably formed on the entire surface of the resin foam molded body by performing the movable step after filling the entire cavity and filling gap with the molten resin. be able to.

The first mold part is a fixed mold part provided with a resin injection port for filling the molten resin into the cavity, and the second mold part is separated from the first mold part by the distance from the first mold part. Preferably, the movable part is movable in the direction.
In this case, the configuration of the apparatus for manufacturing the resin foam molded body can be further simplified.

The rubbery polymer (b1) is an ethylene / α-olefin rubber .
Thereby , the resin foam molding which was more excellent in intensity | strength and an external appearance can be shape | molded.

The chemical blowing agent is preferably selected from the group consisting of sodium hydrogen carbonate, azodicarbonamide, N, N′-dinitrosopentamethylenetetramine, and 4,4′-oxybis (benzenesulfonylhydrazide). (Claim 6 ).
In this case, a chemical foaming material is appropriate, and the molten resin filled in the cavity can be stably foamed.

The rubber-reinforced vinyl resin (B) has a graft rate of 10 to 150%, and an intrinsic viscosity of the acetone soluble part (measured in methyl ethyl ketone at 30 ° C.) of 0.2 to 0.8 dl / g. In addition, the polycarbonate resin (A) preferably has a viscosity average molecular weight of 12,000 to 40,000 (Claim 7 ).
In this case, the physical properties of the rubber-reinforced vinyl resin are appropriate, and a resin foam molded article excellent in strength and appearance can be molded more easily.

  When the graft ratio is less than 10%, the interfacial adhesive strength between the resin and the rubber is inferior, and excellent impact strength cannot be obtained. Moreover, a uniform cell cannot be obtained and the external appearance of a resin foaming molded object may fall. On the other hand, if the graft ratio exceeds 150%, the interface layer becomes thick, and a resin layer grafted inside the rubber develops, resulting in a decrease in rubber elasticity. As a result, excellent impact strength and uniform cells cannot be obtained, and the appearance of the resin foam molded article may be deteriorated.

If the intrinsic viscosity of the acetone-soluble part (measured in methyl ethyl ketone at 30 ° C.) is less than 0.2 dl / g, the impact resistance may be reduced. The intrinsic viscosity of the acetone-soluble part (in methyl ethyl ketone, 30 ° C. ) Exceeds 0.8 dl / g, the fluidity is lowered and the skin layer may not be formed easily.
When the viscosity average molecular weight of the aromatic polycarbonate resin (A) is less than 12,000, the impact resistance may be lowered. When the viscosity average molecular weight of the aromatic polycarbonate resin (A) exceeds 40,000, In some cases, the properties are lowered, uniform cells cannot be obtained, and the appearance of the resin foam molded article is lowered.

In the second reference invention, the foaming ratio of the resin foam molded article is preferably 1.1 to 1.6 times .
In this case, it is possible to obtain a resin foam molded article having an appropriate foaming ratio of the resin foam molded article, no fuzz on the surface, uniform cell diameter by foaming, excellent appearance, and excellent mechanical strength. .
In addition, when the expansion ratio of the resin foam molded body is less than 1.1 times, an effect such as lightening by foaming is not obtained so much. On the other hand, when the expansion ratio of the resin foam molded body exceeds 1.6 times, the molten resin filled in the cavity does not expand sufficiently, and the surface of the molded resin foam molded body may be wavy.
Moreover, the expansion ratio of the resin foam molded body can be more preferably 1.2 to 1.5 times.

The molding temperature of the resin foam molding is appropriately selected depending on the composition of the thermoplastic resin composition, but is usually 220 to 260 ° C. in the present invention. The shape of the resin foam molding is selected according to the purpose, application, etc., and can be plate-shaped (sheet-shaped), cylindrical, semi-cylindrical, rod-shaped, linear, massive, or the like.
The resin foam molded article of the present invention includes civil engineering / architecture related materials such as display boards, interior / exterior materials for vehicles, daily miscellaneous goods such as containers and trays, electrical / electronic parts, sports equipment, walls, floors, machine frames. , Furniture, decorative sheets, partitions, lattices, fences, gutters, sizing boards, interior / exterior materials for homes and offices such as carports, toys, cushioning materials for game machines, reinforcement materials, heat insulating materials, core materials, alternatives It can be used as a plywood or the like.
Furthermore, the resin foam molded article of the present invention can be used as an article that is integrated with another molded product, member, etc. depending on the application, and is applicable to the above application.

Below, the specific composition about the said thermoplastic resin composition and the said chemical foaming agent is demonstrated.
(Polycarbonate resin (A))
The polycarbonate resin (A) used in the present invention is obtained by reaction of various dihydroxyaryl compounds with phosgene (phosgene method), or obtained by transesterification of dihydroxyaryl compounds with diphenyl carbonate (esters). Exchange method). A preferred polycarbonate resin is an aromatic polycarbonate resin. A typical aromatic polycarbonate resin is 2,2′-bis (4-hydroxyphenyl) propane, that is, a polycarbonate resin obtained by a reaction of bisphenol A and phosgene.

  Here, as a dihydroxyaryl compound used as a raw material of the polycarbonate resin, bis (4-hydroxyphenyl) methane, 1,1′-bis (4-hydroxyphenyl) ethane, 2,2′-bis (4-hydroxyphenyl) Propane, 2,2′-bis (4-hydroxyphenyl) butane, 2,2′-bis (4-hydroxyphenyl) octane, 2,2′-bis (4-hydroxyphenyl) phenylmethane, 2,2′- Bis (4-hydroxy-3-methylphenyl) propane, 2,2′-bis (4-hydroxy-3-tert-butylphenyl) propane, 2,2′-bis (4-hydroxy-3-bromophenyl) propane 2,2′-bis (4-hydroxy-3,5-dichlorophenyl) propane, 1,1′-bis (4-hydroxyphenyl) silane Lopentane, 1,1′-bis (4-hydroxyphenyl) cyclohexane, 4,4′-dihydroxydiphenyl ether, 4,4′-dihydroxy-3,3′-dimethyldiphenyl ether, 4,4′-dihydroxyphenyl sulfide, 4, 4′-dihydroxy-3,3′-dimethylphenyl sulfide, 4,4′-dihydroxy-3,3′-dimethylphenyl sulfoxide, 4,4′-dihydroxyphenyl sulfoxide, 4,4′-dihydroxyphenyl sulfone, 4, 4'-dihydroxy-3,3'-dimethylphenylsulfone, 1,1'-bis (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane, 1,1'-bis (4-hydroxyphenyl) -3 , 3-Dimethylcyclohexane, 1,1′-bis (4-hydro Shifeniru) -3,3,5-trimethyl-cyclopentane, hydroquinone, resorcinol and the like, which are used alone or in combination of two or more. Particularly preferred is 2,2'-bis (4-hydroxyphenyl) propane, ie bisphenol A.

The viscosity average molecular weight of the polycarbonate resin (A) is preferably 12,000 to 40,000, more preferably 15,000 to 35,000, and particularly preferably 18,000 to 30,000. The higher the molecular weight, the higher the mechanical strength of the resin foam molded article, but the fluidity decreases, uniform cells cannot be obtained, and the appearance of the resin foam molded article tends to deteriorate. Two or more kinds of polycarbonates having different molecular weights can also be used.
Moreover, content of the polycarbonate resin (A) in the thermoplastic resin composition used for this invention is 20-80 mass%, Preferably it is 30-75 mass%, More preferably, it is 50-70 mass%. When the content of the polycarbonate resin (A) is less than 20% by mass, it becomes difficult to obtain a foamed molded product having a uniform cell diameter. On the other hand, when the content of the polycarbonate resin (A) exceeds 80% by mass, it is excellent. It tends to be difficult to obtain a resin foam molded article having a good appearance.

(Rubber reinforced vinyl resin (B))
(Rubber polymer (b1))
The rubbery polymer (b1) used in the present invention may be a homopolymer or a copolymer as long as it is rubbery at room temperature, but may be a non-diene polymer (non-diene polymer). Diene rubbery polymers) and diene polymers (diene rubbery polymers) are preferred. Furthermore, the rubbery polymer (b1) may be a crosslinked polymer or a non-crosslinked polymer. These can be used alone or in combination of two or more.

  Examples of the non-diene polymer (non-diene rubber polymer) include ethylene / α-olefin copolymer rubbers, urethane rubbers, acrylics containing units composed of ethylene units and α-olefins having 3 or more carbon atoms. Examples thereof include a polymer obtained by hydrogenating a (co) polymer including a unit rubber, a silicone rubber, a silicone / acrylic IPN rubber, and a conjugated diene compound. These copolymers may be block copolymers or random copolymers. These copolymers may be hydrogenated (however, the hydrogenation rate is 50% or more). The said non-diene polymer can be used individually by 1 type or in combination of 2 or more types.

  Examples of the diene polymer (diene rubber polymer) include homopolymers such as polybutadiene, polyisoprene, polychloroprene, styrene / butadiene copolymer, styrene / butadiene / styrene copolymer, Examples include acrylonitrile / butadiene copolymer, styrene / butadiene copolymer rubber such as acrylonitrile / styrene / butadiene copolymer, styrene / isoprene copolymer, styrene / isoprene / styrene copolymer, acrylonitrile / styrene / isoprene. Examples thereof include styrene / isoprene copolymer rubber such as a copolymer, or natural rubber. These copolymers may be block copolymers or random copolymers. These copolymers may be hydrogenated (however, the hydrogenation rate is less than 50%). The said diene polymer can be used individually by 1 type or in combination of 2 or more types.

  The rubber-reinforced vinyl resin (B) obtained when using at least one of ethylene / α-olefin and ethylene / α-olefin / non-conjugated diene copolymer as the rubber polymer (b1), Generally, it is said to be “AES resin”. Further, the rubber reinforced vinyl resin (B) obtained when a diene polymer is used as the rubber polymer (b1) is a diene rubber reinforced vinyl resin, and generally referred to as “ABS resin”. It is said. Furthermore, the rubber-reinforced vinyl resin (B) obtained when acrylic rubber is used as the rubber polymer (b1) is an acrylic rubber-reinforced vinyl resin, and is generally referred to as “ASA resin”. ing.

  The shape of the rubbery polymer (b1) used for forming the rubber-reinforced vinyl resin (B) is not particularly limited, but when it is particulate, the volume average particle diameter is preferably 50 to 3,000 nm. More preferably, it is 100-2,000 nm, More preferably, it is 120-800 nm. If the volume average particle diameter is less than 50 nm, the thermoplastic resin composition of the present invention and a molded product (resin foam molded product) containing the thermoplastic resin composition tend to be inferior in impact resistance. The surface appearance tends to be inferior. The weight average particle diameter can be measured by an electron micrograph, a laser diffraction method, a light scattering method, or the like.

(Vinyl monomer (b2))
The vinyl monomer (b2) used for forming the rubber-reinforced vinyl resin (B) contains an aromatic vinyl compound. The vinyl monomer (b2) may be only an aromatic vinyl compound, and the aromatic vinyl compound and, for example, a vinyl cyanide compound, a (meth) acrylic acid ester compound, a maleimide compound, an acid anhydride It may be a combination of a compound copolymerizable with an aromatic vinyl compound such as a product. The compounds copolymerizable with the above aromatic vinyl compound can be used singly or in combination of two or more.
Accordingly, the vinyl monomer (b2) is a monomer (x) composed of one or more aromatic vinyl compounds, or one or more aromatic vinyl compounds, and copolymerized with the aromatic vinyl compounds. A monomer (y) combined with one or more of the possible compounds can be used.

  The aromatic vinyl compound is not particularly limited as long as it is a compound having at least one vinyl bond and at least one aromatic ring. Examples thereof include styrene, α-methylstyrene, o-methylstyrene, Examples thereof include p-methylstyrene, vinyltoluene, β-methylstyrene, ethylstyrene, p-tert-butylstyrene, vinylxylene, vinylnaphthalene, monochlorostyrene, dichlorostyrene, monobromostyrene, dibromostyrene, and fluorostyrene. These can be used alone or in combination of two or more. Of these, styrene and α-methylstyrene are preferred.

Examples of the vinyl cyanide compound include acrylonitrile and methacrylonitrile. These can be used alone or in combination of two or more. Of these, acrylonitrile is preferred.
Examples of the (meth) acrylate compound include methyl (meth) acrylate, ethyl (meth) acrylate, n-propyl (meth) acrylate, isopropyl (meth) acrylate, n-butyl (meth) acrylate, Examples thereof include isobutyl (meth) acrylate, tert-butyl (meth) acrylate, hexyl (meth) acrylate, cyclohexyl (meth) acrylate, and phenyl (meth) acrylate. These can be used alone or in combination of two or more. Of these, methyl (meth) acrylate is preferred.

  Examples of the maleimide compounds include maleimide, N-methylmaleimide, N-butylmaleimide, N-phenylmaleimide, N- (2-methylphenyl) maleimide, N- (4-hydroxyphenyl) maleimide, N-cyclohexylmaleimide and the like. Can be mentioned. These can be used alone or in combination of two or more. In addition, as another method for introducing a unit composed of a maleimide compound, for example, a method in which maleic anhydride is copolymerized and then imidized may be used.

Examples of the acid anhydride include maleic anhydride, itaconic anhydride, citraconic anhydride, and the like. These can be used alone or in combination of two or more.
In addition to the above compounds, vinyl compounds having a functional group such as a hydroxyl group, an amino group, an epoxy group, an amide group, a carboxyl group, or an oxazoline group can be used as necessary. For example, 2-hydroxyethyl (meth) acrylate, hydroxystyrene, N, N-dimethylaminomethyl (meth) acrylate, N, N-diethyl-p-aminomethylstyrene, glycidyl (meth) acrylate, (meth) Examples include 3,4-oxycyclohexyl acrylate, vinyl glycidyl ether, methallyl glycidyl ether, allyl glycidyl ether, methacrylamide, acrylamide, (meth) acrylic acid, vinyl oxazoline, and the like. These can be used alone or in combination of two or more.

  Examples of the vinyl monomer (b2) include one or more aromatic vinyl compounds and one or more combinations of compounds copolymerizable with the aromatic vinyl compound, that is, the monomer (y). In this case, the mass ratio between the aromatic vinyl compound and the other compound (aromatic vinyl compound / other compound) is usually (100% by mass). 2 to 95) mass% / (98 to 5) mass%, preferably (10 to 90) mass% / (90 to 10) mass%. If the ratio of the aromatic vinyl compound is too small, molding processability tends to be inferior. If it is too large, the resulting molded article may not have sufficient chemical resistance, heat resistance, and the like.

  The monomer (y) is preferably a combination of an aromatic vinyl compound and a vinyl cyanide compound (hereinafter referred to as “monomer (y1)”), an aromatic vinyl compound, and a vinyl cyanide compound. And other compounds (such as (meth) acrylic acid ester compounds) (hereinafter referred to as “monomer (y2)”). By using a vinyl cyanide compound, the balance of physical properties such as chemical resistance and heat resistance is improved.

(Vinyl monomer (b3))
As described above, the rubber-reinforced vinyl resin (B) may be only the rubber-reinforced vinyl resin (B) (graft copolymer (B1)), or the rubber-reinforced vinyl resin ( It may be a mixture comprising B) and a (co) polymer of the vinyl monomer (b3) (hereinafter referred to as “(co) polymer (B2)”).
As the vinyl monomer (b3) used for forming the (co) polymer (B2), the compounds exemplified as the vinyl monomer (b2) can be used. Therefore, the (co) polymer (B2) is a polymer obtained by polymerizing components having exactly the same composition as the vinyl monomer (b2) used for forming the rubber-reinforced vinyl resin (B). It may be a polymer obtained by polymerizing the same type of monomer with different compositions, or a polymer obtained by polymerizing different types of monomers with different compositions. It may be a coalescence. Two or more of these polymers may be contained.

Next, the manufacturing method of the said graft copolymer (B1) and the said copolymer (B2) is demonstrated.
The graft copolymer (B1) as the rubber-reinforced vinyl resin (B) is produced by polymerizing the vinyl monomer (b2) in the presence of the rubbery polymer (b1). Can do. As the polymerization method, emulsion polymerization, solution polymerization, bulk polymerization, and bulk-suspension polymerization are preferable.

  In the production of the graft copolymer (B1), the rubber polymer (b1) and the vinyl monomer (b2) are used in the reaction system in the total amount of the rubber polymer (b1). In the presence, the vinyl monomer (b2) may be added all at once to initiate the polymerization, or the polymerization may be carried out separately or continuously. Further, in the presence or absence of a part of the rubber polymer (b1), the vinyl monomer (b2) may be added all at once to initiate polymerization, or divided or continuously. May be added. At this time, the remainder of the rubber-like polymer (b1) may be added all at once in the course of the reaction, divided or continuously.

  When 100 parts by mass of the graft copolymer (B1) is produced, the amount of the rubbery polymer (b1) used is usually 5 to 80 parts by mass, preferably 10 to 70 parts by mass, and more preferably 15 to 15 parts by mass. 60 parts by mass. Moreover, the usage-amount of the said vinylic monomer (b2) is 25-1,900 mass parts normally with respect to 100 mass parts of said rubber-like polymers (b1), Preferably it is 60-560 mass parts.

  The graft copolymer (B1) used in the present invention can be produced by known emulsion polymerization, solution polymerization, suspension polymerization, etc., but when produced by emulsion polymerization, it is usually coagulated with a coagulant and obtained. The resulting powder is purified by washing and drying. As this coagulant, it is common to use at least one of inorganic salts such as calcium chloride, magnesium sulfate, magnesium chloride, and sodium chloride and inorganic acids such as sulfuric acid, hydrochloric acid, and phosphoric acid. At this time, when the obtained graft copolymer (B1) is blended with the polycarbonate resin (A), there is a problem that the molecular weight of the polycarbonate resin (A) is lowered due to a salt or an emulsifier remaining in the component (B1). Therefore, it is desirable to use an acid such as sulfuric acid as a coagulant.

  In addition, a general thing can be used as a radical initiator at the time of graft polymerization. Specific examples include cumene hydroperoxide, diisopropylbenzene hydroperoxide, potassium persulfate, azobisisobutyronitrile, benzoyl peroxide, lauroyl peroxide, t-butylperoxylaurate, t-butylperoxymonocarbonate. Etc. The usage-amount of a radical initiator is 0.05-5 mass% normally with respect to a monomer component, Preferably it is 0.1-1 mass%.

  In order to achieve the effects of the present invention, an organic peroxide and a solvent are selected so that the grafting reaction proceeds uniformly during graft polymerization, and a rubbery polymer is synthesized by emulsion polymerization and grafted by emulsion polymerization. Polymerize, start the polymerization by uniformly dissolving the rubbery polymer, dissolve the pre-melted kneaded material in the solution and perform solution polymerization or bulk polymerization, emulsion polymerization or suspension polymerization of the re-emulsified It is preferable to devise a polymerization method such as.

The graft ratio of the rubber-reinforced vinyl resin (B) (graft copolymer (B1)) thus obtained is 10 to 150%, preferably 30 to 100%. When the graft ratio is less than 10%, the interfacial adhesive strength between the resin and the rubber is inferior, excellent impact strength and uniform cells cannot be obtained, and the appearance of the resin foam molded article may be deteriorated. On the other hand, if the graft ratio exceeds 150%, the interface layer becomes thick, and a resin layer grafted inside the rubber develops, resulting in a decrease in rubber elasticity. As a result, excellent impact strength and uniform cells cannot be obtained, and the appearance of the resin foam molded article may be deteriorated. The graft ratio can be easily adjusted by changing the type and amount of the rubbery polymer, polymerization initiator, chain transfer agent, emulsifier, and the like, as well as the polymerization time and polymerization temperature.
Here, the graft ratio (%) is as follows when the rubber component in the graft copolymer (B1) component is x (g) and the acetone insoluble content in the graft copolymer (B1) component is y (g). This is a value obtained by the following formula.
Graft rate (%) = ((y−x) / x) × 100

The intrinsic viscosity (measured in methyl ethyl ketone at 30 ° C.) of the acetone soluble part of the rubber-reinforced vinyl resin (B) of the present invention is 0.2 to 0.8 dl / g, preferably 0.3 to 0.00. 7 dl / g. If the intrinsic viscosity of the acetone-soluble part (measured in methyl ethyl ketone at 30 ° C.) is less than 0.2 dl / g, the impact resistance may be reduced. The intrinsic viscosity of the acetone-soluble part (in methyl ethyl ketone, 30 ° C. ) Exceeds 0.8 dl / g, the fluidity is lowered and the skin layer may not be formed easily.
The intrinsic viscosity can be easily controlled by changing the kind and amount of a polymerization initiator, a chain transfer agent, an emulsifier, a solvent, a polymerization time, a polymerization temperature, and the like.

On the other hand, the copolymer (B2) in the rubber-reinforced vinyl resin (B) component used in the present invention preferably has a mass ratio of aromatic vinyl compound / vinyl cyanide compound / other vinyl monomer. It is 50-90 / 10-40 / 0-30, More preferably, it is 60-79 / 21-40 / 0-30, Most preferably, it is 62-78 / 22-38 / 0-30 (mass%). When the amount of the vinyl cyanide compound is 21% by mass or more in the above range, the resulting molded article may be further excellent in chemical resistance. Moreover, if the usage-amount of an aromatic vinyl compound is less than 50 mass%, compatibility with a polycarbonate resin (A) will fall, and impact resistance and heat-resistant deterioration will be inferior, on the other hand, if it exceeds 90 mass%, this will also be In addition, the compatibility with the polycarbonate resin (A) is lowered, and the impact strength and chemical resistance may be inferior. Furthermore, if the amount of the vinyl cyanide compound used is less than 10% by mass, the compatibility with the polycarbonate resin (A) is remarkably reduced, resulting in problems such as reduced impact resistance and surface peeling, while 40% by mass. When it exceeds, heat-resistant deterioration property may fall. Furthermore, when the usage-amount of another vinyl monomer exceeds 30 mass%, compatibility with polycarbonate resin (A) will fall and impact resistance may be inferior.
The aromatic vinyl compound, the vinyl cyanide compound and other vinyl monomers are the same as the monomer components used for the rubber-reinforced vinyl resin (B).

  The intrinsic viscosity (measured in methyl ethyl ketone at 30 ° C.) of the acetone-soluble component of the copolymer (B2) of the present invention is 0.31 to 0.8 dl / g, preferably 0.32 to 0.8 dl / g. It is 32-0.7 dl / g, More preferably, it is 0.36-0.7 dl / g. Within the above range, if the intrinsic viscosity is less than 0.31 dl / g, the resulting molded article (resin foam molded product) is inferior in impact resistance. On the other hand, if it exceeds 0.8 dl / g, the moldability is remarkably lowered. However, it may be difficult to form the skin layer of the resin foam molding.

  The copolymer (B2) used in the present invention can be produced by known emulsion polymerization, solution polymerization, suspension polymerization, etc., but when produced by emulsion polymerization, it is usually a powder that can be coagulated with a coagulant. The product is purified by washing with water and drying. As this coagulant, it is common to use at least one of inorganic salts such as calcium chloride, magnesium sulfate, magnesium chloride, and sodium chloride and inorganic acids such as sulfuric acid, hydrochloric acid, and phosphoric acid. At this time, when the obtained copolymer (B2) is blended with the polycarbonate resin (A), the molecular weight of the polycarbonate resin (A) is reduced due to a salt or an emulsifier remaining in the copolymer (B2) component. There is. Therefore, it is desirable to use an acid such as sulfuric acid as a coagulant.

The blending ratio of the graft copolymer (B1) and the copolymer (B2) used as the rubber-reinforced vinyl resin (B) is such that the component (B1) is 20 to 100% by mass, preferably 30 to 85% by mass, More preferably, it is 35-80 mass%, (B2) component is 0-80 mass%, Preferably it is 15-70 mass%, More preferably, it is 20-65 mass% (however, (B1) + (B2) = 100 mass%) ).
Moreover, the ratio of the rubber-like polymer (b1) in rubber-reinforced vinyl resin (B) is 4-40 mass% normally, Preferably it is 6-35 mass%, More preferably, it is 8-30 mass%.

  The blending ratio of the rubber-reinforced vinyl resin (B) component in the thermoplastic resin composition of the present invention is 20 to 80% by mass. Preferably it is 25-70 mass%, More preferably, it can be 30-50 mass%. When the blending ratio of the rubber-reinforced vinyl resin (B) component is less than 20% by mass, the moldability of the resin composition is lowered and it becomes difficult to obtain a resin foam molded article having an excellent appearance, while 80% by mass. If it exceeds%, it becomes difficult to obtain a resin foam molded article having a uniform cell diameter.

The rubbery polymer (b1) of the present invention is preferably an ethylene / α-olefin rubbery polymer. By using an AES resin as the rubber-reinforced vinyl resin (B), it is possible to easily obtain a resin foam molded article having a uniform cell diameter and excellent appearance as compared with the case where an ABS resin is used. This is presumed to be due to a difference in the degree of crosslinking of the rubbery polymer portion, that is, a difference in the degree of freedom of shape.
Moreover, AES resin is excellent in heat-resistant deterioration. Although the thermoplastic resin composition used in the present invention contains the polycarbonate resin (A), it is required to increase the molding temperature. In this respect, the AES resin can satisfy the requirement that it has excellent heat deterioration resistance and excellent workability.

  In the thermoplastic resin composition used in the present invention, the content of the ethylene / α-olefin rubber polymer derived from the rubber-reinforced vinyl resin (B) component is preferably 2 to 20% by mass, and more preferably. Is 2 to 15% by mass, particularly preferably 3 to 15% by mass. When it is in the above range, the thermoplastic resin composition which is the object of the present invention is easily obtained.

Here, the ethylene / α-olefin-based rubbery polymer (b1) serving as the base rubber of the rubber-reinforced vinyl resin (B) (graft copolymer (B1)) is an ethylene / α having 3 to 20 carbon atoms. -Olefin / non-conjugated diene = A copolymer rubber obtained by copolymerizing a monomer having a mixing ratio of 5 to 95/95 to 5/0 to 30% by mass is preferable.
Examples of the α-olefin having 3 to 20 carbon atoms include propylene, 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, 1-heptene, 1-octene, 1-decene, 1-dodecene and the like. Preferably, propylene, 1-butene, 1-octene, and more preferably propylene. These α-olefins can be used alone or in combination of two or more. The α-olefin has 3 to 20 carbon atoms, preferably 3 to 12 and more preferably 3 to 8. When the number of carbon atoms exceeds 20, the copolymerizability is extremely lowered, which is not preferable. The weight ratio of ethylene and α-olefin is preferably 5 to 95/95 to 5, more preferably 60 to 88/40 to 12, and particularly preferably 70 to 85/30 to 15.

  Examples of non-conjugated dienes that may be used in the ethylene / α-olefin rubbery polymer (b1) include alkenyl norbornenes, cyclic dienes, and aliphatic dienes, preferably 5-ethylidene- 2-norbornene and dicyclopentadiene. These non-conjugated dienes can be used alone or in combination of two or more. The non-conjugated diene content in the ethylene / α-olefin rubbery polymer is 0 to 30% by mass, preferably 0 to 15% by mass. In addition, the amount of unsaturated groups of this rubbery polymer is preferably in the range of 0 to 40 in terms of iodine value.

  In order to produce the ethylene / α-olefin rubber polymer (b1) of the present invention, either a heterogeneous catalyst or a homogeneous catalyst may be used. Examples of the heterogeneous catalyst include a vanadium catalyst in which a vanadium compound and an organoaluminum compound are combined. Examples of the homogeneous catalyst include a metallocene catalyst. In particular, a metallocene catalyst is effective for producing the rubber using an α-olefin having 6 to 20 carbon atoms.

The Mooney viscosity (ML1 + 4, 100 ° C.) of the ethylene / α-olefin rubbery polymer (b1) is preferably 40 or less, more preferably 25 to 35. The Mooney viscosity can be adjusted by changing the type and amount of the molecular weight regulator, the monomer concentration, the reaction temperature, and the like.
The ethylene / α-olefin rubbery polymer preferably has a content of components having a weight average molecular weight of 1 million or more in terms of polystyrene of 10% by mass or less, more preferably 8% by mass or less. Such a rubbery polymer can be produced by changing the type / amount of the molecular weight regulator and the type / amount of the catalyst. Furthermore, the glass transition temperature (Tg) of the ethylene / α-olefin rubber polymer is preferably −110 to −40 ° C., more preferably −70 to −50 ° C., and the melting point (Tm) is preferably 30 to 30 ° C. 110 degreeC, More preferably, it is 40-70 degreeC.

  The ratio of the ethylene / α-olefin rubber polymer is usually 3 to 50% by mass, preferably 5 to 45% by mass, more preferably 7 to 40% by mass in the graft copolymer (B1) component. It is. If it is less than 3% by mass, impact resistance may not be exhibited, whereas if it exceeds 50% by mass, moldability and appearance may be deteriorated.

  The chemical foaming agent to be used is not particularly limited, but is preferably a thermal decomposition type inorganic foaming agent (sodium bicarbonate, ammonium carbonate, ammonium bicarbonate, etc.) that is decomposed to generate carbon dioxide, and decomposed to nitrogen. Pyrolytic foaming agents that generate gas (azodicarbonamide, N, N′-dinitrosopentamethylenetetramine, 4,4′-oxybis (benzenesulfonylhydrazide), azobisisobutyronitrile, p-toluenesulfonylhydrazide, etc. A well-known thermal decomposition type foamable compound is mentioned.

The content of the chemical foaming agent is appropriately selected according to the type of the chemical foaming agent and the resin used so that a desired foaming ratio can be obtained, but the chemical foaming agent is used with respect to 100 parts by mass of the thermoplastic resin. It is 0.05-5 mass parts, Preferably it is 0.1-4 mass parts, More preferably, it is 0.3-3 mass parts. When the content of the chemical foaming agent is less than 0.05 parts by mass, the content of the chemical foaming agent is small and it is difficult to make the cell diameters of foaming uniform. On the other hand, when the content of the chemical foaming agent exceeds 5 parts by mass, the content of the chemical foaming agent is large, mold contamination due to the residue of the chemical foaming agent occurs, and a foam molded article having an excellent appearance is obtained. Becomes difficult.
As a blending method of the foaming agent to the molten state plastic resin, the pellets of the thermoplastic resin composition and the foaming agent master batch pellet are dry blended, and then supplied to the molding machine, and the resin is plasticized in the molding machine. The foaming method is preferably used. Moreover, you may use a physical foaming agent together. Specific examples of the physical foaming agent include propane, butane, water, carbon dioxide gas, and the like.

In addition, a heat aging inhibitor can be mix | blended with the thermoplastic resin composition used for this invention.
Examples of the heat aging inhibitor include phenol, phosphorus, and sulfur, and a phenol, phosphorus, and sulfur mixed system is preferable. When this three-type mixed system is used as a heat aging inhibitor, the effect of maintaining the tensile elongation when exposed to a high temperature for a long time can be obtained.

  Among the heat aging inhibitors, phenolic compounds include 2,6-di-t-butylphenol derivatives, 2-methyl-6-t-butylphenol derivatives, octadecyl 3 (3,5-di-t-butyl-4-hydroxy). Phenyl) propionate, 4,4′-butylidene-bis (6-tert-butyl-m-cresol), pentaerythrityl tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate] 2 [1- (2hydroxy-3,5-di-t-pentylphenyl) -ethyl] -4,6-di-t-pentylphenyl acrylate, 2-t-butyl-6 (3-t-butyl- 2-hydroxy-5-methylbenzyl) -4-methylphenyl acrylate and the like.

Examples of phosphorus-based materials include tris (2,4-di-t-butylphenyl) phosphite, cyclic neopentanetetraylbis (2,4-di-t-butylphenyl phosphite), distearyl pentaerythritol diphosphite. , Sodium dihydrogen phosphate, disodium monohydrogen phosphate, and the like.
Examples of sulfur-based compounds include 3,3′-thiobispropionic acid didodecyl ester, 3,3′-thiobispropionic acid dioctadecyl ester, pentaerythritol-tetrakis (3-laurylpropionate), dilauryl 3,3′-. Examples include thiodipropionate.

  The ratio of the heat aging inhibitor in the thermoplastic resin composition used in the present invention is 0 to 5% by mass, preferably 0 to 3% by mass. In the thermoplastic resin composition of the present invention, the rubber reinforced vinyl resin (B) component other than the polycarbonate resin (A) is improved in heat aging characteristics by adding a heat aging inhibitor. The heat aging inhibitor may act as a catalyst for promoting hydrolysis, and there is a tendency to suppress deterioration when no heat aging inhibitor is added. In view of these contradictory effects, an optimum heat aging prevention effect can be obtained by adding the heat aging inhibitor up to 5% by mass.

  For the thermoplastic resin composition used in the present invention, if necessary, glass fiber, fibrous filler such as carbon fiber, glass beads, rock filler, calcium carbonate, talc, mica, glass flake, barium sulfate, graphite The fillers such as molybdenum disulfide and magnesium oxide can be used alone or in combination of two or more. By blending these fillers, rigidity, high heat distortion temperature, and the like can be further imparted to the thermoplastic resin composition used in the present invention. Moreover, the foaming performance of the thermoplastic resin composition of this invention may improve by mix | blending said talc, calcium carbonate, etc.

The thermoplastic resin composition used in the present invention may contain additives such as known weathering agents, lubricants, colorants, antistatic agents, and silicone oils.
Of these, benzotriazole, triazine, benzophenone, and the like are preferable as the weathering agent. As the lubricant, ethylene bisstearylamide, hydrogenated castor oil and the like are preferable. Examples of the colorant include carbon black and bengara. Examples of the antistatic agent include polyethers and sulfonates having an alkyl group.

  The thermoplastic resin composition used in the present invention can be kneaded using various extruders, Banbury mixers, kneaders, rolls and the like. For example, first, pellets of the thermoplastic resin composition can be obtained by kneading the components (A) and (B) and other additives as necessary. Specific examples include a method of melting the components (A) and (B) with a twin screw extruder. The kneading temperature is appropriately selected depending on the composition of the thermoplastic resin composition, but is usually 220 to 260 ° C. in the present invention.

Hereinafter, embodiments of the resin foam molded body and the manufacturing method thereof according to the present invention will be described with reference to the drawings.
(Example)
As shown in FIGS. 1 to 4, the method for manufacturing the resin foam molded body 6 of the present example uses the first mold part 2 and the second mold part 3 that is movable relative to the first mold part 2. In this method, the skin layer 61 is formed on the surface of the resin foam molded body 6 and the foam layer 62 is formed on the inner portion of the skin layer 61. In the manufacturing method of this example, as shown in FIGS. 2 and 3, as the filling process, the chemical foaming agent is heated in the cavity 41 </ b> A formed between the second mold part 3 and the first mold part 2. A skin layer 61 is formed on a portion of the molten resin 60 that is in contact with the surface of the cavity 41A by filling the molten resin 60 that is kneaded into the plastic resin composition, and as a movable process, as shown in FIG. 2 and the second mold part 3 are moved relative to each other in the separation direction R in which the volume of the cavity 41 </ b> A expands, and a foam layer 62 in which the molten resin 60 is foamed is formed on the inner side of the skin layer 61.

Moreover, content of a chemical foaming agent is 0.05-5 mass parts with respect to 100 mass parts of thermoplastic resin compositions. The thermoplastic resin composition of this example contains an aromatic polycarbonate resin (A) and a rubber-reinforced vinyl resin (B). The rubber-reinforced vinyl resin (B) of this example is obtained by polymerizing a vinyl monomer (b2) containing an aromatic vinyl compound and a vinyl cyanide compound in the presence of the rubbery polymer (b1). It consists of a graft copolymer (B1). The rubber-reinforced vinyl resin (B) in this example is a rubber-reinforced styrene resin (B).
The rubber-reinforced vinyl resin (B) can also be composed of a mixture of the vinyl monomer (b3) copolymer (B2) and the graft copolymer (B1).

Below, it explains in full detail with reference to FIGS. 1-4 about the resin foaming molded object 6 of this example, and its manufacturing method.
The method of manufacturing the resin foam molded body 6 of this example is a method of expanding the volume of the cavity 41A filled with the molten resin 60 using a chemical foaming agent and foaming the molten resin 60. The skin layer 61 in which the molten resin 60 is hardened with almost no foaming can be effectively formed on the entire surface of the body 6.
In this example, as shown in FIGS. 1 and 4, the resin foam molded body 6 is molded using the manufacturing apparatus 1 including the first mold part 2 and the second mold part 3. The first mold part 2 of this example is a fixed mold part provided with a resin injection port 22 for filling the molten resin 60 in the cavity 41. The second mold part 3 of this example is a movable mold part that is movable in the separation direction R with respect to the first mold part 2.

In addition, the second mold part 3 of this example is larger than the first mold part 2 so that the volume of the cavity 41 formed between the first mold part 2 and the first mold part 2 is enlarged by 1.1 to 1.6 times. It is configured to retreat in the separation direction R. And the expansion ratio of the resin foam molded body 6 to be foam-molded in this example is 1.1 to 1.6 times.
As shown in FIGS. 2 and 3, the manufacturing apparatus 1 of this example is connected to a resin injection port 22 provided in the first mold part 2, and an injection nozzle 25 for injecting a molten resin 60 into the cavity 41. have. The second mold part 3 of this example is configured to move forward and backward (move in the movable direction D) with respect to the first mold part 2 by a drive source that operates by hydraulic pressure, air pressure, electric power, and the like.

In this example, a resin foam molded body 6 having a substantially rectangular parallelepiped shape is foam-molded using the first mold part 2 and the second mold part 3.
As shown in FIG. 4, the second mold part 3 of this example is separated from the first mold part 2 until the distal end surface 312 of the cavity forming convex part 31 moves to the end part in the movable direction D of the filling gap 42. It is configured to move in the direction R.
When the second mold part 3 is in the original position 301 with respect to the first mold part 2, a filling gap 42 for filling the molten resin 60 is formed in communication with the cavity 41. As shown in FIGS. 1 and 2, when the second mold part 3 is in the original position 301 before moving in the separation direction R, there is a volume between the second mold part 3 and the first mold part 2. As shown in FIG. 4, when the second mold part 3 is in the movable position 302 that is movable in the separation direction R, the second mold part 3 and the first mold are formed. A cavity 41 </ b> B having an enlarged volume is formed between the portion 2.

As shown in FIG. 1, the first mold portion 2 of this example is orthogonal to the resin injection side surface 212 of the cavity 41 (the surface on which the fixed side surface of the resin foam molded body 6 is molded) and the resin injection side surface. There is a cavity forming recess 21 for forming a side surface 211 (inner side surface 211, a surface on which all the side surfaces of the resin foam molded body 6 are molded) of the entire circumference. The second mold part 3 of the present example includes a surface 312 on the resin receiving side in the cavity 41 (a surface on which the movable surface of the resin foam molded body 6 is molded) and a side surface 311 on the entire circumference orthogonal to the surface on the resin injection side. It has a cavity forming convex portion 31 for forming the outer side surface 311).
The inner side surface 211 of the cavity forming concave portion 21 of the first mold part 2 and the outer side surface 311 of the cavity forming convex part 31 of the second mold part 3 are formed in parallel to the movable direction D.

Further, as shown in the figure, in the first mold part 2 of the present example, there is an outer periphery of the opening tip part 23 and the second mold part 3 around the entire circumference of the opening tip part 23 of the mold wall part that forms the cavity forming recess 21. The closing type part 5 which closes | closes between the side surfaces 311 is provided.
When the manufacturing apparatus 1 moves the second mold part 3 in the separation direction R with respect to the first mold part 2, the outer surface 311 of the second mold part 3 slides on the inner peripheral surface 51 of the closed mold part 5. By moving, the state where the filling gap 42 is formed is maintained, and the volume of the cavity 41A is increased.

As shown in FIG. 4, when the manufacturing apparatus 1 moves the second mold part 3 relative to the first mold part 2 in the separation direction R, the manufacturing apparatus 1 closes the distal end surface 312 of the second mold part 3. The inner end face 52 of the mold part 5 is configured to coincide. In the movable step, when the second mold part 3 is moved in the separation direction R with respect to the first mold part 2, the skin layer 61 is formed on the entire surface of the resin foam molded body 6, and the skin A foam layer 62 can be formed on the inner portion of the layer 61.
Depending on the shape of the resin foam molded body 6 to be molded, the second mold part 3 can be moved in the separation direction R until the front end face 312 of the second mold part 3 and the inner end face 52 of the closing mold part 5 coincide. Alternatively, a shape in which the protruding portion of the skin layer 61 protrudes from the resin foam molded body 6 can be formed.

Next, a method for manufacturing the resin foam molded body 6 using the manufacturing apparatus 1 will be described in detail.
In this example, first, as shown in FIGS. 2 and 3, as shown in FIG. 2 and FIG. inject. At this time, the molten resin 60 flows from the cavity 41 </ b> A into the filling gap 42, and the molten resin 60 is filled into the entire cavity 41 and the filling gap 42 in a reduced state. And the part of the molten resin 60 which contacts the surface of the cavity forming concave part 21 of the first mold part 2 and the surface of the cavity forming convex part 31 of the second mold part 3 is cooled and hardened earlier than the other parts and semi-cured. A skin layer 61 in a state is formed.

Next, as a moving process, as shown in FIG. 4, the second mold part 3 is moved in the separation direction R with respect to the first mold part 2. At this time, the outer surface 311 of the cavity forming convex part 31 of the second mold part 3 slides against the skin layer 61 of the molten resin 60 filled and cured in the filling gap 42, and the skin layer 61 The molten resin 60 flows into the inner portion and foams. Further, on the inner side portion of the skin layer 61 formed on the resin injection side surface 212 of the cavity forming concave portion 21 of the first mold part 2 and the resin receiving side surface 312 of the cavity forming convex part 31 of the second mold part 3. Also, the molten resin 60 flows in and foams.
Thus, the foamed layer 62 in which the molten resin 60 is foamed can be formed inside the resin foam molded body 6, and the skin layer 61 can be formed on the entire surface of the resin foam molded body 6. Therefore, the skin layer 61 can be stably formed on the entire surface, and the strength of the foamed resin foam molded body 6 can be effectively improved.

Further, in this example, when the volume of the cavity 41A is expanded by using the thermoplastic resin composition, the foamed layer 62 is formed inside the molten resin 60 and foamed in the resin foam molded body 6 to be molded. The cell diameter can be made more uniform, and deterioration of the appearance of the resin foam molded body 6 can be suppressed.
Moreover, in this example, the cell diameter by foaming can be made as uniform as possible due to the presence of the aromatic polycarbonate resin (A) having a high viscosity at a predetermined temperature at which resin molding is performed. Can be improved. Further, the skin layer 61 is stably formed on the surface of the resin foam molding 6 due to the presence of the rubber-reinforced styrene resin (B) having a lower viscosity than the aromatic polycarbonate resin (A) at a predetermined temperature at which the resin molding is performed. Can be formed.

  Therefore, according to the method for manufacturing the resin foam molded body 6 of this example, the strength of the resin foam molded body 6 to be molded can be improved by forming the stable skin layer 61, and the cell diameter by foaming can be made more uniform. Thus, deterioration of the appearance of the resin foam molded body 6 can be suppressed.

(Confirmation test)
In this confirmation test, the excellent effect of the resin foam molded body 6 (Inventions 1 to 7) molded using the thermoplastic resin composition was confirmed. Specifically, the molded resin foam molded body 6 was observed by observing the surface appearance, measuring the flexural modulus (MPa) as strength, and observing the internal cross section, and evaluated whether they were excellent. The evaluation result about the resin foam molded object 6 (invention products 1-7) is shown in Table 1, and the resin foam molded object 6 shape | molded using the thermoplastic resin composition different from invention products 1-7 for comparison. Table 2 shows the evaluation results of (Comparative products 1 to 8).

Each resin used for the thermoplastic resin composition (invention products 1 to 7) and other thermoplastic resin compositions (comparative products 1 to 8) in this confirmation test was as follows.
(1) Polycarbonate resin (A) (indicated by PC in Table 1)
“Novalex 7022PJ” manufactured by Mitsubishi Engineering Plastics Co., Ltd. was used as the aromatic polycarbonate resin.

(2) Graft copolymer (B1-1) (indicated as AES in Table 1)
(Preparation of AES resin)
In a stainless steel autoclave with a ribbon-type stirring blade and having an internal volume of 10 liters, 30 parts of EPDM (manufactured by JSR Corporation, EP-82), 45.5 parts of styrene (aromatic vinyl compound), acrylonitrile (vinyl cyanide compound) ) 24.5 parts and 100 parts of toluene were charged, the temperature was raised after stirring, and the rubbery polymer (b1) was completely dissolved to obtain a uniform solution. Subsequently, 0.1 part of t-dodecyl mercaptan, 0.5 part of benzoyl peroxide and 0.1 part of dicumyl peroxide were added, and the polymerization reaction was carried out at a stirring rotational speed of 200 rpm while being kept constant at 95 ° C. It took 1 hour from the 6th hour after the start of the reaction, the temperature was raised to 120 ° C., and the reaction was further completed for 2 hours. The polymerization conversion rate was 97%. After cooling to 100 ° C., 0.2 part of 2,2-methylene-bis-4-methyl-6-butylphenol is added, and then the reaction mixture is withdrawn from the autoclave, and unreacted substances and solvent are distilled off by steam distillation. After being crushed, the volatile matter was substantially distilled off and the polymer was pelletized with an extruder with a 40 mmφ vent (220 ° C., 700 mmHg). The graft ratio was 60%, the intrinsic viscosity (measured in methyl ethyl ketone at 30 ° C.) was 0.42 dl / g, and the volume average particle size was 500 nm.

(3) Graft copolymer (B1-2) (shown as ABS in Table 1)
In a 7-liter glass flask equipped with a stirrer, 100 parts of ion-exchanged water, 1.5 parts of disproportionated sodium rosinate, 0.1 part of t-dodecyl mercaptan, polybutadiene (manufactured by JSR Corporation, # 0700) 40 parts (in terms of solid content), 15 parts of styrene and 5 parts of acrylonitrile were added, and the temperature was increased while stirring. When the temperature reaches 45 ° C., it consists of 0.1 part of ethylenediaminetetraacetate, 0.003 part of ferrous sulfate, 0.2 part of sodium formaldehyde sulfoxylate dihydrate and 15 parts of ion-exchanged water. An aqueous activator solution and 0.1 part of diisopropylbenzene hydroperoxide were added, and the reaction was continued for 1 hour. Thereafter, an incremental polymerization component consisting of 50 parts of ion-exchanged water, 1 part of disproportionated sodium rosinate, 0.1 part of t-dodecyl mercaptan, 0.2 part of diisopropyl hydroperoxide, 30 parts of styrene and 10 parts of acrylonitrile was added to 3 parts. The polymerization reaction was continued by continuously adding over time. After completion of the addition, stirring was further continued for 1 hour, 0.2 part of 2,2-methylene-bis (4-ethylene-6-tert-butylphenol) was added, and the reaction product was taken out from the flask. The reaction product latex was coagulated with 2 parts of sulfuric acid, and the reaction product was thoroughly washed with water and dried at 75 ° C. for 24 hours to obtain a white powder. The polymerization conversion rate was 97.2%, the graft rate was 75%, and the intrinsic viscosity was 0.44 dl / g.

(4) Vinyl monomer (b3) copolymer (B2) (indicated as AS in Table 1)
A technopolymer AS resin (Sanlex SAN-C) and a copolymer of styrene / acrylonitrile = 76/24 (%) were used. The intrinsic viscosity was 0.58 dl / g.

(5) Antioxidant (Indicated by AO1, AO2, and AO3 in Table 1)
As the antioxidant, ADEKA Adeka Stub AO-412S (AO1), Adeka Adeka Stub 2112 (AO2), and Sumitomo Chemical Industries Sumilizer GS (AO3) were used. In Tables 1 and 2, the addition amount (parts by mass) of the antioxidant is indicated by parts by mass with respect to 100 parts by mass of the thermoplastic resin composition.

(6) Chemical foaming agent As the chemical foaming agent, "Polyslen EB207" manufactured by Eiwa Chemical Industry Co., Ltd. and a master batch (sodium bicarbonate / ABS = 20/80 (mass ratio)) were used.

In Table 1 and Table 2, in the observation of the surface appearance, when a good flat surface was obtained, ◯, when there was a surface that was partially wavy, Δ, not flat, distorted and wavy When it is, it was set as x. The reason why the surface appearance deteriorated is considered that the skin layer 61 was not stably formed.
The measurement of the flexural modulus (bending modulus) (MPa) was performed according to ASTM D790. It means that the intensity | strength of the resin foam molded object 6 is so high that the value of a bending elastic modulus is large. The flexural modulus was not measured when the resin foam molded body 6 was wavy or distorted. In this case, “−” is described in the table.
Further, in the observation of the internal cross section, when the cross section of the resin foam molded body 6 is uniform and fine foam cells are formed, ○, when the outer diameter of the foam cells has a large or small distribution, Δ, the foam cells In the case where most of them had a large outer diameter, it was marked as x.

In Tables 1 and 2, the filling time (sec) is the time required to fill the cavity 41 and the filling gap 42 with the molten resin 60 in the filling step, and the expanded thickness (mm) is the value after foam molding. The thickness of the resin foam molded body 6 in the movable direction D was set, and the expansion ratio (−) was the amount of movement of the second mold part 3 in the separation direction R, that is, the expansion rate of the volume of the cavity 41.
In this confirmation test, polycarbonate resin (A) and rubber-reinforced vinyl resin (B) were blended in a blender and then extruded at 250 ° C. using a twin screw extruder TEX44 manufactured by Nippon Steel. A test was conducted using the pellets, and the results were evaluated. As the foam molding machine, a 180 (t) electric molding machine manufactured by Nippon Steel Works was used. Further, the obtained thermoplastic resin pellets and a foaming agent master batch were dry blended and supplied to a foam molding machine.

In Table 1, the inventive products 1 to 7 all had a good surface appearance. In addition, with respect to the internal cross section, except for Invention 5, uniform and fine foam cells were formed. In addition, about the invention product 5, it is thought that the formation state of the foam cell in an internal cross section was a little inferior, for example because the foaming ratio was large. Moreover, the bending elastic moduli (MPa) about invention goods 1-7 became all 1000 or more, and the outstanding result was obtained.
About invention products 1, 2, 4-7, it is thought that the favorable result was obtained by containing 50 mass% or 60 mass% of polycarbonate resin (A). On the other hand, regarding the product 3, the polycarbonate resin (A) has a low content of 30% by mass, but it is considered that good results were obtained by the composition containing 40% by mass of the AS resin.
Inventive products 1 to 7 are all composed of a mixture of an AES resin constituting the graft copolymer (B1) and an AS resin constituting the vinyl monomer (b3) copolymer (B2). did.

  When the expansion ratio was 1.4 times, 1.55 times, and 1.91 times, the test was performed. When the ratio was 1.4 times and 1.55 times, good results were obtained. On the other hand, it was found that when the expansion ratio was 1.91 times, the molten resin 60 filled in the cavity 41 did not expand sufficiently, and the surface of the molded resin foam molded body 6 was wavy. Therefore, it was found that the expansion ratio is preferably in the range of 1.1 to 1.6 times.

In Table 2, some of the comparative products 1 to 8 had a good surface appearance, but it was found that both the flexural modulus and the internal cross section were inferior. In particular, it is considered that the comparative products 1 to 5 do not contain any polycarbonate resin (A), which is the reason why the flexural modulus was low and the foamed cells in the internal cross section were not refined. . Moreover, it is considered that the comparative product 6 does not contain any rubber-reinforced vinyl resin (B), which is a major reason that the surface appearance and internal cross section are poor and the flexural modulus is low.
Moreover, about the comparative product 7, it is thought that the bending elastic modulus was not able to be raised very much, because the content rate of the polycarbonate resin (A) was small. Moreover, about the comparative product 8, when the content rate of polycarbonate resin (A) is large and the content rate of rubber-reinforced vinyl resin (B) is small, the surface appearance and internal cross section are poor, and the flexural modulus is low. This is considered to be a major reason.

  From the above results, the polycarbonate resin (A) and the rubber-reinforced vinyl resin (B) are appropriately used for the resin foam molded products 6 of Inventions 1 to 7 using the thermoplastic resin composition shown in Table 1. It was found that by using the contained thermoplastic resin composition, a stable skin layer 61 can be formed, and the resin foam molded body 6 having excellent strength and appearance can be molded.

Sectional explanatory drawing which shows the manufacturing apparatus which has a 1st type | mold part and a 2nd type | mold part in an Example. Sectional explanatory drawing which shows the state which filled the cavity and the clearance gap for filling with the molten resin in the filling process in an Example. Sectional explanatory drawing which shows the state which filled the molten resin in the cavity and the clearance gap for filling in the Example in the state seen from the direction orthogonal to FIG. Sectional explanatory drawing which shows the state which moved the 2nd type | mold part with respect to the 1st type | mold part in the movable process in an Example, and shape | molded the resin foam molded object in the cavity.

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 Manufacturing apparatus 2 1st type | mold part 21 Cavity formation recessed part 211 Inner side surface 22 Resin injection port 3 2nd type | mold part 31 Cavity formation convex part 311 Outer side surface 41A, B Cavity 42 Filling gap 6 Resin foam molding 60 Molten resin 61 Skin Layer 62 Foam layer D Movable direction R Separation direction

Claims (7)

Using a first mold part and a second mold part movable relative to the first mold part, a chemical foam is formed in a cavity formed between the second mold part and the first mold part. A filling step of filling a molten resin obtained by kneading an agent into a thermoplastic resin composition, and a movable unit that relatively moves the first mold part and the second mold part in a separation direction in which the volume of the cavity is increased. In a method of performing a process and producing a resin foam molded article,
The content of the chemical foaming agent is 0.05 to 5 parts by mass with respect to 100 parts by mass of the thermoplastic resin composition.
The thermoplastic resin composition contains the polycarbonate resin (A) and the rubber-reinforced vinyl resin (B) in such a ratio that (A) is 20 to 80% by mass and (B) is 80 to 20% by mass. And
The rubber-reinforced vinyl resin (B) is obtained by polymerizing a vinyl monomer (b2) containing an aromatic vinyl compound in the presence of a rubbery polymer (b1) which is an ethylene / α-olefin rubber. A resin foam molded article comprising a graft copolymer (B1) or a mixture of a copolymer (B2) of a vinyl monomer (b3) and the graft copolymer (B1). Production method.   2. The thermoplastic resin composition according to claim 1, wherein the polycarbonate resin (A) contains an aromatic polycarbonate resin in an amount of 50 to 70 mass%, and the balance is made of the rubber-reinforced vinyl resin (B). A method for producing a resin foam molded article. In Claim 1 or 2, the second mold part is provided with a cavity forming convex part arranged in a cavity forming concave part provided in the first mold part,
Between the inner surface formed in parallel to the movable direction of the first mold portion and the second mold portion in the cavity forming concave portion and the outer surface formed in parallel to the movable direction in the cavity forming convex portion. A filling gap for filling the molten resin is formed in communication with the cavity;
In the filling step, the molten resin is filled into the cavity and the filling gap is filled,
In the moving step, after filling the cavity and the filling gap with the molten resin, the first mold part and the second mold part are relatively moved in the separation direction. A method for producing a resin foam molded article.   4. The unfoamed skin layer according to any one of claims 1 to 3, wherein in the filling step, the molten resin is filled into the whole of the cavity and the filling gap, and the molten resin is semi-cured. In the movable step, a foam layer in which the first mold part and the second mold part are relatively moved in the separation direction and the molten resin is foamed on the inner part with respect to the skin layer is formed. A method for producing a resin foam molded article, comprising forming the resin foam molded article. The first mold part according to any one of claims 1 to 4, wherein the first mold part is a fixed mold part provided with a resin inlet for filling the molten resin into the cavity.
The method for producing a resin foam molded article, wherein the second mold part is a movable mold part movable in the separation direction with respect to the first mold part. The chemical foaming agent according to any one of claims 1 to 5, wherein the chemical blowing agent is a group of sodium hydrogen carbonate, azodicarbonamide, N, N'-dinitrosopentamethylenetetramine, 4,4'-oxybis (benzenesulfonylhydrazide). A method for producing a resin foam molded article, wherein the foamed molded article is selected from the group consisting of: In any one of Claims 1-6, the said rubber | gum reinforcement | strengthening vinyl-type resin (B) has a graft ratio of 10-150%, and the intrinsic viscosity (measured in methyl ethyl ketone at 30 degreeC) of an acetone soluble part. 0.2-0.8 dl / g,
The polycarbonate resin (A) has a viscosity average molecular weight of 12,000 to 40,000 .