  The present invention relates to a grease composition and a bearing in which the grease composition is enclosed. More specifically, the present invention relates to a novel grease composition not yet published in literature containing a specific antirust additive and a bearing in which the grease composition is enclosed.

  Conventionally, grease compositions containing various rust preventive additives have been proposed. For example, a grease composition using at least one selected from zinc naphthenate and succinic acid derivatives as a rust preventive additive is known (Patent Document 1).

JP 2009-121689 A

  However, when a mixture comprising a nonionic surfactant and zinc 2-ethylhexanoate or zinc calcium amine complex is used as a grease composition as a rust preventive additive, good acoustic characteristics and leakage resistance are obtained. It is not known to exhibit excellent rust prevention properties while maintaining the above.

  The present invention has been found that the above specific rust preventive additive exhibits excellent rust preventive properties while maintaining good acoustic properties and leakage resistance, thereby providing a new grease composition. It is an object of the present invention to provide a long-life bearing in which the grease composition is enclosed.

The grease composition of the present invention is a grease composition comprising (A) a base oil, (B) a thickener, and (C) a rust preventive additive,
The rust preventive additive (C) is
(C-1) a nonionic surfactant;
(C-2) consisting of zinc 2-ethylhexanoate or zinc calcium amine complex,
The said antirust additive (C) is mix | blended 1.8-8 weight part with respect to a total of 100 weight part of (A) base oil and (B) thickener.

  The nonionic surfactant (C-1) is preferably sorbitan monooleate or sorbitan trioleate.

  Moreover, it is preferable that a rust preventive additive (C) further contains (C-3) metal sulfonate.

  The metal sulfonate (C-3) is preferably zinc sulfonate, calcium sulfonate, lithium sulfonate or barium sulfonate.

  The thickener (B) is preferably a diurea compound or lithium soap.

  The bearing of the present invention is characterized in that the grease composition is sealed in a bearing space.

  According to the grease composition of the present invention, it is possible to provide a novel grease composition that exhibits excellent rust prevention properties while maintaining good acoustic characteristics and leakage resistance. In addition, a long-life bearing in which the grease composition is enclosed can be provided.

  The grease composition of the present invention is a grease composition comprising (A) a base oil, (B) a thickener, and (C) a rust preventive additive, wherein the rust preventive additive (C) is: It consists of (C-1) a nonionic surfactant and (C-2) zinc 2-ethylhexanoate or zinc calcium amine complex, and the rust preventive additive (C) comprises (A) a base oil, (B) 1.8 to 8 weight part is mix | blended with respect to a total of 100 weight part with a thickener.

  The base oil (A) is not particularly limited as long as it is used in the grease composition. For example, crude oil is distilled under reduced pressure, solvent is removed, solvent extraction, hydrocracking, solvent dewaxing, sulfuric acid washing, clay Mineral oil refined by appropriately combining purification, hydrorefining, etc., such as dibutyl sebacate, di-2-ethylhexyl sebacate, dioctyl adipate, diisodecyl adipate, ditridecyl adipate, ditridecyl glutarate, methyl acetyl cinnolate, etc. Diester oils, or aromatic ester oils such as trioctyl trimellitate, tridecyl trimellitate, tetraoctyl pyromellitate and the like, and further, for example, trimethylolpropane caprylate, trimethylolpropane pelargonate, pentaerythritol-2- Ethyl hexanoate Polyol ester oils such as pentaerythritol belargonate, and also ester oils such as complex ester oils that are oligoesters of polyhydric alcohols and mixed fatty acids of dibasic acids and monobasic acids, such as polyethylene glycol, polypropylene glycol , Polyethylene glycol monoether, polyglycol such as polypropylene glycol monoether, or phenyl such as monoalkyl triphenyl ether, alkyl diphenyl ether, dialkyl diphenyl ether, pentaphenyl ether, tetraphenyl ether, monoalkyl tetraphenyl ether, dialkyl tetraphenyl ether Ether oils such as ether oils, e.g. normal paraffin, isoparaffin, polybutene, polyiso Styrene, 1-decene oligomer, can be used synthetic hydrocarbon such as polyethylene -α- olefins or their hydrides co oligomer of 1-decene and ethylene. From the viewpoints of low torque and long life, heat resistance and long life, ester oil, poly-α-olefin, and phenyl ether oil are particularly useful. Further, it is useful to use 70 to 90% by weight of the base oil (A) in the grease composition.

As the thickener (B), diurea compounds, lithium soap, calcium soap, sodium soap, aluminum soap, sodium terephthalate, fluorine, organic bentonite, silica gel, and the like can be used. It does not specifically limit as a kind of diurea compound, The diurea and polyurea shown by the following general formula (I) can be used. In the formula, R ² is an aromatic hydrocarbon group having 6 to 15 carbon atoms, R ¹ and R ³ are aromatic hydrocarbon groups having 6 to 18 carbon atoms, a cyclohexyl group, and a cyclohexyl derivative group having 7 to 12 carbon atoms. Alternatively, a diurea compound representing an alkyl group having 8 to 22 carbon atoms can be used.

  The type of the lithium soap is not particularly limited, and lithium soap synthesized from lithium hydroxide and a higher fatty acid having 10 to 28 carbon atoms and / or a higher hydroxy fatty acid having 10 or more hydroxyl groups and having one or more hydroxyl groups is used. be able to. Considering the use as a grease composition, it is useful that the thickener (B) is used in an amount of 5 to 30% by weight in the grease composition, and the hardness is 220 to 340.

  The rust preventive additive (C) comprises (C-1) a nonionic surfactant and (C-2) zinc 2-ethylhexanoate or zinc calcium amine complex. Moreover, (C-3) metal sulfonate can be further mix | blended.

  The nonionic surfactant (C-1) is not particularly limited, but sorbitan monooleate and sorbitan trioleate are useful from the viewpoint of emulsifiability.

  Although it does not specifically limit as metal sulfonate (C-3), From a adsorptive viewpoint, zinc sulfonate, calcium sulfonate, lithium sulfonate, or barium sulfonate is useful.

  In the rust preventive additive (C), the blending ratio of the nonionic surfactant (C-1) and zinc 2-ethylhexanoate or zinc calcium amine complex (C-2) is (C-1) : (C-2) 1-5: 5-1 is particularly useful.

As a compounding quantity of a rust preventive additive (C), it is preferable that 1.8-8 weight part is mix | blended with respect to a total of 100 weight part of (A) base oil and (B) thickener, 3 More preferably, it is blended by -6% by weight. When the amount is less than 1.8% by weight, there is a problem that the rust prevention effect is not sufficient. When the amount exceeds 8% by weight, leakage resistance is deteriorated and in the bearing in which the grease composition is encapsulated, extreme pressure agent, wear resistance There is a problem that the life is shortened by forming a film of a rust preventive agent on the bearing rolling surface in preference to the agent.
These grease compositions also contain various additives such as antioxidants, extreme pressure agents, antiwear agents, dyes, hue stabilizers, thickeners, structural stabilizers, metal deactivators, and viscosity index improvers. May be added in an appropriate amount.

  Next, a bearing in which the grease composition of the present invention is sealed in a bearing space will be described.

  The bearing of the present invention is formed by enclosing the grease composition in a bearing space. In the present invention, a bearing refers to a rotating part of various power units of an automobile engine, for example, an alternator, an electromagnetic clutch for a car air conditioner, an automobile electrical part such as an intermediate pulley, a rolling bearing used for an engine accessory part, a home appliance, It is a concept including a rolling bearing used for a general-purpose motor such as an OA device. The structure of the bearing itself is not limited, and various known ball bearings and roller bearings can be used. The grease of the present invention is formed in the bearing space formed by the inner ring, the outer ring and the rolling elements. The rolling bearing of the present invention is constituted by enclosing the composition. The amount of the grease for the rolling bearing can be appropriately changed according to the type and dimensions of the rolling bearing, but may be approximately the same as that of the conventional one.

  EXAMPLES Hereinafter, although an Example demonstrates this invention in detail, this invention is not limited to these Examples at all.

  The evaluation method is shown below.

(Rust prevention test 1)
0.8 g of the prepared grease composition is sealed in the bearing space of a sealed deep groove ball bearing (model number: 62022 RU), rotated at 1800 min ^-1 for 30 seconds, and then filled with 0.8 mL of 0.5% saline. And rotate for another 30 seconds. Then, it is left still at 40 ° C. for 120 hours, and the state of rust generated on the inner side of the bearing outer ring and the outer side of the bearing inner ring, that is, the rolling surface is visually observed. The test is performed three times.
(Rust prevention test 2)
The test is performed according to ASTM D1743. That is, the prepared grease composition was sealed in a conical roller bearing (model number: inner ring 09974 outer ring 09196), rotated at 1750 min ⁻¹ for 10 seconds, adjusted the amount of grease charged to 2.0 g, and further rotated for 60 seconds. After immersing in 1% saline for 10 seconds, after standing in a sealed container filled with 5 ml of 1% saline for 48 hours at 52 ° C., the state of rust generated on the rolling surface of the inner ring is visually observed. The test is performed three times.
Rating ◎: No rust occurred ○: Only point rust occurred slightly △: Small rust occurred ×: Medium rust occurred XX: Surface rust occurred (acoustic property test)
0.8 g of the prepared grease composition is sealed in a bearing space of a sealed deep groove ball bearing (model number 62022RU), a 20 N thrust load is applied, and it is rotated at 1800 min ^-1 for 30 seconds. Anderon meter (model number ADA- 15, Anderon value was evaluated using (Made by Ebara Laboratory). 5 or less was considered good.

In this example, the following raw materials were used.
Zn sulfonate: synthetic Zn sulfonate Ca sulfonate: petroleum Ca sulfonate Li sulfonate: synthetic Li sulfonate Ba sulfonate: synthetic Ba sulfonate sorbitan monooleate: surfactant sorbitan trioleate: surfactant zinc zinc 2-ethylhexanoate Calcium amine complex: KX1270 (manufactured by King Industries, Inc.)

Examples 1-18 and Comparative Examples 1-7
Add rust preventive additives in the proportions shown in Table 1 to urea grease of 2 to 3 consistency (prepared by adding 16 parts by weight of diurea compound (thickener) to 84 parts by weight of alkyldiphenyl ether oil (base oil)) And uniformly dispersed to prepare a grease composition. The prepared grease composition was subjected to rust prevention test 1 and acoustic characteristic test. The results are shown in Table 1.

Examples 19-31 and Comparative Examples 8-14
Add rust preventive additives in the proportions shown in Table 2 to lithium grease of 2 to 3 consistency (prepared by adding 10 parts by weight of lithium soap (thickener) to 90 parts by weight of ester oil (base oil)) And uniformly dispersed to prepare a grease composition. The prepared grease composition was subjected to rust prevention test 2 and acoustic characteristic test. The results are shown in Table 2. In addition, although the grease composition of Comparative Example 14 was good in both rust prevention and acoustic characteristics, the grease composition itself was softened, resulting in poor leakage resistance and a short life.

Claims (6)

A grease composition comprising (A) a base oil, (B) a thickener, and (C) a rust preventive additive, wherein the rust preventive additive (C) is:
(C-1) a nonionic surfactant;
(C-2) consisting of zinc 2-ethylhexanoate or zinc calcium amine complex,
A grease composition comprising 1.8 to 8 parts by weight of the rust preventive additive (C) based on a total of 100 parts by weight of the base oil (A) and the thickener (B). The grease composition according to claim 1, wherein the nonionic surfactant (C-1) is sorbitan monooleate. The grease composition according to claim 1 or 2, wherein the rust preventive additive (C) further comprises (C-3) a metal sulfonate. The grease composition according to any one of claims 1 to 3, wherein the metal sulfonate (C-3) is zinc sulfonate, calcium sulfonate, lithium sulfonate, or barium sulfonate. The grease composition according to any one of claims 1 to 4, wherein the thickener (B) is a diurea compound or lithium soap. A bearing formed by enclosing the grease composition according to claim 1 in a bearing space.